FI75179B - Dielektriskt upphettbart polyolefinskum. - Google Patents
Dielektriskt upphettbart polyolefinskum. Download PDFInfo
- Publication number
- FI75179B FI75179B FI831597A FI831597A FI75179B FI 75179 B FI75179 B FI 75179B FI 831597 A FI831597 A FI 831597A FI 831597 A FI831597 A FI 831597A FI 75179 B FI75179 B FI 75179B
- Authority
- FI
- Finland
- Prior art keywords
- acid
- polyolefin
- polyolefins
- weight
- foam
- Prior art date
Description
1 75179
Dielektrisesti kuumennettava polyolefiinivaahto
Keksintö kohdistuu dielektrisesti hitsattaviin polyolefiinivaahtoihin, jotka on valmistettu tyydyttv-5 mättömien polyesterihartsien läsnä ollessa.
Tiedetään ennestään, että määrättyjä muoveja voidaan hitsata suurella taajuudella sähkömagneettisen kentän avulla, jolloin tässä menetelmässä muovimole-kyylit saatetaan värähtelemään ja siten ilman ulkoista 10 kuumennusta tai erittäin vähäisen ulkoisen kuumennuksen kanssa muodostuu hitsaustapahtumassa vaadittava lämpö itse muovissa. Tämä tarkoittaa, että vain tarkoin määrättyjä muoveja voidaan hitsata suurtaajuuden avulla, kuten esimerkiksi polyvinyylikloridia. Polyolefiinin, erikoi-15 sesti polyetyleenit eivät ole näitä.
Mutta polyolefiinivaahtojen dielektrinen kuumennus on taloudellisesti erittäin mielenkiintoinen, koska tällöin on mahdollista materiaalin suojaavan kuumennuksen lisäksi muutamien sekuntien aikana käyttää myös hyödyksi suur-20 taajuuskentän elektrodeja samanaikaisesti muodonmuodos- tavana työkaluna. On suoritettu runsaasti kokeita myös polyolefiinien muuttamiseksi määrättyjen lisäaineiden avulla dielektrisesti hitsattaviksi.
On mm. voitu suorittaa polyetyleenin suurtaajuus-25 hitsausta sekoittamalla sitä etyleeni/vinyyliasetaatti- kopolymerisaattien kanssa.
Tämän tapaiset seokset eivät kuitenkaan sovellu verkkoutettujen vaahtojen valmistamiseen,koska valmistettaessa ristiliitettäviä ja vaahdotettavia ratoja 30 voi verkkoutumista tapahtua jo suulakepuristimessa.
Edelleen tiedetään, että lisäämällä monomeerisiä pehmentimiä kuten dioktyyliftalaattia voi useiden muovien dielektrinen kuumennus olla mahdollista.
Tämän tapaisia pehmentimiä ei kuitenkaan voida 35 lisätä niiden yhteensopimattomuuden vuoksi polyolefiinien kanssa ja haittaavat ne jo vähäisinä määrinä polyolefii- 2 75179 nien vaahtoamista.
Lisäksi on erilaisten täyteaineiden kuten esimerkiksi bariumferriitin avulla mahdollista saavuttaa poly-olefiinien kuumennus dielektrisesti.
5 Kuitenkin myös nämä lisäaineet vaikuttavat poly- olefiinien vaahtoamiseen niin,että ei ole mahdollista valmistaa pienen tilavuuspainon omaavia polyolefiinivaah-to ja.
Myös klooratun polyetyleenin, joka johtaa suurtaa-10 juuksien kuumentumisen paranemiseen, käyttö on mahdollis ta. Tällä lämmitysvaikutuksella ei kuitenkaan ole teknillistä merkitystä.
Yllättävästi onnistuu kuitenkin modifioimalla polyolefiineja a,3-tyydyttymättömillä polyestereillä 15 dielektrisesti kuumennettavien vaahtojen valmistus.
Keksinnön kohteena on täten dielektrisesti kuumennettava polyolefiinivaahto, joka sisältää a,β-tyydytty-mättömiä polyestereitä 3-20, edullisesti 5-10 paino-%:n suuruisen määrän.
20 Keksinnön mukaisia vaahtoja voidaan valmistaa sekä jatkuvan että myös epäjatkuvan menetelmän avulla, kuten esimerkiksi DE-patentissa 16 94 130 tai US-patentissa 3 711 584 on esitetty.
Keksinnön mukaiset vaahdot valmistetaan edullisesti 25 siten, että polyolefiinien sekoitus vaahdotusaineiden, verkkutusaineiden, haluttaessa muiden tavanomaisten lisäaineiden sekä keksinnön mukaisesti käytettävien, edellä esitettyinä määrinä lisättävien polyesterien kanssa tapahtuu sekoitustelalaitteessa tai suulakepu-30 ristimessa muotokappaleen valmistamisen, kuten levy jen tai jatkuvien ratojen valmistamisen seuraamana verkkoutus- ja vaahdotusaineen hajaantumislämpötilan alapuolella olevissa lämpötiloissa. Keskimääräinen viipymisaika sekoituslaitteessa on mitoitettava siten, 35 että vaahdotettavan seoksen verkkoutumista ei tässä vai-
II
75179 3 heessa oleellisesti tapahdu. Sitten suoritetaan poly-olefiinilevyn tai -radan ristikytkentä edullisesti vaahdotusaineen hajaantumislämpötilan alapuolella olevissa lämpötiloissa mutta ristikytkentäaineen hajaantu-5 mislämpötilan yläpuolella olevissa lämpötiloissa kuumen tamalla tai säteilyttämällä polyolefiinin sulaviskosi-teetin kasvaessa.Kohotettaessa lämpötila edelleen vaahdotusaineen hajaantumislämpötilaan tai sen yläpuolelle vaahtoutuu muotokappale. Vaahdotusaineen ja ristikytkentä-10 aineen kulloistenkin määrien sekä menetelmäolosuhteiden 3 mukaan muodostuu vaahto, jonka tiheys on 15-300 kg/m , edullisesti 20-200 kg/m^.
Edullisesti käytetään keksinnön mukaista menetelmää vaahtoratojen jatkuvaan valmistukseen, esimerkiksi 15 DE-patentissa 16 94 130 esitetyn menetelmän mukaan, jolloin kuumennus tapahtuu uunissa ja liikkuvaa polyolefiini-rataa tuetaan päättymättömän kuljetusnauhan avulla.
Vaahdotusaineena käytetään tarkoituksenmukaisesti lämmössä kaasua luovuttavaa ainetta, jonka hajaantumis-20 lämpötila on korkeampi kuin käytetyn ristikytkentäaineen, edullisesti orgaanista peroksidia. Sopivia vaahdotusainei-ta ovat esimerkiksi atsodikarbonamidi' ja/tai p,p,-oksi-bis-bentseenisulfonyylihydratsidi ja/tai dinitrosopenta-metyleenitetramiini.
25 Suositeltava vaahdotusaine on atsodikarbonamidi, jonka hajaantumislämpötila tai hajaantumisalue on vähintäin 190°C. Vaahdotusaineen käytetty määrä määräytyy valmistettavan vaahtoaineen halutun tiheyden mukaan ja on se yleensä välillä 0,5 - 25 paino-%, edullisesti 30 1-20 paino-% kokonaisseoksesta laskettuna.
Keksinnön mukaisten vaahtojen verkkoutus voidaan suorittaa tunnetulla tavalla suurenergisen säteilyn vaikutuksen avulla tai tunnettuja ristikytkentäainei-ta käyttäen, edullisesti orgaanisten peroksidien 35 avulla.
4 75179
Orgaanisena peroksidina voidaan polyolefiinikoos-tumuksen mukaan käyttää 2,5-dimetyyli-2,5-di-(tert.-butyyliperoksi)-heksaania, tert.-butyylihydroperoksidia, kumyyli-tert.-butyyliperoksidia, di-tert.-butyyliperok-5 sidia, edullisesti dikumyyliperoksidia. Peroksidia lisätään 0,3-1,5 paino-% suuruinen määrä polyolefiinista laskettuna.
Polyolefiineina voidaan käyttää polyetyleeniä tai polypropyleeniä haluttaessa myös niiden seoksia, 10 edullisesti polyetyleeniä ja erikoisesti matalapaine-polyetyleeniä, jonka tiheys on 0,94-0,97 g/cm ja/tai suurpainepolyetyleeniä, jonka tiheys on 0,91 - noin 0,94 g/cm^, edullisesti suurpainepolyetyleeniä. Termillä "polyolefiinit" tarkoitetaan myös polyolefiini-15 kopolymeerejä, edullisesti niitä, joiden valmistuksessa käytetään monomeeriseoksia, joissa pääosuus muodostuu polyolefiineista.
Näitä kopolymeerejä ovat esimerkiksi etyleeni-propyleeni-kopolymeerit, etyleeni-butyleeni-kopolymeerit, 20 etyleenin ja akryylihappoesterien tai niiden johdannaisten kopolymerisaatit, etyleenin ja metakryylihapon tai sen johdannaisten kopolymeerit. Myös edellä mainittujen poly-olefiinien seoksista kautsujen ja/tai muovien kanssa voidaan keksinnön mukaan valmistaa vaahtoaineita. Tällöin 25 ymmärretään seoksilla esimerkiksi niitä, jotka sisältävät 50 paino-% tai enemmän polyolefiineja. Polyolefiinien kanssa sekoittuvia kautsuja ovat esimerkiksi luonnonkautsu, etyleeni-kautsu, butyylikautsu, polyisobutyleeni, ABS-kautsu, polybutadieeni, polybuteeni ja polyisopreeni.
30 Polyolefiinien kanssa sekoittuvia muoveja ovat esimerkik si polyeteeni, kloorattu polyeteeni tai sulfokloorattu polyetyleeni tai vastaavat aineet.
Modifioivina aineina tulevat kyseeseen a,β-dyydytty-mättömät polyesterit.
35 Suositeltavia a,3-tyydyttymättömiä polyestereitä ovat tunnetut polykondensaatiotuotteet, jotka on saatu a,3-
II
5 75179 yksinkertaisesti tyydyttymättömistä, 4-8 C-atomia sisältävistä dikarboksyylihapoista tai niiden johdannaisista kuten esimerkiksi anhydrideistä halutaessa sekoitettuina 200 mooli-%:iin saakka tyydyttymättömistä dikarboksyylihapoista laskettuna vähitäin yhden tyydy-5 tetyn alifaattisen tai sykloalifaattisen tai aromaattisen 8-10 C-atomia sisältävän dikarboksyylihapon tai sen johdannaisen kanssa vähintäin yhden alifaattisen, sykloalif aattisen tai aromaattisen polyhydroksiyhdisteen, erikoisesti 2-8 C-atomia sisältävän dihydroksiyhdisteen 10 kanssa, edullisesti ne ovat polyestereitä, kuten J.
Björksten et ai., kirjassa "Polyesters and their Applications", julkaissut Reinhold Publishing Corp., New York 1956, ovat esittäneet.
Esimerkkejä edullisesti käytettävistä tyydyttv-15 mättömistä dikarboksyylihapoista tai niiden johdannaisista ovat maleiinihappo tai maleiinihappoanhydridi ja fumaarihappo. Voidaan kuitenkin käyttää myös esimerkiksi mesakonihappoa, sitrakonihappoa, itakonihappoa tai kloorimaleiinihappoa. Esimerkkejä haluttaessa myös käy-20 tettävistä aromaattisista, tyydytetyistä, alifaattisis- ta tai sykloalifaattisista dikarboksyylihapoista tai niiden johdannaisista ovat ftaalihappo tai ftaalihappo-anhydridi, isoftaalihappo, tereftalaattihappo, heksa-tai tetrahydroftaalihappo tai niiden anhydridit, endomety-25 leenitetrahydroftaalihappo tai sen anhydridi, meripihka- happo tai meripihkahappoanhydridi ja meripihkahappoeste-rit ja -kloridit, adipiinihappo, sebasiinihappo. Vaikeasti syttyvien hartsien valmistamiseksi voidaan käyttää myös halogenoituja, dikarboksyylihappoja, kuten esimer-30 kiksi heksaklooriendometyleenitetrahydroftaalihappoa, tetraklooriftaalihappoa tai tetrabromiftaalihappoa. Kaksiarvoisina alkoholeina voidaan lisätä edullisesti ali-faattisia C2_2Q-alkoholeja, kuten etyleeniglykolia, propaanidioli-1,3- dietyleeniglykolia, dipropyleenigly-35 kolia, butaanidioli-1,3, butaanidioli-1,4, neopentyy- · liglykolia, heksaanidioli-1,6, 2,2-bis-(4-hydroksisyklo- 6 75179 heksyyli)-propaania, perhydrobisfenolia fenoleina edullisesti bisoksalkyloitua bisfenolia A:ta ja muita aineita. Edullisesti käytetään etyleeniglykolia, propaanidioli-1,2 dietyleeniglykolia ja dipropyleeniglykolia.
5 Muutkin modifikaatiot ovat mahdollisia lisäämällä yksi-, kaksi- ja neljäarvoisia 1-6 C-atomia sisältäviä alkoholeja kuten metanolia, etanolia, butanolia, allyy-lialkoholia, bentsyylialkoholia, sykloheksanolia ja tetrahydrofurfuryylialkoholia, trimetyylipropaania, gly-10 seriiniä ja pentaerytriittiä, kaksi- ja useampiarvois- ten, 3-6 C-atomia sisältävien alkoholien mono-, di- ja triallyylieettereitä ja bentsyylieettereitä DE-patentin 1 024 654 mukaisesti, esimerkiksi trimetylolipropaanidi-allyylieetteriä sekä lisäämällä monokarboksyylihappoja 15 kuten bentsoehappoa tai akryylihappoa.
Polyesterien happoluvut ovat edullisesti välillä 10-100, edullisesti välillä 20-70, 0H-3uvut välillä 10-150, edullisesti välillä 20-100 ja keskiarvona määrätty molekyylipaino välillä noin 500-5000, edul- 20 lisesti välillä noin 1000-3000 (mitattuna höyrynpaineosmo- metrisesti dioksaanissa ja asetonissa).
Tyydyttymättömien polyesterien kanssa kopolymeroitäviksi, tyydyttymättömiksi monomeereiksi soveltuvat poly-esteriteknologiassa käyttökelpoiset tyydyttymättömät yh-25 disteet, jotka sisältävät edullisesti α-substituoituja vinyyli- tai vinylideeniryhmiä tai 3-substituoituja allyyliryhmiä, edullisesti styreeniä; myös voidaan käyttää esimerkiksi ydinkloorattuja ja -alkyloituja tai alkenyloituja styreenejä, jolloin alkyyliryhmät voivat 30 sisältää 1-4 hiiliatomia, esimerkiksi vinyylitolueenia, divinyylibentseeniä, a-netyylistyreeniä, tert.-butyyli-styreeniä,klooristyreeniä; 2-6 hiiliatomia sisältävien karboksyylihappojen vinyyliestereitä, edullisesti vinyy-liasetaattia, vinyylipropionaattia, vinyylisyklohfeksaa-35 nia, akryylihappoa ja metakryylihappoa ja/tai niiden es- tereitä (edulliset! vinyyli-, allyyli- ja metallyylieste-
II
7 75179 riä), jotka sisältävät 1-4 hiiliatomia alkoholikomponen-tissa, niiden amideja ja nitriilejä, maleiinihappoan-hydridiä, -puoli- ja -diesteriä, jotka sisältävät 1-4 hiiliatomia alkoholikomponentissa, -puoli- ja -diamidia 5 tai syklisiä imidejä kuten butyyliakrylaattia, metyyli- metakrylaattia, akryylinitriiliä, N-metyylimaleiini-imidiä tai N-sykloheksyylimaleiini-imidiä; allyyliyhdis-teitä kuten allyylibentseeniä ja allyyliestereitä kuten 10 allyyliasetaattia, ftaalihappodiallyyliesteriä, isoftaa- lihappodiallyyliesteriä, fumaarihappodiallyyliesteriä, allyylikarbonaattia, diallyylikarbonaattia, triallyyli-fosfaattia ja triallyylisyanuraattia.
Yllättävästi antaa tyydyttymättömien polyesterien 15 lisäys valmistuksen edellyttämässä määrässä mahdollisuu den valmistaa kemiallisesti ristikytkettyjä polyole-fiinivaahtoja, jolloin ristikytkentään edullisesti käytetyn peroksidin määrää voidaan huomattavasti alentaa.
Taloudellisten etujen lisäksi johtaa tämä alenemi-20 nen siihen, että osittain pahanhajuisia hajaantumis- tuotteita, joita muodostuu pääasiallisesti käytetystä dikumyyliperoksidistä, esimerkiksi asetofenonia syntyy huomattavasti vähäisempiä määriä.
Myös tavanomaisia lisäaineita, joita tavallisesti 25 käytetään polyolefiineihin perustuvien muovien kanssa, kuten esimerkiksi valolta suojelevia aineita, pigmenttejä, täyteaineita, palamista estäviä aineita, antistaat-tisia aineita, liukastusaineita, voidaan lisätä verkkoutet-tavaan ja vaahdotettavaan seokseen ennen käsittelyä muoto-30 kappaleeksi.
Keksinnön mukaiset polyolefiinivaahdot ovat dielektrisesti kuumennettavia ja sallivat siten edullisen jatkokäsittelyn sinänsä tunnettujen menetelmien avulla dielektristä kuumennusta käyttäen, esimerkiksi suurtaa-35 juushitsauksen, muovauksen ja meiston noin 27 mHz ole villa taajuuksilla. Täten voidaan erikoisesti lämpötila- 8 751 79 herkkiä materiaaleja, kuten tekstiilikudonnaisia, kiinnittää hitsaamalla polyolefiinivaahtoon yksinkertaisesti.
Esimerkki 1
Suulakepuristimessa puristetaan seuraavien tuottei-5 den muodostamaa seosta esitettyinä paino-osina levyksi:
Suurpainepolyetyleeniä 50 paino-osaa
Kloorattua polyetyleeniä 30 paino-osaa
Tyyydyttymätöntä polyesteriä 5 paino-osaa
Atsodikarbonamidia 14,5 paino-osaa 10 Dikumyyliperoksidia 0,3 paino-osaa
Valmistettiin kaupallista polyesteriä polykonden-soimalla maleiinihappoanhydridiä, etyleeniä, etyleeni-glykolia, dipropyleeniglykolia ja bentsyylialkoholia.
Muotoilumassan suulakepuristuslämpötila on noin 15 130°C niin, ettei esiinny enempää vaahtomaista kuin verk- koutumista.
Täten saatu levy kuumennetaan kuumailmauunissa, kuten DE-patentissa 16 94 130 on esitetty, 210°C lämpötilaan, jolloin muodostuu tasaisesti verkkoutunut vaahto-20 rata.
Vaahtorata jäähdytetään raitisilmapuhaltimellä ja kosketuksen avulla jäähdytettyjen telojen kanssa. Vaahdon pinta on sileä ja sen tilavuuspaino on 35 kg/m3.
Seuraavassa käsittelyssä kaupallisessa suurtaa-25 juushitsauskoneessa 27,12 mHz taajuudella ja 5/7 baarin paineessa on täten valmistetun vaahdon moitteeton hitsaaminen mahdollista sekä itseensä että erilaisten tekstilien kanssa.
Esimerkki 2 30 Kuten esimerkissä 1 on esitetty, valmistetaan pienentämällä ajoainemäärää polyetyleenivaahtorata,
O
jonka paksuus on 3 mm ja tiheys 200 kg/m . Kahden vaah-toradan väLiin sijoitetaan etyleenivinyyliasetaatti-kopolymeeriä oleva kalvo, jonka paksuus on 50 mikromet-35 riä ja radat hitsataan yhteen suurtaaj uuslaitteessa 10 cm:n leveydeltä 5 kW tehoa käyttäen. Radat kiinnittyvät toisiinsa vaikeuksitta eikä niitä voida käytännöllisesti katsoen eroittaa lainkaan yksittäisestä radasta.
Il
Claims (6)
- 9 75179
- 1. Dielektrisesti kuumennettava, edullisesti hitsattava polyolefiinivaahto, t u n n e t tu siitä, 5 että se sisältää 3-20 paino-% vaahdosta laskettuna tyydyttymätöntä polyesteriä.
- 2. Patenttivaatimuksen 1 mukainen polyolefiinivaahto,' t u n n e t tu siitä, että se sisältää 5-10 paino-% tyydyttymätöntä polyesteriä.
- 3. Patenttivaatimuksen 1 tai 2 mukainen polyole- fiinivaahto, t u n n e t tu siitä, että polyesteri on kovetettu 100-%:sesti.
- 4. Patenttivaatimuksien 1-3 mukainen polyolefiinivaahto, t u n n e t tu siitä, että se on ristikytketty. 15 5. Patenttivaatimuksien 1-4 mukainen polyolefiini vaahto, t u n n e t tu siitä, että käytettävän polyesterin happoluku on välillä 10-100 ja 0H-luku on välillä 10-150.
- 6. Patenttivaatimuksien 1-5 mukainen polyolefiini-20 vaahto, t u n n e t tu siitä, että käytetään polyes teriä, jonka happoluku on välillä 20-70 ja 0H-luku välillä 20 - 100.