JP2011084821A - Alkaline zinc-zinc alloy plating bath - Google Patents
Alkaline zinc-zinc alloy plating bath Download PDFInfo
- Publication number
- JP2011084821A JP2011084821A JP2011018529A JP2011018529A JP2011084821A JP 2011084821 A JP2011084821 A JP 2011084821A JP 2011018529 A JP2011018529 A JP 2011018529A JP 2011018529 A JP2011018529 A JP 2011018529A JP 2011084821 A JP2011084821 A JP 2011084821A
- Authority
- JP
- Japan
- Prior art keywords
- zinc
- carboxylate
- plating bath
- pyridinium
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、種々の素地上に光沢のある亜鉛又は亜鉛合金を電着するためのめっき浴、該めっき浴で用いるための光沢剤及び該めっき浴を用いるめっき方法に関するものである。 The present invention relates to a plating bath for electrodepositing shiny zinc or zinc alloy on various substrates, a brightener for use in the plating bath, and a plating method using the plating bath.
アルカリ性亜鉛及び亜鉛合金めっき浴には水溶性亜鉛化合物、苛性ソーダ単独、または青化ソーダを併用しているものなどがある。このようなめっき液をそのまま使用して亜鉛めっきした場合、光沢のある亜鉛めっきを得ることができない。そこで光沢亜鉛めっきを得るために多種多様の光沢剤が提案されている。光沢剤としてはベース成分と光沢成分に大きく分けられる。このうち代表的なものとしては、ベース成分として各種アミンポリマー化合物、チオ尿素またはその誘導体、光沢成分として、脂肪族アルデヒド、芳香族アルデヒドおよびケトンが知られている。たとえば青化亜鉛めっきにおいては析出する亜鉛粒子を微細化して光沢性を与えるためにアニスアルデヒド、ヘリオトロピンなどの芳香族アルデヒド化合物、チオ尿素などの硫黄化合物およびポリビニルアルコール、デキストリン、ニカワなどの高分子コロイド性物質が使用されている。これらは、特公昭４５−１０２０５号公報や特公昭５３−２５２９４号公報に開示されている。
一方、ニコチン酸に塩化ベンジル等の環式有機化合物を反応させたものは光沢性に優れているため広く使用されている。しかしながらこれらの反応物は、アルカリ亜鉛めっき浴中での安定性が劣り、特に陽極上で酸化分解されやすく、その分解生成物がめっき液に浮遊し、被めっき物に付着するなど問題が多い。
またバニリンやベラトルアルデヒドなどの芳香族アルデヒドは、添加した直後の光沢性には優れているが、アルカリ性亜鉛及び合金めっき浴中での安定性が悪く、ランニングにより光沢低下が速いという欠点がある。
Some alkaline zinc and zinc alloy plating baths use a water-soluble zinc compound, caustic soda alone, or sodium blue soda. When such a plating solution is used as it is and galvanized, glossy galvanizing cannot be obtained. Therefore, a wide variety of brighteners have been proposed to obtain bright galvanizing. Brighteners can be broadly divided into base components and glossy components. As typical examples, various amine polymer compounds, thiourea or derivatives thereof as base components, and aliphatic aldehydes, aromatic aldehydes and ketones as gloss components are known. For example, in zinc blue plating, in order to refine the deposited zinc particles to give gloss, aromatic aldehyde compounds such as anisaldehyde and heliotropin, sulfur compounds such as thiourea, and polymers such as polyvinyl alcohol, dextrin and glue Colloidal material is used. These are disclosed in Japanese Patent Publication No. 45-10205 and Japanese Patent Publication No. 53-25294.
On the other hand, a product obtained by reacting nicotinic acid with a cyclic organic compound such as benzyl chloride is widely used because of its excellent gloss. However, these reactants are inferior in stability in an alkaline zinc plating bath, and are particularly susceptible to oxidative decomposition on the anode, and the decomposition products float on the plating solution and adhere to the object to be plated.
Aromatic aldehydes such as vanillin and veratraldehyde are excellent in gloss immediately after being added, but have a drawback that they are poorly stable in alkaline zinc and alloy plating baths, and the gloss is rapidly reduced by running. .
本発明は、亜鉛金属の滑らかで光輝のあるめっきが得られかつ安定なアルカリ性亜鉛及び亜鉛合金めっき浴を提供することを目的とする。
本発明は、亜鉛金属の滑らかで光輝のあるめっきが得られかつ安定なアルカリ性亜鉛及び亜鉛合金めっき浴用の光沢剤を提供することを目的とする。
本発明は、又、上記めっき浴を用いる効率的なめっき方法を提供することを目的とする。
An object of the present invention is to provide a stable alkaline zinc and zinc alloy plating bath in which a smooth and bright plating of zinc metal is obtained.
An object of the present invention is to provide a brightening agent for alkaline zinc and zinc alloy plating baths, in which a smooth and bright plating of zinc metal is obtained.
Another object of the present invention is to provide an efficient plating method using the above plating bath.
本発明は、ニコチン酸と特定の化合物との水溶性反応性生成物をアルカリ性亜鉛及び亜鉛合金めっき浴用の光沢剤として用いると、上記課題を効率的に解決できるとの知見に基づいてなされたのである。
すなわち、本発明は、（a）ニコチン酸と、（b）ハロゲン化炭化水素、アルキレンオキシド、エピハロヒドリン及びハロゲンエーテルからなる群から選ばれる少なくとも１種の化合物との水溶性反応性生成物を含有することを特徴とするアルカリ性亜鉛及び亜鉛合金めっき浴を提供する。
本発明は、又、上記反応性生成物を含有することを特徴とするアルカリ性亜鉛及び亜鉛合金めっき浴用の光沢剤を提供する。
本発明は、又、上記アルカリ性亜鉛及び亜鉛合金めっき浴を用いることを特徴とするアルカリ性亜鉛及び亜鉛合金めっき方法を提供する。
The present invention was made based on the knowledge that the above-mentioned problems can be efficiently solved by using a water-soluble reactive product of nicotinic acid and a specific compound as a brightener for alkaline zinc and zinc alloy plating baths. is there.
That is, the present invention contains a water-soluble reactive product of (a) nicotinic acid and (b) at least one compound selected from the group consisting of halogenated hydrocarbons, alkylene oxides, epihalohydrins and halogen ethers. An alkaline zinc and zinc alloy plating bath is provided.
The present invention also provides a brightener for alkaline zinc and zinc alloy plating baths characterized by containing the reactive product.
The present invention also provides an alkaline zinc and zinc alloy plating method using the alkaline zinc and zinc alloy plating bath.
本発明によれば、従来のアルカリ亜鉛及び亜鉛合金めっき浴で用いる光沢剤に比べて、光沢性及び平滑性にかつ浴安定性に優れためっき浴が得られる。 According to this invention, compared with the brightener used with the conventional alkali zinc and zinc alloy plating bath, the plating bath which was excellent in glossiness, smoothness, and bath stability is obtained.
本発明で光沢剤として用いる（a）ニコチン酸と、（b）ハロゲン化炭化水素、アルキレンオキシド、エピハロヒドリン及びハロゲンエーテルからなる群から選ばれる少なくとも１種の化合物を反応させて得られる反応性生成物は、例えば、次に示す方法により得ることができる。
（a）ニコチン酸 １モルに対して、（b）の化合物を０．５〜２モル、好ましくは１モルの割合で、水溶性反応生成物が得られるように温度７０〜１５０℃で１〜１０時間反応させる。
（b）のハロゲン化炭化水素としては、炭素数が１〜６の脂肪族ハロゲン化炭化水素が好ましく、より好ましくは、炭素数が１〜３の脂肪族ハロゲン化炭化水素である。具体的には、n-エチルブロマイド、n-プロピルブロマイド又はn-ブチルブロマイドが好ましい。
Reactive product obtained by reacting (a) nicotinic acid used as a brightener in the present invention with (b) at least one compound selected from the group consisting of halogenated hydrocarbons, alkylene oxides, epihalohydrins and halogen ethers Can be obtained, for example, by the following method.
(A) With respect to 1 mol of nicotinic acid, the compound of (b) is 0.5 to 2 mol, preferably 1 mol at a temperature of 70 to 150 ° C. so as to obtain a water-soluble reaction product. Let react for 10 hours.
The halogenated hydrocarbon (b) is preferably an aliphatic halogenated hydrocarbon having 1 to 6 carbon atoms, and more preferably an aliphatic halogenated hydrocarbon having 1 to 3 carbon atoms. Specifically, n-ethyl bromide, n-propyl bromide or n-butyl bromide is preferred.
（b）のアルキレンオキシドとしては、炭素数が２〜６のアルキレンオキシドが好ましく、より好ましく、炭素数が２〜４のアルキレンオキシドである。具体的には、エチレンオキシド、プロピレンオキシド又はブチレンオキシドが好ましい。
（b）のエピハロヒドリンとしては、炭素数が３〜６のエピハロヒドリンが好ましく、より好ましくは、炭素数が２〜５のエピハロヒドリンである。具体的には、エピクロロヒドリン、エピブロモヒドリン、エチレンクロルヒドリン又はプロピレンクロルヒドリンが好ましい。
（ｂ）のハロゲンエーテルとしては、アルキル基の炭素数が２〜１０のジクロルアルキルエーテルが好ましく、より好ましくは、２〜６である。具体的には、ジクロルエチルエーテル、ジクロルプロピルエーテル、ジクロルブチルエーテルの１種又は２種以上の混合物が好ましく、より好ましくは、クロルジメチルエーテルである。
上記反応生成物としては、可溶性４級化ニコチン酸化合物が好ましく、特に好ましい化合物は、１−エチル−ピリジニウム３−カルボキシレート、１−プロピル−ピリジニウム３−カルボキシレート、１−ブチル−ピリジニウム３−カルボキレート、１−エタノール−ピリジニウム３−カルボキシレート、１−プロパノール−ピリジニウム３−カルボキシレート、１−ブタノール−ピリジニウム３−カルボキシレート、１−ジメチルエーテル−ピリジニウム３−カルボキシレートである。これらの水溶性反応生成物は、１種又は２種以上の混合物として用いることができる。
The alkylene oxide (b) is preferably an alkylene oxide having 2 to 6 carbon atoms, more preferably an alkylene oxide having 2 to 4 carbon atoms. Specifically, ethylene oxide, propylene oxide, or butylene oxide is preferable.
The epihalohydrin (b) is preferably an epihalohydrin having 3 to 6 carbon atoms, and more preferably an epihalohydrin having 2 to 5 carbon atoms. Specifically, epichlorohydrin, epibromohydrin, ethylene chlorohydrin or propylene chlorohydrin is preferable.
The halogen ether (b) is preferably a dichloroalkyl ether having 2 to 10 carbon atoms in the alkyl group, more preferably 2 to 6. Specifically, one or a mixture of two or more of dichloroethyl ether, dichloropropyl ether and dichlorobutyl ether is preferable, and chlorodimethyl ether is more preferable.
As the reaction product, a soluble quaternized nicotinic acid compound is preferable, and particularly preferable compounds are 1-ethyl-pyridinium 3-carboxylate, 1-propyl-pyridinium 3-carboxylate, 1-butyl-pyridinium 3-carbohydrate. Chelates, 1-ethanol-pyridinium 3-carboxylate, 1-propanol-pyridinium 3-carboxylate, 1-butanol-pyridinium 3-carboxylate, 1-dimethyl ether-pyridinium 3-carboxylate. These water-soluble reaction products can be used as one kind or a mixture of two or more kinds.
本発明では、上記水溶性反応生成物をめっき浴中に０．００１〜１０ｇ／Ｌ含有させるのが好ましく、より好ましくは０．０５〜５ｇ／Ｌである。
本発明のアルカリ性亜鉛及び亜鉛合金めっき浴は、亜鉛を溶解した形態で１〜５０ｇ／Ｌ含有するのが好ましく、より好ましくは５〜２０ｇ／Ｌである。アルカリ金属水酸化物、例えば、水酸化ナトリウムを４０〜２００ｇ／Ｌ含有するのが好ましく、より好ましくは６０〜１５０ｇ／Ｌである。又、シアンを０〜１００ｇ／Ｌ添加したシアン浴でも使用できる。
本発明のアルカリ性亜鉛及び亜鉛合金めっき浴のＰＨは１３以上が好ましく、より好ましくは、ＰＨ１４以上である。
本発明のアルカリ性亜鉛及び亜鉛合金めっき浴には、種々の添加剤を含有させることができる。
例えば、珪酸塩として、コロイダルシリカ、３号珪素等のアルカリ珪酸塩を１〜１００ｇ／Ｌ含有させるのが好ましく、より好ましくは５〜５０ｇ／Ｌである。
In this invention, it is preferable to contain the said water-soluble reaction product 0.001-10 g / L in a plating bath, More preferably, it is 0.05-5 g / L.
The alkaline zinc and zinc alloy plating bath of the present invention preferably contains 1 to 50 g / L in a dissolved zinc form, more preferably 5 to 20 g / L. It is preferable to contain alkali metal hydroxide, for example, sodium hydroxide 40-200g / L, More preferably, it is 60-150g / L. Further, a cyan bath to which cyan is added at 0 to 100 g / L can also be used.
PH of the alkaline zinc and zinc alloy plating bath of the present invention is preferably 13 or more, more preferably PH14 or more.
Various additives can be contained in the alkaline zinc and zinc alloy plating bath of the present invention.
For example, it is preferable to contain 1-100 g / L of alkali silicates such as colloidal silica and No. 3 silicon as silicate, and more preferably 5-50 g / L.
本発明において、亜鉛合金としては、亜鉛と鉄、ニッケル、コバルト、マンガン等の金属の１種以上との合金があげられる。これらの金属の量は０．１〜６０質量％程度とするのがよい。これらの合金めっきを得る場合には、得ようとする合金の種類及びその合金比によって、めっき浴中の金属イオン濃度を変化させるのが好ましく、例えば、亜鉛５〜２０ｇ／Ｌに対して、鉄３０〜１０００ｍｇ／Ｌ、ニッケル０．０２〜５ｇ／Ｌ、コバルト０．０２〜５ｇ／Ｌ、マンガン０．０２〜４０ｇ／Ｌ等の１種又は２種以上を添加するのがよい。また、金属イオンは、塩化物や硫酸塩の形で供給するのがよい。
金属塩を溶解させるためにキレート剤が使用するのが好ましい。キレート剤としては、クエン酸、酒石酸、グルコン酸、グリコール酸のようなヒドロキシカルボン酸及びその塩、モノエタノールアミン、ジエタノールアミン、トリエタノールアミンのようなアミノアルコール、エチレンジアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン等のポリアミンやポリイミン、ポリアミンとエピハロヒドリン（エチレンクロルヒドリン、エピクロロヒドリン、エピブロモヒドリン）又はハロゲンエーテル（ジクロルエチルエーテル、ジクロルプロピルエーテル、ジクロルブチルエーテル）との反応物を用いるのが好ましい。これらは単独又は組み合わせて使用することができる。これらは、浴中に、０．１〜１００ｇ／Ｌ含有させるのが好ましく、より好ましくは１〜５０ｇ／Ｌである。
In the present invention, examples of the zinc alloy include alloys of zinc and one or more metals such as iron, nickel, cobalt, and manganese. The amount of these metals is preferably about 0.1 to 60% by mass. When obtaining these alloy platings, it is preferable to change the metal ion concentration in the plating bath according to the type of alloy to be obtained and the alloy ratio thereof. For example, for zinc 5 to 20 g / L, iron It is good to add 1 type, or 2 or more types, such as 30-1000 mg / L, nickel 0.02-5 g / L, cobalt 0.02-5 g / L, manganese 0.02-40 g / L. Metal ions are preferably supplied in the form of chlorides or sulfates.
A chelating agent is preferably used to dissolve the metal salt. Examples of chelating agents include hydroxycarboxylic acids such as citric acid, tartaric acid, gluconic acid and glycolic acid and salts thereof, amino alcohols such as monoethanolamine, diethanolamine and triethanolamine, ethylenediamine, diethylenetriamine, triethylenetetramine and tetraethylene. Reactions of polyamines such as pentamine, polyimines, polyamines and epihalohydrins (ethylene chlorohydrin, epichlorohydrin, epibromohydrin) or halogen ethers (dichloroethyl ether, dichloropropyl ether, dichlorobutyl ether) It is preferable to use it. These can be used alone or in combination. These are preferably contained in the bath in an amount of 0.1 to 100 g / L, more preferably 1 to 50 g / L.
本発明では、光沢剤として、上記水溶性反応物のみを用いることができるが、さらに、補助光沢成分を添加することもできる。例えばイミダゾールとエピハロヒドリンとの反応物、脂肪族アミンとエピヒドリンとの反応物、尿素とジアルキルアミノアルキルアミンとジクロルエチルエーテルまたはエピハロヒドリンとの反応物がある。これらは単独又は組み合わせて使用できる。
本発明では、被めっき基板（鉄、銅、しんちゅう等）を陰極に、亜鉛板あるいはニッケル等を陽極にし、上記めっき浴を用いて、例えば、電流密度０．０１〜１０Ａ／ｄｍ2、温度１５〜５０℃で所定のめっき厚になるまで、通常は５〜８０分間（例えば、めっき膜厚３〜２０μｍ）めっきする工程を含むめっき方法も提供する。
次に本発明を実施例を用いて説明する。
In the present invention, only the above-mentioned water-soluble reactant can be used as a brightener, but an auxiliary gloss component can also be added. For example, there are a reaction product of imidazole and epihalohydrin, a reaction product of aliphatic amine and epihydrin, and a reaction product of urea and dialkylaminoalkylamine and dichloroethyl ether or epihalohydrin. These can be used alone or in combination.
In the present invention, a substrate to be plated (iron, copper, brass, etc.) is used as a cathode, a zinc plate or nickel or the like is used as an anode, and the plating bath is used, for example, a current density of 0.01 to 10 A / dm 2 , a temperature. A plating method including a step of plating usually for 5 to 80 minutes (for example, a plating film thickness of 3 to 20 μm) until a predetermined plating thickness is obtained at 15 to 50 ° C. is also provided.
Next, the present invention will be described using examples.
実施例１
ＺｎＯ ２５ｇ／Ｌ、ＮａＣＮ ４５ｇ／Ｌ、ＮａＯＨ ７０ｇ／Ｌ、１−プロピル−ピリジニウム３−カルボキシレート ０．００５ｇ／Ｌ、ポリビニルアルコール０．１ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。
また４５℃で１週間放置後のめっき浴を同様にめっきしたところ、放置前と同等のめっき皮膜が得られた。
Example 1
A plating bath (PH14) containing ZnO 25 g / L, NaCN 45 g / L, NaOH 70 g / L, 1-propyl-pyridinium 3-carboxylate 0.005 g / L, polyvinyl alcohol 0.1 g / L, and the balance being water. The hull cell test was performed for 20 minutes at a total current of 2 A and a temperature of 25 ° C. with the iron plate as the cathode and the zinc plate as the anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained.
Further, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a plating film equivalent to that before being left was obtained.
実施例２
ＺｎＯ １２．５ｇ／Ｌ、ＮａＣＮ １５．０ｇ／Ｌ、ＮａＯＨ ７０ｇ／Ｌ、１−エタノール−ピリジニウム３−カルボキシレート０．１ｇ／Ｌ、ポリビニルアルコール０．２ｇ／Ｌ含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。
また実施例１と同様に４５℃で１週間放置後でも良好なめっき皮膜が得られた。
Example 2
Plating containing ZnO 12.5 g / L, NaCN 15.0 g / L, NaOH 70 g / L, 1-ethanol-pyridinium 3-carboxylate 0.1 g / L, polyvinyl alcohol 0.2 g / L, the balance being water A hull cell test was performed for 20 minutes at a total current of 2 A and a temperature of 25 ° C. using a bath (PH 14 or more), an iron plate as a cathode and a zinc plate as an anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained.
Further, as in Example 1, a good plating film was obtained even after being left at 45 ° C. for 1 week.
実施例３
ＺｎＯ １３ｇ／Ｌ、ＮａＯＨ １２０ｇ／Ｌ、１−ブチル−ピリジニウム３−カルボキシレート１ｇ／Ｌ、日東紡績（株）製ＰＡＳ １２０Ｌ ４ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。
また４５℃で１週間放置後のめっき浴を同様にめっきしたところ、放置前と同等の平滑性および光沢性のある緻密な亜鉛めっき皮膜が得られた。
Example 3
In a plating bath (PH14 or more) containing ZnO 13 g / L, NaOH 120 g / L, 1-butyl-pyridinium 3-carboxylate 1 g / L, Nitto Boseki Co., Ltd. PAS 120L 4 g / L, the balance being water The hull cell test was performed for 20 minutes at a total current of 2 A and a temperature of 25 ° C. using an iron plate as a cathode and a zinc plate as an anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained.
Further, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a dense galvanized film having smoothness and glossiness equivalent to that before standing was obtained.
実施例４
ＺｎＯ ２０ｇ／Ｌ、ＮａＯＨ １４０ｇ／Ｌ、１−（ジメチルエーテル）−ピリジニウム３−カルボキシレート１ｇ／Ｌ、イミダゾールとエピクロロヒドリンとの反応物０．５ｇ／Ｌ、ジメチルアミンとエピクロロヒドリンとの反応物１ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。
また４５℃で１週間放置後のめっき浴を同様にめっきしたところ、放置前と同等の、光沢性、平滑性の優れた亜鉛めっき皮膜が得られた。
Example 4
ZnO 20 g / L, NaOH 140 g / L, 1- (dimethyl ether) -pyridinium 3-carboxylate 1 g / L, reaction product of imidazole and epichlorohydrin 0.5 g / L, dimethylamine and epichlorohydrin A hull cell test was carried out at a total current of 2 A and a temperature of 25 ° C. for 20 minutes in a plating bath (PH14 or more) containing 1 g / L of the reaction product, the balance being water, an iron plate as a cathode and a zinc plate as an anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained.
Further, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a galvanized film having excellent glossiness and smoothness equivalent to that before being left was obtained.
実施例５
Ｚｎ １０ｇ／Ｌ、ＮａＯＨ １５０ｇ／Ｌ、Ｎｉ１．５ｇ／Ｌ、ジエチレントリアミンとエピクロロヒドリンの反応物２０ｇ／Ｌ、尿素、ジエチルアミノエチルアミン、ジクロルエチルエーテル反応物を４ｇ／Ｌ、１−エタノール−ピリジニウム３−カルボキシレート ０．５ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。
また４５℃で１週間放置後のめっき浴を同様にめっきしたところ、放置前と同等の光沢性、平滑性の優れた亜鉛めっき皮膜が得られた。
Example 5
Zn 10 g / L, NaOH 150 g / L, Ni 1.5 g / L, reaction product 20 g / L of diethylenetriamine and epichlorohydrin, urea, diethylaminoethylamine, dichloroethyl ether reaction product 4 g / L, 1-ethanol-pyridinium A plating bath (PH14 or more) containing 3-carboxylate 0.5 g / L, the balance being water, an iron plate as a cathode, a zinc plate as an anode, a total current amount of 2 A, and a temperature of 25 ° C. for 20 minutes. Was done. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained.
Further, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a galvanized film having the same glossiness and smoothness as that before being left was obtained.
比較例１
ＺｎＯ ２５ｇ／Ｌ、ＮａＣＮ ４０ｇ／Ｌ、ＮａＯＨ ７０ｇ／Ｌ、ニコチン酸と塩化ベンジルとの反応物０．５ｇ／Ｌ、ポリビニルアルコール０．１ｇ／Ｌ、アニスアルデヒド０．２ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。しかしながら、４５℃で１週間放置後のめっき浴を同様にめっきしたところ、全く光沢の無いめっき皮膜が得られた。
Comparative Example 1
Contains ZnO 25 g / L, NaCN 40 g / L, NaOH 70 g / L, reaction product of nicotinic acid and benzyl chloride 0.5 g / L, polyvinyl alcohol 0.1 g / L, anisaldehyde 0.2 g / L, the balance A hull cell test was performed for 20 minutes at a total current of 2 A and a temperature of 25 ° C. in a plating bath (PH 14 or higher) in which water is used as an iron plate as a cathode and a zinc plate as an anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained. However, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a plating film having no gloss was obtained.
比較例２
ＺｎＯ ２０ｇ／Ｌ、ＮａＯＨ １４０ｇ／Ｌ、アニスアルデヒド０．２ｇ／Ｌ、イミダゾールとエピハロヒドリンとの反応物０．５ｇ／Ｌ、ジメチルアミンとエピクロロヒドリンとの反応物１ｇ／Ｌを含有し、残部が水であるめっき浴（ＰＨ１４以上）に、鉄板を陰極に、亜鉛板を陽極にし、総電流量２Ａ、温度２５℃で２０分間ハルセルテストを行なった。その結果、高電流部から低電流部まで非常に緻密な光沢性、平滑性に優れた亜鉛めっき皮膜が得られた。しかしながら、４５℃で１週間放置後のめっき浴を同様にめっきしたところ、放置前に比較して光沢性、平滑性のない亜鉛めっき皮膜が得られた。
Comparative Example 2
Contains ZnO 20 g / L, NaOH 140 g / L, anisaldehyde 0.2 g / L, a reaction product of imidazole and epihalohydrin 0.5 g / L, a reaction product of dimethylamine and epichlorohydrin 1 g / L, and the balance A hull cell test was performed for 20 minutes at a total current of 2 A and a temperature of 25 ° C. in a plating bath (PH 14 or higher) in which water is used as an iron plate as a cathode and a zinc plate as an anode. As a result, a galvanized film excellent in glossiness and smoothness from a high current portion to a low current portion was obtained. However, when the plating bath was left to stand at 45 ° C. for 1 week in the same manner, a galvanized film having no glossiness and smoothness was obtained as compared with before leaving.
Claims (6)
イミダゾールとエピハロヒドリンとの反応物、脂肪族アミンとエピヒドリンとの反応物、尿素とジアルキルアミノアルキルアミンとジクロルエチルエーテルまたはエピハロヒドリンとの反応物からなる群より選ばれた補助光沢成分を含有することを特徴とするアルカリ性ノーシアン亜鉛及び亜鉛合金めっき浴。 1-ethyl-pyridinium 3-carboxylate, 1-propyl-pyridinium 3-carboxylate, 1-butyl-pyridinium 3-carboxylate, 1-ethanol-pyridinium 3-carboxylate, 1-propanol-pyridinium 3-carboxylate, A compound selected from the group consisting of 1-butanol-pyridinium 3-carboxylate and 1-dimethyl ether-pyridinium 3-carboxylate, and a reaction product of imidazole and epihalohydrin, a reaction product of aliphatic amine and epihydrin, urea and dialkyl An alkaline non-cyanide zinc and zinc alloy plating bath comprising an auxiliary gloss component selected from the group consisting of a reaction product of an aminoalkylamine and dichloroethyl ether or epihalohydrin.