JP2020066228A - 包装材料 - Google Patents
包装材料 Download PDFInfo
- Publication number
- JP2020066228A JP2020066228A JP2019142513A JP2019142513A JP2020066228A JP 2020066228 A JP2020066228 A JP 2020066228A JP 2019142513 A JP2019142513 A JP 2019142513A JP 2019142513 A JP2019142513 A JP 2019142513A JP 2020066228 A JP2020066228 A JP 2020066228A
- Authority
- JP
- Japan
- Prior art keywords
- film
- packaging material
- layer
- pet
- plastic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本実施の形態による包装材料は、少なくとも、第1延伸プラスチックフィルムと、第2延伸プラスチックフィルムと、シーラント層とをこの順に備えるものである。包装材料は、更に、接着剤層、印刷層、金属蒸着層、透明蒸着層等のその他の層を備えてもよい。
第1延伸プラスチックフィルム11及び第2延伸プラスチックフィルム12はいずれも、所定の方向において延伸されているプラスチックフィルムである。各延伸プラスチックフィルム11,12は、所定の一方向において延伸された一軸延伸フィルムであってもよく、所定の二方向において延伸された二軸延伸フィルムであってもよい。各延伸プラスチックフィルム11,12の延伸方向は特には限定されない。例えば、延伸プラスチックフィルム11,12は、包装材料10によって構成される包装袋の高さ方向において延伸されていてもよく、包装袋の幅方向において延伸されていてもよい。また、各延伸プラスチックフィルム11,12の延伸方向は、互いに同一であってもよく、異なっていてもよい。各延伸プラスチックフィルム11,12の延伸倍率は、例えば1.05倍以上である。
リサイクルフィルムは、メカニカルリサイクルによりリサイクルされたポリエチレンテレフタレート(以下、ポリエチレンテレフタレートをPETとも記す)を含む。具体的には、リサイクルフィルムは、PETボトルをメカニカルリサイクルによりリサイクルしたPETを含み、このPETは、ジオール単位がエチレングリコールであり、ジカルボン酸単位がテレフタル酸およびイソフタル酸を含む。ここで、メカニカルリサイクルとは、一般に、回収されたPETボトル等のポリエチレンテレフタレート樹脂製品を粉砕、アルカリ洗浄してPET樹脂製品の表面の汚れ、異物を除去した後、高温・減圧下で一定時間乾燥してPET樹脂の内部に留まっている汚染物質を拡散させ除染を行い、PET樹脂からなる樹脂製品の汚れを取り除き、再びPET樹脂に戻す方法である。以下、本明細書においては、PETボトルをリサイクルしたポリエチレンテレフタレートを「リサイクルポリエチレンテレフタレート(以下、リサイクルPETとも記す)」といい、リサイクルされていないポリエチレンテレフタレートを「ヴァージンポリエチレンテレフタレート(以下、ヴァージンPETとも記す)」というものとする。
剛性フィルムは、耐突き刺し性などの強さを包装材料10に付与するためのフィルムである。剛性フィルムとしては、下記の(1)〜(3)の延伸プラスチックフィルムのいずれかを用いることができる。
(1)ポリアミドを主成分として含む延伸プラスチックフィルム(以下、ポリアミドフィルムとも称する)
(2)ポリブチレンテレフタレート(以下、PBTとも称する)を主成分として含む延伸プラスチックフィルム(以下、PBTフィルムとも称する)
(3)少なくとも1つの方向において0.0017N以上のループスティフネスを有し、且つポリエステルを主成分として含む延伸プラスチックフィルム(以下、高スティフネスフィルムとも称する)
(1)〜(3)の延伸プラスチックフィルムのいずれかを用いて剛性フィルムを構成することにより、剛性フィルムの突き刺し強度を高くすることができ、例えば10N以上にすることができる。これにより、剛性フィルムを含む包装材料10によって構成された袋に、先端が尖った鋭利な部材が接触した場合にも、袋が破けてしまうことを抑制するための剛性を持たせることができる。
引張強度及び引張伸度は、JIS K7127に準拠して測定され得る。測定器としては、オリエンテック社製の引張試験機 STA−1150を用いることができる。試験片としては、PBTフィルムを幅15mm、長さ150mmの矩形状のフィルムに切り出したものを用いることができる。試験片を保持する一対のチャックの間の、測定開始時の間隔は100mmであり、引張速度は300mm/分である。なお、試験片の長さは、一対のチャックによって試験片を把持することができる限りにおいて、調整可能である。本願において、特に断らない限り、試験の際の環境温度は25℃であり、相対湿度は50%である。
高スティフネスフィルムの突き刺し強度は、好ましくは10N以上であり、より好ましくは11N以上である。
少なくとも1つの方向における高スティフネスフィルムの引張強度は、好ましくは250MPa以上であり、より好ましくは280MPa以上である。例えば、流れ方向における高スティフネスフィルムの引張強度は、好ましくは250MPa以上であり、より好ましくは280MPa以上である。垂直方向における高スティフネスフィルムの引張強度は、好ましくは250MPa以上であり、より好ましくは280MPa以上である。
少なくとも1つの方向における高スティフネスフィルムの引張伸度は、好ましくは130%以下であり、より好ましくは120%以下である。例えば、流れ方向における高スティフネスフィルムの引張伸度は、好ましくは130%以下であり、より好ましくは120%以下である。垂直方向における高スティフネスフィルムの引張伸度は、好ましくは120%以下であり、より好ましくは110%以下である。
好ましくは、少なくとも1つの方向において、高スティフネスフィルムの引張強度を引張伸度で割った値が2.0〔MPa/%〕以上である。例えば、垂直方向(TD)における高スティフネスフィルムの引張強度を引張伸度で割った値は、好ましくは2.0〔MPa/%〕以上であり、より好ましくは2.2〔MPa/%〕以上である。流れ方向(MD)における高スティフネスフィルムの引張強度を引張伸度で割った値は、好ましくは1.8〔MPa/%〕以上であり、より好ましくは2.0〔MPa/%〕以上である。
少なくとも1つの方向における高スティフネスフィルムのヤング率は、好ましくは4.0GPa以上であり、より好ましくは4.5GPa以上である。例えば、流れ方向における高スティフネスフィルムのヤング率は、好ましくは4.0GPa以上であり、より好ましくは4.5GPa以上である。垂直方向における高スティフネスフィルムのヤング率は、好ましくは4.0GPa以上であり、より好ましくは4.5GPa以上である。
なお、包装材料10のヤング率は、測定器としてオリエンテック社製の引張試験機 RTC−1310Aを用いること、試験片を保持する一対のチャックの間の、測定開始時の間隔が50mmであること以外は、高スティフネスポリエステルフィルムの場合と同様に測定される。包装材料10のヤング率を測定する場合は、ループスティフネスの測定の場合と同様に、試験片の長辺方向が流れ方向又は垂直方向に一致するよう包装袋70の表面フィルム74、裏面フィルム75又は下部フィルム76を切断することにより、試験片を作製することができる。
次に、金属蒸着層22について説明する。金属蒸着層22は、従来公知の蒸着方法により形成することができる金属蒸着膜からなる層である。金属蒸着層22を備えることで、包装袋に金属光沢を付与することができるため、意匠性を向上させることができる。また、可視光および紫外線等の透過を阻止する遮光性を、付与ないし向上させることができる。また、酸素ガスおよび水蒸気等の透過を阻止するガスバリア性にも寄与し得る。
次に、透明蒸着層23aについて説明する。透明蒸着層23aは、従来公知の蒸着方法により形成することができる透明な蒸着膜からなる層である。透明蒸着層23aは、酸素ガスおよび水蒸気等の透過を阻止するガスバリア性に寄与し得る。
次に、透明蒸着層23aの面上に設けられるガスバリア性塗布膜23bについて説明する。
シーラント層15は、包装材料10を用いて包装袋を製造する際に、包装袋の内容物側に配置されて、包装材料10どうしをシールする機能を有するものである。シーラント層15は、低密度ポリエチレン、直鎖状低密度ポリエチレンなどのポリエチレンやポリプロピレンなどのポリオレフィン樹脂を含むが、密着性や製造コスト等の観点からは、シーラント層15は、直鎖状低密度ポリエチレンを含むことが好ましい。シーラント層15は、好ましくは無延伸のフィルムからなる。
第1接着剤層16は、第1延伸プラスチックフィルム11を含むフィルムと第2延伸プラスチックフィルム12を含むフィルムのうち積層される側のフィルムの表面に、接着剤を塗布して乾燥させることにより形成される層である。第2接着剤層17は、第2延伸プラスチックフィルム12を含むフィルムとシーラント層15を含むフィルムのうち積層される側のフィルムの表面に、接着剤を塗布して乾燥させることにより形成される層である。第1接着剤層16、第2接着剤層17などの接着剤層を構成する接着剤としては、例えば、1液型あるいは2液型の硬化ないし非硬化タイプのビニル系、(メタ)アクリル系、ポリアミド系、ポリエステル系、ポリエーテル系、ポリウレタン系、エポキシ系、ゴム系、その他などの溶剤型、水性型、あるいは、エマルジョン型などの接着剤を用いることができる。2液硬化型の接着剤としては、ポリオールとイソシアネート化合物との硬化物を用いることができる。上記のラミネート用接着剤のコーティング方法としては、例えば、ダイレクトグラビアロールコート法、グラビアロールコート法、キスコート法、リバースロールコート法、フォンテン法、トランスファーロールコート法、その他の方法で塗布することができる。
印刷層21は、装飾、内容物の表示、賞味期間の表示、製造者、販売者などの表示、その他などの表示や美感の付与のために、文字、数字、絵柄、図形、記号、模様などの所望の任意の印刷模様を形成する層である。印刷層21は、必要に応じて設けることができ、例えば、第1延伸プラスチックフィルム11と第1接着剤層16の間に設けることができる。印刷層21は、第1延伸プラスチックフィルム11の全面に設けてもよく、あるいは一部に設けてもよい。印刷層21は、従来公知の顔料や染料を用いて形成することができ、その形成方法は特に限定されない。
構成例1:ポリアミド/印/第1接/蒸着/リサイクル/第2接/シーラント
構成例2:PBT/印/第1接/蒸着/リサイクル/第2接/シーラント
構成例3:高スティフネス/印/第1接/蒸着/リサイクル/第2接/シーラント
構成例4:ポリアミド/印/第1接/リサイクル/第2接/シーラント
構成例5:PBT/印/第1接/リサイクル/第2接/シーラント
構成例6:高スティフネス/印/第1接/リサイクル/第2接/シーラント
構成例7:リサイクル/印/第1接/ポリアミド/第2接/シーラント
構成例8:リサイクル/印/第1接/PBT/第2接/シーラント
構成例9:リサイクル/印/第1接/高スティフネス/第2接/シーラント
構成例10:リサイクル/透明蒸着/印/第1接/ポリアミド/第2接/シーラント
構成例11:リサイクル/透明蒸着/印/第1接/PBT/第2接/シーラント
構成例12:リサイクル/透明蒸着/印/第1接/高スティフネス/第2接/シーラント
「ポリアミド」は、ポリアミドフィルムを表す。「PBT」は、PBTフィルムを表す。「高スティフネス」は、高スティフネスフィルムを表す。「リサイクル」は、リサイクルフィルムを表す。「印」は、印刷層を表す。「蒸着」は、金属蒸着層又は透明蒸着層を表す。「透明蒸着」は、透明蒸着層を表す。「第1接」は、第1接着剤層を表す。「第2接」は、第2接着剤層を表す。
なお、上記の構成例1〜3において、金属蒸着層又は透明蒸着層は、リサイクルフィルムの面のうちシーラント層側の面に設けられていてもよい。また、透明蒸着層の面上にはガスバリア性塗布膜が設けられていてもよい。
次に、包装材料10の製造方法の一例について説明する。
包装材料10は、包装袋を形成するための材料として用いられる。例えば、包装材料10を折り返すか、又は該包装材料10を2枚用意し、表側の包装材料10のシーラント層15と裏側の包装材料10のシーラント層15とを対向させて重ね合わせ、さらにその周辺端部を、例えば、側面シール型、二方シール型、三方シール型、四方シール型、封筒貼りシール型、合掌貼りシール型(ピローシール型)、ひだ付シール型、平底シール型、角底シール型等のヒートシール形態によりヒートシールして、種々の形態の包装袋を製造することができる。また、表側の包装材料10と裏側の包装材料10との間に、折り返された状態の包装材料10を挿入した状態でヒートシールを行い、ガセット型の包装袋を製造することもできる。なお、包装袋を構成する包装材料の全てが、本発明による包装材料10でなくてもよい。すなわち、包装袋を構成する包装材料の少なくとも一部分が、リサイクルフィルム及び剛性フィルムを備える包装材料10であればよく、包装袋を構成する包装材料のその他の部分が、リサイクルフィルム及び剛性フィルムを備えない包装材料であってもよい。
上述の表面フィルム74及び裏面フィルム75を構成する包装材料10(以下、胴部用の包装材料とも称する)と、上述の下部フィルム76を構成する包装材料10(以下、下部用の包装材料とも称する)とを準備した。続いて、胴部用の包装材料10及び下部用の包装材料10をヒートシールすることにより、図11に示す包装袋70を作製した。
ナイロン15/印/第1接/蒸着/リサイクルPET12/第2接/PE100
「PE」は、上述のポリエチレンフィルムを意味する。数字は、層の厚み(単位はμm)を意味する。
なお、上述の実施の形態で説明したように、第1延伸プラスチックフィルム11の剛性フィルムとして、ナイロンフィルムに代えてPBTフィルム又は高スティフネスフィルムを用いてもよい。二軸延伸された高スティフネスフィルムとしては、90質量%以上のPETを含む高スティフネスPETフィルムが好適に用いられ得る。高スティフネスPETフィルムの厚みは14μm以上であり、例えば16μmである。後述する実施例でも同様である。
ナイロン15/印/第1接/リサイクルPET12/第2接/PE100
なお、上述の実施の形態で説明したように、第1延伸プラスチックフィルム11の剛性フィルムとして、ナイロンフィルムに代えてPBTフィルム又は高スティフネスフィルムを用いてもよい。
実施例1の場合と同様に、胴部用の包装材料10及び下部用の包装材料10をヒートシールすることにより、図11に示す包装袋70を作製した。胴部用の包装材料10としては、実施例1の場合と同一のものを用いた。下部用の包装材料10としては、実施例1において説明したナイロンフィルムによって第2延伸プラスチックフィルム12が構成され、実施例1において説明したリサイクルPETフィルムによって第1延伸プラスチックフィルム11が構成されているものを用いた。
リサイクルPET12/印/第1接/ナイロン15/第2接/PE100
なお、上述の実施の形態で説明したように、第1延伸プラスチックフィルム11の剛性フィルムとして、ナイロンフィルムに代えて、二軸延伸されたPBTフィルム又は、二軸延伸された高スティフネスフィルムを用いてもよい。
実施例1の場合と同様に、胴部用の包装材料10及び下部用の包装材料10をヒートシールすることにより、図11に示す包装袋70を作製した。下部用の包装材料10としては、実施例1の場合と同様に、下記のものを用いた。
ナイロン15/印/第1接/リサイクルPET12/第2接/PE100
また、流れ方向における高スティフネスPETフィルムの引張強度は292MPaであり、垂直方向における高スティフネスPETフィルムの引張強度は257MPaであった。また、流れ方向における高スティフネスPETフィルムの引張伸度は107%であり、垂直方向における高スティフネスPETフィルムの引張伸度は102%であった。この場合、流れ方向における高スティフネスPETフィルムの引張強度を引張伸度で割った値は2.73〔MPa/%〕であり、垂直方向における高スティフネスPETフィルムの引張強度を引張伸度で割った値は2.52〔MPa/%〕である。
また、流れ方向及び垂直方向における高スティフネスPETフィルムの熱収縮率はいずれも0.4%であった。
リサイクルPET12/印/第1接/高PET16/第2接/PE120
「高PET」は、高スティフネスPETフィルムを意味する。
続いて、胴部用の包装材料10の突き刺し強度を、JIS Z1707 7.4に準拠して測定した。測定器としては、A&D製のテンシロン万能材料試験機RTC−1310を用いた。具体的には、図13に示すように、固定されている状態の包装材料10の試験片に対して、外面10y側から、直径1.0mm、先端形状半径0.5mmの半円形の針90を、50mm/分(1分あたり50mm)の速度で突き刺し、針90が包装材料10を貫通するまでの応力の最大値を測定した。5個以上の試験片について、応力の最大値を測定し、その平均値を包装材料10の突き刺し強度とした。測定時の環境は、温度23℃、相対湿度50%とした。結果、突き刺し強度は15.8Nであった。
また、胴部用の包装材料10の流れ方向及び垂直方向における引張特性を評価した。具体的には、包装材料10の流れ方向及び垂直方向におけるヤング率を測定した。包装材料10の引張特性は、JIS K7127に準拠して測定され得る。測定器としては、オリエンテック社製の引張試験機 RTC−1310Aを用いることができる。試験片としては、包装材料を幅15mm、長さ150mmの矩形状のフィルムに切り出したものを用いることができる。試験片を保持する一対のチャックの間の、測定開始時の間隔は50mmであり、引張速度は300mm/分である。測定時の環境は、温度25℃、相対湿度50%とした。結果、流れ方向におけるヤング率は3698MPaであり、垂直方向におけるヤング率は3084MPaであった。
実施例1の場合と同様に、胴部用の包装材料10及び下部用の包装材料10をヒートシールすることにより、図11に示す包装袋70を作製した。下部用の包装材料10としては、実施例1の場合と同様に、下記のものを用いた。
ナイロン15/印/第1接/リサイクルPET12/第2接/PE100
高PET16/印/第1接/リサイクルPET12/第2接/PE120
続いて、実施例3の場合と同様にして、胴部用の包装材料10の突き刺し強度を測定した。結果、突き刺し強度は16.2Nであった。
また、実施例3の場合と同様にして、胴部用の包装材料10の流れ方向及び垂直方向におけるヤング率を測定した。結果、流れ方向におけるヤング率は3728MPaであり、垂直方向におけるヤング率は3104MPaであった。
11 第1延伸プラスチックフィルム
12 第2延伸プラスチックフィルム
15 シーラント層
16 第1接着剤層
17 第2接着剤層
21 印刷層
22 金属蒸着層
23a 透明蒸着層
23b ガスバリア性塗布膜
30 リサイクルフィルム
31 第1層
32 第2層
33 第3層
Claims (10)
- 少なくとも、第1延伸プラスチックフィルムと、第2延伸プラスチックフィルムと、シーラント層とをこの順に備える包装材料であって、
前記第1延伸プラスチックフィルム又は前記第2延伸プラスチックフィルムの一方は、エチレングリコールをジオール単位とし、テレフタル酸とイソフタル酸とをジカルボン酸単位とするポリエチレンテレフタレートを含み、
前記第1延伸プラスチックフィルム又は前記第2延伸プラスチックフィルムの他方は、剛性フィルムを含み、
前記剛性フィルムは、ポリアミドを含むか、又は、ポリブチレンテレフタレートを含むか、又は、1つの方向において0.0017N以上のループスティフネスを有するとともにポリエステルを含む、包装材料。 - 前記第2延伸プラスチックフィルムに設けられた金属蒸着層を更に備える、請求項1に記載の包装材料。
- 前記第1延伸プラスチックフィルム又は前記第2延伸プラスチックフィルムに設けられた透明蒸着層を更に備える、請求項1に記載の包装材料。
- 前記シーラント層は、直鎖状低密度ポリエチレンを含む、請求項1乃至3のいずれか一項に記載の包装材料。
- 前記シーラント層は、50μm以上の厚みを有する、請求項1乃至4のいずれか一項に記載の包装材料。
- 前記剛性フィルムは、ポリアミドを含む、請求項1乃至5のいずれか一項に記載の包装材料。
- 前記剛性フィルムは、ポリブチレンテレフタレートを含む、請求項1乃至5のいずれか一項に記載の包装材料。
- 前記剛性フィルムは、1つの方向において0.0017N以上のループスティフネスを有するとともにポリエステルを含む、請求項1乃至5のいずれか一項に記載の包装材料。
- 前記ポリエチレンテレフタレートの極限粘度は、0.58dl/g以上0.80dl/g以下である、請求項1乃至8のいずれか一項に記載の包装材料。
- 一方向における前記包装材料のヤング率が3200MPa以上である、請求項1乃至9のいずれか一項に記載の包装材料。