FR2897291A1 - BASKET FOR CLOSING A MOLDING MOLD BY FULLY MOLDED TECHNIQUE, AND IN PARTICULAR BY INFUSION OR INJECTION OF RESIN - Google Patents

BASKET FOR CLOSING A MOLDING MOLD BY FULLY MOLDED TECHNIQUE, AND IN PARTICULAR BY INFUSION OR INJECTION OF RESIN Download PDF

Info

Publication number
FR2897291A1
FR2897291A1 FR0651431A FR0651431A FR2897291A1 FR 2897291 A1 FR2897291 A1 FR 2897291A1 FR 0651431 A FR0651431 A FR 0651431A FR 0651431 A FR0651431 A FR 0651431A FR 2897291 A1 FR2897291 A1 FR 2897291A1
Authority
FR
France
Prior art keywords
resin
layers
mold
infusion
secured
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR0651431A
Other languages
French (fr)
Other versions
FR2897291B1 (en
Inventor
Gerard Joly
Eric Deneux
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chomarat Composites SAS
Original Assignee
Chomarat Composites SAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FR0601256A external-priority patent/FR2897294A1/en
Application filed by Chomarat Composites SAS filed Critical Chomarat Composites SAS
Priority to FR0651431A priority Critical patent/FR2897291B1/en
Priority to PCT/FR2007/050792 priority patent/WO2007093737A2/en
Publication of FR2897291A1 publication Critical patent/FR2897291A1/en
Application granted granted Critical
Publication of FR2897291B1 publication Critical patent/FR2897291B1/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Bâche (1) destinée à la fermeture d'un moule (4) de moulage par technique de moule fermé, telle que par infusion ou injection de résine, caractérisée en ce qu'elle comporte sur toute ou partie de sa surface, deux couches (2,6) solidarisées, et définissant entre elles un volume libre (13), et en ce qu'elle comporte des agencements (10) pour l'entrée d'un fluide caloporteur en vue de la circulation du fluide caloporteur à l'intérieur du volume libre (13).Tarpaulin (1) intended for closing a mold (4) for molding by closed mold technique, such as by infusion or injection of resin, characterized in that it comprises on all or part of its surface, two layers ( 2,6) secured together and defining between them a free volume (13), and in that it comprises arrangements (10) for the entry of a coolant for the circulation of the heat transfer fluid inside. free volume (13).

Description

-1--1-

BACHE, DESTINEE A LA FERMETURE D'UN MOULE DE MOULAGE PAR TECHNIQUE DE MOULE FERME, ET NOTAMMENT PAR INFUSION OU INJECTION DE RESINE.  PLANT FOR THE CLOSURE OF A MOLDING MOLD BY FIXED MOLD TECHNIQUE, AND IN PARTICULAR BY INFUSION OR INJECTION OF RESIN.

Domaine Technique : L'invention se rattache au domaine de la fabrication des matériaux composites par des procédés de moulage employant des moules fermés. Il peut s'agir de procédés d'infusion ou d'injection de résine. Il peut également s'agir de procédés utilisant des renforts préimprégnés de résine Elle concerne plus spécifiquement un des organes utilisés lors de la mise en oeuvre du procédé de moulage. Plus précisément, elle concerne une bâche destinée à la fermeture du moule lors de l'introduction de la résine. L'invention vise plus spécifiquement une nouvelle structure de ce type de bâche, qui permet notamment de mettre en oeuvre des opérations de régulation thermique. Dans la suite de la description, l'invention sera plus particulièrement décrite pour des procédés d'infusion, sans toutefois être limitée à cette seule technique, étant donc entendu qu'elle peut se transposer aux moulages par injection de résine, ou par polymérisation de renforts préimprégnés.  Technical Field: The invention relates to the field of manufacturing composite materials by molding processes employing closed molds. It can be infusion processes or resin injection. It may also be processes using resin prepreg reinforcements It relates more specifically to one of the organs used during the implementation of the molding process. More specifically, it relates to a tarpaulin for closing the mold during the introduction of the resin. The invention aims more specifically at a new structure of this type of tarpaulin, which makes it possible in particular to implement thermal regulation operations. In the following description, the invention will be more particularly described for infusion processes, without being limited to this technique alone, it being understood that it can be transposed to resin injection molding, or by polymerization of pre-impregnated reinforcements.

Techniques antérieures : De façon générale, les procédés de moulage par infusion de résine mettent en oeuvre plusieurs étapes parmi lesquelles figure la mise en place d'éléments de renfort fibreux sur la forme d'un moule. Le moule est ensuite refermé par l'intermédiaire d'un couvercle souple permettant le passage contrôlé d'une résine qui va infuser à l'intérieur du renfort pour totalement l'investir, puis polymériser, afm de donner une pièce rigide. La propagation de la résine se fait par l'application d'un vide en certains points de la bâche, vers lesquels la résine introduite dans le moule se déplace automatiquement. 2897291 -2-  PRIOR ART: In general, resin infusion molding processes use several steps, including the placing of fibrous reinforcing elements on the shape of a mold. The mold is then closed by means of a flexible cover allowing the controlled passage of a resin which will infuse inside the reinforcement to fully invest it, then polymerize, to give a rigid piece. The propagation of the resin is done by the application of a vacuum at certain points of the sheet, towards which the resin introduced into the mold moves automatically. 2897291 -2-

En pratique, le couvercle du moule peut être réalisé par un film étanche, qui sera ensuite éliminé après moulage. On conçoit que l'emploi d'un film jetable génère des déchets qui compliquent la mise en oeuvre globale du procédé. Il est également connu d'utiliser des couvercles formés d'une bâche plus épaisse, mais réutilisable. 5 Cette bâche doit assurer une étanchéité qui doit être maintenue dans le temps, si l'on souhaite réutiliser la même bâche de fermeture de moule plusieurs fois consécutives. Le procédé d'infusion de résine du fait de sa nature chimique présente plusieurs phases successives. En effet, les résines de polyuréthane, d'époxy et autres, sont obtenues par la polymérisation in-situ de différents composants introduits 10 simultanément dans le moule. La réaction chimique qui a lieu entre ces deux composants nécessite d'être initiée à une température optimisée. Puis, elle présente ensuite un caractère exothermique au fur et à mesure de son déroulement.  In practice, the lid of the mold can be made by a sealed film, which will then be removed after molding. It is conceivable that the use of a disposable film generates waste that complicates the overall implementation of the process. It is also known to use lids formed of a thicker tarpaulin, but reusable. This tarpaulin must provide a seal which must be maintained over time, if it is desired to reuse the same mold closure cover several consecutive times. The resin infusion process due to its chemical nature has several successive phases. Indeed, the polyurethane resins, epoxy resins and others, are obtained by the in-situ polymerization of various components introduced simultaneously into the mold. The chemical reaction that takes place between these two components needs to be initiated at an optimized temperature. Then, it then presents an exothermic character as it unfolds.

Un compromis doit être trouvé, en ce qui concerne la température ambiante 15 du local dans lequel est effectuée l'opération d'infusion. Ainsi, cette température ne doit pas être trop basse pour faciliter le démarrage de la propagation de la résine sans augmenter trop de viscosité. Plus précisément, lors du démarrage de la réaction chimique, il est préférable que la viscosité des deux composants se propageant dans le renfort textile soit globalement faible, pour éviter de créer des phénomènes de 20 mauvaise distribution de la résine. Une augmentation de la température est donc favorable à une diminution de la viscosité de la résine en début de propagation.  A compromise must be found with regard to the ambient temperature of the room in which the infusion operation is carried out. Thus, this temperature should not be too low to facilitate starting the propagation of the resin without increasing too much viscosity. More specifically, during the start of the chemical reaction, it is preferable that the viscosity of the two components propagating in the textile reinforcement is generally low, to avoid creating phenomena of poor distribution of the resin. An increase in temperature is therefore favorable to a decrease in the viscosity of the resin at the beginning of propagation.

A l'inverse, elle ne doit pas être trop élevée, au risque de voir des élévations de température trop importantes à l'intérieur de la pièce infusée. En effet, le 25 caractère exothermique de la réaction de polymérisation provoque une montée en température des zones dans laquelle une quantité plus importante de résine s'est accumulée. Ces élévations de température sont à l'origine de phénomènes de retrait qui se traduisent visuellement par des irrégularités de l'état de surface. Ces irrégularités peuvent être extrêmement visibles, notamment dans le cas de réalisation de pièces de grandes dimensions. A titre d'exemple, on peut citer la réalisation de coques de bateaux par des procédés d'infusion. Dans certaines zones de la coque, 2897291 -3-  Conversely, it should not be too high, at the risk of excessive temperature rises inside the infused room. Indeed, the exothermic nature of the polymerization reaction causes the zones to rise in temperature in which a larger amount of resin has accumulated. These temperature rises are at the origin of shrinkage phenomena that are visually reflected by irregularities in the surface state. These irregularities can be extremely visible, especially in the case of production of large parts. By way of example, mention may be made of making hulls of boats by infusion processes. In certain areas of the hull, 2897291 -3-

qui se trouvent au-dessus de la ligne de flottaison, la coque comporte des varangues ou autres renforts mécaniques qui constituent des zones d'accumulation de résine lors de l'infusion. Les phénomènes de retrait observés consécutivement à des élévations de température localisées sont visuellement très apparents et dégradent 5 l'aspect de la coque. Un des objectifs de l'invention est de permettre de s'affranchir de ces inconvénients, en recherchant à optimiser les problèmes d'ordre thermique liés aux réactions chimiques intervenant lors du procédé d'infusion.  which are above the waterline, the hull has verandas or other mechanical reinforcements that constitute areas of resin accumulation during infusion. The shrinkage phenomena observed following localized temperature rises are visually very apparent and degrade the appearance of the hull. One of the objectives of the invention is to overcome these drawbacks by seeking to optimize thermal problems related to chemical reactions involved in the infusion process.

Exposé de l'invention 10 L'invention concerne donc une bâche destinée à la fermeture d'un moule de moulage par infusion ou injection de résine. Conformément à l'invention, cette bâche se caractérise en ce qu'elle comporte sur tout ou partie de sa surface deux couches solidarisées l'une avec l'autre et qui défmissent entre elles un volume libre. Elle comporte également des agencements pour l'entrée et la sortie d'un fluide 15 caloporteur en vue de permettre la circulation de ce fluide à l'intérieur du volume libre. Autrement dit, l'invention consiste à utiliser comme couvercle de moule une bâche intégrant un circuit de circulation d'un fluide, typiquement de l'air, qui permet d'apporter ou de retirer de l'énergie à la réaction chimique de polymérisation de la 20 résine. Grâce à l'invention, il est ainsi possible de faire circuler de l'air chaud au début de la réaction de polymérisation, pour réduire la viscosité des composants se propageant dans le renfort textile, afm d'assurer une bonne homogénéité de la répartition de la résine au sein du renfort. Ensuite, lorsque la réaction de polymérisation est entamée, et qu'elle dégage donc de la chaleur, la circulation d'un 25 flux d'air frais permet d'évacuer tout ou partie de cette chaleur, afm de limiter les élévations de température néfastes à la qualité de l'aspect de la pièce moulée.  SUMMARY OF THE INVENTION The invention therefore relates to a tarpaulin intended for closing an infusion molding mold or resin injection mold. According to the invention, this cover is characterized in that it comprises on all or part of its surface two layers secured to one another and which define between them a free volume. It also includes arrangements for the entry and exit of a heat transfer fluid to allow the circulation of this fluid within the free volume. In other words, the invention consists in using as a mold cover a cover incorporating a circuit for circulating a fluid, typically air, which makes it possible to supply or withdraw energy to the chemical reaction of polymerization of the resin. Thanks to the invention, it is thus possible to circulate hot air at the beginning of the polymerization reaction, to reduce the viscosity of the components propagating in the textile reinforcement, in order to ensure a good homogeneity of the distribution of the resin within the reinforcement. Then, when the polymerization reaction is started, and therefore emits heat, the circulation of a fresh air flow makes it possible to evacuate all or part of this heat, in order to limit harmful temperature rises. to the quality of the appearance of the molded part.

En pratique, il est possible d'utiliser deux couches qui sont superposées sur toute la surface de la bâche, et qui sont solidarisées au niveau de leurs périphéries 30 communes. Dans ce cas, c'est l'intégralité de la surface, du couvercle du moule qui peut bénéficier de la régulation thermique caractéristique. 2897291 -4- Dans d'autres cas, plus particuliers, on peut envisager que la bâche ne comporte que deux couches que sur une partie seulement de sa surface. Dans ce cas, la couche de moindre superficie, typiquement la couche extérieure, est alors 5 solidarisée à la couche inférieure au niveau de sa périphérie, ce qui permet, lorsque les applications le requièrent, de n'effectuer la régulation thermique caractéristique uniquement dans des zones déterminées.  In practice, it is possible to use two layers which are superimposed over the entire surface of the sheet, and which are secured at their common peripheries. In this case, it is the entire surface of the mold cover that can benefit from the characteristic thermal regulation. In other, more particular cases, it is conceivable that the cover has only two layers on only a part of its surface. In this case, the layer of smaller area, typically the outer layer, is then secured to the lower layer at its periphery, which allows, when the applications require it, to carry out the characteristic thermal regulation only in determined areas.

En pratique, les deux couches peuvent être solidarisées de façon réversible, 10 de manière à pouvoir les séparer lorsque cela se révèle nécessaire et par exemple au moment de la confection du transport, ou de leur mise en place sur le moule. L'assemblage des deux couches entre elles peut par exemple être réalisé en utilisant des bandes du type VELCRO .  In practice, the two layers can be reversibly secured, so as to separate them when necessary and for example at the time of making the transport, or their establishment on the mold. The assembly of the two layers together can for example be achieved using strips of VELCRO type.

15 Avantageusement, on peut également prévoir que les deux couches soient solidarisées dans des zones supplémentaires, de manière à défmir des séparations entre plusieurs canaux de circulation de fluide caloporteur à l'intérieur du volume libre. Autrement dit, les deux couches ne sont pas solidarisées uniquement au niveau de leur périphérie, mais également dans des régions situées à des niveaux 20 intermédiaires. Ceci permet d'éviter que les deux couches ne s'écartent trop fortement lorsque le fluide caloporteur est pulsé à l'intérieur du volume défmi entre les couches. Il est ainsi possible d'optimiser la circulation du fluide caloporteur, et éventuellement de créer plusieurs circuits indépendants en fonction des besoins.  Advantageously, it can also be provided that the two layers are secured in additional zones, so as to define separations between several heat transfer fluid circulation channels within the free volume. In other words, the two layers are not secured only at their periphery, but also in regions located at intermediate levels. This makes it possible to avoid that the two layers deviate too strongly when the coolant is pulsed within the defined volume between the layers. It is thus possible to optimize the circulation of the heat transfer fluid, and possibly to create several independent circuits according to the needs.

25 En pratique, la couche en regard du moule est avantageusement réalisée en un matériau compatible avec les solvants de la résine employée lors du procédé d'injection. 2897291 -5-  In practice, the layer facing the mold is advantageously made of a material compatible with the solvents of the resin used during the injection process. 2897291 -5-

Description sommaire des figures La manière de réaliser l'invention, ainsi que les avantages qui en découlent ressortiront bien de la description du mode de réalisation qui suit, à l'appui de la figure annexée qui est une vue en perspective sommaire d'une partie de bâche, 5 montrée partiellement.  Brief Description of the Figures The manner of carrying out the invention and the advantages thereof will be apparent from the description of the embodiment which follows, in support of the attached figure which is a brief perspective view of a portion of the invention. of tarpaulin, 5 partially shown.

Manière de réaliser l'invention La bâche (1) représentée partiellement à la figure 1 comporte deux couches distinctes à savoir une couche inférieure (2) qui est destinée à venir au contact des 10 éléments, qui sont mis en place à l'intérieur du fond du moule en particulier le renfort textile (2). Cette couche inférieure (2) est réalisée en un matériau qui est compatible avec les différents solvants et autres produits chimiques présents dans la résine infusée. Cette couche (2) peut être ainsi réalisée dans une matière spéciale qui n'est pas adhérente avec les produits contenus dans la résine lors de leur 15 polymérisation. Cette couche inférieure (2) est mise en forme selon une technique classique de chaudronnerie et/ou par thermoformage, afm d'épouser au maximum les formes du moule (4), et notamment les formes en volume telles qu'illustrées à la figure.  DESCRIPTION OF THE INVENTION The cover (1) shown partially in FIG. 1 comprises two distinct layers, namely a lower layer (2) which is intended to come into contact with the elements, which are put in place inside the bottom of the mold, in particular the textile reinforcement (2). This lower layer (2) is made of a material that is compatible with the various solvents and other chemicals present in the infused resin. This layer (2) can thus be made of a special material which is not adherent with the products contained in the resin during their polymerization. This lower layer (2) is shaped according to a standard technique of boilermaking and / or thermoforming, to marry to the maximum shape of the mold (4), and in particular the volume forms as illustrated in FIG.

20 Conformément à l'invention, cette bâche (1) comporte une seconde couche (6), ou couche supérieure, qui peut être présente sur toute ou partie de la surface de la bâche (1). Dans la forme illustrée, cette couche supérieure (6) est présente uniquement sur une portion de la superficie de la bâche, mais il va de soi qu'elle pourrait en occuper l'intégralité de la superficie. 25 Cette couche supérieure (6) est solidarisée à la couche inférieure (2) par différentes zones (7-10). Ainsi, cette solidarisation intervient au niveau des régions communes des pourtours (7-9) des deux couches (2,6), c'est-à-dire en lisière de bâche. Une liaison complémentaire (10), illustrée au milieu de la couche supérieure 30 (6) peut également permettre un accrochage de la couche supérieure sur la couche inférieure. En pratique, cette solidarisation est avantageusement réversible en -6-  According to the invention, this cover (1) comprises a second layer (6), or top layer, which may be present on all or part of the surface of the sheet (1). In the illustrated form, this upper layer (6) is present only on a portion of the surface of the sheet, but it goes without saying that it could occupy the entire area. This upper layer (6) is secured to the lower layer (2) by different zones (7-10). Thus, this solidarity occurs at the level of the common regions of the perimeters (7-9) of the two layers (2,6), that is to say on the edge of tarpaulin. A complementary connection (10), illustrated in the middle of the upper layer (6) may also allow attachment of the upper layer on the lower layer. In practice, this solidarity is advantageously reversible in -6-

utilisant par exemple des systèmes d'accrochage (18,19) du type VELCRO . Toutefois, d'autres systèmes peuvent être employés dès lors qu'ils permettent d'assurer une bonne solidarisation des couches (2,6) entre elles, suffisante pour résister aux efforts minimes exercés lors du passage du flux d'air caractéristique.  using for example VELCRO fastening systems (18,19). However, other systems may be employed as long as they make it possible to ensure good bonding of the layers (2,6) between them, sufficient to withstand the minimal forces exerted during the passage of the characteristic air flow.

En pratique, la présence des deux couches superposées défmit un volume libre à l'intérieur duquel on peut entretenir une circulation d'air. Dans la forme illustrée, ce flux d'air est introduit par un embout (12) permettant la connexion d'un système d'air pulsé (non représenté). Le volume libre (13) débouche dans la forme illustrée dans les zones (14) où la couche supérieure (6) s'interrompt. La présence de la zone intermédiaire (10) d'accrochage des deux couches (2,6) entre elles permet de défmir plusieurs canaux (15,16) du fluide caloporteur. Ces canaux (15,16) peuvent être reliés entre eux par des zones de liaison appropriées permettant d'optimiser la circulation du fluide caloporteur, et notamment le nombre de zones d'entrée du flux d'air.  In practice, the presence of the two superimposed layers defines a free volume within which air circulation can be maintained. In the illustrated form, this air flow is introduced by a nozzle (12) allowing the connection of a forced air system (not shown). The free volume (13) opens in the form shown in the areas (14) where the upper layer (6) is interrupted. The presence of the intermediate zone (10) for hooking the two layers (2, 6) between them makes it possible to define several channels (15, 16) of the coolant. These channels (15, 16) can be interconnected by appropriate connection zones for optimizing the circulation of the coolant, and in particular the number of airflow inlet zones.

Lorsque deux couches (2,6) s'étendent sur l'intégralité de la surface de la bâche, des agencements similaires à l'embout d'entrée (12) peuvent être prévus pour assurer la sortie du flux d'air. Le fluide caloporteur peut ainsi être confmé dans un circuit dédié, avec un possible recyclage afm de ne pas influencer trop fortement la température du local dans lequel intervient l'opération d'infusion.  When two layers (2,6) extend over the entire surface of the sheet, arrangements similar to the inlet nozzle (12) may be provided to ensure the exit of the air stream. The heat transfer fluid can thus be confused in a dedicated circuit, with a possible recycling so as not to influence too strongly the temperature of the room in which the infusion operation takes place.

Grâce à cette possibilité de circulation d'un fluide caloporteur, une régulation thermique peut être effectuée lors de l'opération d'infusion afm de maîtriser les phénomènes thermiques et notamment exothermiques inhérents à la réaction de polymérisation de la résine. Dans une forme évoluée, cette régulation peut inclure une instrumentation par un ensemble de capteurs de température disposé sur la bâche. Dans le cas d'emploi de renforts préimprégnés, la circulation d'air chaud permet de mettre le renfort à la température nécessaire pour obtenir la réaction de polymérisation de la résine. 2897291 -7-  Thanks to this possibility of circulation of a heat transfer fluid, a thermal regulation can be carried out during the infusion operation in order to control the thermal phenomena and in particular exothermic phenomena inherent in the polymerization reaction of the resin. In an advanced form, this regulation may include an instrumentation by a set of temperature sensors disposed on the cover. In the case of using prepreg reinforcements, the hot air circulation makes it possible to put the reinforcement at the temperature necessary to obtain the polymerization reaction of the resin. 2897291 -7-

Dans le même objectif d'optimiser la température de la réaction de polymérisation, on peut prévoir de recouvrir l'extérieur du moule d'une enveloppe analogue à la bâche caractéristique, qui est également reliée à une source d'air à température régulée. Il est ainsi possible d'influencer la température du moule, du 5 coté de la couche extérieure de la future pièce moulée, qui est exposée, et donc plus sensible aux défauts d'aspect.  For the same purpose of optimizing the temperature of the polymerization reaction, it is possible to cover the outside of the mold with a casing similar to the characteristic sheet, which is also connected to a source of controlled temperature air. It is thus possible to influence the temperature of the mold, on the side of the outer layer of the future molded part, which is exposed, and thus more sensitive to appearance defects.

Il ressort de ce qui précède que la bâche servant de couvercle de moule conforme à l'invention présente l'avantage majeur d'autoriser une régulation 10 thermique lors de l'infusion de la résine, par la création d'un flux de fluide caloporteur susceptible de réchauffer la zone d'infusion, au moment de la propagation de la résine, puis d'extraire des calories lorsque la réaction de polymérisation atteint son stade exothermique.  It follows from the foregoing that the cover serving as a mold cover according to the invention has the major advantage of allowing thermal regulation during the infusion of the resin, by the creation of a coolant flow which is capable of heating the infusion zone during the propagation of the resin and then of extracting calories when the polymerization reaction reaches its exothermic stage.

15 Les avantages se traduisent par une maîtrise améliorée des phénomènes de retrait et donc un meilleur respect de surface des objets moulés  The advantages result in improved control of shrinkage phenomena and thus better surface compliance of molded objects

En outre, le procédé permet un gain de temps, par optimisation de la température lors de la réaction chimique.  In addition, the process saves time by optimizing the temperature during the chemical reaction.

Claims (1)

REVENDICATIONS - 1- Bâche (1) destinée à la fermeture d'un moule (4) de moulage par technique de moule fermé, telle que par infusion ou injection de résine, caractérisée en ce qu'elle comporte sur toute ou partie de sa surface, deux couches (2,6) solidarisées, et défmissant entre elles un volume libre (13), et en ce qu'elle comporte des agencements (10) pour l'entrée d'un fluide caloporteur en vue de la circulation du fluide caloporteur à l'intérieur du volume libre (13). -2- Bâche selon la revendication 1, caractérisée en ce que les deux couches sont présentes sur toute la surface de la bâche et sont solidarisées au moins au niveau de leur périphérie. - 3- Bâche selon la revendication 1, caractérisée en ce que les deux couches (2,6) sont présentes sur une partie de la surface de la bâche et sont solidarisées au niveau de la périphérie (7-9) de la couche (6) de moindre superficie. - 4- Bâche selon la revendication 1, caractérisée en ce que les couches (2,6) sont solidarisées de façon réversible. - 5- Bâche selon la revendication 1, caractérisée en ce que les deux couches (2,6) sont solidarisées dans des zones supplémentaires (10) défmissant des séparations entre des canaux (15,16) de circulation du fluide caloporteur à l'intérieur de l'espace libre. - 6- Bâche selon la revendication 1, caractérisée en ce que la couche (2) au regard du moule est réalisée en un matériau compatible avec les solvants de la résine employée lors du procédé d'injection. 25  - 1 tarpaulin (1) intended for closing a mold (4) for molding by closed mold technique, such as by infusion or injection of resin, characterized in that it comprises all or part of its surface, two layers (2,6) secured together and defining between them a free volume (13), and in that it comprises arrangements (10) for the entry of a heat transfer fluid for the circulation of heat transfer fluid to inside the free volume (13). -2- tarpaulin according to claim 1, characterized in that the two layers are present on the entire surface of the sheet and are secured at least at their periphery. - 3- tarpaulin according to claim 1, characterized in that the two layers (2,6) are present on a portion of the surface of the sheet and are secured at the periphery (7-9) of the layer (6). ) of lesser area. - 4- tarpaulin according to claim 1, characterized in that the layers (2,6) are reversibly secured. - 5 tarpaulin according to claim 1, characterized in that the two layers (2,6) are secured in additional zones (10) defining separations between channels (15,16) of circulation of the heat transfer fluid inside free space. - 6 tarpaulin according to claim 1, characterized in that the layer (2) facing the mold is made of a material compatible with the solvents of the resin used in the injection process. 25
FR0651431A 2006-02-14 2006-04-24 BASKET FOR CLOSING A MOLDING MOLD BY FULLY MOLDED TECHNIQUE, AND IN PARTICULAR BY INFUSION OR INJECTION OF RESIN Expired - Fee Related FR2897291B1 (en)