JP2006342421A - 耐溶接割れ性に優れた高張力鋼の製造方法 - Google Patents
耐溶接割れ性に優れた高張力鋼の製造方法 Download PDFInfo
- Publication number
- JP2006342421A JP2006342421A JP2005308535A JP2005308535A JP2006342421A JP 2006342421 A JP2006342421 A JP 2006342421A JP 2005308535 A JP2005308535 A JP 2005308535A JP 2005308535 A JP2005308535 A JP 2005308535A JP 2006342421 A JP2006342421 A JP 2006342421A
- Authority
- JP
- Japan
- Prior art keywords
- steel
- temperature
- strength
- toughness
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 質量%で、C:0.0002〜0.15%、Si:0.01〜2%、Mn:2〜5%、B<0.0003%を含有し、さらに必要に応じて、Cu、Ni、Cr、Mo、V、Nb、Ti、REM、Mg、Ca、Al、Nを含有し、かつPcm=C%+Si%/30+Mn%/20+Cu%/20+Ni%/30+Cr%/20+Mo%/15+V%/10+5B(質量%)≦0.3%を満たす鋼を鋳造後室温まで冷却することなくそのままか一度室温まで冷却した後に950〜1250℃に再加熱し、Ar3点以上の温度で圧延を終了し、かつ、Ar3点以上の温度から室温〜650℃の範囲に強制冷却を行うことを特徴とする。また、前記強制冷却の後に、100〜700℃の温度で熱処理を施すことを特徴とする。
【選択図】 なし
Description
このため、鋼の高強度化を図る観点から、Cの下限を0.0002%とした。これに対して、Cの含有量が0.15%を越えると、加工性、溶接性、靭性が著しく劣化するため、Cの上限を0.15%に設定した。
Claims (7)
- 質量%で、
C :0.0002〜0.15%、
Si:0.01〜2%、
Mn:2〜5%、
B<0.0003%
を含有し、かつ
Pcm=C%+Si%/30+Mn%/20+Cu%/20+Ni%/30+Cr%/20+Mo%/15+V%/10+5B%≦0.3%
を満たし、残部Feおよび不可避的不純物からなる鋼を鋳造し、
室温まで冷却することなくそのまま、または一度室温まで冷却し、
950〜1250℃に再加熱し、Ar3点以上の温度で圧延を終了し、かつ、Ar3点以上の温度から室温〜650℃の温度域に強制冷却することを特徴とする、引張強さ570N/mm2以上の、耐溶接割れ性に優れた高張力鋼の製造方法。 - さらに、質量%で、
Cu:0.001〜3%、
Ni:0.001〜3%、
Cr:0.001〜3%、
Mo:0.001〜3%
の1種または2種以上を含有することを特徴とする、請求項1に記載の耐溶接割れ性に優れた高張力鋼の製造方法。 - さらに、質量%で、
V :0.0001〜0.2%、
Nb:0.0001〜0.1%
Ti:0.0001〜0.2%
の1種または2種以上を含有することを特徴とする、請求項1または2に記載の耐溶接割れ性に優れた高張力鋼の製造方法。 - さらに、質量%で、
REM:0.0001〜0.1%、
Mg:0.0001〜0.02%、
Ca:0.0001〜0.02%
の1種または2種以上を含有することを特徴とする、請求項1乃至3のいずれか1項に記載の耐溶接割れ性に優れた高張力鋼の製造方法。 - さらに、質量%で、
Al:0.0001〜0.1%
を含有することを特徴とする、請求項1乃至4のいずれか1項に記載の耐溶接割れ性に優れた高張力鋼の製造方法。 - さらに、質量%で、
N :0.0001〜0.01%
を含有することを特徴とする、請求項1乃至5のいずれか1項に記載の耐溶接割れ性に優れた高張力鋼の製造方法。 - 前記強制冷却の後に、100〜700℃の温度で熱処理を施すことを特徴とする、請求項1乃至6のいずれか1項に記載の耐溶接割れ性に優れた高張力鋼の製造方法。