GB981143A - Ferromagnetic ferrite materials for use at microwave frequencies - Google Patents
Ferromagnetic ferrite materials for use at microwave frequenciesInfo
- Publication number
- GB981143A GB981143A GB626363A GB626363A GB981143A GB 981143 A GB981143 A GB 981143A GB 626363 A GB626363 A GB 626363A GB 626363 A GB626363 A GB 626363A GB 981143 A GB981143 A GB 981143A
- Authority
- GB
- United Kingdom
- Prior art keywords
- sintering
- tio
- components
- hours
- niofe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
981,143. Magnetic compositions. STANDARD TELEPHONES & CABLES Ltd. Feb. 15, 1963 [Feb. 22, 1962; Jan. 23, 1963], No. 6263/63. Heading H1H. A ferromagnetic ferrite material of spinel crystal structure and suitable for microwave devices requiring stable thermal properties has the formula where x+y= 100 and 0.5 # y # 90, and L and Q represent one or more of the bivalent metals Fe<SP>**</SP>, Mn<SP>**</SP>, Co<SP>**</SP>, Ni<SP>**</SP>, Mg<SP>**</SP>, Zn<SP>**</SP>, R represents one or more of the trivalent metals Fe<SP>***</SP>, Cr<SP>***</SP>, Al<SP>***</SP>, Ga<SP>***</SP>, Mn<SP>***</SP>, Ti is quadrivalent titanium, and Fe 2 O comprises at least ¥ of the R 2 O 3 . Essentially the material is a solid solution of the two components (LOR 2 O 3 ) and (TiO 2 2QO), both of which have similar spinel crystal structures, and is preferably made by sintering a mixture of these two components in powdered form. The two components may each have undergone a presintering in air at 1000‹ C. for an hour prior to the main sintering. The main sintering, which is carried out after the powder mixture has been pressed into shape, comprises a slow rise in temperature to 800‹ C. over several hours, 4 to 5 hours at 1200‹ C. and slow cooling over 20 hours, all in O 2 . The alternative process of sintering from the constituent metal oxides is also envisaged. Specific examples disclosed are 70(NiOFe 2 O 3 ) + 30(TiO 2 2ZnO), 90(NiOFe 2 O 3 ) + 10(TiO 2 2MgO), 90(0.92MgO, 0.18- MnO, 0.90Fe 2 O 2 ) + 10(T 1 O 2 . 2ZnO). The material may be used in a Faraday rotator and in a phase-shifter where a constant phase-shift over the temperature range 0-120‹ C. may be obtained.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR888809A FR1323583A (en) | 1962-02-22 | 1962-02-22 | Ferromagnetic materials and manufacturing methods |
FR922334A FR1354231A (en) | 1962-02-22 | 1963-01-23 | Ferromagnetic materials and manufacturing methods |
Publications (1)
Publication Number | Publication Date |
---|---|
GB981143A true GB981143A (en) | 1965-01-20 |
Family
ID=26194494
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB626363A Expired GB981143A (en) | 1962-02-22 | 1963-02-15 | Ferromagnetic ferrite materials for use at microwave frequencies |
Country Status (5)
Country | Link |
---|---|
BE (1) | BE628751A (en) |
CH (1) | CH448294A (en) |
FR (2) | FR1323583A (en) |
GB (1) | GB981143A (en) |
NL (1) | NL289192A (en) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR1430189A (en) * | 1964-12-29 | 1966-03-04 | Lignes Telegraph Telephon | Ferromagnetic materials and processes for their manufacture |
DE1276534B (en) * | 1965-05-10 | 1968-08-29 | Philips Patentverwaltung | Process for the production of a ferromagnetic ferrite material with a hexagonal crystal structure |
-
1962
- 1962-02-22 FR FR888809A patent/FR1323583A/en not_active Expired
-
1963
- 1963-01-23 FR FR922334A patent/FR1354231A/en not_active Expired
- 1963-02-15 GB GB626363A patent/GB981143A/en not_active Expired
- 1963-02-19 NL NL289192D patent/NL289192A/xx unknown
- 1963-02-22 CH CH227063A patent/CH448294A/en unknown
- 1963-02-22 BE BE628751D patent/BE628751A/xx unknown
Also Published As
Publication number | Publication date |
---|---|
FR1323583A (en) | 1963-04-12 |
CH448294A (en) | 1967-12-15 |
BE628751A (en) | 1963-08-22 |
NL289192A (en) | 1965-03-25 |
FR1354231A (en) | 1964-03-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB1266787A (en) | ||
GB718204A (en) | Ferromagnetic ferrite materials | |
GB981143A (en) | Ferromagnetic ferrite materials for use at microwave frequencies | |
GB1496890A (en) | Manufacture of magnetic materials which exhibit exchange anisotropy | |
GB747737A (en) | Improvements in or relating to methods of manufacturing non-metallic permanent magnets | |
GB823971A (en) | Improvements in or relating to ferromagnetic ferrite materials | |
GB862135A (en) | Improvements in or relating to ferromagnetic materials, more particularly for use inmicro-wave equipment | |
GB739069A (en) | Improvements in or relating to methods of manufacturing magnetic ferrites | |
GB1070510A (en) | Ferromagnetic materials and processes for their manufacture | |
GB1105788A (en) | Improvements relating to ferrimagnetic materials | |
GB979953A (en) | Ferromagnetic ferrite materials and methods of fabrication for use at microwave frequencies | |
SE314144B (en) | ||
GB763494A (en) | Improvements in or relating to magnetic ferrites | |
GB1304237A (en) | ||
GB760799A (en) | Improvements in or relating to magnetic ceramic materials | |
GB988836A (en) | Improvements in or relating to permanent magnet materials | |
GB833007A (en) | Improvements in or relating to ferromagnetic materials, more particularly for ferromagnetic bodies for use at frequencies of at least 50 mc/s, methods of manufacturing such materials and ferromagnetic bodies consisting of such materials | |
GB1027042A (en) | Improvements in or relating to ferrimagnetic garnet materials | |
GB789099A (en) | Improvements in or relating to a method of producing magnetic cores | |
GB1086406A (en) | Improvements relating to ferrimagnetic material | |
GB984837A (en) | Improvements in or relating to manganese ferrites | |
GB861594A (en) | Methods of preparing ferrite cores | |
GB1054096A (en) | ||
GB964273A (en) | Improvements in low flux density ferromagnetic materials | |
JPS57145034A (en) | Cleavable magnetic iron oxide and its production |