JP2018515736A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2018515736A5 JP2018515736A5 JP2017558443A JP2017558443A JP2018515736A5 JP 2018515736 A5 JP2018515736 A5 JP 2018515736A5 JP 2017558443 A JP2017558443 A JP 2017558443A JP 2017558443 A JP2017558443 A JP 2017558443A JP 2018515736 A5 JP2018515736 A5 JP 2018515736A5
- Authority
- JP
- Japan
- Prior art keywords
- zone
- percent
- resin
- composite
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
上表の結果に要約した全ての比較例、本発明の実施例を同一材料の組成物で構成して、同一条件下で試験した。市販の装置で、これらの実施例の製造を実施した。結果から、実施例1および2により例示される特許請求された発明の製品は、40mmでの屈曲試験力測定によって、比較例A、BおよびCよりも非常に高い可撓性能を呈する。実施例1および2は、約10〜約70%の可撓性能の向上を示す。さらに、熱プレス加工時間は、実施例1および2の最も好適な温度選択に応じて、例えば、比較例AおよびCに対して約20分から数秒まで、かなり低減された。加えて、現行規格で実施したナイフ−ブレード貫通、スパイク貫通および耐衝撃性V50試験は、全てこれらの標準の諸要件に準拠している。
本発明は、以下の事項を含んでいるとも言える。
(付記1)
ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適である複合材であって、樹脂を含まない高分子繊維布帛コア部(第一ゾーン)と、前記コア部の少なくとも片面に位置し、エラストマー系または熱可塑性樹脂を含浸させた高分子繊維布帛部(第二ゾーン)と
を含み、
(i)樹脂が、複合材の体積分率5〜79パーセントを含み、
(ii)前記樹脂が、第二ゾーンの繊維を含まない体積の最大100パーセントまで充填され、
(iii)前記第一ゾーンが、前記複合材の総厚の10〜90パーセントを含み、
(iv)前記第一ゾーンまたは前記第二ゾーンの前記繊維が、少なくとも20g/デニールの糸強力と、少なくとも444g/dtexの引張モジュラスを有し、および
(v)前記樹脂が、20〜1200パーセントの破断時伸びを有する複合材。
(付記2)
前記第一ゾーンまたは前記第二ゾーンの前記布帛が、織布、不織布、組物または編物である付記1に記載の複合材。
(付記3)
前記第一または第二ゾーンの前記布帛の前記繊維のポリマーが、芳香族ポリアミド、芳香族コポリアミドまたはポリエチレンである付記1に記載の複合材。
(付記4)
前記熱可塑性樹脂が、ポリビニル、ポリオレフィン、ポリアミド、ポリエステル、ポリウレタン、ポリアクリロニトリルまたはポリスルホンである付記1に記載の複合材。
(付記5)
前記エラストマーが、ゴムまたはシリコーンである付記1に記載の複合材。
(付記6)
前記不織布が、一方向、二軸、多軸である付記2に記載の複合材。
(付記7)
ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適な複合材であって、
(i)布帛を含むが樹脂を含まない第一ゾーンであって、前記第一ゾーンが前記複合材の総厚の10〜90パーセントを含む第一ゾーンと、
(ii)エラストマー系または熱可塑性樹脂を含むが布帛を含まない第三ゾーンであって、前記第三ゾーンが前記複合材の総厚の0〜50パーセントを含む第三ゾーンと、
(iii)第二ゾーンであって、前記第一ゾーンと前記第三ゾーンの間に位置し、布帛およびエラストマー系または熱可塑性樹脂を含み、前記第二ゾーンが前記複合材の総厚の10〜90パーセントを含む第二ゾーンとを含み、
(a)前記第一ゾーンおよび前記第二ゾーンの前記布帛が、少なくとも20g/デニールの糸強力と、少なくとも444g/dtexの引張モジュラスを有する高分子糸から形成され、
(b)前記第二ゾーンまたは前記第三ゾーンの前記エラストマー系または前記熱可塑性樹脂が、20〜1200パーセントの破断時伸びを有し、
(c)樹脂が、第二ゾーンの体積分率5〜79パーセントを含み、
(d)前記樹脂が、前記第二ゾーンの前記繊維を含まない体積の80〜100パーセントを充填される複合材。
(付記8)
前記布帛が、織布、不織布または編物である付記7に記載の複合材。
(付記9)
前記布帛の糸条のポリマーが、芳香族ポリアミド、芳香族コポリアミドまたはポリエチレンである付記7に記載の複合材。
(付記10)
前記熱可塑性樹脂が、ポリビニル、ポリオレフィン、ポリアミド、ポリエステル、ポリウレタン、ポリアクリロニトリルまたはポリスルホンである付記7に記載の複合材。
(付記11)
前記エラストマーが、ゴムまたはシリコーンである付記7に記載の複合材。
(付記12)
前記不織布が、一方向、二軸、多軸である付記8に記載の複合材。
(付記13)
防護物品であって、ナイフ、ピック、弾丸および破片に対して耐性のある付記1または7に記載の複合材のうち少なくとも1つを含む防護物品。
(付記14)
前記物品が、2001年6月付けのNIJ0101.04レベルIIIA RevisionA、200年9月付けのNIJ0115.00、および2007年付けのHOSDB刊行物N°39/07/C防護レベルKR1/SP1 E1基準の要件を満たしている付記13に記載の防護物品。
(付記15)
前記物品が、試験法Aに従って試験される場合に、4000N以下の屈曲試験力を呈する付記13に記載の防護物品。
本発明は、以下の事項を含んでいるとも言える。
(付記1)
ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適である複合材であって、樹脂を含まない高分子繊維布帛コア部(第一ゾーン)と、前記コア部の少なくとも片面に位置し、エラストマー系または熱可塑性樹脂を含浸させた高分子繊維布帛部(第二ゾーン)と
を含み、
(i)樹脂が、複合材の体積分率5〜79パーセントを含み、
(ii)前記樹脂が、第二ゾーンの繊維を含まない体積の最大100パーセントまで充填され、
(iii)前記第一ゾーンが、前記複合材の総厚の10〜90パーセントを含み、
(iv)前記第一ゾーンまたは前記第二ゾーンの前記繊維が、少なくとも20g/デニールの糸強力と、少なくとも444g/dtexの引張モジュラスを有し、および
(v)前記樹脂が、20〜1200パーセントの破断時伸びを有する複合材。
(付記2)
前記第一ゾーンまたは前記第二ゾーンの前記布帛が、織布、不織布、組物または編物である付記1に記載の複合材。
(付記3)
前記第一または第二ゾーンの前記布帛の前記繊維のポリマーが、芳香族ポリアミド、芳香族コポリアミドまたはポリエチレンである付記1に記載の複合材。
(付記4)
前記熱可塑性樹脂が、ポリビニル、ポリオレフィン、ポリアミド、ポリエステル、ポリウレタン、ポリアクリロニトリルまたはポリスルホンである付記1に記載の複合材。
(付記5)
前記エラストマーが、ゴムまたはシリコーンである付記1に記載の複合材。
(付記6)
前記不織布が、一方向、二軸、多軸である付記2に記載の複合材。
(付記7)
ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適な複合材であって、
(i)布帛を含むが樹脂を含まない第一ゾーンであって、前記第一ゾーンが前記複合材の総厚の10〜90パーセントを含む第一ゾーンと、
(ii)エラストマー系または熱可塑性樹脂を含むが布帛を含まない第三ゾーンであって、前記第三ゾーンが前記複合材の総厚の0〜50パーセントを含む第三ゾーンと、
(iii)第二ゾーンであって、前記第一ゾーンと前記第三ゾーンの間に位置し、布帛およびエラストマー系または熱可塑性樹脂を含み、前記第二ゾーンが前記複合材の総厚の10〜90パーセントを含む第二ゾーンとを含み、
(a)前記第一ゾーンおよび前記第二ゾーンの前記布帛が、少なくとも20g/デニールの糸強力と、少なくとも444g/dtexの引張モジュラスを有する高分子糸から形成され、
(b)前記第二ゾーンまたは前記第三ゾーンの前記エラストマー系または前記熱可塑性樹脂が、20〜1200パーセントの破断時伸びを有し、
(c)樹脂が、第二ゾーンの体積分率5〜79パーセントを含み、
(d)前記樹脂が、前記第二ゾーンの前記繊維を含まない体積の80〜100パーセントを充填される複合材。
(付記8)
前記布帛が、織布、不織布または編物である付記7に記載の複合材。
(付記9)
前記布帛の糸条のポリマーが、芳香族ポリアミド、芳香族コポリアミドまたはポリエチレンである付記7に記載の複合材。
(付記10)
前記熱可塑性樹脂が、ポリビニル、ポリオレフィン、ポリアミド、ポリエステル、ポリウレタン、ポリアクリロニトリルまたはポリスルホンである付記7に記載の複合材。
(付記11)
前記エラストマーが、ゴムまたはシリコーンである付記7に記載の複合材。
(付記12)
前記不織布が、一方向、二軸、多軸である付記8に記載の複合材。
(付記13)
防護物品であって、ナイフ、ピック、弾丸および破片に対して耐性のある付記1または7に記載の複合材のうち少なくとも1つを含む防護物品。
(付記14)
前記物品が、2001年6月付けのNIJ0101.04レベルIIIA RevisionA、200年9月付けのNIJ0115.00、および2007年付けのHOSDB刊行物N°39/07/C防護レベルKR1/SP1 E1基準の要件を満たしている付記13に記載の防護物品。
(付記15)
前記物品が、試験法Aに従って試験される場合に、4000N以下の屈曲試験力を呈する付記13に記載の防護物品。
Claims (3)
- ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適である複合材であって、樹脂を含まない高分子繊維布帛コア部(第一ゾーン)と、前記コア部の少なくとも片面に位置し、エラストマー系または熱可塑性樹脂を含浸させた高分子繊維布帛部(第二ゾーン)と
を含み、
(i)樹脂が、複合材の体積分率5〜79パーセントを含み、
(ii)前記樹脂が、第二ゾーンの繊維を含まない体積の最大100パーセントまで充填され、
(iii)前記第一ゾーンが、前記複合材の総厚の10〜90パーセントを含み、
(iv)前記第一ゾーンまたは前記第二ゾーンの前記繊維が、少なくとも20g/デニールの糸強度と、少なくとも444g/dtexの引張弾性率を有し、および
(v)前記樹脂が、20〜1200パーセントの破断時伸びを有する複合材。 - ナイフ、ピック、弾丸および破片に対して耐性のある物品に使用するのに好適な複合材であって、
(i)布帛を含むが樹脂を含まない第一ゾーンであって、前記第一ゾーンが前記複合材の総厚の10〜90パーセントを含む第一ゾーンと、
(ii)エラストマー系または熱可塑性樹脂を含むが布帛を含まない第三ゾーンであって、前記第三ゾーンが前記複合材の総厚の0〜50パーセントを含む第三ゾーンと、
(iii)繊維布帛およびエラストマー系または熱可塑性樹脂を含み、前記複合材の総厚の10〜90パーセントを含む第二ゾーンとを含み、
(a)前記第一ゾーンおよび前記第二ゾーンの前記布帛が、少なくとも20g/デニールの糸強度と、少なくとも444g/dtexの引張弾性率を有する高分子糸から形成され、
(b)前記第二ゾーンまたは前記第三ゾーンの前記エラストマー系または前記熱可塑性樹脂が、20〜1200パーセントの破断時伸びを有し、
(c)樹脂が、第二ゾーンの体積分率5〜79パーセントを含み、
(d)前記樹脂が、前記第二ゾーンの前記繊維を含まない体積の80〜100パーセントを充填する複合材。 - 防護物品であって、ナイフ、ピック、弾丸および破片に対して耐性のある請求項1または2に記載の複合材のうち少なくとも1つを含む防護物品。