JP2019517617A - ポリマー組成物、その製造方法、その使用、及び前記ポリマー組成物を含む組成物 - Google Patents
ポリマー組成物、その製造方法、その使用、及び前記ポリマー組成物を含む組成物 Download PDFInfo
- Publication number
- JP2019517617A JP2019517617A JP2018563541A JP2018563541A JP2019517617A JP 2019517617 A JP2019517617 A JP 2019517617A JP 2018563541 A JP2018563541 A JP 2018563541A JP 2018563541 A JP2018563541 A JP 2018563541A JP 2019517617 A JP2019517617 A JP 2019517617A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polymer
- composition
- composition according
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計で100重量%になるポリマー組成物P1は、熱可塑性ポリマーの耐衝撃性を向上させるとともに、なおも許容可能な融解時間を有し、高速加工の冷却の間に、より良好に熱を消失させることが判明した。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1の製造方法であって、
2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程
を含むことを特徴とする製造方法は、
熱可塑性ポリマーの耐衝撃性を向上させるとともに、なおも許容可能な融解時間を有し、高速加工の冷却の間に、より良好に熱を消失させることが判明した。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1の製造方法であって、
i)2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程、
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする製造方法は、
熱可塑性ポリマーの耐衝撃性を向上させるとともに、なおも許容可能な融解時間を有し、高速加工の冷却の間に、より良好に熱を消失させることが判明した。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1は、熱可塑性ポリマーの耐衝撃性及びコーナー溶着強度を向上させるために使用することができることが判明した。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計して100重量%になることを特徴とする、ポリマー組成物P1に関する。
a)29重量%から60重量%までの無機コンパウンド(F)、
前記無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1であり、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計して100重量%になることを特徴とする、ポリマー組成物P1に関する。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1の製造方法であって、
2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程
を含むことを特徴とする製造方法に関する。
a)29重量%から60重量%までの無機コンパウンド(F)、
前記無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1であり、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法に関し、本方法は、
2種の成分a)及びb)をブレンドする工程であって、成分b)、及び無機充填材(F1)が、ブレンド工程の間に水相における分散体の形態である工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法に関し、本方法は、
i)2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程、
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
前記無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1であり、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法に関し、本方法は、
i)成分a)及びb)をブレンドする工程であって、成分b)、及び無機充填材(F1)が、ブレンド工程の間に水相における分散体の形態である、工程
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1を含む、ポリマー組成物P2の製造方法に関し、ポリマー組成物P2は、
d)熱可塑性ポリマーTP1
も含み、
本方法は、
組成物P1と熱可塑性ポリマーTP1とをブレンドする工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計で100重量%になるポリマー組成物P1の使用であって、ポリマー組成物P1を含む熱可塑性ポリマーTP1のコーナー溶着強度を向上させるための、使用に関する。
本発明のポリマー組成物P1は、少なくとも2種の成分:a)29重量%から60重量%までの無機コンパウンド(F)、b)40重量%から71重量%までのポリマーの耐衝撃性改良剤を含む。
本発明のポリマー粉末は、体積メジアン粒径D50が、1μm〜500μmである。ポリマー粉末の体積メジアン粒径は好ましくは、10μm〜450μmであり、より好ましくは15μm〜400μm、有利には20μm〜350μmである。
無機コンパウンド(F)は、無機充填材若しくは鉱物系充填材(F1)であるか、又は無機充填材若しくは鉱物系充填材(F1)と流動化助剤(F2)の双方を含む。
鉱物系充填材(F1)については、ガラス繊維、中空ガラスマイクロビーズ、無機化合物、例えば鉱物及び塩を挙げることができ、これには炭酸カルシウム(CaCO3)、シリカ、ケイ酸塩、例えばケイ酸カルシウム若しくはメタケイ酸カルシウム、粘土、例えばベントナイト、マイカ、タルク、アルミナ三水和物、水酸化マグネシウム、金属酸化物、又はこれら2種以上の組み合わせが含まれる。
鉱物系充填材のスラリーは、好ましくは5〜90重量%、有利には50〜80重量%の固形分を有する鉱物系充填材の水性分散体である。この水性分散体は、任意の特定の界面活性剤、分散剤、スラリーの品質(安定性、粘度、又はホストポリマーマトリックスとの相溶性)を有利に改善可能な添加剤又は充填材表面処理剤を含むことができる。
流動化助剤(F2)は、無機粉末である。
ポリマーの耐衝撃性改良剤(IM1)は好ましくは、多段構造を有するポリマー粒子である。
熱可塑性ポリマーTP1は、ハロゲン含有ポリマーから選択され、それは例えば、ポリビニルクロリド、ポリアミド、ポリメチルメタクリレート、ポリスチレン、ポリカーボネート、ポリエステル、例えばポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリシクロヘキサンジメタノールテレフタレート、及びポリオレフィンである。
ハロゲン含有ポリマーについては、例えば以下のものが挙げられる:
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法は、
2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法は、
i)2種の成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%は、ブレンド工程の間に水相における分散体の形態である工程、
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
前記無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1であり、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法は、
2種の成分a)及びb)をブレンドする工程であって、2種の成分b)及び(F1)が、ブレンド工程の間に水相における分散体の形態である工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
前記無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1であり、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になる、ポリマー組成物P1の製造方法は、
i)2種の成分a)及びb)をブレンドする工程であって、2種の成分b)及び(F1)が、ブレンド工程の間に水相における分散体の形態である工程
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする。
本方法はさらに、先の工程で得られたブレンドを回収して、ポリマー粉末を形成するか、又は先の工程で得られたブレンドをポリマー粉末として回収する工程を含むことができる。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1を含む、ポリマー組成物P2の製造方法に関し、ポリマー組成物P2は、
d)熱可塑性ポリマーTP1
も含み、
本方法は、
組成物P1を、熱可塑性ポリマーTP1とブレンドする工程
を含むことを特徴とする。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計で100重量%になるポリマー組成物P1の使用であって、熱可塑性ポリマーTP1の耐衝撃性を向上させるとともに、高速加工の冷却の間に熱を消失させるための使用に関する。
a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1の使用であって、ポリマー組成物P1及び熱可塑性ポリマーTP1を含むポリマー組成物P2のコーナー溶着強度を向上させるための使用に関する。
ガラス転移温度
ポリマー又はポリマー混合物のガラス転移温度(Tg)は、熱機械分析が可能な装置によって測定する。Rheometrics Company社製のRDAII “RHEOMETRICS DYNAMIC ANALYSER”を使用した。熱機械分析によって、温度との関数で試料の粘弾性変化、適用されるひずみ又は変形が、正確に測定される。使用する周波数は、1Hzである。この装置は、ひずみを一定に保ちながら、温度変化について制御されたプログラムの間、試料の変形を連続的に記録する。
その結果は、温度との関数で、弾性モジュール(G’)、弾性モジュール損失、及びtanδを描くことによって得られる。Tgは、tanδから導かれる値がゼロに等しい場合、tanδの曲線で読み取られる温度の値よりも高い。
(IM1)の分散体及び鉱物系充填材(F1)のスラリーを、次の比率:分散体9.11kg(9110部)、及びスラリー0.705kg(705部)で混合し、ラテックス分散体単独について従来使用される条件で噴霧乾燥させる。得られた粉末は、粒径が約150μmである。炭酸カルシウム(PCC、0.07ミクロン)3重量%を、回収された粉末に流動性助剤(F2)として添加する。こうして生成する粉末は、アクリル系耐衝撃性改良剤(IM1)/無機コンパウンド(F)CaCO3の比率が、85/15である。
(IM1)の分散体及び鉱物系充填材(F1)のスラリーを、次の比率:分散体2.679kg(2679部)、及びスラリー3.968kg(3968部)で混合し、ラテックス分散体単独について従来使用される条件で噴霧乾燥させる。得られた粉末は、粒径が約150μmである。炭酸カルシウム(PCC、0.07ミクロン)5重量%を、回収された粉末に流動性助剤(F2)として添加する。こうして生成する粉末は、耐衝撃性改良剤(IM1)/無機コンパウンド(F)CaCO3の比率が、25/75である。
2種のアクリル系分散体と無機スラリーとを次の比率:耐衝撃性改良剤分散体(IM1a)5.305kg(5305部)、加工助剤の(メタ)アクリルコポリマー(A1a)0.617kg(617部)、及び無機鉱物系充填材(F1)のスラリー2.469kg(2469部)で混合し、分散体単独について従来使用される条件で噴霧乾燥する。得られた粉末は、粒径が約150μmである。炭酸カルシウム(PCC、0.07ミクロン)3重量%を、回収された粉末に流動性助剤(F2)として添加する。こうして生成する粉末は、ポリマー/無機コンパウンドCaCO3の比率が、55/45である。
(IM1)の分散体及び鉱物系充填材(F1)のスラリーを、次の比率:分散体7.902kg(7902部)、及びスラリー1.587kg(1587部)で混合し、ラテックス分散体単独について従来使用される条件で噴霧乾燥させる。得られた粉末は、粒径が約150μmである。炭酸カルシウム(PCC、0.07ミクロン)3重量%を、回収された粉末に流動性助剤(F2)として添加する。こうして生成する粉末は、耐衝撃性改良剤(IM1)/無機コンパウンド(F)CaCO3の比率が、70/30である。
Claims (27)
- a)29重量%から60重量%までの無機鉱物系コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、
2種の成分a)及びb)が合計して100重量%になることを特徴とする、ポリマー組成物P1。 - 無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1である、請求項1に記載の組成物。
- a)29重量%〜60重量%の無機コンパウンド(F)、
b)40重量%〜71重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項1又は2に記載の組成物。 - a)31重量%〜59重量%の無機コンパウンド(F)、
b)41重量%〜69重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項1又は2に記載の組成物。 - a)33重量%〜58重量%の無機コンパウンド(F)、
b)42重量%〜67重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項1又は2に記載の組成物。 - a)40重量%〜55重量%の無機コンパウンド(F)、
b)45重量%〜60重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項1又は2に記載の組成物。 - a)42重量%〜47重量%の無機コンパウンド(F)、
b)53重量%〜58重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項1又は2に記載の組成物。 - 1μm〜500μmの体積メジアン粒径D50を有する粉末形態である、請求項1から7のいずれか一項に記載の組成物。
- 粉末粒子がそれぞれ、a)のコンパウンド及びb)を含む、請求項8に記載の組成物。
- より多量のポリマー組成物P1から採取した0.1重量%の少量の試料が、2種の各成分a)及びb)の重量比について、組成物P1全体に対して30%未満の差異を有する、請求項1から8までのいずれか一項に記載の組成物。
- ポリマーの耐衝撃性改良剤(IM1)が、多層構造を有するポリマー粒子であり、前記多層構造は、0℃未満のガラス転移温度を有するポリマー(L1)を含む少なくとも1つの層(IM1L1)と、45℃超のガラス転移温度を有するポリマー(L2)を含む少なくとも別の層(IM1L2)とを含む、請求項1から10のいずれか一項に記載の組成物。
- 多段ポリマーにおける層(IM1L1)/層(IM1L2)の重量比が、重量で好ましくは70/30〜99/1、より好ましくは80/20〜98/2、さらにより好ましくは85/15〜97/3、有利には89/11〜96/4の範囲にある、請求項11に記載の組成物。
- 多段ポリマーにおける層(IM1L1)/層(IM1L2)の重量比が、少なくとも86/14、より有利には87/13、より有利には88/12、最も有利には89/11である、請求項11に記載の組成物。
- 多段ポリマーにおける層(IM1L1)/層(IM1L2)の重量比が、重量で86/14〜97/3、より有利には87/13〜97/2、さらにより有利には88/11〜96/4の範囲にある、請求項11に記載の組成物。
- ポリマーL1が、ポリマーの耐衝撃性改良剤(IM1)の85重量%より多く存在する、請求項11に記載の組成物。
- ポリマーL1が、ポリマーの耐衝撃性改良剤(IM1)の86重量%より多く存在する、請求項11に記載の組成物。
- 0℃未満のガラス転移温度を有するポリマー(L1)が、アルキルアクリレートからのモノマーを少なくとも50重量%含む(メタ)アクリルポリマーである、請求項8から10のいずれか一項に記載の組成物。
- 無機鉱物系充填材(F)の少なくとも一部が、炭酸カルシウム、か焼された粘土、シリカ(フュームドシリカ若しくは沈降シリカ)、粘土、モンモリロナイト(ナノクレイ)、ゼオライト又はパーライト、二酸化チタンから選択される鉱物系充填材である、請求項1から11のいずれか一項に記載の組成物。
- 無機鉱物系充填材(F)又はその混合物が、炭酸カルシウムから選択される、請求項1から12のいずれか一項に記載の組成物。
- a)29重量%から60重量%までの無機コンパウンド(F)、
b)40重量%から71重量%までのポリマーの耐衝撃性改良剤(IM1)
を含み、2種の成分a)及びb)が合計して100重量%になるポリマー組成物P1の製造方法において、
成分a)及びb)をブレンドする工程であって、成分b)、及びコンパウンドa)の少なくとも83.33重量%が、ブレンド工程の間に水相における分散体の形態である、工程
を含むことを特徴とする、製造方法。 - ポリマー組成物P1が、
a)31重量%〜59重量%の無機コンパウンド(F)、
b)41重量%〜69重量%のポリマーの耐衝撃性改良剤(IM1)
を含む、請求項14に記載の方法。 - 無機コンパウンド(F)が、無機充填材(F1)及び流動化助剤(F2)から成り、(F1)/(F2)の重量比が少なくとも5/1である、請求項14又は15に記載の方法。
- i)2種の成分a)及びb)をブレンドする工程であって、2種の成分が、ブレンド工程の間に水相における分散体の形態である、工程、
ii)工程i)で得られたブレンドを乾燥させる工程
を含むことを特徴とする、請求項14から16までのいずれか一項に記載の方法。 - 請求項1から13のいずれか一項に記載の、又は請求項14から17のいずれか一項に記載の方法によって得られる、ポリマー組成物P1を含むポリマー組成物P2の製造方法であって、
ポリマー組成物P2が、
d)熱可塑性ポリマーTP1
も含み、
組成物P1と熱可塑性ポリマーTP1とをブレンドする工程
を含むことを特徴とする、製造方法。 - 熱可塑性ポリマーTP1のコーナー溶着強度を向上させるための、請求項1から13のいずれか一項に記載の、又は請求項14から17のいずれか一項に記載の方法によって得られる組成物の使用。
- ポリマー組成物P1及び熱可塑性ポリマーTP1を含むポリマー組成物P2を加工するための、請求項1から13のいずれか一項に記載の、又は請求項14から17のいずれか一項に記載の方法によって得られる組成物の使用。
- 異形材、管、サイディング、発泡体、フィルム、シート、床材用のフィルム又はシートであることを特徴とする、請求項18に記載の加工されたポリマー組成物P2を含む物品。