JP2007117534A - Self-adhesive tape roll - Google Patents
Self-adhesive tape roll Download PDFInfo
- Publication number
- JP2007117534A JP2007117534A JP2005315992A JP2005315992A JP2007117534A JP 2007117534 A JP2007117534 A JP 2007117534A JP 2005315992 A JP2005315992 A JP 2005315992A JP 2005315992 A JP2005315992 A JP 2005315992A JP 2007117534 A JP2007117534 A JP 2007117534A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- adhesive tape
- sensitive adhesive
- material layer
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、粘着面が表側向くようにロール状に巻回された清掃用の粘着テープロールに関し、さらに詳しく言えば、粘着テープの機能性の向上と、生産コストの低減の両立を図る粘着テープロールの生産技術に関する。 The present invention relates to a cleaning pressure-sensitive adhesive tape roll wound in a roll shape so that the pressure-sensitive adhesive surface is directed to the front side. More specifically, the pressure-sensitive adhesive tape aims at achieving both improvement in functionality of the pressure-sensitive adhesive tape and reduction in production cost. It relates to roll production technology.
清掃用の粘着テープロールは、例えば特許文献1に示すように、帯状の基材の一方の面に粘着面が形成された粘着テープを、その粘着面が表側向くようにロール状に巻回したものからなり、専用の治具(特許文献1の図3B参照)に装着して、粘着面を床などの被清掃面に接触させながら転がすことにより、被清掃面上のゴミを粘着面で捕らえることができる。
For example, as shown in
基材の他方の面(反粘着面)には、基材補強用のラミネートフィルムが設けられており、さらにその下には、シリコン樹脂などの剥離材を塗布した剥離処理面が設けられている。剥離処理面は粘着テープをロール状に積層した場合に、下層の粘着テープの粘着面が接触する接触面であり、最外層の粘着テープを剥がし取る際に、下層の粘着面によって基材が破壊されないようにするために設けられている。 A laminate film for reinforcing the substrate is provided on the other surface (anti-adhesion surface) of the substrate, and further, a release treatment surface to which a release material such as silicon resin is applied is provided below the laminate film. . The peeled surface is the contact surface where the adhesive surface of the lower adhesive tape comes into contact when the adhesive tape is laminated in a roll shape. When the outermost adhesive tape is peeled off, the substrate is destroyed by the lower adhesive surface. It is provided to prevent this from happening.
しかしながら、従来より剥離処理面は粘着テープを積層するためには必ず設けなくてはならない。したがって、その分、材料コストや生産コストが高くなっていた。また、巻き戻し力(巻き戻したときの抵抗力)が小さすぎると、粘着テープロールを床面で転がした際に、巻き戻し力が粘着テープと床面との間の粘着力に負けてしまい、粘着テープが床面に張り付く、いわゆるレール引き現象を起こす場合もあり、剥離処理面の設計には慎重を要する。 However, conventionally, the peel-treated surface must be provided for laminating the adhesive tape. Therefore, the material cost and production cost have increased accordingly. Also, if the unwinding force (resistance force when unwinding) is too small, when the adhesive tape roll is rolled on the floor surface, the unwinding force is lost to the adhesive force between the adhesive tape and the floor surface. In some cases, the adhesive tape sticks to the floor surface, which may cause a so-called rail pulling phenomenon.
そこで、本発明は上述した課題を解決するためになされたものであって、その目的は、清掃能力を落とすことなく、より安価な粘着テープロールを提供することにある。 Then, this invention was made | formed in order to solve the subject mentioned above, The objective is to provide a cheaper adhesive tape roll, without reducing cleaning capability.
上述した目的を達成するため、本発明は以下に示すいくつかの特徴を備えている。請求項1に記載の発明は、基材の一方の面に粘着面が形成された粘着テープをその粘着面が表側を向くように巻回してなる粘着テープロールにおいて、上記粘着面には、上記基材の他方の面に対する剥離手段が設けられていることを特徴としている。
In order to achieve the above-described object, the present invention has several features described below. The invention according to
請求項2に記載の発明は、上記請求項1において、上記基材の一方の面には、上記粘着面を形成する粘着材層が設けられており、上記粘着材層の上に上記剥離手段としての剥離材層が部分的に設けられていることを特徴としている。 According to a second aspect of the present invention, in the first aspect, an adhesive material layer that forms the adhesive surface is provided on one surface of the base material, and the peeling means is provided on the adhesive material layer. The release material layer is partially provided.
請求項3に記載の発明は、上記請求項1または2において、上記剥離材層は、上記粘着面に対する単位面積当たりの占有比が5%以上50%以下であることを特徴としている。 A third aspect of the present invention is characterized in that, in the first or second aspect, the release material layer has an occupation ratio per unit area with respect to the adhesive surface of 5% or more and 50% or less.
請求項4に記載の発明は、上記請求項1,2または3において、上記剥離材層は線状,格子状,波状および/または点状に設けられていることを特徴としている。 According to a fourth aspect of the present invention, in the first, second, or third aspect, the release material layer is provided in a line shape, a lattice shape, a wave shape, and / or a dot shape.
請求項5に記載の発明は、上記請求項1〜4のいずれか1項において、上記剥離材層は、ゴム系,アクリル系,ウレタン系,EVA系および/またはアモルファスポリαオレフィン系を主成分とする合成樹脂材からなることを特徴としている。
The invention according to
請求項6に記載の発明は、上記請求項1〜5のいずれか1項において、上記剥離材層は、幅が1mm以下であり、かつ、厚さが30〜120μmであることを特徴としている。 A sixth aspect of the present invention is characterized in that, in any one of the first to fifth aspects, the release material layer has a width of 1 mm or less and a thickness of 30 to 120 μm. .
請求項7に記載の発明は、上記請求項2ないし6のいずれか1項において、上記剥離材層は、少なくとも対向する上記基材の他方の面を支持するに必要な保持力を有する微粘着性を備えていることを特徴としている。 A seventh aspect of the present invention provides the adhesive according to any one of the second to sixth aspects, wherein the release material layer has a holding force necessary to support at least the other surface of the opposing substrate. It is characterized by having sex.
請求項1および2に記載の発明によれば、粘着面の上に剥離材層を形成した剥離手段が設けられていることにより、従来のような剥離処理面を基材の他方の面に設ける必要が無く、よりコストを安く生産することができる。 According to the first and second aspects of the present invention, by providing the peeling means having the release material layer formed on the adhesive surface, a conventional release treatment surface is provided on the other surface of the substrate. This is unnecessary and can be produced at lower cost.
請求項3に記載の発明によれば、剥離材層の専有面積が5%未満の場合は、剥離材層の面積が小さすぎるため、基材と粘着面が張り付き、剥がした際に基材破壊を起こすおそれがある。逆に50%よりも大きいと、粘着面と被清掃面の接触を阻害してしまうため、清掃能力が低下するおそれがあるばかりでなく、レール引き現象を引き起こすおそれもある。
According to the invention described in
請求項4に記載の発明によれば、剥離材層を線状,点状もしくは波状に設けることにより、粘着作用と剥離作用を均等に分布させることができる。 According to the fourth aspect of the present invention, the adhesive action and the peeling action can be evenly distributed by providing the release material layer in a line shape, a dot shape or a wave shape.
請求項5に記載の発明によれば、剥離材層はゴム系,アクリル系,ウレタン系,EVA系および/またはアモルファスポリαオレフィン系を主成分とするため、剥離作用を効果的に持続させることができるばかりでなく、清掃時に適度なクッション性を生むことで、凹凸面に入り込んだゴミを確実に取り込むことができる。
According to the invention described in
請求項6に記載の発明によれば、剥離層の幅が1mmよりも大きいと、粘着面と被清掃面の接触が阻害されるため、粘着力が低下しすぎるおそれがある。また、厚さが30μmよりも薄い場合は、粘着面が上層の基材に張り付きすぎて基材破壊を起こすおそれがある。逆に120μmよりも厚いと、粘着力が低下しすぎてしまうおそれがある。 According to the sixth aspect of the present invention, if the width of the release layer is larger than 1 mm, the contact between the adhesive surface and the surface to be cleaned is hindered, and the adhesive force may be excessively reduced. On the other hand, when the thickness is less than 30 μm, the adhesive surface may stick to the upper layer base material, which may cause base material destruction. On the other hand, if it is thicker than 120 μm, the adhesive strength may be excessively reduced.
請求項7に記載の発明によれば、剥離材層が基材の他方の面を支持するに必要な保持力を有する微粘着性を備えていることにより、被清掃面との粘着力と巻き戻し力のバランスが崩れることにより発生するレール引き現象を防止することができる。 According to the seventh aspect of the present invention, since the release material layer has a slight adhesiveness having a holding force necessary to support the other surface of the base material, the adhesive force with the surface to be cleaned and the winding force are reduced. The rail pulling phenomenon that occurs when the balance of the return force is lost can be prevented.
次に、本発明の実施形態について図面を参照しながら説明するが、本発明はこの限りではない。図1は本発明の一実施形態に係る粘着テープロールの斜視図であり、図2は、そのA−A線断面図である。 Next, embodiments of the present invention will be described with reference to the drawings, but the present invention is not limited thereto. FIG. 1 is a perspective view of an adhesive tape roll according to an embodiment of the present invention, and FIG. 2 is a cross-sectional view taken along line AA.
この粘着テープロール1は、テープ状基材21の一方の面に粘着面22が形成された粘着テープ2を、その粘着面22が表側(図1では上面側)を向くように巻芯3に沿ってロール状に巻回したものからなる。
The pressure-sensitive
通常、巻芯3にはボール紙製の巻芯が用いられているが、これ以外に合成樹脂製など他の材質であってもよい。また、巻芯3を使わずに粘着テープ2のみをロール状に巻回する、いわゆるコアレスタイプであってもよく、本発明において、巻芯3はあくまで任意的な構成要素である。
Usually, a core made of cardboard is used for the
基材21は例えば紙製で、図2に示すように、一方の面(表面)には粘着材が塗布された粘着面22が形成されている。この例において、粘着剤はSIS(スチレン−イソプレン−スチレン)系粘着材にタッキファイヤーやナフテンオイル,老化防止剤などの各種添加剤を加えたものからなるが、粘着材の種類は使用される清掃面(例えばフローリングや絨毯など)に応じて強粘着、弱粘着など任意に選択されてよい。また、基材21の材質も紙以外に樹脂フィルムや不織布が用いられてもよい。
The
粘着面22は、基材21の一方の面に粘着材を一様な厚さT1にベタ塗りした粘着材層からなり、この例において、粘着材層の厚さT1は15〜20μmとなるように塗布されている。
The
基材21の粘着面22の両端には、粘着材が塗布されていない未粘着部(ドライエッジ)23,23が設けられているが、この実施形態において、未粘着部23,23はあくまで任意的な構成要素である。
At both ends of the
粘着面22の上には、上層側の粘着テープ2と下層側の粘着テープ2とが張り付かないようにするための剥離手段4が設けられている。図2に示すように、剥離手段4は、粘着面22の上に粘着テープ2の繰り出し方向に沿って平行に筋状に形成された剥離材層41を有し、それらが所定の間隔(この例では、間隔W1=1.7mm)をもって多数配置されている。
On the
剥離材層41は、幅W2が1mm以下であり、かつ、厚さT2が30〜120μmであることが好ましい。すなわち、剥離材層41の幅が1mmよりも大きいと、粘着力が低下しすぎるおそれがある。また、剥離材層41の厚さが30μmよりも薄い場合は、粘着面が上層の基材に張り付きすぎて基材破壊を起こすおそれがある。逆に120μmよりも厚いと、粘着力が低下しすぎてしまうおそれがある。
The
この実施形態では、剥離材層41は粘着テープ2の繰り出し方向に沿って筋状に形成されているが、これ以外に、格子状であってもよく、また例えば点状に分散して設けられていてもよいし。すなわち、粘着面22に対する単位面積当たりの占有比が5%以上50%以下(より好ましくは10%以上30%以下)であれば、その形態は仕様に応じて任意である。
In this embodiment, the
これによれば、剥離材層41の専有面積が5%未満の場合は、剥離材層41が少なすぎてしまい、基材が粘着面に張り付き、剥がした際に基材破壊を起こすおそれがある。逆に50%よりも大きいと、被清掃面に対する粘着力が小さすぎるため、清掃能力が低下するおそれがあるばかりでなく、レール引き現象を引き起こすおそれもある。
According to this, when the exclusive area of the
この例において、剥離材層41は、例えばCEBC(オレフィン結晶:エチレン:ブチレン:オレフィン結晶ブロックコポリマー)などのゴム系材料を主成分とし、そこに粘着面22との親和性をよくするためSIS系ポリマーを微量添加して、さらにタッキファイヤーやパラフィンオイルなどの各種添加剤を添加したものからなる。
In this example, the
この例において、剥離材層41は、パラフィンオイルなどの添加剤を用いて微粘着性を得るようにしているが、これ以外にマイクロバルーン混合や、N2ガスまたはCO2ガスを使ったメカニカル発泡などの機械的手法を用いてもよい。さらに別の方法としては、弾性粉体を混合したり、アクリル系粘着材に可塑剤を添加するなどしてもよい。
In this example, the
基材21の他方の面(裏面)には、基材21の補強用としてのラミネートフィルム24が設けられている。この例において、ラミネートフィルム24はポリエチレン製の薄いフィルムからなり、基材21に一体的に設けられている。ラミネートフィルム24は、剥離材層41の粘着性をコントロールすることにより不要とすることもできる。なお、基材21がプラスチックフィルム製の場合は、ラミネートフィルム24は不要である。
On the other surface (back surface) of the
再び図1を参照して、粘着テープ2にはほぼ1周長毎に切断用の切れ目5が設けられている。本発明において、切れ目5とは粘着テープ2を幅方向に沿って切断するために用いられる切断手段をいい、例えば長孔や波形のスリットを並べたものやミシン目などの間欠スリットが含まれる。
Referring to FIG. 1 again, the
この実施形態において、切れ目5は粘着テープ2の幅方向に沿ってほぼ平行に設けられているが、これ以外に斜め方向に形成されていてもよい。さらには、粘着テープ2の端部の一部に切断のきっかけとなるための、短い切れ目であってもよい。
In this embodiment, the
次に、剥離材層41の具体的な性状について説明する。図3は、剥離材層41を構成する剥離材の巻き戻し力の径日変化を示すグラフであり、表1はその評価結果をまとめた表である。
Next, specific properties of the
巻き戻し力とは、粘着面22と反粘着面(ラミネートフィルム24の面)との間の界面での接着力をいう。この例では図1と同様に構成した粘着テープを用意し、各温度中で所定日数放置したのち、その巻き戻し力を測定した。
The unwinding force refers to the adhesive force at the interface between the
この巻き戻し力について、剥離材と粘着材とで比較したところ、単に粘着材のみの場合では、粘着材が基材に完全に張り付いてしまい、引き剥がすと基材破壊を起こした。これに対し、剥離材層を備えた粘着テープは常温,中温(35℃),高温(60℃)において、恒久的に安定した巻き戻し力を得ることができ、粘着層の上に設けることにより、十分な剥離作用を得ることができる。なお、粘着材のみの場合は基材背面への粘着性が強く、ブランクから基材破壊が発生するため、各グラフには示されていない。 When this unwinding force was compared between the release material and the adhesive material, when only the adhesive material was used, the adhesive material was completely adhered to the base material, and when it was peeled off, the base material was destroyed. On the other hand, the pressure-sensitive adhesive tape provided with the release material layer can obtain a permanently stable unwinding force at room temperature, medium temperature (35 ° C.), and high temperature (60 ° C.), and is provided on the pressure-sensitive adhesive layer. A sufficient peeling action can be obtained. In addition, in the case of only an adhesive material, since the adhesiveness to the back surface of a base material is strong and base material destruction generate | occur | produces from a blank, it is not shown by each graph.
次に、図4は剥離材と粘着材の接着力の変化を示すグラフであり、表2はその評価結果をまとめた表である。 Next, FIG. 4 is a graph showing a change in the adhesive force between the release material and the adhesive material, and Table 2 is a table summarizing the evaluation results.
接着力とは、粘着面と接触面との間の界面接着力をいい、この例では粘着テープをステンレス板に貼り付け、所定時間放置したのちJIS−Z0237に準拠した180°引き剥がし接着力をいう。 Adhesive force refers to the interfacial adhesive force between the adhesive surface and the contact surface. In this example, the adhesive tape is applied to a stainless steel plate, left for a predetermined time, and then peeled 180 ° in accordance with JIS-Z0237. Say.
これによれば、粘着材は一般に感圧式であるため、貼り付けた後に接着性が漸次向上していくが、剥離材は、常にほぼ一定の微粘着状態を維持しており、基材に対する十分な剥離効果が得られることがわかる。 According to this, since the adhesive material is generally pressure-sensitive, the adhesion gradually improves after being applied, but the release material always maintains a substantially constant slightly adhesive state, which is sufficient for the substrate. It can be seen that a good peeling effect can be obtained.
この例において、粘着テープ2は、ロール状に巻回されているが、例えばシート体を積層するように設けてもよく、粘着テープの粘着面の上に自走の粘着テープの下面が積層する構造であれば、全ての態様に適用可能である。
In this example, the pressure-sensitive
1 粘着テープロール
2 粘着テープ
21 基材
22 粘着面
23 未粘着部(ドライエッジ)
24 ラミネートフィルム
3 巻芯
4 剥離手段
41 剥離材層
5 切れ目
DESCRIPTION OF
24
Claims (7)
上記粘着面には、上記基材の他方の面に対する剥離手段が設けられていることを特徴とする粘着テープロール。 In the pressure-sensitive adhesive tape roll formed by winding the pressure-sensitive adhesive tape having the pressure-sensitive adhesive surface formed on one surface of the substrate so that the pressure-sensitive adhesive surface faces the front side,
The pressure-sensitive adhesive tape roll is provided with a peeling means for the other surface of the substrate.
The pressure-sensitive adhesive according to any one of claims 2 to 6, wherein the release material layer has a slight adhesiveness having a holding force necessary to support at least the other surface of the base material facing the release material layer. Tape roll.