JP2003027398A - Offset-printable pressure-sensitive adhesive recording paper sheet for ink jet printing - Google Patents
Offset-printable pressure-sensitive adhesive recording paper sheet for ink jet printingInfo
- Publication number
- JP2003027398A JP2003027398A JP2001219949A JP2001219949A JP2003027398A JP 2003027398 A JP2003027398 A JP 2003027398A JP 2001219949 A JP2001219949 A JP 2001219949A JP 2001219949 A JP2001219949 A JP 2001219949A JP 2003027398 A JP2003027398 A JP 2003027398A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- ink
- sensitive adhesive
- parts
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明の感圧接着性記録用紙
は、インクジェット方式による記録、並びに水性インク
を用いる他のペンプロッター等の記録、印刷、筆記に用
いることができ、プロセスインキ、ＵＶインキなどによ
るオフセット印刷も可能であり、更に、これら各種の方
法を印刷・印字等の用途に於いて兼用可能な感圧接着性
記録用紙に関するものである。BACKGROUND OF THE INVENTION The pressure-sensitive adhesive recording paper of the present invention can be used for recording by an ink jet system and for recording, printing and writing on other pen plotters using water-based ink, process ink and UV ink. The present invention also relates to a pressure-sensitive adhesive recording paper which can be used for offset printing by, for example, and can also use these various methods in printing and printing applications.
【０００２】[0002]
【従来の技術】従来、官庁、自治体、等の公的及び準公
的機関や銀行、生命保険会社、証券会社等の金融機関、
更には学校等からの成績通知や受験（検）合否通知書等
の個人的プライバシーに係わる親展情報の郵送には、発
送者の判断により、葉書又は封書が使われていた。しか
し、個人情報の隠蔽化の点から葉書に比べ、高価な封書
の使用が多く、発送者に多額の郵便費用が掛かる問題が
あった。2. Description of the Related Art Conventionally, public and quasi-public institutions such as government offices, local governments, financial institutions such as banks, life insurance companies, securities companies, etc.
Furthermore, postcards or envelopes were used at the sender's discretion to mail confidential information relating to personal privacy, such as school grade notifications and examination (examination) pass / fail notifications. However, compared to postcards, the use of expensive envelopes is more common in terms of hiding personal information, and there is a problem in that a large amount of postage is required for the sender.
【０００３】近年、郵便法の改正に伴い、封書よりも郵
便料金が安く、封書と同様に情報の機密保持ができる親
展性葉書として２つ折り、３つ折りの記録用紙を重ね合
わせ、葉書状に圧着する所謂「圧着葉書」が開発され、
普及し始めている。In recent years, with the revision of the Postal Law, the postage is cheaper than a sealed letter, and as a confidential postcard capable of maintaining confidentiality of information similarly to a sealed letter, two folded and three folded recording sheets are superposed and pressed in a postcard. The so-called "crimp postcard" was developed,
It is becoming popular.
【０００４】これらの圧着用紙は感圧接着面側となる支
持体に通常状態では粘着性、接着性ともに示さず、加圧
時に接着性を示す感圧接着層を形成させ、親展情報の印
字後に用紙を折り畳み、感圧接着層同士を合わせた状態
で加圧接着するものである。受取人は接着された感圧接
着面を剥離して親展情報を読み取ることができ、剥離後
は通常の方法では再接着できないことで情報の親展性を
確保できる。These pressure-sensitive adhesive sheets have a pressure-sensitive adhesive layer on the support which is the pressure-sensitive adhesive surface side after the confidential information is printed. The paper is folded and pressure-bonded with the pressure-sensitive adhesive layers aligned. The recipient can read the confidential information by peeling off the pressure-sensitive adhesive surface to which it is adhered, and the information cannot be re-adhered by the usual method after the peeling, so that the confidentiality of information can be secured.
【０００５】情報システムの発展はめざましく、それに
ともない各情報システムに適合した記録方式が種々開発
されている。コピー・印字スピードの高速化のみならず
カラー化に代表される高画質化が進み、これらの実現に
大きく寄与する為に複写・印字方式である電子写真記録
方式、インクジェット記録方式、感熱記録媒体を使用す
るサーマルヘッド記録方式が広く採用されている。The development of information systems has been remarkable, and along with that, various recording methods suitable for each information system have been developed. In addition to speeding up copy / printing speeds, high image quality represented by colorization has advanced, and in order to greatly contribute to the realization of these, electrophotographic recording methods, inkjet recording methods, and thermal recording media are used. The thermal head recording method used is widely adopted.
【０００６】インクジェット記録方式の発展により、商
業印刷では、印字スピードが３００ｍ／分といった高速
印字が可能なインクジェットプリンターが使用されてい
る。このようなシステムにおいては、全ての情報（一般
情報と個人情報）をインクジェットプリンターでシート
に印刷する場合と、あらかじめ連続オフセット印刷機な
どの印刷機により一般情報を印刷したシートに、個人情
報（可変情報）だけ後にインクジェットプリンターによ
り印字する２通りの印刷方法がある。With the development of the ink jet recording system, an ink jet printer capable of high-speed printing at a printing speed of 300 m / min is used in commercial printing. In such a system, when printing all information (general information and personal information) on a sheet with an inkjet printer, and when personal information (variable information) is printed on a sheet on which the general information is printed in advance by a printing machine such as a continuous offset printer, There are two printing methods for printing with an inkjet printer after (information) only.
【０００７】このような２通りの印刷方法がとられるイ
ンクジェット記録用紙には、第一に印字品質や耐水性な
どのインクジェット適性が必須であり、アニオン性イン
クジェット記録用インクを記録用紙に定着させるため
に、カチオン性の染料定着剤や耐水化剤を併用すること
でインクジェット適性をもたせている。この一例とし
て、記録画像を形成するための受像層に感圧接着剤を含
有させ、この塗工層の上にカチオン性樹脂をオーバー塗
工させた印刷用シート（特開平９−１１９０９４号公
報）がある。しかし、オーバー塗工されただけのカチオ
ン性樹脂では表面での定着性が余り得られず、プロセス
インキ、ＵＶインキなどによるオフセット印刷の際に使
用される、湿し水中のアニオン性物質と前記カチオン性
樹脂とが凝集を起こして湿し水を白濁させ、その凝集物
がブランケット胴を介し、印刷版に転移して印刷画像を
汚すという印刷適性上の問題がある。同様な問題が、オ
フセット印刷を行なうインクジェット記録用紙には存在
する。Ink jet recording paper which can be printed by the above two printing methods must first have ink jet aptitude such as print quality and water resistance. In order to fix the anionic ink jet recording ink onto the recording paper. In addition, an ink jet suitability is provided by using a cationic dye fixing agent and a water resistant agent together. As an example of this, a printing sheet in which a pressure-sensitive adhesive is contained in an image receiving layer for forming a recorded image, and a cationic resin is overcoated on this coating layer (Japanese Patent Laid-Open No. 9-119094). There is. However, a cationic resin that has just been over-coated cannot provide sufficient fixability on the surface, and is used in offset printing with process inks, UV inks, etc. There is a problem in terms of printability that the functional resin causes agglomeration to make the dampening water cloudy, and the agglomerates transfer to the printing plate through the blanket cylinder to stain the printed image. A similar problem exists in inkjet recording paper that performs offset printing.
【０００８】上記の問題を解決する手段としてオフセッ
ト印刷時の紙面からのカチオン性樹脂の溶出による、湿
し水の汚染を推定する評価方法としてコロイド摘定が使
用されているが、湿し水の汚染とカチオン性抽出液のポ
リビニル硫酸カリウム溶液による摘定量との相関は、必
ずしも高いものではなかった。As a means for solving the above problems, colloid ablation is used as an evaluation method for estimating contamination of dampening water due to elution of a cationic resin from the paper surface during offset printing. The correlation between the contamination and the aliquot of the cationic extract with the polyvinyl potassium sulfate solution was not necessarily high.
【０００９】[0009]
【発明が解決しようとする課題】よって本発明の第一の
目的は、インクジェットインク受理顔料層又は感圧接着
層中のカチオン性樹脂のオフセット印刷時に使用する湿
し水への溶出を抑制することにより、優れたインクジェ
ット適性を有し、かつプロセスインキ、ＵＶインキなど
を用いることが可能で優れたオフセット印刷適性を有す
る主として二つ折り用のインクジェット用感圧接着性記
録用紙を提供することである。Therefore, the first object of the present invention is to suppress the elution of the cationic resin in the ink jet ink receiving pigment layer or the pressure sensitive adhesive layer into the fountain solution used during offset printing. Accordingly, it is an object of the present invention to provide a pressure-sensitive adhesive recording sheet for inkjet mainly for folding, which has excellent inkjet suitability and can use process ink, UV ink and the like and has excellent offset printing suitability.
【００１０】本発明の第二の目的は、感圧接着層中のカ
チオン性樹脂のオフセット印刷時に使用する湿し水への
溶出を抑制することにより、優れたインクジェット適性
を有し、かつプロセスインキ、ＵＶインキなどを用いる
ことが可能で優れたオフセット印刷適性を有する主とし
て三つ折り用のインクジェット用感圧接着性記録用紙を
提供することである。A second object of the present invention is to have excellent ink jet aptitude by suppressing the elution of the cationic resin in the pressure-sensitive adhesive layer into the fountain solution used in offset printing, and to obtain a process ink. It is to provide a pressure-sensitive adhesive recording sheet for inkjet mainly for tri-fold, which can use UV ink and has excellent offset printing suitability.
【００１１】本発明の第三の目的は、インクジェットイ
ンク受理顔料層中に合成シリカ、少なくとも１種類以上
のカチオン性樹脂、及び少なくとも２種類以上の水系バ
インダーを含有させ、かつカチオン性樹脂の総部数が乾
燥重量部で合成シリカ１００部に対して１０〜６０部で
あり、水系バインダーの総部数が乾燥重量部で合成シリ
カ１００部に対して３０〜１００部とすることによっ
て、インクジェット記録方式においてより優れた発色を
有し、滲みが少なく、かつ高耐水性であるオフセット印
刷可能なインクジェット用感圧接着性記録用紙を提供す
ることにある。さらに、カチオン性樹脂としてアミン・
エピクロロヒドリン縮合樹脂及びジメチルジアリルアン
モニウムクロリド・二酸化イオウ共重合物を含有させた
ものを使用し、水系バインダーとしてポリビニルアルコ
ールとエチレン・酢酸ビニル共重合物、あるいはポリビ
ニルアルコールとスチレン・ブタジエン系エマルジョ
ン、あるいはポリビニルアルコールとアクリル・ブタジ
エン系エマルジョンを含有させたものを使用することに
より、発色性、滲み、耐水性の観点からさらに優れたオ
フセット印刷可能なインクジェット用感圧接着性記録用
紙を提供することも目的とする。A third object of the present invention is to include synthetic silica, at least one or more kinds of cationic resins, and at least two or more kinds of water-based binders in the ink jet ink receiving pigment layer, and the total number of the cationic resins. Is 10 to 60 parts by weight based on 100 parts by weight of synthetic silica, and the total amount of the aqueous binder is 30 to 100 parts by weight based on 100 parts by weight of synthetic silica. An object of the present invention is to provide a pressure-sensitive adhesive recording paper for inkjet, which has excellent color development, little bleeding, and high water resistance and which can be offset printed. Furthermore, as a cationic resin, amine
Using a mixture of epichlorohydrin condensation resin and dimethyldiallylammonium chloride / sulfur dioxide copolymer, polyvinyl alcohol and ethylene / vinyl acetate copolymer as an aqueous binder, or polyvinyl alcohol and styrene / butadiene emulsion, Alternatively, it is also possible to provide a pressure-sensitive adhesive recording paper for ink jet printing, which is more excellent in terms of color developability, bleeding and water resistance, by using a material containing polyvinyl alcohol and an acrylic / butadiene emulsion. To aim.
【００１２】本発明の第４の目的は、水系バインダーに
ポリビニルアルコールを含有させ、かつインクジェット
インク受理顔料層中に、ポリアミドポリウレア樹脂をそ
のポリビニルアルコール１００重量部に対して５〜５０
重量部含有させることで、ポリアミドポリウレア樹脂を
ポリビニルアルコールの架橋剤として作用させてインク
ジェットインク受理顔料層の耐水性を向上させることで
ある。これにより、インクジェット用インクによるポリ
ビニルアルコールの乾燥被膜の膨潤を抑え、インクジェ
ット用インク受理層の耐水性をより改善すると共に、プ
ロセスインキ、ＵＶインキなどによるオフセット印刷の
際に、湿し水によるポリビニルアルコールの乾燥被膜の
膨潤を押さえ、インクジェット用インク受理層からのカ
チオン性物質の湿し水への溶出を防止し、印刷適性を改
善することを目的とする。A fourth object of the present invention is to contain polyvinyl alcohol in an aqueous binder and to add a polyamide polyurea resin in an ink jet ink receiving pigment layer in an amount of 5 to 50 parts by weight per 100 parts by weight of the polyvinyl alcohol.
The content by weight of the polyamide-polyurea resin acts as a crosslinking agent for polyvinyl alcohol to improve the water resistance of the inkjet ink-receiving pigment layer. Thereby, the swelling of the dry film of polyvinyl alcohol by the inkjet ink is suppressed, the water resistance of the inkjet ink receiving layer is further improved, and the polyvinyl alcohol by the dampening water is used in the offset printing with the process ink or UV ink. The present invention aims to suppress the swelling of the dry film of (1) and prevent the elution of a cationic substance from the ink jet ink-receiving layer into the fountain solution to improve the printability.
【００１３】本発明の第五の目的は、感圧接着層に、合
成シリカ、天然ゴム系エマルジョン、合成ゴム系エマル
ジョン及びカチオン性樹脂を含有させ、かつ感圧接着層
に、乾燥重量部で合成シリカ１００部に対して５〜８０
重量部のカチオン性樹脂であるアミン・エピクロロヒド
リン縮合物を含有させることで、もっとも効果的にシリ
カ系顔料をそのカチオン性によりカチオン活性させアニ
オン性を有するインクジェット用インクをイオン結合に
より定着させて、水性インクの耐水性を有するオフセッ
ト印刷可能なインクジェット用感圧接着性記録用紙を提
供することである。A fifth object of the present invention is to make the pressure-sensitive adhesive layer contain synthetic silica, a natural rubber emulsion, a synthetic rubber emulsion and a cationic resin, and to synthesize the pressure-sensitive adhesive layer in a dry weight part. 5-80 for 100 parts of silica
By including parts by weight of a cationic resin, an amine-epichlorohydrin condensate, the silica pigment is most effectively cationically activated by its cationic property, and the anionic inkjet ink is fixed by ionic bonding. Another object of the present invention is to provide a pressure-sensitive adhesive recording paper for inkjet, which has water resistance of a water-based ink and is capable of offset printing.
【００１４】[0014]
【課題を解決するための手段】本発明のオフセット印刷
可能なインクジェット用感圧接着性記録用紙は、支持体
の一方の面にインクジェットインク受理顔料層を設け、
支持体の他方の面に通常状態では粘着性、接着性を示さ
ず、加圧時に接着性を示し、接着後に剥離可能である感
圧接着層を設けた感圧接着性記録用紙において、オフセ
ット印刷で使用する１％湿し水によって前記インクジェ
ットインク受理顔料層塗工面及び前記感圧接着層塗工面
の各々から抽出したカチオン性樹脂と該1％湿し水中の
アニオン性物質との凝集物の生成が、該1％湿し水抽出
液の濁度測定器による濁度として各々２．０ＨＺ(ヘイ
ズ)以下であることを特徴とする。According to the present invention, there is provided an ink jet pressure-sensitive adhesive recording paper for offset printing, wherein an ink jet ink receiving pigment layer is provided on one surface of a support.
Offset printing on a pressure-sensitive adhesive recording paper provided with a pressure-sensitive adhesive layer on the other side of the support, which does not exhibit tackiness or adhesiveness under normal conditions, but exhibits pressure-sensitive adhesiveness when pressed and can be peeled off after adhesion. Of the cationic resin extracted from each of the ink-jet ink-receiving pigment layer coated surface and the pressure-sensitive adhesive layer coated surface with the 1% fountain solution used in 1. and the anionic substance in the 1% fountain solution. The turbidity of the 1% fountain solution extract is 2.0 HZ (haze) or less.
【００１５】本発明のオフセット印刷可能なインクジェ
ット用感圧接着性記録用紙は、支持体の両面に通常状態
では粘着性、接着性を示さず、加圧時に接着性を示し、
接着後に剥離可能である感圧接着層を設けた感圧接着性
記録用紙において、オフセット印刷で使用する１％湿し
水によって前記感圧接着層塗工面の一方の面から抽出し
たカチオン性樹脂と該1％湿し水中のアニオン性物質と
の凝集物の生成が、該1％湿し水抽出液の濁度測定器に
よる濁度として各々２．０ＨＺ以下であることを特徴と
する。The pressure-sensitive adhesive recording paper for inkjet printing capable of offset printing of the present invention does not exhibit tackiness or adhesiveness under normal conditions on both sides of the support, but exhibits adhesiveness under pressure,
In a pressure-sensitive adhesive recording paper provided with a pressure-sensitive adhesive layer that can be peeled off after adhesion, a cationic resin extracted from one surface of the pressure-sensitive adhesive layer coated surface with 1% fountain solution used in offset printing. The formation of aggregates with the anionic substance in the 1% fountain solution is characterized in that the 1% fountain solution extract has a turbidity of 2.0 HZ or less as measured by a turbidity meter.
【００１６】本発明のオフセット印刷可能なインクジェ
ット用感圧接着性記録用紙では、前記インクジェットイ
ンク受理顔料層は、合成シリカ、少なくとも１種類以上
のカチオン性樹脂、及び少なくとも２種類以上の水系バ
インダーを含有し、かつ該カチオン性樹脂の総部数が乾
燥重量部で合成シリカ１００部に対して１０〜６０部で
あり、該水系バインダーの総部数が乾燥重量部で合成シ
リカ１００部に対して３０〜１００部であることが好ま
しい。In the pressure-sensitive adhesive recording sheet for inkjet printing of the present invention, the inkjet ink-receiving pigment layer contains synthetic silica, at least one kind of cationic resin, and at least two kinds of aqueous binder. And the total number of parts of the cationic resin is 10 to 60 parts with respect to 100 parts of synthetic silica in a dry weight part, and the total number of parts of the aqueous binder is 30 to 100 parts with respect to 100 parts of synthetic silica in a dry weight part. It is preferably part.
【００１７】本発明のオフセット印刷可能なインクジェ
ット用感圧接着性記録用紙では、前記カチオン性樹脂
は、アミン・エピクロロヒドリン縮合樹脂及びジメチル
ジアリルアンモニウムクロリド・二酸化イオウ共重合物
を含有し、前記水系バインダーは、ポリビニルアルコー
ルとエチレン・酢酸ビニル共重合物、あるいはポリビニ
ルアルコールとスチレン・ブタジエン系エマルジョン、
あるいはポリビニルアルコールとアクリル・ブタジエン
系エマルジョンを含有することがより好ましい。In the pressure-sensitive adhesive recording sheet for inkjet printing capable of offset printing according to the present invention, the cationic resin contains an amine-epichlorohydrin condensation resin and a dimethyldiallylammonium chloride-sulfur dioxide copolymer. The aqueous binder is polyvinyl alcohol and ethylene / vinyl acetate copolymer, or polyvinyl alcohol and styrene / butadiene emulsion,
Alternatively, it is more preferable to contain polyvinyl alcohol and an acrylic-butadiene emulsion.
【００１８】本発明のオフセット印刷可能なインクジェ
ット用感圧接着性記録用紙では、前記水系バインダーは
ポリビニルアルコールを含有し、かつ前記インクジェッ
トインク受理顔料層は、ポリアミドポリウレア樹脂をポ
リビニルアルコール１００重量部に対して５〜５０重量
部含有することがさらに好ましい。In the pressure-sensitive adhesive recording sheet for inkjet printing according to the present invention, the water-based binder contains polyvinyl alcohol, and the inkjet ink-receiving pigment layer contains polyamide polyurea resin per 100 parts by weight of polyvinyl alcohol. 5 to 50 parts by weight is more preferable.
【００１９】また本発明のオフセット印刷可能なインク
ジェット用感圧接着性記録用紙では、前記感圧接着層
は、合成シリカ、天然ゴム系エマルジョン、合成ゴム系
エマルジョン及びカチオン性樹脂を含有し、かつ前記感
圧接着層は、乾燥重量部で合成シリカ１００部に対して
５〜８０重量部のカチオン性樹脂であるアミン・エピク
ロロヒドリン縮合物を含有することが好ましい。Further, in the pressure-sensitive adhesive recording sheet for ink jet printing capable of offset printing of the present invention, the pressure-sensitive adhesive layer contains synthetic silica, a natural rubber emulsion, a synthetic rubber emulsion and a cationic resin, and It is preferable that the pressure-sensitive adhesive layer contains 5 to 80 parts by weight of the amine-epichlorohydrin condensate which is a cationic resin with respect to 100 parts by weight of synthetic silica in a dry weight part.
【００２０】[0020]
【発明の実施の形態】以下本発明を詳細に説明するが、
本発明は以下の記載に限定的に解釈されない。まず、本
発明に係る感圧接着性記録用紙を作製する方法を説明す
る。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below.
The present invention is not limited to the following description. First, a method for producing the pressure-sensitive adhesive recording paper according to the present invention will be described.
【００２１】二つ折り用の塗工方法は次の通りである。
先ずオフセット印刷可能な顔料塗工液を基材となる原紙
に塗工し、オフセット印刷可能なインクジェット用イン
ク受理層を形成し、次に顔料層とは反対となる面にオフ
セット印刷可能でインクジェット用インク受理可能な感
圧接着層を形成する順序が望ましい。しかしこの逆の順
序でも良く、又２ステージのコーターヘッドで一度に表
裏両面塗工しても良い。The coating method for folding in half is as follows.
First, a pigment coating liquid capable of offset printing is applied to a base paper as a base material to form an ink jet ink receiving layer capable of offset printing, and then offset printing can be performed on the surface opposite to the pigment layer so that it can be offset printing. The order in which the ink receptive pressure sensitive adhesive layer is formed is desirable. However, the reverse order may be used, or both front and back surfaces may be coated at once with a two-stage coater head.
【００２２】三つ折り用の塗工方法は次の通りである。
先ず片面にオフセット印刷可能でインクジェット用イン
ク受理可能な感圧接着層を形成し、次に反対面に同様の
感圧接着層を形成する順序が望ましい。しかし２ステー
ジのコーターヘッドで一度に表裏両面塗工しても良い。The coating method for tri-folding is as follows.
It is desirable to first form a pressure-sensitive adhesive layer capable of offset printing and receiving ink jet ink on one surface and then forming a similar pressure-sensitive adhesive layer on the other surface. However, it is also possible to coat both the front and back sides at once with a two-stage coater head.
【００２３】次に本発明に係る感圧接着性記録用紙を説
明する。支持体として、従来公知のフォーム用紙（非塗
工紙）の他に、上質紙、中質紙（非塗工紙）、各種バイ
ンダーで含浸された含浸紙及び各種顔料で塗工された塗
工紙、アート紙などの原紙を使用することできる。Next, the pressure-sensitive adhesive recording paper according to the present invention will be described. As a support, in addition to conventionally known foam paper (non-coated paper), fine paper, medium-quality paper (non-coated paper), impregnated paper impregnated with various binders, and coating coated with various pigments Base paper such as paper and art paper can be used.
【００２４】オフセット印刷可能でインクジェット用イ
ンク受理可能な顔料層とするためには、インクジェット
方式による発色性、滲み、且つ耐水性並びにプロセスイ
ンキ、ＵＶインキなどによるオフセット印刷適性を満た
す必要がある。本発明の感圧接着性記録用紙では、顔料
塗工液の主成分となる薬品の選択が重要である。合成シ
リカ、水系バインダー、カチオン性樹脂がそれらの条件
を満たすものであり、オフセット印刷で使用する１％湿
し水によってインクジェットインク受理顔料層塗工面か
ら抽出したカチオン性樹脂と1％湿し水中のアニオン性
物質との凝集物の生成が、1％湿し水抽出液の濁度測定
器による濁度として各々２．０ＨＺ(ヘイズ)以下の条件
を満たしうる。In order to form a pigment layer capable of offset printing and receiving an ink jet ink, it is necessary to satisfy the coloring property by the ink jet method, bleeding and water resistance, and the offset printing suitability for process ink, UV ink and the like. In the pressure-sensitive adhesive recording paper of the present invention, it is important to select the chemical that is the main component of the pigment coating liquid. Synthetic silica, water-based binder, and cationic resin satisfy these conditions, and 1% fountain solution used in offset printing is used to extract the cationic resin and 1% fountain solution from the surface coated with the inkjet ink receiving pigment layer. The formation of aggregates with the anionic substance can satisfy the conditions of 2.0 HZ (haze) or less as the turbidity of the 1% fountain solution extract measured by the turbidimeter.
【００２５】合成シリカとしては、インクジェット用イ
ンクを効率良く吸収させる為に、超微粉含水ケイ酸の二
次凝集物で、その平均粒径が３μｍのものを使用し、二
次凝集の細孔にインクジェット用インクを取り込むもの
が最も好ましい。ただし、これ以外の合成シリカや他の
塗工用顔料、例えば酸化チタン、カオリン、炭酸カルシ
ウム、タルク、プラスチックピグメント、硫酸バリウ
ム、水酸化アルミなどを適宜併用しても良い。As the synthetic silica, a secondary aggregate of ultrafine hydrous silicic acid having an average particle size of 3 μm is used in order to efficiently absorb the ink for ink jet, and the secondary aggregation has pores. Most preferred is one that incorporates an inkjet ink. However, other synthetic silica and other coating pigments such as titanium oxide, kaolin, calcium carbonate, talc, plastic pigment, barium sulfate, and aluminum hydroxide may be appropriately used in combination.
【００２６】水系バインダーとしては、ポリビニルアル
コールと、エチレン・酢酸ビニル共重合物又はスチレン
・ブタジエン系エマルジョン又はアクリル・ブタジエン
系エマルジョンとの混合物を使用する。ポリビニルアル
コールとエチレン・酢酸ビニル共重合物の比は２：１〜
１：４の範囲であり、ポリビニルアルコールとスチレン
・ブタジエン系エマルジョンの比は２：１〜１：４の範
囲であり、ポリビニルアルコールとアクリル・ブタジエ
ン系エマルジョンの比は２：１〜１：４の範囲である。
そのポリビニルアルコールと、エチレン・酢酸ビニル共
重合物又はスチレン・ブタジエン系エマルジョン又はア
クリル・ブタジエン系エマルジョンとの合計量を、合成
シリカ１００重量部に対し、３０〜１００重量部配合し
てなることがインクジェット記録方式において発色、滲
み、耐水性を有し、且つオフセット印刷の耐刷力を有す
る為に必要な配合割合である。ただし、この合成シリカ
ならびにポリビニルアルコールならびに、エチレン・酢
酸ビニル共重合物又はスチレン・ブタジエン系エマルジ
ョン又はアクリル・ブタジエン系エマルジョンの混合物
単独ではインクジェット用インクの発色、滲み、耐水性
を十分に満たすものではない。すなわち、前記合成シリ
カならびにポリビニルアルコールならびに、エチレン・
酢酸ビニル共重合物又はスチレン・ブタジエン系エマル
ジョン又はアクリル・ブタジエン系エマルジョンの混合
物に、カチオン樹脂としてアミン・エピクロロヒドリン
縮合樹脂及びジメチルジアリルアンモニウムクロリド・
二酸化イオウ共重合物の混合物を合成シリカ１００重量
部に対し１０〜６０重量部の範囲となるように添加し、
これを塗工乾燥することによりインクジェット用インク
の発色、滲み、耐水性が十分に満たされる。As the water-based binder, a mixture of polyvinyl alcohol and an ethylene / vinyl acetate copolymer, a styrene / butadiene emulsion or an acrylic / butadiene emulsion is used. The ratio of polyvinyl alcohol and ethylene / vinyl acetate copolymer is 2: 1 to
1: 4, the ratio of polyvinyl alcohol to styrene / butadiene emulsion is 2: 1 to 1: 4, and the ratio of polyvinyl alcohol to acrylic / butadiene emulsion is 2: 1 to 1: 4. It is a range.
An ink jet is formed by adding 30 to 100 parts by weight of the total amount of the polyvinyl alcohol and an ethylene / vinyl acetate copolymer, a styrene / butadiene emulsion or an acrylic / butadiene emulsion to 100 parts by weight of synthetic silica. It is a blending ratio necessary for the recording system to have color development, bleeding, water resistance, and printing durability for offset printing. However, this synthetic silica, polyvinyl alcohol, and a mixture of an ethylene / vinyl acetate copolymer, a styrene / butadiene emulsion, or an acrylic / butadiene emulsion alone does not sufficiently satisfy the coloring, bleeding, and water resistance of the inkjet ink. . That is, the synthetic silica, polyvinyl alcohol, and ethylene.
A mixture of vinyl acetate copolymer, styrene / butadiene emulsion or acrylic / butadiene emulsion, as a cationic resin, amine / epichlorohydrin condensation resin and dimethyldiallylammonium chloride /
A mixture of sulfur dioxide copolymer is added in an amount of 10 to 60 parts by weight to 100 parts by weight of synthetic silica,
By coating and drying this, coloring, bleeding and water resistance of the inkjet ink are sufficiently satisfied.
【００２７】ポリビニルアルコールとしては、ケン化度
が９８．５モル％、重合度１７５０のものが、被膜の耐
水性が強く、被膜を形成した後に合成シリカなどの顔料
を支持体に固着させ、更にその水酸基の作用によりイン
クジェット用インクを表面に吸着させ、印字濃度を高く
することができるので、発色性の観点から好ましい。た
だし、他のケン化度、重合度のものを併用あるいは単独
で使用しても良い。Polyvinyl alcohol having a saponification degree of 98.5 mol% and a polymerization degree of 1750 has a strong water resistance of the coating film, and after forming the coating film, a pigment such as synthetic silica is fixed to the support, By the action of the hydroxyl group, the inkjet ink can be adsorbed on the surface to increase the printing density, which is preferable from the viewpoint of color developability. However, those having other degrees of saponification and polymerization may be used in combination or alone.
【００２８】エチレン・酢酸ビニル共重合物としては、
その被膜の耐水性が２０℃２４時間で膨脹率２０％、溶
出率２．７％のものを使用すると被膜の耐水性が強く、
被膜を形成した後は疎水性材質への接着性が強い為、合
成シリカなどの顔料を支持体に固着させ、オフセット印
刷適性を向上させ、更にそのカルボキシル基の作用によ
りインクジェット用インクの滲みを小さく制御すること
ができるので好ましい。ただし、他の膨脹率、溶出率の
ものを併用あるいは単独で使用しても良い。As the ethylene / vinyl acetate copolymer,
The water resistance of the film is strong when the water resistance of the film at 20 ° C. for 24 hours is 20% and the elution rate is 2.7%.
After forming a film, it has strong adhesion to hydrophobic materials, so pigments such as synthetic silica are fixed to the support to improve offset printing suitability, and the bleeding of inkjet ink is reduced by the action of the carboxyl group. It is preferable because it can be controlled. However, those having other expansion rates and elution rates may be used together or alone.
【００２９】スチレン・ブタジエン系エマルジョンとし
ては、スチレンとブタジエンの組成比率が８：２〜４：
６のものが合成シリカなどの顔料を支持体に固着させ、
オフセット印刷適性を向上させ、インクジェット用イン
クの浸透の阻害が小さいので好ましい。The styrene-butadiene emulsion has a composition ratio of styrene and butadiene of 8: 2-4 :.
6 has a pigment such as synthetic silica fixed to a support,
It is preferable because it improves the offset printing suitability and the inhibition of the penetration of the inkjet ink is small.
【００３０】水系バインダーは、ポリビニルアルコール
をはじめ少なくとも２種類以上を混合することが好まし
く、ポリビニルアルコールに対し、エチレン・酢酸ビニ
ル共重合物又はスチレン・ブタジエン系エマルジョン共
重合物又はアクリル・ブタジエン系エマルジョン共重合
物を混合することにより、発色、滲み、耐水性を調節で
きる。そのポリビニルアルコールと、エチレン・酢酸ビ
ニル共重合物又はスチレン・ブタジエン系エマルジョン
共重合物又はアクリル・ブタジエン系エマルジョン共重
合物との混合比は前記の２：１〜１：４の範囲である。The water-based binder is preferably a mixture of at least two kinds including polyvinyl alcohol, and the polyvinyl alcohol is mixed with ethylene / vinyl acetate copolymer, styrene / butadiene emulsion copolymer or acrylic / butadiene emulsion copolymer. Coloring, bleeding, and water resistance can be adjusted by mixing the polymer. The mixing ratio of the polyvinyl alcohol to the ethylene / vinyl acetate copolymer, the styrene / butadiene emulsion copolymer or the acrylic / butadiene emulsion copolymer is in the range of 2: 1 to 1: 4.
【００３１】またオフセット印刷の耐刷力を有する為
に、そのポリビニルアルコールと、エチレン・酢酸ビニ
ル共重合物又はスチレン・ブタジエン系エマルジョン共
重合物又はアクリル・ブタジエン系エマルジョン共重合
物との合計量は、合成シリカ１００重量部に対し３０〜
１００重量部配合してなることが必要である。３０重量
部より少ないとオフセット印刷に使用できる耐刷力に達
せず、また、湿し水へのカチオン性樹脂の溶出が起こ
る。１００重量部より多いとインクジェット用インクの
乾燥性が劣り、また、プロセスインキやＵＶインキなど
のインキ着肉性が劣る。さらにポリビニルアルコール
と、エチレン・酢酸ビニル共重合物又はスチレン・ブタ
ジエン系エマルジョン共重合物又はアクリル・ブタジエ
ン系エマルジョン共重合物の混合物からなる水系バイン
ダーは互いの相溶性に優れている為、この有機高分子接
着剤系における塗工液は物理的化学的に安定性があり塗
工性は良好である。Further, in order to have the printing durability of offset printing, the total amount of the polyvinyl alcohol and the ethylene / vinyl acetate copolymer, the styrene / butadiene emulsion copolymer or the acrylic / butadiene emulsion copolymer is , 30 to 100 parts by weight of synthetic silica
It is necessary to mix 100 parts by weight. If the amount is less than 30 parts by weight, the printing durability that can be used for offset printing will not be reached, and the cationic resin will be eluted into the fountain solution. If the amount is more than 100 parts by weight, the drying property of the inkjet ink is poor and the ink receptivity of process ink or UV ink is poor. Furthermore, since the water-based binder composed of a mixture of polyvinyl alcohol and an ethylene / vinyl acetate copolymer, a styrene / butadiene emulsion copolymer, or an acrylic / butadiene emulsion copolymer is excellent in mutual compatibility, The coating liquid in the molecular adhesive system is physically and chemically stable and has good coatability.
【００３２】カチオン性樹脂は、直接染料、酸性染料あ
るいは反応染料を紙に定着させる染料定着剤として用い
ており、シリカ系顔料をそのカチオン性によりカチオン
活性させ、アニオン性を有するインクジェット用インク
をイオン結合により定着させるのに効果があり、水性イ
ンクの耐水性を付与させる為に含有させる。本発明でい
うカチオン性樹脂としてはポリアミン、ポリアルキルア
ミン及び変性ポリアミン系などのポリアミン系樹脂、ポ
リジアリルアミン系樹脂、ポリアミド・エポキシ系樹
脂、ポリアミン・エピクロロヒドリン系樹脂、ポリアミ
ドポリアミン・エピクロロヒドリン縮合樹脂、ジメチル
ジアリルアンモニウムクロリド・二酸化イオウ共重合物
などが使用できる。特にアミン・エピクロロヒドリン縮
合樹脂及びジメチルジアリルアンモニウムクロリド・二
酸化イオウ共重合物を使用することが望ましい。印刷シ
ートの単位面積当たりの塗工層に含まれるカチオン性樹
脂は０．１〜４．０ｇ/ｍ2とするのが好ましい。塗工層
に含まれるカチオン性樹脂が０．１ｇ/ｍ2を未満では水
性インクの耐水性の効果が不充分であり、４．０ｇ/ｍ2
を超える場合は、カチオン性樹脂の湿し水への溶出が顕
著になるからである。The cationic resin is used as a dye fixing agent for fixing a direct dye, an acid dye or a reactive dye on paper, and a silica-based pigment is cationically activated by its cationic property, and an inkjet ink having an anionic property is ionized. It is effective in fixing by binding, and is contained in order to impart water resistance of the water-based ink. Examples of the cationic resin in the present invention include polyamines such as polyamines, polyalkylamines and modified polyamines, polydiallylamine resins, polyamide / epoxy resins, polyamine / epichlorohydrin resins, polyamide polyamines / epichlorohydrides. A phosphorus condensation resin, a dimethyldiallylammonium chloride / sulfur dioxide copolymer, etc. can be used. In particular, it is preferable to use an amine / epichlorohydrin condensation resin and a dimethyldiallylammonium chloride / sulfur dioxide copolymer. The cationic resin contained in the coating layer per unit area of the printing sheet is preferably 0.1 to 4.0 g / m 2 . If the amount of the cationic resin contained in the coating layer is less than 0.1 g / m 2 , the water resistance of the water-based ink will be insufficient, resulting in 4.0 g / m 2
If it exceeds, the elution of the cationic resin into the fountain solution becomes remarkable.
【００３３】カチオン性樹脂は少なくとも１種類以上を
使用するのが好ましく、上記アミン・エピクロロヒドリ
ン縮合樹脂は、シリカ系顔料をそのカチオン性によりカ
チオン活性させ、アニオン性を有するインクジェット用
インクをイオン結合により定着させるのに効果があり、
耐水性をより改善する。一方、ジメチルジアリルアンモ
ニウムクロリド・二酸化イオウ共重合物は、そのカチオ
ン性により、アニオン性を有するインクジェット用イン
クの定着に寄与する。また、その疎水基の働きによりイ
ンクジェット用インクの滲みを改善する。これらの混合
物をカチオン性樹脂として使用することがより好まし
い。It is preferable to use at least one kind of the cationic resin, and the above-mentioned amine-epichlorohydrin condensation resin makes the silica-based pigment cationically active due to its cationic property, and the ink for inkjet ink having anionic property is ionized. It is effective for fixing by binding,
Improves water resistance. On the other hand, the dimethyldiallylammonium chloride / sulfur dioxide copolymer contributes to the fixing of an inkjet ink having an anionic property due to its cationic property. Further, the function of the hydrophobic group improves the bleeding of the inkjet ink. More preferably, these mixtures are used as cationic resin.
【００３４】本発明では、主成分が合成シリカ、水系バ
インダー及びカチオン性樹脂である顔料塗工液に対して
ポリアミドポリウレア樹脂を添加しても良い。ポリアミ
ドポリウレア樹脂は、ポリビニルアルコールの架橋剤と
して、耐水性を向上させる。すなわち、その架橋作用に
よりインクジェット用インクによるポリビニルアルコー
ルの乾燥被膜の膨潤を抑え、インクジェット用インク受
理層の耐水性をより改善すると共に、プロセスインキ、
ＵＶインキなどによるオフセット印刷の際に、湿し水に
よるポリビニルアルコールの乾燥被膜の膨潤を押さえ、
インクジェット用インク受理層からのカチオン性物質の
湿し水への溶出を防止し、印刷適性を改善する。添加量
としては、ポリビニルアルコール１００重量部に対し、
ポリアミドポリウレア樹脂を５〜５０重量部の範囲で添
加することが好ましい。In the present invention, the polyamide polyurea resin may be added to the pigment coating liquid whose main components are synthetic silica, an aqueous binder and a cationic resin. The polyamide polyurea resin improves water resistance as a crosslinking agent for polyvinyl alcohol. That is, the cross-linking action suppresses the swelling of the polyvinyl alcohol dry film due to the inkjet ink, and further improves the water resistance of the inkjet ink-receiving layer, and the process ink,
When offset printing with UV ink, etc., suppress swelling of polyvinyl alcohol dry film due to dampening water,
Prevents elution of cationic substances from the ink jet ink receiving layer into the fountain solution and improves printability. The amount of addition is 100 parts by weight of polyvinyl alcohol,
It is preferable to add the polyamide polyurea resin in the range of 5 to 50 parts by weight.
【００３５】これらの顔料塗工液には、各種添加剤を含
有しても良く、塗工時の作業性向上の為、レベリング剤
や消泡剤・抑泡剤、後加工性を向上させるためにワック
ス類、視感による白色度向上のため蛍光染料、導電性を
付与させるため界面活性剤や無機塩類からなるいわゆる
帯電防止剤などを含有させることができる。その他、必
要に応じて分散剤、印刷適性向上剤、潤滑剤、撥水剤、
浸透剤、増粘剤、老化防止剤、紫外線吸収剤、染料、染
料定着剤、サイズ剤、紙力増強剤、保水剤、消臭剤、防
腐剤、防黴剤等の添加剤なども目的に応じて併用するこ
とが出来る。These pigment coating liquids may contain various additives, in order to improve workability during coating, in order to improve leveling agents, defoaming agents / foam suppressors and post-processability. In addition, waxes, fluorescent dyes for improving whiteness by visual sense, so-called antistatic agents composed of surfactants and inorganic salts for imparting conductivity can be contained. In addition, if necessary, a dispersant, a printability improver, a lubricant, a water repellent,
Additives such as penetrants, thickeners, anti-aging agents, UV absorbers, dyes, dye fixing agents, sizing agents, paper strengthening agents, water retention agents, deodorants, preservatives, antifungal agents, etc. It can be used together depending on the situation.
【００３６】さらに、印刷強度（表面強度）を向上させ
る目的において酸化澱粉、カルボキシメチルセルロー
ズ、ヒドロキシエチルセルローズ、大豆蛋白、合成蛋
白、カゼイン等を含有させることが可能であるほか、酢
酸ビニル系、メチルメタクリレート・ブタジェン系エマ
ルジョン、スチレン・ブタジエン系エマルジョン、アク
リル・ブタジエン系エマルジョン等を必要に応じ含有さ
せることができる。Further, for the purpose of improving the printing strength (surface strength), it is possible to contain oxidized starch, carboxymethyl cellulose, hydroxyethyl cellulose, soybean protein, synthetic protein, casein, etc., as well as vinyl acetate, methyl If necessary, a methacrylate / butadiene-based emulsion, a styrene / butadiene-based emulsion, an acrylic / butadiene-based emulsion, etc. may be contained.
【００３７】上記のように調整したオフセット印刷可能
でインクジェット用インク受理可能な顔料塗工液の塗工
は、エアーナイフコーター、ロールコーター、ブレード
コーター、ロッドブレードコーター、バーコーター、ダ
イコーター等の一般的なコーターによって行なうが、そ
の塗工量は乾燥重量で３〜１５ｇ／ｍ2の範囲で調整す
ることが望ましい。塗工量を上記範囲に限定した理由
は、３ｇ／ｍ2未満ではインクジェット用インク受理層
且つオフセットインキ受理層として、インクの受容量が
低下し、印字品位や印刷上がりなどの視感的な面で劣
り、更にインクジェット用インクの耐水定着性が低下
し、好ましくないためである。一方、塗工量が１５ｇ／
ｍ2を超えると、印字品位や印刷上がりなどの視感的な
見栄えは向上するが、経済的な面から実用性が劣り、筆
記性が乏しく、紙粉が発生しやすく、好ましくないから
である。The above-prepared pigment printing liquid capable of offset printing and ink-jet ink receptive coating is generally carried out by an air knife coater, roll coater, blade coater, rod blade coater, bar coater, die coater or the like. The coating amount is preferably adjusted within the range of 3 to 15 g / m 2 in terms of dry weight. The reason why the coating amount is limited to the above range is that when the coating amount is less than 3 g / m 2 , the ink receiving amount decreases as an inkjet ink receiving layer and an offset ink receiving layer, and the visual quality such as print quality and printed quality is reduced. This is because the ink-jet ink is inferior and the water-jet fixing resistance of the inkjet ink is lowered, which is not preferable. On the other hand, the coating amount is 15g /
When it exceeds m 2 , the visual quality such as print quality and printed quality is improved, but the practicality is poor from the economical aspect, the writing property is poor, and paper dust is easily generated, which is not preferable. .
【００３８】次に感圧接着層について説明する。オフセ
ット印刷可能でインクジェット用インク受理可能な感圧
接着層とするためには、インクジェット方式による発色
性、滲み、且つ耐水性、並びにプロセスインキ、ＵＶイ
ンキなどによるオフセット印刷適性、並びに再剥離性を
満たす必要がある。本発明の感圧接着性記録用紙では、
感圧接着剤塗工液の主成分となる薬品の選択が重要であ
り、合成シリカ、天然ゴム系エマルジョン、合成ゴム系
エマルジョン、カチオン性樹脂がそれらの条件を満たす
ものであり、オフセット印刷で使用する１％湿し水によ
って感圧接着層塗工面から抽出したカチオン性樹脂と1
％湿し水中のアニオン性物質との凝集物の生成が、1％
湿し水抽出液の濁度測定器による濁度として２．０ＨＺ
以下の条件を満たしうる。合成シリカ、天然ゴム系エマ
ルジョン、合成ゴム系エマルジョンの配合からなる混合
物の感圧接着剤塗工液は、感圧接着剤塗工液の調製及び
塗工機において塗工液の安定性を付与させる。ただし、
この混合物単独ではインクジェット用インクの発色、滲
み、耐水性などの要求特性を十分に満たすものではな
い。すなわち、この混合物に、合成シリカ１００重量部
に対しカチオン性樹脂を５〜８０重量部の範囲となるよ
うに添加し、塗工乾燥することにより、インクジェット
用インクの発色、滲み、耐水性が十分に満たされる。Next, the pressure sensitive adhesive layer will be described. In order to make a pressure-sensitive adhesive layer that can be offset-printed and accepts ink-jet ink, the ink-jet method should meet the color development, bleeding, and water resistance, as well as offset printability with process ink, UV ink, and removability. There is a need. In the pressure-sensitive adhesive recording paper of the present invention,
It is important to select the chemical that is the main component of the pressure-sensitive adhesive coating liquid, and synthetic silica, natural rubber emulsion, synthetic rubber emulsion, and cationic resin satisfy these conditions, and it is used in offset printing. 1% of cationic resin extracted from the coated surface of the pressure sensitive adhesive layer with 1% fountain solution
% Aggregate formation with anionic substances in dampening water, 1%
2.0HZ as turbidity of dampening water extract
The following conditions can be met. A pressure-sensitive adhesive coating liquid that is a mixture of synthetic silica, a natural rubber emulsion, and a synthetic rubber emulsion is added to the preparation of the pressure-sensitive adhesive coating liquid and the stability of the coating liquid in a coating machine. . However,
This mixture alone does not sufficiently satisfy the required properties such as color development, bleeding and water resistance of the inkjet ink. That is, a cationic resin was added to this mixture in an amount of 5 to 80 parts by weight with respect to 100 parts by weight of synthetic silica, and the coating and drying were performed to sufficiently develop coloration, bleeding, and water resistance of the inkjet ink. Is satisfied with.
【００３９】天然ゴム系エマルジョンとしては、通常封
筒用口糊などで用いられている感圧接着剤で良く、天然
生ゴム、天然加硫ゴム、メタクリル酸メチル（ＭＭＡ）
やスチレンモノマーなどのグラフト共重合天然ゴムエマ
ルジョンなどやこれらの混合物を例示できる。一方合成
ゴム系エマルジョンとしては、スチレン・ブタジエン
（ＳＢＲ）やブタジェン（ＢＲ）などの合成ゴム系エマ
ルジョンを例示でき、並びにアクリル酸エステル、スチ
レンアクリルなどのアクリル共重合系エマルジョンなど
を適宜併用しても良い。この中で、天然ゴム系エマルジ
ョンとしてＭＭＡのグラフト共重合天然ゴムエマルジョ
ン、合成ゴム系エマルジョンとしてスチレン・ブタジエ
ン系エマルジョンあるいはアクリルニトリル・ブタジェ
ン系エマルジョンを使用したものが、印刷インキ受理
性、表面強度、耐刷力、耐ブロッキング性、耐熱性、顔
料の固着性などを向上し、カチオン性樹脂の湿し水への
溶出を抑制させるのでより好ましい。なお、アニオンと
カチオンの反応によりショックを起こし、天然ゴムエマ
ルジョンが凝集するので、これを防止する為の緩衝剤と
して非イオン系界面活性剤などを含有することができ
る。The natural rubber emulsion may be a pressure-sensitive adhesive which is usually used as a glue for envelopes and the like. Natural raw rubber, natural vulcanized rubber, methyl methacrylate (MMA)
Examples thereof include graft copolymerized natural rubber emulsion of styrene monomer and the like, and mixtures thereof. On the other hand, examples of the synthetic rubber-based emulsion include styrene-butadiene (SBR), butadiene (BR), and other synthetic rubber-based emulsions, and acrylic ester, styrene-acrylic, and other acrylic copolymer-based emulsions may be used in combination. good. Among these, MMA graft copolymerized natural rubber emulsion is used as the natural rubber-based emulsion, and styrene-butadiene-based emulsion or acrylonitrile-butadiene-based emulsion is used as the synthetic rubber-based emulsion. It is more preferable because it improves printing power, blocking resistance, heat resistance, pigment fixing property, and the like, and suppresses elution of the cationic resin into the fountain solution. A shock occurs due to the reaction between anions and cations, and the natural rubber emulsion agglomerates. Therefore, a nonionic surfactant or the like can be contained as a buffer for preventing this.
【００４０】カチオン性樹脂は、直接染料、酸性染料あ
るいは反応染料を紙に定着させる染料定着剤として用い
ており、シリカ系顔料をそのカチオン性によりカチオン
活性させ、アニオン性を有するインクジェット用インク
をイオン結合により定着させるのに効果があり、水性イ
ンクの耐水性を付与させる為に含有させる。本発明でい
うカチオン性樹脂としては、ポリアミン、ポリアルキル
アミン及び変性ポリアミン系などのポリアミン系樹脂、
ポリジアリルアミン系樹脂、ポリアミド・エポキシ系樹
脂、ポリアミン・エピクロロヒドリン系樹脂、ポリアミ
ドポリアミン・エピクロロヒドリン縮合樹脂などが使用
できる。そのうち、少なくとも１種類以上使用すること
が好ましく、特にアミン・エピクロルヒドリン縮合物を
使用することが望ましい。印刷シートの単位面積当たり
の塗工層に含まれるカチオン性樹脂は０．１〜４．０ｇ
/ｍ2とするのが好ましい。カチオン性樹脂が０．１ｇ/
ｍ2未満の場合は、水性インクの耐水性の効果が不充分
であり、４．０ｇ/ｍ2を超える場合は、カチオン性樹脂
の湿し水への溶出が顕著になるからである。The cationic resin is used as a dye fixing agent for fixing a direct dye, an acid dye or a reactive dye on paper, and a silica-based pigment is cationically activated by its cationic property, and an ink jet ink having an anionic property is ionized. It is effective in fixing by binding, and is contained in order to impart water resistance of the water-based ink. Examples of the cationic resin in the present invention include polyamine-based resins such as polyamines, polyalkylamines and modified polyamine-based resins,
Polydiallylamine type resin, polyamide / epoxy type resin, polyamine / epichlorohydrin type resin, polyamide polyamine / epichlorohydrin condensation resin, etc. can be used. Among them, it is preferable to use at least one kind, and it is particularly preferable to use an amine-epichlorohydrin condensate. The cationic resin contained in the coating layer per unit area of the printing sheet is 0.1 to 4.0 g.
/ m 2 is preferable. 0.1 g of cationic resin /
When it is less than m 2 , the water resistance of the water-based ink is insufficient, and when it exceeds 4.0 g / m 2 , the cationic resin is significantly eluted into the fountain solution.
【００４１】合成シリカは、微粒子状の充填剤として使
用する。合成シリカはインクジェット用インクを効率良
く吸収させる為に、超微粉含水ケイ酸の二次凝集物で、
その平均粒径が３μｍのものを使用し、二次凝集の細孔
にインクジェット用インクを取り込むものが最も好まし
いが、これ以外の合成シリカや他の塗工用顔料、例えば
酸化チタン、カオリン、炭酸カルシウム、タルク、プラ
ッスチックピグメント、硫酸バリウム、水酸化アルミな
どを適宜併用しても良い。小麦澱粉を微粒子状の充填剤
として、その平均粒径が２０．２μｍのものを併用する
ことが、再剥離性圧着層の表面を二つのピークの異なる
凹凸状態を形成し、天然ゴムの自着性を面でなく、点接
触させ、耐ブロッキング性と圧着後の再剥離性を付与さ
せることにつながり最も好ましいが、これ以外の澱粉、
例えば馬鈴薯、タピオカ、コーンなどを原料としたもの
でも良い。Synthetic silica is used as a particulate filler. Synthetic silica is a secondary agglomerate of ultrafine hydrous silicic acid in order to efficiently absorb inkjet ink,
It is most preferable to use one having an average particle diameter of 3 μm and incorporate the ink for inkjet into the secondary aggregation pores, but other synthetic silica and other coating pigments such as titanium oxide, kaolin and carbonic acid. Calcium, talc, plastic pigment, barium sulfate, aluminum hydroxide and the like may be appropriately used in combination. When wheat starch is used as a fine-particle filler with an average particle size of 20.2 μm, the surface of the removable pressure-sensitive adhesive layer forms unevenness with two different peaks, and the natural rubber self-adhesive. It is most preferable because it is not a surface but a point contact, and it provides blocking resistance and removability after pressure bonding, but it is most preferable.
For example, potatoes, tapioca, corn or the like may be used as a raw material.
【００４２】上記の感圧接着剤塗工液には各種添加剤を
含有しても良く、塗工時の作業向上のためレベリング剤
や消泡剤・抑泡剤、後加工性を向上させるためにワック
ス類、視感による白色度向上のため蛍光染料、導電性を
付与させるため界面活性剤や無機塩類からなるいわゆる
帯電防止剤などを含有させることができる。その他、必
要に応じて分散剤、印刷適性向上剤、潤滑剤、撥水剤、
浸透剤、増粘剤、老化防止剤、紫外線吸収剤、染料、染
料定着剤、サイズ剤、紙力増強剤、保水剤、消臭剤、防
腐剤、防黴剤等の添加剤なども目的に応じて併用するこ
とが出来る。The above pressure-sensitive adhesive coating liquid may contain various additives, and in order to improve the work during coating, a leveling agent, a defoaming agent / foam suppressor, and a post-processability are improved. In addition, waxes, fluorescent dyes for improving whiteness by visual sense, so-called antistatic agents composed of surfactants and inorganic salts for imparting conductivity can be contained. In addition, if necessary, a dispersant, a printability improver, a lubricant, a water repellent,
Additives such as penetrants, thickeners, anti-aging agents, UV absorbers, dyes, dye fixing agents, sizing agents, paper strengthening agents, water retention agents, deodorants, preservatives, antifungal agents, etc. It can be used together depending on the situation.
【００４３】さらに、印刷強度を向上させる目的におい
て酸化澱粉、ポリビニルアルコール、カルボキシメチル
セルローズ、ヒドロキシエチルセルローズ、大豆蛋白、
合成蛋白、カゼイン等、並びにスチレン・ブタジエン
系、酢酸ビニル系、メチルメタクリレート・ブタジェン
系、アクリルニトリル・ブタジェン系ラテックス等を必
要に応じ含有させることができる。Further, for the purpose of improving the printing strength, oxidized starch, polyvinyl alcohol, carboxymethyl cellulose, hydroxyethyl cellulose, soybean protein,
If necessary, synthetic proteins, casein, etc., and styrene / butadiene-based, vinyl acetate-based, methyl methacrylate-butadiene-based, acrylonitrile-butadiene-based latex and the like can be contained.
【００４４】上記のように調整した感圧接着剤塗工液の
塗工は、エアーナイフコーター、ロールコーター、ブレ
ードコーター、ロッドブレードコーター、バーコータ
ー、ダイコーター等の一般的なコーターによって塗工さ
れるが、塗工量は乾燥重量で３〜１５ｇ／ｍ2の範囲で
調整されるのが望ましい。塗工量を上記範囲に限定した
理由は、３ｇ／ｍ2未満ではインクジェット用インク受
理層且つオフセットインキ受理層として、インクの受容
量が低下し、印字品位や印刷上がりなどの視感的な面で
劣り、更にインクジェット用インクの耐水定着性や感圧
接着剤層としての接着力が低下し、好ましくないためで
ある。また、塗工量が１５ｇ／ｍ2を超えると、印字品
位や印刷上がりなどの視感的な見栄えは向上するが、経
済的な面から実用性が劣り、筆記性が乏しく、紙粉が発
生しやすく、感圧接着層としての接着力が強すぎて印字
面の紙表面破壊を起こし、好ましくないからである。The pressure-sensitive adhesive coating solution prepared as described above is applied by a general coater such as an air knife coater, roll coater, blade coater, rod blade coater, bar coater, die coater or the like. However, it is desirable that the coating amount is adjusted within the range of 3 to 15 g / m 2 in terms of dry weight. The reason why the coating amount is limited to the above range is that when the coating amount is less than 3 g / m 2 , the ink receiving amount decreases as an inkjet ink receiving layer and an offset ink receiving layer, and the visual quality such as print quality and printed quality is reduced. This is because the water resistance of the inkjet ink and the adhesive strength of the pressure-sensitive adhesive layer are reduced, which is not preferable. Further, when the coating amount exceeds 15 g / m 2 , the visual appearance such as print quality and printed quality is improved, but it is economically impractical, poor writability, and paper dust is generated. This is because the pressure-sensitive adhesive layer has an excessively strong adhesive force and the printed surface is destroyed, which is not preferable.
【００４５】オフセット印刷で使用する１％湿し水によ
ってインクジェットインク受理顔料層塗工面及び感圧接
着層塗工面の各々から抽出したカチオン性樹脂と1％湿
し水中のアニオン性物質との凝集物の生成が、1％湿し
水抽出液の濁度測定器による濁度として各々２．０ＨＺ
以下となるように、上記に例示した感圧接着性記録用紙
を作製することで、水性インクを用いる他のペンプロッ
ター等の記録、印刷、筆記に用いることができ、鉛筆や
ボールペン等を用いた筆記が可能で、インクジェット記
録用紙として発色性、耐水性が良く、滲みが少なく、且
つプロセスインキ、ＵＶインキなどによるオフセット印
刷で画像の鮮明で印刷作業性の良好であるという特徴を
持つ感圧接着性記録用紙が得られる。Aggregates of the cationic resin extracted from each of the ink-jet ink-receiving pigment layer coated surface and the pressure-sensitive adhesive layer coated surface with 1% fountain solution used in offset printing and an anionic substance in 1% fountain solution. Of 1% fountain solution extract produced a turbidity of 2.0HZ
As described below, by producing the pressure-sensitive adhesive recording paper exemplified above, it can be used for recording, printing, and writing on other pen plotters using water-based ink, and a pencil or ballpoint pen was used. A pressure-sensitive adhesive with the features that it is writable, has good colorability and water resistance as an inkjet recording paper, has little bleeding, and has clear images and good workability in offset printing with process ink, UV ink, etc. A sex recording sheet is obtained.
【００４６】[0046]
【実施例】本発明を以下の実施例、比較例により更に本
発明を詳細に説明するが、本発明はこれらの例に限定さ
れるものではない。なお、実施例、比較例の重量部数は
すべて固形分換算での数値で示すものとする。The present invention will be described in more detail with reference to the following examples and comparative examples, but the present invention is not limited to these examples. In addition, all parts by weight in Examples and Comparative Examples are shown in terms of solid content.
【００４７】（実施例１)米坪１２７．９ｇ／ｍ2の塗工
原紙に、以下の組成の顔料塗工液を乾燥塗工量が１０ｇ
／ｍ2となるようにマイヤーバーで塗工し、乾燥させオ
フセット印刷可能なインクジェット用インク受理層を作
製した。
＜顔料塗工液＞合成シリカを１００部、水系バインダー
（ポリビニルアルコールとエチレン・酢酸ビニル共重合
物の1：1の混合物）を３０部、カチオン性樹脂として、
ジメチルジアリルアンモニウムクロリド・二酸化イオウ
共重合物を５部とアミン・エピクロロヒドリン縮合物を
５部、ＰＶＡの架橋剤としてポリアミドポリウレア樹脂
を５部の割合で顔料塗工液を調整した。なお、ポリアミ
ドポリウレア樹脂は、ポリビニルアルコール１００部換
算で３３.３部投入されたこととなる。(Example 1) A pigment coating solution having the following composition was applied to a coated base paper having a basis weight of 127.9 g / m 2 in a dry coating amount of 10 g.
/ M 2 was coated with a Meyer bar and dried to prepare an ink jet ink receiving layer capable of offset printing. <Pigment coating liquid> 100 parts of synthetic silica, 30 parts of an aqueous binder (a 1: 1 mixture of polyvinyl alcohol and ethylene / vinyl acetate copolymer), as a cationic resin,
A pigment coating solution was prepared by mixing 5 parts of a dimethyldiallylammonium chloride / sulfur dioxide copolymer, 5 parts of an amine / epichlorohydrin condensate, and 5 parts of a polyamide polyurea resin as a PVA crosslinking agent. The polyamide polyurea resin was added in an amount of 33.3 parts based on 100 parts of polyvinyl alcohol.
【００４８】（実施例２） 水系バインダーを１００部
（ポリビニルアルコールとエチレン・酢酸ビニル共重合
物の1：1の混合物）、ジメチルジアリルアンモニウムク
ロリド・二酸化イオウ共重合物を３０部、アミン・エピ
クロロヒドリン縮合物を３０部、ＰＶＡの架橋剤として
ポリアミドポリウレア樹脂を５０部とした以外は、実施
例１と同様にしてオフセット印刷可能なインクジェット
用インク受理層を作製した。Example 2 100 parts of an aqueous binder (1: 1 mixture of polyvinyl alcohol and ethylene / vinyl acetate copolymer), 30 parts of dimethyldiallylammonium chloride / sulfur dioxide copolymer, amine / epichloro. An ink jet ink-receiving layer capable of offset printing was prepared in the same manner as in Example 1 except that 30 parts of the hydrin condensate and 50 parts of the polyamide polyurea resin as the PVA crosslinking agent were used.
【００４９】（実施例３) ジメチルジアリルアンモニウ
ムクロリド・二酸化イオウ共重合物を４部、アミン・エ
ピクロロヒドリン縮合物を４部とした以外は、実施例１
と同様にしてインク受理層を作製した。Example 3 Example 1 was repeated except that 4 parts of dimethyldiallylammonium chloride / sulfur dioxide copolymer and 4 parts of amine / epichlorohydrin condensate were used.
An ink receiving layer was prepared in the same manner as in.
【００５０】（比較例１） 水系バインダーを２５部
（ポリビニルアルコールとエチレン・酢酸ビニル共重合
物の1：1の混合物）とした以外は、実施例１と同様にし
てインク受理層を作製した。Comparative Example 1 An ink receiving layer was prepared in the same manner as in Example 1 except that the aqueous binder was 25 parts (a 1: 1 mixture of polyvinyl alcohol and ethylene / vinyl acetate copolymer).
【００５１】（比較例２) ポリアミドポリウレア樹脂を
４部とした以外は、実施例１と同様にしてインク受理層
を作製した。Comparative Example 2 An ink receiving layer was produced in the same manner as in Example 1 except that the polyamide polyurea resin was 4 parts.
【００５２】（比較例３) ジメチルジアリルアンモニウ
ムクロリド・二酸化イオウ共重合物を３５部、アミン・
エピクロロヒドリン縮合物を３０部とした以外は、実施
例２と同様にしてインク受理層を作製した。Comparative Example 3 35 parts of a dimethyldiallylammonium chloride / sulfur dioxide copolymer, amine.
An ink receiving layer was produced in the same manner as in Example 2 except that the epichlorohydrin condensate was changed to 30 parts.
【００５３】（比較例４） 水系バインダーを１１０部
（ポリビニルアルコールとエチレン・酢酸ビニル共重合
物の1：1の混合物）とした以外は、実施例２と同様にし
てインク受理層を作製した。Comparative Example 4 An ink receiving layer was prepared in the same manner as in Example 2 except that the amount of the aqueous binder was 110 parts (a 1: 1 mixture of polyvinyl alcohol and ethylene / vinyl acetate copolymer).
【００５４】（比較例５） ポリアミドポリウレア樹脂
を２７.５部とした以外は、実施例２と同様にしてイン
ク受理層を作製した。Comparative Example 5 An ink receiving layer was prepared in the same manner as in Example 2 except that the polyamide polyurea resin was 27.5 parts.
【００５５】[0055]
【表１】 [Table 1]
【表２】 [Table 2]
【００５６】水系バインダーとしてポリビニルアルコー
ルとスチレン・ブタジエン系エマルジョン、あるいはポ
リビニルアルコールとアクリル・ブタジエン系エマルジ
ョンを用いた場合においても、上記実施例と同様の結果
を得た。When polyvinyl alcohol and styrene-butadiene emulsion or polyvinyl alcohol and acrylic-butadiene emulsion were used as the water-based binder, the same results as in the above examples were obtained.
【００５７】（実施例４)米坪１２７．９ｇ／ｍ2の塗工
原紙に、下記の感圧接着剤塗工液を乾燥塗工量が１０ｇ
／ｍ2となるようにマイヤーバーで塗工し、乾燥させて
オフセット印刷可能なインクジェット用インク受理感圧
接着層を作製した。
＜感圧接着塗工液＞合成シリカを１００部、天然ゴム系
エマルジョンを８０部、スチレン・ブタジエン系エマル
ジョンを２０部、澱粉粒子を９０部、アミン・エピクロ
ロヒドリン縮合樹脂を５部の割合で感圧接着塗工液を調
整した。Example 4 A coating base paper having a surface area of 127.9 g / m 2 was coated with the following pressure-sensitive adhesive coating solution at a dry coating amount of 10 g.
The pressure-sensitive adhesive layer for ink-jet ink-jet printing capable of offset printing was prepared by coating with a Meyer bar so as to be / m 2 and drying. <Pressure-sensitive adhesive coating liquid> 100 parts of synthetic silica, 80 parts of natural rubber emulsion, 20 parts of styrene-butadiene emulsion, 90 parts of starch particles, 5 parts of amine-epichlorohydrin condensation resin The pressure-sensitive adhesive coating liquid was adjusted with.
【００５８】（実施例５）アミン・エピクロロヒドリン
縮合物を８０部とした以外は、実施例４と同様にして、
オフセット印刷可能なインクジェット用インク受理感圧
接着層を作製した。Example 5 The procedure of Example 4 was repeated except that the amount of the amine-epichlorohydrin condensate was changed to 80 parts.
An ink jet pressure-sensitive adhesive layer for inkjet printing capable of offset printing was prepared.
【００５９】（実施例６）アミン・エピクロロヒドリン
縮合物を３部とした以外は、実施例４と同様にして、イ
ンク受理感圧接着層を作製した。Example 6 An ink-receiving pressure-sensitive adhesive layer was produced in the same manner as in Example 4 except that the amine-epichlorohydrin condensate was 3 parts.
【００６０】（比較例６）アミン・エピクロロヒドリン
縮合物を８５部とした以外は、実施例４と同様にして、
インク受理感圧接着層を作製した。(Comparative Example 6) The procedure of Example 4 was repeated except that the amount of the amine-epichlorohydrin condensate was changed to 85 parts.
An ink receiving pressure sensitive adhesive layer was prepared.
【００６１】上記実施例及び各比較例に従って作製した
感圧接着性記録用紙の、顔料塗工面側となるインク受理
層及び、感圧接着面側となるインク受理可能な感圧接着
層について、インクの印字品位、圧着後の剥離強度、耐
水性、インクの転写、湿し水白濁試験、オフセット印刷
適性の各性能試験を行なった。表１に顔料塗工液の配合
を示し、表２に顔料塗工面側となるインク受理層の各実
施例及び各比較例における各性能試験の結果を示す。表
３に感圧接着塗工液の配合を示し、表４にインク受理可
能な感圧接着層の各実施例及び各比較例における各性能
試験の結果を示す。For the pressure-sensitive adhesive recording papers prepared according to the above-mentioned Examples and Comparative Examples, the ink receiving layer on the pigment coated surface side and the ink-acceptable pressure-sensitive adhesive layer on the pressure-sensitive adhesive surface side were used. Each of the performance tests such as the printing quality, peel strength after pressure bonding, water resistance, ink transfer, dampening water turbidity test, and offset printing suitability was performed. Table 1 shows the composition of the pigment coating liquid, and Table 2 shows the results of each performance test of each example and each comparative example of the ink receiving layer on the pigment coated surface side. Table 3 shows the composition of the pressure-sensitive adhesive coating liquid, and Table 4 shows the results of each performance test in each Example and each Comparative Example of the ink-acceptable pressure-sensitive adhesive layer.
【００６２】以下に、各性能試験の方法とその評価の仕
方を示す。
（１）１％湿し水による抽出液の濁度
支持体の一方の面にインクジェットインク受理顔料層を
設け、支持体の他方の面に通常状態では粘着性、接着性
を示さず、加圧時に接着性を示し、接着後に剥離可能で
ある感圧接着層を設けた感圧接着性記録用紙において、
オフセット印刷で使用する１％湿し水によって前記イン
クジェットインク受理顔料層塗工面及び前記感圧接着層
塗工面の各々から抽出したカチオン性樹脂と該1％湿し
水中のアニオン性物質との凝集物の生成量を測定する濁
度濁度測定法、あるいは支持体の両面に通常状態では粘
着性、接着性を示さず、加圧時に接着性を示し、接着後
に剥離可能である感圧接着層を設けた感圧接着性記録用
紙において、オフセット印刷で使用する１％湿し水によ
って前記感圧接着層塗工面の一方の面から抽出したカチ
オン性樹脂と該1％湿し水中のアニオン性物質との凝集
物の生成生成量を測定する濁度濁度測定法は、次の通り
である。オフセット印刷時の紙面からのカチオン性樹脂
の溶出による湿し水の汚れを推定する手段として、下記
のような評価方法を用いた。試料５ｃｍ×５ｃｍ紙片４
枚を用意し、両面塗工紙の場合は２枚に剥がした。塗工
面が湿し水と接触するように、まず試料の塗工面が表に
なるように中心から1回折り、開放している３辺も1回折
り曲げた。その試料４枚を、温度２０℃及び５０ｇの濃
度１％の湿し水に浸漬し、1分後の湿し水の濁度（ヘイ
ズ、HZ）を色差・濁度測定器ＣＯＨ−３００Ａ型（日本
電色工業株式会社製）により測定した。The method of each performance test and the method of evaluation will be shown below. (1) Turbidity of extract with 1% fountain solution An inkjet ink-receiving pigment layer is provided on one side of a support, and the other side of the support does not exhibit tackiness or adhesiveness under normal conditions and is pressed. In a pressure-sensitive adhesive recording paper provided with a pressure-sensitive adhesive layer that exhibits adhesiveness at times and can be peeled off after adhesion,
Aggregates of a cationic resin extracted from each of the ink-jet ink-receiving pigment layer coated surface and the pressure-sensitive adhesive layer coated surface with 1% fountain solution used in offset printing and the 1% fountain solution anionic substance Turbidity turbidity measuring method to measure the production amount of, or a pressure-sensitive adhesive layer on both sides of the support that does not show tackiness or adhesiveness under normal conditions but shows adhesiveness when pressed and can be peeled after adhesion. In the provided pressure-sensitive adhesive recording paper, a cationic resin extracted from one surface of the pressure-sensitive adhesive layer coated surface with 1% dampening water used in offset printing, and an anionic substance in the 1% dampening water. The turbidity turbidity measuring method for measuring the amount of aggregates produced is as follows. The following evaluation method was used as a means for estimating the stain of the dampening water due to the elution of the cationic resin from the paper surface during offset printing. Sample 5 cm x 5 cm Paper piece 4
A sheet was prepared and, in the case of double-sided coated paper, peeled to two sheets. First, the coated surface of the sample was bent once from the center so that the coated surface was in contact with dampening water, and the open three sides were also bent once. The four samples were immersed in dampening water having a concentration of 1% at a temperature of 20 ° C. and 50 g, and the turbidity (haze, HZ) of the dampening water after 1 minute was measured by a color difference / turbidity meter COH-300A type ( It was measured by Nippon Denshoku Industries Co., Ltd.).
【００６３】（２）インクの印字品位
インクジェットプリンター（ヒューレットパッカード社
製ＨＰ ＤｅｓｋＪｅｔ５６０Ｊ）のインクカートリッ
ジにサイテックス１０４０黒インクを注射器で注入し、
圧着面にテスト印字パターン（文字、線、ベタ）を印字
し、視感で評価した。鮮明な画像、印字が得られたもの
から◎、○、△、×とした。(2) Ink Printing Quality Inject ink into the ink cartridge of an ink jet printer (HP DeskJet 560J manufactured by Hewlett Packard) with SITEX 1040 black ink with a syringe.
A test print pattern (characters, lines, solid) was printed on the pressure-bonded surface and evaluated visually. It was evaluated as ⊚, ◯, Δ, and x from the one that gave a clear image and print.
【００６４】（３）耐水性（流水法）
インクジェットプリンター（ヒューレットパッカード社
製ＨＰ ＤｅｓｋＪｅｔ５６０Ｊ）のインクカートリッ
ジにサイテックス１０４０黒インクを注射器で注入し、
宛名面、圧着面にベタ印字を行なう。次に水をはった容
器に水を注ぎながら、テスト印字パターン（ベタ部）を
印字面が水に接するように浮かべ、５分間後のインク濃
度及び滲みを視感で評価した。画像、印字に滲み、イン
クの溶出の全くないものから◎、○、△、×とした。(3) Water resistance (flowing water method) Cytex 1040 black ink was injected into an ink cartridge of an ink jet printer (HP DeskJet560J manufactured by Hewlett-Packard Co.) with a syringe,
Solid printing is performed on the address surface and the pressure bonding surface. Next, while pouring water into a container filled with water, the test print pattern (solid portion) was floated so that the print surface was in contact with water, and the ink density and bleeding after 5 minutes were visually evaluated. Images, bleeding, and no ink elution were evaluated as ⊚, ○, Δ, and x.
【００６５】（４）耐水性（泣き出し法）
インクジェットプリンター（ヒューレットパッカード社
製ＨＰ ＤｅｓｋＪｅｔ５６０Ｊ）のインクカートリッ
ジにサイテックス１０４０黒インクを注射器で注入し、
宛名面、圧着面にベタ印字を行なう。次に濾紙を水に漬
けた後、余分な水分を別紙に取らせ、この濾紙を印字面
に当てて丸型プレス機で２ｋｇ／ｃｍ2 を５秒間かけた
後、濾紙に転写されたインク濃度及び滲みを視感で評価
した。画像、印字に滲み、インクの溶出の全くないもの
から◎、○、△、×とした。(4) Water resistance (weeping method) Cytex 1040 black ink was injected into an ink cartridge of an ink jet printer (HP DeskJet 560J manufactured by Hewlett Packard) with a syringe,
Solid printing is performed on the address surface and the pressure bonding surface. Next, after immersing the filter paper in water, the excess water is taken up on a separate paper, the filter paper is applied to the printing surface, and 2 kg / cm2 is applied for 5 seconds with a round press machine. The bleeding was visually evaluated. Images, bleeding, and no ink elution were evaluated as ⊚, ○, Δ, and x.
【００６６】（５）再剥離強度
感圧接着性記録用紙を葉書の大きさにカットし、圧着面
を内側に折り込み、ロール加圧により圧着し、その圧着
力を測定する。また、圧着面にＵＶ照射（オゾン発生水
銀ランプ 型ＧＳ ＨＩ−２０Ｎ ２０００Ｗ、ＵＶラ
ンプと紙との距離２７ｃｍ、照射時間０．５７秒）後、
葉書の大きさにカットし、圧着面を内側に折り込み、ロ
ール加圧により圧着し、その圧着力を測定する。ロール
加圧には、ドライシーラーＰＲＥＳＳＬＥ ｅｃｏｎｏ
（トッパン・フォームズ株式会社製）を使用した。ロー
ル加圧は、幅１０ｃｍの試料をロールシーラーのギャッ
プ約１３０μｍの条件でローラー処理を行なう。各実施
例及び各比較例の感圧接着性記録用紙は上記の条件でロ
ール圧着を行なう。本作業は迅速に行い、試料はポリ袋
に密封保存するため、試料は実機製造時の水分を維持し
ているものとする。次に２３℃、５０％ＲＨの環境下で
ストログラフＭ−１型（東洋精機製作所製）で速度３０
０ｍｍ／分、剥離角９０度（Ｔ型剥離）で剥離し、その
抵抗値を測定する。試料は幅１０ｃｍの中央部を２５ｍ
ｍ巾に断裁して測定し、数値を平均して圧着力ｇｆ／２
５ｍｍを求める。剥離可能な圧着力とは、望ましくはＵ
Ｖ照射後、６０〜１２０ｇｆ／２５ｍｍである。これよ
り高いと剥離する場合に紙面が破れるなどのトラブルが
発生しやすく、低いと配達中などに剥離してしまうなど
のトラブルが発生しやすい。(5) Removability Strength Pressure-sensitive adhesive recording paper is cut into a postcard size, the pressure-bonding surface is folded inward, pressure is applied by roll pressure, and the pressure-bonding force is measured. After UV irradiation (ozone generating mercury lamp type GS HI-20N 2000W, distance between UV lamp and paper 27 cm, irradiation time 0.57 seconds),
Cut to the size of a postcard, fold the crimping surface inward, pressurize by roll pressure, and measure the crimping force. For roll press, dry sealer PRESLE econo
(Manufactured by Toppan Forms Co., Ltd.) was used. For roll pressing, a sample having a width of 10 cm is subjected to roller treatment under the condition that the gap of the roll sealer is about 130 μm. The pressure-sensitive adhesive recording papers of Examples and Comparative Examples are roll-pressed under the above conditions. This work is done promptly, and the sample is sealed and stored in a plastic bag, so the sample is assumed to maintain the water content at the time of manufacturing. Next, at a temperature of 23 ° C and 50% RH, use a Strograph M-1 type (manufactured by Toyo Seiki Seisakusho) at a speed of 30.
Peeling is performed at 0 mm / min and a peeling angle of 90 degrees (T-type peeling), and the resistance value is measured. The sample has a width of 10 cm and a central part of 25 m
Measured by cutting to m width, and averaging the numerical values for crimping force gf / 2
Determine 5 mm. The peelable pressure is preferably U
After V irradiation, it is 60 to 120 gf / 25 mm. If it is higher than this, troubles such as tearing of the paper surface are likely to occur when peeling, and if it is lower, troubles such as peeling during delivery tend to occur.
【００６７】（６）再剥離後のインクの転写
圧着面にＵＶ照射（オゾン発生水銀ランプ 型ＧＳ Ｈ
Ｉ−２０Ｎ ２０００Ｗ、ＵＶランプと紙との距離２７
ｃｍ、照射時間０．５７秒）後、インクジェットプリン
ター（ヒューレットパッカード社製ＨＰ ＤｅｓｋＪｅ
ｔ５６０Ｊ）のインクカートリッジにサイテックス１０
４０黒インクを注射器で注入し、圧着面にテスト印字パ
ターン（文字）を試料の左半面に印字する。圧着面を内
側に折り込み、剥離強度が３０〜５０ｇｆ／２５ｍｍと
なるような条件を設定し、ドライシーラードライシーラ
ーＰＲＥＳＳＬＥ ｅｃｏｎｏ（トッパン・フォームズ
株式会社製）を使用してロール加圧を行い、手で再剥離
させ、圧着面の右半面に転写したインクの濃度を視感で
評価した。インク写りが全くなくて、対向面がきれいな
ままのものを◎、かすかにインク写りするものを○、イ
ンク写りするが対向面の情報の判読に支障のないものを
△、インク写りがひどく、対向面の情報の判読が困難な
ものを×とした。(6) Transfer of ink after re-peeling UV irradiation (ozone generation mercury lamp type GSH
I-20N 2000W, distance between UV lamp and paper 27
cm, irradiation time 0.57 seconds), and then an inkjet printer (HP DeskJe manufactured by Hewlett Packard).
CYTEX 10 in the ink cartridge of t560J)
40 black ink is injected with a syringe, and a test print pattern (characters) is printed on the pressure-bonded surface on the left half surface of the sample. Fold the pressure-bonded surface inward, set the conditions such that the peel strength is 30 to 50 gf / 25 mm, and roll-press by using a dry sealer PRESELE econo (manufactured by Toppan Forms Co., Ltd.) by hand. The density of the ink re-peeled and transferred to the right half surface of the pressure-bonded surface was visually evaluated. If there is no ink reflection and the opposite surface remains clean, ◎, if there is a slight ink reflection, ○, if there is ink reflection but it does not interfere with the reading of the information on the opposite surface, △, the ink reflection is severe When the information on the surface was difficult to read, it was marked with x.
【００６８】（７）オフセット印刷適性
ＲＩ−３型印刷適性試験機（明製作所製）を使用して耐
刷力を評価した。インクはプロセスインク（東洋インキ
製造社製、ＰＲＩＮＴＩＮＧ ＩＮＫ、墨、ＳＭＸ、Ｔ
Ｖ−１５）を０．４ｃｃ、印刷速度：６０ｒｐｍ、印
圧：８．５ｍｍ、４回刷りとした。視感で評価し、イン
キによる塗工層剥け、紙剥けなどが全くないものから
◎、○、△、×とした。(7) Offset printability The printing durability was evaluated using a RI-3 type printability tester (manufactured by Akira Seisakusho). Ink is process ink (made by Toyo Ink Mfg. Co., Ltd., PRINTING INK, black ink, SMX, T
V-15) was 0.4 cc, the printing speed was 60 rpm, the printing pressure was 8.5 mm, and the printing was performed four times. It was evaluated visually and evaluated as ⊚, ◯, Δ, and x from the fact that the coating layer was not peeled off by ink and the paper was not peeled off.
【００６９】[0069]
【表３】 [Table 3]
【表４】 [Table 4]
【００７０】表２から明らかのように、湿し水濁度を
２.０ヘイズ以下とした本発明において得られたオフセ
ット印刷可能なインクジェット用インク受理層の実施例
は比較例に比べ、インクジェット記録における印字性、
耐水性に優れ、湿し水に対するカチオン性樹脂の溶出が
少なく、かつオフセット印刷適性に優れ、要求品質を全
て満足するものである。As is clear from Table 2, the examples of the ink-jet ink-receiving layer capable of offset printing obtained in the present invention in which the dampening water turbidity was 2.0 haze or less were compared with the comparative examples in the ink jet recording. Printability in
It has excellent water resistance, little elution of the cationic resin in dampening water, and excellent offset printing suitability, and satisfies all required quality.
【００７１】表４から明らかのように、湿し水濁度を
２.０ヘイズ以下とした本発明において得られたオフセ
ット印刷可能でインクジェット用インク受理可能な感圧
接着層の実施例は、比較例に比べ、インクジェット記録
における印字性、耐水性に優れ、かつ再剥離後の対向面
へのインク写りがなく、湿し水に対するカチオン性樹脂
の溶出が少なく、かつオフセット印刷適性に優れ、要求
品質を全て満足するものである。As is clear from Table 4, the examples of the offset-printable ink-jet ink-acceptable pressure-sensitive adhesive layer obtained in the present invention having a dampening water turbidity of 2.0 haze or less are compared. Compared to the examples, it has excellent printability and water resistance in ink jet recording, there is no ink transfer to the facing surface after re-peeling, less elution of cationic resin in dampening water, and excellent offset printing suitability. Satisfy all.
【００７２】[0072]
【発明の効果】請求項１記載の発明では、インクジェッ
トインク受理顔料層又は感圧接着層中のカチオン性樹脂
のオフセット印刷時に使用する湿し水への溶出を抑制し
た、すなわち、オフセット印刷で使用する１％湿し水に
よってインクジェットインク受理顔料層塗工面及び感圧
接着層塗工面の各々から抽出したカチオン性樹脂と該1
％湿し水中のアニオン性物質との凝集物の生成が、1％
湿し水抽出液の濁度測定器による濁度として各々２．０
ＨＺ以下とすることで、優れたインクジェット適性を有
し、かつプロセスインキ、ＵＶインキなどを用いること
が可能で優れたオフセット印刷適性を有する主として２
つ折り用のインクジェット用感圧接着性記録用紙を提供
できた。According to the first aspect of the invention, the elution of the cationic resin in the ink jet ink receiving pigment layer or the pressure-sensitive adhesive layer into the fountain solution used in offset printing is suppressed, that is, in the offset printing. And a cationic resin extracted from each of the ink-jet ink-receiving pigment layer coated surface and the pressure-sensitive adhesive layer coated surface with 1% fountain solution.
% Aggregate formation with anionic substances in dampening water, 1%
The turbidity of the dampening water extract measured by the turbidity meter is 2.0
By setting it to HZ or less, it has excellent inkjet suitability, and it is possible to use process ink, UV ink, etc., and also has excellent offset printability.
An inkjet pressure-sensitive adhesive recording paper for folding could be provided.
【００７３】請求項２記載の発明では、感圧接着層中の
カチオン性樹脂のオフセット印刷時に使用する湿し水へ
の溶出を抑制した、すなわち、感圧接着層に起因する前
記凝集物の生成が、濁度として各々２．０ＨＺ以下とす
ることで、優れたインクジェット適性を有し、かつプロ
セスインキ、ＵＶインキなどを用いることが可能で優れ
たオフセット印刷適性を有する主として三つ折り用のイ
ンクジェット用感圧接着性記録用紙を提供できた。According to the second aspect of the invention, the elution of the cationic resin in the pressure-sensitive adhesive layer into the fountain solution used during offset printing is suppressed, that is, the formation of the aggregates due to the pressure-sensitive adhesive layer. However, by setting the turbidity to 2.0 HZ or less, it has excellent inkjet suitability, and it is possible to use process ink, UV ink, etc., and has excellent offset printing suitability, mainly for tri-fold inkjet A pressure sensitive adhesive recording paper could be provided.
【００７４】請求項３記載の発明では、インクジェット
インク受理顔料層中に合成シリカ、少なくとも１種類以
上のカチオン性樹脂、及び少なくとも２種類以上の水系
バインダーを含有させ、かつカチオン性樹脂の総部数が
乾燥重量部で合成シリカ１００部に対して１０〜６０部
であり、水系バインダーの総部数が乾燥重量部で合成シ
リカ１００部に対して３０〜１００部としたので、イン
クジェット記録方式においてより優れた発色を有し、滲
みが少なく、かつ高耐水性のオフセット印刷可能なイン
クジェット用感圧接着性記録用紙を提供することができ
た。According to the third aspect of the invention, the ink-jet ink receiving pigment layer contains synthetic silica, at least one or more kinds of cationic resins, and at least two or more kinds of water-based binders, and the total number of cationic resins is at least one. Since it is 10 to 60 parts by weight based on 100 parts by weight of synthetic silica and the total number of aqueous binders is 30 to 100 parts by weight based on 100 parts by weight of synthetic silica, it is more excellent in the inkjet recording method. It was possible to provide a pressure-sensitive adhesive recording paper for inkjet which has color development, little bleeding, and high water resistance and which enables offset printing.
【００７５】さらに請求項４記載の発明では、カチオン
性樹脂としてアミン・エピクロロヒドリン縮合樹脂及び
ジメチルジアリルアンモニウムクロリド・二酸化イオウ
共重合物を含有させたものを使用し、水系バインダーと
してポリビニルアルコールとエチレン・酢酸ビニル共重
合物、あるいはポリビニルアルコールとスチレン・ブタ
ジエン系エマルジョン、あるいはポリビニルアルコール
とアクリル・ブタジエン系エマルジョンを含有させたも
のを使用することにより、発色性、滲み、耐水性の観点
からさらに優れたものとすることができた。Further, in the invention according to claim 4, a resin containing an amine / epichlorohydrin condensation resin and a dimethyldiallylammonium chloride / sulfur dioxide copolymer is used as the cationic resin, and polyvinyl alcohol is used as the aqueous binder. Use of ethylene / vinyl acetate copolymer, polyvinyl alcohol and styrene / butadiene emulsion, or polyvinyl alcohol and acrylic / butadiene emulsion is more excellent from the viewpoint of color development, bleeding and water resistance. Could be
【００７６】請求項５記載の発明では、水系バインダー
にポリビニルアルコールを含有させ、かつインクジェッ
トインク受理顔料層中に、ポリアミドポリウレア樹脂を
そのポリビニルアルコール１００重量部に対して５〜５
０重量部含有させることで、ポリアミドポリウレア樹脂
をポリビニルアルコールの架橋剤として作用させてイン
クジェットインク受理顔料層の耐水性を向上させること
ができた。これにより、インクジェット用インクによる
ポリビニルアルコールの乾燥被膜の膨潤を抑え、インク
ジェット用インク受理層の耐水性をより改善すると共
に、プロセスインキ、ＵＶインキなどによるオフセット
印刷の際に、湿し水によるポリビニルアルコールの乾燥
被膜の膨潤を押さえ、インクジェット用インク受理層か
らのカチオン性物質の湿し水への溶出を防止し、印刷適
性を改善することができた。In the invention according to claim 5, polyvinyl alcohol is contained in the aqueous binder, and the polyamide polyurea resin is contained in the ink-jet ink-receiving pigment layer in an amount of 5 to 5 with respect to 100 parts by weight of the polyvinyl alcohol.
By containing 0 parts by weight, the polyamide polyurea resin could act as a cross-linking agent for polyvinyl alcohol to improve the water resistance of the inkjet ink-receiving pigment layer. Thereby, the swelling of the dry film of polyvinyl alcohol by the inkjet ink is suppressed, the water resistance of the inkjet ink receiving layer is further improved, and the polyvinyl alcohol by the dampening water is used in the offset printing with the process ink or UV ink. It was possible to suppress swelling of the dry film of (4), prevent elution of the cationic substance from the ink jet ink-receiving layer into the fountain solution, and improve printability.
【００７７】請求項６記載の発明では、感圧接着層に、
合成シリカ、天然ゴム系エマルジョン、合成ゴム系エマ
ルジョン及びカチオン性樹脂を含有させ、かつ感圧接着
層に、乾燥重量部で合成シリカ１００部に対して５〜８
０重量部のカチオン性樹脂であるアミン・エピクロロヒ
ドリン縮合物を含有させることで、もっとも効果的にシ
リカ系顔料をそのカチオン性によりカチオン活性させア
ニオン性を有するインクジェット用インクをイオン結合
により定着させて、水性インクの耐水性を付与すること
ができた。According to the invention of claim 6, the pressure-sensitive adhesive layer comprises:
Synthetic silica, natural rubber emulsion, synthetic rubber emulsion, and cationic resin are contained, and the pressure-sensitive adhesive layer has a dry weight part of 5 to 8 per 100 parts of synthetic silica.
By including 0 part by weight of a cationic resin, an amine-epichlorohydrin condensate, a silica pigment is most effectively cationically activated by its cationic property and an anionic inkjet ink is fixed by ionic bonding. Thus, the water resistance of the water-based ink could be imparted.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｊ 107/02 Ｃ０９Ｊ 109/10 ４Ｌ０５５ 109/10 179/02 179/02 Ｄ２１Ｈ 19/62 Ｄ２１Ｈ 19/62 Ｂ４１Ｊ 3/04 １０１Ｙ (72)発明者 数森 康二 新潟県長岡市西蔵王３−５−１北越製紙株 式会社研究所内 (72)発明者 長谷川 篤 新潟県長岡市西蔵王３−５−１北越製紙株 式会社研究所内 Ｆターム(参考） 2C005 WA03 2C056 FC06 2H086 BA15 BA24 BA33 BA35 BA37 BA41 4J004 AA04 AA05 AA11 AA13 AA16 AB01 CA02 CB02 CC03 EA06 FA01 4J040 CA011 CA031 EC012 EG002 EH012 GA13 HA126 HA306 JA03 JA09 JB09 KA03 KA23 KA42 KA43 LA05 LA06 LA08 MA09 MB03 NA10 PA23 PA33 4L055 AG09 AG18 AG47 AG52 AG59 AG63 AG64 AG65 AG76 AG80 AG87 AG89 AH02 AH37 AH49 AH50 AJ04 BE08 EA19 EA32 FA15 GA09 GA50 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) C09J 107/02 C09J 109/10 4L055 109/10 179/02 179/02 D21H 19/62 D21H 19/62 B41J 3/04 101Y (72) Inventor Koji Kazumori 3-5-1 Nishizao, Nagaoka City, Niigata Prefecture Hokuetsu Paper Mills Ltd. (72) Inventor Atsushi Hasegawa 3-5-1 Nishizao, Nagaoka City, Niigata Prefecture Hokuetsu Paper Mill Incorporated company F-term in the laboratory (reference) 2C005 WA03 2C056 FC06 2H086 BA15 BA24 BA33 BA35 BA37 BA41 4J004 AA04 AA05 AA11 AA13 AA16 AB01 CA02 CB02 CC03 EA06 FA01 4J040 CA011 CA031 EC032 EC02 EH012 GA42 HA03 B093 LA06 LA08 MA09 MB03 NA10 PA23 PA33 4L055 AG09 AG18 AG47 AG52 AG59 AG63 AG64 AG65 AG76 AG80 AG87 AG89 AH02 AH37 AH49 AH50 AJ04 BE08 EA19 EA32 FA15 GA0 9 GA50
Claims (6)
受理顔料層を設け、支持体の他方の面に通常状態では粘
着性、接着性を示さず、加圧時に接着性を示し、接着後
に剥離可能である感圧接着層を設けた感圧接着性記録用
紙において、 オフセット印刷で使用する１％湿し水によって前記イン
クジェットインク受理顔料層塗工面及び前記感圧接着層
塗工面の各々から抽出したカチオン性樹脂と該1％湿し
水中のアニオン性物質との凝集物の生成が、該1％湿し
水抽出液の濁度測定器による濁度として各々２．０ＨＺ
(ヘイズ)以下であることを特徴とするオフセット印刷可
能なインクジェット用感圧接着性記録用紙。1. An ink-jet ink-receiving pigment layer is provided on one surface of a support, and the other surface of the support does not exhibit tackiness or adhesiveness in a normal state but exhibits adhesiveness when pressed and is peeled off after adhesion. In a pressure-sensitive adhesive recording paper provided with a possible pressure-sensitive adhesive layer, the ink-jet ink receiving pigment layer coated surface and the pressure-sensitive adhesive layer coated surface were extracted with 1% fountain solution used in offset printing. The formation of aggregates of the cationic resin and the anionic substance in the 1% fountain solution is 2.0 HZ as the turbidity of the 1% fountain solution extract measured by the turbidity meter.
(Haze) The following pressure-sensitive adhesive recording paper for inkjet recording, which is characterized by having the following:
性を示さず、加圧時に接着性を示し、接着後に剥離可能
である感圧接着層を設けた感圧接着性記録用紙におい
て、 オフセット印刷で使用する１％湿し水によって前記感圧
接着層塗工面の一方の面から抽出したカチオン性樹脂と
該1％湿し水中のアニオン性物質との凝集物の生成が、
該1％湿し水抽出液の濁度測定器による濁度として各々
２．０ＨＺ以下であることを特徴とするオフセット印刷
可能なインクジェット用感圧接着性記録用紙。2. A pressure-sensitive adhesive recording paper provided with a pressure-sensitive adhesive layer on both sides of a support, which does not exhibit tackiness and adhesiveness under normal conditions, exhibits adhesiveness under pressure, and is peelable after adhesion. The formation of aggregates of the cationic resin extracted from one surface of the pressure-sensitive adhesive layer coated surface by the 1% fountain solution used in offset printing and the anionic substance in the 1% fountain solution,
A pressure-sensitive adhesive recording sheet for inkjet printing, wherein the turbidity of the 1% fountain solution extract is 2.0 HZ or less as measured by a turbidity meter.
合成シリカ、少なくとも１種類以上のカチオン性樹脂、
及び少なくとも２種類以上の水系バインダーを含有し、
かつ該カチオン性樹脂の総部数が乾燥重量部で合成シリ
カ１００部に対して１０〜６０部であり、該水系バイン
ダーの総部数が乾燥重量部で合成シリカ１００部に対し
て３０〜１００部であることを特徴とする請求項１記載
のオフセット印刷可能なインクジェット用感圧接着性記
録用紙。3. The ink-jet ink-receiving pigment layer comprises:
Synthetic silica, at least one or more cationic resins,
And containing at least two types of aqueous binders,
The total amount of the cationic resin is 10 to 60 parts by weight based on 100 parts by weight of synthetic silica, and the total number of the aqueous binder is 30 to 100 parts by weight based on 100 parts by weight of synthetic silica. The pressure-sensitive adhesive recording paper for ink jet printing according to claim 1, wherein the offset printing is possible.
ロヒドリン縮合樹脂及びジメチルジアリルアンモニウム
クロリド・二酸化イオウ共重合物を含有し、前記水系バ
インダーは、ポリビニルアルコールとエチレン・酢酸ビ
ニル共重合物、あるいはポリビニルアルコールとスチレ
ン・ブタジエン系エマルジョン、あるいはポリビニルア
ルコールとアクリル・ブタジエン系エマルジョンを含有
することを特徴とする請求項３記載のオフセット印刷可
能なインクジェット用感圧接着性記録用紙。4. The cationic resin contains an amine / epichlorohydrin condensation resin and a dimethyldiallylammonium chloride / sulfur dioxide copolymer, and the aqueous binder is polyvinyl alcohol and ethylene / vinyl acetate copolymer. 4. The pressure-sensitive adhesive recording sheet for inkjet printing according to claim 3, which contains polyvinyl alcohol and styrene-butadiene emulsion or polyvinyl alcohol and acrylic-butadiene emulsion.
ルを含有し、かつ前記インクジェットインク受理顔料層
は、ポリアミドポリウレア樹脂をポリビニルアルコール
１００重量部に対して５〜５０重量部含有することを特
徴とする請求項３又は４記載のオフセット印刷可能なイ
ンクジェット用感圧接着性記録用紙。5. The aqueous binder contains polyvinyl alcohol, and the ink jet ink-receiving pigment layer contains 5 to 50 parts by weight of a polyamide polyurea resin with respect to 100 parts by weight of polyvinyl alcohol. 3. The pressure-sensitive adhesive recording paper for inkjet, which is capable of offset printing according to 3 or 4.
系エマルジョン、合成ゴム系エマルジョン及びカチオン
性樹脂を含有し、かつ前記感圧接着層は、乾燥重量部で
合成シリカ１００部に対して５〜８０重量部のカチオン
性樹脂であるアミン・エピクロロヒドリン縮合物を含有
することを特徴とする請求項１、２、３、４、又は５記
載のオフセット印刷可能なインクジェット用感圧接着性
記録用紙。6. The pressure-sensitive adhesive layer contains synthetic silica, a natural rubber emulsion, a synthetic rubber emulsion and a cationic resin, and the pressure-sensitive adhesive layer is 100 parts by weight of synthetic silica in a dry weight part. 5 to 80 parts by weight of an amine-epichlorohydrin condensate, which is a cationic resin, is contained therein, and the pressure-sensitive inkjet printable pressure-sensitive ink according to claim 1, 2, 3, 4, or 5. Adhesive recording paper.