JP2018121748A - 脱臭抗菌剤及び脱臭抗菌方法 - Google Patents
脱臭抗菌剤及び脱臭抗菌方法 Download PDFInfo
- Publication number
- JP2018121748A JP2018121748A JP2017014597A JP2017014597A JP2018121748A JP 2018121748 A JP2018121748 A JP 2018121748A JP 2017014597 A JP2017014597 A JP 2017014597A JP 2017014597 A JP2017014597 A JP 2017014597A JP 2018121748 A JP2018121748 A JP 2018121748A
- Authority
- JP
- Japan
- Prior art keywords
- powder
- antibacterial
- deodorizing antibacterial
- inorganic silica
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
[2] 前記アルカリ性粉末と前記無機シリカ系粉末との合計に対する、前記アルカリ性粉末の含有量が、10〜90質量%である[1]に記載の脱臭抗菌剤。
[3] 前記アルカリ性粉末が、消石灰粉末及び/又はドロマイト系粉末である[1]又は[2]に記載の脱臭抗菌剤。
[4] 前記無機シリカ系粉末が、水溶液若しくは分散液のpHが6以下となる無機シリカ系酸性粉末である[1]〜[3]のいずれかに記載の脱臭抗菌剤。
[5] 臭気発生源及び/又はその近傍に、[1]〜[4]のいずれかに記載の脱臭抗菌剤を配置する脱臭抗菌方法。
[6] 前記臭気が腐敗ガスであり、アンモニアガス及び硫化水素ガスを含む[5]に記載の脱臭抗菌方法。
本発明の脱臭抗菌剤の一態様は、水溶液若しくは分散液のpHが12以上となるアルカリ性粉末(以下、単に「アルカリ性粉末」ということがある)と、無機シリカ系粉末とを含む。
例えば、生ものが腐敗した際には、アンモニアガス及び硫化水素ガスといった臭気ガスが発生する。それぞれを吸着により除去する手段があるが、これらはそれぞれアルカリ性及び酸性であるため、同時に除去することは難しい。また、腐敗により菌が繁殖するため、これも同時に抗菌できれば衛生管理や快適性の観点から非常に有意である。しかし、アンモニアガス及び硫化水素ガスを含む臭気ガスを除去し、かつ抗菌をも実現できる有効な技術は見いだされてはいない。
本発明の脱臭抗菌剤の一態様について、以下、詳細に説明する。
アルカリ性粉末は、これを100mlの純水に10g添加し、3分程度撹拌して溶解もしくは分散した際のpHが12以上となる粉末で、例えば、消石灰、生石灰、ドロマイト系化合物等が挙げられる。
上記のなかでも、消石灰粉末及び/又はドロマイト系化合物(特に、水酸化ドロマイト)が、コスト及び取り扱い性の観点から好ましい。
ドロマイト(Dolomite)は、カルサイト(Calcite)と呼ばれる炭酸カルシウム(CaCO3)と、マグネサイト(Magnesite)と呼ばれる炭酸マグネシウム(MgCO3)との、理想的には1:1の複塩である。成分的にみれば、これはカルサイトとマグネサイトとの中間に位置する物質である。ドロマイトを比較的温和な条件で加熱すれば、脱炭酸反応が起こって、「軽焼ドロマイト」と呼ばれる酸化カルシウム(CaO)と酸化マグネシウム(MgO)との酸化物の複塩が得られる。軽焼ドロマイトに水を加えて消化すれば、水酸化カルシウム(Ca(OH)2)と水酸化マグネシウム(Mg(OH)2)との水酸化物の複塩である、水酸化ドロマイトが得られる。水酸化ドロマイトには、炭酸カルシウム、酸化カルシウム、炭酸マグネシウム、酸化マグネシウム、二酸化ケイ素、酸化アルミニウム、酸化第二鉄等の他の成分を本発明の効果を妨げない範囲で含有していてもよい。
また、水酸化ドロマイトの原料として、軽焼ドロマイトを用いることができる。この軽焼ドロマイトとしては、JIS R9001に規定する特号及び1号の軽焼ドロマイトが好適である。軽焼ドロマイトは、処理対象物や原料中に含まれる水と反応して消化により水和され、水酸化ドロマイトに変化する。そのため、水酸化ドロマイトを調製する工程を省略して軽焼ドロマイトをそのまま用いても水酸化ドロマイトによる効果が発揮される。
無機シリカ系粉末とは、化学成分としてシリカを含有する無機粉末である。
無機シリカ系粉末としては、活性白土、酸性白土、珪藻土、シリカゲル、頁岩(特に、膨張性頁岩を焼成したもの)、パーライト、アロフェン、ゼオライト等といった、化学成分としてシリカを含む粉末が挙げられる。なかでも、無機シリカ系粉末が、水溶液若しくは分散液のpHが6以下となる無機シリカ系酸性粉末であることが好ましい。無機シリカ系酸性粉末とは、これを100mlの純水に10g添加し、3分程度撹拌して溶解もしくは分散した際のpHが6以下(好ましくは4以下、より好ましくは3以下)となる粉末をいう。無機シリカ系酸性粉末とすることでアルカリ性粉末との相乗効果が得られやすい。
具体的な無機シリカ系酸性粉末としては、好ましくは、活性白土、珪藻土等が挙げられる。
かかる粉末の平均粒子径(メジアン径(d50))は、10〜200μmであることが好ましく、20〜190μmであることがより好ましい。
本発明の脱臭抗菌方法の一態様は、臭気発生源及びその近傍に、本発明の一態様に係る脱臭抗菌剤を配置する方法である。ここで臭気としては、例えば、アンモニアガス及び硫化水素ガスを含む腐敗ガス、特に、放置した死体から発生する腐敗ガスが挙げられる。
なお、臭気発生源及びその近傍には、アンモニアガス及び硫化水素ガスの他に、メチルメルカプタン、トリメチルアミン、スカトール等が存在することもある。
また、上記のような臭気発生源には、通常、腐敗物が存在するものであるため、大腸菌、黄色ぶどう球菌、緑膿菌、サルモネラ菌等の少なくともいずれかの細菌が存在し、場合によっては、感染菌が存在することもある。
不織紙は、多数の紙繊維が立体的に絡み合って形成されたものであり、繊維間に多数の空隙が形成されているものである。
織布は、繊維を引き揃えて撚りをかけた糸を織り込んで形成されたものであり、糸間に多数の空隙が形成されているものである。
なお、樹脂等からなる多孔質フィルムで通気性及び通水性を有する容器を構成してもよい。
無機シリカ系粉末として、活性白土粉末(日本活性白土(株)社製SA−1)、ゼオライト粉末(ジークライト(株)社製ジークライトSGW)、珪藻土粉末(有限会社 稚内グリーンファクトリー社製 珪藻土−0.7mm)のそれぞれ1gを秤量し、アンモニアガス吸着試験を行った。下記表1−1及び表1−2に上記無機シリカ系粉末の性状・物性、化学成分を示す。
比表面積は、ガス吸着式細孔分布測定器「NOVA−4200」(株式会社セイシン企業製)を用いて、BET法により、窒素の吸着量から1点法により算出した。
細孔容積も、ガス吸着式細孔分布測定器「NOVA−4200」(株式会社セイシン企業製)を用いて、算出した。
pHは、それぞれの試料を10g採取し、これを100mlの純水中に添加してガラス棒を使って3分間よく撹拌した後、pHメータにて測定した。
また、化学成分は、JIS R9011の「石灰の分析方法」に規定された方法により測定した。
i)1M酢酸アンモニウム液
酢酸アンモニウム77.08gを1Lの純水に溶解し、その後、2Mのアンモニア水溶液と2Mの酢酸とで、pHを7に調整して、1M酢酸アンモニウム液を調製した。
ii)エタノール(0.8m3/m3)
エタノール800mLに純水100mLを加えて、BTB試験紙によりアンモニア水でpHを7に調整した。
iii)塩化ナトリウム溶液(10質量%)
塩化ナトリウム100gに純水を加えて1Lとした。
(2)操作−交換−
試料0.1gを遠心管に分取した。そこへ1M酢酸アンモニウム液を40mL添加した。25℃の恒温槽中で適宜振り混ぜながら放置した。その後、5000rpmで遠心分離し上澄み液を捨てた。
(3)操作−洗浄−
次に、エタノール40mLを加えて振り混ぜ、5000rpmで遠心分離し上澄みを捨てた。この洗浄操作を4回繰り返した後、室温で乾燥させた。
(4)操作−浸出−
乾燥後、塩化ナトリウム溶液40mLを加え、25℃の恒温槽中で適宜振り混ぜながら24時間放置した。その後、5000rpmで遠心分離し上澄み液を採取し、純水にて50mLにメスアップした。
(5)測定
50mLに定容とした、浸透塩化ナトリウム溶液から正確に一定量(20ml)はかり、ブレムナー蒸留装置により、NH4 +を定量して陽イオン交換容量を求めた。
・実施例1
アルカリ性粉末として下記表3に示す性状・物性の消石灰(吉澤石灰工業(株)製工業用特号消石灰)1gを用い、無機シリカ系粉末として、上記“無機シリカ系粉末によるアンモニアガス吸着試験”で使用した活性白土粉末1gを用い、これらを混合して脱臭抗菌剤を作製した。
アルカリ性粉末として実施例1で使用した消石灰1gを用い、無機シリカ系粉末として、上記“無機シリカ系粉末によるアンモニアガス吸着試験”で使用したゼオライト粉末1gを用い、これらを混合して脱臭抗菌剤を作製した。
アルカリ性粉末として実施例1で使用した消石灰1gを用い、無機シリカ系粉末として、上記“無機シリカ系粉末によるアンモニアガス吸着試験”で使用した珪藻土1gを用い、これらを混合して脱臭抗菌剤を作製した。
実施例1〜3で作製した脱臭抗菌剤をそれぞれ1g用いて、“無機シリカ系粉末によるアンモニアガス吸着試験”と同様にして、アンモニアガス吸着試験を行った。結果を下記表4に示す。
アンモニアガスを硫化水素ガスとし、硫化水素ガス濃度を20ppmとした以外は、上記“・アンモニアガス吸着試験”と同様にして、実施例1〜3で作製した脱臭抗菌剤をそれぞれ1g用いて、硫化水素ガス吸着試験を行った。結果を下記表5に示す。
消石灰と活性白土との割合を下記表6のとおりにした以外は実施例1と同様にして脱臭抗菌剤を作製した。作製した各脱臭抗菌剤を1g用いて、実施例1と同様にアンモニアガス吸着試験及び硫化水素ガス吸着試験を行った。結果を下記表6及び表7示す。
「JIS Z 2801:2012 抗菌加工製品・抗菌性試験方法・抗菌効果」を参考にした試験方法によって、実施例1、実施例4〜6、比較例1、2の脱臭抗菌剤(20g)を収納したパック(試験品)の各種細菌に対する常温下(25℃)での抗菌効果を調べた。具体的には下記のようにして試験を行った。
試験品の両面にパルスドキセノンランプ(コメット,BHX−200)をそれぞれ20秒間照射して清浄化した。
(2)試験条件
i)作用温湿度:25±1℃、90%RH以上
ii)作用時間:直後(無加工試験品のみ)、24時間
i)試験菌
a)Escherichia coli NBRC3972(大腸菌)
b)Staphylococcus aureus NBRC12732(黄色ぶどう球菌)
ii)試験菌液の調製
凍結保存された菌株を普通寒天培地(日水製薬)で35±1℃、24時間培養した。この培養菌を新たな普通寒天培地に移植して、35±1℃で19時間培養した。発育した集落をかき取り、1/500濃度の普通ブイヨン培地(栄研化学)で約105個/mLに調製し、これを試験菌液とした。
試験方法は「JIS Z 2801:2012 抗菌加工製品・抗菌性試験方法・抗菌効果」を参考にした。詳細を以下に示す。
i)試験菌液の接種と培養
試験品をシャーレに入れ、試験品表面全体に試験菌液0.4mLを9箇所滴下した。滴下した試験菌液が浸み込んだ後、パック内の内容物と菌液の接触効率を高めるために、菌液接種面を裏返して、作用温湿度条件(25℃±1℃、90%RH)下で所定時間作用させた。
所定時間作用後に予めSCDLPブイヨン培地(栄研化学)100mLを入れたストマッカー用減菌袋に試験品を回収し、試験品から試験菌を洗い出した。洗い出した液を菌数測定用試料液とした。試料液はリン酸緩衝生理食塩液を用いて希釈列を作製し、試料液原液及び希釈液の各1mLをシャーレに移し、標準寒天培地(日水製薬)約20mLと混合後、固化させて35±1℃で48時間培養した。培養後の発育集落を数えて、試験品あたりの試験菌数(定量下限値:100個/試験品)を求めた。また、得られた試験菌数から、無加工試験品を対照として、各抗菌加工品の抗菌活性値を求めた。
黄色ブドウ球菌対する試験結果を下記表8、表9に示し、大腸菌に対する試験結果を下記表10、表11に示す。
式:R=(Ut−Uo)−(At−Uo)=Ut−At
R:抗菌活性値(数値は小数点以下2桁目を切り捨て、小数点1桁で表示)
Ut:無加工試験品の接種直後の生菌数の対数値
Uo:無加工試験品の各作用時間後の生菌数の対数値
At:抗菌加工品の各作用時間後の生菌数の対数値
参考とした試験規格「JIS Z 2801」における「抗菌効果」は、試験菌である大腸菌や黄色ブドウ球菌に対する24時間作用における抗菌活性値が2.0以上とされており、これを鑑みれば、実施例に係る脱臭抗菌剤は優れた抗菌効果を発揮したことがわかる。
Claims (6)
- 水溶液若しくは分散液のpHが12以上となるアルカリ性粉末と、無機シリカ系粉末と、を含む脱臭抗菌剤。
- 前記アルカリ性粉末と前記無機シリカ系粉末との合計に対する、前記アルカリ性粉末の含有量が、10〜90質量%である請求項1に記載の脱臭抗菌剤。
- 前記アルカリ性粉末が、消石灰粉末及び/又はドロマイト系粉末である請求項1又は2に記載の脱臭抗菌剤。
- 前記無機シリカ系粉末が、水溶液若しくは分散液のpHが6以下となる無機シリカ系酸性粉末である請求項1〜3のいずれか1項に記載の脱臭抗菌剤。
- 臭気発生源及び/又はその近傍に、請求項1〜4のいずれか1項に記載の脱臭抗菌剤を配置する脱臭抗菌方法。
- 前記臭気が腐敗ガスであり、アンモニアガス及び硫化水素ガスを含む請求項5に記載の脱臭抗菌方法。