JP2019143286A - アクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法 - Google Patents
アクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法 Download PDFInfo
- Publication number
- JP2019143286A JP2019143286A JP2019028383A JP2019028383A JP2019143286A JP 2019143286 A JP2019143286 A JP 2019143286A JP 2019028383 A JP2019028383 A JP 2019028383A JP 2019028383 A JP2019028383 A JP 2019028383A JP 2019143286 A JP2019143286 A JP 2019143286A
- Authority
- JP
- Japan
- Prior art keywords
- dyeing
- fiber
- acrylonitrile
- dye
- crosslinked acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)アクリロニトリル系繊維および架橋アクリレート系繊維を含むアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法であって、酸およびカチオン染料が添加されたpH3.5未満の浴で染色する工程と、アニオン性基を有する染料が添加された浴で染色する工程とを個別に、または、同時に施すことを特徴とするアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
(2)アニオン性基を有する染料で染色する工程をpH4.0未満で行うことを特徴とする(1)に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
(3)アニオン性基を有する染料が酸性染料であることを特徴とする(1)または(2)に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
(4)酸性染料が、ミリング酸性染料、ハーフミリング酸性染料および金属錯塩酸性染料からなる群から選択される1種以上であることを特徴とする(3)に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
(5)酸が、有機酸であることを特徴とする(1)〜(4)のいずれかに記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
染色した布帛の色相を、色彩色差計CR−300(MINOLTA社製)を用いて、L*、a*、b*値を測定し、後述するアクリロニトリル系繊維のみからなる染色布帛A(参考例1)を基準としたときの色差を下記式により算出した。
色差={(試料のL*−基準のL*)2+(試料のa*−基準のa*)2+(試料のb*−基準のb*)2}0.5
また、下記の評価基準による視感での評価を行った。
○ : 同等の色相で、実用上問題とならない
△ : 色相が少し異なるため、実用上問題となる可能性がある
× : 色相が大きく異なるため、実用上利用し難い
なお、色差の数値と人の感覚的な捉え方の対応関係については、素材や用途によって様々な基準が設けられているが、色差が3程度までは一般には同じ色だと思われるレベルとされている基準が多い。
アクリロニトリル(AN)88%、酢酸ビニル11.5%、メタスルホン酸ナトリウム0.5%からなるアクリロニトリル系重合体10部を48%ロダンソーダ水溶液90部に溶解した紡糸原液を、常法に従って紡糸、延伸(全延伸倍率:10倍)した後、乾球/湿球=120℃/60℃の雰囲気下で乾燥、湿熱処理してアクリロニトリル系繊維を得た。
上述のアクリロニトリル系繊維を原料繊維とし、該原料繊維に、水加ヒドラジン0.5重量%および水酸化ナトリウム1.4重量%を含有する水溶液中で、100℃×2時間、架橋導入処理および加水分解処理を同時に行い、8重量%硝酸水溶液で、120℃×3時間処理し、水洗した。得られた繊維を水に浸漬し、水酸化ナトリウムを添加してpH9に調整し、水洗、乾燥することにより架橋アクリレート系繊維を得た。
上述の製造方法により得られたアクリロニトリル系繊維と架橋アクリレート系繊維を70:30の割合で混紡し、メートル番手1/52の紡績糸を作成し、該紡績糸を用いて編地を作製し、サンプル布帛とした。
上述するアクリロニトリル系繊維の製造方法によって得られたアクリロニトリル繊維を用い、メートル番手1/52の紡績糸を作成し、該紡績糸を用いて編地を作製しサンプル布帛とした。該サンプル布帛の重量に対して2.5%のカチオン染料Nichilon Black G 200%(日成化成社製)が入った浴に、酢酸を投入し、pHを3.3に調整した。続いて、該浴に、サンプル布帛を投入し、浴比を1:50、100℃で30分間浸漬してカチオン染料による染色を行い、さらに、ソーピング、水洗、乾燥を行うことで、染色布帛Aを得た。該染色布帛Aの染色性評価結果を表1に示す。
上述のサンプル布帛の製造方法によって得られたサンプル布帛中の架橋アクリレート系繊維重量に対して、2.5重量%の金属錯塩酸性染料Isolan Black 2S−LD(Dyster社製)が入った浴に、クエン酸を投入し、pH3.0に調整した。続いて、該浴にサンプル布帛を投入し、浴比を1:50、100℃で30分間浸漬して金属錯塩酸性染料によるサンプル布帛の染色を行った。次に、サンプル布帛中のアクリロニトリル系繊維重量に対して2.5%のカチオン染料Nichilon Black G 200%(日成化成社製)が入った浴に、酢酸を投入し、pHを3.0に調整した。続いて、該浴に、前述する金属錯塩酸性染料で染色したサンプル布帛を投入し、浴比を1:50、100℃で30分間浸漬してカチオン染料による染色を行い、さらに、ソーピング、水洗、乾燥を行うことで、染色布帛Bを得た。該染色布帛Bの染色性評価結果を表1に示す。
実施例1において、カチオン染料による染色時にクエン酸を投入してpHを2.6としたこと以外は同様に処理を行い、染色布帛Cを得た。該染色布帛Cの染色性評価結果を表1に示す。
実施例1において、カチオン染料による染色時のpHを3.4としてこと以外は同様に処理を行い、染色布帛Dを得た。該染色布帛Dの染色性評価結果を表1に示す。
実施例1において、カチオン染料での染色工程と、金属錯塩酸性染料での染色工程とを逆の順序で行ったこと以外は同様に処理を行い、染色布帛Eを得た。該染色布帛Eの染色性評価結果を表1に示す。
実施例1において、カチオン染料による染色時のpHを3.5としたこと以外は同様に処理を行い、染色布帛Fを得た。該染色布帛Fの染色性評価結果を表1に示す。
実施例1において、カチオン染料による染色時のpHを3.6としたこと以外は同様に処理を行い、染色布帛Gを得た。該染色布帛Gの染色性評価結果を表1に示す。
実施例1において、カチオン染料による染色時のpHを3.7としたこと以外は同様に処理を行い、染色布帛Hを得た。該染色布帛Hの染色性評価結果を表1に示す。
Claims (5)
- アクリロニトリル系繊維および架橋アクリレート系繊維を含むアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法であって、酸およびカチオン染料が添加されたpH3.5未満の浴で染色する工程と、アニオン性基を有する染料が添加された浴で染色する工程とを個別に、又は、同時に施すことを特徴とするアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
- アニオン性基を有する染料で染色する工程をpH4.0未満で行うことを特徴とする請求項1に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
- アニオン性基を有する染料が酸性染料であることを特徴とする請求項1または2に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
- 酸性染料が、ミリング酸性染料、ハーフミリング酸性染料および金属錯塩酸性染料からなる群から選択される1種以上であることを特徴とする請求項3に記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。
- 酸が、有機酸であることを特徴とする請求項1〜4のいずれかに記載のアクリロニトリル/架橋アクリレート系含有繊維構造体の染色方法。