JP2019179611A - 電池用非水電解液及びリチウム二次電池 - Google Patents
電池用非水電解液及びリチウム二次電池 Download PDFInfo
- Publication number
- JP2019179611A JP2019179611A JP2018066703A JP2018066703A JP2019179611A JP 2019179611 A JP2019179611 A JP 2019179611A JP 2018066703 A JP2018066703 A JP 2018066703A JP 2018066703 A JP2018066703 A JP 2018066703A JP 2019179611 A JP2019179611 A JP 2019179611A
- Authority
- JP
- Japan
- Prior art keywords
- battery
- carbonate
- mass
- group
- lithium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
従って、本開示の課題は、保存後の電池抵抗を低減でき、かつ、保存時の開放電圧の低下を抑制できる電池用非水電解液、並びに、この電池用非水電解液を用いたリチウム二次電池を提供することである。
<1> 電解質と、
非水溶媒と、
下記式(A)で表される化合物である添加剤Aと、
下記式(B)で表される化合物である添加剤Bと、
を含有する電池用非水電解液。
前記添加剤Bの含有量が、電池用非水電解液の全量に対し、0.001質量%〜10質量%である<1>に記載の電池用非水電解液。
<3> 前記非水溶媒が、環状カーボネート化合物と、前記式(A)で表される化合物以外の鎖状カーボネート化合物と、を含む<1>又は<2>に記載の電池用非水電解液。
<4> 前記非水溶媒中に占める、前記環状カーボネート化合物と前記式(A)で表される化合物以外の鎖状カーボネート化合物との合計の割合が、80質量%以上である<3>に記載の電池用非水電解液。
<5> 電池用非水電解液中に占める前記非水溶媒の割合が、60質量%以上である<1>〜<4>のいずれか1つに記載の電池用非水電解液。
金属リチウム、リチウム含有合金、リチウムとの合金化が可能な金属若しくは合金、リチウムイオンのドープ・脱ドープが可能な酸化物、リチウムイオンのドープ・脱ドープが可能な遷移金属窒素化物、及び、リチウムイオンのドープ・脱ドープが可能な炭素材料からなる群から選ばれる少なくとも1種を負極活物質として含む負極と、
<1>〜<5>のいずれか1つに記載の電池用非水電解液と、
を含むリチウム二次電池。
<7> <6>に記載のリチウム二次電池を充放電させて得られたリチウム二次電池。
本明細書において、組成物中の各成分の量は、組成物中に各成分に該当する物質が複数存在する場合は、特に断らない限り、組成物中に存在する当該複数の物質の合計量を意味する。
本開示の電池用非水電解液(以下、単に「非水電解液」ともいう)は、下記式(A)で表される化合物である添加剤Aと、式(B)で表される化合物である添加剤Bと、
を含有する。
かかる効果が奏される理由は明らかではないが、電池の保存前において添加剤Aと添加剤Bとの組み合わせによって電極上に被膜が形成され、かつ、電池の保存時において上記被膜の劣化が少ないためと考えられる。
添加剤Aは、下記式(A)で表される化合物である。
添加剤Aは、下記式(A)で表される化合物に該当する1種のみの化合物であってもよいし、下記式(A)で表される化合物に該当する2種以上の化合物であってもよい。
フルオロメチル基、ジフルオロメチル基、トリフルオロメチル基、2,2,2−トリフルオロエチル基、1,1,2,2−テトラフルオロエチル基、パーフルオロエチル基、2,2,3,3−テトラフルオロプロピル基、パーフルオロプロピル基、パーフルオロブチル基、パーフルオロペンチル基、パーフルオロヘキシル基、パーフルオロイソプロピル基、パーフルオロイソブチル基等のフルオロアルキル基;
2−フルオロエテニル基、2,2−ジフルオロエテニル基、2−フルオロ−2−プロペニル基、3,3−ジフルオロ−2−プロペニル基、2,3−ジフルオロ−2−プロペニル基、3,3−ジフルオロ−2−メチル−2−プロペニル基、3−フルオロ−2−ブテニル基、パーフルオロビニル基、パーフルオロプロペニル基、パーフルオロブテニル基等のフルオロアルケニル基;
等が挙げられる。
Ra1で表される炭素数1〜6のフッ化炭化水素基としては、炭素数1〜6のフルオロアルキル基が好ましく、炭素数1〜3のフルオロアルキル基がより好ましく、フルオロメチル基、ジフルオロメチル基、トリフルオロメチル基、2,2,2−トリフルオロエチル基、1,1,2,2−テトラフルオロエチル基、パーフルオロエチル基、2,2,3,3−テトラフルオロプロピル基、又はパーフルオロプロピル基が更に好ましく、2,2,2−トリフルオロエチル基が特に好ましい。
メチル基、エチル基、n−プロピル基、イソプロピル基、1−エチルプロピル基、n−ブチル基、イソブチル基、sec−ブチル基、tert−ブチル基、2−メチルブチル基、3,3−ジメチルブチル基、n−ペンチル基、イソペンチル基、ネオペンチル基、1−メチルペンチル基、n−ヘキシル基、イソヘキシル基、sec−ヘキシル基、tert−ヘキシル基等のアルキル基;
ビニル基、1−プロペニル基、アリル基、1−ブテニル基、2−ブテニル基、3−ブテニル基、ペンテニル基、ヘキセニル基、イソプロペニル基、2−メチル−2−プロペニル基、1−メチル−2−プロペニル基、2−メチル−1−プロペニル基等のアルケニル基;
等が挙げられる。
Ra2で表される炭素数1〜6の炭化水素基としては、炭素数1〜6のアルキル基が好ましく、炭素数1〜3のアルキル基がより好ましく、メチル基又はエチル基が更に好ましく、メチル基が特に好ましい。
2,2,2−トリフルオロエチルメチルカーボネート、ビス(2,2,2−トリフルオロエチル)カーボネート、パーフルオロエチルメチルカーボネート、又はビス(パーフルオロエチル)カーボネートが好ましく、
2,2,2−トリフルオロエチルメチルカーボネート(以下、「MFEC」と称することがある)が特に好ましい。
添加剤Bは、下記式(B)で表される化合物である。
添加剤Bは、下記式(B)で表される化合物に該当する1種のみの化合物であってもよいし、下記式(B)で表される化合物に該当する2種以上の化合物であってもよい。
式(B)中、Rb1〜Rb9で表される炭素数1〜6のフッ化炭化水素基は、それぞれ、式(A)中のRa1で表される炭素数1〜6のフッ化炭化水素基と同義であり、好ましい態様も同様である。
トリス(トリメチルシリル)ホスフェート、トリス(トリエチルシリル)ホスフェート、トリス(トリプロピルシリル)ホスフェート、トリス(トリビニルシリル)ホスフェート、又はトリス(トリフルオロメチルシリル)ホスフェートが好ましく、
トリス(トリメチルシリル)ホスフェート(以下、「TMSP」と称することがある)が特に好ましい。
本開示の非水電解液は、更に、下記式(C)で表される化合物である添加剤Cを含有してもよい。
これらのうちでビニレンカーボネート(式(C)中、Rc1及びRc2がいずれも水素原子である化合物)が特に好ましい。
非水電解液は、非水溶媒と電解質とを含有する。
非水電解液は、非水溶媒を含有する。
非水電解液に含有される非水溶媒は、1種のみであってもよいし、2種以上であってもよい。
非水溶媒としては、種々公知のものを適宜選択することができる。
非水溶媒としては、例えば、特開2017−45723号公報の段落0069〜0087に記載の非水溶媒を用いることができる。
この場合、非水溶媒に含まれる環状カーボネート化合物及び特定鎖状カーボネート化合物は、それぞれ、1種のみであってもよいし2種以上であってもよい。
これらのうち、誘電率が高い、エチレンカーボネート及びプロピレンカーボネートが好適である。黒鉛を含む負極活物質を使用した電池の場合は、非水溶媒は、エチレンカーボネートを含むことがより好ましい。
この場合、非水溶媒に含まれるその他の化合物は、1種のみであってもよいし、2種以上であってもよい。
その他の化合物としては、環状カルボン酸エステル化合物(例えばγブチロラクトン)、環状スルホン化合物、環状エーテル化合物、鎖状カルボン酸エステル化合物、鎖状エーテル化合物、鎖状リン酸エステル化合物、アミド化合物、鎖状カーバメート化合物、環状アミド化合物、環状ウレア化合物、ホウ素化合物、ポリエチレングリコール誘導体、等が挙げられる。
これらの化合物については、特開2017−45723号公報の段落0069〜0087の記載を適宜参照できる。
非水溶媒中に占める、環状カーボネート化合物及び特定鎖状カーボネート化合物の割合は、100質量%であってもよい。
非水電解液中に占める非水溶媒の割合の上限は、他の成分(添加剤A、添加剤B、電解質、等)の含有量にもよるが、上限は、例えば99質量%であり、好ましくは97質量%であり、更に好ましくは90質量%である。
本開示の非水電解液は、電解質を含有する。
電解質としては、通常、非水電解液用電解質として使用されているものであれば、いずれをも使用することができる。
これらのうち、特にリチウム塩が望ましく、さらには、LiPF6、LiBF4、LiOSO2CkF(2k+1)(k=1〜8の整数)、LiClO4、LiAsF6、LiNSO2[CkF(2k+1)]2(k=1〜8の整数)、LiPFn[CkF(2k+1)](6−n)(n=1〜5、k=1〜8の整数)が好ましい。
具体例としては、LiPF6とLiBF4、LiPF6とLiN[SO2CkF(2k+1)]2(k=1〜8の整数)、LiPF6とLiBF4とLiN[SO2CkF(2k+1)](k=1〜8の整数)などが例示される。
本開示のリチウム二次電池は、正極と、負極と、本開示の非水電解液と、を含む。
負極は、負極活物質及び負極集電体を含んでもよい。
負極における負極活物質としては、金属リチウム、リチウム含有合金、リチウムとの合金化が可能な金属もしくは合金、リチウムイオンのドープ・脱ドープが可能な酸化物、リチウムイオンのドープ・脱ドープが可能な遷移金属窒素化物、及び、リチウムイオンのドープ・脱ドープが可能な炭素材料からなる群から選ばれた少なくとも1種(単独で用いてもよいし、これらの2種以上を含む混合物を用いてもよい)を用いることができる。
リチウム(又はリチウムイオン)との合金化が可能な金属もしくは合金としては、シリコン、シリコン合金、スズ、スズ合金などを挙げることができる。また、チタン酸リチウムでもよい。
これらの中でもリチウムイオンをドープ・脱ドープすることが可能な炭素材料が好ましい。このような炭素材料としては、カーボンブラック、活性炭、黒鉛材料(人造黒鉛、天然黒鉛)、非晶質炭素材料、等が挙げられる。上記炭素材料の形態は、繊維状、球状、ポテト状、フレーク状いずれの形態であってもよい。
上記黒鉛材料としては、天然黒鉛、人造黒鉛が挙げられる。人造黒鉛としては、黒鉛化MCMB、黒鉛化MCFなどが用いられる。また、黒鉛材料としては、ホウ素を含有するものなども用いることができる。また、黒鉛材料としては、金、白金、銀、銅、スズなどの金属で被覆したもの、非晶質炭素で被覆したもの、非晶質炭素と黒鉛を混合したものも使用することができる。
上記炭素材料としては、特にX線解析で測定した(002)面の面間隔d(002)が0.340nm以下の炭素材料が好ましい。また、炭素材料としては、真密度が1.70g/cm3以上である黒鉛又はそれに近い性質を有する高結晶性炭素材料も好ましい。以上のような炭素材料を使用すると、電池のエネルギー密度をより高くすることができる。
負極集電体の具体例としては、銅、ニッケル、ステンレス鋼、ニッケルメッキ鋼等の金属材料が挙げられる。中でも、加工しやすさの点から特に銅が好ましい。
正極は、正極活物質及び正極集電体を含んでもよい。
正極における正極活物質としては、MoS2、TiS2、MnO2、V2O5などの遷移金属酸化物又は遷移金属硫化物、LiCoO2、LiMnO2、LiMn2O4、LiNiO2、LiNiXCo(1−X)O2〔0<X<1〕、α−NaFeO2型結晶構造を有するLi1+αMe1−αO2(Meは、Mn、Ni及びCoを含む遷移金属元素、1.0≦(1+α)/(1−α)≦1.6)、LiNixCoyMnzO2〔x+y+z=1、0<x<1、0<y<1、0<z<1〕(例えば、LiNi0.33Co0.33Mn0.33O2、LiNi0.5Co0.2Mn0.3O2等)、LiFePO4、LiMnPO4などのリチウムと遷移金属とからなる複合酸化物、ポリアニリン、ポリチオフェン、ポリピロール、ポリアセチレン、ポリアセン、ジメルカプトチアジアゾール、ポリアニリン複合体などの導電性高分子材料等が挙げられる。これらの中でも、特にリチウムと遷移金属とからなる複合酸化物が好ましい。負極がリチウム金属又はリチウム合金である場合は、正極として炭素材料を用いることもできる。また、正極として、リチウムと遷移金属との複合酸化物と、炭素材料と、の混合物を用いることもできる。
正極活物質は、1種類で使用してもよく、2種類以上を混合して使用してもよい。正極活物質は導電性が不充分である場合には、導電性助剤とともに使用して正極を構成することができる。導電性助剤としては、カーボンブラック、アモルファスウィスカー、グラファイトなどの炭素材料を例示することができる。
正極集電体の具体例としては、例えば、アルミニウム、アルミニウム合金、ステンレス鋼、ニッケル、チタン、タンタルなどの金属材料;カーボンクロス、カーボンペーパーなどの炭素材料;等が挙げられる。
本開示のリチウム二次電池は、負極と正極との間にセパレータを含むことが好ましい。
セパレータは、正極と負極とを電気的に絶縁し且つリチウムイオンを透過する膜であって、多孔性膜や高分子電解質が例示される。
多孔性膜としては微多孔性高分子フィルムが好適に使用され、材質としてポリオレフィン、ポリイミド、ポリフッ化ビニリデン、ポリエステル等が例示される。
特に、多孔性ポリオレフィンが好ましく、具体的には多孔性ポリエチレンフィルム、多孔性ポリプロピレンフィルム、又は多孔性のポリエチレンフィルムとポリプロピレンフィルムとの多層フィルムを例示することができる。多孔性ポリオレフィンフィルム上には、熱安定性に優れる他の樹脂がコーティングされてもよい。
高分子電解質としては、リチウム塩を溶解した高分子や、電解液で膨潤させた高分子等が挙げられる。
本開示の非水電解液は、高分子を膨潤させて高分子電解質を得る目的で使用してもよい。
本開示のリチウム二次電池は、種々公知の形状をとることができ、円筒型、コイン型、角型、ラミネート型、フィルム型その他任意の形状に形成することができる。しかし、電池の基本構造は、形状によらず同じであり、目的に応じて設計変更を施すことができる。
図1は、本開示のリチウム二次電池の一例であるラミネート型電池の一例を示す概略斜視図であり、図2は、図1に示すラミネート型電池に収容される積層型電極体の厚さ方向の概略断面図である。
図1に示すラミネート型電池は、内部に非水電解液(図1中では不図示)及び積層型電極体(図1中では不図示)が収納され、且つ、周縁部が封止されることにより内部が密閉されたラミネート外装体1を備える。ラミネート外装体1としては、例えばアルミニウム製のラミネート外装体が用いられる。
ラミネート外装体1に収容される積層型電極体は、図2に示されるように、正極板5と負極板6とがセパレータ7を介して交互に積層されてなる積層体と、この積層体の周囲を囲むセパレータ8と、を備える。正極板5、負極板6、セパレータ7、及びセパレータ8には、本開示の非水電解液が含浸されている。
上記積層型電極体における複数の正極板5は、いずれも正極タブを介して正極端子2と電気的に接続されており(不図示)、この正極端子2の一部が上記ラミネート外装体1の周端部から外側に突出している(図1)。ラミネート外装体1の周端部において正極端子2が突出する部分は、絶縁シール4によってシールされている。
同様に、上記積層型電極体における複数の負極板6は、いずれも負極タブを介して負極端子3と電気的に接続されており(不図示)、この負極端子3の一部が上記ラミネート外装体1の周端部から外側に突出している(図1)。ラミネート外装体1の周端部において負極端子3が突出する部分は、絶縁シール4によってシールされている。
なお、上記一例に係るラミネート型電池では、正極板5の数が5枚、負極板6の数が6枚となっており、正極板5と負極板6とがセパレータ7を介し、両側の最外層がいずれも負極板6となる配置で積層されている。しかし、ラミネート型電池における、正極板の数、負極板の数、及び配置については、この一例には限定されず、種々の変更がなされてもよいことは言うまでもない。
図3は、本開示のリチウム二次電池の別の一例であるコイン型電池の一例を示す概略斜視図である。
図3に示すコイン型電池では、円盤状負極12、非水電解液を注入したセパレータ15、円盤状正極11、必要に応じて、ステンレス、又はアルミニウムなどのスペーサー板17、18が、この順序に積層された状態で、正極缶13(以下、「電池缶」ともいう)と封口板14(以下、「電池缶蓋」ともいう)との間に収納される。正極缶13と封口板14とはガスケット16を介してかしめ密封する。
この一例では、セパレータ15に注入される非水電解液として、本開示の非水電解液を用いる。
即ち、本開示のリチウム二次電池は、まず、負極と、正極と、上記本開示の非水電解液と、を含む充放電前のリチウム二次電池を作製し、次いで、この充放電前のリチウム二次電池を1回以上充放電させることによって作製されたリチウム二次電池(充放電されたリチウム二次電池)であってもよい。
以下の実施例において、「添加量」は、最終的に得られる非水電解液中における含有量(即ち、最終的に得られる非水電解液全量に対する量)を意味する。
また、「wt%」は、質量%を意味する。
以下の手順にて、リチウム二次電池であるコイン型電池(試験用電池)を作製した。
<負極の作製>
アモルファスコート天然黒鉛(97質量部)、カルボキシメチルセルロース(1質量部)及びSBRラテックス(2質量部)を水溶媒で混練してペースト状の負極合剤スラリーを調製した。
次に、この負極合剤スラリーを厚さ10μmの帯状銅箔製の負極集電体に塗布し乾燥した後に、ロールプレスで圧縮して負極集電体と負極活物質層からなるシート状の負極を得た。このときの負極活物質層の塗布密度は10mg/cm2であり、充填密度は1.5g/mlであった。
LiNi0.5Co0.2Mn0.3O2(90質量部)、アセチレンブラック(5質量部)及びポリフッ化ビニリデン(5質量部)を、N−メチルピロリジノンを溶媒として混練してペースト状の正極合剤スラリーを調製した。
次に、この正極合剤スラリーを厚さ20μmの帯状アルミ箔の正極集電体に塗布し乾燥した後に、ロールプレスで圧縮して正極集電体と正極活物質層とからなるシート状の正極を得た。このときの正極活物質層の塗布密度は30mg/cm2であり、充填密度は2.5g/mlであった。
非水溶媒として、エチレンカーボネート(EC)とジメチルカーボネート(DMC)とメチルエチルカーボネート(EMC)とをそれぞれ30:30:40(質量比)の割合で混合し、混合溶媒を得た。
得られた混合溶媒中に、電解質としてのLiPF6を、最終的に得られる非水電解液中におけるLiPF6の濃度が1.0mol/Lとなるように溶解させた。
上記で得られた溶液に対して、
添加剤Aである2,2,2−トリフルオロエチルメチルカーボネート(MFEC)(添加量10質量%)、及び
添加剤Bであるトリス(トリメチルシリル)ホスフェート(TMSP)(添加量0.5質量%)
を添加し、非水電解液を得た。
得られた非水電解液中に占める非水溶媒(即ち、上述した、EC、DMC及びEMCの混合溶媒)の割合は、79.5質量%である。
上述の負極を直径14mmで、上述の正極を直径13mmで、それぞれ円盤状に打ち抜き、コイン状の負極及びコイン状の正極をそれぞれ得た。また、厚さ20μmの微多孔性ポリエチレンフィルムを直径17mmの円盤状に打ち抜き、セパレータを得た。
得られたコイン状の負極、セパレータ、及びコイン状の正極を、この順序でステンレス製の電池缶(2032サイズ)内に積層し、次いで、この電池缶内に、上述の非水電解液20μLを注入し、セパレータと正極と負極とに含漬させた。
次に、正極上にアルミニウム製の板(厚さ1.2mm、直径16mm)及びバネを乗せ、ポリプロピレン製のガスケットを介して、電池缶蓋をかしめることにより電池を密封した。
以上により、直径20mm、高さ3.2mmの図3で示す構成を有するコイン型電池(即ち、コイン型のリチウム二次電池)を得た。
得られたコイン型電池に対し、コンディショニングを施し、コンディショニング後のコイン型電池について、電池抵抗の評価を行った。
ここで、「コンディショニング」とは、コイン型電池を、恒温槽内で25℃にて、2.75Vと4.2Vとの間で充放電を三回繰り返すことを指す。
以下、「高温保存」とは、コイン型電池を、恒温槽内で、80℃で48時間保存する操作を意味する。
以下、電池抵抗(DCIR)は、25℃及び−20℃の2つの温度条件の各々にて測定した。
コンディショニング後のコイン型電池のSOC(State of Charge)を80%に調整し、次いで、以下の方法により、コイン型電池の高温保存前のDCIR(Direct current internal resistance;直流抵抗)を測定した。
上述のSOC80%に調整されたコイン型電池を用い、放電レート0.2CでのCC10s放電、300秒間の休止、放電レート1CでのCC10s放電、300秒間の休止、放電レート2CでのCC10s放電、300秒間の休止、及び、放電レート5CでのCC10s放電をこの順に行った。
なお、CC10s放電とは、定電流(Constant Current)にて10秒間放電することを意味する。
各放電レートと、各放電レートでの放電開始後10秒目の電圧と、の関係に基づき直流抵抗を求め、得られた直流抵抗(Ω)を、コイン型電池の高温保存前の電池抵抗(Ω)とした。
結果を表1(「保存前」欄)に示す。
コンディショニング後であってSOCを80%に調整する前のコイン型電池に対し、恒温槽内で25℃にて充電レート0.2Cで4.25VまでCC−CV充電し、次いで高温保存を施す操作を追加したこと以外は前述の高温保存前の電池抵抗の測定と同様にして、高温保存後の電池抵抗(Ω)を測定した。
結果を表1(「保存後」欄)に示す。
ここで、CC−CV充電とは、定電流定電圧(Constant Current - Constant Voltage)を意味する。
コンディショニング後のコイン型電池を恒温槽内で25℃にて充電レート0.2Cで4.25VまでCC−CV充電し、次いで、25℃にて、放電レート0.2Cにて、高温保存後の放電容量(0.2C)(mAh)を測定した。
結果を表1(「保存前」欄)に示す。
上記で得られたコイン型電池に対し、コンディショニングを施した。
コンディショニング後のコイン型電池を恒温槽内で25℃にて充電レート0.2Cで4.25VまでCC−CV充電した後、高温保存した。
高温保存後のコイン型電池について、25℃で、放電レート0.2CにてCC放電させて高温保存後の放電容量(残存容量;0.2C)を測定した。
結果を表1(「残存」欄)に示す。
上記で得られたコイン型電池に上記のコンディショニングを施した。
コンディショニング後のコイン型電池を恒温槽内で25℃にて充電レート0.2Cで4.25VまでCC−CV充電した後、コイン型電池を高温保存した。
高温保存後のコイン型電池を、恒温槽内で25℃にて、SOCが0%となるまで放電レート0.2CでCC放電させ、次いで充電レート0.2Cで4.2VまでCC−CV充電し、次いで放電レート0.2CにてCC放電させて高温保存後の放電容量(回復容量;0.2C)を測定した。
結果を表1(「回復」欄)に示す。
上記で得られたコイン型電池に上記のコンディショニングを施した。
コンディショニング後のコイン型電池を恒温槽内で25℃にて充電レート0.2Cで4.25VまでCC−CV充電した後、コイン型電池を高温保存した。
高温保存後のコイン型電池について、25℃にて、コイン型電池の開放電圧(Open Circuit Voltage;OCV)[V]を測定し、下式によりOCV低下(mV)を計算した。
結果を表1に示す。
OCV低下(mV)=4250(mV)−高温保存後の開放電圧(mV)
非水電解液の調製において、添加剤Aを用いず、かつ、添加剤Bの添加量0.5質量%が維持されるように、添加剤Bの量を調整したこと以外は実施例1と同様の操作を行った。
結果を表1に示す。
非水電解液の調製において、添加剤Bを用いず、かつ、添加剤Aの添加量10質量%が維持されるように、添加剤Aの量を調整したこと以外は実施例1と同様の操作を行った。
結果を表1に示す。
実施例1は、比較例1及び2と比較して、電池容量も同等であった。
2 正極端子
3 負極端子
4 絶縁シール
5 正極板
6 負極板
7、8 セパレータ
11 正極
12 負極
13 正極缶
14 封口板
15 セパレータ
16 ガスケット
17、18 スペーサー板
Claims (7)
- 電解質と、
非水溶媒と、
下記式(A)で表される化合物である添加剤Aと、
下記式(B)で表される化合物である添加剤Bと、
を含有する電池用非水電解液。
〔式(A)中、Ra1は、炭素数1〜6のフッ化炭化水素基を表し、Ra2は、炭素数1〜6の炭化水素基又は炭素数1〜6のフッ化炭化水素基を表す。〕
〔式(B)中、Rb1〜Rb9は、それぞれ独立に、炭素数1〜6の炭化水素基又は炭素数1〜6のフッ化炭化水素基を表す。 - 前記添加剤Aの含有量が、電池用非水電解液の全量に対し、0.001質量%〜30質量%であり、
前記添加剤Bの含有量が、電池用非水電解液の全量に対し、0.001質量%〜10質量%である請求項1に記載の電池用非水電解液。 - 前記非水溶媒が、環状カーボネート化合物と、前記式(A)で表される化合物以外の鎖状カーボネート化合物と、を含む請求項1又は請求項2に記載の電池用非水電解液。
- 前記非水溶媒中に占める、前記環状カーボネート化合物と前記式(A)で表される化合物以外の鎖状カーボネート化合物との合計の割合が、80質量%以上である請求項3に記載の電池用非水電解液。
- 電池用非水電解液中に占める前記非水溶媒の割合が、60質量%以上である請求項1〜請求項4のいずれか1項に記載の電池用非水電解液。
- 正極と、
金属リチウム、リチウム含有合金、リチウムとの合金化が可能な金属若しくは合金、リチウムイオンのドープ・脱ドープが可能な酸化物、リチウムイオンのドープ・脱ドープが可能な遷移金属窒素化物、及び、リチウムイオンのドープ・脱ドープが可能な炭素材料からなる群から選ばれる少なくとも1種を負極活物質として含む負極と、
請求項1〜請求項5のいずれか1項に記載の電池用非水電解液と、
を含むリチウム二次電池。 - 請求項6に記載のリチウム二次電池を充放電させて得られたリチウム二次電池。