JP2016108641A - Member made of titanium - Google Patents
Member made of titanium Download PDFInfo
- Publication number
- JP2016108641A JP2016108641A JP2014249899A JP2014249899A JP2016108641A JP 2016108641 A JP2016108641 A JP 2016108641A JP 2014249899 A JP2014249899 A JP 2014249899A JP 2014249899 A JP2014249899 A JP 2014249899A JP 2016108641 A JP2016108641 A JP 2016108641A
- Authority
- JP
- Japan
- Prior art keywords
- diffusion region
- nickel
- titanium
- base material
- amorphous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、チタン材の表面に非晶質クロムめっきを施したものに関する。 The present invention relates to a surface of a titanium material that has been subjected to amorphous chromium plating.
金属製の母材の表面にクロムめっきを施すことは従来から行われている。しかしながら、クロムめっきは硬度が高くなく耐摩耗性という観点では不十分である。かかるクロムめっきは結晶質であるが、非晶質のクロムめっきを施すことも行われている(下記特許文献1参照)。この非晶質クロムめっきによる被膜は硬度が非常に高く、結晶質のクロムめっきに比して耐摩耗性に優れているという特徴がある。 Conventionally, chromium plating is applied to the surface of a metal base material. However, chromium plating is not high in hardness and is insufficient from the viewpoint of wear resistance. Such chrome plating is crystalline, but amorphous chrome plating is also applied (see Patent Document 1 below). This amorphous chrome-plated coating has a very high hardness and is characterized by excellent wear resistance compared to crystalline chrome plating.
そこで、本発明者らは、チタン材を母材としてその表面に非晶質クロムめっきを施すことを試みた。しかしながら、チタン材には非晶質クロムめっきの密着性が良くないということが判明した。 Therefore, the present inventors tried to perform amorphous chromium plating on the surface of a titanium material as a base material. However, it has been found that the adhesion of amorphous chrome plating is not good for titanium materials.
それゆえに本発明は上記従来の問題点に鑑みてなされ、耐摩耗性に優れたチタン製部材を提供することを課題とする。 Therefore, the present invention has been made in view of the above-mentioned conventional problems, and an object thereof is to provide a titanium member having excellent wear resistance.
本発明者らは上記課題を解決すべく鋭意研究を重ねた結果、チタン材の中でも特にチタン合金に着目し、そのチタン合金に種々の前処理を施した後に非晶質クロムめっきを施すことによって耐摩耗性に優れたチタン材が得られることを見出した。 As a result of intensive studies to solve the above problems, the present inventors have focused on titanium alloys among titanium materials, and by applying various pretreatments to the titanium alloys and then applying amorphous chromium plating. It has been found that a titanium material having excellent wear resistance can be obtained.
即ち、本発明に係るチタン製部材は、母材がチタン合金であり、表面には非晶質クロムめっき被膜が形成され、該非晶質クロムめっき被膜の内側には、ニッケルが母材に拡散した拡散領域が存在していることを特徴とする。 That is, in the titanium member according to the present invention, the base material is a titanium alloy, an amorphous chromium plating film is formed on the surface, and nickel diffuses into the base material inside the amorphous chromium plating film. A diffusion region is present.
該構成のチタン製部材は、母材がチタン合金からなり、ニッケルの拡散領域を介して非晶質クロムめっき被膜が形成されているので、非晶質クロムめっき被膜の密着性が高く、耐摩耗性に優れている。 In the titanium member having the above structure, the base material is made of a titanium alloy, and an amorphous chromium plating film is formed through a nickel diffusion region, so that the adhesion of the amorphous chromium plating film is high and wear resistance is increased. Excellent in properties.
かかるチタン製部材は以下のようにして形成することができる。即ち、母材の表面を所定のエッチング液にてエッチングする。完全にα相のみからなるα型のチタン合金である場合を除いて、チタン合金の表面はα相とβ相とがまだら模様に混在した結晶構造となっている。α+β型のチタン合金はもとより、β型のチタン合金であってもα相が存在しており、また、α型のチタン合金であってもニアαとも称されるものではβ相が若干ながら存在している。そこで、そのようにα相とβ相が混在している母材の表面をエッチングすることによって、α相のみを溶かして母材の表面に微細な凹凸を形成することができる。そして、その後、ニッケルめっきを施した後、更に、非晶質クロムめっきを施して、所定温度で熱処理を行う。これにより、母材の表面に非晶質クロムめっき被膜が形成されると共にその内側にはニッケルが母材側(内側)に向けて拡散浸透した拡散領域が形成される。非晶質クロムめっきは炭化クロム(Cr−C)からなり、結晶性のクロムめっきに比して高い硬度が得られるが、チタン材への密着性が問題となる。そこで、母材をチタン合金とし、そのα相をエッチングにて溶解させることで表面に微細な凹凸を形成した上で更に、その上に直接非晶質クロムめっきを施すのではなく、まずはニッケルめっきを施し、その上で非晶質クロムめっきを施すようにする。非晶質クロムめっき後の熱処理によって、ニッケルが母材へと拡散浸透するので、ニッケルめっきの密着性が高く、その上の非晶質クロムめっきの密着性も高くなる。 Such a titanium member can be formed as follows. That is, the surface of the base material is etched with a predetermined etching solution. The surface of the titanium alloy has a crystal structure in which the α phase and the β phase are mixed in a mottled pattern, except in the case of an α-type titanium alloy consisting entirely of the α phase. α-β type titanium alloys as well as β-type titanium alloys have an α phase, and even α-type titanium alloys, which are also called near α, have a slight β phase. doing. Therefore, by etching the surface of the base material in which the α phase and the β phase are mixed, it is possible to melt only the α phase and form fine irregularities on the surface of the base material. Then, after nickel plating, amorphous chrome plating is further applied and heat treatment is performed at a predetermined temperature. Thereby, an amorphous chromium plating film is formed on the surface of the base material, and a diffusion region in which nickel diffuses and penetrates toward the base material side (inside) is formed inside thereof. Amorphous chromium plating is made of chromium carbide (Cr—C) and can provide higher hardness than crystalline chromium plating, but adhesion to a titanium material is a problem. Therefore, the base material is a titanium alloy, and the α phase is dissolved by etching to form fine irregularities on the surface. Further, amorphous chromium plating is not directly applied on the surface, but nickel plating is first performed. And amorphous chrome plating is applied thereon. Since nickel diffuses and penetrates into the base material by the heat treatment after the amorphous chrome plating, the adhesion of the nickel plating is high, and the adhesion of the amorphous chrome plating thereon is also high.
上記構成においては特に、拡散領域として、非晶質クロムめっき被膜の内側に位置し、ニッケルの濃度が相対的に高い第一の拡散領域と、該第一の拡散領域の内側に位置し、ニッケルの濃度が相対的に低い第二の拡散領域とが存在し、第一の拡散領域と第二の拡散領域との境界においてニッケルの濃度がステップ状に変化していることが好ましい。このように拡散領域として二つの領域が存在していると、より一層非晶質クロムめっきの密着性が高くなり、耐摩耗性が向上する。 In the above configuration, in particular, the diffusion region is located inside the amorphous chromium plating film, the first diffusion region having a relatively high nickel concentration, and located inside the first diffusion region. Preferably, there is a second diffusion region having a relatively low concentration of nickel, and the nickel concentration changes stepwise at the boundary between the first diffusion region and the second diffusion region. When two regions exist as diffusion regions in this way, the adhesion of the amorphous chrome plating is further enhanced and the wear resistance is improved.
また、母材はβ型のチタン合金であることが好ましい。母材がβ型のチタン合金であると、冷間加工性が良く、部材の強度も容易に確保できる。しかも、エッチング処理によって表面に微小な凹凸を分散した状態で形成することができ、ニッケルめっきの密着性が高くなって、非晶質クロムめっきの密着性も高くなる。 The base material is preferably a β-type titanium alloy. When the base material is a β-type titanium alloy, the cold workability is good and the strength of the member can be easily secured. Moreover, it can be formed in a state in which minute irregularities are dispersed on the surface by the etching process, the adhesion of nickel plating is increased, and the adhesion of amorphous chrome plating is also increased.
以上のように、本発明に係るチタン製部材にあっては、母材をチタン合金とすると共にニッケルの拡散領域を介して非晶質クロムめっき被膜が形成されているので、非晶質クロムめっき被膜の密着性が高く、耐摩耗性に優れている。 As described above, in the titanium member according to the present invention, the base material is a titanium alloy and the amorphous chromium plating film is formed through the nickel diffusion region. The film has high adhesion and excellent wear resistance.
以下、本発明の一実施形態に係るチタン製部材について図面を参酌しつつ説明する。図1に本実施形態におけるチタン製部材の表面付近の要部断面を模式的に示している。本実施形態におけるチタン製部材は、母材1がチタン合金からなるものであって、部材の表面には非晶質クロムめっき被膜2が形成されているものである。かかるチタン製部材は各種の用途に使用でき、各種の釣り具や自転車部品として好適である。例えば、釣り具としてはリールの部品や、釣竿の釣り糸ガイドに適用できる。釣り糸ガイドでは、釣り糸が摺動する部分であるガイドリングに適用できる。また、釣り糸ガイドにおいてフレームとガイドリングが一体的に形成されている構成では、釣り糸が摺動する部分であるリング部に適用できる。 Hereinafter, a titanium member according to an embodiment of the present invention will be described with reference to the drawings. FIG. 1 schematically shows a cross section of the main part near the surface of a titanium member in the present embodiment. In the titanium member in the present embodiment, the base material 1 is made of a titanium alloy, and an amorphous chromium plating film 2 is formed on the surface of the member. Such titanium members can be used for various applications and are suitable as various fishing gears and bicycle parts. For example, the fishing gear can be applied to reel parts and fishing line guides for fishing rods. The fishing line guide can be applied to a guide ring which is a portion where the fishing line slides. In addition, in the structure in which the frame and the guide ring are integrally formed in the fishing line guide, the structure can be applied to a ring portion that is a portion where the fishing line slides.
母材1は、各種のチタン合金からなる。チタン合金は、α相とβ相が混在しているものであって、主としてα相であって一部にβ相が残留したニアα型(少量のβ安定化元素を添加したα合金)、α+β型、β型が適用できる。ニアα型としては、例えば、Ti−8Al−1Mo−1VやTi−6Al−2Nb−1Ta−0.8Mo等である。α+β型は、ニアα型よりも多量のβ相が残留しており、例えば、Ti−3Al−2.5VやTi−6Al−4V等である。β型は、準安定β型とも称されるものであって、α+β型に比してβ安定化元素が多く、α安定化元素が少ない。β型では、残留β相中に微細な粒でα相が分散して生成しており、従って、β型においてもその表面にはα相とβ相とがまだら模様となって存在している。β型としては、例えば、Ti−15V−3Cr−3Sn−3Alや、Ti−3Al−8V−6Cr−4Zr−4Moや、Ti−10V−2Fe−3Al等があるが、特に、冷間加工性に優れていることからTi−15V−3Cr−3Sn−3Alが好ましい。 The base material 1 is made of various titanium alloys. Titanium alloy is a mixture of α phase and β phase, and is mainly α phase and a near α type (α alloy with a small amount of β stabilizing element added) in which β phase remains in part, α + β type and β type can be applied. Examples of the near α type include Ti-8Al-1Mo-1V and Ti-6Al-2Nb-1Ta-0.8Mo. The α + β type has a larger amount of β phase remaining than the near α type, such as Ti-3Al-2.5V and Ti-6Al-4V. The β type is also called a metastable β type, and has more β stabilizing elements and fewer α stabilizing elements than the α + β type. In the β type, the α phase is dispersed and formed in fine grains in the residual β phase. Therefore, the α phase and the β phase are present in a mottled pattern on the surface of the β type. . Examples of β-type include Ti-15V-3Cr-3Sn-3Al, Ti-3Al-8V-6Cr-4Zr-4Mo, Ti-10V-2Fe-3Al, etc. Ti-15V-3Cr-3Sn-3Al is preferable because it is excellent.
非晶質クロムめっき被膜2は、厚さが1μm以上、好ましくは5μm以上、更に好ましくは10μm以上であって、実用上は50μm以下である。非晶質クロムめっき被膜2は、炭化クロムからなり、非晶質(アモルファス)である。また、その硬度はHv1100〜2000である。 The amorphous chromium plating film 2 has a thickness of 1 μm or more, preferably 5 μm or more, more preferably 10 μm or more, and practically 50 μm or less. The amorphous chromium plating film 2 is made of chromium carbide and is amorphous. Moreover, the hardness is Hv1100-2000.
非晶質クロムめっき被膜2の内側には拡散領域3が存在している。該拡散領域3は、母材1にニッケル(Ni)が拡散浸透した領域である。該拡散領域3は、二つの領域から構成されている。即ち、拡散領域3は、浅い側である第一の拡散領域3aと深い側である第二の拡散領域3bから構成されており、第一の拡散領域3aは非晶質クロムめっき被膜の内側に位置し、第二の拡散領域3bは第一の拡散領域3aの内側に位置している。第一の拡散領域3aは母材1の表面近傍に形成されていて、比較的薄い層状となって母材1の表面に沿って形成されている。第二の拡散領域3bは第一の拡散領域3aの直ぐ内側に第一の拡散領域3aよりも厚く形成されている。尚、拡散領域3の厚さは、例えば非晶質クロムめっき被膜2と同程度の厚さ、あるいはそれよりも厚く、例えば数十μmから数百μmである。第一の拡散領域3aの厚さは例えば非晶質クロムめっき被膜2よりも薄い。第一の拡散領域3aは、ニッケルの濃度が相対的に高い。これに対して第二の拡散領域3bは、ニッケルの濃度が相対的に低い。そして、ニッケルの濃度は、第一の拡散領域3aと第二の拡散領域3bとの境界においてステップ状に変化しており、第二の拡散領域3bにおけるニッケルの濃度は、第一の拡散領域3aにおけるそれよりも一段低くなっている。そして、拡散領域3の内側即ちそれよりも深い母材1の部分には、ニッケルが実質上(含有率1%以下)拡散浸透していない非拡散領域4が存在している。即ち、母材1は非拡散領域4とその外側(表面側)の拡散領域3とを有しており、拡散領域3は母材1の表層を構成しており、その拡散領域3の更に外側に非晶質クロムめっき被膜2が形成されている。 A diffusion region 3 exists inside the amorphous chromium plating film 2. The diffusion region 3 is a region where nickel (Ni) diffuses and penetrates into the base material 1. The diffusion region 3 is composed of two regions. That is, the diffusion region 3 is composed of a first diffusion region 3a on the shallow side and a second diffusion region 3b on the deep side, and the first diffusion region 3a is located inside the amorphous chromium plating film. The second diffusion region 3b is located inside the first diffusion region 3a. The first diffusion region 3 a is formed in the vicinity of the surface of the base material 1 and is formed in a relatively thin layer shape along the surface of the base material 1. The second diffusion region 3b is formed thicker than the first diffusion region 3a immediately inside the first diffusion region 3a. Note that the thickness of the diffusion region 3 is, for example, about the same thickness as the amorphous chromium plating film 2 or thicker, for example, several tens μm to several hundreds μm. The thickness of the first diffusion region 3a is thinner than that of the amorphous chromium plating film 2, for example. The first diffusion region 3a has a relatively high nickel concentration. In contrast, the second diffusion region 3b has a relatively low nickel concentration. The nickel concentration changes stepwise at the boundary between the first diffusion region 3a and the second diffusion region 3b, and the nickel concentration in the second diffusion region 3b is the first diffusion region 3a. It is one step lower than that. In addition, the non-diffusion region 4 in which nickel is substantially not diffused (content 1% or less) is present inside the diffusion region 3, that is, in the portion of the base material 1 deeper than that. That is, the base material 1 has a non-diffusion region 4 and a diffusion region 3 on the outside (surface side). The diffusion region 3 constitutes a surface layer of the base material 1, and is further outside the diffusion region 3. An amorphous chromium plating film 2 is formed on the surface.
図2にチタン製部材のGD−OES分析結果(グロー放電発光分析法)を示している。尚、チタン合金としては、β型のものであり、その中でも特にTi−15V−3Cr−3Sn−3Alとしている。但し、チタン合金に含有している元素であるバナジウム(V)、スズ(Sn)、アルミニウム(Al)についてはその表示を省略している。グラフの横軸は分析深さであって右側に向けて表面から深くなっていく。横軸の単位はμmである。グラフの縦軸は含有する元素の含有率(濃度)であって単位は%である。この図2に示すように、表面から一定の深さまで、実質上クロム(Cr)と炭素(C)のみからなり、クロムと炭素の濃度がそれぞれ略一定となった領域が存在している。この領域が非晶質クロムめっき被膜2である。また、クロムと炭素の濃度がそれぞれ略一定となった領域の内側には、ニッケルが母材1を構成しているチタンに拡散した領域が認められる。この領域が拡散領域3である。 FIG. 2 shows a GD-OES analysis result (glow discharge emission analysis method) of the titanium member. In addition, as a titanium alloy, it is a (beta) type, and it is set as Ti-15V-3Cr-3Sn-3Al especially among them. However, vanadium (V), tin (Sn), and aluminum (Al), which are elements contained in the titanium alloy, are not shown. The horizontal axis of the graph is the analysis depth, which increases from the surface toward the right. The unit of the horizontal axis is μm. The vertical axis of the graph represents the content rate (concentration) of the contained element, and the unit is%. As shown in FIG. 2, there is a region which is substantially made only of chromium (Cr) and carbon (C) from the surface to a certain depth, and the concentrations of chromium and carbon are substantially constant. This region is the amorphous chromium plating film 2. Further, a region where nickel diffuses into titanium constituting the base material 1 is recognized inside the region where the concentrations of chromium and carbon are substantially constant. This region is the diffusion region 3.
図3に、このチタン製部材をFE−EPMA(電界放出型電子線マイクロアナライザ)による元素分析結果の写真を示している。但し、グレースケールにて示しているため、元々のカラー表示ではなくなっている。また、含有する元素のうちクロム(Cr)、ニッケル(Ni)、チタン(Ti)のみを表示している。尚、合計四枚の写真は何れも同じ箇所を示したものであって、下側が表面側(外側)であり上側が内側(深い側)である。左端のものから順にクロム(Cr)、ニッケル(Ni)、チタン(Ti)の分析結果を示しており、最も右側の写真は光学顕微鏡写真である。光学顕微鏡写真において上下方向の中央やや下側に横方向に延びる一筋のラインとして白く写っているところが部材の表面であり、それよりも上側が部材内部である。ニッケルの分析結果を見ると、部材表面のクロムの層(非晶質クロムめっき被膜2)の内側に、ニッケルの元素が集中的に存在している部分が薄い層状となって存在している。この薄い層状の部分は、第一の拡散領域3aであり、チタンとオーバーラップしていることから、ニッケルがチタンに分散浸透していることがわかる。この第一の拡散領域3aは、一番右側の光学顕微鏡写真においても、表面から所定深さ内部に入ったところに薄く層状に写っている。また、ニッケルの分析結果において、第一の拡散領域3aの内側にもニッケルが点状に分散して存在しており、この部分が第二の拡散領域3bであって、ニッケルがチタン内部へと深く拡散浸透していることがわかる。このように第一の拡散領域3aにおいてはニッケルの濃度が高く、第二の拡散領域3bにおいてはニッケルの濃度が低くなっていて、第一の拡散領域3aにおけるニッケルの濃度に対して第二の拡散領域3bのそれは一段ステップ状に低くなっている。 FIG. 3 shows a photograph of elemental analysis results of this titanium member by FE-EPMA (field emission electron beam microanalyzer). However, since it is shown in grayscale, it is no longer the original color display. Of the elements contained, only chromium (Cr), nickel (Ni), and titanium (Ti) are shown. Note that all four photographs show the same part, with the lower side being the front side (outer side) and the upper side being the inner side (deep side). The analysis results of chromium (Cr), nickel (Ni), and titanium (Ti) are shown in order from the leftmost one, and the rightmost photograph is an optical microscope photograph. In the optical micrograph, the surface of the member that appears white as a straight line extending in the horizontal direction slightly below the center in the vertical direction is the surface of the member, and the upper side is the inside of the member. When the analysis result of nickel is seen, the portion where the nickel element is concentrated is present in a thin layer inside the chromium layer (amorphous chromium plating film 2) on the surface of the member. This thin layered portion is the first diffusion region 3a, and since it overlaps with titanium, it can be seen that nickel is dispersed and permeated into titanium. This first diffusion region 3a is also shown in a thin layer in the rightmost optical micrograph at a depth of a predetermined depth from the surface. Further, in the analysis result of nickel, nickel is also dispersed in the form of dots inside the first diffusion region 3a, and this portion is the second diffusion region 3b, and the nickel moves into the titanium. It can be seen that it penetrates deeply. As described above, the nickel concentration is high in the first diffusion region 3a, and the nickel concentration is low in the second diffusion region 3b. The second concentration region has a second concentration relative to the nickel concentration in the first diffusion region 3a. That of the diffusion region 3b is lowered stepwise.
かかるチタン製部材の製造方法の概要について説明すると、まず、母材1の表面を脱脂した後、所定のエッチング液にてエッチングする。尚、脱脂処理の前に例えばショットブラスト等によって表面を粗面にしてもよい。エッチング液は、母材1の材質によって種々調整する。即ち、チタン合金の種類等に応じて適宜調整して、チタン合金の表面におけるα相のみが溶けて母材1の表面に微細な凹凸が形成されるようにする。尚、チタン合金としてβ型のものを使用すれば、表面に微細な凹凸を容易に形成でき、また、分散状態で凹凸を形成できる。その後、ニッケルめっきを施す。ニッケルめっきとしては、特に電気めっきが好ましく、本実施形態におけるチタン製部材は電気めっき処理を行ったものである。電気めっきは密着性が良く、特に部材の表面形状が平面であっても曲面であっても良好な密着性が得られるため好ましい。従って、部材を例えばガイドリングのようなリング状とする場合に適している。 The outline of the method for manufacturing the titanium member will be described. First, the surface of the base material 1 is degreased and then etched with a predetermined etching solution. Note that the surface may be roughened by, for example, shot blasting before degreasing. The etching solution is variously adjusted depending on the material of the base material 1. That is, it is adjusted as appropriate according to the type of titanium alloy, etc., so that only the α phase on the surface of the titanium alloy melts and fine irregularities are formed on the surface of the base material 1. If a β-type titanium alloy is used, fine irregularities can be easily formed on the surface, and irregularities can be formed in a dispersed state. Then, nickel plating is performed. As the nickel plating, electroplating is particularly preferable, and the titanium member in this embodiment is subjected to electroplating treatment. Electroplating has good adhesion, and is particularly preferable because good adhesion can be obtained regardless of whether the surface shape of the member is flat or curved. Therefore, it is suitable when the member is formed in a ring shape such as a guide ring.
その後、非晶質クロムめっきを施す。めっき浴には、シュウ酸やクエン酸、ギ酸等の有機酸を添加するが、特に、ギ酸を使用することが好ましく、凹凸の少ない滑らかな表面が得られる。その後、200℃〜800℃で熱処理を行う。熱処理の時間は例えば数十時間、一例としては50時間とする。尚、熱処理の時間は任意であって更に所望に応じて調整する。この熱処理を行うことによって高い硬度の非晶質クロムめっき被膜2が得られる。 Thereafter, amorphous chrome plating is applied. An organic acid such as oxalic acid, citric acid, and formic acid is added to the plating bath, but it is particularly preferable to use formic acid, and a smooth surface with few irregularities can be obtained. Thereafter, heat treatment is performed at 200 ° C. to 800 ° C. The heat treatment time is, for example, several tens of hours, for example 50 hours. The heat treatment time is arbitrary and further adjusted as desired. By performing this heat treatment, an amorphous chromium plating film 2 having high hardness can be obtained.
更にその後、所定温度で時効を行う。所定温度での時効には二種類あって、上記熱処理終了段階での冷却性能によって異なってくるが、例えば、上記熱処理後に溶体化して時効する場合には、例えば800℃に加熱した後冷却して、例えば300〜600℃で12時間時効を行う。一方、上記熱処理時に溶体化している場合には、例えば300〜600℃で12時間時効を行う。尚、時効の時間も任意であって更に長時間行ってもよい。このように非晶質クロムめっき後の熱処理とその後の更なる熱時効を行うことによって、ニッケルめっきによって母材1の表面に付着したニッケルが母材1の深い部分へと拡散浸透し、非晶質クロムめっき被膜2の内側に拡散領域3が形成される。 Thereafter, aging is performed at a predetermined temperature. There are two types of aging at a predetermined temperature, and it varies depending on the cooling performance at the end of the heat treatment. For example, when the solution is aged after the heat treatment, for example, it is heated to 800 ° C. and then cooled. For example, aging is performed at 300 to 600 ° C. for 12 hours. On the other hand, when the solution is formed during the heat treatment, aging is performed at 300 to 600 ° C. for 12 hours, for example. In addition, the aging time is also arbitrary and may be performed for a longer time. Thus, by performing the heat treatment after the amorphous chrome plating and further thermal aging thereafter, the nickel adhered to the surface of the base material 1 by the nickel plating diffuses and penetrates into the deep part of the base material 1, and is amorphous. A diffusion region 3 is formed inside the quality chromium plating film 2.
以上のようなチタン製部材においては、部材の表面が硬い非晶質クロムめっき被膜2によって覆われており、該非晶質クロムめっき被膜2の内側にはニッケルが母材1に浸透拡散した拡散領域3が形成されているので、非晶質クロムめっき被膜2の母材1への密着性が高く、耐摩耗性に優れた表面被膜が得られる。特に、母材1をチタン合金とすることで、エッチングによって表面に微細な凹凸を形成することができ、特にβ型のチタン合金とすることにより、微細な凹凸を分散して形成することができる。従って、その後のニッケルめっきの密着性が高まり、その結果、非晶質クロムめっきの密着性も高くなって、耐摩耗性に優れることになる。しかも、ニッケルの濃度が相対的に高い外側の第一の拡散領域3aとニッケルの濃度が相対的に低い内側の第二の拡散領域3bとが存在しているので、非晶質クロムめっきの密着性がより一層高くなる。更には、第一の拡散領域3aと第二の拡散領域3bとの境界においてニッケルの濃度がステップ状に変化してニッケルが母材1に深く浸透しているので、非晶質クロムめっきの密着性がより向上する。 In the titanium member as described above, the surface of the member is covered with a hard amorphous chrome plating film 2, and a diffusion region in which nickel penetrates and diffuses into the base material 1 inside the amorphous chrome plating film 2. 3 is formed, it is possible to obtain a surface film having high adhesion to the base material 1 of the amorphous chromium plating film 2 and excellent wear resistance. In particular, when the base material 1 is made of a titanium alloy, fine irregularities can be formed on the surface by etching. In particular, when a β-type titanium alloy is used, fine irregularities can be dispersed and formed. . Therefore, the adhesion of the subsequent nickel plating is increased, and as a result, the adhesion of the amorphous chrome plating is also improved and the wear resistance is excellent. Moreover, since there is an outer first diffusion region 3a having a relatively high nickel concentration and an inner second diffusion region 3b having a relatively low nickel concentration, the adhesion of amorphous chromium plating The nature becomes even higher. Furthermore, since the nickel concentration changes stepwise at the boundary between the first diffusion region 3a and the second diffusion region 3b and the nickel penetrates deep into the base material 1, the adhesion of the amorphous chromium plating More improved.
尚、本実施形態ではニッケルめっきとして電気めっきを行ったが、無電解ニッケルめっきであってもよい。詳細には、無電解ニッケル−リンめっきを施す。無電解ニッケル−リンめっきの中でも特に、リンの含有率が低い低リンタイプで行うことが好ましい。無電解ニッケルめっきは、部材の表面形状が平面である場合に特に好ましい。図4に低リンタイプの無電解ニッケル−リンめっきを行ったチタン製部材のGD−OES分析結果を示す。母材1は同様にβ型のチタン合金(Ti−15V−3Cr−3Sn−3Al)としている。このグラフのように、非晶質クロムめっき被膜2の内側には、母材1にニッケルとリンとが拡散浸透した拡散領域3が形成される。 In this embodiment, electroplating is performed as nickel plating, but electroless nickel plating may be used. Specifically, electroless nickel-phosphorus plating is performed. Among electroless nickel-phosphorus plating, it is particularly preferable to use a low phosphorus type with a low phosphorus content. Electroless nickel plating is particularly preferable when the surface shape of the member is flat. FIG. 4 shows a GD-OES analysis result of a titanium member subjected to low phosphorus type electroless nickel-phosphorus plating. Similarly, the base material 1 is a β-type titanium alloy (Ti-15V-3Cr-3Sn-3Al). As shown in this graph, a diffusion region 3 in which nickel and phosphorus are diffused and penetrated into the base material 1 is formed inside the amorphous chromium plating film 2.
1 母材
2 非晶質クロムめっき被膜
3 拡散領域
3a 第一の拡散領域
3b 第二の拡散領域
4 非拡散領域
DESCRIPTION OF SYMBOLS 1 Base material 2 Amorphous chromium plating film 3 Diffusion area 3a First diffusion area 3b Second diffusion area 4 Non-diffusion area
Claims (3)