JP2007247341A - Water proof structure - Google Patents
Water proof structure Download PDFInfo
- Publication number
- JP2007247341A JP2007247341A JP2006075135A JP2006075135A JP2007247341A JP 2007247341 A JP2007247341 A JP 2007247341A JP 2006075135 A JP2006075135 A JP 2006075135A JP 2006075135 A JP2006075135 A JP 2006075135A JP 2007247341 A JP2007247341 A JP 2007247341A
- Authority
- JP
- Japan
- Prior art keywords
- waterproof
- resin
- thermoplastic resin
- water proof
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は建築物の屋上、ベランダまたはバルコニー等の屋外のコンクリート製などの躯体表面に塗工された塗膜防水材と熱可塑性樹脂系防水シートの接合する防水構造に関するものである。 The present invention relates to a waterproof structure in which a waterproof coating material coated on a roof surface of a building, an outdoor concrete body such as a balcony or a balcony, and a thermoplastic resin waterproof sheet are joined.
従来、熱可塑性樹脂系防水シートと塗膜防水材を併用する際には、平場部などの比較的容易な部分は熱可塑性樹脂系防水シートを敷設し、躯体の構造上施工が困難な部分、例えば架台回りや側溝部には塗膜防水材を塗布する場合がある。その施工方法として主に以下に記載する二つの方法がある。一つは塗膜防水材を熱可塑性樹脂系防水シート上まで塗膜することにより一体化する工法であり、二つめは塗膜防水材上に定形接着材を貼りつけ、その定形接着材上に熱可塑性樹脂系防水シートを貼りあわせることにより接合する方法である。 Conventionally, when using a thermoplastic resin-based waterproof sheet and a waterproof coating material together, a relatively easy part such as a flat field part is laid with a thermoplastic resin-based waterproof sheet, and the construction of the housing is difficult, For example, a waterproof coating material may be applied around the pedestal or the side groove. There are two main methods of construction as described below. The first is a method of integrating the waterproof coating material by coating it onto the thermoplastic resin waterproof sheet, and the second is to apply a fixed adhesive on the waterproof waterproof film, and then onto the fixed adhesive. It is a method of joining by sticking together a thermoplastic resin waterproof sheet.
図２は、従来の熱可塑性樹脂系防水シートとウレタン系塗膜防水とを接合した防水構造の一例を示したものである。 FIG. 2 shows an example of a waterproof structure in which a conventional thermoplastic resin waterproof sheet and urethane film waterproof are joined.
図示するように、この防水構造はコンクリート躯体上に固定ビスを使用して定形接着材上に樹脂被覆鋼板を留めつけ、その樹脂被覆鋼板上に熱可塑性樹脂系防水シートの端部を重ね合わせ熱融着または溶剤溶着により接合したのち、熱可塑性樹脂系防水シートの端部上にプライマーを塗布して、プライマー乾燥後に塗膜防水材を塗布することにより一体化する工法である。しかしながら、この構造では、樹脂被覆鋼板や固定ビス及び定形接着材などの副資材が必要であるため、手間がかかることとコスト高になってしまう。また、定形接着材および樹脂被覆鋼板上に熱可塑性樹脂系防水シートさらにその上に塗膜防水材が形成されるため、接合部分は隆起して仕上がりが良くない。さらに、意匠性を有する熱可塑性樹脂系防水シートの場合には、熱可塑性樹脂系防水シート上に塗膜防水材が積層されるため、その意匠が隠れてしまうという問題が存在する。 As shown in the figure, this waterproof structure uses a fixing screw on a concrete frame to fasten a resin-coated steel sheet on a fixed adhesive, and heats the end of a thermoplastic resin-based waterproof sheet on the resin-coated steel sheet. After joining by fusion or solvent welding, a primer is applied on the end portion of the thermoplastic resin waterproof sheet, and the primer is dried and then applied by applying a waterproof coating material. However, this structure requires additional materials such as a resin-coated steel plate, a fixed screw, and a fixed adhesive, which is troublesome and expensive. Further, since the thermoplastic resin waterproof sheet is formed on the regular adhesive and the resin-coated steel sheet, and the waterproof film is formed on the thermoplastic resin waterproof sheet, the joint portion is raised and the finish is not good. Further, in the case of a thermoplastic resin-based waterproof sheet having design properties, there is a problem that the design is hidden because the waterproof coating material is laminated on the thermoplastic resin-based waterproof sheet.
上記問題点を解消する防水構造として、図３に示すように塗膜防水材上に定形接着材を貼りつけ、その定形接着材と熱可塑性樹脂系防水シートを貼り合わせることにより塗膜防水材と接合する防水構造（特許文献１）が知られている。 As a waterproof structure that solves the above-mentioned problems, a waterproof adhesive film is applied by attaching a fixed adhesive on a waterproof coating film as shown in FIG. 3 and bonding the fixed adhesive and a thermoplastic resin waterproof sheet together. A waterproof structure to be joined (Patent Document 1) is known.
しかしながら、この方法も定形接着剤を介して接合しているため、熱可塑性樹脂系防水シートに可塑剤などの液状成分が含有されている場合には、定形接着材にそれら液状成分が移行し、長期的にみると接合部分のみ硬化および劣化が著しくなったり、亀裂を生じて漏水する危険性がでてくる。また、定形接着材の影響により熱可塑性樹脂系防水シートが変色する危険性もある。さらに、熱可塑性樹脂系防水シートと塗膜防水材は定形接着材の接着力のみに依存するため、長期の使用に際し接着性の低下により、定形接着材と熱可塑性樹脂系防水シートあるいは塗膜防水材の界面から剥離する恐れがあり、水密性の確保に問題がある。 However, since this method is also joined through a fixed adhesive, when the thermoplastic resin waterproof sheet contains a liquid component such as a plasticizer, the liquid component migrates to the fixed adhesive, In the long term, there is a risk that only the joint will be hardened and deteriorated, and there will be a risk of water leakage due to cracks. In addition, there is a risk that the thermoplastic resin waterproof sheet may be discolored due to the influence of the fixed adhesive. In addition, since the thermoplastic resin-based waterproof sheet and the waterproof coating material depend only on the adhesive strength of the fixed adhesive, the fixed adhesive and the thermoplastic resin-based waterproof sheet or the waterproof coating film are used due to a decrease in adhesiveness during long-term use. There is a risk of peeling from the interface of the material, and there is a problem in ensuring water tightness.
そこで、本発明は熱可塑性樹脂系防水シートを塗膜防水材上に接合する際に、長期的な使用においても充分な接合強度、水密性といった防水性能を確保し、かつ従来通りの熱可塑性樹脂系防水シート同士の接合方法と同様に熱融着または溶剤溶着で接合できる防水構造を提供することを目的とする。 Therefore, the present invention ensures a waterproof performance such as sufficient bonding strength and water tightness even in long-term use when bonding a thermoplastic resin waterproof sheet on a waterproof coating film, and a conventional thermoplastic resin. It aims at providing the waterproof structure which can be joined by heat sealing | fusion or solvent welding similarly to the joining method of type | system | group waterproof sheets.
上記課題を解決するために講じた本発明の手段は、コンクリート、プレキャストコンクリート、ＡＬＣ（Ａｕｔｏｃｌａｖｅｄ ｌｉｇｈｔ ｗｅｉｇｈｔ ｃｏｎｃｒｅｔｅ）板等の躯体に塗工された塗膜防水材上に熱可塑性樹脂を含有する液状樹脂を塗布し固化して樹脂膜層を形成させ、その樹脂膜層に熱可塑性樹脂系防水シートを重ね合わせ熱融着または溶剤溶着により接合する防水構造としたことであり、上記液状樹脂が熱可塑性樹脂系防水シートと同素材の樹脂を含有する防水構造としたことである。 The means of the present invention taken in order to solve the above problems is a liquid resin containing a thermoplastic resin on a waterproof coating material coated on a casing such as concrete, precast concrete, ALC (Autoclaved light weight concrete) board, etc. Is applied to the resin film layer to form a resin film layer, and a waterproof structure in which a thermoplastic resin waterproof sheet is superposed on the resin film layer and bonded by thermal fusion or solvent welding is used. The liquid resin is thermoplastic. This is a waterproof structure containing a resin of the same material as the resin waterproof sheet.
本発明によれば、従来の熱可塑性樹脂系防水シート同士の接合方法と同様に、熱可塑性樹脂系防水シートと塗膜防水材とを熱融着または溶剤溶着で接合でき、充分な接合強度、水密性を確保することができる。また、熱可塑性樹脂系防水シートが意匠性を有する防水シートであっても、その意匠を損なうことはない。 According to the present invention, the thermoplastic resin-based waterproof sheet and the waterproof coating material can be bonded together by thermal fusion or solvent welding in the same manner as in the conventional bonding method between thermoplastic resin-based waterproof sheets, sufficient bonding strength, Watertightness can be ensured. Moreover, even if the thermoplastic resin-based waterproof sheet is a waterproof sheet having design properties, the design is not impaired.
さらに、従来のような定形接着材を使用しないため、熱可塑性樹脂系防水シートに可塑剤などの液状成分が含有されていても、液状成分の移行による不具合がない。また、定形接着材を使用しないので、従来のような極端な段差も生じることなく、仕上がりの見栄えがよくなる。 Furthermore, since a conventional fixed adhesive is not used, even if a liquid component such as a plasticizer is contained in the thermoplastic resin waterproof sheet, there is no problem due to the migration of the liquid component. In addition, since no fixed adhesive is used, the appearance of the finish is improved without causing an extreme step as in the prior art.
本発明で使用する液状樹脂は、熱可塑性樹脂系防水シートと接合性がよいことが必要であり、液状樹脂及び防水シートに用いられる熱可塑性樹脂は互いに組成的に近いことがよく、同素材であることがより好ましい。このことにより液状樹脂と防水シートとの接合が強固になり、充分な密着性および水密性を確保することができる。 The liquid resin used in the present invention needs to have good bondability with the thermoplastic resin-based waterproof sheet, and the thermoplastic resin used for the liquid resin and the waterproof sheet should be close to each other in terms of composition. More preferably. As a result, the bonding between the liquid resin and the waterproof sheet is strengthened, and sufficient adhesion and water tightness can be ensured.
液状樹脂に用いられる熱可塑性樹脂は特に限定されないが、塩化ビニル系樹脂、塩素化ポリエチレン、エチレン−酢酸ビニル共重合体、ポリオレフィン系樹脂、アクリル系樹脂、熱可塑性エラストマー（オレフィン系、スチレン系、ポリエステル系、ウレタン系）などが挙げられ、塩化ビニル系樹脂、エチレン−酢酸ビニル系樹脂、熱可塑性エラストマーが好ましい。 The thermoplastic resin used for the liquid resin is not particularly limited, but vinyl chloride resin, chlorinated polyethylene, ethylene-vinyl acetate copolymer, polyolefin resin, acrylic resin, thermoplastic elastomer (olefin, styrene, polyester) And vinyl chloride resins, ethylene-vinyl acetate resins, and thermoplastic elastomers are preferred.
液状樹脂は、上記樹脂を溶剤に溶解したもの、上記樹脂を分散媒に分散したものなどを使用することができる。
通常、防水シートには塩化ビニル樹脂製のものが使用されることが多く、その場合、耐久性及び防水シートとの接合性を考慮すると、液状樹脂は塩化ビニル系樹脂が好ましく、防水シート表層配合と近似の組成物を溶剤に溶解したものが好ましい。
As the liquid resin, one obtained by dissolving the resin in a solvent, one obtained by dispersing the resin in a dispersion medium, or the like can be used.
Usually, a vinyl chloride resin is often used for the waterproof sheet. In that case, in consideration of durability and bondability with the waterproof sheet, the liquid resin is preferably a vinyl chloride resin, and the waterproof sheet has a surface layer composition. And an approximate composition dissolved in a solvent are preferred.
液状樹脂の粘度は１０００〜２００００ｍPa・sがよく、より好ましくは２０００〜５０００ｍPa・sである。５０００ｍPa・s以上であると取扱い性、塗工性などの作業性が悪くなる傾向があり、逆に２０００ｍPa・s未満であると粘度が低く塗膜防水上に塗布した際に流れ易くなり膜圧を確保しづらくなる。 The viscosity of the liquid resin is preferably 1000 to 20000 mPa · s, more preferably 2000 to 5000 mPa · s. When it is 5000 mPa · s or more, workability such as handling property and coating property tends to be deteriorated. On the other hand, when it is less than 2000 mPa · s, the viscosity is low and it is easy to flow when applied on the waterproof coating film. It is difficult to secure.
液状樹脂を塗布して固化した時の厚みは０．２〜０．５ｍｍが好ましい。厚みが０．２ｍｍ未満であると、液状樹脂で形成した樹脂膜層と熱可塑性樹脂系防水シートを熱融着で接合する際に、樹脂膜層が溶けて塗膜防水材が出現して溶着されない恐れがある。また、厚みが０．５ｍｍ以上になるように液状樹脂を塗布すると、厚く塗布しなければならず、溶剤の揮発時間が長くなってしまう。そのため樹脂膜層を形成するまでの固化時間が長くなってしまい、次の作業工程に進むのが遅くなる恐れがある。 The thickness when the liquid resin is applied and solidified is preferably 0.2 to 0.5 mm. When the thickness is less than 0.2 mm, when the resin film layer formed of a liquid resin and the thermoplastic resin waterproof sheet are joined by thermal fusion, the resin film layer melts and a waterproof coating material appears and is welded. There is a fear that it will not be. Further, if the liquid resin is applied so that the thickness is 0.5 mm or more, it has to be applied thickly, and the volatilization time of the solvent becomes long. For this reason, the solidification time until the resin film layer is formed becomes long, and there is a possibility that the process proceeds to the next work process.
液状樹脂を塗工するには、ゴムベラ、櫛目ゴテ、オイラー、ローラー刷毛などを使用することができる。 In order to apply the liquid resin, rubber spatula, comb iron, Euler, roller brush and the like can be used.
本発明で使用する塗膜防水材としては、ウレタン系塗膜防水材、アクリルゴム系塗膜防水材、クロロプレン系塗膜防水材、ゴムアスファルト系塗膜防水材、ＦＲＰ系塗膜防水材、ポリマーセメント系塗膜防水材が挙げられる。なかでも、作業性を考慮すると、ウレタン系塗膜防水材、アクリルゴム系塗膜防水材が好ましい。通常は、その上に仕上げ材としてトップコートが塗布される。 Examples of the waterproof membrane used in the present invention include urethane-based waterproof membrane, acrylic rubber-based waterproof membrane, chloroprene-based waterproof membrane, rubber asphalt-based waterproof membrane, FRP-based waterproof membrane, polymer A cement-based waterproofing material can be used. Especially, when workability | operativity is considered, a urethane type coating-film waterproofing material and an acrylic rubber-type coating-film waterproofing material are preferable. Usually, a top coat is applied as a finishing material thereon.
仕上げ材として使用されるトップコートとしては、アクリル系、アクリルウレタン系、アクリルシリコン系、ポリエステル系、フッ素系、エポキシ系などのコート材が挙げられる。 Examples of the top coat used as the finishing material include acrylic, acrylic urethane, acrylic silicon, polyester, fluorine, and epoxy coating materials.
仕上げ材としての上記トップコートを塗布して固化した時の厚みは０．０５〜０．３ｍｍが好ましい。０．０５ｍｍ未満では液状樹脂との密着性が低下し、０．３ｍｍ以上では乾燥時間が長くなってしまう。 The thickness when the top coat as a finishing material is applied and solidified is preferably 0.05 to 0.3 mm. If it is less than 0.05 mm, the adhesiveness with the liquid resin is lowered, and if it is 0.3 mm or more, the drying time becomes long.
塗膜防水材の上にトップコートを塗布して、液状樹脂をその上に塗布する際には、トップコートが完全に乾燥する前に液状樹脂を塗布することが好ましい。これにより液状樹脂とトップコートとの充分な密着強度が得ることができる。 When a top coat is applied on the waterproof coating material and the liquid resin is applied thereon, the liquid resin is preferably applied before the top coat is completely dried. Thereby, sufficient adhesion strength between the liquid resin and the top coat can be obtained.
本発明で使用する防水シートに用いられる熱可塑性樹脂としては、塩化ビニル系樹脂、塩素化ポリエチレン、エチレン−酢酸ビニル共重合体、ポリオレフィン系樹脂、アクリル系樹脂、熱可塑性エラストマー（オレフィン系、スチレン系、ポリエステル系、ウレタン系）などが挙げられる。 The thermoplastic resin used in the waterproof sheet used in the present invention includes vinyl chloride resin, chlorinated polyethylene, ethylene-vinyl acetate copolymer, polyolefin resin, acrylic resin, thermoplastic elastomer (olefin-based, styrene-based). , Polyester and urethane).
塗膜防水材と熱可塑性樹脂系防水シートとを接合するには、塗膜防水材上の所定位置に４０〜７０ｍｍの幅になるように液状樹脂を塗布し、その幅で熱可塑性樹脂系防水シートを接合するとよい。この幅が７０ｍｍ以上だと熱可塑性樹脂系防水シートとの接合に時間が掛かりすぎ、４０ｍｍ以下であると充分な水密性を確保することができない恐れが出てくる。 In order to join the waterproof coating material and the thermoplastic resin waterproof sheet, a liquid resin is applied to a predetermined position on the waterproof coating material so that the width is 40 to 70 mm, and the thermoplastic resin waterproof is applied with the width. It is advisable to join the sheets. If this width is 70 mm or more, it takes too much time to join the thermoplastic resin waterproof sheet, and if it is 40 mm or less, there is a possibility that sufficient watertightness cannot be ensured.
以下、本発明を、実施例を挙げてさらに詳しく説明する。 Hereinafter, the present invention will be described in more detail with reference to examples.
熱可塑性樹脂系防水シートとして、塩化ビニルシート（当社製：ロンプルーフエース ２．０ｍｍ）、塗膜防水材に２液型ウレタン系塗膜防水材および液状樹脂として、上記ロンプルーフエースの表層組成物１００重量部に対して溶剤（ＴＨＦ：シクロヘキサノン＝７：３）３００重量部に溶かし増粘剤で粘度を３０００ｍPa・sに調整したものを使用した。 As a thermoplastic resin-based waterproof sheet, a vinyl chloride sheet (made by our company: Romproof Ace 2.0 mm), a two-component urethane-based waterproofing film and a liquid resin as a coating film waterproofing material, and a surface layer composition of the above-mentioned Rompproof Ace 100 parts by weight of a solvent (THF: cyclohexanone = 7: 3) dissolved in 300 parts by weight and having a viscosity adjusted to 3000 mPa · s with a thickener was used.
まず、コンクリート下地にプライマー（当社製：ロンレタンプライマー）を塗布し乾燥させた後、２液型ウレタン系塗膜防水材を２．７ｋｇ／ｍ２を塗布して、硬化させたのち、その上に２液型アクリルウレタン系トップコートを０．３ｋｇ／ｍ２を塗布した。１時間後トップコートが乾燥する前に、アクリルウレタン系トップコートの端部上に６０ｍｍ幅になるよう上記液状樹脂を１．５ｋｇ／ｍ２で塗布して固化させた後、その上に上記厚さ２．０ｍｍの塩化ビニルシートを５０ｍｍ幅になるよう重ね合わせ、刷毛を用いて溶剤溶着により液状樹脂の層と塩化ビニルシートとを接合した。 First, a primer (manufactured by our company: Ronretane Primer) is applied to the concrete base, dried, and then applied with 2.7 kg / m 2 of a two-component urethane-based waterproofing film, and then cured. the two-pack type acrylic urethane-based topcoat was applied 0.3 kg / m 2 to. After 1 hour before the top coat dries, the liquid resin is applied at 1.5 kg / m 2 so as to have a width of 60 mm on the end portion of the acrylic urethane top coat and then solidified, and then the above thickness A 2.0 mm-thick vinyl chloride sheet was laminated to a width of 50 mm, and the liquid resin layer and the vinyl chloride sheet were joined by solvent welding using a brush.
一週間養生後、塩化ビニルシートとトップコート付きウレタン系塗膜防水材とを接合した部分を３０ｍｍ幅の短冊状にカッターで切り込みを入れ、引張試験機を使用して塩化ビニルシート側から９０度剥離試験（ＪＩＳ Ａ５５３６「ビニル系床材用接着剤」の「９０度はく離接着強さ試験」に準拠、但し、試験片の幅は３０ｍｍで実施）を行なった。また、環境の変化による接合性の確認を目的として、一週間養生後からさらに８０℃のオーブンで一週間加熱後、および温水６０℃の恒温槽に一週間浸漬後の試験体についても同様の９０度剥離試験を行なった。その結果を表１に示す。 After curing for one week, cut the portion where the vinyl chloride sheet and the urethane-based waterproofing material with a top coat were joined into a 30mm wide strip with a cutter, and 90 degrees from the vinyl chloride sheet side using a tensile tester A peel test (in accordance with “90 degree peel adhesion strength test” of JIS A5536 “Adhesive for vinyl flooring”) was carried out, but the test piece width was 30 mm. In addition, for the purpose of confirming the bonding property due to environmental changes, the same 90 is applied to the test specimen after curing for one week, heating for another week in an oven at 80 ° C., and immersed in a constant temperature bath at 60 ° C. for one week. A peel test was performed. The results are shown in Table 1.
一般に防水シート同士の接合において、上記９０度剥離試験の評価では３０Ｎ／３０ｍｍ以上が必要とされている。表１から明らかなように、いずれの環境下においても充分な接着強度を示し、破断状況においては、塩化ビニルシートもしくはウレタン系塗膜防水材の材料破壊であった。このことから、液状樹脂による塗膜防水材と熱可塑性樹脂系防水シートとの接合が充分な強度を有し密着性が優れていることを確認できた。 Generally, in joining the waterproof sheets, 30N / 30 mm or more is required in the evaluation of the 90-degree peel test. As is clear from Table 1, the adhesive strength was sufficient in any environment, and the material was broken in the vinyl chloride sheet or the urethane-based coating waterproof material in the breaking state. From this, it was confirmed that the bonding between the waterproof coating film made of liquid resin and the thermoplastic resin waterproof sheet had sufficient strength and excellent adhesion.
本発明の防水構造により、熱可塑性樹脂系防水シート同士の接合と同様に熱融着または溶剤溶着で、液状樹脂の塗工層を表面に有する塗膜防水材と熱可塑性樹脂系防水シートとを容易に接合でき、長期的に使用しても充分な接合強度、水密性といった防水性能を確保できるため、建築物の屋上、ベランダ、バルコニーなどの防水構造に、広く利用することができる。 According to the waterproof structure of the present invention, a waterproof coating material having a liquid resin coating layer on its surface and a thermoplastic resin waterproof sheet by thermal fusion or solvent welding in the same manner as joining of thermoplastic resin waterproof sheets. Since it can be easily joined and waterproof performance such as sufficient joint strength and water tightness can be secured even after long-term use, it can be widely used for waterproof structures such as rooftops of buildings, verandas, and balconies.
１ コンクリート躯体
２ コンクリート用プライマー
３ 塗膜防水材
４ トップコート
５ 液状樹脂層
６ 熱可塑性樹脂系防水シート
７ 防水シート用プライマー
８ 定形接着材
９ 樹脂被覆鋼板
１０ 固定ビス
DESCRIPTION OF
Claims (2)
The waterproof structure characterized in that the liquid resin contains a resin of the same material as the thermoplastic resin-based waterproof sheet.