FI91493B - Förfarande för att bilda en metallmatriskomposit - Google Patents
Förfarande för att bilda en metallmatriskomposit Download PDFInfo
- Publication number
- FI91493B FI91493B FI894938A FI894938A FI91493B FI 91493 B FI91493 B FI 91493B FI 894938 A FI894938 A FI 894938A FI 894938 A FI894938 A FI 894938A FI 91493 B FI91493 B FI 91493B
- Authority
- FI
- Finland
- Prior art keywords
- metal
- matrix
- filler
- preform
- matrix metal
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
- C04B41/009—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone characterised by the material treated
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
- C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
- C04B41/50—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements with inorganic materials
- C04B41/51—Metallising, e.g. infiltration of sintered ceramic preforms with molten metal
- C04B41/515—Other specific metals
- C04B41/5155—Aluminium
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
- C04B41/80—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone of only ceramics
- C04B41/81—Coating or impregnation
- C04B41/85—Coating or impregnation with inorganic materials
- C04B41/88—Metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/10—Alloys containing non-metals
- C22C1/1005—Pretreatment of the non-metallic additives
- C22C1/1015—Pretreatment of the non-metallic additives by preparing or treating a non-metallic additive preform
- C22C1/1021—Pretreatment of the non-metallic additives by preparing or treating a non-metallic additive preform the preform being ceramic
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/10—Alloys containing non-metals
- C22C1/1036—Alloys containing non-metals starting from a melt
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/10—Alloys containing non-metals
- C22C1/1036—Alloys containing non-metals starting from a melt
- C22C1/1057—Reactive infiltration
- C22C1/1063—Gas reaction, e.g. lanxide
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
- C04B2111/00905—Uses not provided for elsewhere in C04B2111/00 as preforms
- C04B2111/00913—Uses not provided for elsewhere in C04B2111/00 as preforms as ceramic preforms for the fabrication of metal matrix comp, e.g. cermets
- C04B2111/00931—Coated or infiltrated preforms, e.g. with molten metal
Claims (11)
1. Förfarande för att bilda en makrokompositkropp, känne-tecknat av att a) man väljer en genomtränglig fyllnadsmedelmassa; 5 b) man placerar matrismetallens kalla invid den genomträng-liga fyllnadsmedelmassan; c) man placerar ett införingsorgan mellan fyllnadsmedelmassan och matrismetallens kalla; d) man upphettar matrismetallen tili ett temperaturomräde som 10 ligger ovanför dess smältpunkt för att bilda smält matrisme- tallmassa; och e) ätminstone i nägot skede av processen används ett infiltra-tionsfrämjande medel och/eller föregängare tili ett infiltrations fr ämjande medel för att fä den smälta matrismetallen att 15 strömma genom införingsorganet och spontant infiltrera fyllnadsmedelmassan .
2. Förfarande enligt patentkrav 1, kännetecknat av att den genomträngliga fyllnadsmedelmassan omfattar en förform. 20
3. Förfarande enligt patentkrav 1, kännetecknat av att fyll-nadsmedlets gränsyta definieras med ett barriärmedel, varvid matrismetallen spontant tränger in ända tili barriärmedlet. 25
4. Förfarande enligt patentkrav 1, kännetecknat av att fyll- nadsmedlet innehäller ätminstone ett ämne valt i gruppen be-stäende av pulver, flingor, mikrostärer, fiberkristaller, bubblor, fibrer, partiklar, fibermattor, brutna fiber, kulor, pelletar, smä rörämnen och brandbeständigt tyg. 30
5. Förfarande enligt patentkrav 1, kännetecknat av att nämn-da införingsorgan innehäller ett ämne som den smälta matrismetallen inte väsentligt förmär väta. 35
6. Förfarande enligt patentkrav 1, kännetecknat av att in föringsorganet minskar bindningen mellan fyllnadsmedlet, tili vilket den spontana inträngningen skett, och resten av even-- tuellt kvarbliven matrismetall. 91 4 96
7. Förfarande enligt patentkrav l, kännetecknat av att in-föringsorganet har en tillräcklig tjocklek för att minska förvridning som beror pä olika solidifiering av fyllnadsmedlet tili vilken den spontana inträngningen skett och den eventuel- 5 la matrismetallresten.
8. Förfarande enligt patentkrav l, kännetecknat av att in-föringsorganet bestdr av ett perforerat arkmaterial. 10
9. Förfarande enligt patentkrav 8, kännetecknat av att in- föringsorganet innehdller grafit.
10. Förfarande enligt patentkrav 8, kännetecknat av att in-föringsorganet omfattar ett enda genomgaende hai eller flera 15 hai i nämnda arkmaterial.
11. Förfarande enligt patentkrav 8, kännetecknat av att hälen är sd placerade att de främjar den väsentligt jämna spontana infiltrationen.