JP2011128512A - 光学体およびその製造方法 - Google Patents
光学体およびその製造方法 Download PDFInfo
- Publication number
- JP2011128512A JP2011128512A JP2009289042A JP2009289042A JP2011128512A JP 2011128512 A JP2011128512 A JP 2011128512A JP 2009289042 A JP2009289042 A JP 2009289042A JP 2009289042 A JP2009289042 A JP 2009289042A JP 2011128512 A JP2011128512 A JP 2011128512A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- optical
- optical layer
- elastic modulus
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明に係る光学体は、凹凸形状の界面を内部に有する光学層と、界面に設けられた無機材料を主成分とする中間層とを備える。光学層が、凹凸形状の第1の面を有する第1の光学層と、凹凸形状の第2の面を有する第2の光学層とを備える。界面は、対向配置された第1の面と第2の面とにより形成され、第1の光学層、および第2の光学層の少なくとも一方が、100℃での貯蔵弾性率が3×107Pa以上であり、25℃での貯蔵弾性率が3×109Pa以下である。
【選択図】図1
Description
凹凸形状の界面を内部に有する光学層と、
上記界面に設けられた無機材料を主成分とする中間層と
を備え、
上記光学層が、
凹凸形状の第1の面を有する第1の光学層と、
凹凸形状の第2の面を有する第2の光学層と
を備え、
上記界面は、対向配置された上記第1の面と上記第2の面とにより形成され、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体である。
第1の光学層と、
上記第1の光学層の凹凸面上に形成された無機材料を主成分とする中間層と、
上記中間層が形成された上記凹凸面上に、該凹凸を埋めるように形成された第2の光学層と
を備え、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体である。
凹凸形状の界面を内部に有する光学層と、
上記界面に設けられた無機材料を主成分とする中間層と
を備え、
上記光学層が、
凹凸形状の第1の面を有する第1の光学層と、
凹凸形状の第2の面を有する第2の光学層と
を備え、
上記界面は、対向配置された上記第1の面と上記第2の面とにより形成され、
上記第1の光学層が、
上記第2の光学層形成時のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体である。
第1の光学層と、
上記第1の光学層の凹凸面上に形成された無機材料を主成分とする中間層と、
上記中間層が形成された上記凹凸面上に、該凹凸を埋めるように形成された第2の光学層と
を備え、
上記第1の光学層が、
上記第2の光学層形成時のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体である。
第1の光学層の凹凸面上に無機材料を主成分とする中間層を形成する工程と、
上記中間層が形成された上記凹凸面を第2の光学層により包埋する工程と
を備え、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体の製造方法である。
第1の光学層の凹凸面上に無機材料を主成分とする中間層を形成する工程と、
上記中間層が形成された上記凹凸面を第2の光学層により包埋する工程と
を備え、
上記第1の光学層が、
上記包埋工程のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体の製造方法である。
1.第1の実施形態(構造体を1次元配列した例)
2.第2の実施形態(構造体を2次元配列した例)
3.第3の実施形態(ルーバ型の波長選択反射層の例)
4.第4の実施形態(光学フィルムに光散乱体を設けた例)
[光学フィルムの構成]
図1Aは、本発明の第1の実施形態に係る光学フィルムの一構成例を示す断面図である。図1Bは、本発明の第1の実施形態に係る光学フィルムを被着体に貼り合わせた例を示す断面図である。光学体としての光学フィルム1は、いわゆる指向反射性能を有する光学フィルムである。図1Aに示すように、この光学フィルム1は、凹凸形状の界面を内部に有する光学層2と、この光学層2の界面に設けられた波長選択反射層(無機材料を主成分とする中間層)3とを備える。光学層2は、凹凸形状の第1の面を有する第1の光学層4と、凹凸形状の第2の面を有する第2の光学層5とを備える。光学層内部の界面は、対向配置された凹凸形状の第1の面と第2の面とにより形成されている。光学フィルム1は、太陽光などの光が入射する入射面S1と、この入射面S1より入射した光のうち、光学フィルム1を透過した光が出射される出射面S2とを有する。
測定装置:全自動微細形状測定機 サーフコーダーET4000A(株式会社小坂研究所)
λc=0.8mm、評価長さ4mm、カットオフ×5倍
データサンプリング間隔0.5μm
第1の光学層4は、例えば、波長選択反射層3を支持し、かつ保護するためのものである。第1の光学層4は、光学フィルム1に可撓性を付与する観点から、例えば、樹脂を主成分とする層からなる。第1の光学層4の両主面のうち、例えば、一方の面は平滑面であり、他方の面は凹凸面(第1の面)である。波長選択反射層3は該凹凸面上に形成される。
上述したプレポリマーなどの含有量は、波長選択反射層3に含まれる誘電体層、または金属層などの性質に応じて任意に調整することができる。
波長選択反射層3は、例えば、積層膜、透明導電層、機能層、または半透過層である。また、積層膜、透明導電層、および機能層、半透過層を2以上組み合わせて波長選択反射層としてもよい。波長選択反射層3の平均膜厚は、好ましくは20μm、より好ましくは5μm以下、さらに好ましくは1μm以下である。波長選択反射層3の平均膜厚が20μmを超えると、透過光が屈折する光路が長くなり、透過像が歪んで見える傾向がある。波長選択反射層の形成方法としては、例えば、スパッタ法、蒸着法、ディップコーティング法、ダイコーティング法などを用いることができる。
(積層膜)
積層膜は、例えば、屈折率の異なる低屈折率層および高屈折率層を交互に積層してなる積層膜である。または、積層膜は、例えば、赤外領域において反射率の高い金属層と、可視領域において屈折率が高く反射防止層として機能する光学透明層、または透明導電層とを交互に積層してなる積層膜である。
透明導電層は、可視領域において透明性を有する導電性材料を主成分とする透明導電層である。透明導電層は、例えば、酸化錫、酸化亜鉛、酸化インジウム錫(ITO)、酸化インジウム亜鉛(IZO)、アンチモンドープ酸化錫、カーボンナノチューブ含有体などの透明導電物質を主成分とする。もしくはこれらのナノ粒子や金属などの導電性を持つ材料のナノ粒子、ナノロッド、ナノワイヤーを樹脂中に高濃度に分散させた層を用いても良い。
機能層は、外部刺激により反射性能などが可逆的に変化するクロミック材料を主成分とする。クロミック材料は、例えば、熱、光、侵入分子などの外部刺激により構造を可逆的に変化させる材料である。クロミック材料としては、例えば、フォトクロミック材料、サーモクロミック材料、ガスクロミック材料、エレクトロクロミック材料を用いることができる。
半透過層は、例えば、単層または複数層の金属層からなり、半透過性を有するものである。金属層の材料としては、例えば、上述の積層膜の金属層と同様のものを用いることができる。
図5A、図5Bは、光学フィルムの機能の一例を説明するための断面図である。ここでは、例として、構造体の形状が傾斜角45°のプリズム形状である場合を例として説明する。図5Aに示すように、この光学フィルム1に入射した太陽光のうち近赤外線L1の一部は、入射した方向と同程度の上空方向に指向反射するのに対して、可視光L2は光学フィルム1を透過する。
x=(sin(45−α')+cos(45−α’)/tan(45+α'))/(sin(45−α')+cos(45−α'))×R2 ・・・(1)
但し、α'=sin-1(sinα/n)
図8は、本発明の第1の実施形態に係る光学フィルムを製造するための製造装置の一構成例を示す概略図である。図8に示すように、この製造装置は、ラミネートロール41、42、ガイドロール43、塗布装置45、および照射装置46を備える。
以下、図8〜図11を参照して、本発明の第1の実施形態に係る光学フィルムの製造方法の一例について説明する。なお、以下に示す製造プロセスの一部または全部は、生産性を考慮して、図8に示すようなロール・ツー・ロールにより行われることが好ましい。但し、金型の作製工程は除くものとする。
図12〜図14は、本発明の第2の実施形態に係る光学フィルムの構造体の構成例を示す断面図である。第2の実施形態において、第1の実施形態と対応する箇所には同一の符号を付す。第2の実施形態は、第1の光学層4の一主面にて構造体4cが2次元配列されている点において、第1の実施形態とは異なっている。
図15Aは、本発明の第3の実施形態に係る光学フィルムの一構成例を示す断面図である。第3の実施形態において、第1の実施形態と同一の箇所には同一の符号を付して説明を省略する。第3の実施形態は、光の入射面に対して傾斜した複数の波長選択反射層3を光学層2内に備え、これらの波長選択反射層3を互いに平行に配列している点において、第1の実施形態とは異なっている。
第4の実施形態は、特定波長の光を指向反射するのに対して、特定波長以外の光を散乱させる点において、第1の実施形態とは異なっている。光学フィルム1は、入射光を散乱する光散乱体を備えている。この散乱体は、例えば、光学層2の表面、光学層2の内部、および波長選択反射層3と光学層2との間のうち、少なくとも1箇所に設けられている。光散乱体は、好ましくは、波長選択反射層3と第1の光学層4との間、第1の光学層4の内部、および第1の光学層4の表面のうちの少なくとも一箇所に設けられている。光学フィルム1を窓材などの支持体に貼り合わせる場合、室内側および室外側のどちらにも適用可能である。光学フィルム1を室外側に対して貼り合わせる場合、波長選択反射層3と窓材などの支持体との間にのみ、特定波長以外の光を散乱させる光散乱体を設けることが好ましい。波長選択反射層3と入射面との間に光散乱体が存在すると、指向反射特性が失われてしまうからである。また、室内側に光学フィルム1を貼り合せる場合には、その貼り合わせ面とは反対側の出射面と、波長選択反射層3との間に光散乱体を設けることが好ましい。
膜厚が100μmになるように硬化させた樹脂を、幅5mm、長さ約20mmに打ち抜き、温度を−50℃から150℃まで毎分5℃上昇させ、1Hzで動的粘弾性測定を行った。測定には、動的粘弾性測定装置DVA−220(アイティ計測制御株式会社製)を用いた。
まず、図17に示すように、バイトによる切削加工によりプリズム形状をNi―P製金型に付与した。次に、このNi―P製金型に下記配合の樹脂組成物を塗布し、さらにその上に厚み75μmのPETフィルム(東洋紡製、商品名A4300)を載置した。次に、PET(ポリエチレンテレフタレート)フィルム側からUV光を樹脂組成物に対して照射し硬化させることにより、第1の光学層とPETフィルムとからなる積層体を得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 70重量部
ジペンタエリスリトールヘキサアクリレート(新中村化学工業社製、商品名:A−DPH) 30重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 70重量部
ジペンタエリスリトールヘキサアクリレート(新中村化学工業社製、商品名:A−DPH) 30重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
リン酸を官能基に有する(メタ)アクリルモノマー(密着剤)(共栄社化学(株)社製、商品名:P−2M) 0.3重量部
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 70重量部
トリメチロールプロパントリアクリレート(日本化薬社製、商品名:カヤラッドTMPTA) 30重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いること、および樹脂組成物を作製する際に加える圧力を0.01MPaとする以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 85重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 15重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 85重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 15重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 80重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 20重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 70重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 30重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層の界面に形成する無機材料を主成分とする中間層として半透過性のAl膜(膜圧11nm)を用いた以外は、実施例4と同様にして光学フィルムを得た。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(共栄社化学社製、商品名:UF8001G) 100重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(共栄社化学社製、商品名:UF8001G) 70重量部
ジペンタエリスリトールヘキサアクリレート(新中村化学工業社製、商品名:A−DPH) 30重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(共栄社化学社製、商品名:UF8001G) 60重量部
トリメチロールプロパントリアクリレート(日本化薬社製、商品名:カヤラッドTMPTA) 40重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(共栄社化学社製、商品名:UF8001G) 60重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 40重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成するアクリレートとして、ウレタンアクリレート(東亞合成製、商品名:アロニックス)を用いること、および樹脂組成物を作製する際に加える圧力を0.01MPaとすること以外は、実施例1と同様にして光学フィルムを得た。
第1の光学層、および第2の光学層を形成するアクリレートとして、ウレタンアクリレート(東亞合成製、商品名:アロニックス)を用いる以外は、実施例1と同様にして光学フィルムを得た。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 95重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 5重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
第1の光学層、および第2の光学層を形成する樹脂組成物として、下記配合の樹脂組成物を用いる以外は、実施例1と同様にして光学フィルムを得た。
<樹脂配合>
ウレタンアクリレート(東亞合成製、商品名:アロニックス) 90重量部
エチレンオキシド変性グリセロールトリアクリレート(東京化成工業社製、商品名:T2325) 10重量部
開始剤(チバ・スペシャルティ・ケミカルズ社製、商品名:イルガキュア184) 3重量部
但し、第2の光学層を形成するための樹脂組成物には、実施例1と同様の密着剤を0.3重量部添加した。
実施例1〜7、比較例1〜8の光学フィルムの成形面の形状を以下のようにして評価した。ミクロトームで光学フィルムを切削し、走査型共焦点レーザ顕微鏡(オリンパス株式会社製、商品名:OLS3000)にて観察し画像を得た。得られた画像と、成形面の理想形状と比較し、以下の基準で評価した。
Y:頂角付近と底面付近の角度が、理想形状の角度から±1度以内である
N:頂角付近と底面付近の角度が、理想形状の角度から±1度を超える
実施例1〜7、比較例1〜8の光学フィルムの指向反射率を以下のようにして評価した。
図18は、光学フィルムの再帰反射率を測定するため測定装置の構成を示す。まず、ハロゲン灯光源101から出射されレンズによりコリメートされた直線光が、光の進行方向に対し45°の角度に設置されたハーフミラー102に入射する。入射光の半分は、ハーフミラー102により反射されてその進行方向が90°回転するのに対して、入射光の残り半分は、ハーフミラー102を透過する。次に、反射光がサンプル103で再帰反射し、再びハーフミラー102に入射する。この入射光の半分が、ハーフミラー102を透過しディテクター104に入射する。この入射光の強度が、反射強度としてディテクター104により測定される。
Y:波長900nm、および1100nmで0度の反射率が60%以上、かつ、20度の反射率が20%以下の関係を満たす
N:波長900nm、および1100nmで0度の反射率が60%以上、かつ、20度の反射率が20%以下の関係を満たさない
実施例1〜7では、100℃での貯蔵弾性率が3×107Pa以上であり、25℃での貯蔵弾性率が3×109Pa以下である樹脂を用いて、第1の光学層、および第2の光学層を形成しているので、界面の凹凸形状の歪みを抑制することができる。したがって、優れた再帰性反射性能を得ることができる。
2 光学層
3 波長選択反射層
4 第1の光学層
4a 第1の基材
5 第2の光学層
5a 第2の基材
6 接合層
7 剥離層
8 ハードコート層
9 反射層付き光学層
S1 入射面
S2 出射面
Claims (18)
- 凹凸形状の界面を内部に有する光学層と、
上記界面に設けられた無機材料を主成分とする中間層と
を備え、
上記光学層が、
凹凸形状の第1の面を有する第1の光学層と、
凹凸形状の第2の面を有する第2の光学層と
を備え、
上記界面は、対向配置された上記第1の面と上記第2の面とにより形成され、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体。 - 第1の光学層と、
上記第1の光学層の凹凸面上に形成された無機材料を主成分とする中間層と、
上記中間層が形成された上記凹凸面上に、該凹凸を埋めるように形成された第2の光学層と
を備え、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体。 - 凹凸形状の界面を内部に有する光学層と、
上記界面に設けられた無機材料を主成分とする中間層と
を備え、
上記光学層が、
凹凸形状の第1の面を有する第1の光学層と、
凹凸形状の第2の面を有する第2の光学層と
を備え、
上記界面は、対向配置された上記第1の面と上記第2の面とにより形成され、
上記第1の光学層が、
上記第2の光学層形成時のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体。 - 第1の光学層と、
上記第1の光学層の凹凸面上に形成された無機材料を主成分とする中間層と、
上記中間層が形成された上記凹凸面上に、該凹凸を埋めるように形成された第2の光学層と、
を備え、
上記第1の光学層が、
上記第2の光学層形成時のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体。 - 上記中間層は、特定波長帯の光を選択的に指向反射するのに対して、上記特定波長帯以外の光を透過する波長選択反射層である請求項1〜4のいずれか1項に記載の光学体。
- 上記波長選択反射層が、可視光領域において透明性を有する導電性材料を主成分とする透明導電層、または外部刺激により反射性能が可逆的に変化するクロミック材料を主成分とする機能層である請求項5記載の光学体。
- 上記波長選択反射層が、単層または複数層の金属層からなり、半透過性を有する請求項5記載の光学体。
- 上記光学層の両主面の少なくとも一方に形成された基材をさらに備える請求項1〜4のいずれか1項に記載の光学体。
- 上記第1の光学層、および上記第2の光学層の少なくとも一方が、エネルギー線硬化型樹脂、または熱硬化型樹脂と、架橋剤とを含んでいる請求項1〜4のいずれか1項に記載の光学体。
- 上記架橋剤が、環状構造を有する架橋剤である請求項9記載の光学体。
- 上記第1の面および上記第2の面の凹凸形状は、1次元配列または2次元配列された複数の構造体により形成されている請求項1〜4のいずれか1項に記載の光学体。
- 上記構造体が、プリズム形状、シリンドリカル形状、半球状、またはコーナーキューブ状である請求項11記載の光学体。
- 第1の光学層の凹凸面上に無機材料を主成分とする中間層を形成する工程と、
上記中間層が形成された上記凹凸面を第2の光学層により包埋する工程と
を備え、
上記第1の光学層、および上記第2の光学層の少なくとも一方が、
100℃での貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体の製造方法。 - 第1の光学層の凹凸面上に無機材料を主成分とする中間層を形成する工程と、
上記中間層が形成された上記凹凸面を第2の光学層により包埋する工程と
を備え、
上記第1の光学層が、
上記包埋工程のプロセス温度をt℃としたときに、(t−20)℃における貯蔵弾性率が3×107Pa以上であり、
25℃での貯蔵弾性率が3×109Pa以下である光学体の製造方法。 - 上記包埋工程のプロセス温度tの上限が200℃以下である請求項14記載の光学体の製造方法。
- 上記第1の光学層、および/または上記第2の光学層に対して熱および圧力を加える工程をさらに備える請求項13または14に記載の光学体の製造方法。
- 上記第1の光学層、および上記第2の光学層の少なくとも一方が、エネルギー線硬化型樹脂、または熱硬化型樹脂と、架橋剤とを含んでいる請求項13または14に記載の光学体の製造方法。
- 上記架橋剤が、環状構造を有する架橋剤である請求項17記載の光学体の製造方法。