JP2005279936A - Paper recording material - Google Patents
Paper recording material Download PDFInfo
- Publication number
- JP2005279936A JP2005279936A JP2004092750A JP2004092750A JP2005279936A JP 2005279936 A JP2005279936 A JP 2005279936A JP 2004092750 A JP2004092750 A JP 2004092750A JP 2004092750 A JP2004092750 A JP 2004092750A JP 2005279936 A JP2005279936 A JP 2005279936A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- paper
- laser beam
- beam irradiation
- recording material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、紙製記録材料に関し、更に詳しくは、真偽の判定あるいは偽造または改竄等の防止に有用な印字機能を有する紙製記録材料に関するものである。 The present invention relates to a paper recording material, and more particularly to a paper recording material having a printing function useful for determining authenticity or preventing forgery or tampering.
従来、紙基材をベ−スとした紙製記録材料としては、例えば、紙幣、株券、商品券、宝くじ、その他等の有価証券類、帳票類、記録紙類、その他等の種々の形態のものが知られている。
而して、これらの紙製記録材料は、一般に、紙基材をベ−ズ素材とし、例えば、紙基材自身にすかしを施したり、あるいは、その片面あるいは両面に、マイクロ文字、凹半印刷、隠し文字、蛍光印刷等の特殊印刷を施したり、更には、金属箔やホログラム箔等を転写あるいはシ−ルして、その真偽の判定をしたり、あるいは、その偽造または改竄等を防止している。
例えば、有価証券類においては、紙基材の表面、あるいは、裏面等の面に、印刷等により、例えば、発行者名、コ−ド番号、発行年月日、金額、その他等が印字されると共に、その使用者あるいは所有者の氏名等を自署して有価証券類として使用されている。
しかし、上記の例では、技術の向上等により、その真偽の判定が極めて難しく、また、その使用者あるいは所有者の氏名等の自署等は、主に、ボ−ルペン、万年質等による手書きが多く、記名直後にその部分に接触すると、簡単に消えてしまったり、また、磨耗や溶剤等により容易に消去が可能であったり、その安全性、信頼性、真偽、偽造、改竄、その他等の観点から非常に問題視されているものである。
上記のような問題点を解決すべく、例えば、紙中に発泡層を積層した基材を漉き入れして隠蔽したことを特徴とする用紙等が提案されている（例えば、特許文献１参照。）。
Thus, these paper recording materials generally use a paper base material as a base material. For example, the paper base material itself is watermarked, or one side or both sides are provided with a micro character, a concave half. Perform special printing such as printing, hidden characters, fluorescent printing, and transfer or seal metal foil, hologram foil, etc. to determine its authenticity, or counterfeit or tampering It is preventing.
For example, in securities, the issuer's name, code number, issue date, amount, etc. are printed on the surface of the paper substrate, such as the back surface, by printing, etc. At the same time, the name of the user or owner is self-signed and used as securities.
However, in the above example, it is extremely difficult to determine the authenticity due to improvement of technology, etc. Also, the self-signature of the user or owner's name etc. is mainly due to ball pen, perennial quality, etc. There are many handwriting, and if it touches the part immediately after the name, it will disappear easily, and it can be easily erased due to wear, solvent, etc., its safety, reliability, authenticity, forgery, falsification, It is regarded as very problematic from other viewpoints.
In order to solve the above-described problems, for example, a paper or the like characterized in that a base material in which a foam layer is laminated in paper is inserted and concealed has been proposed (see, for example, Patent Document 1). ).
しかしながら、上記で提案されている用紙では、紙中に発泡層を積層した基材を所望どおりに漉き入ること自体が極めて困難であるばかりではなく、それにより真偽の判定あるいは偽造または改竄等を防止するために、微細なパタ−ンを付与することも困難であり、、更に、絵柄パタ−ンと発泡パタ−ン等を同調整合させる必要性等が生じる場合、その対応、柔軟性等に欠けるという問題点を有するものである。
更に、上記で提案されている用紙では、紙基材の表面あるいは裏面に設けた印字情報等は、摩擦、その他等の各種の外力、水、溶剤、酸、アルカリ、その他等の各種の薬品、その他等により、容易に消失するという問題点があり、また、その美麗感、意匠性等に劣るという問題点を有するものである。
そこで本発明は、真偽の判定あるいは偽造または改竄等の防止に有用な印字機能を有する紙製記録材料を提供することである。
However, in the paper proposed above, it is not only extremely difficult to insert a base material in which a foamed layer is laminated in paper as desired, but it is also possible to determine authenticity or counterfeit or falsify. In order to prevent this, it is difficult to give a fine pattern, and when there is a need to synchronize and match the pattern and foam pattern, etc. It has the problem of lacking.
Furthermore, in the paper proposed above, the printing information provided on the front or back surface of the paper substrate includes various external forces such as friction, other, various chemicals such as water, solvent, acid, alkali, etc. There is a problem that it disappears easily due to others and the like, and there is a problem that it is inferior in its beauty and design.
Therefore, the present invention is to provide a paper recording material having a printing function useful for authenticity determination or prevention of forgery or falsification.
本発明者は、上記のような問題点を解決すべく種々研究の結果、紙基材と、樹脂をビヒクルとし、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、樹脂に対し、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層と、紙基材とを順次に積層して紙製記録材料を製造し、而して、該紙製記録材料の表面および／または裏面の面に、例えば、ＹＡＧレ−ザ−光線を照射したところ、紙製記録材料を構成する紙基材等は、ＹＡＧレ−ザ−光線による影響を受けることなく、他方、紙製記録材料を構成するレ−ザ−光線照射発色樹脂層において、上記のＹＡＧレ−ザ−光線のエネルギ−を吸収し、その部分において、炭化による黒色発色、あるいは、発泡による白色発色を形成し、これにより、その印字状態を透かし画像あるいはぼかし画像として明確に視認し得ることができ、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得る共に印字後のレ−ザ−印字画像による透かし画像あるいはぼかし画像は、その外側に位置する紙基材により保護されて、外的影響を受けることなく、レ−ザ−印字画像による透かし画像あるいはぼかし画像が、消失、不鮮明等になることもなく、また、その真偽の判定等が容易であると共にその改変、偽造、改竄等を防止することができ、極めて有用なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得る紙製記録材料を見出して本発明を完成したものである。 As a result of various studies to solve the above problems, the present inventor has a paper base material, a resin as a vehicle, and a color former that develops color by laser beam irradiation. -A laser beam irradiation coloring resin layer made of a resin composition in which the content of the color former that develops color upon irradiation with light is 0.01 wt% to 50.0 wt% with respect to the resin; and a paper substrate. A paper recording material is manufactured by laminating sequentially, and the surface of the paper recording material and / or the back surface is irradiated with, for example, a YAG laser beam. The paper base material, etc., which is not affected by the YAG laser beam, on the other hand, in the laser beam irradiation coloring resin layer constituting the paper recording material, the above YAG laser beam Absorbs energy, and in that part, black coloration due to carbonization, or A white color is formed by foaming, so that the printed state can be clearly seen as a watermark image or a blurred image, and a watermark image or a blurred image can be formed by an extremely clear laser printed image. The watermark image or blurred image by the laser-printed image after printing is protected by the paper substrate located outside thereof, and the watermark image or blurred image by the laser-printed image is not affected externally. However, it is easy to determine the authenticity of the image and prevent its alteration, forgery, falsification, etc., and it is a very useful laser-printed watermark. The present invention has been completed by finding a paper recording material capable of forming an image or a blurred image.
すなわち、本発明は、紙基材と、樹脂をビヒクルとし、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、樹脂に対し、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層と、紙基材とを順次に積層したことを特徴とする紙製記録材料に関するものである。 That is, the present invention comprises a paper base material, a resin as a vehicle, a color former that develops color by laser beam irradiation, and the content of the color former that develops color by laser beam irradiation is a resin. On the other hand, the present invention relates to a paper recording material characterized by laminating a laser beam irradiation coloring resin layer comprising a resin composition comprising 0.01 wt% to 50.0 wt% and a paper substrate in order. Is.
本発明においては、ＹＡＧレ−ザ−光線等を照射しても、紙製記録材料を構成する紙基材等は、ＹＡＧレ−ザ−光線による影響を受けることなく、かつ、カ−ド基材を構成するレ−ザ−光線照射発色樹脂層において、上記のＹＡＧレ−ザ−光線のエネルギ−を吸収し、その部分において、炭化による黒色発色、あるいは、発砲による白色発色を形成し、それにより、その印字状態を透かし画像あるいはぼかし画像として明確に視認し得ることができ、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得る共に印字後のレ−ザ−印字画像によるによる透かし画像あるいはぼかし画像は、その外側に位置する紙基材により保護されて、外的影響を受けることなく、レ−ザ−印字画像による透かし画像あるいはぼかし画像が、消失、不鮮明等になることもなく、また、その真偽の判定等が容易であると共にその改変、偽造、改竄等を防止することができ、極めて有用なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得るという利点を有するものである。 In the present invention, the paper base material constituting the paper recording material is not affected by the YAG laser beam even when irradiated with the YAG laser beam, and the card group. The laser beam irradiation coloring resin layer constituting the material absorbs the energy of the above-mentioned YAG laser beam, and forms a black coloration by carbonization or a white coloration by firing in that portion. Thus, the printing state can be clearly recognized as a watermark image or a blurred image, and a watermark image or a blurred image can be formed by a very clear laser printed image, and the laser printed image after printing can be formed. The watermark image or blurred image by the image is protected by the paper base located outside, and the watermark image or blurred image by the laser print image is not affected by external influences. However, it is easy to determine the authenticity of the image and prevent its alteration, forgery, falsification, etc., and it is a very useful laser-printed watermark. This has the advantage that an image or a blurred image can be formed.
以下、上記の本発明に係る紙製記録材料について図面等を用いて更に詳しく説明する。 まず、本発明に係る紙製記録材料を構成する層構成についてその二三例を例示して図面を用いて説明すると、図１、図２、および図３は、本発明に係る紙製記録材料についてその二三例の層構成を示す概略的断面図であり、図４は、上記の図１に示す本発明に係る紙製記録材料を使用し、これに、レ−ザ−光線を照射してレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成した紙製記録材料についしその層構成の一例を示す概略的断面図である。 Hereinafter, the paper recording material according to the present invention will be described in more detail with reference to the drawings. First, the layer configuration constituting the paper recording material according to the present invention will be described with reference to the drawings by illustrating a few examples. FIGS. 1, 2 and 3 show the paper recording material according to the present invention. FIG. 4 is a schematic cross-sectional view showing the layer structure of a few examples of the paper, and FIG. 4 is a diagram showing a paper recording material according to the present invention shown in FIG. FIG. 6 is a schematic cross-sectional view showing an example of the layer structure of a paper recording material on which a watermark image or a blurred image formed by a laser print image is formed.
まず、本発明に係る紙製記録材料Ａとしては、図１に示すように、紙基材１と、樹脂をビヒクルとし、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、樹脂に対し、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層２と、紙基材１ａとを順次に積層した構成からなることを基本構造とするものである。
First, as shown in FIG. 1, the paper recording material A according to the present invention includes a
而して、本発明に係る紙製記録材料について、具体例を例示すると、図２に示すように、紙基材１と、樹脂を主成分とする樹脂組成物による樹脂層３と、樹脂をビヒクルとし、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、樹脂に対し、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層２と、紙基材１ａとを順次に積層した構成からなる本発明に係る紙製記録材料Ａ1 を例示することがてきる。
更に、本発明に係る紙製記録材料について、別の具体例を例示すると、図３に示すように紙基材１と、樹脂を主成分とする樹脂組成物による樹脂層３と、樹脂をビヒクルとし、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、樹脂に対し、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層２、樹脂を主成分とする樹脂組成物による樹脂層３ａと、紙基材１ａとを順次に積層した構成からなる本発明に係る紙製記録材料Ａ2 を例示することがてきる。
Thus, as a specific example of the paper recording material according to the present invention, as shown in FIG. 2, a
Furthermore, another specific example of the paper recording material according to the present invention is illustrated. As shown in FIG. 3, a
上記の例示は、本発明に係る紙製記録材料についてその一二例を例示したものであり、本発明は、これに限定されるものではないものである。
なお、本発明において、図示しないが、本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層は、紙基材の全面のみならず記録したい部分に部分的に設けることもできるものである。
また、本発明においては、図示しないが、更に、その使用目的、用途等によって、他の基材を任意に積層して、種々の形態からなる多層の紙製記録材料を設計して製造することができるものである。
The above exemplification illustrates one or two examples of the paper recording material according to the present invention, and the present invention is not limited thereto.
In the present invention, although not shown, the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention may be partially provided not only on the entire surface of the paper substrate but also on the portion to be recorded. It can be done.
In the present invention, although not shown in the drawings, according to the purpose of use, application, etc., other base materials are arbitrarily laminated, and multilayer paper recording materials having various forms are designed and manufactured. It is something that can be done.
次に、本発明において、上記のような本発明に係る紙製記録材料を使用し、これにレ−ザ−光線を照射してレ−ザ−印字画像を形成した紙製記録体およびそのレ−ザ−光線照射方法等について、上記の図１に示す本発明に係る紙製記録材料Ａを使用する場合で説明すると、図４に示すように、本発明に係る紙製記録材料Ａを構成するレ−ザ−光線照射発色樹脂層２の表面に、レ−ザ−光線１１を照射すると、該レ−ザ−光線１１は、上記のレ−ザ−光線照射発色樹脂層２に到達し、その部分のレ−ザ−光線照射発色樹脂層２においてレ−ザ−光線によるエネルギ−を吸収し、そのレ−ザ−光線照射部分において、炭化による黒色発色、あるいは、発砲による白色発色等を生成して、例えば、文字、数字、記号、図柄、その他等からなるレ−ザ−印字画像１２による透かし画像あるいはぼかし画像１２ａを極めて鮮明に形成して、本発明に係る紙製記録材料Ａを使用した本発明に係る紙製記録体Ｂを製造し得るものである。
上記の例示は、本発明に係る紙製記録材料を使用してレ−ザ−印字するその一例を例示したものであり、本発明は、これに限定されるものではないものである。
なお、本発明において、本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層の表面に、レ−ザ−光線を照射しても、紙基材の表面あるいは裏面には何ら影響を与えることもないものである。
また、本発明において、図示しないが、勿論、上記の図２、３に示す本発明に係る紙製記録材料について上記と同様にしてレ−ザ−光線を照射して、レ−ザ−印字画像による透かし画像あるいはぼかし画像を形成した本発明に係る紙製記録体を同様に製造し得るものである。
Next, in the present invention, a paper recording material using the paper recording material according to the present invention as described above and irradiating it with a laser beam to form a laser print image, and its laser When the paper recording material A according to the present invention shown in FIG. 1 is used to explain the method of irradiating the light beam, the paper recording material A according to the present invention is configured as shown in FIG. When the
The above illustration is an example of laser printing using the paper recording material according to the present invention, and the present invention is not limited to this.
In the present invention, even if the laser beam is irradiated on the surface of the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention, It has no effect.
In the present invention, although not shown in the drawing, of course, the paper recording material according to the present invention shown in FIGS. Thus, the paper recording body according to the present invention in which the watermark image or the blurred image is formed can be similarly manufactured.
ところで、本発明に係る紙製記録材料においては、基本的には、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層が、例えば、ＹＡＧレ−ザ−等のレ−ザ−光線によるエネルギ−を吸収し、その部分において、炭化による黒色発色、あるいは、発泡による白色発色等を生成し、それにより、例えば、文字、数字、記号、図柄、その他等からなるレ−ザ−印字画像による透かし画像あるいはぼかし画像を極めて鮮明に形成し得るものである。
また、本発明に係る紙製記録材料においては、ＹＡＧレ−ザ−光線等を照射しても、紙製記録材料を構成する紙基材の表面、裏面等は、ＹＡＧレ−ザ−光線による影響を受けることなく、該紙基材を介して、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し、その印字状態を明確に視認し得るものである。
更に、本発明に係る紙製記録材料においては、上記のようにレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得ると共にそのレ−ザ−印字画像による透かし画像あるいはぼかし画像の外側に、紙基材が存在し、これにより、レ−ザ−印字画像による透かし画像あるいはぼかし画像を保護して、その外的影響を排除し、例えば、改変、偽造等を防止するものである。
そのため、本発明において、上記のレ−ザ−印字画像は、例えば、紙幣、株券、商品券、宝くじ、その他等の有価証券類、帳票類、記録紙類、その他等の印字画像の形成に適用することができるものである。
By the way, in the paper recording material according to the present invention, basically, a resin is the main component of the vehicle, and further, it contains a color former that develops color by laser beam irradiation, and the laser beam. A laser beam irradiation coloring resin layer made of a resin composition having a color developing agent content of 0.01% by weight to 50.0% by weight by irradiation, for example, a YAG laser or the like. It absorbs the energy of the laser beam and generates black color by carbonization or white color development by foaming in that part, thereby, for example, a laser consisting of letters, numbers, symbols, designs, etc. -A watermark image or a blurred image by a printed image can be formed very clearly.
Further, in the paper recording material according to the present invention, even when YAG laser beam or the like is irradiated, the front and back surfaces of the paper base material constituting the paper recording material are caused by the YAG laser beam. Without being affected, a watermark image or a blurred image by a very clear laser-printed image can be formed through the paper base material, and the printed state can be clearly recognized.
Further, in the paper recording material according to the present invention, a watermark image or a blurred image can be formed by a laser printed image as described above, and the watermark image or the blurred image by the laser printed image can be formed outside. There is a paper base, which protects the watermark image or blurred image by the laser-printed image, eliminates its external influence, and prevents alteration, forgery, etc., for example.
Therefore, in the present invention, the above laser-printed image is applied to the formation of printed images such as securities such as banknotes, stock certificates, gift certificates, lotteries, etc., forms, recording papers, etc. Is something that can be done.
すなわち、本発明に係る紙製記録材料においては、例えば、ＹＡＧレ−ザ−光線等を照射すると、本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層において、上記のＹＡＧレ−ザ−光線のエネルギ−を吸収し、その部分において、炭化による黒色発色、あるいは、発泡による白色発色等を形成し、それにより、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し、その印字状態を明確に視認し得ることができるものである。
また、本発明に係る紙製記録材料においては、例えば、ＹＡＧレ−ザ−光線等を照射しても、本発明に係る紙製記録材料を構成する紙基材等は、ＹＡＧレ−ザ−光線による影響を受けることなく、更に、本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層においては、上記のＹＡＧレ−ザ−光線のエネルギ−を吸収し、その部分において、炭化による黒色発色、あるいは、発砲による白色発色等を形成し、それにより、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し、その印字状態を明確に視認し得ると共に印字後のレ−ザ−印字画像による透かし画像あるいはぼかし画像が、その外側に位置して存在する紙基材等により保護されて、外的影響を受けることなく、更に、消失、不鮮明等になることもなく、また、磨耗や溶剤等による擦過、その他等により消去、偽造、変造、改変、その他等を行うことは極めて困難なものであるという特性を有し、その安全性、信頼性等は極めて高いものである。
That is, in the paper recording material according to the present invention, for example, when the YAG laser beam or the like is irradiated, the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention Absorbs the energy of the YAG laser beam and forms black coloration due to carbonization or white coloration due to foaming in that portion, thereby enabling a watermark image or blurring due to a very clear laser-printed image. An image can be formed and the printed state can be clearly recognized.
Further, in the paper recording material according to the present invention, for example, even if YAG laser beam or the like is irradiated, the paper base material or the like constituting the paper recording material according to the present invention is the YAG laser. Without being affected by the light beam, the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention absorbs the energy of the YAG laser beam, and the portion In this case, black coloration due to carbonization or white coloration due to firing is formed, thereby forming a watermark image or blurred image by an extremely clear laser print image, and the print state can be clearly recognized. The watermark image or blurred image by the laser-printed image after printing is protected by the paper base material existing outside the image, and further disappeared, unclear, etc. without being affected externally. This In addition, it has characteristics that it is extremely difficult to erase, counterfeit, alter, alter, etc. due to abrasion, abrasion with solvents, etc., and its safety, reliability, etc. are extremely It is expensive.
本発明において、レ−ザ−光線としては、ＹＡＧ〔イットリウム（Ｙ）・アルミニウム（Ａ）・ガ−ネット（Ｇ）〕レ−ザ−光線（波長＝１．０６４μｍ）を用いてレ−ザ−印字を行うことが好ましいものである。
なお、上記において、レ−ザ−光線として、通常、レ−ザ−印字で多く用いられている炭酸ガス〔ＣＯ2 〕レ−ザ−（波長＝１０．６μｍ）を用いる場合には、炭酸ガス〔ＣＯ2 〕レ−ザ−光線を照射して表面を切削、炭化させることによりレ−ザ−印字を行うものであり、照射中に煙を発すること、作業性等に劣ること、あるいは、レ−ザ−印字画像の部分に穴開きが容易に発生すること等の問題点があるので好ましくないものである。
而して、本発明において、上記のＹＡＧレ−ザ−光線は、透明体を透過してしまう性質を有し、その性質を利用し、更に、レ−ザ−光線照射発色樹脂層を紙基材等で挟み込むことにより、煙等の発生を抑え、また、レ−ザ−光線照射発色樹脂層中に存在するレ−ザ−光線照射により発色する発色剤の添加量、レ−ザ−光線照射発色樹脂層の膜厚、その他等を制御して、発色濃度、表面保護層等に与える影響等を調整し、レ−ザ−印字画像による透かし画像あるいはぼかし画像を形成しても穴開き等がない極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を形成し得るものである。
In the present invention, the laser beam is YAG [yttrium (Y) / aluminum (A) / garnet (G)] laser beam (wavelength = 1.064 μm). It is preferable to perform printing.
In the above, when a carbon dioxide [CO 2 ] laser (wavelength = 10.6 μm), which is usually used in laser printing, is used as the laser beam, carbon dioxide is used. [CO 2] Re - the - cutting the surface by irradiating light, Les by carbonization - the - is intended for printing, to emit smoke during irradiation, it is inferior in workability and the like, or, Les -It is not preferable because there are problems such as the occurrence of holes in the printed image portion.
Thus, in the present invention, the above YAG laser beam has a property of transmitting through a transparent body, and the laser beam irradiation color developing resin layer is further formed on a paper base. The amount of coloring agent added in the laser beam irradiation coloring resin layer to suppress the generation of smoke, etc. by being sandwiched between the materials, etc., and the laser beam irradiation The film thickness of the color developing resin layer, etc. are controlled to adjust the color density, the effect on the surface protective layer, etc., and even if a watermark image or blurred image is formed by a laser print image, there will be no perforations. It is possible to form a watermark image or a blurred image by an extremely clear laser-printed image.
また、本発明に係る紙製記録材料においては、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物によるレ−ザ−光線照射発色樹脂層の一方の面、あるいは、両方の面に、樹脂を主成分とする樹脂組成物による樹脂層を積層する場合には、上記のレ−ザ−光線照射発色樹脂層を上記の樹脂層と共に、例えば、Ｔダイ共押出機、あるいは、インフレ−ション共押出機、その他等を使用し、共押出積層して形成することができるという利点を有し、更に、ＹＡＧレ−ザ−光線等を照射しても、樹脂を主成分とする樹脂組成物による樹脂層自身においては、ＹＡＧレ−ザ−光線が透過し、それによる影響を受けることなく、該樹脂層を介して、極めて鮮明なレ−ザ−印字画像による透かし画像あるいはぼかし画像を視認し得ることができ、その印字状態を明確に確認し得るという利点を有するものである。 In the paper recording material according to the present invention, the resin is the main component of the vehicle, and further includes a color former that develops color by laser beam irradiation, and the color that develops color by laser beam irradiation. The resin is the main component on one or both sides of the laser beam irradiation coloring resin layer with the resin composition comprising 0.01% by weight to 50.0% by weight of the agent. When laminating a resin layer made of a resin composition, the laser beam irradiation coloring resin layer is combined with the resin layer, for example, a T-die co-extruder, an inflation co-extruder, or the like. In the resin layer itself of the resin composition containing the resin as a main component, even when irradiated with a YAG laser beam or the like. , YAG laser beam is transmitted, Through the resin layer, it is possible to visually recognize a watermark image or a blurred image by an extremely clear laser-printed image, and to clearly check the print state. Is.
次に、本発明において、本発明に係る紙性記録材料等を構成する材料、製造法等について説明すると、まず、本発明に係る紙性記録材料等を構成する紙基材としては、例えば、紙幣、株券、商品券、宝くじ、その他等の有価証券類、帳票類、記録紙類、その他等を構成する従来公知の紙基材を使用することができる。
具体的には、これが本発明に係る紙製記録材料を構成する基本素材となることから、耐屈曲性、剛性、腰、強度等を有するものを使用することができ、例えば、強サイズ性の晒または未晒の紙基材、あるいは、純白ロ−ル紙、クラフト紙、板紙、加工紙、コ−ト紙、その他等の各種の紙基材を使用することができる。
本発明において、紙基材としては、例えば、坪量２０ｇ／ｍ2 〜３００ｇ／ｍ2 位のもの、好ましくは、坪量約６０〜２５０ｇ／ｍ2 位のものを使用することができる。
なお、本発明において、上記の紙基材には、例えば、文字、図形、絵柄、記号、その他等の所望の印刷絵柄を通常の印刷方式にて任意に形成することができるものである。
また、本発明においては、上記の紙基材の表面に、例えば、上記のレ−ザ−光線照射発色樹脂層、樹脂層等を積層する際に、その密着性等を向上させるために、例えば、コロナ放電処理、プラズマ処理、火炎処理、オゾン処理、その他等の前処理を任意に施すことができるものである。
Next, in the present invention, the material constituting the paper-based recording material according to the present invention, the production method, etc. will be described. First, as the paper base material constituting the paper-based recording material according to the present invention, for example, Conventionally known paper base materials constituting securities such as banknotes, stock certificates, gift certificates, lotteries, etc., forms, recording papers, etc. can be used.
Specifically, since this is a basic material constituting the paper recording material according to the present invention, it is possible to use one having bending resistance, rigidity, waist, strength, etc. Various paper base materials such as bleached or unbleached paper base, or pure white roll paper, kraft paper, paperboard, processed paper, coated paper, and the like can be used.
In the present invention, the paper substrate, for example, those having a basis weight of 20g / m 2 ~300g / m 2 position, preferably, can be used as a basis weight of about 60~250g / m 2 position.
In the present invention, a desired printed picture such as a character, a figure, a picture, a symbol, or the like can be arbitrarily formed on the paper base by a normal printing method.
Further, in the present invention, for example, in order to improve the adhesion when laminating the above laser beam irradiation coloring resin layer, resin layer, etc. on the surface of the above paper base, for example, Pretreatment such as corona discharge treatment, plasma treatment, flame treatment, ozone treatment, etc. can be optionally performed.
次に、本発明において、本発明に係る紙製記録材料等を構成するレ−ザ−光線照射発色樹脂層を形成する樹脂としては、例えば、熱によって溶融し、押出機等の押出ダイ等から押出可能であり、更に、相互に熱融着し得る熱可塑性樹脂の１種ないし２種以上の混合物を使用することができ、具体的には、例えば、低密度ポリエチレン（ＬＤＰＥ）、直鎖状（線状）低密度ポリエチレン（マルチサイト触媒を使用して重合したポリマ−、ＬＬＤＰＥ）、メタロセン触媒（シングルサイト触媒）使用して重合したエチレン−α・オレフィン共重合体、中密度ポリエチレン（ＭＤＰＥ）、高密度ポリエチレン（ＨＤＰＥ）、ポリプロピレン樹脂、エチレン−酢酸ビニル共重合体、アイオノマ−樹脂、エチレン−アクリル酸共重合体、エチレン−アクリル酸エチル共重合体、エチレン−メタクリル酸共重合体、エチレン−メタクリル酸メチル共重合体、エチレン−プロピレン共重合体、メチルペンテンポリマ−、ポリブテンポリマ−、ポリエチレンまたはポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、フマ−ル酸、イタコン酸等の不飽和カルボン酸で変性した酸変性ポリオレフィン樹脂、ポリ酢酸ビニル系樹脂、ポリ（メタ）アクリル系樹脂、ポリ塩化ビニル系樹脂、ポリスチレン系樹脂、ポリカ−ボネ−ト系樹脂、熱可塑性ポリエステル系樹脂、熱可塑性ポリアミド系樹脂、その他等の熱可塑性樹脂の１種ないし２種以上を使用することができる。 Next, in the present invention, the resin forming the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention is, for example, melted by heat and from an extrusion die such as an extruder. A mixture of one or more thermoplastic resins that can be extruded and can be heat-sealed with each other can be used. Specifically, for example, low density polyethylene (LDPE), linear (Linear) Low density polyethylene (Polymer polymerized using multisite catalyst, LLDPE), Ethylene-α / olefin copolymer polymerized using metallocene catalyst (single site catalyst), Medium density polyethylene (MDPE) , High density polyethylene (HDPE), polypropylene resin, ethylene-vinyl acetate copolymer, ionomer resin, ethylene-acrylic acid copolymer, ethylene-acrylic acid Acrylic polyolefin resin such as ethyl acrylate copolymer, ethylene-methacrylic acid copolymer, ethylene-methyl methacrylate copolymer, ethylene-propylene copolymer, methylpentene polymer, polybutene polymer, polyethylene or polypropylene. Acid-modified polyolefin resin modified with unsaturated carboxylic acid such as acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, itaconic acid, polyvinyl acetate resin, poly (meth) acrylic resin, polyvinyl chloride One type or two or more types of thermoplastic resins such as a series resin, a polystyrene series resin, a polycarbonate series resin, a thermoplastic polyester series resin, a thermoplastic polyamide series resin, and the like can be used.
次に、本発明において、本発明に係る紙製記録材料等を構成するレ−ザ−光線照射発色樹脂層を形成するレ−ザ−光線照射により発色する発色剤としては、従来公知のもの、例えば、染料・顔料等の着色剤、粘土類、その他等を使用することができ、具体的には、黄色酸化鉄、無機鉛化合物、マンガンバイオレット、コバルトバイオレット、水銀、コバルト、銅、ビスマス、ニッケル等の金属化合物、真珠光沢顔料、珪素化合物、雲母類、カオリン類、珪砂、硅藻土、タルク、酸化チタン被覆雲母類、二酸化錫被覆雲母類、アンチモン被覆雲母類、スズ＋アンチモン被覆雲母類、スズ＋アンチモン＋酸化チタン被覆雲母類、その他等の１種ないし２種以上を使用することができる。
その使用量としては、上記の熱可塑性樹脂に対し、０．０１重量％〜５０．０重量％位、好ましくは、１．０重量％〜１０重量％位添加して使用することが望ましいものである。
Next, in the present invention, as the color former that forms a laser beam irradiation color forming resin layer constituting the paper recording material or the like according to the present invention, the color former that develops color by laser beam irradiation is a conventionally known one. For example, coloring agents such as dyes and pigments, clays, etc. can be used. Specifically, yellow iron oxide, inorganic lead compounds, manganese violet, cobalt violet, mercury, cobalt, copper, bismuth, nickel Metal compounds such as pearlescent pigments, silicon compounds, mica, kaolins, silica sand, diatomaceous earth, talc, titanium oxide-coated mica, tin dioxide-coated mica, antimony-coated mica, tin + antimony-coated mica, One or more of tin + antimony + titanium oxide-coated mica, etc. can be used.
As for the amount used, it is desirable to add about 0.01 wt% to 50.0 wt%, preferably about 1.0 wt% to 10 wt% with respect to the thermoplastic resin. is there.
次に、本発明において、本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層を形成する、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物について説明すると、本発明においては、例えば、上記の熱可塑性樹脂の１種ないし２種以上をビヒクルの主成分とし、これに、上記のレ−ザ−光線照射により発色する発色剤の１種ないし２種以上を、その含有量が０．０１重量％〜５０．０重量％の範囲内で添加し、更に、必要ならば、その製膜化に際して、例えば、フィルムの加工性、耐熱性、耐候性、機械的性質、寸法安定性、抗酸化性、滑り性、離形性、難燃性、抗カビ性、電気的特性、強度、その他等を改良、改質する目的で、種々のプラスチック配合剤や添加剤等の１種ないし２種以上を任意に添加し、更に、要すれば、溶剤、希釈剤等を添加し、十分に混練して、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含む樹脂組成物を調整することができる。 Next, in the present invention, the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention is formed. The resin is the main component of the vehicle, and further, color is developed by laser beam irradiation. The resin composition containing a color former and having a color former content of 0.01 to 50.0% by weight when irradiated with a laser beam will be described. One or more of the above-mentioned thermoplastic resins are used as the main component of the vehicle, and the content of one or more of the color formers that develop color by laser beam irradiation is 0. .01 wt% to 50.0 wt%, and if necessary, for example, when forming the film, for example, film processability, heat resistance, weather resistance, mechanical properties, dimensional stability, Antioxidant, slippery, mold release, flame retardant, antifungal For the purpose of improving and modifying electrical characteristics, strength, etc., one or more of various plastic compounding agents and additives are arbitrarily added, and if necessary, solvents, diluents, etc. And kneaded sufficiently to prepare a resin composition comprising a resin as a main component of the vehicle and a color former that develops color by laser light irradiation.
なお、本発明において、上記の本発明に係る紙製記録材料を構成する樹脂組成物において、上記のプラスチック配合剤や添加剤等としては、例えば、滑剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、充填剤、補強剤、帯電防止剤、難燃剤、耐炎剤、発泡剤、防カビ剤、顔料、染料、分散剤、界面活性剤、ブロッキング防止剤、その他等を使用することができ、更には、改質用樹脂等も使用することがてき、更に、その添加量としては、極く微量から数十重量％まで、その目的に応じて、任意に添加することができる。 In the present invention, in the resin composition constituting the paper recording material according to the present invention, examples of the plastic compounding agent and additive include a lubricant, a crosslinking agent, an antioxidant, and an ultraviolet absorber. , Light stabilizers, fillers, reinforcing agents, antistatic agents, flame retardants, flame retardants, foaming agents, antifungal agents, pigments, dyes, dispersants, surfactants, antiblocking agents, etc. Further, a modifying resin or the like can be used, and the addition amount can be arbitrarily added from a very small amount to several tens of weight% depending on the purpose.
更に、上記において、配合剤や添加剤等としては、具体的には、それ自身が滑性を有し、かつ、樹脂中における移行が少ない滑剤を使用することができ、例えば、流動パラフィン、白色ワセリン、石油系ワックス、マイクロクリスタリンワックス、モンタンワックス、ポリエチレンワックス等のワックス類、炭素数が８〜２２の高級脂肪酸、または、高級脂肪酸アルミニウム、高級脂肪酸カルシウム、高級脂肪酸マグネシウム高級脂肪酸亜鉛、高級脂肪酸リチウム等の高級脂肪酸またはその金属塩、炭素数が８〜１８の直鎖脂肪族１価アルコ−ル、グリセリン、ソルビト−ル、プロピレングリコ−ル、ペンタエリスリト−ル、トリエチレングリコ−ル等の脂肪族アルコ−ル類、炭素数が４〜２２の高級脂肪酸と炭素数が８〜１８の直鎖脂肪族１価アルコ−ルとのエステル類、アセチルクエン酸ドリブチル、アジピン酸ジ−２エチル−ヘキシル、アゼライン酸−ｎ−ヘキシル、エタンジオ−ルモンタン酸エステル、ポリ（１．３−ブタンジオ−ルアジピン酸）エステル、アセチルリシノ−ル酸メチル、ポリ（１．３−ブチレングリコ−ル、１．４−ブチレングリコ−ル、アジピン酸オクチルアルコ−ル）エステル、糖ろう等のアルコ−ルと脂肪酸とのエステル類、水添食用油脂、ひまし油、スパ−ムアセチワックス、アセチル化モノグリセライド糖のグリセライド類、炭素数が１６〜１８の例えばエチレンビスオレイルアミドに代表されるエチレンビス脂肪酸アミド、炭素数が８〜２２の高級脂肪酸アミド、ステアリルエルカアミド、エルカ酸アミド、オレイルパルミトアミド等の高級脂肪酸アミド類、その他、メチルヒドロジエンポリシロキサン、ジメチルポリシロキサン、メチルフェニルポリシロキサン、ポリオキシアルキレン・ジメチルポリシロキサン等のシリコ−ン油ヤロジンやマレイン酸変性ロジンのグリセリンエステル等の１種ないし２種以上を使用することができる。
なお、本発明においては、上記のような滑剤の中でも、特に、エルカ酸アミドやエチレンビスオレイルアミド、ステアリン酸アミド、オレイン酸アミド、メチレンビスステアリン酸アミド等は、それ自身が滑性をもち、極めて有効な材料である。
上記の滑剤の添加量としては、熱可塑性樹脂１００重量部に対し０．０８重量％〜１０．０重量％位の割合で添加することが好ましいものである。
Furthermore, in the above, as the compounding agent or additive, specifically, a lubricant having its own lubricity and little migration in the resin can be used. For example, liquid paraffin, white Vaseline, petroleum wax, microcrystalline wax, montan wax, polyethylene wax and the like, higher fatty acids having 8 to 22 carbon atoms, or higher fatty acid aluminum, higher fatty acid calcium, higher fatty acid magnesium higher fatty acid zinc, higher fatty acid lithium Higher fatty acids or metal salts thereof, linear aliphatic monohydric alcohols having 8 to 18 carbon atoms, glycerin, sorbitol, propylene glycol, pentaerythritol, triethylene glycol, etc. Aliphatic alcohols, higher fatty acids having 4 to 22 carbon atoms and straight chain aliphatics having 8 to 18 carbon atoms Esters with polyhydric alcohols, butyl acetyl citrate, di-2-ethyl-hexyl adipate, azelaic acid-n-hexyl, ethanediol montanate, poly (1.3-butanediol adipate) ester, acetylricino -Esters of alcohol and fatty acid such as methyl oxalate, poly (1.3-butylene glycol, 1.4-butylene glycol, adipic acid octyl alcohol) ester, sugar wax, etc., hydrogenation Edible fats and oils, castor oil, spam acetyl wax, glycerides of acetylated monoglyceride sugar, ethylene bis-fatty acid amide represented by, for example, ethylene bisoleyl amide having 16 to 18 carbon atoms, higher fatty acid amide having 8 to 22 carbon atoms , Stearyl erucamide, erucic acid amide, oleyl palmitoamide, etc. 1 to 2 types of fatty acid amides, and other types such as methylhydrodiene polysiloxane, dimethyl polysiloxane, methylphenyl polysiloxane, silicone oil jarodine such as polyoxyalkylene dimethylpolysiloxane, and glycerin ester of maleic acid modified rosin The above can be used.
In the present invention, among the lubricants as described above, erucic acid amide, ethylene bis oleyl amide, stearic acid amide, oleic acid amide, methylene bis stearic acid amide, etc., are themselves slippery, It is a very effective material.
As the addition amount of the above-mentioned lubricant, it is preferable to add at a ratio of about 0.08 wt% to 10.0 wt% with respect to 100 parts by weight of the thermoplastic resin.
また、本発明においては、その他、例えば、酸化アルミニウム、酸化マグネシウム、シリカ、酸化カルシウム、酸化チタン、酸化亜鉛等の酸化物、水酸化アルミニウム、水酸化マグネシウム、水酸化カルシウム等の水酸化物、炭酸マグネシウム、炭酸カルシウム等の炭酸塩、硫酸カルシウム、硫酸バリウム等の硫酸塩、ケイ酸マグネシウム、ケイ酸アルミニウム、ケイ酸カルシウム、アルミノケイ酸等のケイ酸塩、その他、カオリン、タルク、けいそう土等の無機化合物系のブロッキング防止剤、あるいは、高密度ポリエチレン、分子量３０００００以上の超高分子ポリエチレン、ポリプロピレン、ポリカ−ボネ−ト、ポリアミド、ポリエステル、メラミン樹脂、ジアリルフタレ−ト樹脂、アクリル系樹脂、その他等の微粉末等からなる有機化合物系のブロッキング防止剤の１種ないし２種以上を添加することができる。
その添加量としては、樹脂１００重量部に対し０．０１〜３重量％位が好ましい。
In the present invention, other oxides such as aluminum oxide, magnesium oxide, silica, calcium oxide, titanium oxide, and zinc oxide; hydroxides such as aluminum hydroxide, magnesium hydroxide, and calcium hydroxide; Carbonates such as magnesium and calcium carbonate, sulfates such as calcium sulfate and barium sulfate, silicates such as magnesium silicate, aluminum silicate, calcium silicate and aluminosilicate, and others such as kaolin, talc and diatomaceous earth Anti-blocking agent based on inorganic compounds, or high density polyethylene, ultra-high molecular weight polyethylene having a molecular weight of 300000 or more, polypropylene, polycarbonate, polyamide, polyester, melamine resin, diallyl phthalate resin, acrylic resin, etc. Organic consisting of fine powder It one free of compounds based antiblocking agents can be added two or more.
The addition amount is preferably about 0.01 to 3% by weight with respect to 100 parts by weight of the resin.
次に、本発明において、上記のような樹脂組成物を使用して、本発明に係るレ−ザ−光線照射発色樹脂層を形成する方法について説明すると、まず、本発明においては、上記で、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物を調製後、該樹脂組成物を使用し、これらを、例えば、Ｔダイ押出機、インフレ−ション成形機等を使用して、上記の樹脂組成物によるレ−ザ−光線照射発色樹脂フィルムを製造し、これを、前述の本発明に係る紙製記録材料を構成する紙基材を使用し、紙基材とレ−ザ−光線照射発色樹脂フィルムと紙基材との３者を順次に積層して、本発明に係るレ−ザ−光線照射発色樹脂層を形成することができる。 Next, in the present invention, a method for forming a laser beam irradiation color developing resin layer according to the present invention using the resin composition as described above will be described. First, in the present invention, The resin is a main component of the vehicle, and further contains a color former that develops color when irradiated with a laser beam, and the content of the color former that develops color when irradiated with a laser beam is 0.01 to 50% by weight. After preparing a resin composition consisting of 0.0% by weight, the resin composition is used, and these are used, for example, by using a T-die extruder, an inflation molding machine, etc. A laser beam irradiation color developing resin film is produced, and the paper base material constituting the paper recording material according to the present invention is used. The three according to the present invention are laminated in order, and the laser according to the present invention It is possible to form a line illumination color resin layer.
あるいは、本発明においては、上記の樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物を調製後、該樹脂組成物を使用し、これを、前述の本発明に係る紙製記録材料を構成する紙基材の２枚の層間に、例えば、Ｔダイ押出機、その他等の押出機等を使用して、押出積層して、本発明に係るレ−ザ−光線照射発色樹脂層を形成することもできる。 Alternatively, in the present invention, the content of the color former that contains the above resin as a main component of the vehicle, further includes a color former that develops color by laser beam irradiation, and that develops color by the laser beam irradiation. However, after preparing a resin composition comprising 0.01 wt% to 50.0 wt%, the resin composition was used, and this was used for the paper substrate constituting the paper recording material according to the present invention described above. The laser beam irradiation coloring resin layer according to the present invention may be formed by extrusion lamination between two layers using, for example, an extruder such as a T-die extruder or the like.
または、本発明においては、上記の樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物、および、樹脂を主成分とする樹脂組成物を調製後、その２種の樹脂組成物を使用し、これを、前述の本発明に係る紙製記録材料を構成する紙基材の２枚の層間に、例えば、Ｔダイ共押出機、その他等の共押出機等を使用して、共押出積層して、本発明に係るレ−ザ−光線照射発色樹脂層を形成することもできる。 Alternatively, in the present invention, the content of the color former that contains the above resin as a main component of the vehicle, further includes a color former that develops color by laser beam irradiation, and that develops color by the laser beam irradiation. However, after preparing a resin composition consisting of 0.01 wt% to 50.0 wt% and a resin composition containing a resin as a main component, the two types of resin compositions were used, and these were used as described above. The two layers of the paper substrate constituting the paper recording material according to the present invention are co-extruded and laminated using, for example, a T-die co-extruder or other co-extruder, etc. Such a laser beam irradiation colored resin layer can also be formed.
更に、本発明においては、上記と同様に、まず、上記の樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物を調製後、該樹脂組成物を使用し、これらを、前述の本発明に係る紙製記録材料を構成する一方の紙基材の一方の面に、例えば、ロ−ルコ−ト法、グラビアロ−ルコ−ト法、スプレイコ−ト法、キスコ−ト法、押出コ−ト、その他等の通常のコ−ト法ないし印刷法等により塗布ないし印刷して、上記の樹脂組成物によるコ−ト膜ないし印刷膜を形成し、しかる後、そのコ−ト膜ないし印刷膜の面に、他方の紙基材材を積層して、本発明に係るレ−ザ−光線照射発色樹脂層を形成することができる。
上記の例示は、本発明に係るレ−ザ−光線照射発色樹脂層を形成する方法についてその一二例を例示したものであり、本発明は、これに限定されるものではないものである。
Further, in the present invention, in the same manner as described above, first, the above resin is the main component of the vehicle, and further contains a color former that develops color by laser beam irradiation, and by laser beam irradiation. After preparing a resin composition having a color former content of 0.01% to 50.0% by weight, the resin composition is used, and these are used as the paper recording material according to the present invention. On one side of one of the paper bases constituting, for example, a roll coat method, a gravure roll coat method, a spray coat method, a kiss coat method, an extrusion coat, etc. Coating or printing is performed by a coating method or a printing method to form a coating film or a printing film of the above resin composition, and then the other paper is placed on the surface of the coating film or the printing film. A base material is laminated to form a laser beam irradiation coloring resin layer according to the present invention. Door can be.
The above examples illustrate one or two examples of the method of forming the laser beam irradiation color resin layer according to the present invention, and the present invention is not limited thereto.
なお、本発明において、本発明に係るレ−ザ−光線照射発色樹脂層の膜厚としては、膜厚１μｍ〜５０μｍ位、好ましくは、５μｍ〜３０μｍ位が望ましいものである。
上記において、本発明に係るレ−ザ−光線照射発色樹脂層の膜厚として、膜厚１μｍ、更には、５μｍ未満であると、レ−ザ−光線照射により発色する発色剤による発色、印字が不十分、不鮮明となること等の理由から好ましくなく、また、膜厚５０μｍ、更には、３０μｍを越えると、レ−ザ−光線照射により発色する発色剤による発色、印字は、十分となるが、コストアップ、レ−ザ−光線照射発色樹脂層の物性（強度）低下、レ−ザ−光線照射により発色する発色剤自体の顔料色が着色すること等の理由から好ましくないものである。
In the present invention, the film thickness of the laser beam irradiation coloring resin layer according to the present invention is desirably about 1 μm to 50 μm, preferably about 5 μm to 30 μm.
In the above, when the thickness of the laser beam irradiation coloring resin layer according to the present invention is 1 μm or less, and less than 5 μm, color development or printing by a color former that develops color by laser beam irradiation is possible. Insufficient and unpreferable for reasons such as unclearness, and when the film thickness exceeds 50 μm, and more than 30 μm, coloring and printing with a color former that develops color by laser beam irradiation are sufficient, This is not preferable for reasons such as an increase in cost, a decrease in physical properties (strength) of the laser beam irradiation coloring resin layer, and a coloring of the color former itself that develops color by laser beam irradiation.
次に、本発明において、本発明に係る紙製記録材料を構成する樹脂層について説明すると、かかる樹脂層を形成する樹脂としては、前述の本発明に係る紙製記録材料等を構成するレ−ザ−光線照射発色樹脂層を形成する樹脂を同様に使用することができる。
具体的には、熱によって溶融し、押出機等の押出ダイ等から押出可能であり、更に、相互に熱融着し得る熱可塑性樹脂の１種ないし２種以上の混合物を使用することができ、例えば、低密度ポリエチレン（ＬＤＰＥ）、直鎖状（線状）低密度ポリエチレン（マルチサイト触媒を使用して重合したポリマ−、ＬＬＤＰＥ）、メタロセン触媒（シングルサイト触媒）使用して重合したエチレン−α・オレフィン共重合体、中密度ポリエチレン（ＭＤＰＥ）、高密度ポリエチレン（ＨＤＰＥ）、ポリプロピレン樹脂、エチレン−酢酸ビニル共重合体、アイオノマ−樹脂、エチレン−アクリル酸共重合体、エチレン−アクリル酸エチル共重合体、エチレン−メタクリル酸共重合体、エチレン−メタクリル酸メチル共重合体、エチレン−プロピレン共重合体、メチルペンテンポリマ−、ポリブテンポリマ−、ポリエチレンまたはポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、フマ−ル酸、イタコン酸等の不飽和カルボン酸で変性した酸変性ポリオレフィン樹脂、ポリ酢酸ビニル系樹脂、ポリ（メタ）アクリル系樹脂、ポリ塩化ビニル系樹脂、ポリスチレン系樹脂、ポリカ−ボネ−ト系樹脂、熱可塑性ポリエステル系樹脂、熱可塑性ポリアミド系樹脂、その他等の熱可塑性樹脂の１種ないし２種以上を使用することができる。
Next, in the present invention, the resin layer constituting the paper recording material according to the present invention will be described. As the resin forming the resin layer, the above-described paper recording material according to the present invention is used. The resin that forms the resin-irradiated coloring resin layer can be used in the same manner.
Specifically, it is possible to use a mixture of one or more thermoplastic resins that can be melted by heat and extruded from an extrusion die such as an extruder, and can be heat-sealed to each other. For example, low density polyethylene (LDPE), linear (linear) low density polyethylene (polymer polymerized using multisite catalyst, LLDPE), ethylene polymerized using metallocene catalyst (single site catalyst) α-olefin copolymer, medium density polyethylene (MDPE), high density polyethylene (HDPE), polypropylene resin, ethylene-vinyl acetate copolymer, ionomer resin, ethylene-acrylic acid copolymer, ethylene-ethyl acrylate copolymer Polymer, ethylene-methacrylic acid copolymer, ethylene-methyl methacrylate copolymer, ethylene-propylene copolymer Acid modified with an unsaturated carboxylic acid such as acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, itaconic acid or the like, or a polyolefin resin such as methylpentene polymer, polybutene polymer, polyethylene or polypropylene. Modified polyolefin resin, polyvinyl acetate resin, poly (meth) acrylic resin, polyvinyl chloride resin, polystyrene resin, polycarbonate resin, thermoplastic polyester resin, thermoplastic polyamide resin, etc. One or more of these thermoplastic resins can be used.
次に、本発明において、本発明に係る紙製記録材料等を構成する樹脂層を形成する樹脂を主成分とする樹脂組成物について説明すると、本発明においては、例えば、上記の熱可塑性樹脂の１種ないし２種以上をビヒクルの主成分とし、これに、更に、必要ならば、その製膜化に際して、例えば、フィルムの加工性、耐熱性、耐候性、機械的性質、寸法安定性、抗酸化性、滑り性、離形性、難燃性、抗カビ性、電気的特性、強度、その他等を改良、改質する目的で、種々のプラスチック配合剤や添加剤等の１種ないし２種以上を任意に添加し、更に、要すれば、溶剤、希釈剤等を添加し、十分に混練して、樹脂をビヒクルの主成分とする樹脂組成物を調整することができる。 Next, in the present invention, a resin composition mainly composed of a resin that forms the resin layer constituting the paper recording material according to the present invention will be described. In the present invention, for example, the above-described thermoplastic resin One or two or more types are the main components of the vehicle, and if necessary, for example, when forming the film, for example, film processability, heat resistance, weather resistance, mechanical properties, dimensional stability, resistance, One or two kinds of various plastic compounding agents and additives for the purpose of improving and modifying oxidation, slipperiness, releasability, flame retardancy, antifungal property, electrical properties, strength, etc. The above can be arbitrarily added, and further, if necessary, a solvent, a diluent and the like can be added and sufficiently kneaded to prepare a resin composition containing the resin as the main component of the vehicle.
なお、本発明において、上記のような樹脂組成物において、前述と同様に、上記のプラスチック配合剤や添加剤等としては、例えば、滑剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、充填剤、補強剤、帯電防止剤、難燃剤、耐炎剤、発泡剤、防カビ剤、顔料、染料、分散剤、界面活性剤、ブロッキング防止剤、その他等を使用することができ、更には、改質用樹脂等も使用することがてき、更に、その添加量としては、極く微量から数十重量％まで、その目的に応じて、任意に添加することができる。 In the present invention, in the resin composition as described above, as described above, examples of the plastic compounding agent and additive include a lubricant, a crosslinking agent, an antioxidant, an ultraviolet absorber, and a light stabilizer. , Fillers, reinforcing agents, antistatic agents, flame retardants, flame retardants, foaming agents, antifungal agents, pigments, dyes, dispersants, surfactants, antiblocking agents, etc., and more Further, a modifying resin or the like can be used, and the addition amount can be arbitrarily added from a very small amount to several tens of weight% depending on the purpose.
更に、上記において、配合剤や添加剤等としては、前述と同様に、具体的には、それ自身が滑性を有し、かつ、樹脂中における移行が少ない滑剤を使用することができ、例えば、流動パラフィン、白色ワセリン、石油系ワックス、マイクロクリスタリンワックス、モンタンワックス、ポリエチレンワックス等のワックス類、炭素数が８〜２２の高級脂肪酸、または、高級脂肪酸アルミニウム、高級脂肪酸カルシウム、高級脂肪酸マグネシウム高級脂肪酸亜鉛、高級脂肪酸リチウム等の高級脂肪酸またはその金属塩、炭素数が８〜１８の直鎖脂肪族１価アルコ−ル、グリセリン、ソルビト−ル、プロピレングリコ−ル、ペンタエリスリト−ル、トリエチレングリコ−ル等の脂肪族アルコ−ル類、炭素数が４〜２２の高級脂肪酸と炭素数が８〜１８の直鎖脂肪族１価アルコ−ルとのエステル類、アセチルクエン酸ドリブチル、アジピン酸ジ−２エチル−ヘキシル、アゼライン酸−ｎ−ヘキシル、エタンジオ−ルモンタン酸エステル、ポリ（１．３−ブタンジオ−ルアジピン酸）エステル、アセチルリシノ−ル酸メチル、ポリ（１．３−ブチレングリコ−ル、１．４−ブチレングリコ−ル、アジピン酸オクチルアルコ−ル）エステル、糖ろう等のアルコ−ルと脂肪酸とのエステル類、水添食用油脂、ひまし油、スパ−ムアセチワックス、アセチル化モノグリセライド糖のグリセライド類、炭素数が１６〜１８の例えばエチレンビスオレイルアミドに代表されるエチレンビス脂肪酸アミド、炭素数が８〜２２の高級脂肪酸アミド、ステアリルエルカアミド、エルカ酸アミド、オレイルパルミトアミド等の高級脂肪酸アミド類、その他、メチルヒドロジエンポリシロキサン、ジメチルポリシロキサン、メチルフェニルポリシロキサン、ポリオキシアルキレン・ジメチルポリシロキサン等のシリコ−ン油ヤロジンやマレイン酸変性ロジンのグリセリンエステル等の１種ないし２種以上を使用することができる。
なお、本発明においては、上記のような滑剤の中でも、特に、エルカ酸アミドやエチレンビスオレイルアミド、ステアリン酸アミド、オレイン酸アミド、メチレンビスステアリン酸アミド等は、それ自身が滑性をもち、極めて有効な材料である。
上記の滑剤の添加量としては、熱可塑性樹脂１００重量部に対し０．０８重量％〜１０．０重量％位の割合で添加することが好ましいものである。
Furthermore, in the above, as a compounding agent and an additive, as described above, specifically, a lubricant having its own lubricity and less migration in the resin can be used, for example, , Liquid paraffin, white petrolatum, petroleum wax, microcrystalline wax, montan wax, polyethylene wax and the like, higher fatty acids having 8 to 22 carbon atoms, or higher fatty acid aluminum, higher fatty acid calcium, higher fatty acid magnesium higher fatty acid Zinc, higher fatty acids such as higher fatty acid lithium or metal salts thereof, linear aliphatic monohydric alcohol having 8 to 18 carbon atoms, glycerin, sorbitol, propylene glycol, pentaerythritol, triethylene Aliphatic alcohols such as glycol, higher fatty acids having 4 to 22 carbon atoms, and 8 to 1 carbon atoms Esters of linear aliphatic monohydric alcohols, butyl acetyl citrate, di-2-ethyl-hexyl adipate, azelaic acid-n-hexyl, ethanediol montanate, poly (1.3-butanedio- Alcohol, fatty acid, poly (1.3-butylene glycol, 1.4-butylene glycol, octyl alcohol adipate) ester, sugar wax, etc. Esters, hydrogenated edible fats and oils, castor oil, spam acetyl wax, glycerides of acetylated monoglyceride sugars, ethylene bis-fatty acid amides having 16 to 18 carbon atoms, for example, ethylene bis-oleylamide, 8 carbon atoms -22 higher fatty acid amide, stearyl erucamide, erucic acid amide,
In the present invention, among the lubricants as described above, erucic acid amide, ethylene bis oleyl amide, stearic acid amide, oleic acid amide, methylene bis stearic acid amide, etc., are themselves slippery, It is a very effective material.
As the addition amount of the above-mentioned lubricant, it is preferable to add at a ratio of about 0.08 wt% to 10.0 wt% with respect to 100 parts by weight of the thermoplastic resin.
また、本発明においては、前述と同様に、その他、例えば、酸化アルミニウム、酸化マグネシウム、シリカ、酸化カルシウム、酸化チタン、酸化亜鉛等の酸化物、水酸化アルミニウム、水酸化マグネシウム、水酸化カルシウム等の水酸化物、炭酸マグネシウム、炭酸カルシウム等の炭酸塩、硫酸カルシウム、硫酸バリウム等の硫酸塩、ケイ酸マグネシウム、ケイ酸アルミニウム、ケイ酸カルシウム、アルミノケイ酸等のケイ酸塩、その他、カオリン、タルク、けいそう土等の無機化合物系のブロッキング防止剤、あるいは、高密度ポリエチレン、分子量３０００００以上の超高分子ポリエチレン、ポリプロピレン、ポリカ−ボネ−ト、ポリアミド、ポリエステル、メラミン樹脂、ジアリルフタレ−ト樹脂、アクリル系樹脂、その他等の微粉末等からなる有機化合物系のブロッキング防止剤の１種ないし２種以上を添加することができる。
その添加量としては、樹脂１００重量部に対し０．０１〜３重量％位が好ましい。
In the present invention, as described above, other oxides such as aluminum oxide, magnesium oxide, silica, calcium oxide, titanium oxide, and zinc oxide, aluminum hydroxide, magnesium hydroxide, calcium hydroxide, etc. Hydroxides, carbonates such as magnesium carbonate and calcium carbonate, sulfates such as calcium sulfate and barium sulfate, silicates such as magnesium silicate, aluminum silicate, calcium silicate and aluminosilicate, other kaolin, talc, Anti-blocking agent of inorganic compounds such as diatomaceous earth, or high density polyethylene, ultra high molecular weight polyethylene with molecular weight of 300,000 or more, polypropylene, polycarbonate, polyamide, polyester, melamine resin, diallyl phthalate resin, acrylic Resin, other fine powder One free of organic compound-based antiblocking agent consists of, it can be added two or more.
The addition amount is preferably about 0.01 to 3% by weight with respect to 100 parts by weight of the resin.
次に、本発明において、上記のような樹脂組成物を使用して、本発明に係る樹脂を形成する方法について説明すると、まず、本発明においては、上記で、樹脂をビヒクルの主成分とする樹脂組成物を調製後、該樹脂組成物を使用し、これらを、例えば、Ｔダイ押出機、インフレ−ション成形機等を使用して、上記の樹脂組成物による樹脂フィルムを製造し、これを、前述の本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層の一方の面、あるいは、その両方の面に積層して、本発明に係る樹脂層を形成することができる。 Next, in the present invention, a method for forming a resin according to the present invention using the resin composition as described above will be described. First, in the present invention, the resin is the main component of the vehicle. After preparing the resin composition, the resin composition is used. Using these resin compositions, for example, using a T-die extruder, an inflation molding machine, etc., a resin film made of the above resin composition is produced. The resin layer according to the present invention may be formed by laminating the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention on one surface or both surfaces thereof. it can.
あるいは、本発明においては、上記と同様に、まず、上記で、樹脂をビヒクルの主成分とする樹脂組成物を調製後、該樹脂組成物を使用し、これらを、前述の本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層の一方の面、あるいは、その両方の面に、例えば、ロ−ルコ−ト法、グラビアロ−ルコ−ト法、スプレイコ−ト法、キスコ−ト法、押出コ−ト、その他等の通常のコ−ト法ないし印刷法等により塗布ないし印刷して、上記の樹脂組成物によるコ−ト膜ないし印刷膜を形成して、本発明に係る樹脂層を形成することができる。 Alternatively, in the present invention, similarly to the above, first, after preparing a resin composition containing a resin as a main component of the vehicle as described above, the resin composition is used, and these are used as the paper according to the present invention. For example, a roll coating method, a gravure roll coating method, a spray coating method, a kiss coating may be applied to one surface or both surfaces of the laser beam irradiation coloring resin layer constituting the recording material. -Coating or printing by a normal coating method such as coating method, extrusion coating, etc. or printing method, etc. to form a coating film or printing film by the above resin composition, Such a resin layer can be formed.
更に、本発明において、上記のような樹脂組成物を使用して、本発明に係る樹脂層を形成する方法について説明すると、まず、本発明においては、上記の、樹脂をビヒクルの主成分とする樹脂組成物と、前述の本発明に係る紙製記録材料を構成するレ−ザ−光線照射発色樹脂層を形成する、樹脂をビヒクルの主成分とし、更に、レ−ザ−光線照射により発色する発色剤を含み、かつ、そのレ−ザ−光線照射により発色する発色剤の含有量が、０．０１重量％〜５０．０重量％からなる樹脂組成物とを使用し、これらの２種の樹脂組成物を、前述の本発明に係る紙製記録材料を構成す２枚の紙基材の層間に、例えば、Ｔダイ共押出機、その他等の共押出成形機等を使用して共押出積層して、本発明に係るレ−ザ−光線照射発色樹脂層と樹脂層との２〜３層共押出樹脂層を同時に形成することができる。 上記の例示は、本発明に係る表面保護層を形成する方法についてその一二例を例示したものであり、本発明は、これに限定されるものではないものである。 Furthermore, in the present invention, a method for forming the resin layer according to the present invention using the resin composition as described above will be described. First, in the present invention, the resin is the main component of the vehicle. The resin composition and the laser beam irradiation coloring resin layer constituting the paper recording material according to the present invention described above are formed. The resin is a main component of the vehicle, and further, the color is developed by laser beam irradiation. A resin composition containing a color former and having a color former content of 0.01% to 50.0% by weight when irradiated with a laser beam. The resin composition is coextruded between the two paper bases constituting the paper recording material according to the present invention using, for example, a T-die coextrusion machine, a coextrusion molding machine, etc. The laser beam irradiation coloring resin layer and the resin layer according to the present invention are laminated. It can be simultaneously formed two or three layer co-extruded resin layer. The above exemplification illustrates one or two examples of the method for forming the surface protective layer according to the present invention, and the present invention is not limited thereto.
本発明において、本発明に係る樹脂層としては、前述のレ−ザ−印字画像による透かし画像あるいはぼかし画像等を透視ないし保護することから、透明ないしは透明の樹脂膜からなることが好ましいものである。
なお、本発明において、本発明に係る樹脂層の膜厚としては、膜厚５μｍ〜６０μｍ位、好ましくは、１０μｍ〜４０μｍ位が望ましいものである。
上記において、本発明に係る樹脂層の膜厚として、膜厚５μｍ、更には、１０μｍ未満であると、保護機能が喪失することから好ましくなく、また、膜厚６０μｍ、更には、４０μｍを越えると、本発明に係る紙製記録材料の全体の総厚が増し、コストアップ等の要因となることから好ましくないものである。
In the present invention, the resin layer according to the present invention is preferably made of a transparent or transparent resin film in order to see through or protect the watermark image or blurred image by the laser-printed image described above. .
In the present invention, the film thickness of the resin layer according to the present invention is desirably about 5 μm to 60 μm, preferably about 10 μm to 40 μm.
In the above, if the film thickness of the resin layer according to the present invention is 5 μm, more preferably less than 10 μm, it is not preferable because the protective function is lost, and if the film thickness exceeds 60 μm, further 40 μm. The total thickness of the paper recording material according to the present invention is undesirably increased because it increases the cost.
なお、本発明において、本発明に係る紙製記録材を構成する紙基材、レ−ザ−光線照射発色樹脂層、あるいは、樹脂層等のいずれかの一層あるいはそれ以上の層に、所望の印刷模様層を形成することができるものである。
而して、上記の印刷模様層としては、通常のインキビヒクルの１種ないし２種以上を主成分とし、これに、必要ならば、可塑剤、安定剤、酸化防止剤、光安定剤、紫外線吸収剤、硬化剤、架橋剤、滑剤、帯電防止剤、充填剤、その他等の添加剤の１種ないし２種以上を任意に添加し、更に、染料・顔料等の着色剤を添加し、溶媒、希釈剤等で充分に混練してインキ組成物を調整し、次いで、該インキ組成物を使用し、例えば、グラビア印刷、オフセット印刷、凸版印刷、スクリ−ン印刷、転写印刷、フレキソ印刷、その他等の印刷方式を使用し、前述のコ−ティング薄膜の上に、文字、図形、記号、模様等からなる所望の印刷模様を印刷して、本発明にかかる印刷模様層を形成することができる。
In the present invention, a desired one or more layers such as a paper base material, a laser beam irradiation color developing resin layer, or a resin layer constituting the paper recording material according to the present invention may be used. A printed pattern layer can be formed.
Thus, the printed pattern layer is mainly composed of one or more ordinary ink vehicles, and if necessary, a plasticizer, a stabilizer, an antioxidant, a light stabilizer, an ultraviolet ray, and the like. One or more additives such as an absorbent, a curing agent, a crosslinking agent, a lubricant, an antistatic agent, a filler, and the like are arbitrarily added, and a colorant such as a dye / pigment is added, and a solvent is added. The ink composition is prepared by sufficiently kneading with a diluent, and then the ink composition is used. For example, gravure printing, offset printing, letterpress printing, screen printing, transfer printing, flexographic printing, etc. The printing pattern layer according to the present invention can be formed by printing a desired printing pattern composed of characters, figures, symbols, patterns, etc. on the above-described coating thin film using a printing method such as .
また、本発明において、本発明に係る紙製記録材を構成する紙基材、レ−ザ−光線照射発色樹脂層、あるいは、樹脂層等のいずれかの一層あるいはそれ以上の層に、更には、その層間等に、例えば、カ−ドの暗証番号、その他等を記録する磁気層、ＩＣチップ、その他等を積層一体化することができるものである。
更に、本発明において、上記の積層一体化に際しては、エンボス加工等を行うこともできるものである。
Further, in the present invention, any one or more layers such as a paper base material, a laser beam irradiation coloring resin layer, or a resin layer constituting the paper recording material according to the present invention, and further, For example, a magnetic layer for recording a card PIN code, etc., an IC chip, etc. can be laminated and integrated between the layers.
Furthermore, in the present invention, embossing or the like can be performed in the above-described lamination and integration.
而して、本発明において、上記で製造される本発明に係る紙製記録材料は、前述のように、その一方の面、あるいは、両方の面からレ−ザ−光線を照射すると、該レ−ザ−光線は、レ−ザ−光線照射発色樹脂層に到達し、その部分のレ−ザ−光線照射発色樹脂層でそのレ−ザ−光線によるエネルギ−を吸収し、そのレ−ザ−光線照射部分において、炭化による黒色発色、あるいは、発泡による白色発色等を形成して、例えば、文字、数字、記号、図柄、その他等からなるレ−ザ−印字画像による透かし画像あるいはぼかし画像等を極めて鮮明に形成し得るものであるから、これを利用して、製品の偽造防止、改変防止、その他等の付加価値を付けた紙製記録体の製造を可能とするものであり、これにより、例えば、紙幣、株券、商品券、宝くじ、その他等の有価証券類、帳票類、記録紙類、会員カ−ド、身分証明カ−ド、ポイントカ−ド、キャッシュカ−ド、クレジットカ−ド、ＩＣカ−ド、その他等の種々の高機能化を図ることができるものである。
次に、本発明について実施例を挙げて更に具体的に説明する。
Thus, in the present invention, the paper recording material according to the present invention produced as described above is irradiated with a laser beam from one side or both sides as described above. The laser beam reaches the laser beam irradiation coloring resin layer, and the laser beam irradiation coloring resin layer in the portion absorbs the energy generated by the laser beam, and the laser beam is absorbed. In the light irradiation part, black color formation by carbonization or white color formation by foaming is formed, for example, a watermark image or a blurred image by a laser print image composed of letters, numbers, symbols, designs, etc. Since it can be formed very clearly, it is possible to produce a paper recording body with added value such as prevention of counterfeiting, prevention of modification, etc. by using this, For example, banknotes, stock certificates, gift certificates, treasure Various other securities such as securities, forms, recording paper, membership cards, identification cards, point cards, cash cards, credit cards, IC cards, etc. It can be functionalized.
Next, the present invention will be described more specifically with reference to examples.
まず、第１層と第３層に、坪量３０ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ５０μｍ）を準備した。
他方、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（メルクジャパン株式会社製、商品名、イリオジンＬＳ−８２５）５．０重量部とを十分に混練した樹脂組成物を調製した。
次いで、上記の２枚の薄紙の層間に、上記で調製した樹脂組成物を使用し、これを３３０℃まで加熱し、次いで、押出機で押出コ−トして、厚さ３０μｍのレ−ザ−光線照射発色樹脂層を押出積層して、３層積層体からなる、本発明に係る紙製記録材料を製造した。 次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な暗色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, a thin paper (made by Tokushu Paper Co., Ltd., thickness 50 μm) having a basis weight of 30 g / m 2 was prepared for the first layer and the third layer.
On the other hand, polyethylene resin (Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: Density = 0.923 g / cm 3, melt flow - rate (MFR) = 3.7 g / 10 min) and 95.0 parts by weight, YAG Les A resin composition was prepared by sufficiently kneading 5.0 parts by weight of the coloring pigment (Merck Japan, trade name, Iriodin LS-825).
Next, the resin composition prepared above is used between the two thin paper layers, and the resin composition is heated to 330 ° C. and then extrusion coated with an extruder to obtain a laser having a thickness of 30 μm. -A paper recording material according to the present invention consisting of a three-layer laminate was produced by extrusion laminating a light-irradiated coloring resin layer. Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. As a result, it was confirmed that the characters of dark and dark colors emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
まず、第１層と第３層に、坪量３０ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ５０μｍ）を準備した。
他方、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（大日精化工業株式会社製、商品名、ＰＥ−ＲＭＡＺＭＤ１２３９）５．０重量部とを十分に混練した樹脂組成物を調製した。
次いで、上記の２枚の薄紙の層間に、上記で調製した樹脂組成物を使用し、これを３３０℃まで加熱し、次いで、Ｔダイ押出機で押出コ−トして、厚さ３０μｍのレ−ザ−光線照射発色樹脂層を押出積層して、３層積層体からなる本発明に係る紙製記録材料を製造した。
次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な白色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, a thin paper (made by Tokushu Paper Co., Ltd., thickness 50 μm) having a basis weight of 30 g / m 2 was prepared for the first layer and the third layer.
On the other hand, 95.0 parts by weight of polyethylene resin (manufactured by Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: density = 0.923 g / cm 3 , melt flow rate (MFR) = 3.7 g / 10 min), YAG A resin composition was prepared by sufficiently kneading 5.0 parts by weight of the coloring pigment (manufactured by Dainichi Seika Kogyo Co., Ltd., trade name, PE-RMAZMD1239).
Next, the resin composition prepared above is used between the two thin paper layers, which is heated to 330 ° C., and then extrusion coated with a T-die extruder to obtain a 30 μm thick layer. A paper recording material according to the present invention consisting of a three-layer laminate was produced by extrusion laminating the light-irradiated coloring resin layer.
Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. It was confirmed that the crisp white characters emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
まず、第１層と第３層に、坪量３０ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ５０μｍ）を準備した。
他方、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（メルクジャパン株式会社製、商品名、イリオジンＬＳ−８２５）２．５重量部と、ＹＡＧレ−ザ−発色顔料（大日精化工業株式会社製、商品名、ＰＥ−ＲＭＡＺＭＤ１２３９）２．５重量部とを十分に混練した樹脂組成物を調製した。
次いで、上記の２枚の薄紙の層間に、上記で調製した樹脂組成物を使用し、これを３３０℃まで加熱し、次いで、Ｔダイ押出機で押出コ−トして、厚さ３０μｍのレ−ザ−光線照射発色樹脂層を押出積層して、３層積層体からなる本発明に係る紙製記録材料を製造した。
次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な黒色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, a thin paper (made by Tokushu Paper Co., Ltd., thickness 50 μm) having a basis weight of 30 g / m 2 was prepared for the first layer and the third layer.
On the other hand, 95.0 parts by weight of polyethylene resin (manufactured by Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: density = 0.923 g / cm 3 , melt flow rate (MFR) = 3.7 g / 10 min), YAG -The coloring pigment (Merck Japan Co., Ltd., trade name, Iriodin LS-825) 2.5 parts by weight and YAG laser coloring pigment (Daiichi Seika Kogyo Co., Ltd., trade name, PE-RMAZMD1239) A resin composition was prepared by sufficiently kneading 2.5 parts by weight.
Next, the resin composition prepared above is used between the two thin paper layers, which is heated to 330 ° C., and then extrusion coated with a T-die extruder to obtain a 30 μm thick layer. A paper recording material according to the present invention consisting of a three-layer laminate was produced by extrusion laminating the light-irradiated coloring resin layer.
Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. As a result, it was confirmed that the unclear black characters emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
まず、第１層と第３層に、坪量４５ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ８０μｍ）を準備した。
他方、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（メルクジャパン株式会社製、商品名、イリオジンＬＳ−８２５）５．０重量部とを十分に混練した樹脂組成物を調製した。
次いで、上記の２枚の薄紙の層間に、上記で調製した樹脂組成物を使用し、これを３３０℃まで加熱し、次いで、押出機で押出コ−トして、厚さ３０μｍのレ−ザ−光線照射発色樹脂層を押出積層して、３層積層体からなる本発明に係る紙製記録材料を製造した。 次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な暗色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, thin paper (made by Tokushu Paper Co., Ltd., thickness 80 μm) having a basis weight of 45 g / m 2 was prepared for the first layer and the third layer.
On the other hand, polyethylene resin (Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: Density = 0.923 g / cm 3, melt flow - rate (MFR) = 3.7 g / 10 min) and 95.0 parts by weight, YAG Les A resin composition was prepared by sufficiently kneading 5.0 parts by weight of the coloring pigment (Merck Japan, trade name, Iriodin LS-825).
Next, the resin composition prepared above is used between the two thin paper layers, and the resin composition is heated to 330 ° C. and then extrusion coated with an extruder to obtain a laser having a thickness of 30 μm. -A paper recording material according to the present invention consisting of a three-layer laminate was produced by extrusion lamination of the light-irradiated coloring resin layer. Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. As a result, it was confirmed that the characters of dark and dark colors emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
まず、第１層と第４層に、坪量３０ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ５０μｍ）を準備した。
他方、第２層に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）１００．０重量部を十分に混練した第１の樹脂組成物を調製した。
次に、第３層に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（メルクジャパン株式会社製、商品名、イリオジンＬＳ−８２５）５．０重量部とを十分に混練した第２の樹脂組成物を調製した。 更に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）１００．０重量部を十分に混練した第２の樹脂組成物を調製した。
次いで、上記の２枚の第１層と第４層との薄紙の層間に、上記で調製した２種類の樹脂組成物を使用し、これらをそれぞれ３３０℃まで加熱し、次いで、Ｔダイ共押出機を用いて、第２層、厚さ５μｍ、第３層、厚さ２０μｍのそれぞれの膜厚でこられらの順序で共押出積層して、４層積層体からなる本発明に係る紙製記録材料を製造した。
次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な暗色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, thin paper (made by Tokushu Paper Co., Ltd., thickness 50 μm) having a basis weight of 30 g / m 2 was prepared for the first layer and the fourth layer.
On the other hand, a polyethylene resin (trade name, Sumikasen 16P: Density = 0.923 g / cm 3 , Melt Flow Rate (MFR) = 3.7 g / 10 min), 100.0 wt. The 1st resin composition which knead | mixed the part fully was prepared.
Next, a polyethylene resin (manufactured by Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: Density = 0.923 g / cm 3 , Melt Flow Rate (MFR) = 3.7 g / 10 min) 95.0 is applied to the third layer. A second resin composition was prepared by sufficiently kneading parts by weight and 5.0 parts by weight of YAG laser coloring pigment (Merck Japan, trade name, Iriodin LS-825). Further, the polyethylene resin (Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: Density = 0.923 g / cm 3, melt flow - rate (MFR) = 3.7 g / 10 min) thoroughly kneaded 100.0 parts by weight A second resin composition was prepared.
Next, the two types of resin compositions prepared above were used between the two thin paper layers of the first layer and the fourth layer, and each was heated to 330 ° C., and then T-die coextrusion The paper according to the present invention consisting of a four-layer laminate by coextrusion laminating in these order with the thicknesses of the second layer, thickness 5 μm, third layer, thickness 20 μm. A recording material was produced.
Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. As a result, it was confirmed that the characters of dark and dark colors emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
まず、第１層と第５層に、坪量３０ｇ／ｍ2 の薄紙（特種製紙株式会社製、厚さ５０μｍ）を準備した。
他方、第２層に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）１００．０重量部を十分に混練した第１の樹脂組成物を調製した。
次に、第３層に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）９５．０重量部と、ＹＡＧレ−ザ−発色顔料（メルクジャパン株式会社製、商品名、イリオジンＬＳ−８２５）５．０重量部とを十分に混練した第２の樹脂組成物を調製した。
更に、第４層に、上記の第２層と同様に、ポリエチレン樹脂（三井住友ポリオレフィン株式会社製、商品名、スミカセン１６Ｐ：密度＝０．９２３ｇ／ｃｍ3 、メルトフロ−レイト（ＭＦＲ）＝３．７ｇ／１０分）１００．０重量部を十分に混練した第３の樹脂組成物を調製した。
次いで、上記の２枚の第１層と第５層との薄紙の層間に、上記で調製した３種類の樹脂組成物を使用し、これらをぞれぞれ３３０℃まで加熱し、次いで、Ｔダイ共押出機を用いて、第２層、厚さ５μｍ、第３層、厚さ２０μｍ、第４層、厚さ５μｍのそれぞれの膜厚でこられらの順序で共押出積層して、５層積層体からなる本発明に係る紙製記録材料を製造した。
次いで、上記で製造した紙製記録材料の表面に、ＹＡＧレ−ザ−を照射したところ、薄紙には印字およびその他の影響は認められず、上記のレ−ザ−光線照射発色樹脂層に起因した不鮮明な暗色の文字が浮き出てきて、文字画像を印字できることを確認した。
そして、レ−ザ−印字画像を形成した紙製記録体を、蛍光灯の光、および、日光で透かしたところ、印字文字を明確に視認し得て、透かし画像あるいはぼかし画像の形成を確認することができた。
なお、上記の印字においては、煙は発生ぜず、また、穴開きも認められなかった。
First, thin paper (made by Tokushu Paper Co., Ltd., thickness 50 μm) having a basis weight of 30 g / m 2 was prepared for the first layer and the fifth layer.
On the other hand, the second layer, the polyethylene resin (Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: Density = 0.923 g / cm 3, melt flow - rate (MFR) = 3.7 g / 10 min) 100.0 Weight The 1st resin composition which knead | mixed the part fully was prepared.
Next, a polyethylene resin (manufactured by Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: density = 0.923 g / cm 3 , melt flow rate (MFR) = 3.7 g / 10 min) 95.0 is used for the third layer. A second resin composition was prepared by sufficiently kneading parts by weight and 5.0 parts by weight of YAG laser coloring pigment (Merck Japan, trade name, Iriodin LS-825).
Further, in the same manner as the second layer, a polyethylene resin (manufactured by Sumitomo Mitsui Polyolefin Co., Ltd., trade name, Sumikasen 16P: density = 0.923 g / cm 3 , melt flow rate (MFR) = 3. 7 g / 10 minutes) A third resin composition was prepared by sufficiently kneading 100.0 parts by weight.
Next, the three types of resin compositions prepared above are used between the two thin paper layers of the first layer and the fifth layer, and each of them is heated to 330 ° C., and then T Using a die co-extrusion machine, the second layer, thickness 5 μm, third layer, thickness 20 μm, fourth layer, and thickness 5 μm were co-extrusion laminated in these order, and 5 A paper recording material according to the present invention comprising a layered laminate was produced.
Next, when the surface of the paper recording material produced above was irradiated with a YAG laser, printing and other effects were not observed on the thin paper, and this was caused by the above-mentioned laser beam irradiation color resin layer. As a result, it was confirmed that the characters of dark and dark colors emerged and the character image could be printed.
Then, when the paper recording body on which the laser print image is formed is watermarked with fluorescent light and sunlight, the printed characters can be clearly recognized, and the formation of the watermark image or blurred image is confirmed. I was able to.
In the above printing, no smoke was generated and no perforations were observed.
なお、上記の各実施例において、各層を構成する材料の膜厚は、ソニ−株式会社製のμ−メ−タ−にて測定した。
また、上記の各実施例において、ＹＡＧレ−ザ−印字は、富士電機株式会社製、ＹＡＧレ−ザ−システム（機種名、ＤＷ５２００）から、１６．５Ａ、６ｋＨｚにてレ−ザ−照射した。
In each of the above examples, the film thickness of the material constituting each layer was measured with a μ-meter manufactured by Sony Corporation.
In each of the above embodiments, YAG laser printing was performed by laser irradiation at 16.5 A, 6 kHz from a YAG laser system (model name, DW5200) manufactured by Fuji Electric Co., Ltd. .
而して、本発明において、上記で製造される本発明に係る紙製記録材料は、前述のように、その一方の面、あるいは、両方の面からレ−ザ−光線を照射すると、該レ−ザ−光線は、レ−ザ−光線照射発色樹脂層に到達し、その部分のレ−ザ−光線照射発色樹脂層でそのレ−ザ−光線によるエネルギ−を吸収し、そのレ−ザ−光線照射部分において、炭化による黒色発色、あるいは、発泡による白色発色等を形成して、例えば、文字、数字、記号、図柄、その他等からなるレ−ザ−印字画像による透かし画像あるいはぼかし画像等を極めて鮮明に形成し得るものであるから、これを利用して、製品の偽造防止、改変防止、その他等の付加価値を付けた紙製記録体の製造を可能とするものであり、これにより、例えば、紙幣、株券、商品券、宝くじ、その他等の有価証券類、帳票類、記録紙類、会員カ−ド、身分証明カ−ド、ポイントカ−ド、キャッシュカ−ド、クレジットカ−ド、ＩＣカ−ド、その他等の種々の高機能化を図ることができるものである。 Thus, in the present invention, the paper recording material according to the present invention produced as described above is irradiated with a laser beam from one side or both sides as described above. The laser beam reaches the laser beam irradiation coloring resin layer, and the laser beam irradiation coloring resin layer in the portion absorbs the energy generated by the laser beam, and the laser beam is absorbed. In the light irradiation part, black color formation by carbonization or white color formation by foaming is formed, for example, a watermark image or a blurred image by a laser print image composed of letters, numbers, symbols, designs, etc. Since it can be formed very clearly, it is possible to produce a paper recording body with added value such as prevention of counterfeiting, prevention of modification, etc. by using this, For example, banknotes, stock certificates, gift certificates, treasure Various other securities such as securities, forms, recording paper, membership cards, identification cards, point cards, cash cards, credit cards, IC cards, etc. It can be functionalized.
１、１ａ 紙基材
２ レ−ザ−光線照射発色樹脂層
３、３ａ 樹脂層
１１ レ−ザ−光線
１２ レ−ザ−印字画像
１２ａ レ−ザ−印字画像による透かし画像あるいはぼかし画像
DESCRIPTION OF
Claims (7)
The paper recording material according to any one of claims 1 to 6, wherein the laser beam irradiation coloring resin layer has a thickness of 1 µm to 100 µm.