GB810774A - Improvements in and relating to alloys and the metallizing of ceramic or cermet materials therewith - Google Patents

Improvements in and relating to alloys and the metallizing of ceramic or cermet materials therewith

Info

Publication number
GB810774A
GB810774A GB5712/56A GB571256A GB810774A GB 810774 A GB810774 A GB 810774A GB 5712/56 A GB5712/56 A GB 5712/56A GB 571256 A GB571256 A GB 571256A GB 810774 A GB810774 A GB 810774A
Authority
GB
United Kingdom
Prior art keywords
ceramic
alloy
per cent
metallizing
alloys
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB5712/56A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GTE Sylvania Inc
Original Assignee
Sylvania Electric Products Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sylvania Electric Products Inc filed Critical Sylvania Electric Products Inc
Publication of GB810774A publication Critical patent/GB810774A/en
Expired legal-status Critical Current

Abstract

A ceramic or cermet member is coated with an alloy of essentially 3-10 per cent Ti, 10-25 per cent Cu, and 65-87 per cent Ag by the application of a thin layer of the alloy or a mixture of the metal powders to the surface and firing in a dry oxygen-free atmosphere at 850-1150 DEG C. until metalized. The process may also serve to bond a metal e.g. Cu to a ceramic of similar coefficient of thermal expansion e.g. alumina. The atmosphere may be inert e.g. argon, reducing e.g. hydrogen, or a vacuum. Alternatively a Ni, Cu or Cd coating may be superposed on the alloy-coated ceramic which is then brazed to a metal member by usual methods e.g. using a Ag or Ag-Cu brazing powder and heating to 900 DEG C. in argon.
GB5712/56A 1955-02-28 1956-02-23 Improvements in and relating to alloys and the metallizing of ceramic or cermet materials therewith Expired GB810774A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US810774XA 1955-02-28 1955-02-28

Publications (1)

Publication Number Publication Date
GB810774A true GB810774A (en) 1959-03-25

Family

ID=22161953

Family Applications (1)

Application Number Title Priority Date Filing Date
GB5712/56A Expired GB810774A (en) 1955-02-28 1956-02-23 Improvements in and relating to alloys and the metallizing of ceramic or cermet materials therewith

Country Status (1)

Country Link
GB (1) GB810774A (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998028467A1 (en) * 1996-12-20 1998-07-02 The Dow Chemical Company Method of coating complex-shaped ceramic-metal composites and the products produced thereby
CN112176337A (en) * 2020-09-30 2021-01-05 万事泰集团(广东)技术研究有限公司 Laser cladding biological metal ceramic pot and preparation method thereof

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998028467A1 (en) * 1996-12-20 1998-07-02 The Dow Chemical Company Method of coating complex-shaped ceramic-metal composites and the products produced thereby
CN112176337A (en) * 2020-09-30 2021-01-05 万事泰集团(广东)技术研究有限公司 Laser cladding biological metal ceramic pot and preparation method thereof
CN112176337B (en) * 2020-09-30 2022-08-12 万事泰集团(广东)技术研究有限公司 Laser cladding biological metal ceramic pot and preparation method thereof

Similar Documents

Publication Publication Date Title
US2776472A (en) Method of making a ceramic-to-metal bond
US3547673A (en) Method of forming cermet-type protective coatings on heat resistant alloys
SE8604949D0 (en) TITANIUM COMPOSITE HAVING A POROUS SURFACE AND PROCESS FOR PRODUCING THE SAME
DE3169727D1 (en) Base material for firing in order to prepare an intermediate layer between a high melting dental alloy and a tooth porcelain
CN107326330A (en) A kind of integrated evaporation boat of the internal heat type with aluminum oxide porous textured buffer layers
GB963546A (en) Friction coating and method of making the same
US3443978A (en) Method of coating metals with a silicide layer and an outer layer of aluminasilicate
GB810774A (en) Improvements in and relating to alloys and the metallizing of ceramic or cermet materials therewith
GB817659A (en) Improvements in and relating to the metallizing of ceramic or cermet materials
EP0215638A1 (en) Metallizing composition for sintered ceramic article
US3730507A (en) Boron nitride base evaporation vessel having a surface coating of titanium-silicon thereon
GB1241401A (en) Method for metallizing a ceramic member and the article produced thereby
JPS6442370A (en) Method for joining ceramics and metal
US3713790A (en) Joined body of pyrolytic graphite and metallic members
GB624369A (en) Improvements in and relating to soldering metals and alloys, more particularly thosethat are difficult to solder
GB891705A (en) An improved method of forming an adherent layer on a ceramic material
GB906022A (en) Improvements in or relating to methods of metallising ceramic surfaces
GB573142A (en) Improvements in the metallising of ceramics
GB811088A (en) Improvements in or relating to methods of making joints between metallic and non-metallic parts
JPS6031595B2 (en) Tuyere manufacturing method
ES338442A1 (en) Method of forming a refractory metal-to-ceramic seal
JPS6126781A (en) Heat resisting laminated body and its manufacture
JPH04235246A (en) Alloy for metalizing for ceramics and metalizing method
GB874303A (en) Metalized ceramic bond and method for producing same
JPH0266150A (en) Heat shielding coating method