JP2019521075A - ガラスシートの厚さにかかわらずニュートラル性に近づくガラスシート - Google Patents
ガラスシートの厚さにかかわらずニュートラル性に近づくガラスシート Download PDFInfo
- Publication number
- JP2019521075A JP2019521075A JP2019502644A JP2019502644A JP2019521075A JP 2019521075 A JP2019521075 A JP 2019521075A JP 2019502644 A JP2019502644 A JP 2019502644A JP 2019502644 A JP2019502644 A JP 2019502644A JP 2019521075 A JP2019521075 A JP 2019521075A
- Authority
- JP
- Japan
- Prior art keywords
- glass sheet
- glass
- weight
- ppm
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
a)それらの主面を通して見るとき、それは、厚さ4mmについて裸眼に対して無色である。
b)厚さ4mmのシートのエッジを通して見るとき、それは、緑色がかった〜黄色がかった色合いを有する。
c)それらの主面を通して見るとき、それは、例えば、非常に大きい厚さ(すなわち30mm)において可視的な緑色がかった〜黄色がかった色合いを有する。
より正確には、本発明の1つの目的は、(その主面を通して、またはそのエッジを通して、または拡散コーティングを支持する領域を通して見るときに)前記ガラスシートを統合する物体を見る人に利用可能な目視経路を問わず本質的に同じである前記シートの演色を得ることを可能にする組成物を有する低鉄ガラスシートを提供することである。
として定義される。
として定義され、a*x,b*x座標は、厚さxmmのガラスについて決定される。
として定義される。
SiO2 40〜78重量%
Al2O3 0〜18重量%
B2O3 0〜18重量%
Na2O 0〜20重量%
CaO 0〜15重量%
MgO 0〜10重量%
K2O 0〜10重量%
BaO 0〜5重量%。
SiO2 60〜78重量%
Al2O3 0〜8重量%
B2O3 0〜4重量%
CaO 0〜15重量%
MgO 0〜10重量%
Na2O 5〜20重量%
K2O 0〜10重量%
BaO 0〜5重量%。
SiO2 60〜78重量%
Al2O3 0〜6重量%
B2O3 0〜1重量%
CaO 5〜15重量%
MgO 0〜8重量%
Na2O 10〜20重量%
K2O 0〜10重量%
BaO 0〜1重量%。
65≦SiO2≦78重量%
5≦Na2O≦20重量%
0≦K2O<5重量%
1≦Al2O3<6重量%
0≦CaO<4.5重量%
4≦MgO≦12重量%
(MgO/(MgO+CaO))≧0.5。
65≦SiO2≦78%
5≦Na2O≦20%
0≦K2O<5%
3<Al2O3≦5%
0<CaO<4.5%
4≦MgO≦12%;
0.88≦[MgO/(MgO+CaO)]<1。
60≦SiO2≦78%
5≦Na2O≦20%
0.9<K2O≦12%
4.9≦Al2O3≦8%
0.4<CaO<2%
4<MgO≦12%。
65≦SiO2≦78重量%
5≦Na2O≦20重量%
1≦K2O<8重量%
1≦Al2O3<6重量%
2≦CaO<10重量%
0≦MgO≦8重量%
K2O/(K2O+Na2O):0.1〜0.7。
本発明の包括的概念を説明するために、異なる厚さについてのガラス色のいくつかのシミュレーション、従来技術からのガラス(典型的なソーラー低鉄ガラスシートおよび公知のニュートラル化低鉄ガラスシート)および本発明によるガラスのシミュレーションを実施した。ガラス中の様々な着色剤の吸収係数から、異なる厚さで一定の光学スペクトルを得ることができる。そこで、ガラスの厚さによる色の変化を得ることができる。
本発明または比較例による異なるガラスシートが、3組の実施例として実験室においてもしくは工業的に作製されるかまたは計算/シミュレートされた。
− 2°の立体視角を使用して(D65光源)および380〜780nmの波長範囲について視感透過率LTDをISO9050標準に従って測定した。
− CIE L*a*b*パラメーターは、以下のパラメーター:D65光源、10°を使用して透過において測定された。
EX1.x実施例(比較例)は、異なる厚さを有する典型的な透明ガラスシート(全鉄含有量約0.1重量%)に対応する。
EX3実施例は、従来技術の典型的な低鉄ガラスの全鉄の量に近い全鉄の量(約0.015重量%)を含み、本発明の実施形態に従ってエルビウムが添加された、厚さ2mmを有する本発明によるガラスシートに対応する。
本発明に従って低いN*5と一緒にセレンおよびコバルトを使用することにより、ガラスの厚さを問わず著しく一定の色に達することを可能にする方法が以下に示される。
本発明に従って低いN*5と一緒にクロムおよびマンガンを使用することにより、ガラスの厚さを問わず著しく一定の色に達することを可能にする方法が以下に示される。
Claims (13)
- N*5≦0.03を有することを特徴とする、請求項1に記載のガラスシート。
- N*5≦0.01を有することを特徴とする、請求項2に記載のガラスシート。
- − 前記組成物は、エルビウム(Er2O3の形態で表わされる)を以下の通り:0.003〜0.5重量%含むか、または
− 前記組成物は、セレン(Seとして表わされる)を以下の通り:3〜50ppmおよびコバルト(Coとして表わされる)を以下の通り:0.1〜15ppm含むか、または
− 前記組成物は、クロム(Cr2O3として表わされる)を以下の通り:3〜75ppmおよびマンガン(MnOとして表わされる)を以下の通り:50〜1000ppm含むことを特徴とする、請求項1〜3のいずれか一項に記載のガラスシート。 - 前記組成物は、エルビウム(Er2O3の形態で表わされる)を以下の通り:0.003〜0.5重量%含むことを特徴とする、請求項4に記載のガラスシート。
- 前記組成物は、Er2O3≦0.1重量%を含むことを特徴とする、請求項5に記載のガラスシート。
- 前記組成物は、Er2O3≧0.01重量%を含むことを特徴とする、請求項5または6に記載のガラスシート。
- 前記組成物は、セレン(Seとして表わされる)を以下の通り:3〜50ppmおよびコバルト(Coとして表わされる)を以下の通り:0.1〜15ppm含むことを特徴とする、請求項4に記載のガラスシート。
- 前記組成物は、クロム(Cr2O3として表わされる)を以下の通り:3〜75ppmおよびマンガン(MnOとして表わされる)を以下の通り:50〜1000ppm含むことを特徴とする、請求項4に記載のガラスシート。
- 前記組成物は、Coを以下の通り:0.25〜20ppm含むことを特徴とする、請求項9に記載のガラスシート。
- 前記組成物は、全鉄0.002〜0.02重量%を含むことを特徴とする、請求項1〜10のいずれか一項に記載のガラスシート。
- 前記組成物は、全鉄0.002〜0.015重量%を含むことを特徴とする、請求項11に記載のガラスシート。
- 前記組成物は、レドックス比≦32%を有することを特徴とする、請求項1〜12のいずれか一項に記載のガラスシート。