KR101142857B1 - Improved waterproof sheet, method for constructing waterproof and waterproof structure using the same - Google Patents
Improved waterproof sheet, method for constructing waterproof and waterproof structure using the same Download PDFInfo
- Publication number
- KR101142857B1 KR101142857B1 KR1020090024118A KR20090024118A KR101142857B1 KR 101142857 B1 KR101142857 B1 KR 101142857B1 KR 1020090024118 A KR1020090024118 A KR 1020090024118A KR 20090024118 A KR20090024118 A KR 20090024118A KR 101142857 B1 KR101142857 B1 KR 101142857B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproof
- sheet
- asphalt
- layer
- waterproof sheet
- Prior art date
Abstract
개시된 본 발명은 모체의 표면에 아스팔트 프라이머가 도포되어 형성된 아스팔트 프라이머층과, 이 아스팔트 프라이머층의 상부에 부직포가 부착된 방수시트를 맞대음 형식으로 배치시켜 형성된 시트방수층과, 이 시트방수층에서 상기 개량방수시트들의 맞대음 조인트부분에 아스팔트 프라이머층과 같은 계통의 재질로 도포되어 형성된 수밀부와, 이 수밀부의 외부표면과 그 주위에 수밀성을 유지하면서 고정시키기 위해 부착된 마감 부틸 테이프와, 시트방수층과 마감 부틸 테이프의 각각 노출되는 외부표면에 전면 도포되는 도막재방수층을 포함하는 방수구조를 구현하여, 노출공법 뿐만 아니라 비노출공법에서도 그 수밀성을 안정적이고 완벽하게 확보할 수 있는 개량방수시트와 이를 사용한 방수시공방법 및 방수구조에 관한 것이다.The present invention disclosed is an asphalt primer layer formed by applying an asphalt primer on the surface of the matrix, a sheet waterproof layer formed by arranging a non-woven fabric-attached waterproof sheet on the upper surface of the asphalt primer layer in a butt form, and the improvement in the sheet waterproof layer. The watertight portion formed by applying a material of the same type as the asphalt primer layer to the butt joint portion of the waterproof sheets, the finished butyl tape attached to fix the watertightness on the outer surface of the watertight portion and its surroundings, Improving the waterproof structure including the coating layer waterproofing layer applied to each exposed outer surface of the finished butyl tape, and improved waterproof sheet that can secure the watertightness stably and perfectly not only in the exposure method but also in the non-exposure method and the waterproofing using the same It relates to a construction method and a waterproof structure.
방수구조, 맞대음 방식, 복합방수시공, 부분절연 Waterproof structure, butt type, composite waterproof construction, partial insulation
Description
본 발명은 개량방수시트와 이를 사용한 방수시공방법 및 방수구조에 관한 것으로서, 보다 상세하게는 다수개의 개량방수시트를 맞대음 방식으로 배치시키고 그 맞대음 조인트부분에 아스팔트 프라이머를 도포시키고, 그 표면을 마감 부틸 테이프를 부착한 다음 다시 도막재를 도포하는 방수구조에 의하여 맞대음 공법에서의 취약점인 비노출 방수공법에서의 방수시트 모서리의 피로에 의한 방수시트파손 및 수밀부의 불안정성을 해결할 수 있는 방수구조를 구현하여, 노출공법 뿐만 아니라 비노출공법에서도 그 수밀성을 완벽히 확보할 수 있는 개량방수시트와 이를 사용한 방수시공방법 및 방수구조에 관한 것이다.The present invention relates to an improved waterproof sheet, a waterproof construction method and a waterproof structure using the same, and more particularly, a plurality of improved waterproof sheets are disposed in a butt manner, and an asphalt primer is applied to the butt joint portions, and the surface thereof is coated. The waterproof structure that attaches the finishing butyl tape and then apply the coating material again prevents the waterproof sheet breakage and the instability of the watertight portion due to the fatigue of the edge of the waterproof sheet in the non-exposed waterproof method, which is a weak point in the butt method. The present invention relates to an improved waterproof sheet, a waterproof construction method using the same, and a waterproof structure, which can completely secure the watertightness not only in the exposure method but also in the non-exposure method.
일반적으로 건축물을 형성하는 콘크리트나 모르타르와 같은 무기질 재료의 하지에는 균열로 인한 누수 및 결로현상이 발생하며, 이러한 문제점은 건물의 내구성을 약화시켜 건물의 노후화를 촉진시키는 역할을 한다. 따라서, 이러한 하자 발생의 원인을 제거하기 위하여 건물의 옥상/외벽 등의 외부 방수는 방수시트를 사용 한 시트방수공법, 도막방수재료를 사용한 도막방수공법 및 시트와 도막을 함께 사용한 복합도막방수공법을 사용하고 있다.In general, leaks and condensation due to cracks occur on the base of inorganic materials such as concrete or mortar forming a building, and this problem plays a role in facilitating aging of the building by weakening the durability of the building. Therefore, in order to eliminate the causes of such defects, the external waterproofing of the roof / outer wall of the building includes sheet waterproofing method using waterproof sheet, film waterproofing method using waterproof film material, and composite film waterproofing method using sheet and film together. I use it.
이하에 종래의 방수공법의 장단점을 살펴보면 다음과 같다.Looking at the advantages and disadvantages of the conventional waterproof method as follows.
먼저, 합성고분자계 시트방수공법은 합성고분자계 시트를 사용하므로 시공이 쉽다는 장점이 있으나, 얇기 때문에 손상을 받기 쉽고, 수밀성도 문제가 있다. 또한, 이 공법을 이용하는 경우는 토목용의 시트를 병용하고 보호층에 만전을 기해야하는 문제점이 있다.First, the synthetic polymer sheet waterproof method has the advantage of easy construction because it uses a synthetic polymer sheet, but is easy to be damaged because of the thin, there is also a problem of watertightness. In addition, in the case of using this method, there is a problem in that a sheet for civil engineering is used in combination and the protective layer must be ensured.
또한, 개량 아스팔트 시트 방수공법은 토오치 버너로 개량 아스팔트 시트를 붙이기 때문에 다소의 훈련에 의해 수밀성을 확보할 수 있어 지하방수용으로 적용된다. 상기 개량 아스팔트 시트 방수공법은 현재 가장 일반적으로 사용되는 공법으로서 방수시트의 뒷면에 부착된 아스팔트를 프로판 가스버너(토치버너)로 가열하여 용융한 상태에서 시트를 콘크리트 슬라브(slab)에 펼쳐서 붙이는 방법이다.In addition, the improved asphalt sheet waterproofing method is applied to underground waterproofing because the improved asphalt sheet is attached to the torch burner to secure watertightness by some training. The improved asphalt sheet waterproofing method is currently the most commonly used method is a method of unfolding and attaching the sheet to the concrete slab in the molten state by heating the asphalt attached to the back of the waterproof sheet with a propane gas burner (torch burner). .
이러한 개량 아스팔트 시트는 보강용 부직포 시트가 아스팔트 시트와 동일한 크기로 일측면에 열융착되어 있고, 아스팔트 시트의 타측면에는 롤형으로 제작시에 서로 접착되는 것을 방지하기 위한 이형지가 부착되어 있다.The improved asphalt sheet has a non-woven reinforcing sheet is heat-sealed on one side with the same size as the asphalt sheet, and the other side of the asphalt sheet is attached with a release paper for preventing the adhesive sheet from being adhered to each other during production.
그런데, 이러한 개량 아스팔트를 이용한 시공방법은 각 아스팔트 시트의 콘크리트 슬라브에 대한 전면부착과 아스팔트 시트 사이의 조인트 부분 처리후 보강재 작업을 거쳐야 하기 때문에 시트 설치의 작업성이 나쁘고 조인트 부분의 수밀성 확보가 어려운 문제점이 있으며, 아스팔트 시트 사이의 조인트 부분을 겹치게 하여 연속적으로 아스팔트 시트를 부설하기 때문에 차후 하자 발생시 누수부위를 찾기가 곤란하며, 보수시에는 광범위하게 작업을 해야되는 문제점이 있다.However, the construction method using the improved asphalt has a problem of poor workability of the seat installation and difficulty in securing the watertightness of the joint part because the asphalt should be subjected to reinforcement work after the front attachment to the concrete slab of each asphalt sheet and the joint part treatment between the asphalt sheets. There is a problem in that it is difficult to find a leaking part in the event of a later defect because the asphalt sheet is continuously laid by overlapping joint portions between the asphalt sheets, and there is a problem that a wide range of work should be performed during repair.
또한, 상기한 종래의 시트방수 공법에서는 방수시트를 밀착시키기 위하여 프라이머로 접착층을 형성하는 공정의 시공성과, 시트와 시트를 일정부분 중첩시키는데 따른 원자재의 낭비에 따른 비경제적인면과, 조인트 부분의 수밀성 확보의 어려움이 존재하고 있다.In addition, in the conventional sheet waterproofing method, the construction of the process of forming an adhesive layer with a primer in order to adhere the waterproof sheet, the uneconomical aspect of waste of raw materials by overlapping the sheet and the sheet, and the watertightness of the joint portion Difficulties in securing exist.
한편, 도막방수의 하나로서 아스팔트 방수공법(열공법)은 접합부는 있으나 3~4장의 루핑을 서로 겹쳐 놓으면 투수의 위험성이 적어지며 두께가 있기 때문에 방수층이 손상될 우려는 적다. 그러나, 이 공법은 높은 벽면에 시공할 때 고온의 용융 아스팔트 시공에 따른 위험이 있고, 용융된 아스팔트의 경화과정에서 물길이 생기기 쉬우므로 방수의 확실성은 기대할 수 없으며 숙련된 기능자가 많지 않아 방수의 신뢰성이 떨어지는 문제점이 있다.On the other hand, asphalt waterproofing method (heating method) as one of the waterproof coating film, but if the three to four roofs overlap each other, the risk of permeability is less and the thickness is less likely to damage the waterproof layer. However, this method has the risk of high temperature molten asphalt construction when applied to high wall surface, and since water is easily generated during hardening of molten asphalt, it is impossible to expect certainty of waterproofing and reliability of waterproofing because there are not many skilled functional workers. There is a falling problem.
상기한, 종래의 도막방수공법으로 공개특허 제2000-72868호에는 고탄성, 고강도의 도막을 형성하는 수용성 아크릴계 1액형 탄성 도막 방수제 조성물을 이용하며, 프라이머로 접착층을 먼저 형성하고 도막 방수제를 다수회 도포하여 다수의 방수막을 형성한 후, 방수막 상부에 보호막을 형성하는 도막방수공법이 개시되어 있다.In the above-described conventional coating waterproofing method, Korean Patent Laid-Open Publication No. 2000-72868 uses a water-soluble acrylic one-component elastic coating waterproofing composition to form a highly elastic, high strength coating film. And forming a plurality of waterproof films, and then forming a protective film over the waterproof film.
그러나, 이 공법은 접착층 및 도막 방수제의 경화에 시간이 오래 걸려 시공성이 나쁘고, 방수층의 방수성능을 나타내는 항장적(인장강도ㅧ신장율)이 낮은 단점이 있다However, this method has a disadvantage in that construction takes a long time to cure the adhesive layer and the coating waterproofing agent, resulting in poor workability and low tensile strength (tensile strength vs. elongation).
반면에, 액체방수공법은 공정회수가 적어 시공이 간단하고 방수층의 두께가 일정하며 신율 및 균열 저항성이 있어 거동이 있는 바탕에 사용이 가능하고 노출공법이 가능한 장점이 있다. 그러나, 이 공법은 이음부와 끝단부의 누수가 많고, 누수의 원인을 찾기 어려우며, 모체와 절연되어 부풀음 및 파단이 잘 일어나고 통기성이 없어 탈기장치가 필요하며, 더욱이 유기재료로서 경년에 따른 열화가 잘 일어나는 문제점이 있다.On the other hand, the liquid waterproof method has the advantage that the construction process is simple, the thickness of the waterproof layer is constant, and the elongation and crack resistance can be used on the basis of the behavior and the exposure method is possible because the process is small. However, this method is difficult to find the cause of the leakage of the joint and the end, it is difficult to find the cause of the leak, it is insulated from the mother, swelling and rupture occurs well, there is no breathability, degassing device is required, and as the organic material deterioration with age well There is a problem that occurs.
또한, 우레탄 방수공법은 신축성이 양호하며 1mm 미만의 바탕균열에도 견딜 수 있고, 바탕면과 접착성이 우수한 일반적으로 사용하는 도막방수공법이지만, 이 공법은 바탕의 습기가 8% 이상의 경우 접착시 불량이 발생할 수 있고, 부풀음 현상이 발생하며 경화시간이 길다는 문제점과 수직부위의 흐름성이 크다는 문제점이 있다.In addition, the urethane waterproofing method has a good elasticity and can withstand cracks of less than 1mm, and is a commonly used coating waterproofing method with excellent adhesion to the base surface. However, this method is poor in adhesion when the moisture of the base is 8% or more. This may occur, the swelling phenomenon occurs, there is a problem that the curing time is long and the flowability of the vertical portion is large.
이러한 액상 도막 방수제 사용의 문제점을 해결하기 위하여 공개특허 제2001-18221호에는 개량 방수시트 및 이를 사용한 복합도막 방수시공방법이 제안되어 있다.In order to solve the problem of the use of the liquid coating waterproofing agent, Korean Patent Laid-Open Publication No. 2001-18221 proposes an improved waterproof sheet and a composite coating waterproofing method using the same.
상기 복합도막 방수시공방법은 복합도막 방수시공에 사용되는 각종 방수시트의 구조를 변경함에 의해 방수시트의 조인트 시공이 간단하고 별도의 조인트 부분 보강없이 시공을 진행할 수 있어, 시공 작업의 작업성(단순성)을 개선할 수 있으며, 조인트 부분의 완전 방수를 기할 수 있는 개량 방수시트 및 이를 사용한 복합도막 방수시공방법에 관한 것이다.In the composite coating waterproof construction method, the joint construction of the waterproof sheet is simple by changing the structure of various waterproof sheets used for the composite coating waterproof construction, and the construction can be performed without reinforcing a separate joint, thereby improving workability (simpleness). The present invention relates to an improved waterproof sheet and a composite coating waterproofing method using the same.
여기서, 상기 개량 방수시트는 방수기능을 갖는 방수시트는 방수기능을 갖는 방수시트 본체와, 인접한 방수시트와 중첩되어 조인트 시공되는 측면으로 일정한 길이만큼 상기 방수시트 본체로부터 변위된 상태로 열융착된 부직포와, 상기 방수시트 본체의 하부면에 부착된 이형재료층으로 구성되며, 상기 방수시트 본체는 인접한 방수시트와 중첩되어 조인트되는 부분에 노출부가 형성되는 것을 특징으로 한다.Here, the improved waterproof sheet is a waterproof sheet having a waterproof function is a waterproof sheet body having a waterproof function, the non-woven fabric heat-sealed in a state displaced from the waterproof sheet body by a predetermined length to the side of the joint construction overlapping the adjacent waterproof sheet And a release material layer attached to a lower surface of the waterproof sheet main body, wherein the waterproof sheet main body is formed with an exposed part formed at a portion that is overlapped with an adjacent waterproof sheet.
다른 예로, 공개특허 제2000-72869호에는 기재 시트에 무기질 탄성 복합 도막을 코팅하여 통기성 및 투습성을 갖도록 하여 도막의 내구성, 내후성, 시공 작업의 작업성을 개선할 수 있으며, 모체(하지)에 부분 접착식으로 시공이 이루어지므로 모체의 균열에 따라 방수층에 영향을 받지 않는 복합 도막 방수시트 및 이를 사용한 복합 도막 방수시공밥법이 개시되어 있다.As another example, Korean Patent Laid-Open Publication No. 2000-72869 discloses an inorganic elastic composite coating film on a base sheet to improve breathability and moisture permeability, thereby improving durability, weather resistance, and workability of a construction work, and parting on a base (base). Since the construction is performed by the adhesive method, a composite coating film waterproof sheet and a composite coating film waterproofing method using the same have been disclosed, which are not affected by the cracking layer of the mother.
이 시공방법은 바탕면 위에 각각 표면에 부직포가 부착된 다수의 방수시트(폴리 에틸렌(P.E.)계 경질(연질)시트)각각의 하부면을 부분적으로 접착함과 동시에 시트의 주변부가 다른 시트의 주변부와 일정폭 만큼 중첩된 상태로 밀봉 접착하고, 방수시트 상부면에 프라이머를 도포하여 접착층을 형성한 후 접착층 상부면에 무기질 탄성 도막 방수제를 적어도 1회 도포하여 방수막을 형성하고, 방수막 상부면에 보호막을 형성하는 단계로 구성되어 있다.This construction method partially adheres the lower surfaces of a plurality of waterproof sheets (polyethylene (PE) -based hard (soft) sheets), each of which has a nonwoven fabric attached to its surface, on the base surface, and at the same time, And seal in a state where they overlap each other by a certain width, form an adhesive layer by applying a primer on the upper surface of the waterproof sheet, and then apply an inorganic elastic coating waterproofing agent at least once on the upper surface of the adhesive layer to form a waterproof layer, It consists of forming a protective film.
그런데, 상기 방수시공방법은 방수시트의 조인트 부분을 시트의 주변부가 다른 시트의 주변부와 일정폭 만큼 중첩된 상태로 밀봉 접착하는 구조이므로 약10%정도의 원자재가 추가로 소모되며, 작업자의 숙련도에 따라 그 방수성능이 결정되므로 안정적이고 확실한 수밀성을 보장받지 못하고 있다.However, the waterproof construction method is a structure in which the joint portion of the waterproof sheet is sealed and bonded in a state where the periphery of the sheet overlaps with the periphery of the other sheet by a predetermined width, so that about 10% of raw materials are additionally consumed. Therefore, the waterproof performance is determined, so that stable and reliable watertightness is not guaranteed.
또한, 공개특허 제1999-31067호에는 상기한 조인트 부분의 수밀성을 강화하 기 위하여 아스팔트 시트와 폴리우레탄 도막방수재의 장점들을 택하고 단점들을 서로 보완하도록 아스팔트 시트 구조를 개량하여 접착력을 증대시켜 주는 복합방수구조 및 그 시공방법이 개시되어 있다.In addition, Korean Patent Laid-Open Publication No. 1999-31067 discloses a composite that increases the adhesive strength by taking advantage of the asphalt sheet and the polyurethane waterproofing material to reinforce the watertightness of the joint portion, and improving the asphalt sheet structure to compensate for the disadvantages. A waterproof structure and a construction method thereof are disclosed.
상기 방수구조는 이음부의 끝단부들이 서로 소정의 간격을 유지하면서 슬라브층 상면에 부설되도록 하되, 아스팔트로 형성되는 아스팔트 시트의 상면에 부직포 하부의 일부가 심겨진 상태로 융착되며 그 상부의 일부는 외부로 돌출되게 만들어지는 바탕 방수시트와, 상기 바탕 방수 시트의 상면에 액상의 폴리우레탄을 도포하여 형성되는 폴리우레탄층으로 구성되어 있다.The waterproof structure allows the end portions of the joints to be laid on the upper surface of the slab layer while maintaining a predetermined distance from each other. The waterproof structure is fused in a state in which a portion of the lower portion of the nonwoven fabric is planted on the upper surface of the asphalt sheet formed of asphalt. The base waterproof sheet is formed to protrude, and a polyurethane layer formed by applying a liquid polyurethane on the upper surface of the base waterproof sheet.
상기한 시공방법은 상기 시트와 시트 사이의 수밀성을 확보하기 위해 액상 폴리우레탄을 사용하기 때문에, 도포된 폴리우레탄이 경화되는 데 장시간이 소요되어 시공기간이 길어지는 문제점이 발생한다.Since the construction method uses a liquid polyurethane to secure the watertightness between the sheet and the sheet, a problem arises in that the coated polyurethane takes a long time to cure and the construction period is long.
이 때문에, 상기 복합방수구조 시공방법은 누름층을 두지 않는 노출공법에서는 그 방수성에 문제가 없지만, 실제로 현장에서 일정 무게를 가지는 누름층이 형성되는 비노출공법(누름공법)에서 상기 복합방수구조의 시공방법을 채택할 경우에는, 시트와 시트사이가 소정간격 떨어져 있기 때문에 상기 도막 방수제 즉, 액상 폴리우레탄의 경화 시간에 따른 대기시간을 확보하지 못하고 상기 액상 폴리우레탄이 경화되기 전에 누름층을 형성시키면, 누름층의 하중에 의해 미처 완전히 경화되지 못한 폴리우레탄층이 특히 시트와 시트 사이의 조인트 부분에서 약화된다. 이에 따라 시트와 시트 사이에서 누름층에 의한 상기 방수시트 각 모서리에 지속적인 피로가 발생하여 시트와 시트 사이의 시트 모서리부에 피로파괴가 발생하므로 시트 사이의 수밀성을 확보할 수 없는 문제점이 있다.For this reason, the composite waterproof structure construction method does not have a problem in the waterproofness in the exposure method without a pressing layer, but the construction of the composite waterproof structure in a non-exposure method (pressing method) in which a pressing layer having a certain weight is actually formed in the field. In the case of adopting the method, since the space between the sheet and the sheet is separated by a predetermined interval, if the coating layer, that is, the waiting time according to the curing time of the liquid polyurethane is not secured, and the pressing layer is formed before the liquid polyurethane is cured, The polyurethane layer, which has not yet fully cured by the load of the pressing layer, is weakened, especially at the joint portion between the sheet and the sheet. As a result, continuous fatigue occurs in each corner of the waterproof sheet due to the pressing layer between the sheet and the sheet, and fatigue fracture occurs in the sheet edge portion between the sheet and the sheet, thereby preventing the watertightness between the sheets.
따라서, 상기한 바에 따라 종래에 시공되는 방수공법은 크게 시트형태의 방수재를 부착하는 방법과 도막형태의 방수재를 도포하는 방식 및 이들의 장단점을 보완한 복합도막방수공법이 시행되고 있으며, 이 때의 각각의 방수공법은 서로 장단점을 지니고 있다.Therefore, the waterproofing method conventionally constructed according to the above is a method of attaching a sheet-shaped waterproofing material, a method of applying a waterproofing material in the form of a coating film, and a composite coating waterproofing method that supplements their advantages and disadvantages. Each waterproofing method has advantages and disadvantages.
먼저, 시트형태의 방수재를 부착하는 방법의 경우에는 방수재 시트가 공장에서 일괄 생산되는 방식이라 품질이 균일하고 특히 아스팔트를 베이스로 하는 방수시트는 여타의 방수재에 비해 가격이 저렴 하나 시트 조인트 부위 접합에 많은 문제점을 가지고 있다.First, in the case of attaching the sheet-type waterproofing material, the waterproofing sheet is produced in a batch at the factory, so the quality is uniform and the asphalt-based waterproofing sheet is cheaper than other waterproofing materials. There are many problems.
반면, 도막방수재를 도포하는 방식은 시트 형태의 방수재가 지니는 조인트 부위가 없기 때문에 일체화 된 방수층을 얻을 수 있으나 시공 모체가 매우 평탄하지 않으면 그 두께 형성에 매우 어려운 문제를 지니고 있다.On the other hand, the method of applying the coating waterproofing material can be obtained because there is no joint portion of the sheet-shaped waterproofing material, but the integrated waterproof layer has a problem that is very difficult to form the thickness if the construction mother is not very flat.
또한, 상기 도막형태와 시트형태의 방수재의 두재료가 지니는 장단점을 활용할 수 있도록 용융아스팔트를 아스팔트 펠트와 아스팔트 루핑을 사용하여 적층하는 공법이 있으나 이는 아스팔트를 끓이는 과정에서 공해와 화재 작업자의 화상 안전등의 문제가 있어 거의 사용되지 못하고 있는 실정이다.In addition, there is a method of laminating molten asphalt using asphalt felt and asphalt roofing to take advantage of the advantages and disadvantages of the two materials of the coating film and the sheet-shaped waterproofing material. There is a problem that is rarely used.
이에, 상기 시트형태와 도막형태의 방수공법을 함께 적용한 복합도막방수공법으로서 상기 방수시트의 조인트부위 공정의 수밀성에 중점을 두고 여러가지 방안이 강구되었는데, 그중 오버랩 방식에 의한 공법은 작업자의 숙련도에 따라 방수성능이 좌우되기 때문에, 작업자의 실수등에 의한 하자가 매우 많이 발생하고 있다. Therefore, as a composite coating waterproofing method applying both the sheet-like and coating-type waterproofing methods together, various methods have been devised, with an emphasis on the watertightness of the joint part process of the waterproofing sheet, among which the overlapping method depends on the skill of the operator. Since waterproof performance is dependent, there are many defects caused by operator's mistakes.
이에 따라, 공개특허 제1999-31067호와 같이 복합도막 방수시공으로서 이를 보완한 방수 시트 조인트 부위를 일정 넓이 벌리고 도막재를 충진하는 조인트 처리방식이 개발되어 시행되고 있다.Accordingly, a joint treatment method for filling the coating material with a certain width of the waterproof sheet joint area that has been supplemented as a composite coating waterproofing construction as disclosed in Korean Patent No. 1999-31067 has been developed and implemented.
그러나, 상기 조인트처리방식은 노출공법으로 시공하는 경우에는 그 도막재의 경화가 충분하게 이루어질 수 있는 시간을 확보할 수 있어 매우 유용한 공법이나, 누름층이 있는 비노출공법으로 시공하는 경우에는 현장 여건상 도막재가 요구하는 경화대기 시간을 확보할 수 없어, 상기 도막재가 채 경화되기 전에 누름층이 형성되므로 누름층에 의한 하중에 의해 수밀성 및 누름층의 하중을 견딜수 있는 쿠션역할을 하는 도막재층이 조인트부분에서 약화되어, 이에 따라 누름층의 하중에 따른 피로를 집중으로 받는 방수시트 각 모서리에 지속적인 피로가 발생하여 각 시트사이의 시트모서리부에 피로파괴가 발생하기 때문에 수밀성을 확보하지 못하는 문제점이 발생하게 된다. However, when the joint treatment method is applied by the exposure method, it is possible to secure sufficient time for the curing of the coating material, which is a very useful method, or when using the non-exposed method with the pressing layer, Since the hardening waiting time required by the ash cannot be secured, and the pressing layer is formed before the coating material is hardened, the coating layer having the role of cushioning to withstand the water tightness and the pressing layer load by the pressing layer is formed at the joint part. It is weakened, and thus, continuous fatigue occurs at each corner of the waterproof sheet which receives the fatigue due to the pressure of the pressing layer, and fatigue failure occurs at the corners of the sheets between the sheets, thereby failing to secure watertightness. .
따라서, 본 발명은 이러한 종래기술의 문제점을 감안하여 안출된 것으로서, 그 목적은 다수개의 개량방수시트를 맞대음 방식으로 배치시키고 맞대음 조인트부분에 아스팔트 프라이머를 도포시킨 수밀부를 둔다음 그 표면을 마감 부틸 테이프로 부착한다음 도막재로 도포한 구조로 하여, 맞대음 공법에서의 취약점인 비노출 방수공법에서의 시트 모서리의 피로에 의한 시트파손 및 수밀부의 불안정성을 해결할 수 있는 방수구조를 구현하여, 노출공법 뿐만 아니라 비노출공법에서도 그 수밀 성을 완벽히 확보할 수 있는 개량방수시트와 이를 사용한 방수시공방법 및 방수구조물을 제공하는 데 있다.Accordingly, the present invention has been made in view of the problems of the prior art, the object of which is to place a plurality of improved waterproof sheet in a butt manner, place the watertight portion coated with asphalt primer on the butt joint portion and then finish the surface By attaching it with butyl tape and applying it with a coating material, it realizes a waterproof structure that solves the instability of sheet breakage and watertightness due to the sheet edge fatigue in the non-exposed waterproof method, which is a weak point in the butt method. It is to provide an improved waterproof sheet, waterproof construction method and waterproof structure using the same as well as the non-exposure method, which can secure the watertightness perfectly.
또한, 본 발명의 다른 목적은 부분절연(絶緣)공법이 가능한 개량방수시트에 의해 에어포켓현상을 방지하고, 모체의 변화에 의한 방수층의 손상을 없앨 수 있으며, 모체에 도포된 아스팔트 프라이머와 개량방수시트간의 맞대음 조인트부분의 수밀부의 아스팔트 프라이머를 모두 동일한 재료로 하여 수밀부와 모체의 아스팔트 프라이머층이 단일체로 방수막을 형성하여 시간이 경과하여도 분리가 일어나지 않아 신뢰성이 높은 방수구조를 형성할 수 있는 개량방수시트와 이를 사용한 방수시공방법 및 방수구조물을 제공하는 데 있다.In addition, another object of the present invention is to prevent the air pocket phenomenon by the improved waterproof sheet capable of a partial insulation method, to prevent damage to the waterproof layer due to the change of the matrix, the asphalt primer and improved waterproof applied to the mother The watertight part and the mother's asphalt primer layer form a waterproofing film as a single body using all the asphalt primers of the watertight part of the butt joint part between the sheets, so that separation does not occur even over time, thereby forming a reliable waterproof structure. It is to provide an improved waterproof sheet and a waterproof construction method and a waterproof structure using the same.
상기의 목적을 달성하기 위한 본 발명의 1특징에 따르면, 본 발명은, 아스팔트 콤파운드층과, 상기 아스팔트 콤파운드층의 상부에 형성되며, 그 표면에 도포되는 도막재의 흡수율을 높여 결합력을 증대시키는 부직포와, 상기 아스팔트 콤파운드층의 하부에 형성되어 모체와 접착되는 필름 및 상기 필름의 하부에 형성된 이형지를 포함한다.According to one aspect of the present invention for achieving the above object, the present invention is formed on the asphalt compound layer and the asphalt compound layer, the nonwoven fabric to increase the bonding strength by increasing the absorption of the coating material applied to the surface and , A film formed on the lower portion of the asphalt compound layer and adhered to the mother body, and a release paper formed on the lower portion of the film.
또한, 본 발명의 제2특징에 의하면, 모체에 제1 아스팔트 프라이머를 도포하는 단계와, 상기 제1 아스팔트 프라이머가 건조 된 후 그 표면에 부직포가 부착된 방수시트 다수개를 맞대음형식으로 배치시켜 부착하는 단계와, 상기 다수개의 개량방수시트의 맞대음 조인트부분에 제2 아스팔트 프라이머를 도포하는 단계와, 상기 제 2 아스팔트 프라이머가 건조된 후 그 외부표면과 주위에 수밀성을 유지하면서 고정시킬 수 있는 마감 부틸 테이프를 부착하는 단계 및 상기 마감 부틸 테이프와 상기 개량방수시트의 각각 노출되는 외부표면에 도막재를 전면 도포하는 단계를 포함하는 방수방법이 제공된다.In addition, according to the second aspect of the present invention, the step of applying the first asphalt primer to the matrix, and after the first asphalt primer is dried, a plurality of non-woven fabric is attached to the surface of the non-woven fabric arranged in a butt Attaching, applying a second asphalt primer to the butt joint portions of the plurality of improved waterproof sheets, and after the second asphalt primer is dried, it can be fixed while maintaining watertightness on its outer surface and surroundings Attaching a finishing butyl tape and a front coating of the coating material on each of the exposed outer surface of the finished butyl tape and the improved waterproof sheet is provided.
또한, 본 발명 제3특징에 따르면, 본 발명은 모체의 표면에 아스팔트 프라이머가 도포되어 형성된 아스팔트 프라이머층과, 상기 아스팔트 프라이머층의 상부에 각각의 표면에 부직포가 부착된 아스팔트 콤파운드로 이루어진 다수의 개량방수시트를 맞대음 형식으로 배치시켜 형성된 시트방수층과, 상기 시트방수층에서 상기 방수시트들의 맞대음 조인트부분에 상기 아스팔트 프라이머층과 같은 물성의 재질로 도포되어 맞대음 조인트를 이루고 있는 상기 방수시트와 방수시트 사이에 스며든 아스팔트 프라이머가 접촉면을 용융결합시켜 일체화되어 형성된 수밀부와, 상기 수밀부의 외부표면과 그 주위에 수밀성을 유지하면서 고정시키기 위해 부착된 마감 부틸 테이프 및 상기 시트방수층과 상기 마감 부틸 테이프의 각각 노출되는 외부표면에 전면 도포되는 도막재방수층을 포함하는 방수구조가 제공된다.In addition, according to the third aspect of the present invention, the present invention provides a plurality of improvements including an asphalt primer layer formed by applying an asphalt primer on the surface of the mother body, and an asphalt compound having a nonwoven fabric attached to each surface on top of the asphalt primer layer. The sheet waterproof layer formed by arranging the waterproof sheet in a butt-type form, and the waterproof sheet and the waterproof sheet formed on the butt joint portions of the waterproof sheets in the sheet waterproof layer by applying a material such as the asphalt primer layer to form a butt joint. Asphalt primer infiltrated between the sheets melt-bonded the contact surface is integrally formed with a watertight portion, and a finish butyl tape attached to secure the watertightness around the outer surface of the watertight portion and around it, and the sheet waterproofing layer and the finish butyl tape Front to outer surfaces of each exposed The waterproof structure is provided that comprises a capsule coating material that is waterproof.
또한, 본 발명 제4특징에 따르면, 본 발명은 모체의 표면에 각각의 표면에 부직포가 부착된 아스팔트 콤파운드로 이루어진 다수의 방수시트를 맞대음 형식으로 배치시켜 형성된 시트방수층과; 상기 시트방수층에서 상기 방수시트들의 맞대음 조인트부분의 하부에 아스팔트 프라이머가 도포되어 형성된 아스팔트 프라이머층과; 상기 아스팔트 프라이머층의 상부와 상기 방수시트 하부 사이에 부착된 부틸시트와; 상기 시트방수층에서 상기 방수시트들이 맞대음 조인트부분의 상부에 주위에 수밀성을 유지하면서 고정시키기 위해 부착된 보강포와; 상기 보강포의 상부에 상 기 보강포가 덮히도록 탄성퍼티를 도포하여 형성된 탄성퍼티층과; 상기 시트방수층과 상기 탄성퍼티층의 각각 노출되는 외부표면에 전면 도포되는 도막재방수층을 포함하는 방수구조가 제공된다.In addition, according to a fourth aspect of the present invention, the present invention provides a sheet waterproofing layer formed by arranging a plurality of waterproof sheets made of asphalt compound having a nonwoven fabric attached to each surface thereof on a surface of a matrix in a butt-type fashion; An asphalt primer layer formed by applying an asphalt primer to a lower portion of the butt joint portion of the waterproof sheets in the sheet waterproof layer; A butyl sheet attached between an upper portion of the asphalt primer layer and a lower portion of the waterproof sheet; A reinforcement cloth attached to the watertight sheets in the sheet waterproofing layer to fix the watertight sheets on top of the butt joint part while maintaining watertightness; An elastic putty layer formed by applying an elastic putty on the reinforcement cloth to cover the reinforcement cloth; There is provided a waterproof structure including a coating film waterproofing layer applied to the entire surface of the sheet waterproofing layer and the outer surface of the elastic putty layer.
또한, 본 발명의 제5특징에 의하면, 모체의 가로 또는 세로를 포함한 모서리부분에 접혀져서 부착되는 방수시트와; 상기 모체의 세로측면에 부착되는 방수시트의 일단부의 하부에 도포되어 형성되는 프라이머층과; 상기 프라이머층의 상부와 상기 방수시트의 일단부의 하부사이에 부착된 부틸테잎과; 상기 방수시트 일단부의 상부에 수밀성을 유지하면서 고정시키기 위해 부착된 보강포와; 상기 방수시트와 상기 보강포의 각각 노출되는 외부표면에 전면도포되는 도막재방수층과; 상기 도막재방수층의 외부표면에 마감재를 도포하여 형성된 마감재도포층을 포함하는 방수구조를 제공한다.In addition, according to a fifth aspect of the present invention, the waterproof sheet is folded and attached to the corner portion including the horizontal or vertical of the mother; A primer layer formed by being applied to a lower portion of one end of the waterproof sheet attached to the longitudinal side of the mother body; A butyl tape attached between an upper portion of the primer layer and a lower portion of one end of the waterproof sheet; A reinforcement cloth attached to the upper portion of the waterproof sheet while maintaining the watertightness; A coating film repellent waterproofing layer coated on the outer surface of each of the waterproof sheet and the reinforcement cloth; It provides a waterproof structure comprising a finish coating layer formed by applying a finish on the outer surface of the waterproof coating layer.
상기한 바와 같이 본 발명의 개량방수시트에 의하면, 아스팔트 콤파운드층에 부착된 필름에 다수개의 노출홀을 형성시키고 동시에 길이편차를 두고 제작하여, 부분절연공법이 가능하고 이에 따라 방수층의 부풀음 현상(에어포켓 현상)을 방지할 수 있으며, 방수시공작업시 모체와의 밀착을 향상시킬 수 있다.As described above, according to the improved waterproof sheet of the present invention, a plurality of exposed holes are formed in the film attached to the asphalt compound layer and manufactured with a length deviation at the same time, so that a partial insulation method is possible, and thus the swelling phenomenon of the waterproof layer (air) Pocket phenomenon) can be prevented, and the adhesion to the mother can be improved during waterproof construction.
또한, 상기 본 발명의 개량방수시트를 맞대음 방식으로 배치한 후 맞대음 조인트 부분에 아스팔트 프라이머를 도포한 후 마감 부틸 테이프를 부착하고 도막재를 전면 도포하여, 일반적으로 시트 맞대음 방식의 방수구조에서 수밀성이 취약한 조인트 부분에 대하여 완벽한 수밀성을 확보할 수 있는 방수시공구조 및 방수시공방법을 구현하여, 전체적으로 항장력이 우수하며 그 수밀성이 완벽하며, 작업이 간 단하고 시공시간이 짧아 작업성을 향상시킬 수 있다.In addition, after the improved waterproof sheet of the present invention is disposed in a butt method, an asphalt primer is applied to the butt joint part, and then a butyl tape is attached and the coating material is applied to the entire surface. Implement waterproof construction structure and waterproof construction method to secure perfect water tightness for joint parts that are weak in watertightness, and improve the workability as it has excellent tensile strength, perfect watertightness, simple work and short construction time. You can.
상술한 바와 같이 본 발명의 개량방수시트와 이를 사용한 방수시공방법 및 방수구조는 다음과 같은 효과를 제공한다.As described above, the improved waterproof sheet and the waterproof construction method and the waterproof structure using the same provide the following effects.
첫째, 다수개의 개량방수시트를 맞대음 방식으로 배치시키고 맞대음 조인트부분에 아스팔트 프라이머를 도포시킨 수밀부를 둔다음 그 표면을 마감 부틸 테이프로 부착한다음 도막재로 도포한 구조로 하여, 맞대음 공법에서의 취약점인 비노출 방수공법에서의 시트 모서리의 피로에 의한 시트파손 및 수밀부의 불안정성을 해결할 수 있는 방수구조를 구현하여, 노출공법 뿐만 아니라 비노출공법에서도 그 수밀성을 완벽히 확보할 수 있다.Firstly, a number of improved waterproof sheets are placed in a butt-to-butt manner, a watertight portion coated with asphalt primer is applied to the butt joint part, and then the surface is attached with a finishing butyl tape, and then coated with a coating material. In the non-exposure waterproofing method, which is a weak point of Esau, the waterproof structure can be solved to solve the sheet breakage and the instability of the watertight portion due to the fatigue of the edge of the sheet.
둘째, 부분절연공법이 가능한 개량방수시트에 의해 에어포켓현상을 방지할 수 있으며, 모체의 변화에 의한 방수층의 손상을 없앨 수 있다.Second, the airtight phenomenon can be prevented by the improved waterproof sheet capable of partial insulation, and the damage of the waterproof layer due to the change of the mother body can be eliminated.
셋째, 모체에 도포된 아스팔트 프라이머와 개량방수시트간의 맞대음 조인트부분의 수밀부의 아스팔트 프라이머를 모두 동일한 재료로 하여 수밀부와 모체의 아스팔트 프라이머층 및 개량방수시트의 아스팔트 콤파운드층이 단일체로 방수막을 형성하여 시간이 경과하여도 분리가 일어나지 않아 신뢰성이 높은 방수구조를 형성하게 된다.Third, the watertight part and the mother's asphalt primer layer and the asphalt compound layer of the improved waterproof sheet are formed in one body by using both the asphalt primer applied to the mother and the asphalt primer of the watertight portion of the butt joint portion between the improved waterproof sheet. As a result, no separation occurs over time, thereby forming a highly reliable waterproof structure.
이하 첨부된 도면을 참조로 본 발명의 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
우선, 본 발명에 의한 개량방수시트와 이를 사용한 방수시공방법 및 방수구조는 비노출 방수시공방법(일명 누름층 공법)과 노출 방수시공방법에 대하여 각각 적용될 수 있으며, 하기에 설명되는 본 발명의 바람직한 일 실시예는 비노출 방수시공방법을 적용한 예에 대하여 설명하기로 한다.First, the improved waterproof sheet according to the present invention, the waterproof construction method and the waterproof structure using the same can be applied to the non-exposed waterproof construction method (aka press layer construction method) and the exposure waterproof construction method, respectively, which is described below. The embodiment will be described for an example in which the non-exposed waterproof construction method is applied.
도 1은 본 발명의 바람직한 일 실시예에 따른 개량방수시트를 사용한 방수구조를 나타낸 사시도이며, 도 2와 도 3은 도 1에 사용된 개량방수시트를 각각 나타낸 평면도와 단면도이다. 또한, 도 4는 도 1의 개량방수시트들을 맞대음 방식으로 모체에 부착했을 때를 나타낸 도면이고, 도 5는 도 1의 개량방수시트들의 맞대음 조인트부분에 사용되는 마감 부틸 테이프를 나타낸 사시도이며, 도 6은 도 1의 I-I선에 따른 단면도이다.1 is a perspective view showing a waterproof structure using an improved waterproof sheet according to an embodiment of the present invention, Figures 2 and 3 are a plan view and a cross-sectional view showing the improved waterproof sheet used in FIG. 4 is a view showing when the improved waterproof sheets of FIG. 1 are attached to the mother body in a butt-fitting manner, and FIG. 5 is a perspective view showing a finished butyl tape used in the butt joint portion of the improved waterproof sheets of FIG. 6 is a cross-sectional view taken along line II of FIG. 1.
먼저, 도 1을 참조하면, 본 발명의 바람직한 일 실시예에 따른 방수구조는 콘크리트 슬라브의 모체(10)의 표면에 아스팔트 프라이머가 도포되어 형성된 아스팔트 프라이머층(20)과, 상기 아스팔트 프라이머층(20)의 상부에서 다수개의 개량방수시트(80)에 의해 형성되는 시트방수층(30)과, 상기 시트방수층(30)의 다수개의 개량방수시트(80) 조인트부분에 형성된 수밀부(40)와, 상기 수밀부(40)의 수밀성을 유지하면서 고정시키기 위해 그 외부표면에 수밀하게 부착되는 마감 부틸 테이프(50)와, 도막재방수층(60)으로 이루어져 있다. First, referring to Figure 1, the waterproof structure according to an embodiment of the present invention is an
여기서, 상기 시트방수층(30)은 상기 프라이머층의 상부에 다수개의 개량방수시트(80)를 도시된 바와 같이 서로 맞대음 방식으로 최대한 근접 배치시켜 형성되어 있다.Here, the sheet
이 때, 상기 시트방수층(30)의 다수개의 개량방수시트(80)의 맞대음 조인트부분에는 수밀성을 확보하기 위하여 수밀부(40)가 형성되는데, 여기서 수밀부(40)는 상기 아스팔트 프라이머층(20)과 일체화를 유도할 수 있도록 상기 개량방수시트(80)의 상부에 상기 아스팔트 프라이머층(20)과 같은 물성의 재질로 도포되는 것이 바람직하며, 따라서 본 발명에서는 상기 수밀부(40)에 상기 아스팔트 프라이머를 도포시켰다.At this time, the
또한, 상기 시트방수층(30)과 상기 마감 부틸 테이프(50)의 각각 노출되는 외부표면 전면에는 완벽한 수밀성을 구현할 수 있도록 도막재가 도포된 도막재방수층(60)이 형성되어 있다. 여기서, 상기 도막재는 그 용도에 맞게 우레탄 도막재, 용제형 아스팔트 도막재, 수용성 아스팔트 도막재 중 선택된 어느 하나로 하는 것이 바람직하며, 그 외 상기 도막재의 기능을 수행할 수 있는 것이면 다른 것도 사용가능하다.In addition, the outer surface of each of the
한편, 상기 개량방수시트(80)에 대하여 구체적으로 살펴보면 다음과 같다.On the other hand, with reference to the improved
상기 개량방수시트(80)는 도 2에 나타난 바와 같이, 부분절연공법이 가능하도록 개발된 것으로서, 바탕이 되는 아스팔트 콤파운드층(83)과, 상기 아스팔트 콤파운드층(83)의 상부에 부착되어 도막재의 흡수율을 높여 결합력을 증대시키기 위한 부직포(84)와, 도 3에 나타난 바와 같이 상기 아스팔트 콤파운드층(83)의 하부에 부착되는 필름(82)과, 상기 필름(82)의 하부에 형성되어, 시공성을 편리하게 할 수 있는 이형지(81)로 이루어져 있다.As shown in FIG. 2, the improved
구체적으로, 상기 아스팔트 콤파운드층(83)의 상부에는 어떠한 도막재와도 흡수율이 좋아 도막재와 결합력을 증대시킬 수 있으며, 더욱이 자체가 질긴 망상으로 구성되어 상기 아스팔트 콤파운드층(83)과 상기 도막재의 내부에 삽입됨으로써 전체적인 방수구조의 인성을 증대시켜 주는 부직포(84)가 부착되어 있으며, 이러한 부직포로는 폴리에스터 부직포와, 매쉬형 화이버 글라스와, 폴리프로필렌 직포 중 선택된 어느 하나로 하는 것이 바람직하다.Specifically, the upper part of the
한편, 상기 개량방수시트(80)는 상기 필름(82)에 다수개의 노출홀(82a)이 형성되어 있어 있기 때문에, 상기 아스팔트 콤파운드층(83)의 하부에 부착이 되면, 상기 노출홀(83a)을 통해 상기 아스팔트 콤파운드층(83)이 일부분 노출되어 부분절연공법이 가능하게 되고, 이렇게 함으로써, 밀착으로 인해 발생할 수 있는 에어포켓현상 즉, 스웰링(swelling) 현상을 방지할 수 있을 뿐만 아니라 상기 개량방수시트(80)가 프라이머가, 도포된 모체(10)에 밀착되었을 때 발생할 수 있는 모체(10)와 상기 개량방수시트(80) 상호간의 이동 및 흔들림을 효과적으로 방지할 수 있다.On the other hand, the improved
게다가, 상기 필름(82)은 상기 아스팔트 콤파운드층(83)의 길이방향의 노출영역(82b)가 노출이 되어 아스팔트 프라이머가 도포된 모체(10)에 효과적으로 접착될 수 있도록, 상기 아스팔트 콤파운드층(83)의 폭보다 작게 길이편차를 두어 제조되었기 때문에 상기 개량방수시트(80)를 모체에 접착시 더욱 면밀하게 밀착시킬 수 있다.In addition, the
도 4는 본 발명의 바람직한 실시예에 따른 개량방수시트를 모체의 바탕면에 맞대음방식으로 부착시공했을 때를 나타낸 도면이다.4 is a view showing when the improved waterproof sheet according to a preferred embodiment of the present invention when attached to the base surface of the mother body by a butt method.
도면을 참조하면, 본 발명의 바람직한 실시예에 따른 상기 개량방수시트(80) 는, 모체(10)에 부착시공했을 때 상기 개량방수시트(80)들의 단부는 맞대음 방식으로 연결되어 수밀부(40; 도1참조)가 형성되고, 또한 상기 개량방수시트(80)들의 노출영역(82b)는 상기 개량방수시트(80)의 외부로 노출된 아스팔트 콤파운드층(83)이 모체(10)에 밀착되기 때문에, 도시된 바와 같이 만약 누수가 발생하였을 경우 누수범위의 확대없이 도면의 해칭된 부분 즉, 상기 단일 개량방수시트(80)의 범위로 누수가능지역이 국한되는 효과를 얻을 수 있다.Referring to the drawings, the improved
따라서, 본 발명의 바람직한 실시예에 따른 방수시트(80)는, 수밀부(40)의 완벽한 수밀성 확보 뿐만 아니라, 누수가 발생하였을 경우 그 누수범위를 국부적으로 한정시킬 수 있어 다른 범위로의 누수확대를 방지하며, 또한 이에 따라 누수지점을 찾는데 용이한 잇점을 가짐으로서 보수공사시 작업성을 효율적으로 할 수 있다.Therefore, the
이 때 본 발명에서는, 상기 개량방수시트(80)로서 콤파운드에 개량 아스팔트를 사용한 아스팔트 콤파운드를 사용한 것을 예를 들어 설명하였으나, 이에 한정되지 않고 아스팔트 콤파운드와 유사한 물성을 갖는 다른 콤파운드를 사용하는 것도 가능하다.At this time, the present invention has been described using the asphalt compound using the improved asphalt as a compound as the improved
또한, 본 발명의 바람직한 실시예에 따른 상기 개량방수시트(80) 외에도 중심보강재가 내재되어 있는 방수시트를 사용할 수도 있다.In addition, in addition to the improved
도 5는 본 발명의 바람직한 실시예에 사용되는 마감 부틸 테이프(50)를 나타낸 도면으로서, 상기 마감 부틸 테이프(50)는 상기 개량방수시트(80)들 간의 맞대음 조인트 부분에 부착되어 상기 개량방수시트(80)들을 안정적으로 고정시켜줌과 동시에 맞대음 조인트 부분 즉, 수밀부(40)의 수밀성을 확보할 수 있다. 5 is a view showing a
이러한 상기 마감 부틸 테이프(50)를 구체적으로 살펴보면, 상기 마감 부틸 테이프(50)는 우선 하면에 이형지(51)가 부착된 내열, 내한, 내구성, 수밀성, 접착성과 신장율 및 저온성이 우수한 재질의 부틸고무(52)를 바탕으로 하고, 상기 부틸고무(52)의 상부에는 부직포(53)가 부착되어 방수시공시 그 외부표면에 도막재가 도포되었을 때 상기 개량방수시트의 부직포와 일체성을 지닐 수 있게 할 수 있다. 여기서, 도시되지 않았지만 상기 부틸고무에는 중심재로서 중심 보강재를 삽입할 수 있으며, 이러한 중심보강재로는 강도가 우수한 폴리에스터 직포로 할 수 있다.Looking specifically at the
따라서, 상기한 구성의 개량방수시트(80) 및 마감부틸테이프(50)를 사용한 본 발명의 바람직한 실시예에 따른 방수구조는, 도 6에 나타난 바와 같은 단면구조를 지니게 된다.Therefore, the waterproof structure according to the preferred embodiment of the present invention using the improved
도면을 참조하면, 본 발명의 바람직한 일 실시예에 따른 방수시공방법을 적용한 방수구조는, 모체의 바탕면에 도포된 아스팔트 프라이머층(20)과, 이 아스팔트 프라이머층(20)의 상부에 맞대음 방식으로 배치된 상기 개량방수시트(80)들과, 상기 개량방수시트(80)간의 맞대음 조인트부분에 도포된 아스팔트 프라이머에 의해 형성된 수밀부(40)와, 상기 수밀부(40)의 상부 즉, 상기 아스팔트 프라이머가 도포된 부분의 상부에 부착되는 마감 부틸 테이프(50)와, 상기 마감 부틸 테이프(50)를 포함한 상기 개량방수시트(80)들의 상부에 도포되는 도막재방수층(60) 및 상기 도막재방수층(60)의 상부에 설치된 누름층(70)으로 이루어져 있다.Referring to the drawings, the waterproof structure to which the waterproof construction method according to the preferred embodiment of the present invention is applied, the
여기서, 본 발명의 바람직한 일 실시예에 따른 방수구조는, 특히 수밀부(40) 에 대하여 상기 개량방수시트(80)들간의 맞대음 조인트 부분인 수밀부(40)에 도포된 아스팔트 프라이머가 상기 개량방수시트(80)의 부직포(84)내로 스며들어, 상기 아스팔트 프라이머층(20)과 상기 개량방수시트(80)의 아스팔트 콤파운드층(83) 및 상기 개량방수시트(80)간의 맞대음 조인트 부분의 상부에 도포된 아스팔트 프라이머가 서로 같은 물성으로 인해 용융결합되어 전체적으로 상기 개량방수시트(80)들이 일체화되는 효과를 얻을 수가 있기 때문에, 개량방수시트(80)의 맞대음으로 인한 개량방수시트(80)간의 수밀부의 누수를 원천적으로 방지할 수 있는 구조이다.Here, the waterproof structure according to an embodiment of the present invention, in particular, the asphalt primer applied to the
따라서, 본 발명의 바람직한 일 실시예에 따른 방수구조는, 상기 개량방수시트(80)들의 맞대음 방식에 따른 맞대음 조인트 부위의 수밀성을 안정적이고 완벽히 확보할 수 있으며, 상기 수밀부(40)의 구조와 마감 부틸 테이프(50)에 의해 노출방식 뿐만 아니라 누름층이 형성되는 비노출방식에서도 상기 누름층의 하중에 따른 개량방수시트 모서리부의 피로를 저하시키고 수밀부(40)의 안정성을 확보할 수 있다.Therefore, the waterproof structure according to the preferred embodiment of the present invention, it is possible to securely and completely ensure the watertightness of the butt joint portion according to the butt method of the improved
뿐만 아니라, 본 발명의 바람직한 일 실시예에 따른 방수구조는, 상기 개량방수시트(80)의 상부에 도포되는 아스팔트 프라이머가 상기 개량방수시트의 부직포(84)에 스며들면서, 대략 상기 부직포(84)의 두께로 침식을 하게 되는데, 이때 아스팔트 프라이머에 의해 침식된 단차만큼 상기 마감 부틸 테이프(50)가 부착되어 결과적으로 전체 방수구조의 단차에 의한 문제점을 해결할 수 있었다. In addition, the waterproof structure according to an embodiment of the present invention, while the asphalt primer applied to the upper portion of the improved
도 7a 내지 도 7g는 본 발명의 바람직한 실시예에 따른 상기 개량방수시트를 사용한 방수구조에 따른 방수시공방법을 나타낸 도면들로서, 도면을 참조하여 본 발명의 방수시공방법을 설명하면 다음과 같다.7A to 7G are views illustrating a waterproof construction method according to the waterproof structure using the improved waterproof sheet according to the preferred embodiment of the present invention. Referring to the drawings, the waterproof construction method of the present invention is as follows.
먼저, 방수시공에 앞서 콘크리트 슬라브, 즉, 모체(10)의 바탕면에 대해 원활한 물배수가 이루어지도록 물매공사를 실시한다. 이때, 콘크리트 바탕면의 물구배가 보행용 옥상방수인 경우는 1/100, 비보행용 옥상방수인 경우는 1/50 이상의 구배를 갖도록 하여 빗물 등이 정체되지 않고 원활하게 배수될 수 있게 한다.First, prior to the waterproofing construction is carried out so that the concrete slab, that is, the smooth drainage to the base surface of the
그 후 방수 바탕면을 깨끗하게 처리하고 청소하는 면처리를 실시한 후 도 7a에 도시된 바와 같이 제1 아스팔트 프라이머를 도포함으로써 프라이머층(20)을 형성시켜, 모체(10)와 후속공정에서 부착될 상기 개량방수시트(80)와의 기밀한 밀착을 가능하게 하며, 그 상태를 오랫동안 유지할 수 있게 해준다. After performing the surface treatment to clean and clean the waterproof base surface, and then as shown in Figure 7a by applying a first asphalt primer to form a
상기 제1 아스팔트 프라이머가 건조된 후에는 도 7b에 도시된 바와 같이 상기 개량방수시트(80) 다수개를 맞대음형식으로 배치하여 부착하는데, 상기 개량방수시트(80)의 시공은 먼저 이형지(81)를 제거하고 각각의 개량방수시트(80)간의 사이를 최대 10mm를 넘지 않도록 최대한 맞대음하여 모체(10)의 바탕면에 부착한다. After the first asphalt primer is dried, as shown in FIG. 7B, a plurality of the improved
본 발명에서는 상기 개량방수시트(80)로서 아스팔트 콤파운드층(83)을 형성하고 있는 것을 예를 들어 설명하였으나, 본 발명은 이에 한정되지 않고 상기 개량방수시트(80)와 유사한 물성을 갖는 다른 콤파운드를 사용하는 것도 가능하다.In the present invention, for example, the
상기한 개량방수시트 부착시공을 거친 다음, 상기 개량방수시트(80)의 맞대음 조인트 부위인 수밀부(40)에는 도 7c에 도시된 바와 같이 상기 제1 아스팔트 프라이머와 같은 물성인 제2 아스팔트 프라이머를 도포한다.After the installation of the improved waterproof sheet, the
상기 제2 아스팔트 프라이머가 도포된 후 일정시간 경과하면, 도 7d에 나타 난 바와 같이 상기 제2 아스팔트 프라이머가 상기 개량방수시트의 부직포(84)내로 스며들게 되고, 이에 따라 상기 개량방수시트의 아스팔트 콤파운드층은 상기 제2 아스팔트 프라이머와 물성이 같기 때문에 상기 제2 아스팔트 프라이머는 상기 개량방수시트의 아스팔트 콤파운드층과 용융결합하게 되며, 더욱이 상기 개량방수시트(80)사이로 스며든 제2 아스팔트 프라이머는 제1 아스팔트 프라이머와 합쳐지게 된다.After a predetermined time after the second asphalt primer is applied, as shown in FIG. 7D, the second asphalt primer is permeated into the
이 때, 상기 개량방수시트는, 도포되는 상기 제2 아스팔트 프라이머에 의해 상부의 부직포가 스며들면서 침식하게 되어 대략 부직포의 두께만큼 단차가 생기게 된다.At this time, the improved waterproof sheet is eroded while the upper nonwoven fabric is soaked by the second asphalt primer to be applied, so that a step is generated by approximately the thickness of the nonwoven fabric.
상기 제2 아스팔트 프라이머가 건조경화된 후에는, 도 7e에 도시된 바와 같이 조인트부위의 단차부분에 상기 마감 부틸 테이프(50)를 수밀하게 부착하는데, 이 때 상기 개량방수시트의 부직포(84)가 침식된 부분에 상기 마감 부틸 테이프(50)를 부착함으로써 마감 부틸 테이프 부착에 의한 단차에 의한 문제점을 해소할 수 있었다.After the second asphalt primer is dry hardened, as shown in FIG. 7E, the finishing
부가하여, 상기 마감 부틸 테이프(50)는 상부에 고무롤러 등을 이용하여 가압하면서 밀착시키면 더욱 우수한 수밀성을 가져올 수 있다.In addition, the
본 발명에서는 상기 개량방수시트(80)와 조인트용 마감 부틸 테이프(50)를 이용하여 시공하기 때문에, 아스팔트 프라이머를 이용한 접착층 시공, 시트와 시트의 조인트 시공, 도막 방수제 도포 시공 등과 같이 작업자의 숙련도에 따라 시공상의 하자가 발생할 수 있는 공정 요인을 제거하여 방수구조의 신뢰성을 높이고, 규 격품 사용과 숙련공정의 제거로 인하여 재료비와 인건비를 크게 절감할 수 있다.In the present invention, since the improved
그런 다음, 상기 상기 마감 부틸 테이프(50)와 상기 개량방수시트(80)의 각각 노출되는 외부표면 전면에 도 7f에 도시된 바와 같이 도막재를 1.0~1.5mm두께로 전면도포하여 도막재 방수층(60)을 형성시키는데, 이 때 상기 도막재는 우레탄 도막재, 용제형 아스팔트 도막재, 수용성 아스팔트 도막재 중 선택된 어느 하나로 할 수 있다.Then, as shown in Figure 7f the front surface of each of the
다음으로, 상기 도막재 방수층(60)의 상부에 방수층을 보호하기 위한 보호몰탈 등을 시공한 후, 도 7g에 도시된 바와 같이 누름층(70)을 형성시킨다. Next, after applying a protective mortar for protecting the waterproof layer on the top of the coating material
이 때, 본 발명은 상부면에 누름층(70)을 갖는 비노출 방식의 방수시공방법 이외에 누름층을 형성하지 않는 노출 공법인 경우는 일반 우레탄 또는 노출우레탄과 같은 도막방수재를 동일한 두께로 시공하고, 주지된 탑코팅재를 도포하여 마감한다.At this time, in the present invention, in the case of an exposure method that does not form a pressing layer other than the non-exposed waterproof construction method having the
한편, 상기한 본 발명의 개량방수시트를 이용한 다른 실시예의 방수구조를 살펴보면 다음과 같다.On the other hand, look at the waterproof structure of another embodiment using the improved waterproof sheet of the present invention as follows.
도 8은 상기 개량방수시트를 사용한 본 발명의 다른 실시예에 따른 방수구조를 나타낸 사시도이고, 도 9는 도 8의 A-A선에 따른 단면도이며, 도 10은 도 8의 B-B선에 따른 단면도이다.8 is a perspective view showing a waterproof structure according to another embodiment of the present invention using the improved waterproof sheet, Figure 9 is a cross-sectional view taken along the line A-A of Figure 8, Figure 10 is a cross-sectional view taken along the line B-B of FIG.
먼저, 도 8 및 도 9를 참조하면, 본 발명의 다른 실시예에 따른 방수구조는, 모체(10)의 표면에 다수개의 방수시트(80)를 맞대음 형식으로 배치시켜 형성된 시트방수층과, 이 시트방수층의 하부에 형성된 아스팔트 프라이머층(20)과, 상기 아 스팔트 프라이머층(20)과 방수시트(80) 하부 사이에 부착된 부틸시트(50a)와, 시트방수층의 방수시트(80)의 맞대음 조인트부분(C)의 상부에 주위에 수밀성을 유지하면서 고정시키기 위해 부착된 보강포(100a)와, 보강포(100a)의 상부에 보강포(100a)가 덮히도록 탄성퍼티를 도포하여 형성된 탄성퍼티층(110)과, 도막재방수층(60)으로 이루어져 있다.First, referring to FIG. 8 and FIG. 9, the waterproof structure according to another embodiment of the present invention includes a sheet waterproof layer formed by arranging a plurality of
여기서, 상기 도막재방수층(60)의 상부에는 마감재를 도포하여 마감재도포층(120)이 형성되어 있으며, 상기 마감재는 일반적인 노출형 코팅제로서 적용가능하다.Here, the
상기 프라이머층(20)은 시트방수층의 맞대음 조인트부분(C)의 하부에 형성되며, 상기 부틸시트(50a)가 부착될 부분에만 프라이머를 도포하는 것이 바람직하다.The
그리고, 상기 탄성퍼티는 메움재로서의 역할과 평탄용으로서, 보강포(100a)를 부착하면서 탄성퍼티를 롤러 등을 사용하여 도포한다.The elastic putty serves as a filling material and for flatness, and the elastic putty is applied by using a roller or the like while attaching the reinforcing
한편, 노출형일 경우 상기 도막재방수층(60)을 형성시키지만, 상부에 누름층(미도시)을 설치하는 비노출형인 경우에는, 상기한 방수구조의 보호를 위하여 보호몰탈 또는 보호재를 형성시킨 후 누름층을 설치한다.On the other hand, in the case of the exposure type, the coating
그리고, 상기 도막재방수층(60)은 기후 및 현장 여건에 따라 자연친화적인 수용성 아크릴탄성도막재, 폴리우레탄, 아스팔트씰, 에폭시계도막재, 아스팔트계도막재 및 무기질도막재 등 다양하게 사용할 수 있다.In addition, the coating
여기서, 상기 방수시트(80)는 도 2에 도시된 개량방수시트로서, 상기 시트방수층은 상기 개량방수시트를 서로 맞대음 방식으로 최대한 근접 배치시켜 형성된 다.Here, the
한편, 세로측면의 방수시공에 있어서의 방수구조는, 도 10에 나타난 바와 같이, 모체(10)의 가로 또는 세로를 포함한 모서리부분에 접혀져서 부착되는 방수시트(80)와, 모체(10)의 세로측면에 부착되는 방수시트(80)의 일단부의 하부에 프라이머를 도포하여 형성된 프라이머층(20)과, 이 프라이머층(20)의 상부와 상기 방수시트(80)의 일단부의 하부사이에 부착된 부틸테잎(50b)과, 방수시트(80) 일단부의 상부에 수밀성을 유지하면서 고정시키기 위해 부착된 보강포(100b)와, 방수시트(80)와 상기 보강포(100b)의 각각 노출되는 외부표면에 전면도포되는 도막재방수층(60)과, 도막재방수층(60)의 외부표면에 마감재를 도포하여 형성된 마감재도포층(120)으로 이루어졌다.On the other hand, the waterproof structure in the waterproof construction of the vertical side, as shown in Figure 10, the
여기서, 상기 방수구조는 모체(10)의 세로측면에 부착된 방수시트(80)의 일단부 주위에만 프라이머를 도포하는 것이 바람직하나, 모체의 가로 또는 세로측면을 포함하여 도포할 수 있다.Here, the waterproof structure is preferably to apply a primer only around one end of the
부가하여, 본 발명의 실시예에서, 도막재방수층(60)의 다른 실시예로서 우레탄을 사용할 수 있는데, 이렇게 우레탄을 사용한 도막재방수층은, 상기 맞대음 조인트 부위(C)에 보강포(10a, 100b)를 부착하면서 도막재로서 롤러 등을 사용하여 우레탄을 전체면에 골고루 1차도포하고, 1차도포후에는 규사를 균일하게 도포한 다음, 다시 도막재인 우레탄을 전체면에 골고루 2차도포하여 이루어진다.In addition, in the embodiment of the present invention, urethane may be used as another embodiment of the film
그런 다음, 상기 공정 후, 노출형인 경우에는 상기 도막재 2차도포 후 우레탄이 경화후 마감재로서 탑코팅을 도장하고, 누름층이 형성되는 비노출형인 경우에 는 상기한 방수층의 보호를 위하여 보호몰탈 또는 방수층 보호재를 설치한 후 누름층(미도시)을 설치한다.Then, after the process, in the case of the exposure type, after the second coating of the coating material, the urethane is coated with the top coating as a finishing material after curing, and in the case of the non-exposed type in which the pressing layer is formed, the protective mortar or After installing the waterproofing layer protective material is installed a pressing layer (not shown).
상기한 바와 같은 방수구조를 갖도록 방수시공방법을 시행하는 본 발명은, 개량방수시트(80)와 방수 도막재를 사용한 복합방수공법으로서, 상기 개량방수시트(80)를 맞대음방식으로 배치시켜 원자재를 절감할 뿐만 아니라, 상기 개량방수시트(80)와 아스팔트 프라이머층(20) 및 상기 개량방수시트(80) 맞대음 조인트부분 상부에 도포되는 아스팔트 프라이머에 의해 수밀부(40) 구조를 동일재료로 일체화시킴으로써 수밀성를 완벽하게 확보할 수 있는 구조를 구현할 수 있으며, 단차의 문제점을 해소할 수 있다.The present invention for implementing a waterproof construction method to have a waterproof structure as described above, the composite waterproof method using the improved
상술한 바와 같이 본 발명은 맞대음 공법에서의 취약점인 비노출 방수공법에서의 시트 모서리의 피로에 의한 시트파손 및 수밀부의 불안정성을 해결할 수 있는 방수구조를 구현하여, 노출공법 뿐만 아니라 비노출공법에서도 그 수밀성을 완벽히 확보할 수 있는 개량방수시트와 이를 사용한 방수시공방법 및 방수구조에 관한 것으로, 건물의 옥상방수에 적용된다.As described above, the present invention implements a waterproof structure that can solve sheet breakage and instability of the watertight portion due to fatigue of the edge of the sheet in the non-exposed waterproof method, which is a weak point in the butt method, and its watertightness not only in the exposed method but also in the non-exposed method. The present invention relates to an improved waterproof sheet and a waterproof construction method and a waterproof structure using the same, which are applied to the rooftop waterproofing of a building.
이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술 사상과 아래에 기재될 특허청구범위의 균등 범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.As mentioned above, although this invention was demonstrated by the limited embodiment and drawing, this invention is not limited by this, The person of ordinary skill in the art to which this invention belongs, Of course, various modifications and variations are possible within the scope of equivalents of the claims to be described.
도 1은 본 발명의 바람직한 일 실시예에 따른 개량방수시트를 사용한 방수구조를 나타낸 사시도,1 is a perspective view showing a waterproof structure using an improved waterproof sheet according to an embodiment of the present invention,
도 2와 도 3은 도 1에 사용된 개량방수시트를 각각 나타낸 평면도와 단면도,2 and 3 are a plan view and a cross-sectional view respectively showing the improved waterproof sheet used in FIG.
도 4는 도 1의 개량방수시트들을 맞대음 방식으로 모체에 부착했을 때를 나타낸 도면,4 is a view showing when the improved waterproof sheet of FIG.
도 5는 도 1의 개량방수시트들의 맞대음 조인트부분에 사용되는 마감 부틸 테이프를 나타낸 사시도,FIG. 5 is a perspective view showing a finished butyl tape used in the butt joint portion of the improved waterproof sheets of FIG. 1; FIG.
도 6은 도 1의 I-I선에 따른 단면도,6 is a cross-sectional view taken along the line I-I of FIG.
도 7a 내지 도 7g는 도 1의 본 발명의 방수구조에 따른 방수시공방법을 나타낸 공정단면도,7a to 7g is a process cross-sectional view showing a waterproof construction method according to the waterproof structure of the present invention of Figure 1,
도 8은 본 발명의 다른 실시예에 따른 방수구조를 나타낸 사시도,8 is a perspective view showing a waterproof structure according to another embodiment of the present invention,
도 9는 도 8의 A-A선에 따른 단면도, 9 is a cross-sectional view taken along the line A-A of FIG. 8;
도 10은 도 8의 B-B선에 따른 단면도이다.10 is a cross-sectional view taken along line B-B of FIG. 8.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
10... 모체 20... 프라이머 층10 ...
30... 시트방수층 40... 수밀부30 ...
50... 마감 부틸 테이프 51, 81... 이형지50 ...
52... 부틸고무 53, 84... 부직포52 ...
60... 도막재 방수층 70... 누름층60 ... coating material
80... 개량방수시트 82... 필름80 ...
82a... 노출홀 82b... 노출영역82a ... exposed
83... 아스팔트 콤파운드층 83. Asphalt Compound Layer
Claims (15)