JP2005254121A - 低級炭化水素直接改質触媒の製造方法 - Google Patents
低級炭化水素直接改質触媒の製造方法 Download PDFInfo
- Publication number
- JP2005254121A JP2005254121A JP2004068437A JP2004068437A JP2005254121A JP 2005254121 A JP2005254121 A JP 2005254121A JP 2004068437 A JP2004068437 A JP 2004068437A JP 2004068437 A JP2004068437 A JP 2004068437A JP 2005254121 A JP2005254121 A JP 2005254121A
- Authority
- JP
- Japan
- Prior art keywords
- molybdenum
- catalyst
- component
- metal component
- metallosilicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】メタロシリケートにモリブデンとモリブデン以外の金属成分とを担持した後に炭化処理して低級炭化水素直接改質触媒を製造にあたり、前記メタロシリケートにモリブデンと前記金属成分とを個別に担持した後に、これを炭化処理する際に還元ガスを混合して処理を行なう。前記モリブデン成分と前記金属成分とを個別に担持する際、メタロシリケートに前記金属成分を担持した後にモリブデン成分を担持するか、メタロシリケートにモリブデン成分を担持した後に前記金属成分を担持する。前記金属成分には例えば鉄族元素があり、鉄、コバルトまたはニッケルが例示される。前記モリブデン成分と前記金属成分とを個別に担持する際、前記金属成分の溶液濃度は金属塩濃度として0.01〜0.2mol/lとするとよい。
【選択図】 なし
Description
JOURNAL OF CATALYSIS,1997年,pp.165,pp.150−161
1.低級炭化水素改質触媒の製造
触媒の主成分であるメタロシリケートにはアンモニウム型ZSM−5(SiO2/Al2O3=25〜60)を採用し、これを他の無機成分と有機バインダーと共に混練して成形し乾燥さらに焼成し、その後、金属成分を含浸させてから酸化及び炭化処理に供して低級炭化水素直接改質触媒(以下、触媒と称する)得た。以下に比較例及び実施例に係る触媒の製造の各工程について説明する。
比較例1に係る触媒はモリブデンのみを担持したものである。製造工程を以下に示した。
触媒の構成成分とその配合比率(重量%)以下に示した。
また、無機成分の構成成分とその配合比率(重量%)以下に示した。
2)成形 無機成分と有機バインダーと水分とを前記比率で配合し、ニーダ等の混練手段によって混練した。次いで、この混合体を真空押し出し成型機によって棒状(径5mm)に成形した。このときの成形圧力は70〜100kg/cm2とした。そして、この押し出し成型で得られた径5mmの棒状担体を長さ6mmに切断して成形体を得た。
比較例2に係る触媒は、モリブデンとコバルトとを同時担持したもので、含浸工程と酸化処理工程以外は、比較例1に係る触媒の製造工程と同じ方法で製造した。
実施例1に係る触媒は、モリブデンとコバルトとを個別担持して得たもので、特に、先ずコバルト成分を担持し、その後、モリブデン成分を担持して得たものであり、以下のア)〜エ)の工程からなる含浸・酸化工程以外は、比較例1に係る触媒の製造工程と同じ方法で製造した。
実施例2に係る触媒は、モリブデンとコバルトとを個別担持して得たもので、特に、先ずモリブデン成分を担持し、その後、コバルト成分を担持して得たものであり、以下のア)〜エ)の工程からなる含浸・酸化工程以外は、比較例1に係る触媒の製造工程と同じ方法で製造した。
2.触媒の評価
比較例及び実施例に係る触媒の評価法について述べる。
表1は図1〜図4の結果に基づき、比較例1、比較例2、実施例1、実施例2に係る各触媒による水素、ベンゼン、トルエン、ナフタレンの生成について、従来法に係る触媒(比較例1)を基準(「△」)とし、初期活性と安定性のどちらも効果が認められたものを「○」、初期活性と安定性のどちらも著しく効果が認められたものを「◎」として示したものである。
Claims (6)
- メタロシリケートにモリブデンとモリブデン以外の金属成分とを担持した後に炭化処理して低級炭化水素直接改質触媒を得る低級炭化水素直接改質触媒の製造方法であって、前記メタロシリケートにモリブデンと前記金属成分とを個別に担持した後に、これを炭化処理する際に還元ガスを混合して処理を行なうことを特徴とする低級炭化水素直接改質触媒の製造方法。
- 前記メタロシリケートにモリブデン成分と前記金属成分とを個別に担持するに際し、メタロシリケートに前記金属成分を担持した後にモリブデン成分を担持することを特徴とする請求項1記載の低級炭化水素直接改質触媒の製造方法。
- 前記メタロシリケートにモリブデン成分と前記金属成分とを個別に担持するに際し、メタロシリケートにモリブデン成分を担持した後に前記金属成分を担持することを特徴とする請求項1記載の低級炭化水素直接改質触媒の製造方法。
- 前記メタロシリケートにモリブデン成分と前記金属成分とを個別に担持する際に供される前記金属成分の溶液濃度は金属塩濃度として0.01〜0.2mol/lとすることを特徴とする請求項1から3のいずれか1項に記載の低級炭化水素直接改質触媒の製造方法。
- 前記金属成分は鉄族元素であることを特徴とする請求項1から4のいずれか1項に記載の低級炭化水素直接改質触媒の製造方法。
- 前記鉄族元素は、鉄、コバルトまたはニッケルであることを特徴とする請求項5記載の低級炭化水素直接改質触媒の製造方法。