GB1401378A - Elastomer coated fabric and method of making the same - Google Patents

Elastomer coated fabric and method of making the same

Info

Publication number
GB1401378A
GB1401378A GB989073A GB989073A GB1401378A GB 1401378 A GB1401378 A GB 1401378A GB 989073 A GB989073 A GB 989073A GB 989073 A GB989073 A GB 989073A GB 1401378 A GB1401378 A GB 1401378A
Authority
GB
United Kingdom
Prior art keywords
fabric
composition
asbestos
elastomer
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB989073A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Johns Manville Corp
Johns Manville
Original Assignee
Johns Manville Corp
Johns Manville
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Johns Manville Corp, Johns Manville filed Critical Johns Manville Corp
Publication of GB1401378A publication Critical patent/GB1401378A/en
Expired legal-status Critical Current

Abstract

1401378 Coated asbestos fabrics JOHNSMANVILLE CORP 28 Feb 1973 [2 March 1972] 9890/73 Heading B2E [Also in Division D1] A coated fabric i.e., Fig 1 comprises: an open weave fabric layer 12, said fabric layer being made of blended strands comprising asbestos yarns intertwined with aromatic polyamide fibres or polyester fibres; and a layer of an elastomer 16 bonded to each side of the fabric with elastomer extending through the weave openings to adjoin the layers. The elastomer is preferably a fluoroelastomer applied as a composition comprising: fluoroelastomer 60 to 80 wt % (preferably 72.5); magnesium oxide 4 to 20 wt % (10.85); medium thermal carbon black 4 to 40 wt % (10.85); polyethylene 0.5 to 10 wt % (1.44); diamine 0.5 to 6 wt % (2.18); and polyester liquid 0 to 15 wt % (2.18). The preferred fabric is a woven fabric of a blended yarn having an aromatic polyamide or polyester core round which is wound asbestos fibres to form a sheath and finally the asbestos yarns have further yarn(s) of aromatic polyamide or polyester wound round them. The asbestos yarns may each comprise a cotton strand embedded in asbestos. The fabric is preferably primed with a cement comprising a dilute solution of the fluoroelastomer compositions by spraying or dipping. A first layer of the coating composition is then applied, Fig 4, by passing the composition in a plastic state through the nip of heated rollers 28, 30 then onto the fabric which passes from a roller 34 through heated rollers 30, 32. The composition is thereby pressed into the holes 18, Fig 1, between the yarns of the fabric. A further coating of the composition is then applied to the other side of the yarn in like manner, whereby the further coating reaches the first coating through the holes 18. The further coating is then dusted with mica powder before being fed to a takeup roll with a rubber sheet under tension, which causes the elastomer composition coatings to be squeezed together. After each coating step the elastomer is steam vulcanised.
GB989073A 1972-03-02 1973-02-28 Elastomer coated fabric and method of making the same Expired GB1401378A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US23134472A 1972-03-02 1972-03-02

Publications (1)

Publication Number Publication Date
GB1401378A true GB1401378A (en) 1975-07-16

Family

ID=22868838

Family Applications (1)

Application Number Title Priority Date Filing Date
GB989073A Expired GB1401378A (en) 1972-03-02 1973-02-28 Elastomer coated fabric and method of making the same

Country Status (9)

Country Link
JP (1) JPS50111366A (en)
AU (1) AU467307B2 (en)
BE (1) BE796153A (en)
CA (1) CA1029262A (en)
DE (1) DE2310962C3 (en)
FR (1) FR2174277B1 (en)
GB (1) GB1401378A (en)
IT (1) IT979691B (en)
NL (1) NL7302795A (en)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5070540A (en) * 1983-03-11 1991-12-10 Bettcher Industries, Inc. Protective garment
US5655358A (en) * 1985-08-16 1997-08-12 Kolmes; Nathaniel H. Cut resistant support yarn suitable for wrapping with an additional yarn covering
US5822791A (en) * 1996-06-24 1998-10-20 Whizard Protective Wear Corp Protective material and method
US6279305B1 (en) 1985-10-17 2001-08-28 Wells Lamont Industry Group, Inc. Knittable yarn and safety apparel
WO2003026868A1 (en) * 2001-09-26 2003-04-03 Federal-Mogul Wiesbaden Gmbh & Co. Kg Method for the production of bearing materials, bearing materials produced by said methods and use of said bearing materials
USRE38136E1 (en) * 1985-08-16 2003-06-10 Supreme Elastic Corporation Cut resistant support yarn suitable for wrapping with an additional yarn covering

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2635114A1 (en) * 1976-08-04 1978-02-09 Ver Seidenwebereien Ag Gas-tight coated aromatic polyamide textile fabrics - with a coating of polyester-urea!, laminated to a film e.g. of PTFE or PVC, for inflatable craft, balloons, etc.
JPS56107073A (en) * 1980-01-22 1981-08-25 Teijin Ltd Improved all aromatic polyamide fiber and cloth
CA1138272A (en) * 1980-06-09 1982-12-28 James L. Johnson Non-sticking ply end turn-over bladder and method of manufacture thereof
JPS57140148A (en) * 1981-02-26 1982-08-30 Hasegawa Kagaku Kogyo Kk Plastic reinforcing material
FR2520394A1 (en) * 1982-01-22 1983-07-29 Tuyaux Flexibles Forge Ste Nle FLEXIBLE WOVEN PIPE AND MANUFACTURING METHOD THEREOF

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB871582A (en) * 1957-08-21 1961-06-28 Du Pont Improvements in or relating to elastomer-coated fabrics
GB893684A (en) * 1958-12-04 1962-04-11 Midland Silicones Ltd Fabric having controlled stretch

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5070540A (en) * 1983-03-11 1991-12-10 Bettcher Industries, Inc. Protective garment
US5655358A (en) * 1985-08-16 1997-08-12 Kolmes; Nathaniel H. Cut resistant support yarn suitable for wrapping with an additional yarn covering
USRE38136E1 (en) * 1985-08-16 2003-06-10 Supreme Elastic Corporation Cut resistant support yarn suitable for wrapping with an additional yarn covering
US6279305B1 (en) 1985-10-17 2001-08-28 Wells Lamont Industry Group, Inc. Knittable yarn and safety apparel
US6826898B1 (en) 1985-10-17 2004-12-07 Wells Lamont Industry Group Knittable yarn and safety apparel
US5822791A (en) * 1996-06-24 1998-10-20 Whizard Protective Wear Corp Protective material and method
WO2003026868A1 (en) * 2001-09-26 2003-04-03 Federal-Mogul Wiesbaden Gmbh & Co. Kg Method for the production of bearing materials, bearing materials produced by said methods and use of said bearing materials

Also Published As

Publication number Publication date
IT979691B (en) 1974-09-30
FR2174277A1 (en) 1973-10-12
NL7302795A (en) 1973-09-04
JPS50111366A (en) 1975-09-02
DE2310962C3 (en) 1975-11-13
FR2174277B1 (en) 1975-04-04
CA1029262A (en) 1978-04-11
DE2310962B2 (en) 1975-03-27
DE2310962A1 (en) 1973-09-13
BE796153A (en) 1973-09-03
AU467307B2 (en) 1975-11-27
AU5283773A (en) 1974-09-05

Similar Documents

Publication Publication Date Title
US6270083B1 (en) Packing yarn made of graphite foil and plastic foil and method of manufacturing a packing yarn
US2865790A (en) Method of treating fibrous material utilizing a radio-frequency field which extends predominantly at right angles to the length of said material
US2930106A (en) Gaskets
GB1401378A (en) Elastomer coated fabric and method of making the same
US2306781A (en) Product containing siliceous fibers and method of making the same
US4526637A (en) Method of making conveyor belt
US2949394A (en) Sheet material
US4731283A (en) Waterproof cloth and process for production thereof
US2823156A (en) Vinyl coated knit fabric
US3463690A (en) Method of laminating polyurethane foam and fabric
US3095338A (en) Web-like continuous textile structure
US2620851A (en) Inorganic sheet material
US4813533A (en) Conveyor belt
EP0041849A1 (en) PVC fabric
US3822176A (en) Carpet underlay
US3620797A (en) Impregnation of a nonwoven fabric
JP3124582B2 (en) Air spring bellows made from elastomeric composites
US4473521A (en) Method and apparatus for making a polymeric coated fabric layer
US3947922A (en) Foundations for card clothing
GB698611A (en) Improvements in anti-friction materials or products
US3250662A (en) Coated fabric
GB1165987A (en) Process for Producing a Leather Substitute
US4332842A (en) Production of belting
GB821059A (en) Improvements in or relating to the production of power transmission and conveyor belting
US2312200A (en) Elastic pile fabric

Legal Events

Date Code Title Description
PS Patent sealed
PCNP Patent ceased through non-payment of renewal fee