GB1436436A - Table-tennis bats - Google Patents
Table-tennis batsInfo
- Publication number
- GB1436436A GB1436436A GB5114473A GB5114473A GB1436436A GB 1436436 A GB1436436 A GB 1436436A GB 5114473 A GB5114473 A GB 5114473A GB 5114473 A GB5114473 A GB 5114473A GB 1436436 A GB1436436 A GB 1436436A
- Authority
- GB
- United Kingdom
- Prior art keywords
- resin
- wood
- impregnated fibre
- layer
- bonding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1436436 Laminates DUNLOP Ltd 14 Oct 1974 [3 Nov 1973] 51144/73 Heading B5N [Also in Division A6] A laminate is formed of a wood layer sandwiched between two resin-impregnated fibre layers. Preferably, the resin impregnated fibre layer, which is of thickness 0À004 to 0À015 inch, contains by weight 40-60% fibres, and the wood layer which is of thickness 0À125 to 0À25 inch is formed of a low density (#0À45.10<SP>3</SP> kgm.<SP>-3</SP>) wood; e.g. obeche, balsa. In one embodiment, the resin-impregnated fibre layer is formed by the impregnation of a woven fibre sheet with a thermosetting resin, e.g. epoxy, phenolic, polyester or urea-formaldehyde. The fibres themselves are preferably of a low density (#1À6.10<SP>3</SP> kgm.<SP>-3</SP>) high elastic modulus (Young's Modulus #50 GNm.<SP>-2</SP>) type; e.g. aromatic polyamide. The resin impregnated fibre layers may be formed separately and cured before bonding to the wood with a suitable adhesive (e.g. epoxy resin) or may be formed by initially impregnating with resin and then curing and bonding to the wood in a single operation (the resin itself acting as a bonding agent). In the latter case the curing temperature should not exceed 100‹ C. to avoid wood damage; the range 80-100‹ C. being preferable.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB5114473A GB1436436A (en) | 1973-11-03 | 1973-11-03 | Table-tennis bats |
ZA00746579A ZA746579B (en) | 1973-11-03 | 1974-10-16 | Table-tennis bats |
FR7435267A FR2249681B1 (en) | 1973-11-03 | 1974-10-21 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB5114473A GB1436436A (en) | 1973-11-03 | 1973-11-03 | Table-tennis bats |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1436436A true GB1436436A (en) | 1976-05-19 |
Family
ID=10458823
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB5114473A Expired GB1436436A (en) | 1973-11-03 | 1973-11-03 | Table-tennis bats |
Country Status (3)
Country | Link |
---|---|
FR (1) | FR2249681B1 (en) |
GB (1) | GB1436436A (en) |
ZA (1) | ZA746579B (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4324400A (en) * | 1979-08-08 | 1982-04-13 | Est Industries, Inc. | Table tennis bat blade |
EP1473064A1 (en) * | 2003-04-30 | 2004-11-03 | Tamasu Co., Ltd | Blade of a table tennis racket and table tennis racket |
FR2883483A1 (en) * | 2005-03-22 | 2006-09-29 | Virginie Gamboa | Fibrous reinforcing plate for table tennis racket, has fibrous reinforcing frames constituted of carbon, aramid fiber or glass plates, where plates are covered by foam and rubber plates and frames are impregnated with thermosetting resin |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3417728A1 (en) * | 1984-05-12 | 1985-11-14 | Adolf K.W. 7441 Unterensingen Stroh | Racket blade for a table tennis racket |
-
1973
- 1973-11-03 GB GB5114473A patent/GB1436436A/en not_active Expired
-
1974
- 1974-10-16 ZA ZA00746579A patent/ZA746579B/en unknown
- 1974-10-21 FR FR7435267A patent/FR2249681B1/fr not_active Expired
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4324400A (en) * | 1979-08-08 | 1982-04-13 | Est Industries, Inc. | Table tennis bat blade |
EP1473064A1 (en) * | 2003-04-30 | 2004-11-03 | Tamasu Co., Ltd | Blade of a table tennis racket and table tennis racket |
FR2883483A1 (en) * | 2005-03-22 | 2006-09-29 | Virginie Gamboa | Fibrous reinforcing plate for table tennis racket, has fibrous reinforcing frames constituted of carbon, aramid fiber or glass plates, where plates are covered by foam and rubber plates and frames are impregnated with thermosetting resin |
Also Published As
Publication number | Publication date |
---|---|
ZA746579B (en) | 1975-11-26 |
FR2249681B1 (en) | 1976-10-22 |
FR2249681A1 (en) | 1975-05-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4263373A (en) | Method of making an ultra thin glue adherable decorative laminate | |
EP0366979A3 (en) | Improved interleaf layer in fiber reinforced resin laminate composites | |
ES8602484A1 (en) | High impact strength fiber resin matrix composites. | |
US2894503A (en) | Archery bow | |
EP1142920A4 (en) | Epoxy resin composition, prepreg, and roll made of resin reinforced with reinforcing fibers | |
GB1436436A (en) | Table-tennis bats | |
GB1514625A (en) | Table tennis bat | |
US2550002A (en) | Laminated ski | |
FR2033630A5 (en) | Tennis rackets | |
US2456005A (en) | Aircraft structural material and method of making the same | |
JPS5938895B2 (en) | plate-like complex | |
US3660219A (en) | Heterogeneous construction of textile shuttle side walls | |
JPH09174765A (en) | Composite molding | |
FR2114869A5 (en) | Composite plastic table top - with reinforced plastic surface and wood particle core | |
GB1387692A (en) | Multiply-reinforced structural panel | |
GB1197064A (en) | Glass Fibre Reinforced Thermoplastic Resin Structures | |
JPS6115710B2 (en) | ||
GB992506A (en) | Improvements relating to laminates | |
GB1151442A (en) | Improvements in or relating to Laminates | |
JPS6123385Y2 (en) | ||
GB2161424A (en) | Energy absorbant laminates | |
JPS6115711B2 (en) | ||
JPH06122105A (en) | Carbon fiber reinforced laminated wood | |
KR960021083A (en) | Fuselage skin for model aircraft and its manufacturing method | |
GB1454501A (en) | Transformer end platforms |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed | ||
PCNP | Patent ceased through non-payment of renewal fee |