GB457872A - Improvements in or relating to molybdenum alloy steels - Google Patents
Improvements in or relating to molybdenum alloy steelsInfo
- Publication number
- GB457872A GB457872A GB6649/35A GB664935A GB457872A GB 457872 A GB457872 A GB 457872A GB 6649/35 A GB6649/35 A GB 6649/35A GB 664935 A GB664935 A GB 664935A GB 457872 A GB457872 A GB 457872A
- Authority
- GB
- United Kingdom
- Prior art keywords
- steel
- per cent
- ferro
- aluminium
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
An alloy steel containing from 0,2 to 1,5 per cent of molybdenum, 0,15 to 2 per cent of carbon, 0,3 to 3 per cent of manganese, 91 to 99,2 per cent of iron and, if desired, 0,15 to 2,5 per cent of aluminium is produced in which after the molten constituents have been substantially deoxidized in the usual way and the heat killed, a predetermined amount of an agent, e.g. aluminium or vanadium, is added to produce cementitic dispersion and fine grain size, e.g. of from No. 5 to No. 8 of the A.S.T.M., in the steel. From 0,032 to 0,8 per cent of p chromium may be included, the iron content being correspondingly reduced. Where the steel is made by the open hearth process, and where ferro-silicon is used as the deoxidant, about one-third of the ferro-silicon is added to the molten metal followed by about 1,25 pounds of aluminium per ton of steel, and the remainder of the ferro-silicon. If the steel is produced in an electric furnace, the oxidation is effected by the addition of ferro-manganese followed by ferro-silicon and from 1 to 1,25 pounds of aluminium per ton of steel. The aluminium is added when the temperature of the bath is about 2800 DEG F. Specific analyses of steel are given.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US457872XA | 1934-03-14 | 1934-03-14 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB457872A true GB457872A (en) | 1936-12-02 |
Family
ID=21939883
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB6649/35A Expired GB457872A (en) | 1934-03-14 | 1935-03-02 | Improvements in or relating to molybdenum alloy steels |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB457872A (en) |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2791500A (en) * | 1954-03-19 | 1957-05-07 | Int Nickel Co | High strength aircraft landing gear steel alloy elements |
DE1113950B (en) * | 1958-08-06 | 1961-09-21 | Hoesch Ag | Steel for grinding bodies |
US3060016A (en) * | 1961-01-23 | 1962-10-23 | Bethlehem Steel Corp | Hardened steel roll and composition therefor |
DE1207095B (en) * | 1962-12-31 | 1965-12-16 | United States Steel Corp | Use of a steel alloy as a material with at least 50 Rockwell C for steel bodies for lining mills, e.g. B. ball mills |
US3250610A (en) * | 1962-12-31 | 1966-05-10 | United States Steel Corp | Deeply hardenable liner member for grinding mill |
EP0020357B1 (en) * | 1978-11-15 | 1984-07-18 | Caterpillar Tractor Co. | Lower bainite alloy steel article |
US5122337A (en) * | 1988-02-09 | 1992-06-16 | Ovako Steel, Ab | Steel intended for highly stressed structural members with high demands for ductility and fatigue resistance |
CN105936036A (en) * | 2016-06-15 | 2016-09-14 | 国家电网公司 | Portable maintenance box for hydropower station |
-
1935
- 1935-03-02 GB GB6649/35A patent/GB457872A/en not_active Expired
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2791500A (en) * | 1954-03-19 | 1957-05-07 | Int Nickel Co | High strength aircraft landing gear steel alloy elements |
DE1113950B (en) * | 1958-08-06 | 1961-09-21 | Hoesch Ag | Steel for grinding bodies |
US3060016A (en) * | 1961-01-23 | 1962-10-23 | Bethlehem Steel Corp | Hardened steel roll and composition therefor |
DE1207095B (en) * | 1962-12-31 | 1965-12-16 | United States Steel Corp | Use of a steel alloy as a material with at least 50 Rockwell C for steel bodies for lining mills, e.g. B. ball mills |
US3250610A (en) * | 1962-12-31 | 1966-05-10 | United States Steel Corp | Deeply hardenable liner member for grinding mill |
EP0020357B1 (en) * | 1978-11-15 | 1984-07-18 | Caterpillar Tractor Co. | Lower bainite alloy steel article |
US5122337A (en) * | 1988-02-09 | 1992-06-16 | Ovako Steel, Ab | Steel intended for highly stressed structural members with high demands for ductility and fatigue resistance |
CN105936036A (en) * | 2016-06-15 | 2016-09-14 | 国家电网公司 | Portable maintenance box for hydropower station |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US2283299A (en) | Manufacture of steel | |
GB457872A (en) | Improvements in or relating to molybdenum alloy steels | |
US2501138A (en) | Globular inclusion control for steel making | |
GB428950A (en) | Improvements in processes for the manufacture of ironchromium alloys | |
US2281179A (en) | Production of rustless iron | |
US3306737A (en) | Magnesium and rare earth metal containing prealloy for the treatment of iron and steel melts | |
US2096318A (en) | Method of making chromium steel from chromium steel scrap | |
US1955791A (en) | High-strength cast iron and method of making same | |
GB395158A (en) | Improvements in or relating to the refining of steels | |
US1423847A (en) | Method of producing silicon-manganese-chrome steel | |
US1613571A (en) | Process of making molybdenum steel | |
US1529669A (en) | Method of making chrome steel having various carbon contents | |
US2800406A (en) | Process for making manganese-bearing steels | |
US1346344A (en) | Method for making chrome-steel | |
GB718373A (en) | Process for the production of alloyed steels | |
US3899321A (en) | Method of producing a vaccum treated effervescing boron steel | |
GB437806A (en) | Improvements in processes for the production of steel and iron alloys | |
SU724591A1 (en) | Alloy for steel deoxidizing and alloying | |
GB282387A (en) | Manufacture of stainless iron | |
GB477294A (en) | Improved process of producing free-cutting steel | |
GB202181A (en) | Improvements in or relating to the production and refining of nickel-chrome steels | |
GB316329A (en) | Process of decarburizing ferro-alloys | |
GB304371A (en) | Improvements in or relating to nickel and nickel alloys | |
GB377951A (en) | Improvements in and relating to the manufacture of chromium steel alloys | |
GB656396A (en) | Improvements in and relating to the refining of oxidised steels and the manufacture of alloy steels |