JP2020111723A - 水性多液型ポリウレタン塗料組成物 - Google Patents
水性多液型ポリウレタン塗料組成物 Download PDFInfo
- Publication number
- JP2020111723A JP2020111723A JP2019211594A JP2019211594A JP2020111723A JP 2020111723 A JP2020111723 A JP 2020111723A JP 2019211594 A JP2019211594 A JP 2019211594A JP 2019211594 A JP2019211594 A JP 2019211594A JP 2020111723 A JP2020111723 A JP 2020111723A
- Authority
- JP
- Japan
- Prior art keywords
- coating composition
- polymerizable unsaturated
- liquid
- unsaturated monomer
- polyisocyanate compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、以下の水性多液型ポリウレタン塗料組成物及び塗装方法の実施形態を包含する。
項1.水酸基含有樹脂(a1)及び水を含有する第1液(A)、並びに、ポリイソシアネート化合物(b1)を有する第2液(B)を含有する水性多液型ポリウレタン塗料組成物であり、該ポリイソシアネート化合物(b1)が、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)を含有することを特徴とする、水性多液型ポリウレタン塗料組成物。
項2.前記水酸基含有樹脂(a1)が、ガラス転移温度40℃以上の水酸基含有アクリル樹脂の水分散体を含有することを特徴とする、項1に記載の水性多液型ポリウレタン塗料組成物。
項3.前記水酸基含有アクリル樹脂の水分散体が、親水性基含有重合性不飽和モノマーを構成成分の一部として含有する、自己乳化型のアクリル樹脂の水分散体であることを特徴とする、項2に記載の水性多液型ポリウレタン塗料組成物。
項4.前記水酸基含有アクリル樹脂の水分散体が、主鎖部及び側鎖部からなるグラフト構造を有する水酸基含有アクリル樹脂の水分散体であって、主鎖部及び側鎖部のどちらか一方を構成する重合性不飽和モノマー成分(X)が、エポキシ基含有重合性不飽和モノマー(x1)、水酸基含有重合性不飽和モノマー(x2)及びその他の重合性不飽和モノマー(x3)を含有し、もう一方を構成する重合性不飽和モノマー成分(Y)が、カルボキシル基含有重合性不飽和モノマー(y1)、水酸基含有重合性不飽和モノマー(y2)及びその他の重合性不飽和モノマー(y3)を含有することを特徴とする、項2又は3に記載の水性多液型ポリウレタン塗料組成物。
項5.前記第1液(A)が、ポリエーテルポリオールを含有することを特徴とする、項1から4のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項6.前記第1液(A)の不揮発分濃度が25〜55質量%の範囲内である、項1から5のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項7.前記第2液(B)において、ポリイソシアネート化合物(b1)が、さらに親水性ポリイソシアネート化合物を含有することを特徴とする、項1から6のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項8.前記第2液(B)において、ポリイソシアネート化合物(b1)内のイソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)の割合が10〜90質量%であることを特徴とする、項1から7のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項9.前記第2液(B)において、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)が脂肪族トリイソシアネート化合物である、項1から8のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項10.前記第2液(B)の不揮発分濃度が20〜100質量%の範囲内である、項1から9のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項11.透明塗料組成物である、項1から10のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
項12.被塗物に、項1から11のいずれか一項に記載の水性多液型ポリウレタン塗料組成物を塗装する塗装方法。
1.第1液(A)
本発明の第1液(A)は、水酸基含有樹脂(a1)及び水を含有することを特徴とする。
本発明に係る水性多液型ポリウレタン塗料組成物の第1液を構成する水酸基含有樹脂(a1)としては、例えば、アクリル樹脂、ポリエステル樹脂、アルキド樹脂、ウレタン樹脂、フッ素樹脂、エポキシ樹脂、シリコーン樹脂、ポリエーテル樹脂、アクリルシリコーン樹脂、酢酸ビニル・ベオバ樹脂等が挙げられる。また、これらは単独で使用しても2種以上を併用しても良い。中でも、水酸基含有樹脂(a1)として、少なくとも一種のアクリル樹脂を含有することが好ましい。また、水酸基含有樹脂(a1)は、主剤の安定性及び作業性の観点から、水溶性樹脂及び/又は水分散性樹脂であることが好ましく、特に、乾燥性及び耐候性の点から、水酸基含有アクリル樹脂の水分散体(エマルション)が好ましい。
1/Tg(K)=W1/T1+W2/T2+・・・Wn/Tn
Tg(℃)=Tg(K)−273
式中、W1、W2、・・・Wnは各モノマーの質量分率であり、T1、T2・・・Tnは各モノマーのホモポリマーのガラス転移温度Tg(K)である。尚、各モノマーのホモポリマーのガラス転移温度は、POLYMER HANDBOOK Fourth Edition,J.Brandrup,E.h.Immergut,E.A.Grulke編(1999年)による値であり、該文献に記載されていないモノマーのガラス転移温度は、該モノマーのホモポリマーを重量平均分子量が50000程度になるようにして合成したときの静的ガラス転移温度とする。
SP値=SP1×fw1+SP2×fw2+………+SPn×fwn
上記式中、SP1、SP2、………SPnは、各重合性モノマーのホモポリマーのSP値を表し、fw1、fw2、………fwnは、各重合性不飽和モノマーのモノマー総量に対する質量分率を表す。
本発明における水酸基含有樹脂(a1)は、形成塗膜の硬度が優れることなどから、その成分の一部として水酸基含有アクリル樹脂の水分散体である水酸基含有アクリル樹脂エマルション(a1−1)を含有することが好ましい。
(1)一段階目で主鎖部及び側鎖部のどちらか一方を構成する重合性不飽和モノマー成分(X)による共重合体を合成し、次に二段階目でもう一方を構成する重合性不飽和モノマー成分(Y)を添加して共重合体の合成を行う。
(2)一段階目で主鎖部及び側鎖部のどちらか一方を構成する重合性不飽和モノマー成分(X)による共重合体を合成し、それとは別に二段階目でもう一方を構成する重合性不飽和モノマー成分(Y)の共重合体を合成し、1段目で合成した共重合体に2段目で合成した共重合体を添加して共重合を行う。
本発明における水酸基含有アクリル樹脂エマルション(a1−1)においては、上記(1)の方法で製造されることが好ましい。
一段階目を形成する重合性不飽和モノマー成分(X)は、エポキシ基含有重合性不飽和モノマー(x1)、水酸基含有重合性不飽和モノマー(x2)及びその他の重合性不飽和モノマー(x3)を含有することが好ましい。
特に本発明に好ましく適用されうる水酸基含有アクリル樹脂は、上述の通り水酸基含有アクリル樹脂を製造する少なくとも1つの段階の重合性不飽和モノマー成分(X)以外にさらに重合性不飽和モノマー成分(Y)を共重合成分とする少なくとも2段階以上の多段階で製造されたものである。
主鎖部及び側鎖部の一方を構成する重合性不飽和モノマー成分(X)が、エポキシ基含有重合性不飽和モノマー(x1)、水酸基含有重合性不飽和モノマー(x2)及びその他の重合性不飽和モノマー(x3)を含有し、もう一方を構成する重合性不飽和モノマー成分(Y)が、カルボキシル基含有重合性不飽和モノマー(y1)、水酸基含有重合性不飽和モノマー(y2)及びその他の重合性不飽和モノマー(y3)を含有することで、水酸基含有樹脂(a1)のガラス転移温度の調整、水酸基価の調整、上記モノマーの反応性の調整等がより容易となり、短い乾燥時間で硬度に優れた塗膜を作製する点、また得られる樹脂の分散性および貯蔵安定性の点で有利である。
本発明において、第1液(A)は、仕上がり外観に優れた塗膜が得られることから、ポリエーテルポリオールを含むことが適している。ポリエーテルポリオールは前記水酸基含有樹脂(a1)とは異なる化合物である。
本発明の第1液(A)には、水酸基含有樹脂(a1)以外の樹脂エマルション又は水溶性樹脂、顔料分、中和剤、レオロジーコントロール剤、表面調整剤、消泡剤、硬化触媒、紫外線吸収剤、光安定化剤、有機溶剤等を必要に応じて配合することができる。
硬化触媒を本発明の水性塗料組成物に配合することにより、該組成物の乾燥性をより向上させる場合があるため特に好ましい。
硬化触媒としては、例えば、ジアセチル錫ジアセテート、ジブチル錫ジラウレート、ジブチル錫ジアセテート、ジオクチル錫ジラウレート、ジアセチル錫ジオクトエート、オクチル酸錫、ジブチル錫ジアセテート、ジブチル錫ジオクトエート等の有機錫化合物;アルミニウムトリメトキシド、アルミニウムトリス(アセチルアセトネート)、アルミニウムトリ−n−ブトキシド、アルミニウムトリス(アセトアセテートエチル)、アルミニウムジイソプロポキシ(アセトアセテートエチル)、アルミニウムアセチルアセトナート等の有機アルミニウム化合物;チタニウムテトラ(モノエチルエトキシド)、チタニウムテトラ(モノエチルエトキシド)、チタニウムテトラ(モノブチルエトキシド)、チタニウムテトラキス(アセチルアセトネート)、テトラノルマルブチルチタネート等の有機チタン化合物;ジルコニウムテトラ(モノメチルエトキシド)、ジルコニウムテトラ(モノエチルエトキシド)、ジルコニウムテトラ(モノブチルエトキシド)、ジルコニウムノルマルプロピレート、ジルコニウムノルマルブチレート、ジルコニウムテトラキス(アセチルアセトネート)等の有機ジルコニウム化合物;ナフテン酸亜鉛等の有機亜鉛化合物;オクチル酸コバルト、ナフテン酸コバルト等の有機コバルト化合物;トリメチルアミン、トリエチルアミン、2−(ジメチルアミノ)エチルメタクリレート、1,4−ジアザビシクロ[2.2.2]オクタン、1,8−ジアザビシクロ[5.4.0]−7−ウンデセン、1,5−ジアザビシクロ[4.3.0]−5−ノネン、1−メチルピペリジン、1−メチルピロリジン等の脂肪族アミン、ピリジン、4−ジメチルアミノピリジン、4−(1−ピペリジル)ピリジン、N−メチルイミダゾール、N,N−ジメチルアニリン等のアミン触媒;カルボン酸の鉛、スズ、亜鉛、及び鉄錯体;ホウ酸トリメチル、ホウ酸トリエチル、ホウ酸トリプロピル、ホウ酸トリブチル、ホウ酸トリフェニル、ホウ酸トリ(4−クロロフェニル)、ホウ酸トリヘキサフルオロイソプロピル等のホウ酸エステル等のホウ酸化合物;モリブデン酸、モリブデン酸カリウム、モリブデン酸カルシウム、モリブデン(VI)酸二ナトリウム二水和物、モリブデン酸アンモニウム、モリブデン酸リチウム、モリブデン酸六アンモニウム四水和物、七モリブデン酸六アンモニウム四水和物、モリブデン酸マグネシウム、モリブデン酸ルビジウム、モリブデン酸セシウム、モリブデン酸コバルト(II)、モリブデン酸マンガン(II)、モリブデン酸亜鉛等のモリブデン酸化合物又はモリブデン酸塩;酸化モリブデン;リンモリブデン酸n水和物、リンモリブデン酸ナトリウムn水和物、リンモリブデン酸アンモニウム三水和物等のリンモリブデン酸化合物又はリンモリブデン酸塩;モリブデニム(IV)オキサイドビスアセチルアセトネート、ビス(アセチルアセトナト)酸化モリブデン(IV)、二酸化モリブデンテトラメチルヘプタジオネート、モリブデン酸テトラエチルアンモニウム、モリブデン酸トリメチルスタンニル・テトラブチルアンモニウム、モリブデンアルコキシド、2−エチルヘキサン酸モリブデン、ヘキサカルボニルモリブデン等の有機モリブデン化合物等が挙げられ、これらは単独で又は2種以上組み合わせて使用することができる。これらの中でも特に、人体や環境への配慮及び、硬化性と得られる塗膜の仕上り性とのバランスの観点から、有機亜鉛化合物及び/又はモリブデン化合物が好ましく、さらに乾燥性と塗膜硬度の点から、モリブデン化合物が特に好ましい。
また、第1液(A)が硬化触媒を配合する場合その含有量は、水酸基含有樹脂(a1)不揮発分100質量部を基準として、0.01〜1.00質量部、特に0.01〜0.50質量部の範囲内にあることが好ましい。
本発明の第2液(B)は、ポリイソシアネート化合物(b1)を含有することを特徴とする。
本発明におけるポリイソシアネート化合物(b1)は、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)を含むことを特徴とする。
第2液(B)がイソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)を含有することを特徴とする。具体的には、例えば、1,8−ジイソシアナト−4−イソシアナトメチルオクタン、(2S)−2,6−ジイソシアナトヘキサン酸2−イソシアナトエチル(慣用名:リジントリイソシアネート)、2,6−ジイソシアナトヘキサン酸2−イソシアナトエチル、1,6,11−トリイソシアナトウンデカン等の脂肪族トリイソシアネート化合物、1,3,5−トリイソシアナトシクロヘキサン、1,3,5−トリメチルイソシアナトシクロヘキサン等の脂環族トリイソシアネート化合物、1,3,5−トリイソシアナトベンゼン、2,4,6−トリイソシアナトトルエン等の芳香族トリイソシアネート等が挙げられ、これらは単独で又は2種以上を組み合わせて使用することができる。
本発明におけるポリイソシアネート化合物(b1)は、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物以外のその他のポリイソシアネート化合物(b1−2)を含有することができる。ポリイソシアネート化合物とは、1分子中に遊離のイソシアネート基を2個以上有する化合物であり、例えば、脂肪族ポリイソシアネート化合物、脂環族ポリイソシアネート化合物、芳香脂肪族ポリイソシアネート化合物、芳香族ポリイソシアネート化合物、該ポリイソシアネート化合物の誘導体等が挙げられ、これらは単独で又は2種以上を組み合わせて使用することができる。
本発明の第2液(B)には、ポリイソシアネート化合物(b1)と反応しない樹脂、顔料分、中和剤、レオロジーコントロール剤、表面調整剤、消泡剤、硬化触媒、紫外線吸収剤、光安定化剤、脱水剤等を必要に応じて配合することができる。
本発明の水性多液型ポリウレタン塗料組成物は、前記第1液(A)と前記第2液(B)とを、使用直前に混合して、得られた混合物を適宜希釈して塗装することができる。第1液(A)と第2液(B)の使用割合としては、第1液(A)100質量部を基準として第2液(B)が20〜100質量部、特に30〜70質量部となるような割合が適している。
本発明の水性多液型ポリウレタン塗料組成物は、前記第1液(A)、前記第2液(B)、及び必要に応じて前記第1液(A)と第2液(B)以外の成分と、を使用直前に混合して、得られた混合物を適宜希釈して塗装することができる。
セッティングは、通常、塗装された被塗物をほこりのない雰囲気に室温で30秒〜60分放置することにより行うことができる。セッティング時における相対湿度(以下RHと略すことがある)は、80%以下、特に70%以下が好ましい。
乾燥にはIR炉、電気熱風乾燥器等を用いることができる。
製造例1
温度計、撹拌機、還流冷却管、窒素導入口を備えたガラス製4つ口フラスコにプロピレングリコールモノプロピルエーテルを50部入れ、撹拌しながら窒素気流下120℃まで昇温した。120℃に達したところで、表1の第1段階欄に記載のモノマー配合と重合開始剤にt−ブチルパーオキシ−2−エチルヘキサノエート1.5部を予め混合した混合溶液を4時間かけて滴下し、さらに滴下終了後120℃の温度に1時間保持した。引き続き120℃の温度を保持したまま、上記フラスコ中に、同表1の第2段階の欄に記載のモノマー配合とt−ブチルパーオキシ−2−エチルヘキサノエート0.3部を予め混合した混合溶液を1時間かけて滴下し、さらに滴下終了後120℃で1.5時間保持してアクリルポリオール溶液を得た。続いて、得られたアクリルポリオール溶液から不揮発分が85%になるまでプロピレングリコールモノプロピルエーテルを減圧下で留去した。これを95℃まで冷却し、ジメチルエタノールアミンでpHを8.0に調整して30分間撹拌した。さらに、撹拌しながら不揮発分が50%となるように脱イオン水を2時間かけて滴下してアクリル樹脂の水分散体(エマルション)を得た。得られたアクリル樹脂エマルション(A1−1)の重量平均分子量、酸価、水酸基価及び平均粒子径を下記表1に示す。
製造例1において、各共重合成分のモノマー組成及び配合量を下記表1に示す内容とする以外は製造例1と同様にして、アクリル樹脂エマルション(A1−2)及び(A1−4)を得た。
温度計、撹拌機、還流冷却管、窒素導入口を備えたガラス製4つ口フラスコにプロピレングリコールモノプロピルエーテルを50部入れ、撹拌しながら窒素気流下120℃まで昇温した。120℃に達したところで、表1の第1段階欄に記載のモノマー配合と重合開始剤t−ブチルパーオキシ−2−エチルヘキサノエート1.5部とを予め混合した混合溶液を4時間かけて滴下し、さらに滴下終了後120℃の温度に1時間保持した。引き続き120℃の温度を保持したまま、上記フラスコ中に、同表1の第2段階の欄に記載のモノマー配合とt−ブチルパーオキシ−2−エチルヘキサノエート0.3部とを予め混合した混合溶液を1時間かけて滴下し、さらに滴下終了後120℃で1.5時間保持してアクリルポリオール溶液を得た。続いて、得られたアクリルポリオール溶液から不揮発分が85%になるまでプロピレングリコールモノプロピルエーテルを減圧下で留去した。これを95℃まで冷却し、「ニューコール707SF」(注1)を5部加えて30分間撹拌した。さらに、撹拌しながら不揮発分が50%となるように脱イオン水を2時間かけて滴下してアクリル樹脂エマルション(A1−3)を得た。
温度計、撹拌機、還流冷却管、窒素導入口を備えたガラス製4つ口フラスコにプロピレングリコールモノプロピルエーテルを50部入れ、撹拌しながら窒素気流下120℃まで昇温した。120℃に達したところで、表1の第1段階欄に記載のモノマー配合と重合開始剤t−ブチルパーオキシ−2−エチルヘキサノエート1.8部とを予め混合した混合溶液を4時間かけて滴下し、さらに滴下終了後120℃の温度に1時間保持してアクリルポリオール溶液を得た。続いて、得られたアクリルポリオール溶液から不揮発分が85%になるまでプロピレングリコールモノプロピルエーテルを減圧下で留去した。これを95℃まで冷却し、ジメチルエタノールアミンでpHを8.0に調整して30分間撹拌した。さらに、撹拌しながら不揮発分が50%となるように脱イオン水を2時間かけて滴下してアクリル樹脂エマルション(A1−5)を得た。
温度計、サーモスタット、撹拌装置、還流冷却器、窒素導入管及び滴下装置を備えた反応容器に、脱イオン水85部及び「アデカリアソープSR−1025」(商品名、ADEKA社製、乳化剤、有効成分25%)0.8部を仕込み、窒素気流中で撹拌混合し、80℃に昇温させた。次いで下記コア部用モノマー乳化物の全量のうちの5%量及び6%過硫酸アンモニウム水溶液2.5部を反応容器内に配合し80℃で15分間保持した。その後、コア部用モノマー乳化物の残部を3時間かけて、同温度に保持した反応容器内に滴下し、滴下終了後1時間熟成を行った。次に、下記シェル部用モノマー乳化物を1時間かけて滴下し、1時間熟成した後、5%ジメチルアミノエタノール水溶液3.8部を反応容器に徐々に加えながら30℃まで冷却し、100メッシュのナイロンクロスで濾過しながら排出し、固形分35%のアクリル樹脂エマルション(A1−6)を得た。得られたアクリル樹脂エマルションは、コア部は重合性不飽和基を1分子中に2個以上有する重合性不飽和モノマー(アリルメタクリレート)によって架橋している。
「コア部用モノマー乳化物」:脱イオン水50部、「アデカリアソープSR−1025」3.1部、アリルメタクリレート1部、スチレン10部、メチルメタクリレート28部、エチルアクリレート20部及び2−ヒドロキシエチルメタクリレート18部を混合攪拌することにより、コア部用モノマー乳化物を得た。
「シェル部用モノマー乳化物」:脱イオン水50部、「アデカリアソープSR−1025」1.8部、6%過硫酸アンモニウム水溶液0.04部、スチレン3部、2−ヒドロキシエチルメタクリレート10部、メタクリル酸3部、エチルアクリレート3部及びメチルメタクリレート4部を混合攪拌することにより、シェル部用モノマー乳化物を得た。
実施例1
容器に、製造例1で得られた不揮発分50%のアクリル樹脂エマルション(A1−1)70部、「BYK−348」(注4)0.5部、「BYK−015」(注5)1部、「TINUVIN384−2」(注6)1部、「TINUVIN292」(注7)0.5部、「SNシックナー621N」(注8)0.5部(不揮発分0.2部)、脱イオン水26部を配合し、室温で攪拌下、ジメチルエタノールアミンをpH7.6となるまで滴下して第1液(A)を作製した。
別の容器に、1,8−ジイソシアナト−4−イソシアナトメチルオクタン12.5部、「バイヒジュールXP2655」(注10)12.5部、ジプロピレングリコールジメチルエーテル15部、エチレングリコールモノブチルエーテルアセテート5部、ジエチレングリコールモノエチルエーテルアセテート5部を配合し、均一になるまで混合して第2液(B)を作製した。
前記第1液(A)100部に、第2液(B)が50部となるように両者を混合し、不揮発分含有率が40%となるように脱イオン水を加えて攪拌して水性多液型ポリウレタン塗料組成物(X−1)を得た。
実施例1において、各塗料組成物の配合量を表2〜表7に示すものとする以外は実施例1と同様にして、水性多液型ポリウレタン塗料組成物(X−2)〜(X−26)を得た。
注3)「サンニックスGP−3000」:商品名、三洋化成工業社製、ポリオキシプロピレングリセリルエーテル、数平均分子量3000、水酸基価52.6mgKOH/g、不揮発分100%
注4)「BYK−348」:商品名、ビックケミー・ジャパン社製、ポリエーテル変性シロキサン、重量平均分子量1,500、不揮発分100%
注5)「BYK−015」:商品名、ビックケミー・ジャパン社製、ポリエーテル変性シロキサン、重量平均分子量2,200、不揮発分100%
注6)「TINUVIN 384−2」:商品名、BASF社製、ベンゾトリアゾール系紫外線吸収剤、不揮発分95%、1−メトキシ−2−プロピルアセテート5%、
注7)「TINUVIN 292」:商品名、BASF社製、ヒンダードアミン系光安定剤、不揮発分100%
注8)「SNシックナー621N」:商品名、サンノプコ社製、非イオン性レオロジーコントロール剤、不揮発分30%
注9)pH7.6となる量を滴下:第1液(A)の配合成分を全て配合して23℃で攪拌下しながらpH7.6となるまで滴下
注10)「バイヒジュール XP2655」:商品名、住化コベストロウレタン社製、スルホン酸基を有するヘキサメチレンジイソシアネート系ポリイソシアネート、NCO含量21%、不揮発分100%
注11)「バイヒジュール 304」:商品名、住化コベストロウレタン社製、エチレンオキサイド基を有するヘキサメチレンジイソシアネート系ポリイソシアネート、NCO含量18%、不揮発分100%
注12)「デスモジュール N3900」:商品名、住化コベストロウレタン社製、疎水性ポリイソシアネート、ヘキサメチレンジイソシアネートの環化重合体、NCO含量23.5%、不揮発分100%
注13)亜鉛化合物:「K−KAT XK−614」:商品名、KING INDUSTRIES社製
注14)錫化合物:ジブチル錫ジラウレート
注15)モリブデン化合物:モリブデン化合物(アンモニウム塩):リンモリブデン酸アンモニウム三水和物
上記表2〜7に、後述する評価試験の結果を記載する。本発明においては、全ての性能に優れていることが重要であり、いずれか1つに不合格「D」の評価がある場合は不合格である。
<被塗物>
自動車車体用クリヤー塗料が塗装された塗装板を、#800耐水ペーパーで研磨、脱脂した。これを水平に置いて25℃、相対湿度40%の条件下で市販の水性着色ベース塗料組成物「レタンWBエコベース」(商品名、関西ペイント社製自動車補修用水性メタリックベース塗料)を均一になるように3段階に分けて塗り重ね塗装をして全体膜厚が15μmの着色ベース塗膜を得た。各段階の塗装後は溶媒が揮発して光沢が低くなるまで(具体的には光沢度25程度となるように)エアブローをした。このメタリック色の着色ベース塗膜が形成された板を被塗物(V)とした。
上記被塗物(V)に、実施例及び比較例で得られた塗料組成物を乾燥膜厚が40μmになるようにエアスプレー塗装し、その後室温で水平に20分間静置し、電気熱風乾燥器を用いて60℃で乾燥時間を20分、30分、40分と変動させ、同一塗料サンプルについて60℃の乾燥時間が異なる試験塗板(乾燥性評価用)を複数作製した。次いで試験塗板(乾燥性評価用)それぞれについて、下記磨き補修方法(*)を実施し、その中からペーパーキズ残りや光沢低下のない、良好な塗膜状態の試験塗板(乾燥性評価用)を選定した。評価としては、A、B、Cが合格で、Dが不合格である。
A:乾燥時間20分以上の試験塗板で磨き補修が可能である。
B:乾燥時間30分以上の試験塗板で磨き補修が可能である。
C:乾燥時間40分の試験塗板で磨き補修が可能である。
D:乾燥時間40分の試験塗板で磨き補修が不可能である。
(*磨き補修方法)
各試験塗板(乾燥性評価用)を#2000の耐水研磨紙を用いて水研ぎした後、粗磨き用バフで粗磨き用コンパウンドを使って、60秒間ポリッシングし、耐水研磨紙によるペーパーキズを除去し、さらに、仕上げ用バフで仕上げ用コンパウンドを使って60秒間ポリッシングし、バフ磨きキズの除去を行った。
実施例及び比較例で得られる塗料組成物について、第1液と第2液を手攪拌で混合したサンプル(*1)と、ディスパーで1000rpmにて3分間攪拌したサンプル(*2)を用意した。それぞれ攪拌後15分間静置した後の塗料組成物の外観を目視することで、第1液と第2液の混合性を評価した。評価としては、A、Cが合格で、Dが不合格である。
A:サンプル(*1)、サンプル(*2)ともに均一状態となっており、静置後に分離していない。
C:サンプル(*2)は均一状態となっているが、サンプル(*1)は静置後に一部分離が見られる。
D:サンプル(*1)、サンプル(*2)ともに著しく分離する。
実施例及び比較例で得られた塗料組成物を25℃で静置し、規定時間ごとにフォードカップで粘度を測り、塗装限界の粘度に達する時間をポットライフとした。評価としては、A、B、Cが合格で、Dが不合格である。
A:ポットライフが2時間以上である。
B:ポットライフが1時間以上2時間未満である。
C:ポットライフが30分以上1時間未満である。
D:ポットライフが30分未満である。
上記被塗物(V)に、実施例及び比較例で得られた塗料組成物を乾燥膜厚が40μmになるようにエアスプレー塗装し、その後塗装板を水平に20分間室温で保った後、電気熱風乾燥器を用いて60℃で30分乾燥して室温まで冷却して、水性多液型塗料組成物がトップコートとして塗装された試験塗板(仕上がり性評価用)を作製し、ムラ、チヂミ、ワキ、平滑性、ツヤ感等の塗膜外観を目視観察し、評価した。評価としては、A、B、Cが合格で、Dが不合格である。
A:塗膜の外観が非常に良好である。
B:ムラ、ワキ、チヂミほとんど認められず、平滑性、ツヤ感が良好である。
C:平滑性の低下、ツヤビケがわずかに認められるが、ムラ、ワキ、チヂミはほとんど認められず、実用上問題ないレベルである。
D:ムラ、ワキ、チヂミ、ツヤビケが著しく発生し、明らかに問題がある。
フィッシャースコープ HM2000(FISCHER社)を用いて、上記仕上がり性評価用試験塗板の表面に圧子を押し込み、その際の押し込み深さと押し込み力から得られるマルテンス硬さ値を評価した。
A:マルテンス硬さ値が20N/mm2以上である。
B:マルテンス硬さ値が10N/mm2以上で且つ20N/mm2未満である。
C:マルテンス硬さ値が5N/mm2以上で且つ10N/mm2未満である。
D:マルテンス硬さ値が5N/mm2未満である。
上記仕上がり性評価用試験塗板を40℃の恒温水槽に10日間浸漬し取り出した後、1時間放置後の塗膜の状態を目視で評価した。
A:異常なし。
B:極少量、ツヤビケ・ワレ・ブリスター(又はフクレと呼ばれることがある)の少なくとも1つの異常が若干認められる。
C:部分的に、ツヤビケ・ワレ・ブリスター(又はフクレ)の少なくとも1つの異常が認められる。
D:部分的もしくは塗膜の全面に、ツヤビケ・ワレ・ブリスター(又はフクレ)の少なくとも1つの異常が顕著に認められる。
実施例で作製した第1液及び第2液をそれぞれ40℃で1ヶ月貯蔵し、外観、色味の変化を評価した。
A:分離、ゲル化、変色等が認められず、非常に良好である。
B:分離が少し認められるが、ゲル化、変色等は認められない。
C:分離、ゲル化、変色等が少し認められるが、攪拌すれば問題ないレベルである。
D:分離、ゲル化、変色等が著しく認められ、明らかに問題がある。
Claims (12)
- 水酸基含有樹脂(a1)及び水を含有する第1液(A)、並びに、ポリイソシアネート化合物(b1)を有する第2液(B)を含有する水性多液型ポリウレタン塗料組成物であり、該ポリイソシアネート化合物(b1)が、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)を含有することを特徴とする、水性多液型ポリウレタン塗料組成物。
- 前記水酸基含有樹脂(a1)が、ガラス転移温度40℃以上の水酸基含有アクリル樹脂の水分散体を含有することを特徴とする、請求項1に記載の水性多液型ポリウレタン塗料組成物。
- 前記水酸基含有アクリル樹脂の水分散体が、親水性基含有重合性不飽和モノマーを構成成分の一部として含有する、自己乳化型のアクリル樹脂の水分散体であることを特徴とする、請求項2に記載の水性多液型ポリウレタン塗料組成物。
- 前記水酸基含有アクリル樹脂の水分散体が、主鎖部及び側鎖部からなるグラフト構造を有する水酸基含有アクリル樹脂の水分散体であって、主鎖部及び側鎖部のどちらか一方を構成する重合性不飽和モノマー成分(X)が、エポキシ基含有重合性不飽和モノマー(x1)、水酸基含有重合性不飽和モノマー(x2)及びその他の重合性不飽和モノマー(x3)を含有し、もう一方を構成する重合性不飽和モノマー成分(Y)が、カルボキシル基含有重合性不飽和モノマー(y1)、水酸基含有重合性不飽和モノマー(y2)及びその他の重合性不飽和モノマー(y3)を含有することを特徴とする、請求項2又は3に記載の水性多液型ポリウレタン塗料組成物。
- 前記第1液(A)が、ポリエーテルポリオールを含有することを特徴とする、請求項1から4のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 前記第1液(A)の不揮発分濃度が25〜55質量%の範囲内である、請求項1から5のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 前記第2液(B)において、ポリイソシアネート化合物(b1)が、さらに親水性ポリイソシアネート化合物を含有することを特徴とする、請求項1から6のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 前記第2液(B)において、ポリイソシアネート化合物(b1)内のイソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)の割合が10〜90質量%であることを特徴とする、請求項1から7のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 前記第2液(B)において、イソシアネート基を3個以上有する分子量350以下のポリイソシアネート化合物(b1−1)が脂肪族トリイソシアネート化合物である、請求項1から8のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 前記第2液(B)の不揮発分濃度が20〜100質量%の範囲内である、請求項1から9のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 透明塗料組成物である、請求項1から10のいずれか一項に記載の水性多液型ポリウレタン塗料組成物。
- 被塗物に、請求項1から11のいずれか一項に記載の水性多液型ポリウレタン塗料組成物を塗装する塗装方法。