GB303639A - Improvements in and relating to the production of hydraulic cement - Google Patents
Improvements in and relating to the production of hydraulic cementInfo
- Publication number
- GB303639A GB303639A GB3415827A GB3415827A GB303639A GB 303639 A GB303639 A GB 303639A GB 3415827 A GB3415827 A GB 3415827A GB 3415827 A GB3415827 A GB 3415827A GB 303639 A GB303639 A GB 303639A
- Authority
- GB
- United Kingdom
- Prior art keywords
- bauxite
- lime
- subjecting
- parts
- per cent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
303,639. Knibbs, N. V. S. Dec. 16, 1927. Cements, Portland and Roman.-A cement of the high alumina type is produced by subjecting a mixture of lime and bauxite or other highly aluminous material to the action of steam, preferably under pressure, to secure reaction between the raw materials, and then subjecting the resultant product to a higher temperature which is normally however below the melting- point. The proportions may vary from one to two parts of lime to three parts of bauxite. The bauxite is ground and mixed with either quick or hydrated lime. The steam treatment when carried out at a pressure of 100 lbs. per square inch may be completed in one hour. The heat treatment may be at a temperature between 1000‹ and 1400‹ C. With bauxite containing 50 per cent alumina and 20 per cent iron oxide, four hours heating at 1100‹ to 1150‹ C. is sufficient, or two hours at 1150‹ to 1200‹ C.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3415827A GB303639A (en) | 1927-12-16 | 1927-12-16 | Improvements in and relating to the production of hydraulic cement |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3415827A GB303639A (en) | 1927-12-16 | 1927-12-16 | Improvements in and relating to the production of hydraulic cement |
Publications (1)
Publication Number | Publication Date |
---|---|
GB303639A true GB303639A (en) | 1929-01-10 |
Family
ID=10362112
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3415827A Expired GB303639A (en) | 1927-12-16 | 1927-12-16 | Improvements in and relating to the production of hydraulic cement |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB303639A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2546509A1 (en) * | 1983-05-27 | 1984-11-30 | Inst Aljuminievoi | Cement for the manufacture of foundry cores and moulds and process for its manufacture |
-
1927
- 1927-12-16 GB GB3415827A patent/GB303639A/en not_active Expired
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2546509A1 (en) * | 1983-05-27 | 1984-11-30 | Inst Aljuminievoi | Cement for the manufacture of foundry cores and moulds and process for its manufacture |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB369593A (en) | Improvements in or relating to the recovery of alumina from aluminous silicious material | |
GB303639A (en) | Improvements in and relating to the production of hydraulic cement | |
GB324541A (en) | An improved contact material for catalytic cracking and like operations | |
GB317783A (en) | New hydraulic binding medium | |
GB354502A (en) | Improvements relating to the manufacture of cement | |
US2049881A (en) | Manufacture of slag cement | |
GB253929A (en) | Building cement or plaster | |
GB474917A (en) | Improvements in hydraulic binders | |
GB445164A (en) | A process for producing cements with the aid of blast furnace slag | |
GB710562A (en) | Improvements in or relating to the production of ceramic compositions | |
AT236280B (en) | Process for the production of portland cement with high green strength | |
US2265665A (en) | Cementing material | |
GB250246A (en) | ||
SU51411A1 (en) | The method of obtaining carborundum refractories | |
GB266775A (en) | Improvements in and relating to the production of cementitious material | |
GB503847A (en) | Synthesis of base exchange materials | |
GB309069A (en) | Improved manufacture of cement | |
GB345145A (en) | Improvements in and relating to the production of cementitious material | |
GB456780A (en) | Improvements in and relating to the manufacture of artificial stone | |
GB532189A (en) | A process of treating plaster, lime, cement and the like | |
GB437855A (en) | Improvements in and relating to the manufacture of cement | |
GB310315A (en) | ||
GB231535A (en) | Manufacture of a portland cement | |
GB233698A (en) | Process for the manufacture of an aluminous cement of high initial strength | |
GB199575A (en) | Process for the manufacture of cement |