JP2013010817A - Rubber composition and pneumatic tire - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a rubber composition in which high mileage and wet grip performance can be improved well-balancedly, and to provide a pneumatic tire that uses the rubber composition for each member of the tire (especially, tread).SOLUTION: The rubber composition includes: a rubber component containing a copolymer that is obtained by copolymerizing 1,3-butadiene, styrene, and a compound shown by Formula (I) (in the formula, Rdenotes a 1-10C hydrocarbon group), has an amino group at one terminal, has at the other terminal, a functional group containing at least one atom selected from the group consisting of nitrogen, oxygen and silicon, and has 1.0×10-2.5×10of a weight average molecular weight; silica; and a liquid resin having -20 to 20°C of a softening point.

Description

The present invention relates to a rubber composition and a pneumatic tire produced using the rubber composition.

In recent years, from the standpoint of resource saving, energy saving, and environmental protection, social demands for reduction of carbon dioxide emissions have increased. Various countermeasures such as reducing the weight of automobiles and using electric energy have been studied for the purpose of reducing carbon dioxide emissions from automobiles.

As a common problem for automobiles, it is necessary to improve fuel efficiency by improving the rolling resistance of tires, and further, there is an increasing demand for automobiles to improve safety during driving. The fuel efficiency and safety of these automobiles depend largely on the performance of the tires used, and the demand for improvements in fuel economy, wet grip performance, handling stability, and durability has been increasing for automobile tires. Yes. These tire characteristics depend on various factors such as the structure and materials used of the tire, but in particular, greatly depend on the performance of the rubber composition used for the tread portion in contact with the road surface. For this reason, many technical improvements of rubber compositions for tires have been studied and proposed and put into practical use.

For example, the tire tread rubber is required to have low hysteresis loss for improving fuel efficiency and high wet skid resistance for improving wet grip performance. However, the relationship between low hysteresis loss and high wet skid resistance is contradictory, and it is difficult to solve the problem with only one performance improvement. A typical technique for improving the rubber composition for tires is to improve the raw materials used, improving the structure of the raw rubber typified by styrene butadiene rubber and butadiene rubber, reinforcing fillers such as carbon black and silica, Improvements in the structure and composition of vulcanizing agents and plasticizers have been made.

As a method for improving fuel economy and wet grip performance in a well-balanced manner, there is a method using silica as a filler. Silica has strong self-aggregation property and there is room for improvement in that it is difficult to disperse. In Patent Document 1, a styrene butadiene rubber terminal-modified with a specific compound containing a nitrogen atom and a silicon atom and an aliphatic carboxylic acid zinc salt are blended, and a rubber composition excellent in fuel efficiency and wet grip performance is obtained. Although a method for obtaining an object is described, provision of other methods is also sought.

JP 2010-111754 A

The present invention solves the above-mentioned problems and provides a rubber composition capable of improving fuel economy and wet grip performance in a well-balanced manner, and a pneumatic tire using the rubber composition for each member (particularly, tread) of the tire. For the purpose.

（式中、Ｒ^１は、炭素数が１〜１０の炭化水素基を表す。） The present invention is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by the following formula (I), having an amino group at one end and nitrogen, oxygen and silicon at the other end. A rubber component containing a copolymer having a functional group containing at least one atom selected from the group consisting of a weight average molecular weight of 1.0 × 10 ^{5 to} 2.5 × 10 ⁶ , silica, and a softening point The present invention relates to a rubber composition containing a liquid resin at -20 to 20 ° C.

(In the formula, R ¹ represents a hydrocarbon group having 1 to 10 carbon atoms.)

The functional group is preferably an alkoxysilyl group, and more preferably an alkoxysilyl group and an amino group.

（式中、Ｒ^１１は、炭素数が２〜５０の２価の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） The amino group at one end is preferably an alkylamino group or a group represented by the following formula (II).

(In the formula, R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms, and may have a nitrogen atom or an oxygen atom.)

（式中、Ｒ^１２〜Ｒ^１９は、同一又は異なって、水素原子、又は炭素数が１〜５の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） The group represented by the formula (II) is preferably a group represented by the following formula (III).

(In formula, R < ¹² > -R < ¹⁹ > is the same or different, represents a hydrogen atom or a C1-C5 hydrocarbon group, and may have a nitrogen atom and an oxygen atom.)

It is preferable to have an isoprene unit together with an amino group at the one end.

In the copolymer, the content of the compound represented by the formula (I) is preferably 0.05 to 35% by mass.

The above copolymer is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by the above formula (I) using a compound having a lithium atom and an amino group as a polymerization initiator, and then, at the polymerization terminal, nitrogen, oxygen And a material obtained by modification with a modifier having a functional group containing at least one atom selected from the group consisting of silicon and silicon.

（式中、Ｒ^２１、Ｒ^２２及びＲ^２３は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基、メルカプト基又はこれらの誘導体を表す。Ｒ^２４及びＲ^２５は、同一若しくは異なって、水素原子又はアルキル基を表す。ｎは整数を表す。）

（式中、Ｒ^２６、Ｒ^２７及びＲ^２８は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基、メルカプト基又はこれらの誘導体を表す。Ｒ^２９は、環状エーテル基を表す。ｐ及びｑは整数を表す。）

（式中、Ｒ^３０〜Ｒ^３３は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基、メルカプト基又はこれらの誘導体を表す。） The modifying agent is preferably a compound represented by the following formula (IV), the following formula (V), or the following formula (VI).

(Wherein R ²¹ , R ²² and R ²³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group, or a derivative thereof. R ²⁴ and R ²⁵ are the same or different. And represents a hydrogen atom or an alkyl group, and n represents an integer.)

(Wherein R ²⁶ , R ²⁷ and R ²⁸ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group or a derivative thereof. R ²⁹ represents a cyclic ether group. p and q represent integers.)

(In the formula, R ^{30 to} R ³³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group, or a derivative thereof.)

（式中、Ｒ^１１は、炭素数が２〜５０の２価の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） The polymerization initiator preferably has an alkylamino group or a group represented by the following formula (II).

(In the formula, R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms, and may have a nitrogen atom or an oxygen atom.)

（式中、Ｒ^１２〜Ｒ^１９は、同一又は異なって、水素原子、又は炭素数が１〜５の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） The group represented by the formula (II) is preferably a group represented by the following formula (III).

(In formula, R < ¹² > -R < ¹⁹ > is the same or different, represents a hydrogen atom or a C1-C5 hydrocarbon group, and may have a nitrogen atom and an oxygen atom.)

It is preferable that the polymerization initiator has an isoprene unit.

The liquid resin is preferably at least one selected from the group consisting of a liquid coumarone indene resin, a liquid indene resin, and a liquid α-methylstyrene resin.

In 100% by mass of the rubber component, the content of the copolymer is preferably 5% by mass or more.

It is preferable to contain 5-150 mass parts of silica with respect to 100 mass parts of said rubber components.

It is preferable that 3-40 mass parts of liquid resins are included with respect to 100 mass parts of the rubber components.

The rubber composition is preferably used as a rubber composition for tire treads.

The present invention also relates to a pneumatic tire produced using the rubber composition.

According to the present invention, it is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by the following formula (I), having an amino group at one end, nitrogen, oxygen and A rubber component containing a copolymer having a functional group containing at least one atom selected from the group consisting of silicon and having a weight average molecular weight within a specific range, silica, and a liquid resin having a specific softening point; Since the rubber composition contains the fuel composition, the fuel economy and wet grip performance can be improved in a well-balanced manner. By using the rubber composition for each member of the tire (particularly, the tread), a pneumatic tire excellent in the above performance can be obtained. Can be provided.

（式中、Ｒ^１は、炭素数が１〜１０の炭化水素基を表す。） The rubber composition of the present invention is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by the following formula (I), has an amino group at one end, nitrogen at the other end, A rubber component comprising a copolymer having a weight average molecular weight of 1.0 × 10 ^{5 to} 2.5 × 10 ⁶ having a functional group containing at least one atom selected from the group consisting of oxygen and silicon; and silica And a liquid resin having a softening point of -20 to 20 ° C.

(In the formula, R ¹ represents a hydrocarbon group having 1 to 10 carbon atoms.)

In the present invention, low fuel consumption and wet grip performance (particularly low fuel consumption) can be synergistically improved by using the copolymer, silica, and a liquid resin having a specific softening point.

[Rubber component]
<Copolymer>
In the present specification, the “copolymer” is described as a concept included in the rubber component.
Since the main chain of the copolymer is modified with the compound represented by the above formula (I), the interaction between the compound (particularly the oxygen atom contained in the compound) and the filler occurs, and the filler The dispersibility of the polymer is improved and the movement of the copolymer is restricted. As a result, hysteresis loss can be reduced, fuel efficiency can be improved, and good wet grip performance can be obtained. Further, since the copolymer has an amino group at one end and the functional group at the other end, interaction with the filler occurs at both end portions of the copolymer, and the dispersibility of the filler is reduced. As it improves, the movement of the copolymer is constrained. As a result, hysteresis loss can be reduced, fuel efficiency can be improved, and good wet grip performance can be obtained. And in the said copolymer which combined the structural unit based on the compound represented by the said Formula (I), the amino group which has one terminal, and the said functional group which has the other terminal, low fuel consumption, wet grip performance Can improve synergistically.
Usually, even when a functional group is further added to the terminal of a polymer having a functional group in the main chain (main chain modified polymer) (when the main chain terminal modified polymer is used), the above performance is improved. Can not be said in general. This is because the affinity with the filler varies depending on the type of functional group, and the combination of functional groups is very important in order to improve the performance suitably. In the present invention, since the combination of the structural unit based on the compound represented by the above formula (I), the amino group at one end, and the functional group at the other end is very good, fuel efficiency, wet It is estimated that the grip performance can be improved synergistically.

In the above formula (I), R ¹ represents a hydrocarbon group having 1 to 10 carbon atoms. If the carbon number exceeds 10, the cost tends to be high. Further, there is a tendency that the fuel efficiency and wet grip performance cannot be sufficiently improved. The number of carbon atoms is preferably 1-8, more preferably 1-6, and still more preferably 1-3, because the resulting polymer is highly effective in reducing fuel consumption and wet grip performance.

Examples of the hydrocarbon group represented by R ¹ include a monovalent aliphatic hydrocarbon group such as an alkyl group, and a monovalent aromatic hydrocarbon group such as an aryl group. R ¹ is preferably an alkyl group, more preferably a methyl group or a tert-butyl group, from the viewpoint that the resulting polymer is highly effective in improving fuel economy and wet grip performance.

（上記式（Ｉ−Ｉ）中のＲ^１は、上記式（Ｉ）中のＲ^１と同様である。） In addition, the compound represented by the following formula (I-I) among the compounds represented by the formula (I) among the compounds represented by the formula (I) is highly effective in improving fuel economy and wet grip performance due to the obtained copolymer. preferable.

^{(R 1} in the formula (I-I) is the same as ^{R 1} in the formula (I).)

Examples of the compound represented by the formula (I) include p-methoxystyrene, p-ethoxystyrene, p- (n-propoxy) styrene, p- (tert-butoxy) styrene, m-methoxystyrene, and the like. . These may be used alone or in combination of two or more.

The content of the compound represented by the above formula (I) in the copolymer is preferably 0.05% by mass or more, more preferably 0.1% by mass or more, and further preferably 0.3% by mass or more. Moreover, it is preferably 35% by mass or less, more preferably 20% by mass or less, further preferably 10% by mass or less, particularly preferably 5% by mass or less, and most preferably 2% by mass or less. If it is less than 0.05% by mass, it is difficult to obtain an effect of improving fuel economy and wet grip performance, while if it exceeds 35% by mass, the cost tends to be high.

The styrene content in the copolymer is preferably 2% by mass or more, more preferably 5% by mass or more, still more preferably 10% by mass or more, particularly preferably 15% by mass or more, and preferably 50% by mass. Hereinafter, it is more preferably 30% by mass or less, further preferably 25% by mass or less, and particularly preferably 22% by mass or less. If it is less than 2% by mass, the wet grip performance tends to deteriorate, whereas if it exceeds 50% by mass, the fuel efficiency tends to deteriorate.

The content of 1,3-butadiene in the copolymer is not particularly limited, and may be appropriately adjusted according to the content of other components, but is preferably 15% by mass or more, more preferably 20% by mass or more, More preferably, it is 60 mass% or more, Preferably it is 97 mass% or less, More preferably, it is 85 mass% or less, More preferably, it is 80 mass% or less. If it is less than 15% by mass, the wet grip performance tends to deteriorate, whereas if it exceeds 97% by mass, the fuel efficiency tends to deteriorate.

The content of the compound represented by the formula (I), 1,3-butadiene and styrene in the copolymer can be measured by the method of Examples described later.

The amino group (primary amino group, secondary amino group, tertiary amino group) at one end may be an acyclic amino group or a cyclic amino group.

Examples of the acyclic amine constituting the acyclic amino group include 1,1-dimethylpropylamine, 1,2-dimethylpropylamine, 2,2-dimethylpropylamine, 2-ethylbutylamine, pentylamine, 2,2 -Monoalkylamines such as dimethylbutylamine, hexylamine, cyclohexylamine, octylamine, 2-ethylhexylamine, isodecylamine, dimethylamine, methylisobutylamine, methyl (t-butyl) amine, methylpentylamine, methylhexylamine Methyl (2-ethylhexyl) amine, methyloctylamine, methylnonylamine, methylisodecylamine, diethylamine, ethylpropylamine, ethylisopropylamine, ethylbutylamine, ethylisobutylamine, Tyl (t-butyl) amine, ethylpentylamine, ethylhexylamine, ethyl (2-ethylhexyl) amine, ethyloctylamine, dipropylamine, diisopropylamine, propylbutylamine, propylisobutylamine, propyl (t-butyl) amine, propyl Pentylamine, propylhexylamine, propyl (2-ethylhexyl) amine, propyloctylamine, isopropylbutylamine, isopropylisobutylamine, isopropyl (t-butyl) amine, isopropylpentylamine, isopropylhexylamine, isopropyl (2-ethylhexyl) amine, Isopropyloctylamine, dibutylamine, diisobutylamine, di-t-butylamine, butylpentylamine, dipentylamine , And the like dialkylamine and laurylamine methylbutylamine including dicyclohexylamine. By removing a hydrogen atom bonded to a nitrogen atom of these acyclic amines, a non-cyclic amino group is formed.

As a non-cyclic amino group, when combined with a structural unit based on the compound represented by the above formula (I) and the above functional group at the other end, fuel economy and wet grip performance can be improved more synergistically. Therefore, an alkylamino group (a group in which a hydrogen atom bonded to a nitrogen atom of a monoalkylamine or dialkylamine is removed) is preferable, and a dialkylamino group (a hydrogen bonded to a nitrogen atom of a dialkylamine) A group from which an atom is eliminated is more preferred. In addition, 1-10 are preferable and, as for carbon number of the alkyl group which an alkylamino group and a dialkylamino group have, 1-3 are more preferable.

Examples of the cyclic amine constituting the cyclic amino group include aziridine, 2-methylaziridine, 2-ethylaziridine, a compound having a pyrrolidine ring (pyrrolidine, 2-methylpyrrolidine, 2-ethylpyrrolidine, 2-pyrrolidone, succinimide). ), Piperidine, 2-methylpiperidine, 3,5-dimethylpiperidine, 2-ethylpiperidine, 4-piperidinopiperidine, 2-methyl-4-pyrrolidinopiperidine, 1-methylpiperazine, 1-methyl-3-ethyl Piperazine morpholine, 2-methylmorpholine, 3,5-dimethylmorpholine, thiomorpholine, 3-pyrroline, 2,5-dimethyl-3-pyrroline, 2-phenyl-2-pyrroline, pyrazoline, 2-methylimidazole 2-ethyl-4-methylimidazole, 2 Phenyl imidazole, pyrazole, pyrazole carboxylic acid, alpha-pyridone, .gamma.-pyridone, aniline, 3-methylaniline, N- methyl aniline, N- isopropyl aniline. A cyclic amino group is formed by elimination of a hydrogen atom bonded to a nitrogen atom of these cyclic amines.

（式中、Ｒ^１１は、炭素数が２〜５０の２価の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） As the cyclic amino group, when combined with the structural unit based on the compound represented by the above formula (I) and the above functional group at the other end, the fuel economy and wet grip performance can be improved more synergistically. For the reason, a group represented by the following formula (II) is preferable.

(In the formula, R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms, and may have a nitrogen atom or an oxygen atom.)

R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms (preferably 2 to 10, more preferably 3 to 5).
Examples of the hydrocarbon group include alkylene groups having 2 to 10 carbon atoms, alkenylene groups having 2 to 10 carbon atoms, 2 to 10 alkynylene groups, and arylene groups having 6 to 10 carbon atoms. Of these, an alkylene group is preferable.

（式中、Ｒ^１２〜Ｒ^１９は、同一又は異なって、水素原子、又は炭素数が１〜５の炭化水素基を表し、窒素原子、酸素原子を有してもよい。） Of the groups represented by the above formula (II), groups represented by the following formula (III) are preferred.

(In formula, R < ¹² > -R < ¹⁹ > is the same or different, represents a hydrogen atom or a C1-C5 hydrocarbon group, and may have a nitrogen atom and an oxygen atom.)

Examples of the hydrocarbon group having 1 to 5 (preferably 1 to 3) carbon atoms of R ^{12 to} R ¹⁹ include the same groups as the hydrocarbon group represented by R ¹ . Of these, an alkyl group is preferable, and a methyl group and an ethyl group are more preferable.

As R < ¹² > -R < ¹⁹ >, a hydrogen atom is preferable and it is more preferable that all of R < ¹² > -R < ¹⁹ > are hydrogen atoms.

（式中、ｓは、１〜１００（好ましくは１〜５０、より好ましくは１〜１０、更に好ましくは１〜５）の整数を表す。）

（式中、ｓは、１〜１００（好ましくは１〜５０、より好ましくは１〜１０、更に好ましくは１〜５）の整数を表す。） One terminal preferably has an isoprene unit (unit represented by the following formula (VII)) together with the amino group. Thereby, when it combines with the structural unit based on the compound represented by the said Formula (I), and the said functional group which has the other terminal, low-fuel-consumption property and wet grip performance can be improved more synergistically. In particular, it is more preferable to have an isoprene unit together with an alkylamino group, more preferably an isoprene unit together with a dialkylamino group, and for example, a group represented by the formula (A) is preferable.

(In the formula, s represents an integer of 1 to 100 (preferably 1 to 50, more preferably 1 to 10, more preferably 1 to 5).)

(In the formula, s represents an integer of 1 to 100 (preferably 1 to 50, more preferably 1 to 10, more preferably 1 to 5).)

On the other hand, examples of the functional group containing at least one atom selected from the group consisting of nitrogen, oxygen and silicon at the other end include an amino group, an amide group, an alkoxysilyl group, an isocyanate group, an imino group, and an imidazole. Group, urea group, ether group, carbonyl group, carboxyl group, hydroxyl group, nitrile group, pyridyl group and the like.

The functional group at the other end is synergistic in terms of fuel efficiency and wet grip performance when combined with a structural unit based on the compound represented by formula (I) and an amino group at one end. From the reason that it can be improved, an alkoxysilyl group, an amino group, and an ether group are preferable, and it is more preferable to have both an alkoxysilyl group and an amino group.

Examples of the amino group include the same groups as the amino group at one end described above. Of these, an alkylamino group is preferable, and a dialkylamino group is more preferable. In addition, 1-10 are preferable and, as for carbon number of the alkyl group which an alkylamino group and a dialkylamino group have, 1-3 are more preferable.

Examples of the alkoxysilyl group include a methoxysilyl group, an ethoxysilyl group, a propoxysilyl group, and a butoxysilyl group. 1-10 are preferable and, as for carbon number of the alkoxy group which an alkoxy silyl group has, 1-3 are more preferable.

<Method for producing copolymer>
For example, the copolymer of the present invention is prepared by copolymerizing 1,3-butadiene, styrene, and a compound represented by the above formula (I) with a compound having a lithium atom and an amino group as a polymerization initiator, and then polymerizing terminals. Can be produced by modifying with a modifier having a functional group containing at least one atom selected from the group consisting of nitrogen, oxygen and silicon. Specifically, it can be produced by the following production method.

(Polymerization method)
There is no particular limitation on the polymerization method when copolymerizing monomer components such as styrene, 1,3-butadiene and the compound represented by the above formula (I), and there are no solution polymerization method, gas phase polymerization method and bulk polymerization method. Any of them can be used, but the solution polymerization method is particularly preferable from the viewpoint of the stability of the compound represented by the formula (I). Moreover, any of a batch type and a continuous type may be sufficient as the superposition | polymerization form.

When the solution polymerization method is used, the monomer concentration in the solution (total of styrene, 1,3-butadiene, compounds represented by the formula (I), etc.) is preferably 5% by mass or more, more preferably 10%. It is at least mass%. When the monomer concentration in the solution is less than 5% by mass, the amount of the copolymer obtained is small and the cost tends to be high. The monomer concentration in the solution is preferably 50% by mass or less, more preferably 30% by mass or less. If the monomer concentration in the solution exceeds 50% by mass, the solution viscosity becomes too high, stirring becomes difficult, and polymerization tends to be difficult.

(Polymerization initiator in anionic polymerization)
When anionic polymerization is performed, it is preferable to use a compound having a lithium atom and an amino group as a polymerization initiator. Thereby, a conjugated diene polymer (living polymer) having an amino group at the polymerization initiation terminal and the other terminal being a polymerization active site is obtained.

As the amino group possessed by the polymerization initiator (compound having a lithium atom and an amino group), since the amino group remains as it is at the polymerization initiation terminal, the same groups as the acyclic amino group and the cyclic amino group described above Is preferred. The preferred embodiment is also the same.

The compound having a lithium atom and an amino group can be obtained, for example, by reacting a lithium compound with a compound having an amino group (for example, a lithium amide compound).

Although there is no restriction | limiting in particular as a lithium compound, Hydrocarbyl lithium is used preferably. As the hydrocarbyl lithium, those having a hydrocarbyl group having 2 to 20 carbon atoms are preferable, for example, ethyl lithium, n-propyl lithium, isopropyl lithium, n-butyl lithium, sec-butyl lithium, tert-octyl lithium, n-decyl lithium. , Phenyl lithium, 2-naphthyl lithium, 2-butyl-phenyl lithium, 4-phenyl-butyl lithium, cyclohexyl lithium, cyclopentyl lithium, reaction products of diisopropenylbenzene and butyl lithium, and the like. Of these, n-butyllithium is particularly preferred.

As the compound having an amino group, the amino group remains at the polymerization initiation terminal. Therefore, the acyclic amine constituting the above-mentioned acyclic amino group, the cyclic amine constituting the cyclic amino group (particularly, the pyrrolidine ring is formed). The compound similar to the compound having () can be preferably used. Therefore, the compound having an amino group is preferably a compound having an alkylamino group (monoalkylamine or dialkylamine), and more preferably a compound having a dialkylamino group (dialkylamine). In addition, the preferable carbon number of the alkyl group which an alkylamino group and a dialkylamino group have is the same as that of the case of the above-mentioned acyclic amino group.

Moreover, as a compound which has an amino group, the compound which has group represented by the said Formula (II) is preferable, and the compound which has group represented by the said Formula (III) is more preferable. The preferred embodiment of the group represented by the above formula (II) and the group represented by the above formula (III) is the same as in the case of the above-mentioned cyclic amino group.

The conditions for reacting the lithium compound and the compound having an amino group are not particularly limited. For example, the lithium compound and the compound having an amino group are dissolved in a hydrocarbon solvent, and the reaction temperature is 0 to 80 ° C. What is necessary is just to make it react for -1 hour. The molar ratio of the lithium compound to be used and the compound having an amino group (lithium compound / compound having an amino group) is not particularly limited, but may be, for example, 0.8 to 1.5.

The hydrocarbon solvent used in the reaction is not particularly limited, but preferably has 3 to 8 carbon atoms, such as propane, n-butane, isobutane, n-pentane, isopentane, n-hexane, cyclohexane, propene, Examples thereof include 1-butene, isobutene, trans-2-butene, cis-2-butene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, benzene, toluene, xylene, and ethylbenzene. These may be used alone or in combination of two or more.

The compound having a lithium atom and an amino group (for example, a lithium amide compound) may be obtained by reacting a lithium compound with a compound having an amino group, or a commercially available product may be used. When reacting a lithium compound with a compound having an amino group, it may be allowed to react in advance before adding the monomer component, and the lithium compound and the compound having an amino group are reacted in the presence of the monomer component. Also good. Even if the monomer component is present, the compound having an amino group is more reactive, so that the reaction between the lithium compound and the compound having an amino group proceeds preferentially.

Examples of the lithium amide compound include lithium hexamethylene imide, lithium pyrrolidide, lithium piperide, lithium heptamethylene imide, lithium dodecamethylene imide, lithium dimethyl amide, lithium diethyl amide, lithium dibutyl amide, lithium dipropyl amide, and lithium di Putylamide, lithium dihexylamide, lithium dioctylamide, lithium di-2-ethylhexylamide, lithium didecylamide, lithium-N-methylpiverazide, lithium ethylpropylamide, lithium ethylbutyramide, lithium ethylbenzylamide, lithium methylphenethylamide, below Examples include compounds represented by the formula. Of these, lithium pyrrolidide, lithium dimethylamide, and lithium diethylamide are preferable.

（式中、ｓは、１〜１００（好ましくは１〜５０、より好ましくは１〜１０、更に好ましくは１〜５）の整数を表す。） Moreover, the compound which has an isoprene unit (unit represented by following formula (VII)) with an amino group as a compound which has a lithium atom and an amino group can also be used conveniently. Thereby, when it combines with the structural unit based on the compound represented by the said Formula (I), and the said functional group which has the other terminal, low-fuel-consumption property and wet grip performance can be improved more synergistically.

(In the formula, s represents an integer of 1 to 100 (preferably 1 to 50, more preferably 1 to 10, more preferably 1 to 5).)

（式中、ｓは、１〜１００（好ましくは１〜５０、より好ましくは１〜１０、更に好ましくは１〜５）の整数を表す。） Especially, it is more preferable to have the said isoprene unit with an alkylamino group, and it is still more preferable to have the said isoprene unit with a dialkylamino group, for example, the compound represented by a following formula is suitable. In addition, the compound of s = 2 among the compounds represented by the following formula is sold under the trade name AI-200 by FMC Lithium.

(In the formula, s represents an integer of 1 to 100 (preferably 1 to 50, more preferably 1 to 10, more preferably 1 to 5).)

(Method of anionic polymerization)
There is no restriction | limiting in particular as a method of manufacturing a copolymer by anionic polymerization using the said compound which has a lithium atom and an amino group as a polymerization initiator, A conventionally well-known method can be used. Specifically, in an organic solvent inert to the reaction, for example, a hydrocarbon solvent such as an aliphatic, alicyclic or aromatic hydrocarbon compound, the compound having the lithium atom and amino group is used as a polymerization initiator, If necessary, styrene, 1,3-butadiene, a compound represented by the formula (I), and the like may be anionically polymerized in the presence of a randomizer. In addition, after anionic polymerization, you may add a well-known anti-aging agent and alcohol etc. for the purpose of stopping a polymerization reaction as needed.

(Hydrocarbon solvents in anionic polymerization)
The hydrocarbon solvent is preferably one having 3 to 8 carbon atoms, such as propane, n-butane, isobutane, n-pentane, isopentane, n-hexane, cyclohexane, propene, 1-butene, isobutene and trans-2. -Butene, cis-2-butene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, benzene, toluene, xylene, ethylbenzene and the like. These may be used alone or in combination of two or more.

(Randomizer in anionic polymerization)
The randomizer is a microstructure control of a conjugated diene moiety in a copolymer (for example, an increase in 1,2-bonds in butadiene, etc.) and a control of the composition distribution of monomer units in the copolymer (for example, It is a compound having an action such as a butadiene unit, randomization of a styrene unit, etc. in a butadiene-styrene copolymer. The randomizer is not particularly limited, and any known compound generally used as a conventional randomizer can be used. For example, dimethoxybenzene, tetrahydrofuran, dimethoxyethane, diethylene glycol dibutyl ether, diethylene glycol dimethyl ether, bistetrahydrofurylpropane, triethylamine, pyridine, N-methylmorpholine, N, N, N ′, N′-tetramethylethylenediamine, 1,2-di Examples include ethers such as piperidinoethane and tertiary amines. Further, potassium salts such as potassium-t-amylate and potassium-t-butoxide, and sodium salts such as sodium-t-amylate can also be used.

The amount of randomizer used is preferably 0.01 molar equivalents or more, more preferably 0.05 molar equivalents or more per mole of the polymerization initiator. If the amount of randomizer used is less than 0.01 molar equivalent, the effect of addition tends to be small and it tends to be difficult to randomize. The amount of randomizer used is preferably 1000 molar equivalents or less, more preferably 500 molar equivalents or less per mole of the polymerization initiator. When the amount of the randomizer used exceeds 1000 molar equivalents, the monomer reaction rate changes greatly, and conversely, it tends to be difficult to randomize.

It does not specifically limit as a modification | denaturation method with the said modifier | denaturant, A well-known method can be used. For example, after synthesizing a copolymer whose main chain is modified by anionic polymerization, the anion at the end of the copolymer reacts with the functional group of the modifying agent by bringing the copolymer into contact with the modifying agent. The terminal end of the copolymer is modified. The amount of the modifier to be reacted is usually 0.01 to 10 parts by mass with respect to 100 parts by mass of the copolymer.

<Modifier>
Examples of the modifier include 3-glycidoxypropyltrimethoxysilane, (3-triethoxysilylpropyl) tetrasulfide, 1- (4-N, Ndimethylaminophenyl) -1-phenylethylene, 1,1- Dimethoxytrimethylamine, 1,2-bis (trichlorosilyl) ethane, 1,3,5-tris (3-triethoxysilylpropyl) isocyanurate, 1,3,5-tris (3-trimethoxysilylpropyl) isocyanurate, 1,3-dimethyl-2-imidazolidinone, 1,3-propanediamine, 1,4-diaminobutane, 1- [3- (triethoxysilyl) propyl] -4,5-dihydroimidazole, 1-glycidyl- 4- (2-pyridyl) piperazine, 1-glycidyl-4-phenylpiperazine, 1-glycidyl -4-methylpiverazine, 1-glycidyl-4-methylhomopiverazine, 1-glycidylhexamethyleneimine, 11-aminoundecyltriethoxysilane, 11-aminoundecyltrimethoxysilane, 1-benzyl-4-glycidylpiperazine 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 2- (4-morpholinodithio) benzothiazole, 2- (6-aminoethyl) -3-aminopropyltrimethoxysilane, 2- (triethoxy Silylethyl) pyridine, 2- (trimethoxysilylethyl) pyridine, 2- (2-pyridylethyl) thiopropyltrimethoxysilane, 2- (4-pyridylethyl) thioprovir trimethoxysilane, 2,2-diethoxy- 1,6-diaza-2-silacyclooctane, 2 2-dimethoxy-1,6-diaza-2-silacyclooctane, 2,3-cyclo-1,4-naphthoquinone, 2,4-dinitrobenzenesulfonyl chloride, 2,4-tolylene diisocyanate, 2- (4 -Pyridylethyl) triethoxysilane, 2- (4-pyridylethyl) trimethoxysilane, 2-cyanoethyltriethoxysilane, 2-tributylstannyl-1,3-butadiene, 2- (trimethoxysilylethyl) pyridine, 2 -Vinylpyridine, 2- (4-pyridylethyl) triethoxysilane, 2- (4-pyridylethyl) trimethoxysilane, 2-laurylthioethylphenylketone, 3- (1-hexamethyleneimino) propyl (triethoxy) silane , 3- (1,3-Dimethylbutylidene) aminopropyltriethoxysilane Lan, 3- (1,3-dimethylbutylidene) aminopropyltrimethoxysilane, 3- (2-aminoethylaminopropyl) trimethoxysilane, 3- (m-aminophenoxy) propyltrimethoxysilane, 3- (N , N-dimethylamino) propyltriethoxysilane, 3- (N, N-dimethylamino) propyltrimethoxysilane, 3- (N-methylamino) propyltriethoxysilane, 3- (N-methylamino) propyltrimethoxy Silane, 3- (N-allylamino) propyltrimethoxysilane, 3,4-diaminobenzoic acid, 3-aminopropyldimethylethoxysilane, 3-aminopropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyl Tris (methoxydiethoxy) silane, 3-amino Propyldiisopropylethoxysilane, 3-isocyanatopropyltriethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3-diethylaminopropyltrimethoxysilane 3-diethoxy (methyl) silylpropyl succinic anhydride, 3- (N, N-diethylaminopropyl) triethoxysilane, 3- (N, N-diethylaminopropyl) trimethoxysilane, 3- (N, N-dimethylamino) Propyl) diethoxymethylsilane, 3- (N, N-dimethylaminopropyl) triethoxysilane, 3- (N, N-dimethylaminopropyl) trimethoxysilane, 3-triethoxysilylpropyl succinic anhydride, 3-tri Toxisilylpropyl acetic anhydride, 3-triphenoxysilylpropyl succinic anhydride, 3-triphenoxysilylpropyl acetic anhydride, 3-trimethoxysilylpropylbenzothiazole tetrasulfide, 3-hexamethyleneiminopropyltriethoxysilane, 3-mercaptopropyl Trimethoxysilane, (3-triethoxysilylpropyl) diethylenetriamine, (3-trimethoxysilylpropyl) diethylenetriamine, 4,4′-bis (diethylamino) benzophenone, 4,4′-bis (dimethylamino) benzophenone, 4′- (Imidazol-1-yl) -acetophenone, 4- [3- (N, N-diglycidylamino) propyl] morpholine, 4-glycidyl-2,2,6,6-tetramethylpiberidinyloxy, 4- amino Butyltriethoxysilane, 4-vinylpyridine, 4-morpholinoacetophenone, 4-morpholinobenzophenone, m-aminophenyltrimethoxysilane, N- (1,3-dimethylbutylidene) -3- (triethoxysilyl) -1- Propanamine, N- (1,3-dimethylbutylidene) -3- (trimethoxysilyl) -1-propanamine, N- (1-methylethylidene) -3- (triethoxysilyl) -1-propanamine, N- (2-aminoethyl) -3-aminopropylmethyldiethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, N- (2-aminoethyl) -3-aminopropyltri Ethoxysilane, N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, N- (2-a Noethyl) -11-aminoundecyltriethoxysilane, N- (2-aminoethyl) -11-aminoundecyltrimethoxysilane, N- (2-aminoethyl) -3-aminoisobutylmethyldiethoxysilane, N- (2-aminoethyl) -3-aminoisobutylmethyldimethoxysilane, N- (3-diethoxymethylsilylpropyl) succinimide, N- (3-triethoxysilylpropyl) -4,5-dihydroimidazole, N- (3 -Triethoxysilylpropyl) pyrrole, N- (3-trimethoxysilylpropyl) pyrrole, N-3- [amino (polypropyleneoxy)] aminopropyltrimethoxysilane, N- [5- (triethoxysilyl) -2- Aza-1-oxopentyl] caprolactam, N- [5- (trimethoxy) Silyl) -2-aza-1-oxopentyl] caprolactam, N- (6-aminohexyl) aminomethyltriethoxysilane, N- (6-aminohexyl) aminomethyltrimethoxysilane, N-allyl-aza-2, 2-diethoxysilacyclopentane, N-allyl-aza-2,2-dimethoxysilacyclopentane, N- (cyclohexylthio) phthalimide, Nn-butyl-aza-2,2-diethoxysilacyclopentane, N -N-butyl-aza-2,2-dimethoxysilacyclopentane, N, N, N ', N'-tetraethylaminobenzophenone, N, N, N', N'-tetramethylthiourea, N, N, N ' , N′-tetramethylurea, N, N′-ethyleneurea, N, N′-diethylaminobenzophenone, N, N′-diethylaminobenzopheno N, N′-diethylaminobenzofuran, methyl N, N′-diethylcarbamate, N, N′-diethylurea, (N, N-diethyl-3-aminopropyl) triethoxysilane, (N, N-diethyl) -3-aminopropyl) trimethoxysilane, N, N-dioctyl-N′-triethoxysilylpropylurea, N, N-dioctyl-N′-trimethoxysilylpropylurea, methyl N, N-diethylcarbamate, N , N-diglycidylcyclohexylamine, N, N-dimethyl-o-toluidine, N, N-dimethylaminostyrene, N, N-diethylaminopropylacrylamide, N, N-dimethylaminopropylacrylamide, N-ethylaminoisobutyltriethoxy Silane, N-ethylaminoisobutyltrimethoxysilane, -Ethylaminoisobutylmethyldiethoxysilane, N-oxydiethylene-2-benzothiazolesulfenamide, N-cyclohexylaminopropyltriethoxysilane, N-cyclohexylaminopropyltrimethoxysilane, N-methylaminopropylmethyldimethoxysilane, N -Methylaminopropylmethyldiethoxysilane, N-vinylbenzylazacycloheptane, N-phenylpyrrolidone, N-phenylaminopropyltriethoxysilane, N-phenylaminopropyltrimethoxysilane, N-phenylaminomethyltriethoxysilane, N -Phenylaminomethyltrimethoxysilane, n-butylaminopropyltriethoxysilane, n-butylaminopropyltrimethoxysilane, N-methylaminopropyltri Ethoxysilane, N-methylaminopropyltrimethoxysilane, N-methyl-2-piperidone, N-methyl-2-pyrrolidone, N-methyl-ε-caprolactam, N-methylindolinone, N-methylpyrrolidone, p- ( 2-dimethylaminoethyl) styrene, p-aminophenyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, (aminoethylamino) -3-isobutyldiethoxysilane, (amino Ethylamino) -3-isobutyldimethoxysilane, (aminoethylaminomethyl) phenethyltriethoxysilane, (aminoethylaminomethyl) phenethyltrimethoxysilane, acrylic acid, diethyl adipate, acetamidopropyltrimethoxysilane, amino Enyltrimethoxysilane, aminobenzophenone, ureidopropyltriethoxysilane, ureidopropyltrimethoxysilane, ethylene oxide, octadecyldimethyl (3-trimethoxysilylpropyl) ammonium chloride, glycidoxypropyltriethoxysilane, glycidoxypropyltrimethoxysilane , Glycerol tristearate, chlorotriethoxysilane, chloropropyltriethoxysilane, chloropolydimethylsiloxane, chloromethyldiphenoxysilane, diallyldiphenyltin, diethylaminomethyltriethoxysilane, diethylaminomethyltrimethoxysilane, diethyl (glycidyl) amine, diethyl Dithiocarbamic acid 2-benzothiazoylester, diethoxydichlorosilane, ( (Cyclohexylaminomethyl) triethoxysilane, (cyclohexylaminomethyl) trimethoxysilane, diglycidylpolysiloxane, dichlorodiphenoxysilane, dicyclohexylcarbodiimide, divinylbenzene, diphenylcarbodiimide, diphenylcyanamide, diphenylmethane diisocyanate, diphenoxymethylchlorosilane, dibutyldichloro Tin, dimethyl (acetoxy-methylsiloxane) polydimethylsiloxane, dimethylaminomethyltriethoxysilane, dimethylaminomethyltrimethoxysilane, dimethyl (methoxy-methylsiloxane) polydimethylsiloxane, dimethylimidazolidinone, dimethylethyleneurea, dimethyldichlorosilane , Dimethylsulfoyl chloride, silsesquioxane Sorbitan trioleate, sorbitan monolaurate, titanium tetrakis (2-ethylhexoxide), tetraethoxysilane, tetraglycidyl-1,3-bisaminomethylcyclohexane, tetraphenoxysilane, tetramethylthiuram disulfide, tetramethoxy Silane, triethoxyvinylsilane, tris (3-trimethoxysilylpropyl) cyanurate, triphenyl phosphate, triphenoxychlorosilane, triphenoxymethylsilicon, triphenoxymethylsilane, carbon dioxide, bis (triethoxysilylpropyl) amine, bis (tri Methoxysilylpropyl) amine, bis [3- (triethoxysilyl) propyl] ethylenediamine, bis [3- (trimethoxysilyl) propyl] Range amine, bis [3- (triethoxysilyl) propyl] urea, bis [(trimethoxysilyl) propyl] urea, bis (2-hydroxymethyl) -3-aminopropyltriethoxysilane, bis (2-hydroxymethyl) -3-aminopropyltrimethoxysilane, bis (2-ethylhexanoate) tin, bis (2-methylbutoxy) methylchlorosilane, bis (3-triethoxysilylpropyl) tetrasulfide, bisdiethylaminobenzophenone, bisphenol A diglycidyl Ether, bisphenoxyethanol fluorenediglycidyl ether, bis (methyldiethoxysilylpropyl) amine, bis (methyldimethoxysilylpropyl) -N-methylamine, hydroxymethyltriethoxysilane, vinyltri (2-ethylhexyloxy) silane, vinylbenzyldiethylamine, vinylbenzyldimethylamine, vinylbenzyltributyltin, vinylbenzylpiperidine, vinylbenzylpyrrolidine, pyrrolidine, phenyl isocyanate, phenylisothiocyanate, (phenylaminomethyl) methyldimethoxysilane, ( Phenylaminomethyl) methyldiethoxysilane, phthalic acid amide, hexamethylene diisocyanate, benzylidene aniline, polydiphenylmethane diisocyanate, polydimethylsiloxane, methyl-4-pyridyl ketone, methylcaprolactam, methyltriethoxysilane, methyltriphenoxysilane, Examples include methyl lauryl thiopropionate and silicon tetrachloride.

（式中、Ｒ^２１、Ｒ^２２及びＲ^２３は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基（−ＣＯＯＨ）、メルカプト基（−ＳＨ）又はこれらの誘導体を表す。Ｒ^２４及びＲ^２５は、同一若しくは異なって、水素原子又はアルキル基を表す。ｎは整数を表す。）

（式中、Ｒ^２６、Ｒ^２７及びＲ^２８は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基（−ＣＯＯＨ）、メルカプト基（−ＳＨ）又はこれらの誘導体を表す。Ｒ^２９は、環状エーテル基を表す。ｐ及びｑは整数を表す。）

（式中、Ｒ^３０〜Ｒ^３３は、同一若しくは異なって、アルキル基、アルコキシ基、シリルオキシ基、カルボキシル基（−ＣＯＯＨ）、メルカプト基（−ＳＨ）又はこれらの誘導体を表す。） The structural unit based on the compound represented by the above formula (I), when combined with an amino group having one end, the fuel economy and wet grip performance can be improved more synergistically, as the modifier. Is preferably a compound represented by the following formula (IV), the following formula (V) or the following formula (VI), more preferably a compound represented by the following formula (IV) or the following formula (V), The compound represented by (IV) is more preferable.

(Wherein R ²¹ , R ²² and R ²³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group (—COOH), a mercapto group (—SH), or a derivative thereof. R ²⁴ And R ²⁵ are the same or different and each represents a hydrogen atom or an alkyl group, and n represents an integer.)

(Wherein R ²⁶ , R ²⁷ and R ²⁸ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group (—COOH), a mercapto group (—SH) or a derivative thereof. R ²⁹ Represents a cyclic ether group, and p and q represent an integer.)

(Wherein R ^{30 to} R ³³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group (—COOH), a mercapto group (—SH), or a derivative thereof).

In the compound represented by the above formula (IV), examples of the alkyl group of R ²¹ , R ²² and R ²³ include an alkyl group having 1 to 4 carbon atoms such as a methyl group (preferably having 1 to 3 carbon atoms). Is mentioned. Examples of the alkoxy group of R ²¹ , R ²² and R ²³ include an alkoxy group having 1 to 8 carbon atoms (preferably 1 to 6 carbon atoms, more preferably 1 to 4 carbon atoms) such as a methoxy group. . The alkoxy group includes a cycloalkoxy group and an aryloxy group. Examples of the silyloxy group of R ²¹ , R ²² and R ²³ include silyloxy groups substituted with an aliphatic group having 1 to 20 carbon atoms and an aromatic group (such as a trimethylsilyloxy group and a tribenzylsilyloxy group). .

In the compound represented by the above formula (IV), examples of the alkyl group of R ²⁴ and R ²⁵ include the same groups as the above alkyl groups (alkyl groups of R ²¹ , R ²² and R ²³ ). .

R ²¹ , R ²² and R ²³ are preferably an alkoxy group, and R ²⁴ and R ²⁵ are preferably an alkyl group for the reason that the effect of improving fuel economy and wet grip performance is great.

n (integer) is preferably 0 to 5 for the reason of availability. Furthermore, n is more preferably 2 to 4, and most preferably 3. If n is 6 or more, the cost increases.

Specific examples of the compound represented by the formula (IV) include 3- (N, N-dimethylamino) propyltriethoxysilane and 3- (N, N-dimethylamino) propyltrimethoxy exemplified as the modifier. Silane etc. are mentioned. Of these, 3- (N, N-dimethylamino) propyltrimethoxysilane is preferable.

In the compound represented by the above formula (V), R ²⁶ , R ²⁷ and R ²⁸ are the same as R ²¹ , R ²² and R ²³ in the compound represented by the above formula (IV). As R ²⁶ , R ^27, and R ²⁸ , an alkoxy group is preferable because it has a large effect of improving fuel economy and wet grip performance.

In the compound represented by the formula (V), examples of the cyclic ether group of R ²⁹ include a cyclic ether group having one ether bond such as an oxirane group and a cyclic ether group having two ether bonds such as a dioxolane group. And a cyclic ether group having three ether bonds such as a trioxane group. Among these, a cyclic ether group having one ether bond is preferable, and an oxirane group is more preferable because the effect of improving fuel economy and wet grip performance is great. Carbon number of a cyclic ether group becomes like this. Preferably it is 2-7, More preferably, it is 2-4. The cyclic ether group preferably has no unsaturated bond in the ring skeleton.

The p (integer) is preferably 0 to 5 for reasons of availability and reactivity. Further, p is more preferably from 2 to 4, and most preferably 3. If p is 6 or more, the cost increases.

q (integer) is preferably 0 to 5 for reasons of availability and reactivity. Furthermore, q is more preferably 1 to 3, and most preferably 1. If q is 6 or more, the cost increases.

Specific examples of the compound represented by the formula (V) include 3-glycidoxypropyltrimethoxysilane and 3-glycidoxypropyltriethoxysilane exemplified as the modifier. Of these, 3-glycidoxypropyltrimethoxysilane is preferable.

In the compound represented by the formula (VI), R ^{30 to} R ³³ are the same as R ²¹ , R ²² and R ²³ in the compound represented by the formula (IV). As R < ³⁰ > -R < ³³ >, an alkoxy group is preferable because the improvement effect of low fuel consumption and wet grip performance is great.

Specific examples of the compound represented by the formula (VI) include tetraethoxysilane and tetramethoxysilane exemplified as the modifier. Of these, tetraethoxysilane is preferable.

As a suitable modifier other than the compound represented by the above formula (IV), (V), or (VI), N- (3-triethoxysilylpropyl) -4,5-dihydroimidazole, silicon tetrachloride, etc. It can also be mentioned.

In the present invention, after carrying out the modification reaction with the above-mentioned modifier, a known anti-aging agent or alcohol may be added as necessary to stop the polymerization reaction.

The weight average molecular weight Mw of the copolymer is 1.0 × 10 ^{5 to} 2.5 × 10 ⁶ . When Mw is less than 1.0 × 10 ^5, fuel economy tends to be poor, whereas when Mw exceeds 2.5 × 10 ⁶ , workability tends to be deteriorated. The lower limit of Mw is preferably 2.0 × 10 ⁵ or more, more preferably 3.0 × 10 ⁵ or more, and the upper limit is preferably 1.5 × 10 ⁶ or less, more preferably 1.0 × 10 ^6. It is as follows.
In addition, Mw can be adjusted suitably by methods, such as changing the quantity of the polymerization initiator used at the time of superposition | polymerization, and can be measured by the method of the below-mentioned Example.

The content of the copolymer in 100% by mass of the rubber component is preferably 5% by mass or more, more preferably 10% by mass or more, and further preferably 40% by mass or more. If it is less than 5% by mass, there is a tendency that it is difficult to obtain an effect of improving fuel efficiency and wet grip performance. Further, the content of the copolymer is preferably 90% by mass or less, more preferably 80% by mass or less, and still more preferably 60% by mass or less. When it exceeds 90 mass%, it will become high cost and there exists a tendency for abrasion resistance to fall.

The above copolymer may be used in combination with other rubber components. As another rubber component, it is preferable to use a diene rubber. As the diene rubber, natural rubber (NR) and diene synthetic rubber can be used. Examples of the diene synthetic rubber include isoprene rubber (IR), butadiene rubber (BR), styrene butadiene rubber (SBR), and acrylonitrile butadiene rubber. (NBR), chloroprene rubber (CR), butyl rubber (IIR) and the like. Among these, NR, BR, and SBR are preferable because of low fuel consumption and wet grip performance, and it is more preferable to use NR, BR, and SBR together with the copolymer. These rubber components may be used alone or in combination of two or more.

The content of NR in 100% by mass of the rubber component is preferably 5% by mass or more, more preferably 10% by mass or more, and preferably 40% by mass or less, more preferably 30% by mass or less. Within the above range, low fuel consumption and wet grip performance can be obtained in a well-balanced manner.

The content of BR in 100% by mass of the rubber component is preferably 5% by mass or more, more preferably 8% by mass or more, and preferably 30% by mass or less, more preferably 20% by mass or less. Within the above range, low fuel consumption and wet grip performance can be obtained in a well-balanced manner.

The content of SBR in 100% by mass of the rubber component is preferably 5% by mass or more, more preferably 10% by mass or more, and preferably 95% by mass or less, more preferably 90% by mass or less, still more preferably. It is 75 mass% or less, Most preferably, it is 50 mass% or less. Within the above range, low fuel consumption and wet grip performance can be obtained in a well-balanced manner.

(silica)
In the present invention, silica is used. By blending silica together with the copolymer and the liquid resin having the specific softening point, dispersion of silica is promoted, and the effect of improving fuel economy and wet grip performance can be enhanced synergistically. The silica is not particularly limited, and examples thereof include dry process silica (anhydrous silicic acid), wet process silica (hydrous silicic acid), and the like, but wet process silica is preferable because of its large number of silanol groups. Silica may be used alone or in combination of two or more.

The nitrogen adsorption specific surface area _(N 2 SA) of silica is preferably not less than ^{50 m} 2 / g, more preferably at least ^{80m 2 / g, 100m 2 /} g or more, and particularly preferably equal to or greater than 150m ² / g. If it is less than 50 m < ² > / g, there exists a tendency for break strength, abrasion resistance, and wet grip performance to fall. The _N 2 SA of the silica is preferably 300 meters ² / g or less, more preferably ^{250m 2 / g, 200m 2 /} g or less is more preferable. If it exceeds 300 m ² / g, the dispersibility in the rubber composition is poor, the hysteresis loss of the rubber composition increases, and the fuel efficiency tends to decrease.
The nitrogen adsorption specific surface area of silica is a value measured by the BET method according to ASTM D3037-81.

The content of silica is preferably 5 parts by mass or more, more preferably 30 parts by mass or more, and still more preferably 50 parts by mass or more with respect to 100 parts by mass of the rubber component. If it is less than 5 parts by mass, the fuel economy and wet grip performance may not be sufficiently improved. Further, the content of silica is preferably 150 parts by mass or less, more preferably 100 parts by mass or less. If it exceeds 150 parts by mass, the fuel efficiency tends to decrease.

The content of silica in a total of 100% by mass of silica and carbon black is preferably 60% by mass or more, more preferably 85% by mass or more, and further preferably 95% by mass or more, and the upper limit is not particularly limited. If it is in the said range, low-fuel-consumption property and wet grip performance can be improved in a high-dimensional and well-balanced manner.

(Silane coupling agent)
In the present invention, it is preferable to use a silane coupling agent together with silica. The silane coupling agent is not particularly limited, and those conventionally used in the tire field can be used. For example, sulfide-based, mercapto-based, vinyl-based, amino-based, glycidoxy-based, nitro-based, chloro-based silane coupling Agents and the like. Among them, bis (3-triethoxysilylpropyl) tetrasulfide, bis (2-triethoxysilylethyl) tetrasulfide, bis (3-triethoxysilylpropyl) disulfide, bis (2-triethoxysilylethyl) disulfide, etc. A sulfide system can be preferably used. Of these, bis (3-triethoxysilylpropyl) tetrasulfide and 3-trimethoxysilylpropylbenzothiazolyl tetrasulfide are preferable from the viewpoint of improving the reinforcing property of the rubber composition. These silane coupling agents may be used alone or in combination of two or more.

The content of the silane coupling agent is preferably 1 part by mass or more, more preferably 2 parts by mass or more with respect to 100 parts by mass of silica. When the content of the silane coupling agent is less than 1 part by mass, the viscosity of the unvulcanized rubber composition tends to be high, and the processability tends to deteriorate. Further, the content of the silane coupling agent is preferably 20 parts by mass or less, more preferably 15 parts by mass or less with respect to 100 parts by mass of silica. When the content of the silane coupling agent exceeds 20 parts by mass, the blending effect of the silane coupling agent as much as the content cannot be obtained, and the cost tends to be high.

(Liquid resin)
The rubber composition of the present invention contains a liquid resin having a specific softening point. By using the liquid resin together with the copolymer and silica, it is possible to synergistically improve fuel economy and wet grip performance.

Examples of the liquid resin include liquid petroleum-based or coal-based resins such as liquid coumarone indene resin, liquid indene resin, liquid α-methylstyrene resin, liquid vinyltoluene resin, and liquid polyisopentane resin. Among these, at least one selected from the group consisting of liquid coumarone indene resin, liquid indene resin, and liquid α-methylstyrene resin is preferable, and liquid coumarone indene resin is more preferable.

The softening point of the liquid resin is −20 ° C. or higher, preferably −5 ° C. or higher, more preferably 0 ° C. or higher. When the temperature is lower than -20 ° C, the viscosity of the liquid resin becomes too low, and the kneadability with the rubber component tends to deteriorate. The softening point of the liquid resin is 20 ° C. or lower, preferably 18 ° C. or lower, more preferably 17 ° C. or lower. When the temperature exceeds 20 ° C., the exothermic property of the liquid resin increases, and there is a tendency that low fuel consumption cannot be sufficiently improved. In addition, wet grip performance tends to decrease.
In this specification, the softening point is a temperature at which a sphere descends when a softening point defined in JIS K6220: 2001 is measured by a ring and ball softening point measuring apparatus.

The content of the liquid resin is preferably 3 parts by mass or more, more preferably 5 parts by mass or more, still more preferably 10 parts by mass or more, and particularly preferably 15 parts by mass or more with respect to 100 parts by mass of the rubber component. If it is less than 3 parts by mass, the effect of blending the liquid resin may not be sufficiently obtained. The content of the liquid resin is preferably 40 parts by mass or less, more preferably 30 parts by mass or less, and still more preferably 25 parts by mass or less. When it exceeds 40 mass parts, there exists a tendency for abrasion resistance to deteriorate.

Since the liquid resin has a function of softening the rubber composition, the use of the liquid resin can reduce the content of oil in the rubber composition and further improve the fuel efficiency. Moreover, the fall of the wet grip performance by the mixing | blending of oil can also be suppressed. Thus, from the reason that fuel efficiency and wet grip performance can be suitably improved, in the rubber composition of the present invention, the oil content is preferably 6 parts by mass or less, with respect to 100 parts by mass of the rubber component. More preferably, it is 1 mass part or less, More preferably, it is 0 mass part (it does not contain substantially).

(Anti-aging agent)
The rubber composition of the present invention can contain an anti-aging agent. As the anti-aging agent, amine-based, phenol-based, and imidazole-based compounds, carbamic acid metal salts, waxes, and the like can be appropriately selected and used.

(Vulcanizing agent)
The rubber composition of the present invention can contain a vulcanizing agent. As the vulcanizing agent, an organic peroxide or a sulfur vulcanizing agent can be used. Examples of the organic peroxide include benzoyl peroxide, dicumyl peroxide, di-t-butyl peroxide, t-butyl cumyl peroxide, methyl ethyl ketone peroxide, cumene hydroperoxide, 2,5-dimethyl-2, 5-di (t-butylperoxy) hexane, 2,5-dimethyl-2,5-di (benzoylperoxy) hexane, 2,5-dimethyl-2,5-di (t-butylperoxy) hexyne- 3 or 1,3-bis (t-butylperoxypropyl) benzene or the like can be used. Moreover, as a sulfur type vulcanizing agent, sulfur, morpholine disulfide, etc. can be used, for example. Of these, sulfur is preferred.

(Vulcanization accelerator)
The rubber composition of the present invention can contain a vulcanization accelerator. Examples of the vulcanization accelerator include sulfenamide, thiazole, thiuram, thiourea, guanidine, dithiocarbamic acid, aldehyde-amine, aldehyde-ammonia, imidazoline, and xanthate vulcanization accelerators. Is mentioned. These may be used alone or in combination of two or more.

(Vulcanization aid)
The rubber composition of the present invention can contain a vulcanization aid. As the vulcanization aid, stearic acid, zinc oxide (zinc white) or the like can be used.

(Other ingredients)
In the rubber composition of the present invention, various compounding agents and additives blended for tires or general rubber compositions such as other reinforcing agents, plasticizers and coupling agents can be blended. Moreover, the content of these compounding agents and additives can also be set to general amounts.

<Method for producing rubber composition>
The rubber composition of the present invention can be produced by a conventionally known production method, and the production method is not limited. For example, it can be produced by kneading each of the above components using a kneading machine such as a Banbury mixer or a kneading roll under ordinary methods and conditions.

By using the rubber composition of the present invention thus obtained, a pneumatic tire with improved fuel economy and wet grip performance in a well-balanced manner can be obtained. The rubber composition can be used for each member of a tire, and in particular, can be suitably used for a tread, a sidewall, and the like.

<Pneumatic tire>
The pneumatic tire of the present invention is produced by a usual method using the rubber composition.
That is, by extruding a rubber composition containing the above components in accordance with the shape of a tread or the like at an unvulcanized stage, and molding it with a tire molding machine by a normal method along with other tire members, Form an unvulcanized tire. The unvulcanized tire is heated and pressurized in a vulcanizer to obtain a pneumatic tire.

The present invention will be specifically described based on examples, but the present invention is not limited to these examples.

ｎ−ブチルリチウム：関東化学（株）製の１．６Ｍ ｎ−ブチルリチウムヘキサン溶液
変性剤Ｂ−１：関東化学（株）製のテトラエトキシシラン
変性剤Ｂ−２：アヅマックス社製の３−グリシドキシプロピルトリメトキシシラン
変性剤Ｂ−３：アヅマックス社製の３−（Ｎ，Ｎ−ジメチルアミノ）プロピルトリメトキシシラン
２，６−ｔｅｒｔ−ブチル−ｐ−クレゾール：大内新興化学工業（株）製のノクラック２００ Hereinafter, various chemicals used at the time of synthesis and polymerization will be described together. In addition, the chemical | medical agent refine | purified according to the usual method as needed.
n-hexane: manufactured by Kanto Chemical Co., Ltd .: styrene manufactured by Kanto Chemical Co., Ltd. 1,3-butadiene: manufactured by Tokyo Chemical Industry Co., Ltd. p-methoxystyrene: manufactured by Kanto Chemical Co., Ltd. (expressed by the formula (I) Compound)
p- (tert-Butoxy) styrene: Wako Pure Chemical Industries, Ltd. (compound represented by formula (I))
Tetramethylethylenediamine: Modifier A-1 manufactured by Kanto Chemical Co., Ltd .: Dimethylamine modifier A-2 manufactured by Kanto Chemical Co., Ltd. Pyrrolidine modifier A-3 manufactured by Kanto Chemical Co., Ltd. AI-3 manufactured by FMC Lithium Corporation 200 (compound represented by the following formula (s = 2))

n-Butyllithium: 1.6M n-butyllithium hexane solution modifier manufactured by Kanto Chemical Co., Inc. B-1: Tetraethoxysilane modifier B-2 manufactured by Kanto Chemical Co., Ltd. B-2: 3-Gly manufactured by Amax Co. Sidoxypropyltrimethoxysilane modifier B-3: 3- (N, N-dimethylamino) propyltrimethoxysilane 2,6-tert-butyl-p-cresol manufactured by AMAX Co., Ltd .: Ouchi Shinsei Chemical Co., Ltd. Made of no crack 200

<Analysis of copolymer>
The copolymer obtained as described below was analyzed by the following method.

(Measurement of weight average molecular weight Mw)
The weight average molecular weight Mw of the copolymer is a gel permeation chromatograph (GPC) (GPC-8000 series manufactured by Tosoh Corp., detector: differential refractometer, column: TSKGEL SUPERMALTPORE HZ-M manufactured by Tosoh Corp.) It calculated | required by standard polystyrene conversion based on the measured value by.

(Structural identification of copolymer)
The structure of the copolymer was identified using a JNM-ECA series device manufactured by JEOL Ltd. From the measurement results, the content of 1,3-butadiene, the compound represented by the formula (I) (p-methoxystyrene, p- (tert-butoxy) styrene), and styrene in the copolymer was calculated.

<Synthesis of copolymer>
(Copolymer (1))
In a heat-resistant container sufficiently substituted with nitrogen, 1500 ml of n-hexane, 100 mmol of styrene, 800 mmol of 1,3-butadiene, 5 mmol of p-methoxystyrene, 0.2 mmol of tetramethylethylenediamine, 0.12 mmol of modifying agent A-1, n-butyllithium 0 .12 mmol was added and it stirred at 0 degreeC for 48 hours. Thereafter, 0.15 mmol of the modifier B-1 was added and stirred at 0 ° C. for 15 minutes. Thereafter, alcohol was added to stop the reaction, 1 g of 2,6-tert-butyl-p-cresol was added to the reaction solution, and then copolymer (1) was obtained by reprecipitation purification. The weight average molecular weight of the obtained copolymer (1) is 500,000, the content of the compound represented by the above formula (I) (alkoxystyrene component content) is 1.1% by mass, and the styrene content (styrene). The component content was 19% by mass.

(Copolymers (2) to (12))
Synthesis was performed in the same manner as for the copolymer (1) using the recipe in Table 1. The properties of the obtained polymer are shown in Table 1.

<Examples and Comparative Examples>
Below, various chemical | medical agents used by the Example and the comparative example are demonstrated.
NR: RSS # 3
BR: Ubepol BR150B manufactured by Ube Industries, Ltd.
SBR: SL574 manufactured by JSR Corporation
Copolymers (1) to (12): Synthetic silica by the above method: Ultrasil VN3 (N ₂ SA: 175 m ² / g) manufactured by Degussa
Silane coupling agent: Si69 (bis (3-triethoxysilylpropyl) tetrasulfide) manufactured by Evonik Degussa
Resin (1): NOVARES C10 manufactured by Rutgers Chemicals (liquid coumarone indene resin, softening point: 5 to 15 ° C.)
Resin (2): NOVARES TL10 manufactured by Rutgers Chemicals (liquid resin mainly composed of α-methylstyrene and indene, softening point: 5 to 15 ° C.)
Resin (3): NOVARES C90 manufactured by Rutgers Chemicals (solid coumarone indene resin, softening point: 90 ° C.)
Anti-aging agent: NOCRACK 6C (N-1,3-dimethylbutyl-N′-phenyl-p-phenylenediamine) manufactured by Ouchi Shinsei Chemical Co., Ltd.
Stearic acid: Zinc stearate manufactured by NOF Corporation: Zinc Hana No. 1 manufactured by Mitsui Mining & Smelting Co., Ltd. Sulfur: Powdered sulfur vulcanization accelerator manufactured by Tsurumi Chemical Co., Ltd. (1): Emerging Ouchi Noxeller CZ (N-cyclohexyl-2-benzothiazolylsulfenamide) manufactured by Chemical Industry Co., Ltd.
Vulcanization accelerator (2): Noxeller D (diphenylguanidine) manufactured by Ouchi Shinsei Chemical Industry Co., Ltd.

According to the contents shown in Table 2, materials other than sulfur and a vulcanization accelerator were kneaded for 3 minutes at 150 ° C. using a 1.7 L Banbury mixer to obtain a kneaded product. Next, sulfur and a vulcanization accelerator were added to the obtained kneaded product, and kneaded for 3 minutes at 80 ° C. using an open roll to obtain an unvulcanized rubber composition. The obtained unvulcanized rubber composition was press vulcanized at 170 ° C. for 15 minutes to obtain a vulcanized rubber composition.
Further, the obtained unvulcanized rubber composition was molded into a tread shape and bonded together with other tire members on a tire molding machine to form an unvulcanized tire, and then press vulcanized at 170 ° C. for 10 minutes. A test tire (size: 195 / 65R15) was produced.
The performance of the obtained vulcanized rubber composition and test tire was evaluated by the following test method.

<Evaluation items and test methods>
(Low fuel consumption)
Using a spectrometer manufactured by Ueshima Seisakusho, tan δ of the obtained vulcanized rubber composition was measured at a dynamic strain amplitude of 1%, a frequency of 10 Hz, and a temperature of 50 ° C. And the measurement result was displayed as an index according to the following formula. The larger the index, the lower the rolling resistance and the better the fuel efficiency.
(Low fuel consumption index) = (tan δ of Comparative Example 1) / (tan δ of each formulation) × 100

(Wet grip performance (1))
Wet grip performance was evaluated using a flat belt friction tester (FR5010 type) manufactured by Ueshima Seisakusho. A cylindrical rubber test piece having a width of 20 mm and a diameter of 100 mm made of the above vulcanized rubber composition was used as a sample, and the slip ratio of the sample with respect to the road surface was 0 to 0 at a speed of 20 km / hour, a load of 4 kgf and a road surface temperature of 20 ° C. The maximum value of the friction coefficient detected at that time was read up to 70%. And the measurement result was displayed as an index according to the following formula. A larger index indicates better wet grip performance.
(Wet grip performance (1) index) = (maximum friction coefficient of each formulation) / (maximum friction coefficient of Comparative Example 1) × 100

(Wet grip performance (2))
On a test course with wet water and wet road surface, the test tire is mounted on a 2000 cc domestic FR vehicle, braked at a speed of 70 km / h, and the distance traveled between braking the tire and stopping (Brake distance) was measured. And the measurement result was displayed as an index according to the following formula. A larger index indicates better wet grip performance.
(Wet grip performance (2) index) = (braking distance of comparative example 1) / (braking distance of each formulation) × 100

As shown in Table 2, it is obtained by copolymerizing 1,3-butadiene, styrene and the compound represented by the above formula (I), has an amino group at one end, and nitrogen, oxygen at the other end. And a rubber component containing a copolymer having a functional group containing at least one atom selected from the group consisting of silicon and having a weight average molecular weight within a specific range, silica, and a liquid resin having a specific softening point In the examples including the above, low fuel consumption and wet grip performance could be improved in a well-balanced manner.

Comparison of Comparative Examples 1, 4, 5 and Example 12 shows that low fuel consumption can be improved synergistically by using the above copolymer, silica, and a liquid resin having a specific softening point. It was.

Claims (18)

It is obtained by copolymerizing 1,3-butadiene, styrene and a compound represented by the following formula (I), has an amino group at one end, and is selected from the group consisting of nitrogen, oxygen and silicon at the other end A rubber component containing a copolymer having a functional group containing at least one kind of atom and a weight average molecular weight of 1.0 × 10 ^{5 to} 2.5 × 10 ⁶ , silica, and a softening point of 20 to 20 A rubber composition comprising a liquid resin at 0 ° C.

(In the formula, R ¹ represents a hydrocarbon group having 1 to 10 carbon atoms.) The rubber composition according to claim 1, wherein the functional group is an alkoxysilyl group. The rubber composition according to claim 1, wherein the functional group is an alkoxysilyl group or an amino group. The rubber composition according to any one of claims 1 to 3, wherein the amino group at one terminal is an alkylamino group or a group represented by the following formula (II).

(In the formula, R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms, and may have a nitrogen atom or an oxygen atom.) The rubber composition according to claim 4, wherein the group represented by the formula (II) is a group represented by the following formula (III).

(In formula, R < ¹² > -R < ¹⁹ > is the same or different, represents a hydrogen atom or a C1-C5 hydrocarbon group, and may have a nitrogen atom and an oxygen atom.) The rubber composition according to any one of claims 1 to 5, which has an isoprene unit together with an amino group at the one end. The rubber composition according to any one of claims 1 to 6, wherein a content of the compound represented by the formula (I) in the copolymer is 0.05 to 35% by mass. The copolymer is prepared by copolymerizing 1,3-butadiene, styrene and the compound represented by the formula (I) by using a compound having a lithium atom and an amino group as a polymerization initiator, and then polymerizing the terminal with nitrogen and oxygen. The rubber composition according to any one of claims 1 to 7, wherein the rubber composition is obtained by modification with a modifier having a functional group containing at least one atom selected from the group consisting of silicon and silicon. The rubber composition according to claim 8, wherein the modifier is a compound represented by the following formula (IV), the following formula (V), or the following formula (VI).

(Wherein R ²¹ , R ²² and R ²³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group, or a derivative thereof. R ²⁴ and R ²⁵ are the same or different. And represents a hydrogen atom or an alkyl group, and n represents an integer.)

(Wherein R ²⁶ , R ²⁷ and R ²⁸ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group or a derivative thereof. R ²⁹ represents a cyclic ether group. p and q represent integers.)

(In the formula, R ^{30 to} R ³³ are the same or different and each represents an alkyl group, an alkoxy group, a silyloxy group, a carboxyl group, a mercapto group, or a derivative thereof.) The rubber composition according to claim 8 or 9, wherein the polymerization initiator has an alkylamino group or a group represented by the following formula (II).

(In the formula, R ¹¹ represents a divalent hydrocarbon group having 2 to 50 carbon atoms, and may have a nitrogen atom or an oxygen atom.) The rubber composition according to claim 10, wherein the group represented by the formula (II) is a group represented by the following formula (III).

(In formula, R < ¹² > -R < ¹⁹ > is the same or different, represents a hydrogen atom or a C1-C5 hydrocarbon group, and may have a nitrogen atom and an oxygen atom.) The rubber composition according to any one of claims 8 to 11, wherein the polymerization initiator has an isoprene unit. The rubber composition according to any one of claims 1 to 12, wherein the liquid resin is at least one selected from the group consisting of a liquid coumarone indene resin, a liquid indene resin, and a liquid α-methylstyrene resin. The rubber composition according to any one of claims 1 to 13, wherein a content of the copolymer is 5% by mass or more in 100% by mass of the rubber component. The rubber composition according to any one of claims 1 to 14, comprising 5 to 150 parts by mass of silica with respect to 100 parts by mass of the rubber component. The rubber composition according to any one of claims 1 to 15, comprising 3 to 40 parts by mass of a liquid resin with respect to 100 parts by mass of the rubber component. The rubber composition according to any one of claims 1 to 16, which is used as a rubber composition for a tire tread. The pneumatic tire produced using the rubber composition in any one of Claims 1-17.