JP2011136881A - 薄片化黒鉛分散液の製造方法、薄片化黒鉛分散液、薄膜の製造方法、樹脂組成物及びモノマー組成物 - Google Patents
薄片化黒鉛分散液の製造方法、薄片化黒鉛分散液、薄膜の製造方法、樹脂組成物及びモノマー組成物 Download PDFInfo
- Publication number
- JP2011136881A JP2011136881A JP2009298850A JP2009298850A JP2011136881A JP 2011136881 A JP2011136881 A JP 2011136881A JP 2009298850 A JP2009298850 A JP 2009298850A JP 2009298850 A JP2009298850 A JP 2009298850A JP 2011136881 A JP2011136881 A JP 2011136881A
- Authority
- JP
- Japan
- Prior art keywords
- graphite
- exfoliated graphite
- compound
- exfoliated
- producing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】 本発明は、黒鉛化合物と、テトラヒドロフランやN−メチルピロリドンなどの五員環を含有する環状化合物とを含む被処理液を振とうさせて、上記黒鉛化合物を薄片化することを特徴とするので、黒鉛化合物の層面同士を剥離して薄片化黒鉛が安定的に分散してなる薄片化黒鉛分散液を効率良く製造することができる。
【選択図】 なし
Description
黒鉛化合物(SECカーボン社製 商品名「SNO−15」、レーザー光回折法により粒度分布を測定した場合に50%径として得られる値:15μm、ESCAにより測定した黒鉛化合物中の酸素原子の含有率:2.9%)を用意した。
テトラヒドロフランの代わりにN−メチルピロリドンを用いたこと以外は実施例1と同様にして、薄片化黒鉛がN−メチルピロリドン中に分散してなる薄片化黒鉛分散液を得た。なお、薄片化黒鉛分散液中に沈殿物が残っていた。更に、実施例1と同様の要領で、薄片化黒鉛分散液中に分散している薄片化黒鉛及び黒鉛化合物における層面間の剥離を促進させた。なお、薄片化黒鉛分散液中には黒鉛化合物と推定される沈殿物が残っていたので、薄片化黒鉛分散液の沈殿物のない上方部分を採取した。採取液は目視にて金属様の光沢を有する濃黒銀色の懸濁液であり、薄片化黒鉛分散液中には高度に薄片化された薄片化黒鉛が分散していると推定された。
黒鉛化合物として、XGSience社から商品名「XGnP−5」にて市販されている黒鉛化合物(レーザー光回折法により粒度分布を測定した場合に50%径として得られる値:5μm、ESCAにより測定した黒鉛化合物中の酸素原子の含有率:5.8%)を用いたこと以外は実施例1と同様にして薄片化黒鉛分散液を得た。なお、薄片化黒鉛分散液中には沈殿物が残っていた。更に、実施例1と同様の要領で、薄片化黒鉛分散液中に分散している薄片化黒鉛及び黒鉛化合物における層面間の剥離を促進させた。なお、薄片化黒鉛分散液中には黒鉛化合物と推定される沈殿物が残っていたので、薄片化黒鉛分散液の沈殿物のない上方部分を採取した。採取液は目視にて透明度の高い濃灰色であり、薄片化黒鉛分散液中には高度に薄片化された薄片化黒鉛が分散していると推定された。
黒鉛化合物として、XGSience社から商品名「XGnP−5」にて市販されている黒鉛化合物(レーザー光回折法により粒度分布を測定した場合に50%径として得られる値:5μm、ESCAにより測定した黒鉛化合物中の酸素原子の含有率:5.8%)を用いたこと、テトラヒドロフランの代わりにN−メチルピロリドンを用いたこと以外は実施例2と同様にして薄片化黒鉛分散液を得た。なお、薄片化黒鉛分散液中には沈殿物が残っていた。更に、実施例1と同様の要領で、薄片化黒鉛分散液中に分散している薄片化黒鉛及び黒鉛化合物における層面間の剥離を促進させた。なお、薄片化黒鉛分散液中には黒鉛化合物と推定される沈殿物が残っていたので、薄片化黒鉛分散液の沈殿物のない上方部分を採取した。採取液は目視にて非常に透明度の高い灰色であり、薄片化黒鉛分散液中には高度に薄片化された薄片化黒鉛が分散していると推定された。
Claims (7)
- 黒鉛化合物と五員環を含有する環状化合物とを含む被処理液を振とうさせて、上記黒鉛化合物を薄片化することを特徴とする薄片化黒鉛分散液の製造方法。
- 五員環を含有する環状化合物がテトラヒロドフラン又はN−メチルピロリドンであることを特徴とする請求項1に記載の薄片化黒鉛分散液の製造方法。
- 黒鉛化合物におけるX線光電子分析(ESCA)により測定した酸素原子の含有率が4%以下であることを特徴とする請求項1に記載の薄片化黒鉛分散液の製造方法。
- 請求項1乃至請求項3の何れか1項に記載の薄片化黒鉛分散液の製造方法によって製造されてなることを特徴とする薄片化黒鉛分散液。
- 請求項1乃至請求項3の何れか1項に記載の薄片化黒鉛分散液の製造方法で得られた薄片化黒鉛分散液を基材に塗布、乾燥させて薄片化黒鉛を含む薄膜を形成することを特徴とする薄膜の製造方法。
- 請求項1乃至請求項3の何れか1項に記載の薄片化黒鉛分散液の製造方法で得られた薄片化黒鉛分散液と合成樹脂とを混合してなることを特徴とする樹脂組成物。
- 請求項1乃至請求項3の何れか1項に記載の薄片化黒鉛分散液の製造方法で得られた薄片化黒鉛分散液とモノマーとを混合してなることを特徴とするモノマー組成物。