JP2019019300A - Polycarbonate resin composition - Google Patents

Abstract

To provide a polycarbonate resin composition capable of blocking ultraviolet light as well as light in a wavelength of 400 to 420 nm closer to the visible light, while causing no problem of gas generation at the time of molding.SOLUTION: The polycarbonate resin composition contains, with respect to 100 parts by weight of polycarbonate resin (A), 0.02 to 1 part by weight of an ultraviolet absorber (B1) which has 375 nm or more of a maximum absorption wavelength of an absorption curve obtained in conformity with JIS K7105, or 0.01 to 0.5 part by weight of a stabilizer (C).SELECTED DRAWING: None

Description

  The present invention relates to a polycarbonate resin composition, and more particularly to a polycarbonate resin composition that can cut light having a wavelength of 400 to 420 nm on the visible light side of ultraviolet light and that does not have a problem of gas generation during molding.

The eyes are always exposed to damage from sunlight, and it is important to protect the eyes from ultraviolet light up to a wavelength of 400 nm. Further, recent studies have revealed that the wavelength band from the ultraviolet light to the visible light side can also damage the eye tissue and cause pathogenesis such as cataracts. Furthermore, it has been reported that blue light, which is abundantly contained in LED light sources, causes eye diseases as devices and illuminations using LEDs as light sources are widespread.
For this reason, in addition to ultraviolet light, a material capable of cutting light having a wavelength of 400 to 420 nm on the visible light side is demanded.

In general, polycarbonate resin is excellent in mechanical properties, weather resistance, and transparency. Polycarbonate resin composition containing UV absorber is used as transparent UV-absorbing material for glasses, sunglasses, goggles, various lighting covers, etc. It is used. And as a ultraviolet absorber, ultraviolet absorbers, such as a benzophenone series, a benzotriazole series, a triazine series, and a salicylate series, are utilized (for example, patent documents 1-2).
However, a polycarbonate resin composition that can actually effectively absorb and block wavelengths of 400 to 420 nm is not known.
Further, when trying to cut light of 420 nm wavelength with the conventional ultraviolet absorber as described above, there is a problem that the blending amount increases and gas generation during molding increases.

  Thus, a resin composition comprising an ultraviolet absorber and a polycarbonate resin is known, but a polycarbonate resin composition that can effectively absorb and block wavelengths of 400 to 420 nm and has no problem of gas generation during molding is known. The current situation is that it is not.

JP 09-291205 A Japanese Patent Publication No. 06-51840

  The present invention has been made in view of the above circumstances, and its object (problem) is to cut light having a wavelength of 400 to 420 nm on the visible light side in addition to ultraviolet light, and to generate gas during molding. An object of the present invention is to provide a polycarbonate resin composition that does not have this problem.

As a result of intensive studies in order to achieve the above-mentioned problems, the present inventor blended a specific amount of an ultraviolet absorber having a specific maximum absorption wavelength and a phosphorus-based stabilizer, whereby a wavelength of 400 to 420 nm. The inventors have found that a polycarbonate resin composition capable of cutting light and having no problem of gas generation during molding can be obtained, and the present invention has been completed.
The present invention relates to the following polycarbonate resin composition.

[1] 0.02 to 1 part by mass of an ultraviolet absorber (B1) having a maximum absorption wavelength of 375 nm or more based on JIS K7105 based on the following formula with respect to 100 parts by mass of the polycarbonate resin (A), And a stabilizer (C) in an amount of 0.01 to 0.5 parts by mass, a polycarbonate resin composition.
[Absorbance of polycarbonate resin containing 0.005% by mass of UV absorber]-[Absorbance of polycarbonate resin alone]
[2] The polycarbonate resin composition according to the above [1], wherein the ultraviolet absorber (B1) is a benzotriazole-based ultraviolet absorber having a sesamol group.
[3] The polycarbonate resin composition according to the above [1] or [2], wherein the ultraviolet absorber (B1) is an ultraviolet absorber represented by the following general formula (1).
(In the formula, X represents a halogen atom.)

[4] Further, a benzotriazole-based ultraviolet absorber (B2) having a sesamol group having a maximum absorption wavelength of 360 nm or more and less than 375 nm in accordance with JIS K7105, obtained from the above formula, 100 parts by mass of a polycarbonate resin (A) The polycarbonate resin composition according to any one of [1] to [3], which is contained in an amount of 0.01 parts by mass or more and less than 0.08 parts by mass.
[5] Furthermore, 0.01 to 0.2 parts by mass of an ultraviolet absorber (B2) having a maximum absorption wavelength determined from the above formula in accordance with JIS K7105 of less than 360 nm with respect to 100 parts by mass of the polycarbonate resin (A). The polycarbonate resin composition according to any one of the above [1] to [4].
[6] The ultraviolet absorber (B2) is at least one selected from a benzotriazole-based ultraviolet absorber having no sesamol group, a triazine-based ultraviolet absorber, a malonic ester-based ultraviolet absorber, and a benzoxazine-based ultraviolet absorber. The polycarbonate resin composition according to [5] above.
[7] The polycarbonate resin composition according to any one of [1] to [6], wherein a transmittance of a molded product having a thickness of 2 mm measured at a wavelength of 420 nm is 25% or less in accordance with JIS K7105.
[8] A molded article of the polycarbonate resin composition according to any one of [1] to [7].

  The polycarbonate resin composition of the present invention can cut light having a wavelength of 400 to 420 nm on the visible light side in addition to ultraviolet light, and there is no problem of gas generation during molding.

It is a top view of the drop mold used for evaluation of mold contamination in an example.

Hereinafter, the present invention will be described in detail with reference to embodiments and examples.
In the present specification, “to” is used in the sense of including the numerical values described before and after the lower and upper limits unless otherwise specified.

The polycarbonate resin composition of the present invention has an ultraviolet absorber (B1) having an absorption curve having a maximum absorption wavelength of 375 nm or more obtained from the following formula in accordance with JIS K7105, based on 100 parts by mass of the polycarbonate resin (A). It is characterized by containing 02 to 1 part by mass and 0.01 to 0.5 part by mass of the stabilizer (C).
[Absorbance of polycarbonate resin containing 0.005% by mass of UV absorber]-[Absorbance of polycarbonate resin alone]

  Hereafter, each component etc. which comprise the polycarbonate resin composition of this invention are demonstrated in detail.

[Polycarbonate resin (A)]
The polycarbonate resin is a polymer having a basic structure having a carbonic acid bond represented by the formula: — [— O—X—O—C (═O) —] —. In the formula, X is generally a hydrocarbon, but for imparting various properties, X into which a hetero atom or a hetero bond is introduced may be used.

  The polycarbonate resin can be classified into an aromatic polycarbonate resin in which carbon directly bonded to a carbonic acid bond is aromatic carbon and an aliphatic polycarbonate resin in which aliphatic carbon is aliphatic carbon, either of which can be used. Of these, aromatic polycarbonate resins are preferred from the viewpoints of heat resistance, mechanical properties, electrical characteristics, and the like.

  Although there is no restriction | limiting in the specific kind of polycarbonate resin, For example, the polycarbonate polymer formed by making a dihydroxy compound and a carbonate precursor react is mentioned. At this time, in addition to the dihydroxy compound and the carbonate precursor, a polyhydroxy compound or the like may be reacted. Further, a method of reacting carbon dioxide with a cyclic ether using a carbonate precursor may be used. The polycarbonate polymer may be linear or branched. Further, the polycarbonate polymer may be a homopolymer composed of one type of repeating unit or a copolymer having two or more types of repeating units. At this time, the copolymer can be selected from various copolymerization forms such as a random copolymer and a block copolymer. In general, such a polycarbonate polymer is a thermoplastic resin.

Among monomers used as raw materials for aromatic polycarbonate resins, examples of aromatic dihydroxy compounds include:
Dihydroxybenzenes such as 1,2-dihydroxybenzene, 1,3-dihydroxybenzene (ie, resorcinol), 1,4-dihydroxybenzene;
Dihydroxybiphenyls such as 2,5-dihydroxybiphenyl, 2,2′-dihydroxybiphenyl, 4,4′-dihydroxybiphenyl;

2,2′-dihydroxy-1,1′-binaphthyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, , 7-dihydroxynaphthalene, dihydroxynaphthalene such as 2,7-dihydroxynaphthalene;

2,2′-dihydroxydiphenyl ether, 3,3′-dihydroxydiphenyl ether, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dimethyldiphenyl ether, 1,4-bis (3-hydroxyphenoxy) Dihydroxy diaryl ethers such as benzene and 1,3-bis (4-hydroxyphenoxy) benzene;

2,2-bis (4-hydroxyphenyl) propane (ie, bisphenol A),
1,1-bis (4-hydroxyphenyl) propane,
2,2-bis (3-methyl-4-hydroxyphenyl) propane,
2,2-bis (3-methoxy-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-methoxy-4-hydroxyphenyl) propane,
1,1-bis (3-tert-butyl-4-hydroxyphenyl) propane,
2,2-bis (3,5-dimethyl-4-hydroxyphenyl) propane,
2,2-bis (3-cyclohexyl-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-cyclohexyl-4-hydroxyphenyl) propane,
α, α′-bis (4-hydroxyphenyl) -1,4-diisopropylbenzene,
1,3-bis [2- (4-hydroxyphenyl) -2-propyl] benzene,
Bis (4-hydroxyphenyl) methane,
Bis (4-hydroxyphenyl) cyclohexylmethane,
Bis (4-hydroxyphenyl) phenylmethane,
Bis (4-hydroxyphenyl) (4-propenylphenyl) methane,
Bis (4-hydroxyphenyl) diphenylmethane,
Bis (4-hydroxyphenyl) naphthylmethane,
1,1-bis (4-hydroxyphenyl) ethane,
1,1-bis (4-hydroxyphenyl) -1-phenylethane,
1,1-bis (4-hydroxyphenyl) -1-naphthylethane,
1,1-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) pentane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
1,1-bis (4-hydroxyphenyl) octane,
2,2-bis (4-hydroxyphenyl) octane,
4,4-bis (4-hydroxyphenyl) heptane,
2,2-bis (4-hydroxyphenyl) nonane,
1,1-bis (4-hydroxyphenyl) decane,
1,1-bis (4-hydroxyphenyl) dodecane,
Bis (hydroxyaryl) alkanes such as;

1,1-bis (4-hydroxyphenyl) cyclopentane,
1,1-bis (4-hydroxyphenyl) cyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,4-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,5-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxy-3,5-dimethylphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-propyl-5-methylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -4-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-phenylcyclohexane,
1,1-bis (4-hydroxyphenyl) -4-phenylcyclohexane,
Bis (hydroxyaryl) cycloalkanes such as;

9,9-bis (4-hydroxyphenyl) fluorene,
Cardio structure-containing bisphenols such as 9,9-bis (4-hydroxy-3-methylphenyl) fluorene;

4,4′-dihydroxydiphenyl sulfide,
Dihydroxydiaryl sulfides such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide;

Dihydroxydiaryl sulfoxides such as 4,4'-dihydroxydiphenyl sulfoxide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide;

4,4′-dihydroxydiphenyl sulfone,
Dihydroxydiaryl sulfones such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone;
Etc.

Among these, bis (hydroxyaryl) alkanes are preferable, and bis (4-hydroxyphenyl) alkanes are particularly preferable, and 2,2-bis (4-hydroxyphenyl) propane (especially from the viewpoint of impact resistance and heat resistance). That is, bisphenol A) is preferred.
In addition, 1 type may be used for an aromatic dihydroxy compound and it may use 2 or more types together by arbitrary combinations and a ratio.

In addition, when an example of a monomer that is a raw material of the aliphatic polycarbonate resin is given,
Ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, 2,2-dimethylpropane-1,3-diol, 2-methyl-2-propylpropane-1,3- Alkanediols such as diol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, decane-1,10-diol;

  Cyclopentane-1,2-diol, cyclohexane-1,2-diol, cyclohexane-1,4-diol, 1,4-cyclohexanedimethanol, 4- (2-hydroxyethyl) cyclohexanol, 2,2,4, Cycloalkanediols such as 4-tetramethyl-cyclobutane-1,3-diol;

  Glycols such as ethylene glycol, 2,2'-oxydiethanol (ie, diethylene glycol), triethylene glycol, propylene glycol, spiro glycol and the like;

  1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 1,4-benzenediethanol, 1,3-bis (2-hydroxyethoxy) benzene, 1,4-bis ( 2-hydroxyethoxy) benzene, 2,3-bis (hydroxymethyl) naphthalene, 1,6-bis (hydroxyethoxy) naphthalene, 4,4′-biphenyldimethanol, 4,4′-biphenyldiethanol, 1,4- Aralkyl diols such as bis (2-hydroxyethoxy) biphenyl, bisphenol A bis (2-hydroxyethyl) ether, bisphenol S bis (2-hydroxyethyl) ether;

  1,2-epoxyethane (ie ethylene oxide), 1,2-epoxypropane (ie propylene oxide), 1,2-epoxycyclopentane, 1,2-epoxycyclohexane, 1,4-epoxycyclohexane, 1-methyl And cyclic ethers such as -1,2-epoxycyclohexane, 2,3-epoxynorbornane, and 1,3-epoxypropane;

  Among the monomers used as the raw material for the polycarbonate resin, carbonyl halides, carbonate esters and the like are used as examples of the carbonate precursor. In addition, 1 type may be used for a carbonate precursor and it may use 2 or more types together by arbitrary combinations and a ratio.

  Specific examples of carbonyl halides include phosgene; haloformates such as bischloroformate of dihydroxy compounds and monochloroformate of dihydroxy compounds.

  Specific examples of the carbonate ester include diaryl carbonates such as diphenyl carbonate and ditolyl carbonate; dialkyl carbonates such as dimethyl carbonate and diethyl carbonate; biscarbonate bodies of dihydroxy compounds, monocarbonate bodies of dihydroxy compounds, and cyclic carbonates. And carbonate bodies of dihydroxy compounds such as

  The method for producing the polycarbonate resin is not particularly limited, and any method can be adopted. Examples thereof include an interfacial polymerization method, a melt transesterification method, a pyridine method, a ring-opening polymerization method of a cyclic carbonate compound, and a solid phase transesterification method of a prepolymer.

The molecular weight of the polycarbonate resin (A) is a viscosity average molecular weight (Mv), preferably in the range of 16000 to 50000, more preferably 18000 or more, further preferably 20000 or more, more preferably 45000 or less, still more preferably. Is 40000, particularly preferably 38000 or less. If the viscosity average molecular weight is less than 16000, the impact resistance of the molded product tends to be lowered and cracking may occur. Since it is easy, it is not preferable.
The polycarbonate resin (A) may be used by mixing two or more kinds of polycarbonate resins having different viscosity average molecular weights. In this case, the polycarbonate resin having a viscosity average molecular weight outside the above preferred range is mixed. May be.

In the present invention, the viscosity average molecular weight [Mv] of the polycarbonate resin is obtained by using methylene chloride as a solvent and determining the intrinsic viscosity [η] (unit dl / g) at a temperature of 20 ° C. using an Ubbelohde viscometer. , Schnell's viscosity formula,
It means a value calculated from η = 1.23 × 10 ⁻⁴ Mv ^0.83 . The intrinsic viscosity [η] is a value calculated from the following equation by measuring the specific viscosity [η _sp ] at each solution concentration [C] (g / dl).

  Moreover, in this invention, you may use in combination with a polycarbonate resin and another thermoplastic resin. Further, for example, for the purpose of further improving flame retardancy and impact resistance, a polycarbonate resin is copolymerized with an oligomer or polymer having a siloxane structure; for the purpose of further improving thermal oxidation stability and flame retardancy A monomer, oligomer or polymer having a copolymer; a copolymer with a monomer, oligomer or polymer having a dihydroxyanthraquinone structure for the purpose of improving thermal oxidation stability; Copolymers with oligomers or polymers having an olefinic structure; copolymers with polyester resin oligomers or polymers for the purpose of improving chemical resistance; Good.

  Further, in order to improve the appearance of the molded product and improve the fluidity, the polycarbonate resin may contain a polycarbonate oligomer. The viscosity average molecular weight (Mv) of this polycarbonate oligomer is usually 1500 or more, preferably 2000 or more, and is usually 9500 or less, preferably 9000 or less. Furthermore, the polycarbonate ligomer contained is preferably 30% by mass or less of the polycarbonate resin (including the polycarbonate oligomer).

Further, the polycarbonate resin may be not only a virgin raw material but also a polycarbonate resin regenerated from a used product (so-called material-recycled polycarbonate resin).
However, the regenerated polycarbonate resin is preferably 80% by mass or less of the polycarbonate resin, and more preferably 50% by mass or less. Recycled polycarbonate resin is likely to have undergone deterioration such as heat deterioration and aging deterioration, so when such polycarbonate resin is used more than the above range, hue and mechanical properties can be reduced. It is because there is sex.

[Ultraviolet absorber (B1)]
The polycarbonate resin composition of this invention contains the ultraviolet absorber (B1) whose maximum absorption wavelength of the absorption curve calculated | required from the following formula | equation (1) is 375 nm or more based on JISK7105.
[Absorbance of polycarbonate resin containing 0.005% by mass of UV absorber]-[Absorbance of polycarbonate resin only] (1)

In the present invention, the maximum absorption wavelength of the ultraviolet absorber (B1) is determined by the same polycarbonate resin from the absorbance of the flat plate molded product of the polycarbonate resin containing 0.005% by mass of the ultraviolet absorber according to the above formula (1). It is defined as the maximum absorption wavelength of an absorption curve obtained by subtracting the absorbance of a flat molded product having the same shape and thickness of a polycarbonate resin containing no ultraviolet absorber. Although it is considered in principle that the maximum absorption wavelength defined in this way does not change depending on the thickness of the flat-plate test piece to be used, in the present invention, it is preferable to compare at a thickness of 2 mm.
In addition, the maximum absorption wavelength of the ultraviolet absorbers (B2) and (B3) described later is also synonymous.
Moreover, the specific conditions of the measurement / determination method of the maximum absorption wavelength are as described in the examples.

  The maximum absorption wavelength of the ultraviolet absorber (B1) is 375 nm or more, and the upper limit thereof is preferably 420 nm or less, more preferably 400 nm or less.

Examples of such an ultraviolet absorber (B1) include benzotriazole compounds, benzophenone compounds, triazine compounds, benzoate compounds, salicylic acid phenyl ester compounds, cyanoacrylate compounds, malonic acid ester compounds, and oxalic acid anilides. Of these compounds, those having a maximum absorption wavelength of 375 nm or more are selected, but benzotriazole ultraviolet absorbers are preferred, and sesamol groups (benzo [1,3] -dioxol-5-ol groups) are more preferred. A benzotriazole-based ultraviolet absorber having the following formula, particularly preferably an ultraviolet absorber represented by the following general formula (1).
X in the general formula (1) is a halogen atom, preferably a halogen atom such as chlorine, bromine, fluorine or iodine, more preferably a chlorine atom, specifically 6- (5-chloro -2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol is preferred.

  Content of a ultraviolet absorber (B1) is 0.02-1 mass part with respect to 100 mass parts of polycarbonate resin (A). When the content is less than 0.02 parts by mass, the transmittance of the resin composition obtained in the 400 to 420 nm wavelength region is too high, and when it exceeds 1 part by mass, the transmittance in the 400 to 420 nm wavelength region is low. Gas generation at the time of molding becomes remarkable, and volatile matter adheres to the molded product and the appearance of the product is significantly impaired. The preferable content of the ultraviolet absorber (B1) is 0.025 parts by mass or more, 0.8 parts by mass or less, more preferably 0.7 parts by mass or less, with respect to 100 parts by mass of the polycarbonate resin (A). Is preferably 0.6 parts by mass or less.

[Ultraviolet absorber (B2)]
The polycarbonate resin composition of the present invention further comprises a benzotriazole-based ultraviolet absorber (B2) having a sesamol group having a maximum absorption wavelength of 360 nm or more and less than 375 nm of an absorption curve obtained from the formula (1) in accordance with JIS K7105. It is preferable to contain.
By containing the ultraviolet absorber (B2), when the ultraviolet absorber (B1) is contained in a small amount, the transmittance in the vicinity of 320 nm becomes high, and it becomes possible to improve the tendency of rinsing.

  According to JIS K7105, the benzotriazole ultraviolet absorber (B2) having a sesamol group having a maximum absorption wavelength of 360 nm or more and less than 375 nm in the absorption curve obtained from the formula (1) is represented by the following general formula (2). UV absorber.

(In General Formula (2), R is a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, a hydroxyl group, a carboxyl group, or an alkyloxycarbonyl having 1 to 8 carbon atoms in the alkyl group. Group, a hydroxyalkyl group having 1 to 8 carbon atoms or an alkylcarbonyloxyalkyl group having 1 to 8 carbon atoms in each alkyl group.)

  In the general formula (2), specific examples of R include hydrogen atom; methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, tert-butyl group, n-hexyl. A linear or branched alkyl group having 1 to 8 carbon atoms which may be substituted, such as a group, n-octyl group, 2-ethylhexyl group; methoxy group, ethoxy group, propoxy group, isopropoxy group, n-butoxy group, A linear or branched alkoxy group having 1 to 8 carbon atoms which may be substituted, such as isobutoxy group, sec-butoxy group, tert-butoxy group, n-hexyloxy group, n-octyloxy group, 2-ethylhexyloxy group, etc. Hydroxyl group; carboxyl group; methoxycarbonyl group, ethoxycarbonyl group, isopropoxycarbonyl group, n-butoxycarbonyl Carbon number of an optionally substituted alkyl group such as isobutoxycarbonyl group, sec-butoxycarbonyl group, tert-butoxycarbonyl group, n-hexyloxycarbonyl group, n-octyloxycarbonyl group, 2-ethylhexyloxycarbonyl group, etc. 1 to 8 linear or branched alkyloxycarbonyl groups; those having 1 to 8 carbon atoms which may be substituted such as hydroxymethyl group, hydroxyethyl group, hydroxypropyl group, hydroxybutyl group, hydroxyhexyl group, hydroxyoctyl group, etc. Linear or branched hydroxyalkyl group; methylcarbonyloxymethyl group, ethylcarbonyloxymethyl group, propylcarbonyloxymethyl group, butylcarbonyloxymethyl group, hexylcarbonyloxymethyl group, heptylcarbonyloxy Tyl group, octylcarbonyloxymethyl group, methylcarbonyloxyethyl group, ethylcarbonyloxyethyl group, propylcarbonyloxyethyl group, butylcarbonyloxyethyl group, hexylcarbonyloxyethyl group, heptylcarbonyloxyethyl group, octylcarbonyloxyethyl group A linear or branched alkylcarbonyloxyalkyl group having 1 to 8 carbon atoms each of which may be substituted, and the like.

  Among these, R is preferably a hydrogen atom, an alkyl group, an alkoxy group, a hydroxyl group, a carboxyl group, an alkyloxycarbonyl group, a hydroxyalkyl group or an alkylcarbonyloxyalkyl group. More preferably, hydrogen atom, methyl group, methoxy group, n-octyloxy group, hydroxyl group, carboxyl group, methoxycarbonyl group, n-octyloxycarbonyl group, hydroxyethyl group, methylcarbonyloxyethyl group, heptylcarbonyloxyethyl group It is.

  Preferred examples of the compound represented by the general formula (2) and having a maximum absorption wavelength of 360 nm or more and less than 375 nm include 6- (2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-n-heptylcarbonyloxyethyl-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-isoheptylcarbonyloxyethyl-2H-benzotriazole-2 -Yl) benzo [1,3] dioxol-5-ol, 6- (5-methyl-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-methoxy- 2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-hydroxy-2H-benzotriazo Ru-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-octyloxy-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- ( 5-carboxy-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-hydroxyethyl-2H-benzotriazol-2-yl) benzo [1,3] dioxole- 5-ol, 6- (5-methylcarbonyloxyethyl-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, and the like.

  Among these, 6- (2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-n-heptylcarbonyloxyethyl-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol, 6- (5-isoheptylcarbonyloxyethyl-2H-benzotriazol-2-yl) benzo [1,3] dioxol-5-ol is particularly preferred.

  The preferable content of the ultraviolet absorber (B2) is 0.01 parts by mass or more and less than 0.08 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). When the amount is less than 0.01 parts by mass, the resin composition obtained easily transmits in the vicinity of a wavelength of 320 nm, and when the amount is 0.08 parts by mass or more, gas is easily generated during molding and the appearance of the product is easily impaired. The content of the ultraviolet absorber (B2) is more preferably 0.02 parts by mass or more, further preferably 0.03 parts by mass or more, and 0.07 parts by mass or less with respect to 100 parts by mass of the polycarbonate resin (A). Is more preferably 0.05 parts by mass or less, and particularly preferably 0.04 parts by mass or less.

[Ultraviolet absorber (B3)]
The polycarbonate resin composition of the present invention preferably further contains an ultraviolet absorber (B3) having a maximum absorption wavelength of less than 360 nm in the absorption curve obtained from the above formula (1) in accordance with JIS K7105.
By containing the ultraviolet absorber (B3), when the ultraviolet absorber (B1) is contained in a small amount, the transmittance near 320 nm becomes high, and it becomes possible to improve the tendency of rinsing.

  Examples of the ultraviolet absorber (B3) include benzotriazole compounds, benzophenone compounds, triazine compounds, benzoxazine compounds, benzoate compounds, salicylic acid phenyl ester compounds, cyanoacrylate compounds, malonic acid ester compounds, Examples thereof include oxalic anilide compounds. Of these, benzotriazole compounds, triazine compounds, malonic ester compounds, and benzoxazine compounds are preferred. These may be used alone or in combination of two or more.

Examples of hydroxybenzophenone compounds include 2-hydroxy-4-octoxybenzophenone.
Examples of malonic ester compounds include dimethyl (p-methoxybenzylidene) malonate, 2- (1-arylalkylidene) malonic esters, tetraethyl-2,2 ′-(1,4-phenylene-dimethylidene) -bismalonate, and the like. Can be mentioned.
Examples of the triazine compound include 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-[(hexyl) oxy] -phenol.
Examples of benzoate compounds include 2,4-di-t-butylphenyl-3,5-di-t-butyl-4-hydroxybenzoate.
Examples of the benzoxazine-based compound include 2,2 ′-(1,4-phenylene) bis (4H-3,1-benzoxazin-4-one).

  As the ultraviolet absorber (B3), a benzotriazole-based ultraviolet absorber is more preferable, and a benzotriazole-based compound having no sesamol group is particularly preferable. More specific examples of such benzotriazole compounds include, for example, 2- (2-hydroxy-5-t-octylphenyl) -2H-benzotriazole, 2- (3-t-butyl-2-hydroxy -5-methylphenyl) -5-chloro-2H-benzotriazole, 2- [5-chloro (2H) -benzotriazol-2-yl] -4-methyl-6- (t-butyl) phenol, 2,4 -Di-tert-butyl-6- (5-chlorobenzotriazol-2-yl) phenol, (2- [5-chloro (2H) -benzotriazol-2-yl] -4,6-di (tert-pentyl) ) Phenol), 3- [3-tert-butyl-5- (5-chloro-2H-benzotriazol-2-yl) -4-hydroxyphenyl] octylpropionate 2- (3-t-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (2H-benzotriazol-2-yl) -6-dodecyl-4-methylphenol, 2- (2H-benzotriazol-2-yl) -p-cresol, 2-[(2H) -benzotriazol-2-yl] -4,6-bis- (1-methyl-1-phenylethyl) phenol and the like are preferable. Can be mentioned.

  The preferable content of the ultraviolet absorber (B3) is 0.01 to 0.2 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). When the amount is less than 0.01 parts by mass, the resin composition obtained easily transmits in the vicinity of a wavelength of 320 nm, and when the amount exceeds 0.2 parts by mass, gas is easily generated during molding, and the appearance of the product is easily impaired. The content of the ultraviolet absorber (B3) is more preferably 0.02 parts by mass or more, further preferably 0.03 parts by mass or more, and 0.15 parts by mass or less with respect to 100 parts by mass of the polycarbonate resin (A). It is more preferable that

[Stabilizer (C)]
The polycarbonate resin composition of the present invention contains a stabilizer. Examples of the stabilizer include phosphorus stabilizers, phenol stabilizers, sulfur stabilizers and the like.

[Phosphorus stabilizer]
When the polycarbonate resin composition of the present invention contains a phosphorus-based stabilizer, the hue of the polycarbonate resin composition is improved, and the heat discoloration is further improved.
Any known phosphorous stabilizer can be used. Specific examples include phosphorus oxo acids such as phosphoric acid, phosphonic acid, phosphorous acid, phosphinic acid, and polyphosphoric acid; acidic pyrophosphate metal salts such as acidic sodium pyrophosphate, acidic potassium pyrophosphate, and acidic calcium pyrophosphate; phosphoric acid Phosphates of Group 1 or Group 2B metals such as potassium, sodium phosphate, cesium phosphate, and zinc phosphate; phosphate compounds, phosphite compounds, phosphonite compounds and the like can be mentioned, and phosphite compounds are particularly preferred. By selecting a phosphite compound, a polycarbonate resin composition having higher discoloration resistance and continuous productivity can be obtained.

Here, the phosphite compound is a trivalent phosphorus compound represented by the general formula: P (OR) ₃ , and R represents a monovalent or divalent organic group.
Examples of such phosphite compounds include triphenyl phosphite, tris (monononylphenyl) phosphite, tris (monononyl / dinonyl phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphine. Phyto, monooctyl diphenyl phosphite, dioctyl monophenyl phosphite, monodecyl diphenyl phosphite, didecyl monophenyl phosphite, tridecyl phosphite, trilauryl phosphite, tristearyl phosphite, distearyl pentaerythritol diphosphite, Bis (2,4-di-tert-butyl-4-methylphenyl) pentaerythritol phosphite, bis (2,6-di-tert-butylphenyl) octyl phosphite, 2,2-methylene (4,6-di-tert-butylphenyl) octyl phosphite, tetrakis (2,4-di-tert-butylphenyl) -4,4′-biphenylene-diphosphite, 6- [3- (3-tert- Butyl-hydroxy-5-methylphenyl) propoxy] -2,4,8,10-tetra-tert-butyldibenzo [d, f] [1,3,2] -dioxaphosphine.

  Among such phosphite compounds, the aromatic phosphite compound represented by the following general formula (3) or (4) effectively increases the heat discoloration of the polycarbonate resin composition of the present invention. preferable.

(In the formula, R ¹ , R ² and R ³ may be the same or different and each represents an aryl group having 6 to 30 carbon atoms.)

(In the formula, R ⁴ and R ⁵ may be the same or different and each represents an aryl group having 6 to 30 carbon atoms.)

  As the phosphite compound represented by the above formula (3), triphenyl phosphite, tris (monononylphenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite and the like are preferable. Tris (2,4-di-tert-butylphenyl) phosphite is more preferred.

  Examples of the phosphite compound represented by the above formula (4) include bis (2,4-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite and bis (2,6-di-tert-butyl). Those having a pentaerythritol diphosphite structure such as -4-methylphenyl) pentaerythritol diphosphite and bis (2,4-dicumylphenyl) pentaerythritol diphosphite are particularly preferred.

Among the phosphite compounds, the aromatic phosphite compound represented by the above formula (4) is more preferable because the hue is more excellent.
In addition, 1 type may contain phosphorus stabilizer and 2 or more types may contain it by arbitrary combinations and a ratio.

  Content of phosphorus stabilizer is 0.01-0.5 mass part with respect to 100 mass parts of polycarbonate resin (A), Preferably it is 0.02 mass part or more, More preferably, it is 0.03 mass part. In addition, it is preferably 0.4 mass parts or less, more preferably 0.3 mass parts or less, and still more preferably 0.2 mass parts or less. When the phosphorus stabilizer content is less than 0.005 parts by mass, the hue and heat discoloration are insufficient, and when it exceeds 0.5 parts by mass, the heat discoloration is not only deteriorated, Wet heat stability also decreases.

[Phenolic stabilizer]
The polycarbonate resin composition of the present invention may contain a phenol-based stabilizer as a stabilizer. As a phenol type stabilizer, a hindered phenol type antioxidant is mentioned, for example. Specific examples thereof include pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl). ) Propionate, thiodiethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], N, N′-hexane-1,6-diylbis [3- (3,5-di-) tert-butyl-4-hydroxyphenylpropionamide), 2,4-dimethyl-6- (1-methylpentadecyl) phenol, diethyl [[3,5-bis (1,1-dimethylethyl) -4-hydroxyphenyl ] Methyl] phosphoate, 3,3 ′, 3 ″, 5,5 ′, 5 ″ -hexa-tert-butyl-a, a ′, a ″-(mesi Tylene-2,4,6-triyl) tri-p-cresol, 4,6-bis (octylthiomethyl) -o-cresol, ethylenebis (oxyethylene) bis [3- (5-tert-butyl-4- Hydroxy-m-tolyl) propionate], hexamethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], 1,3,5-tris (3,5-di-tert- Butyl-4-hydroxybenzyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) -trione, 2,6-di-tert-butyl-4- (4,6-bis ( Octylthio) -1,3,5-triazin-2-ylamino) phenol, 2- [1- (2-hydroxy-3,5-di-tert-pentylphenyl) ethyl] -4,6-di-te t- pentylphenyl acrylate.

Of these, pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate] and octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate are preferable. . Specific examples of such a phenolic antioxidant include “Irganox 1010”, “Irganox 1076” manufactured by BASF, “Adekastab AO-50”, “Adekastab AO-60” manufactured by ADEKA, and the like. Is mentioned.
In addition, 1 type may be contained for the phenol type stabilizer, and 2 or more types may be contained by arbitrary combinations and ratios.

  Content of a phenol type stabilizer is 0.01-0.5 mass part with respect to 100 mass parts of polycarbonate resin (A), Preferably it is 0.02 mass part or more, More preferably, it is 0.03 mass part. In addition, it is preferably 0.4 mass parts or less, more preferably 0.3 mass parts or less, and still more preferably 0.2 mass parts or less. When the content of the phenol-based stabilizer is less than the lower limit of the range, the effect as the phenol-based stabilizer may be insufficient, and the content of the phenol-based stabilizer exceeds the upper limit of the range. If this is the case, the effect may reach its peak and not economical.

  A phosphorus stabilizer and a phenol stabilizer may be used in combination. In that case, the total content of the phosphorus stabilizer and the phenol stabilizer is 0.01 to 0.5 parts by weight, preferably 0.02 parts by weight or more, with respect to 100 parts by weight of the polycarbonate resin (A). More preferably, it is 0.03 parts by mass or more, preferably 0.4 parts by mass or less, more preferably 0.3 parts by mass or less, and further preferably 0.2 parts by mass or less.

[Sulfur-based stabilizer]
Examples of the sulfur stabilizer include dilauryl-3,3′-thiodipropionic acid ester, ditridecyl-3,3′-thiodipropionic acid ester, dimyristyl-3,3′-thiodipropionic acid ester, and distearyl. −3,3′-thiodipropionic acid ester, lauryl stearyl-3,3′-thiodipropionic acid ester, pentaerythritol tetrakis (3-laurylthiopropionate), bis [2-methyl-4- (3- Laurylthiopropionyloxy) -5-tert-butylphenyl] sulfide, octadecyl disulfide, mercaptobenzimidazole, 2-mercapto-6-methylbenzimidazole, 1,1′-thiobis (2-naphthol) and the like.

Among the above, pentaerythritol tetrakis (3-lauryl thiopropionate) is preferable. Specific examples of such a sulfur stabilizer include “ADEKA STAB AO-412S” manufactured by ADEKA.

  Content of a sulfur type stabilizer is 0.01-0.5 mass part with respect to 100 mass parts of polycarbonate resin (A), Preferably it is 0.02 mass part or more, More preferably, it is 0.03 mass part. In addition, it is preferably 0.4 mass parts or less, more preferably 0.3 mass parts or less, and still more preferably 0.2 mass parts or less. When the content of the sulfur stabilizer is less than the lower limit of the range, the effect as the sulfur stabilizer may be insufficient, and the content of the sulfur stabilizer exceeds the upper limit of the range. If this is the case, the effect may reach its peak and not economical.

[Additives, etc.]
The polycarbonate resin composition of the present invention has other additives other than those described above, for example, release agents, fluorescent whitening agents, pigments, dyes, flame retardants, impact resistance improvers, antistatic agents, plasticizers, and compatibilizing agents. An additive such as an agent and other polymers other than the polycarbonate resin can be contained. These additives or other resins may be used alone or in combination.

[Production Method of Polycarbonate Resin Composition]
There is no restriction | limiting in the manufacturing method of the polycarbonate resin composition of this invention, The manufacturing method of a well-known polycarbonate resin composition can be employ | adopted widely, a polycarbonate resin (A), a ultraviolet absorber (B1), a phosphorus stabilizer (C), In addition, other components to be blended as necessary are mixed in advance using various mixers such as a tumbler and a Henschel mixer, and then Banbury mixer, roll, Brabender, single-screw kneading extruder, twin-screw kneading extruder And a melt kneading method using a mixer such as a kneader. The temperature for melt kneading is not particularly limited, but is usually in the range of 240 to 320 ° C.

  The polycarbonate resin composition of the present invention can produce various molded articles by molding pellets obtained by pelletizing the above-described polycarbonate resin composition by various molding methods. Further, the resin melt-kneaded by an extruder can be directly molded into a molded product without going through the pellets.

  The polycarbonate resin composition of the present invention has a transmittance of 25% or less measured at a wavelength of 420 nm in accordance with JIS K7105 for a molded product having a thickness of 2 mm obtained by molding this polycarbonate resin composition. Is preferably 10% or less, more preferably 5% or less, and particularly preferably 1% or less. If the transmittance at a wavelength of 420 nm exceeds 25%, it is insufficient as a material for a sunglasses lens or the like that aims to cut the wavelength range of 400 to 420 nm.

  The molded product obtained from the polycarbonate resin composition of the present invention is excellent in cutability of 400 to 420 nm wavelength light on the visible light side in addition to ultraviolet light, and has no problem of gas generation during molding, The polycarbonate resin has various excellent mechanical and thermal properties. Therefore, the application can be used widely and suitably for applications where deterioration due to ultraviolet rays is a concern. Examples thereof include sheets, films, sundries, home appliance parts, automobile parts, building materials, and hollow containers. More specifically, for example, eyeglass lenses, sunglasses lenses, goggles (for skiing, etc.), protective glasses, protective face bodies, etc., roof panels such as arcades, indoor pools, carports, sunroofs, signal lights, sound insulation walls, automobile side Preferred examples include windows, rear windows, solar cell housings, street lamp covers, and the like.

  Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not construed as being limited to the following examples.

The raw materials and evaluation methods used in the following examples and comparative examples are as follows.

In the above Table 1, the maximum absorption wavelength of the ultraviolet absorber, and the absorbance A _lambda composition of the polycarbonate resin of Table 1, wherein the respective UV absorber containing 0.005%, does not contain a UV absorber This is the maximum absorption wavelength obtained from the absorption curve (A _λ -A _λ0 ) obtained by subtracting the absorbance A _λ0 from the absorbance A _λ , respectively, by obtaining the absorbance A _λ0 of the polycarbonate resin described in Table 1 above. Absorbance A _λ and absorbance A _λ0 were measured in the same manner as described in [Measurement of transmittance and absorbance] below.

(Examples 1-22, Comparative Examples 1-9)
[Production of resin composition pellets]
Each component described in Table 1 above was blended in the proportions (parts by mass) described in Table 2 below and mixed for 20 minutes with a tumbler, and then a single screw extruder with a vent with a screw diameter of 40 mm (Tanabe Plastic Machine) The product was melt-kneaded at a cylinder temperature of 280 [deg.] C. using a product "VS-40" manufactured by the company, and pellets of a polycarbonate resin composition were obtained by strand cutting.

[Measurement of transmittance and absorbance]
The obtained pellets were dried with a hot air circulation dryer at 120 ° C. for 5 hours, and then molded with an injection molding machine (“SE50DUZ” manufactured by Sumitomo Heavy Industries, Ltd.) at a resin temperature of 280 ° C. and a mold temperature of 80 ° C. Under the condition of a cycle of 30 seconds, a stepped flat plate-shaped test piece having a width of 50 mm × a length of 90 mm and a thickness of 1 mm, 2 mm, and 3 mm was formed.
In accordance with JIS K7105, the transmittance and absorbance of the 2 mm thick portion of the stepped flat plate test piece were measured using a spectrophotometer (“UV-3100PC” manufactured by Shimadzu Corporation).
The transmittance (unit:%) at 420 nm, 380 nm and 320 nm is shown in Table 2 and below.

[Evaluation of gas generation during molding]
After the pellets obtained above were dried at 120 ° C. for 5 hours, using an injection molding machine (“SE18DUZ” manufactured by Sumitomo Heavy Industries, Ltd.), using the drop mold shown in FIG. Compared with Comparative Example 2, the state of dirt due to white deposits generated on the metal mirror surface on the mold fixing side after 100 shot injection molding under the conditions of 320 ° C., molding cycle 10 seconds, mold temperature 80 ° C. According to the following criteria, the evaluation was made visually to evaluate the gas generation during molding.
A: Mold deposits are much less than the state after 100 shot molding of Comparative Example 2, and the mold contamination resistance is very good.
B: Although mold deposits are less than the state after 100 shot molding in Comparative Example 2, some mold resistance is observed.
C: Mold adhering material is at the same level as that after 100-shot molding in Comparative Example 2, and mold contamination is observed.
D: There are more mold deposits than the state after 100 shot molding of Comparative Example 2, and mold contamination is noticeable.

The drop mold shown in FIG. 1 is a mold designed to introduce a resin composition from the gate G so that the generated gas easily accumulates at the tip P portion. The gate G has a width of 1 mm and a thickness of 1 mm. In FIG. 1, the width h1 is 14.5 mm, the length h2 is 7 mm, the length h3 is 27 mm, and the thickness of the molded part is 3 mm.
The above evaluation results are shown in Table 2 below.

  The molded product obtained from the polycarbonate resin composition of the present invention is excellent in cutability of 400 to 420 nm wavelength light on the visible light side in addition to ultraviolet light, and has no problem of gas generation during molding, The polycarbonate resin has various excellent mechanical and thermal properties, and can be suitably used for applications where deterioration due to ultraviolet rays is a concern. Industrial applicability is high.

Claims (8)

0.02 to 1 part by mass of an ultraviolet absorber (B1) having a maximum absorption wavelength of 375 nm or more based on JIS K7105 based on the following formula with respect to 100 parts by mass of the polycarbonate resin (A), and a stabilizer A polycarbonate resin composition containing 0.01 to 0.5 parts by mass of (C).
[Absorbance of polycarbonate resin containing 0.005% by mass of UV absorber]-[Absorbance of polycarbonate resin alone]   The polycarbonate resin composition according to claim 1, wherein the ultraviolet absorber (B1) is a benzotriazole-based ultraviolet absorber having a sesamol group. The polycarbonate resin composition according to claim 1 or 2, wherein the ultraviolet absorber (B1) is an ultraviolet absorber represented by the following general formula (1).
(In the formula, X represents a halogen atom.)   Furthermore, a benzotriazole-based ultraviolet absorber (B2) having a sesamol group having a maximum absorption wavelength of 360 nm or more and less than 375 nm of the absorption curve obtained from the above formula in accordance with JIS K7105, relative to 100 parts by mass of the polycarbonate resin (A), The polycarbonate resin composition according to any one of claims 1 to 3, which is contained in an amount of 0.01 parts by mass or more and less than 0.08 parts by mass.   Furthermore, 0.01 to 0.2 parts by mass of the ultraviolet absorber (B3) having a maximum absorption wavelength of less than 360 nm in the absorption curve obtained from the above formula in accordance with JIS K7105 with respect to 100 parts by mass of the polycarbonate resin (A). The polycarbonate resin composition according to any one of claims 1 to 4.   The ultraviolet absorber (B3) is at least one selected from a benzotriazole-based ultraviolet absorber having no sesamol group, a triazine-based ultraviolet absorber, a malonic ester-based ultraviolet absorber, and a benzoxazine-based ultraviolet absorber. 5. The polycarbonate resin composition according to 5.   The polycarbonate resin composition according to any one of claims 1 to 6, wherein a transmittance of a molded product having a thickness of 2 mm measured at a wavelength of 420 nm in accordance with JIS K7105 is 25% or less.   A molded article of the polycarbonate resin composition according to any one of claims 1 to 7.