JP2002317542A - Granitic coating material aggregate, granitic surface finish coating material and granitic finish coating method - Google Patents
Granitic coating material aggregate, granitic surface finish coating material and granitic finish coating methodInfo
- Publication number
- JP2002317542A JP2002317542A JP2001123094A JP2001123094A JP2002317542A JP 2002317542 A JP2002317542 A JP 2002317542A JP 2001123094 A JP2001123094 A JP 2001123094A JP 2001123094 A JP2001123094 A JP 2001123094A JP 2002317542 A JP2002317542 A JP 2002317542A
- Authority
- JP
- Japan
- Prior art keywords
- granite
- coating material
- aggregate
- granitic
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、建築物や構造物な
ど（以下、建築物等という）の表面仕上に使用する御影
石調塗材用骨材及び御影石調表面仕上用塗材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a granite-like coating material used for surface finishing of buildings and structures (hereinafter referred to as buildings, etc.) and a coating material for granite-like surface finishing.
【０００２】[0002]
【従来の技術】建築物等の表面は、その用途や目的に合
わせて砂壁状、スタッコ状、大理石調、御影石調等の種
々の色合い、或いは模様に仕上げられる。近年、マンシ
ョンや商業ビル、あるいは戸建てなどの壁面において
は、より重厚で質感の高い塗装が好まれる傾向にある。2. Description of the Related Art The surface of a building or the like is finished in various colors or patterns such as sand walls, stucco, marble, granite, etc., according to the use and purpose. 2. Description of the Related Art In recent years, there has been a tendency for heavier and higher-quality paint to be applied to wall surfaces of condominiums, commercial buildings, and detached houses.
【０００３】このような要望に応えるべく、従来、塗材
中に天然石粉や着色砂、陶磁器粉等を混入したものを用
いたり、また、吹き付け、ローラー、又は鏝などを用い
た塗装方法の改良といった手段により、塗装面に擬石調
等の質感を醸し出すことが行われている。[0003] In order to respond to such demands, conventionally, natural stone powder, colored sand, ceramic powder and the like are mixed into a coating material, and a coating method using a spray, a roller, a trowel or the like has been improved. By such means, a texture such as pseudo stone tone is applied to the painted surface.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、従来技
術においては、塗材に添加される骨材として、主に寒水
石や硅砂、雲母、などの天然石粉や、又はこれらの表面
を着色したものが使用されているが、これらの骨材はあ
くまでも擬似的に石調を現すべく人為的に配合されたも
のであるため、その質感や重厚感が十分とは言えないも
のであった。However, in the prior art, as the aggregate added to the coating material, natural stone powder such as cold water stone, silica sand, mica or the like, or those whose surface is colored are mainly used. Although they are used, these aggregates are artificially blended to give a pseudo-stone tone to the last, so their texture and profound feeling are not sufficient.
【０００５】また、より一層御影石の質感に近づけるた
めには、その天然石である花崗岩の砕石を骨材として用
いることが考えられる。しかしながら、花崗岩は、透明
性のある石英と白濁した長石と黒色である雲母とが種々
の割合で混在して構成された天然石であるため、該天然
石の砕石をそのまま骨材として用いても、そのような塗
装によって現される色調は常に一定ではないという問題
があった。In order to further bring the texture closer to that of granite, it is conceivable to use crushed granite, which is a natural stone, as an aggregate. However, granite is a natural stone composed of a mixture of transparent quartz, opaque feldspar and black mica in various proportions. There has been a problem that the color tone expressed by such a coating is not always constant.
【０００６】本発明は、上記の点に鑑みてなされたもの
であり、御影石調の重厚な質感を醸し出すことができ、
また、原料となる花崗岩の組成によっても色調にばらつ
きを生じることのない御影石調塗材用骨材および御影石
調表面仕上用塗材を提供することを課題とする。The present invention has been made in view of the above points, and can provide a granite-like solid texture.
It is another object of the present invention to provide a granite-like coating material and a granite-like surface finishing coating material that do not vary in color tone even by the composition of granite as a raw material.
【０００７】[0007]
【課題を解決するための手段】本発明は、上記課題を解
決するためになされたものであり、その解決手段は、花
崗岩の砕石からなる骨材本体の表面が、合成樹脂溶液中
に顔料トナーが分散されてなる塗料で着色されたことを
特徴とする御影石調塗材用骨材にある。Means for Solving the Problems The present invention has been made to solve the above-mentioned problems, and the means for solving the problems is that the surface of the aggregate body made of crushed granite is prepared by adding pigment toner in a synthetic resin solution. And a pigment for granite-like coating material characterized by being colored with a paint in which is dispersed.
【０００８】骨材本体として花崗岩の砕石をそのまま骨
材として用いることにより、花崗岩の成分として含まれ
る石英、長石、雲母の自然な質感をそのまま御影石の質
感として表すことができ、また、該骨材本体の表面を着
色することによってその色合いを調整することができる
ため、花崗岩の成分組成の変化による色調のばらつきを
抑え、安定した色合いを得ることができる。[0008] By using granite crushed stone as the aggregate as the aggregate body as it is, the natural texture of quartz, feldspar, and mica contained as a component of the granite can be directly expressed as the texture of granite. Since the color can be adjusted by coloring the surface of the main body, variation in the color tone due to a change in the composition of the granite can be suppressed, and a stable color can be obtained.
【０００９】また、本発明の手段は、斯かる御影石調塗
材用骨材と、乾燥又は硬化後に実質的に無色透明となる
結合材とを含有してなる御影石調表面仕上用塗材にあ
る。Further, the means of the present invention is a granite-like surface finishing coating material comprising such a granite-like coating material aggregate and a binder which becomes substantially colorless and transparent after drying or curing. .
【００１０】結合材が実質的に無色透明であることによ
り、該表面仕上用塗材の塗布面に御影石と同様の深みを
与えることができる。[0010] When the binder is substantially colorless and transparent, it is possible to give the coating surface of the surface finishing coating material the same depth as granite.
【００１１】さらに、本発明の手段は、上記御影石調塗
材用骨材と、乾燥又は硬化後に実質的に無色透明となる
結合材とを配合して御影石調表面仕上用塗材を調製し、
建築物等の内外壁に塗布することを特徴とする御影石調
表面仕上塗装方法にある。Further, the means of the present invention comprises preparing a granite-like surface finishing coating material by blending the above-mentioned aggregate for granite-like coating material and a binder which becomes substantially colorless and transparent after drying or curing.
A granite-like surface finish coating method characterized by being applied to inner and outer walls of a building or the like.
【００１２】[0012]
【発明の実施の形態】以下、本発明について、より詳細
に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail.
【００１３】本発明に斯かる御影石調塗材用骨材は、花
崗岩を解砕して得られた砕石をそのまま骨材本体とし、
さらに該骨材本体の表面を、合成樹脂溶液中に顔料トナ
ーが分散されてなる塗料によって着色したものである。The aggregate for granite-like coating material according to the present invention is a crushed stone obtained by crushing granite as an aggregate body as it is.
Further, the surface of the aggregate main body is colored by a paint in which a pigment toner is dispersed in a synthetic resin solution.
【００１４】着色の際には、骨材本体の表面積１０ｍ2
に対して、合成樹脂の固形分が５〜５０ｇであり且つ顔
料トナーが０．０５〜２ｇとなるような配合の塗料を用
いて行うことが好ましい。顔料トナーの量を２ｇ以上と
すると花崗岩より得られる自然な質感が損なわれ、ま
た、０．０５ｇ以下であれば、花崗岩の組成割合の変動
によって生じる色調の変化を安定させることができず、
好ましくない。At the time of coloring, the surface area of the aggregate body is 10 m 2.
On the other hand, it is preferable to use a paint having a composition such that the solid content of the synthetic resin is 5 to 50 g and the pigment toner is 0.05 to 2 g. When the amount of the pigment toner is 2 g or more, the natural texture obtained from the granite is impaired. When the amount is 0.05 g or less, the change in the color tone caused by the change in the composition ratio of the granite cannot be stabilized,
Not preferred.
【００１５】尚、ここでいう骨材本体の表面積とは、透
過法、吸着法、比濁計法などの直接測定法により測定さ
れた比表面積から算出された値である。例えば、吸着法
のうち、気相法の代表例としてＢＥＴ法を挙げることが
でき、具体的には、直読全自動表面測定装置（ユアサア
イオニクス（株）製、モノソープ）を用い、ＢＥＴ式１
点法（７７Ｋ、Ｎ2吸着）によって容易に測定すること
ができる。Here, the surface area of the aggregate main body is a value calculated from the specific surface area measured by a direct measurement method such as a permeation method, an adsorption method, and a turbidimeter method. For example, among the adsorption methods, a BET method can be cited as a typical example of the gas phase method. Specifically, a direct reading fully automatic surface measuring device (manufactured by Yuasa Ionics Inc., Monosoap) is used, 1
It can be readily determined by the point method (77K, N 2 adsorption).
【００１６】また、花崗岩の砕石の平均粒径は０．５〜
５ｍｍが好ましい。平均粒径が０．５ｍｍより小さくな
ると、塗装面において花崗岩の上記三成分が識別され難
いものとなり、御影石調の質感を現すことができない。
また、平均粒径が５ｍｍより大きくなると、該骨材が収
まるように塗布膜を厚くする必要があり、あるいは吹き
付け用の機器において閉塞等の問題を生じる虞がある。The average particle size of the crushed granite is 0.5 to
5 mm is preferred. When the average particle size is smaller than 0.5 mm, the three components of the granite are difficult to be distinguished on the painted surface, and a granite-like texture cannot be exhibited.
If the average particle size is larger than 5 mm, it is necessary to increase the thickness of the coating film so that the aggregate can be accommodated, or there may be a problem such as blockage in a spraying device.
【００１７】また、塗料を構成する顔料トナーは、耐候
性に優れ、変色、退色の少ない無機系顔料トナーである
ことが好ましい。該無機系顔料トナーとしては、例えば
鉄黒、オーカ、カーボンブラック、ベンガラ、チタン白
等が挙げられる。It is preferable that the pigment toner constituting the coating material is an inorganic pigment toner having excellent weather resistance and little discoloration and fading. Examples of the inorganic pigment toner include iron black, oak, carbon black, red iron, titanium white and the like.
【００１８】また、合成樹脂は、前記骨材本体への付着
強度が高く、被膜が強靭であり、耐候性に優れたもので
あることが好ましい。斯かる合成樹脂としては、例えば
エポキシ系樹脂、アクリル系共重合樹脂、ウレタン系樹
脂を挙げることができ、また、これらの樹脂をシリコン
変性させたものについても使用することができる。ま
た、これらの樹脂は溶媒が飛散した後に被膜化する１液
タイプのものと、使用時に硬化剤と混合することによっ
て反応して硬化する２液タイプのものを使用することが
できる。２液タイプのものとしては、アクリルポリオー
ルに硬化剤としてポリイソシアネートを配合するもの
や、エポキシ樹脂にポリアミンやポリアミドを配合する
ものなどが挙げられる。斯かる合成樹脂を使用すること
によって、機械によるせん断力や骨材同士の衝突による
磨耗に対して強度が増すため、高速攪拌機を使用して塗
材を混練することが可能となり、作業性が良好となる。Further, it is preferable that the synthetic resin has a high adhesion strength to the above-mentioned aggregate main body, a tough film, and excellent weather resistance. Examples of such a synthetic resin include an epoxy resin, an acrylic copolymer resin, and a urethane resin, and those obtained by modifying these resins with silicon can also be used. These resins can be used as a one-pack type resin which forms a film after the solvent is scattered, and a two-pack type resin which reacts and cures by mixing with a curing agent at the time of use. Examples of the two-pack type include those in which a polyisocyanate is blended as a curing agent with an acrylic polyol, and those in which a polyamine or polyamide is blended with an epoxy resin. By using such a synthetic resin, the strength against mechanical shearing force and abrasion due to collision between aggregates is increased, so that it is possible to knead the coating material using a high-speed stirrer, thereby improving workability. Becomes
【００１９】塗料の混合比率は、顔料トナー１重量部に
対して合成樹脂溶液の固形分が２．５〜１０００重量部
であり、好ましくは２５〜１５０重量部である。このよ
うな比率の塗料を用いることにより、花崗岩の砕石から
なる骨材本体の表面を好適に着色することができる。The mixing ratio of the paint is such that the solid content of the synthetic resin solution is 2.5 to 1000 parts by weight, preferably 25 to 150 parts by weight, based on 1 part by weight of the pigment toner. By using a paint having such a ratio, the surface of the aggregate body made of crushed granite can be suitably colored.
【００２０】また、本発明に係る御影石調表面仕上用塗
材は、上述したような御影石調塗材用骨材に、乾燥又は
硬化後に実質的に無色透明となるような結合材を混合し
てなるものである。The coating material for granite-like surface finishing according to the present invention is obtained by mixing the above-mentioned aggregate for granite-like coating material with a binder which becomes substantially colorless and transparent after drying or curing. It becomes.
【００２１】斯かる結合材としては、合成樹脂エマルシ
ョンが好ましい。合成樹脂エマルションは、例えばアク
リル系合成樹脂エマルション、エチレン−酢酸ビニル系
樹脂エマルション、ウレタン系樹脂エマルション、塩化
ビニル系樹脂エマルション等を使用することができる
が、特にイソシアネート基と反応性である水酸基を含む
合成樹脂エマルションに水溶性ポリイソシアネートを配
合してなるものや、エポキシ基を含む合成樹脂エマルシ
ョンにポリアミンやポリアミドを配合してなる２液タイ
プのものは、強靭で且つ速乾性のある塗膜を形成するこ
とが可能となるため、耐摩耗性の必要とされる土間や、
通路等の床面の塗装にも好適に使用することができると
いう点で好ましい。As such a binder, a synthetic resin emulsion is preferable. As the synthetic resin emulsion, for example, an acrylic synthetic resin emulsion, an ethylene-vinyl acetate resin emulsion, a urethane resin emulsion, a vinyl chloride resin emulsion, or the like can be used, and particularly contains a hydroxyl group reactive with an isocyanate group. A two-pack type composition obtained by blending a water-soluble polyisocyanate with a synthetic resin emulsion or a polyamine or polyamide with a synthetic resin emulsion containing an epoxy group forms a tough and quick-drying coating film. Can be used, such as in the dirt where abrasion resistance is required,
It is preferable in that it can be suitably used for painting floor surfaces such as passageways.
【００２２】結合材と骨材との配合割合は、特に限定さ
れるものではないが、御影石の質感により近づけるため
には、前記御影石調塗材用骨材１００重量部に対して結
合材の樹脂の固形分が２〜２０重量部となるように配合
することが好ましい。The mixing ratio of the binder and the aggregate is not particularly limited. However, in order to make the texture of the granite closer to the texture, the resin of the binder is mixed with 100 parts by weight of the aggregate for the granite-like coating material. Is preferably blended so that the solid content of the rubber composition becomes 2 to 20 parts by weight.
【００２３】また、前記御影石調表面仕上用塗材には、
上述した花崗岩砕石からなる骨材本体表面を着色してな
る御影石調塗材用骨材以外にも、従来の他の骨材を混合
することも可能である。但し、御影石の質感を損なわな
いことを考慮すると、前記御影石調塗材用骨材１００重
量部に対して、４００重量部以下とすることが好まし
い。[0023] The granite-like surface finishing coating material includes
In addition to the above-mentioned aggregate for granite-like coating material obtained by coloring the surface of the aggregate main body made of crushed granite, other conventional aggregates can also be mixed. However, considering that the texture of the granite is not impaired, the content is preferably 400 parts by weight or less based on 100 parts by weight of the aggregate for the granite-like coating material.
【００２４】本発明に係る御影石調表面仕上用塗材は、
通常の塗装方法と同様にして、例えば金鏝仕上、吹付仕
上、ローラー仕上などで、塗装対象面上に塗布すること
ができる。また塗装表面を、砂壁状、凹凸状、ゆず肌
状、平滑状などの多様に変化させることによって、建築
石材の表面仕上であるところの本磨き仕上、バーナー仕
上、びしゃん仕上、コブ出し仕上、のみ切り仕上等に酷
似した質感の塗装に仕上げることができる。The granite-like surface finishing coating material according to the present invention comprises:
In the same manner as in a normal coating method, it can be applied to the surface to be coated by, for example, a gold iron finish, a spray finish, a roller finish, or the like. In addition, by changing the painted surface variously, such as sand wall shape, uneven shape, yuzu skin shape, smooth shape, etc., only the final polishing finish, burner finish, bush finish, cobbing finish which is the surface finish of building stone material It is possible to finish the painting with a texture very similar to the cut finish.
【００２５】本発明は、コンクリート、木材、タイル、
石材などの何れにも塗布することができ、建築物等以外
にも、例えば、通路や溝蓋、土間などの床面に対して塗
布することが可能である。The present invention relates to concrete, wood, tile,
It can be applied to any of stone materials and the like, and can be applied to floor surfaces such as passages, gutters, and dirt floors in addition to buildings and the like.
【００２６】[0026]
【実施例】（実施例１）まず、下記表１の材料を混合し
て塗料を調製した。EXAMPLES (Example 1) First, the coating materials were prepared by mixing the materials shown in Table 1 below.
【表１】 次いで、このようにして調製した塗料を、花崗岩砕石
（常陸稲田砕石販売合資会社製、平均粒系３mm）約１０
００ｋｇ（表面積約１００００ｍ2）に添加し、モルタ
ルミキサーで攪拌混合した後、乾燥することにより御影
石調塗材用骨材を作製した。[Table 1] Then, the paint thus prepared was crushed with granite crushed stone (manufactured by Hitachi Inada Crushed Stone Co., Ltd., average grain size: 3 mm) for about 10 minutes.
The resulting mixture was added to 00 kg (surface area: about 10,000 m 2 ), stirred and mixed with a mortar mixer, and dried to prepare an aggregate for a granite-like coating material.
【００２７】（実施例２）下記表２の材料を混合して塗
料を調製する以外は、実施例１と同様にして御影石調塗
材用骨材を作製した。Example 2 An aggregate for a granite-like coating material was prepared in the same manner as in Example 1 except that a coating material was prepared by mixing the materials shown in Table 2 below.
【表２】 [Table 2]
【００２８】（実施例３）下記表３の材料を混合して塗
料を調製する以外は、実施例１と同様にして御影石調塗
材用骨材を作製した。Example 3 An aggregate for a granite-like coating material was prepared in the same manner as in Example 1 except that a coating material was prepared by mixing the materials shown in Table 3 below.
【表３】 [Table 3]
【００２９】以上のようにして作製した実施例１〜３そ
れぞれの御影石調塗材用骨材１０００重量部に対し、ア
クリル樹脂エマルション（旭化成（株）製、ホ゜リトロン E-
316）３００重量部、成膜助剤（テキサノール）２４重量部、
増粘剤（松本油脂製薬株式会社製、マーホ゜ロース゛60MP-400
0）１．０重量部、消泡剤（ヒ゛ックケミーシ゛ャハ゜ン株式会社製、
BYK-022）０．１重量部、水５０重量部、炭酸カルシウ
ム（（株）同和カルファイン製、KS-800）１５０重量部
を混合攪拌して塗材を作製した。An acrylic resin emulsion (available from Asahi Kasei Corporation, Polytron E-) was added to 1000 parts by weight of the granite-like coating material of each of Examples 1 to 3 prepared as described above.
316) 300 parts by weight, 24 parts by weight of a film forming aid (Texanol),
Thickener (Matsuroyu 60MP-400, manufactured by Matsumoto Yushi Seiyaku Co., Ltd.)
0) 1.0 parts by weight, an antifoaming agent (manufactured by Heck Chemie Sharp Co., Ltd.
(BYK-022) 0.1 part by weight, water 50 parts by weight, and calcium carbonate (KS-800, manufactured by Dowa Calfine Co., Ltd.) 150 parts by weight were mixed and stirred to prepare a coating material.
【００３０】上記実施例１〜３の骨材を使用して得られ
たそれぞれの塗材を、口径６ｍｍのリシンガンによって
吹き圧５ｋｇ／ｃｍ2でモルタル板上に吹き付け、塗布
厚４ｍｍの塗膜を形成した。これらの塗膜について色調
と色調の安定性を評価した。結果を表１に示す。Each coating material obtained by using the aggregates of Examples 1 to 3 was sprayed on a mortar plate with a blowing pressure of 5 kg / cm 2 by a ricin gun having a diameter of 6 mm to form a coating film having a coating thickness of 4 mm. Formed. These coating films were evaluated for color tone and color stability. Table 1 shows the results.
【００３１】実施例１の御影石調塗材用骨材を用いた場
合には、花崗岩中に含まれる石英、長石のそれぞれの質
感が残された状態で着色されており、また、骨材による
色ムラもなく色調の安定した良好な塗装が得られた。実
施例２の御影石調塗材用骨材を用いた場合には、安定し
た色調が得られる点で優れているものの、実施例１の骨
材との比較においては、石英の色調と長石の色調とが比
較的似通ったものとなる傾向があった。さらに、実施例
３の御影石調塗材用骨材を用いた場合には、石英や長石
による自然な質感が得られる点で優れているものの、実
施例１の骨材との比較においては、やや色むらの生じや
すい傾向があった。When the granite-like aggregate for the coating material of Example 1 was used, it was colored with the texture of each of the quartz and feldspar contained in the granite remaining. A good coating with stable color tone without unevenness was obtained. When the aggregate for the granite-like coating material of Example 2 was used, it was excellent in that a stable color tone was obtained, but in comparison with the aggregate of Example 1, the color tone of quartz and the color tone of feldspar were used. And tended to be relatively similar. Furthermore, when the aggregate for granite-like coating material of Example 3 was used, although it was excellent in that a natural texture by quartz or feldspar was obtained, it was slightly compared with the aggregate of Example 1. Color unevenness tended to occur.
【００３２】[0032]
【発明の効果】以上のように、本発明に係る御影石調塗
材用骨材および御影石調表面仕上用塗材によれば、御影
石調の重厚な質感を醸し出すことができるとともに、原
料となる花崗岩の組成によっても色調にばらつきを抑
え、安定した御影石調の塗装を得ることができる。As described above, according to the aggregate for the granite-like coating material and the coating material for the granite-like surface finishing according to the present invention, a granite-like solid texture can be produced, and the granite as a raw material can be produced. The variation in the color tone can be suppressed by the composition of the above, and a stable granite-tone coating can be obtained.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｄ 201/00 Ｃ０９Ｄ 201/00 // Ｃ０９Ｃ 1/28 Ｃ０９Ｃ 1/28 3/10 3/10 Ｆターム(参考） 4D075 CA02 CA03 CA47 CB06 CB16 DA06 DA11 DA23 DB12 DB14 DB21 DC02 DC05 EA13 EA43 EB13 EB15 EB19 EB22 EB32 EB33 EB38 EB39 EB43 EB56 EC11 EC13 EC53 EC54 4J037 AA17 EE03 EE28 4J038 KA08 KA15 PB05 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C09D 201/00 C09D 201/00 // C09C 1/28 C09C 1/28 3/10 3/10 F term ( 4D075 CA02 CA03 CA47 CB06 CB16 DA06 DA11 DA23 DB12 DB14 DB21 DC02 DC05 EA13 EA43 EB13 EB15 EB19 EB22 EB32 EB33 EB38 EB39 EB43 EB56 EC11 EC13 EC53 EC54 4J037 AA17 EE03 EE28 4J038KA05
Claims (7)
が、合成樹脂溶液中に顔料トナーが分散されてなる塗料
で着色されたことを特徴とする御影石調塗材用骨材。1. An aggregate for a granite-like coating material, characterized in that the surface of the aggregate body made of crushed granite is colored with a paint in which a pigment toner is dispersed in a synthetic resin solution.
て、前記合成樹脂の固形分が５〜５０ｇであり、且つ前
記顔料トナーが０．０５〜２ｇであることを特徴とする
請求項１記載の御影石調塗材用骨材。2. The synthetic resin has a solid content of 5 to 50 g and a pigment toner of 0.05 to 2 g with respect to a surface area of 10 m 2 of the aggregate main body. The aggregate for the granite-like coating material described.
〜５ｍｍであることを特徴とする請求項１又は２記載の
御影石調塗材用骨材。3. The granite crushed stone has an average particle size of 0.5.
The aggregate for a granite-like coating material according to claim 1 or 2, wherein the size is from 5 to 5 mm.
あることを特徴とする請求項１〜３のいずれかに記載の
御影石調塗材用骨材。4. The aggregate for a granite-like coating material according to claim 1, wherein the pigment toner is an inorganic pigment toner.
リル系共重合樹脂、ウレタン系樹脂のうちいずれか１つ
であることを特徴とする請求項１〜４のいずれかに記載
の御影石調塗材用骨材。5. The granite-like coating according to claim 1, wherein the synthetic resin is any one of an epoxy resin, an acrylic copolymer resin, and a urethane resin. Aggregate for timber.
調塗材用骨材と、乾燥又は硬化後に実質的に無色透明と
なる結合材とを含有してなる御影石調表面仕上用塗材。6. A granite-like surface finish coating comprising the aggregate for granite-like coating material according to claim 1 and a binder which becomes substantially colorless and transparent after drying or curing. Wood.
調塗材用骨材と、乾燥又は硬化後に実質的に無色透明と
なる結合材とを配合して御影石調表面仕上用塗材を調製
し、建築物等の内外壁に塗布することを特徴とする御影
石調表面仕上塗装方法。7. A coating material for granite-like surface finishing by blending the aggregate for granite-like coating material according to claim 1 and a binder which becomes substantially colorless and transparent after drying or curing. A granite-like surface finish coating method, wherein the method is prepared and applied to the inner and outer walls of a building or the like.