FI112785B - Biaxialt högorienterad polypropylenfolie och förfarande för framställning av denna - Google Patents

Biaxialt högorienterad polypropylenfolie och förfarande för framställning av denna Download PDF

Info

Publication number
FI112785B
FI112785B FI952326A FI952326A FI112785B FI 112785 B FI112785 B FI 112785B FI 952326 A FI952326 A FI 952326A FI 952326 A FI952326 A FI 952326A FI 112785 B FI112785 B FI 112785B
Authority
FI
Finland
Prior art keywords
film
weight
polypropylene film
transverse
resin
Prior art date
Application number
FI952326A
Other languages
English (en)
Finnish (fi)
Other versions
FI952326A (sv
FI952326A0 (sv
Inventor
Ursula Murschall
Herbert Peiffer
Detlef Busch
Harald Lohmann
Original Assignee
Trespaphan Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Trespaphan Gmbh filed Critical Trespaphan Gmbh
Publication of FI952326A0 publication Critical patent/FI952326A0/sv
Publication of FI952326A publication Critical patent/FI952326A/sv
Application granted granted Critical
Publication of FI112785B publication Critical patent/FI112785B/sv

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C55/00—Shaping by stretching, e.g. drawing through a die; Apparatus therefor
    • B29C55/005—Shaping by stretching, e.g. drawing through a die; Apparatus therefor characterised by the choice of materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F8/00—Chemical modification by after-treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/10—Polymers of propylene
    • B29K2023/12—PP, i.e. polypropylene

Landscapes

  • Chemical & Material Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Laminated Bodies (AREA)
  • Shaping By String And By Release Of Stress In Plastics And The Like (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)

Claims (8)

1. Biaxialt orienterad polypropylenfolie innehäl-lande harts, kännetecknad av att den n-heptanolösliga 5 delen av tolien uppvisar ett med 13C-NMR-spektroskopi matt kedjeisotaxicitetsindex pä minst 85 - 94 %, att basskiktet innehäller mindre än 10 vikt-% harts och att tolien är ut-tänjd salunda att rivstyrkan i längdriktningen är över 170 N/mm2 och i tvärriktningen over 290 N/mm2, och att produk-10 ten av de i längd- och tvärriktningen matta rivstyrkorna är over 50 000 (N/mm2)2.
2. Polypropylenfolie enligt patentkrav 1, kännetecknad av att produkten av foliens elasticitetsmo-dul i längdriktningen och foliens elasticitetsmodul i 15 tvärriktningen är över 9-10e (N/mm2)2.
3. Polypropylenfolie enligt patentkrav 1 eller 2, kännetecknad av att vattenänggenomsläppligheten är < 24/tjocklek i enheten /nri[g/m2-d] .
4. Polypropylenfolie enligt nägot av patentkraven 20 1 - 3, kännetecknad av att foliens glans är > 110 % och slöjbildning s 2,5. ,1
5. Polypropylenfolie enligt nägot av patentkraven 1-4, kännetecknad av att folien är uttänjd i längd-, : riktningen inom omrädet 6:1 - 9:1 och i tvärriktningen ,·, 25 inom omrädet 7,5:1 - 15:1, varvid produkten av längdtöj - ningsförhällandet och tvärtöjningsförhällandet är > 60.
6. Polypropylenfolie enligt nägot av patentkraven 1 - 5, kännetecknad av att folien bestär endast av * ‘ basskiktet. '·.·1 30
7. Förfarande för framställning av en polypropy- lenfolie, väri polymeren/polymererna pressas och smälts i : en extruder, smältan/smältorna extruderas genom en slits- dysa och spolas pä ätminstone en dragvals, varvid smäl- * » *“ tan/smältorna äter härdnar, och den pä sä sätt erhällna : ‘ 35 förfolien orienteras i längd- och tvärriktningen, kän- netecknat av att orienteringen utförs i längd- och 33 1 12785 tvärriktningen pä sa sätt att produkten av längdtöjnings-förhällandet och tvärtöjningsförhällandet är > 60.
8. Förfarande enligt patentkrav 7, känneteck-nat av att tolien orienteras i längdriktningen i ett för-5 hällande av 6:1 - 9:1, särskilt 6,5:1 - 8:1, och i tvärriktningen i ett förhällande av 7,5:1 - 15:1, särskilt 8:1 - 13:1. 1 » »
FI952326A 1994-05-16 1995-05-12 Biaxialt högorienterad polypropylenfolie och förfarande för framställning av denna FI112785B (sv)