JP2015120313A - 光学積層体の製造方法 - Google Patents
光学積層体の製造方法 Download PDFInfo
- Publication number
- JP2015120313A JP2015120313A JP2013266473A JP2013266473A JP2015120313A JP 2015120313 A JP2015120313 A JP 2015120313A JP 2013266473 A JP2013266473 A JP 2013266473A JP 2013266473 A JP2013266473 A JP 2013266473A JP 2015120313 A JP2015120313 A JP 2015120313A
- Authority
- JP
- Japan
- Prior art keywords
- film
- laminate
- optical functional
- optical
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】樹脂基材11と樹脂基材の片側に塗布形成された第1の光学機能層12とを有する積層体10を作製する工程と;積層体の第1の光学機能層に光学機能フィルム21を積層して第2の光学機能層を形成する工程とを含む光学積層体の製造方法。積層体及び光学機能フィルムの少なくとも一方にナーリングが形成された状態で、積層体と光学機能フィルムとを積層する製造方法。
【選択図】図1
Description
1つの実施形態においては、上記積層体および上記光学機能フィルムは長尺状であり、該積層体および該光学機能フィルムを搬送しながら長尺方向を揃えて積層する。1つの実施形態においては、上記ナーリングは、上記積層体および上記光学機能フィルムの少なくとも一方の幅方向の両端部に形成される。1つの実施形態においては、上記積層体および上記光学機能フィルムは異なる幅を有し、上記ナーリングは、該積層体および該光学機能フィルムの重なり合う部分の幅方向の両端部に形成される。
1つの実施形態においては、上記ナーリングの厚みは8μm〜15μmである。
1つの実施形態においては、上記ナーリングは、上記積層体と上記光学機能フィルムとの積層前、積層時、および積層直後から選択される少なくとも1つのタイミングで形成される。
1つの実施形態においては、上記光学機能フィルムの厚みは30μm以下である。
1つの実施形態においては、上記第1の光学機能層は、上記樹脂基材の片側に塗布形成されたポリビニルアルコール系樹脂層を延伸および染色して得られる偏光膜であり、ならびに、上記第2の光学機能層は該偏光膜の保護層である。別の実施形態においては、上記第1の光学機能層は、上記樹脂基材の片側に液晶組成物を塗布し、乾燥または硬化することにより得られる位相差層であり、ならびに、上記第2の光学機能層は、高分子フィルムの延伸フィルムで構成される別の位相差層である。
A−1.偏光膜の作製工程
A−1−1.積層体
図1は、本実施形態の偏光板の製造方法の一例を示す概略図である。図1(a)に示すように、積層体10は、樹脂基材11とPVA系樹脂層12とを有する。積層体10は、長尺状の樹脂基材11にPVA系樹脂層12を形成することにより作製される。PVA系樹脂層12の形成方法としては、任意の適切な方法が採用され得る。好ましくは、樹脂基材11上に、PVA系樹脂を含む塗布液を塗布し、乾燥することにより、PVA系樹脂層12を形成する。
積層体の延伸方法としては、任意の適切な方法が採用され得る。具体的には、固定端延伸でもよいし、自由端延伸(例えば、周速の異なるロール間に積層体を通して一軸延伸する方法)でもよい。好ましくは、自由端延伸である。
上記積層体の染色は、代表的には、PVA系樹脂層に二色性物質(好ましくは、ヨウ素)を吸着させることにより行う。当該吸着方法としては、例えば、ヨウ素を含む染色液にPVA系樹脂層(積層体)を浸漬させる方法、PVA系樹脂層に当該染色液を塗工する方法、当該染色液をPVA系樹脂層に噴霧する方法等が挙げられる。好ましくは、染色液に積層体を浸漬させる方法である。ヨウ素が良好に吸着し得るからである。
上記積層体は、延伸、染色以外に、そのPVA系樹脂層を偏光膜とするための処理が、適宜施され得る。偏光膜とするための処理としては、例えば、不溶化処理、架橋処理、洗浄処理、乾燥処理等が挙げられる。なお、これらの処理の回数、順序等は、特に限定されない。
上記偏光膜は、実質的には、二色性物質が吸着配向されたPVA系樹脂膜である。偏光膜の厚みは、代表的には25μm以下であり、好ましくは15μm以下、より好ましくは10μm以下、さらに好ましくは7μm以下、特に好ましくは5μm以下である。一方、偏光膜の厚みは、好ましくは0.5μm以上、より好ましくは1.5μm以上である。偏光膜は、好ましくは、波長380nm〜780nmのいずれかの波長で吸収二色性を示す。偏光膜の単体透過率は、好ましくは40.0%以上、より好ましくは41.0%以上、さらに好ましくは42.0%以上、特に好ましくは43.0%以上である。偏光膜の偏光度は、好ましくは99.8%以上、より好ましくは99.9%以上、さらに好ましくは99.95%以上である。
上記積層体(PVA系樹脂層)に上記各処理を施した後、図1(b)に示すように、積層体10の偏光膜(PVA系樹脂層:第1の光学機能層)12側に光学機能フィルムを積層して第2の光学機能層21を形成し、光学積層体100を作製する。代表的には、長尺状の積層体に長尺状の光学機能フィルムを搬送しながら、互いの長尺方向を揃えるようにして積層する。
理解を容易にするために、本発明の代表的な実施形態として偏光板の製造方法を上記A項で説明したが、本発明が樹脂基材と塗布層である第1の光学機能層とを有する積層体と光学機能フィルムとの貼り合わせに広く適用され得ることは、当業者に明らかである。すなわち、第1の光学機能層および/または第2の光学機能層の光学特性にかかわらず、本発明が薄い塗布層を有する光学積層体の製造においてシワの発生を良好に抑制し得ることは、当業者に明らかである。以下、本発明の別の実施形態による製造方法が適用される光学積層体の具体例を簡単に説明する。
1.厚み
デジタルマイクロメーター(アンリツ社製、製品名「KC−351C」)を用いて測定した。
2.ガラス転移温度(Tg)
JIS K 7121に準じて測定した。
樹脂基材として、長尺状で、吸水率0.60%、Tg80℃、弾性率2.5GPaの非晶質ポリエチレンテレフタレート(A−PET)フィルム(三菱化学社製、商品名「ノバクリア」、厚み:100μm)を用いた。
樹脂基材の片面に、コロナ処理(処理条件:55W・min/m2)を施し、このコロナ処理面に、ポリビニルアルコール(重合度4200、ケン化度99.2モル%)90重量部およびアセトアセチル変性PVA(重合度1200、アセトアセチル変性度4.6%、ケン化度99.0モル%以上、日本合成化学工業社製、商品名「ゴーセファイマーZ200」)10重量部を含む水溶液を60℃で塗布および乾燥して、厚み10μmのPVA系樹脂層を形成し、積層体を作製した。
次いで、積層体を、液温30℃の不溶化浴(水100重量部に対して、ホウ酸を4重量部配合して得られたホウ酸水溶液)に30秒間浸漬させた(不溶化処理)。
次いで、液温30℃の染色浴(水100重量部に対して、ヨウ素を0.2重量部配合し、ヨウ化カリウムを1.0重量部配合して得られたヨウ素水溶液)に60秒間浸漬させた(染色処理)。
次いで、液温30℃の架橋浴(水100重量部に対して、ヨウ化カリウムを3重量部配合し、ホウ酸を3重量部配合して得られたホウ酸水溶液)に30秒間浸漬させた(架橋処理)。
その後、積層体を、液温70℃のホウ酸水溶液(水100重量部に対して、ホウ酸を4重量部配合し、ヨウ化カリウムを5重量部配合して得られた水溶液)に浸漬させながら、周速の異なるロール間で縦方向(長尺方向)に一軸延伸を行った(水中延伸)。ここで、積層体が破断する直前まで延伸した(最大延伸倍率は6.0倍)。
その後、積層体を液温30℃の洗浄浴(水100重量部に対して、ヨウ化カリウムを4重量部配合して得られた水溶液)に浸漬させた(洗浄処理)。
アクリル系フィルムに対するレーザー照射条件を変えてナーリングの厚みを9μmとしたこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体について、実施例1と同様にして評価を行った。結果を表1に示す。
アクリル系フィルムの代わりにシクロオレフィン系フィルム(JSR社製、商品名「アートン」、厚み25μm)を用いたこと、および、当該フィルムにナーリングを形成しなかったこと以外は実施例1と同様にして光学積層体を作製した。得られた光学積層体について、実施例1と同様にして評価を行った。結果を表1に示す。
シクロオレフィン系フィルムの厚みを18μmとしたこと以外は比較例1と同様にして光学積層体を作製した。得られた光学積層体について、実施例1と同様にして評価を行った。結果を表1に示す。
シクロオレフィン系フィルムの厚みを55μmとしたこと以外は比較例1と同様にして光学積層体を作製した。得られた光学積層体について、実施例1と同様にして評価を行った。結果を表1に示す。
11 樹脂基材
12 ポリビニルアルコール系樹脂層(偏光膜)
21 光学機能フィルム
22 光学機能フィルム
100 光学積層体
Claims (9)
- 樹脂基材と該樹脂基材の片側に塗布形成された第1の光学機能層とを有する積層体を作製する工程と、
該積層体の第1の光学機能層に光学機能フィルムを積層して第2の光学機能層を形成する工程と、を含み、
該積層体および該光学機能フィルムの少なくとも一方にナーリングが形成された状態で、該積層体と該光学機能フィルムとを積層する、
光学積層体の製造方法。 - 前記積層体および前記光学機能フィルムが長尺状であり、該積層体および該光学機能フィルムを搬送しながら長尺方向を揃えて積層する、請求項1に記載の製造方法。
- 前記ナーリングが、前記積層体および前記光学機能フィルムの少なくとも一方の幅方向の両端部に形成される、請求項2に記載の製造方法。
- 前記積層体および前記光学機能フィルムが異なる幅を有し、前記ナーリングが、該積層体および該光学機能フィルムの重なり合う部分の幅方向の両端部に形成される、請求項3に記載の製造方法。
- 前記ナーリングの厚みが8μm〜15μmである、請求項1から4のいずれかに記載の製造方法。
- 前記ナーリングが、前記積層体と前記光学機能フィルムとの積層前、積層時、および積層直後から選択される少なくとも1つのタイミングで形成される、請求項1から5のいずれかに記載の製造方法。
- 前記光学機能フィルムの厚みが30μm以下である、請求項1から6のいずれかに記載の製造方法。
- 前記第1の光学機能層が、前記樹脂基材の片側に塗布形成されたポリビニルアルコール系樹脂層を延伸および染色して得られる偏光膜であり、ならびに、前記第2の光学機能層が該偏光膜の保護層である、請求項1から7のいずれかに記載の製造方法。
- 前記第1の光学機能層が、前記樹脂基材の片側に液晶組成物を塗布し、乾燥または硬化することにより得られる位相差層であり、ならびに、前記第2の光学機能層が、高分子フィルムの延伸フィルムで構成される別の位相差層である、請求項1から7のいずれかに記載の製造方法。