JP2010522278A - Synthetic hair and its manufacturing method - Google Patents

Synthetic hair and its manufacturing method Download PDF

Info

Publication number
JP2010522278A
JP2010522278A JP2009554096A JP2009554096A JP2010522278A JP 2010522278 A JP2010522278 A JP 2010522278A JP 2009554096 A JP2009554096 A JP 2009554096A JP 2009554096 A JP2009554096 A JP 2009554096A JP 2010522278 A JP2010522278 A JP 2010522278A
Authority
JP
Japan
Prior art keywords
artificial hair
compounds
filaments
twisted
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2009554096A
Other languages
Japanese (ja)
Inventor
ローイ，ラインハルト，コルネリス ファン
Original Assignee
プロテイン ヘアー コーティング ファクトリー エスアイエー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by プロテイン ヘアー コーティング ファクトリー エスアイエー filed Critical プロテイン ヘアー コーティング ファクトリー エスアイエー
Publication of JP2010522278A publication Critical patent/JP2010522278A/en
Pending legal-status Critical Current

Abstract

人工毛であって、主として2本以上のフィラメント(2)から成り、これらのフィラメントが、撚り合わされているかまたは編み合わされており、かつ/または共通の被覆(3)を備えていることを特徴とする人工毛。
【選択図】図3Synthetic hair, mainly consisting of two or more filaments (2), characterized in that these filaments are twisted or knitted and / or provided with a common coating (3) Artificial hair.
[Selection] Figure 3

Description

本発明は、人工毛に関する。この人工毛は、特に、かつらの製造、髪延長材の製造に使用でき、人形の髪として使用でき、あるいはその他のことに使用できる。   The present invention relates to artificial hair. This artificial hair can be used, in particular, for the production of wigs, hair extension materials, can be used as doll's hair, or otherwise.

公知のように、人工毛は合成物質の単一フィラメントから成る。このフィラメントには通常、顔料が分散させられており、これがフィラメントしたがって人工毛の色を決定する。   As is known, artificial hair consists of a single filament of synthetic material. The filament is usually dispersed with a pigment, which determines the color of the filament and thus the artificial hair.

公知の人工毛のフィラメントは、合成物質、たとえばポリエステル、ナイロンまたはファッション用のアクリル樹脂(Nomex(登録商標))の押出しによって得られるモノフィラメントである。   Known artificial hair filaments are monofilaments obtained by extrusion of synthetic materials such as polyester, nylon or fashion acrylic resins (Nomex®).

公知の人工毛の直径は、どんな用途のために製造されたかにより、0.025〜0.09 mmの範囲で変えられる。人形用の人工毛は、直径0.025 mm以上とすることができるが、人間用の人工毛は、十分な機械的強度を有するように、少なくとも0.06 mmの直径とすべきである。というのは、0.05 mm以下の直径の人工毛は、強度が不十分であり、髪をくしでといているときに、破断する危険があるからである。   The diameter of the known artificial hair can be varied in the range of 0.025 to 0.09 mm, depending on what application it is made for. Artificial hair for dolls can be 0.025 mm or more in diameter, but artificial hair for humans should be at least 0.06 mm in diameter so as to have sufficient mechanical strength. This is because artificial hair having a diameter of 0.05 mm or less has insufficient strength and there is a risk of breaking when the hair is combed.

欧州人の天然毛髪は、通常、約0.05 mmの直径を有し、人間用の公知の人工毛は、通常、もっと太いので、人間の天然毛髪の挙動と人工毛の挙動とは異なり、これはもちろん好ましいことではない。   European natural hair usually has a diameter of about 0.05 mm, and known artificial hair for humans is usually thicker, so the behavior of human natural hair differs from that of artificial hair, which is Of course, it is not preferable.

公知の人工毛のもう一つの欠点は、モノフィラメントがポリアミドまたはコポリアミドで作られている場合には特にそうであるが、特定の条件下で、あるいはある種のコンディショナーを使用すると、顔料がモノフィラメントから出ていき、その結果、人工毛がその色を失い、あるいは人工毛における色むらが発生しうる、ということである。   Another disadvantage of the known artificial hairs, especially when the monofilament is made of polyamide or copolyamide, but under certain conditions or when using certain conditioners, the pigment is removed from the monofilament. As a result, the artificial hair loses its color, or color unevenness in the artificial hair can occur.

公知の人工毛のもう一つの欠点は、光がある特定の角度で入射すると、いわゆる不自然な(false)光反射が起こる、ということである。特に、黒い人工毛は、このような不自然な反射により、オレンジ色の輝きを示すことがあり、これは非常に好ましくない。前記不自然な反射は、特に、モノフィラメントがポリエステルまたはナイロン基材で作られている人工毛の場合に観察される。   Another drawback of the known artificial hair is that when light is incident at a certain angle, so-called false light reflection occurs. In particular, black artificial hair may exhibit an orange shine due to such unnatural reflection, which is very undesirable. Said unnatural reflection is observed especially in the case of artificial hair whose monofilament is made of a polyester or nylon substrate.

本発明の目的は、前記欠点およびその他の欠点の一つまたはいくつかを克服することである。   The object of the present invention is to overcome one or several of the above and other disadvantages.

この目的に応じて、本発明は、
人工毛であって、主として2本以上のフィラメントから成り、これらのフィラメントが、撚り合わされているかまたは編み合わされており、かつ/または共通の被覆を備えていることを特徴とする人工毛、
に関する。 Depending on this purpose, the present invention provides:
Artificial hair, characterized in that it consists mainly of two or more filaments, these filaments being twisted or knitted and / or provided with a common coating,
About.

本発明の利点は、繊維をかなり細くできるということである。というのは、人工毛のフィラメントの撚り合わせまたは編み合わせによって、共軸方向で、同程度の直径の公知の人工毛に比して、大きな強度が得られるからである。   An advantage of the present invention is that the fibers can be made quite thin. This is because twisting or weaving the filaments of artificial hair provides a greater strength in the coaxial direction than known synthetic hairs of the same diameter.

いくつかの繊維を共通の被覆で封じても、同じ効果が得られる。   The same effect can be achieved by sealing several fibers with a common coating.

すなわち、本発明の人工毛は、0.05 mm以下の直径を有し、人間の天然頭髪の強度と同程度以上の強度を有するように作ることができる。   That is, the artificial hair of the present invention has a diameter of 0.05 mm or less and can be made to have a strength equal to or higher than that of human natural hair.

繊維は、好ましくは、撚り合わせまたは編み合わせられ、またこれらの繊維を包囲する共通被覆が使用される。   The fibers are preferably twisted or knitted and a common coating surrounding these fibers is used.

この好ましい実施形態の一つの利点は、人工毛の構造が、薄層(plates)で包囲されたいくつかのらせん状撚り合わせケラチン繊維から成る天然繊維の周知の構造によく似ている、ということである。試験により、本発明の人工毛の挙動が天然頭髪の挙動とよく似ている、ということがわかった。   One advantage of this preferred embodiment is that the structure of the artificial hair is very similar to the well-known structure of natural fibers consisting of several helically twisted keratin fibers surrounded by plates. It is. Tests have shown that the behavior of the artificial hair of the present invention is very similar to that of natural hair.

顔料は、好ましくは、被覆に添加され、そのような被覆が人工毛の色を決定する。   Pigments are preferably added to the coating, and such coating determines the color of the artificial hair.

試験により、人工毛の被覆したがって人工毛の外表面近くに顔料を添加することにより、不自然な反射はほとんどまたはまったく起こらず、その結果、人工毛が常に自然に見える、ということがわかった。   Tests have shown that by adding pigments near the coating of the artificial hair and thus the outer surface of the artificial hair, little or no unnatural reflection occurs, so that the artificial hair always looks natural.

被覆に顔料を添加することのもう一つの利点は、顔料を安定に被覆内に分散させることができ、したがって顔料の移動または流動の危険が強く抑えられる、ということである。   Another advantage of adding pigments to the coating is that the pigment can be stably dispersed within the coating, thus greatly reducing the risk of pigment migration or flow.

以下、本発明の特徴をさらに十分に説明するために、添付の図面を参照しつつ、限定を意図しない単なる例として、本発明の人工毛の好ましい実施形態について説明する。   In order to more fully describe the features of the present invention, preferred embodiments of the artificial hair of the present invention will now be described by way of example only and not by way of limitation with reference to the accompanying drawings.

図1は、本発明の人口毛1を示す。この人口毛1は、撚り合わされた少なくとも2本、この場合は、3本のフィラメント2から成る。   FIG. 1 shows artificial hair 1 of the present invention. The artificial hair 1 is composed of at least two filaments 2 twisted together, in this case, three filaments 2.

フィラメント2は、好ましくは、ポリエステル(PE)、ナイロン(PA)、ポリエチレンテレフタレート(PET)、ファッション用アクリル(Nomex(登録商標))、ポリブチルテレフタレート(PBT)、ポリエチレン、ポリオキシメチレン(POM)、ポリテトラフルオロエチレン(PTFE)、芳香族ポリアミド(アラミド、たとえばケブラー(登録商標))から成るグループから選択される一つまたはいくつかの合成物質のモノポリマーまたはコポリマーで作られる。ここで、合成フィラメント2内には、顔料を分散させることもさせないことも可能である。   Filament 2 is preferably polyester (PE), nylon (PA), polyethylene terephthalate (PET), fashion acrylic (Nomex (registered trademark)), polybutyl terephthalate (PBT), polyethylene, polyoxymethylene (POM), Made of one or several synthetic monopolymers or copolymers selected from the group consisting of polytetrafluoroethylene (PTFE), aromatic polyamide (aramid, eg Kevlar®). Here, it is possible to disperse the pigment in the synthetic filament 2 or not.

フィラメント2がナイロン(PA)を含む場合、このナイロンは、好ましくは、PA6、PA6.6、PA11、PA12、PA6/12、PA6.10、PA4.6、PA6/6.6、PA6.12、PA66またはPEから成るグループから選択される一つのPAである。   When filament 2 comprises nylon (PA), this nylon is preferably PA6, PA6.6, PA11, PA12, PA6 / 12, PA6.10, PA4.6, PA6 / 6.6, PA6.12, PA66 or A PA selected from the group consisting of PEs.

明らかに、フィラメント2を撚り合わせることにより、非撚り合わせまたは非ねじり形状の同じフィラメントを有する人工毛に比して、共軸方向の強度の大きな人工毛1が得られ、その結果、共軸方向における人工毛の強度が人間の天然頭髪よりも小さくなることなく、本発明の人工毛1の直径を、0.06 mmよりも小、好ましくは0.05 mmよりも小に抑えることができる。   Obviously, twisting the filaments 2 gives artificial hairs 1 with higher coaxial strength compared to artificial hairs having the same filaments in untwisted or non-twisted shape, resulting in the coaxial direction The diameter of the artificial hair 1 of the present invention can be suppressed to be smaller than 0.06 mm, preferably smaller than 0.05 mm, without the strength of the artificial hair being smaller than that of human natural hair.

また、当然のことながら、本発明においては、撚り合わせという言葉は広い意味に解釈すべきであり、すなわち、ねじり、曲げ、らせん巻き、その他の意味にも解釈すべきである。   Of course, in the present invention, the term twisting should be interpreted in a broad sense, that is, twisting, bending, spiral winding, and other meanings.

さらに、フィラメント2は、編み合わせることもできる。   Furthermore, the filament 2 can also be knitted.

注意すべきことは、本発明の人工毛1には、好ましくは、3〜34本のフィラメント2を使用することができ、これらのフィラメント2は撚り合わせるか編み合わせることができ、あるいは2本以上のフィラメントを撚り合わせるか編み合わせて、繊維とし、それからいくつかのそのような繊維を撚り合わせるか編み合わせることができる、ということである。   It should be noted that the artificial hair 1 of the present invention can preferably use 3 to 34 filaments 2, and these filaments 2 can be twisted or knitted, or two or more. The filaments can be twisted or knitted into a fiber, and then several such fibers can be twisted or knitted.

フィラメント2の形状に関して注意すべきことは、フィラメント2は、円形断面のほか、楕円、二重円(double round)、その他の形状の断面を有することができる、ということである。   It should be noted about the shape of the filament 2 that the filament 2 can have an elliptical, double round, or other shaped cross section in addition to a circular cross section.

図2は、少なくとも長さの一部にわたって、2本以上のフィラメント2が共通の被覆3に包囲されている変形実施形態を示す。   FIG. 2 shows a variant embodiment in which two or more filaments 2 are surrounded by a common coating 3 over at least part of the length.

この被覆3には、人工毛1の色を決定する顔料を添加してもしなくてもよい。   This coating 3 may or may not contain a pigment that determines the color of the artificial hair 1.

被覆3は、好ましくは、ポリウレタン化合物、ビスコースポリウレタン化合物、アクリル化合物、ビニル化合物、テフロン(登録商標)化合物、ビスコースナイロン化合物、ビスコースポリエステル化合物から成るグループから選択される一つの要素を基材として作られる。   The coating 3 is preferably based on one element selected from the group consisting of polyurethane compounds, viscose polyurethane compounds, acrylic compounds, vinyl compounds, Teflon (registered trademark) compounds, viscose nylon compounds, viscose polyester compounds. Made as.

注意すべきことは、共通被覆3という言葉は、被覆3が、それぞれのフィラメント2がまとまって、被覆された単一の束を作るように、フィラメントのまわりに備えられる、ということを意味する。   It should be noted that the term common coating 3 means that the coating 3 is provided around the filaments so that each filament 2 is bundled together to form a single bundle coated.

人工毛1に着色するための顔料は被覆3に添加されるので、明らかに、これらの顔料は、人工毛1の表面またはそのすぐ近くに配置され、したがって不自然な反射効果が防止される。   Since pigments for coloring the artificial hair 1 are added to the coating 3, it is clear that these pigments are placed at or near the surface of the artificial hair 1, thus preventing unnatural reflection effects.

最後に、図3は、本発明の人工毛のもう一つの変形実施形態を示す。この場合、撚り合わされるかねじりあわされたいくつかのフィラメント2が、前記共通被覆3を備えている。   Finally, FIG. 3 shows another variant embodiment of the artificial hair of the present invention. In this case, several filaments 2 twisted or twisted are provided with the common coating 3.

注意すべきことは、この変形実施形態における人工毛1においては、好ましくは3〜34本のフィラメント2が使用され、これらのフィラメント2は、撚り合わされるか編み合わされるかすることができ、あるいは2本以上のフィラメントを撚り合わせるか編み合わせて繊維とし、それからこれらの繊維のいくつかを撚り合わせるかまたは編み合わせることができる、ということである。   It should be noted that in the artificial hair 1 in this variant embodiment, preferably 3 to 34 filaments 2 are used, these filaments 2 can be twisted or knitted, or Two or more filaments can be twisted or knitted into fibers, and then some of these fibers can be twisted or knitted.

フィラメント2の形状に関して注意すべきことは、これらのフィラメントは、円形断面のほか、楕円、二重円、その他の形状の断面を有することができる、ということである。   It should be noted with respect to the shape of the filament 2 that these filaments can have an elliptical, double-circular or other shaped cross section in addition to a circular cross section.

本発明は、図面に示した前記実施形態のみに限定されるものではない。逆に、本発明の人工毛は、本発明の範囲を逸脱することのないあらゆる種類の変形を加えて具体化することができる。   The present invention is not limited only to the embodiment shown in the drawings. On the contrary, the artificial hair of the present invention can be embodied by adding all kinds of modifications without departing from the scope of the present invention.

本発明の人口毛の斜視図である。It is a perspective view of artificial hair of the present invention. 図1の人口毛の変形を示す図である。FIG. 2 is a diagram showing a deformation of artificial hair of FIG. 図1の人口毛のもう一つの変形を示す図である。FIG. 2 is a diagram showing another variation of the artificial hair of FIG.

1 人工毛
2 フィラメント
3 被覆 1 Synthetic hair
2 Filament
3 Coating

Claims (8)

人工毛であって、主として2本以上のフィラメント(2)から成り、これらのフィラメントが、撚り合わされているかまたは編み合わされており、かつ/または共通の被覆(3)を備えていることを特徴とする人工毛。   Synthetic hair, mainly consisting of two or more filaments (2), characterized in that these filaments are twisted or knitted and / or provided with a common coating (3) Synthetic hair. 当該フィラメント(2)が、撚り合わされているかまたは編み合わされており、かつ共通の被覆(3)を備えていることを特徴とする請求項1に記載の人工毛。   The artificial hair according to claim 1, characterized in that the filament (2) is twisted or knitted and provided with a common coating (3). 3〜34本の編み合わされるかまたは撚り合されているフィラメント(2)から成ることを特徴とする請求項1または2に記載の人工毛。   3. An artificial hair according to claim 1 or 2, characterized in that it comprises 3 to 34 filaments (2) which are knitted or twisted. 被覆(3)に顔料が添加されていることを特徴とする請求項1から3の中のいずれか一つに記載の人工毛。 The artificial hair according to any one of claims 1 to 3, wherein a pigment is added to the coating (3). フィラメント(2)が合成物質で作られていることを特徴とする請求項1から4の中のいずれか一つに記載の人工毛。   5. The artificial hair according to claim 1, wherein the filament (2) is made of a synthetic material. 当該合成物質が、ポリエステル(PE)、ナイロン(PA)、ポリエチレンテレフタレート(PET)、ファッション用アクリル(Nomex(登録商標))、ポリブチルテレフタレート(PBT)、ポリエチレン、ポリオキシメチレン(POM)、ポリテトラフルオロエチレン(PTFE)または芳香族ポリアミド(アラミド)から成るグループから選択される一つまたはいくつかの成分のモノポリマーまたはコポリマーから成ることを特徴とする請求項5に記載の人工毛。   The synthetic materials are polyester (PE), nylon (PA), polyethylene terephthalate (PET), acrylic for fashion (Nomex (registered trademark)), polybutyl terephthalate (PBT), polyethylene, polyoxymethylene (POM), polytetra 6. The artificial hair according to claim 5, comprising a monopolymer or copolymer of one or several components selected from the group consisting of fluoroethylene (PTFE) or aromatic polyamide (aramid). 当該被覆(3)が、ポリウレタン化合物、ビスコースポリウレタン化合物、アクリル化合物、ビニル化合物、テフロン(登録商標)化合物、ビスコースナイロン化合物、ビスコースポリエステル化合物から成るグループから選択される一つの化合物から成ることを特徴とする請求項1から6の中のいずれか一つに記載の人工毛。   The coating (3) is made of one compound selected from the group consisting of polyurethane compounds, viscose polyurethane compounds, acrylic compounds, vinyl compounds, Teflon (registered trademark) compounds, viscose nylon compounds, and viscose polyester compounds. The artificial hair according to any one of claims 1 to 6, wherein: 0.06 mmよりも小、好ましくは0.05 mmよりも小の直径を有することを特徴とする請求項1から7の中のいずれか一つに記載の人工毛。   8. The artificial hair according to any one of claims 1 to 7, characterized in that it has a diameter of less than 0.06 mm, preferably less than 0.05 mm.
JP2009554096A 2007-03-22 2008-03-20 Synthetic hair and its manufacturing method Pending JP2010522278A (en)