ES2148141T3 - Revestimiento de oxido no cromado para sustratos de aluminio. - Google Patents
Revestimiento de oxido no cromado para sustratos de aluminio.Info
- Publication number
- ES2148141T3 ES2148141T3 ES91103498T ES91103498T ES2148141T3 ES 2148141 T3 ES2148141 T3 ES 2148141T3 ES 91103498 T ES91103498 T ES 91103498T ES 91103498 T ES91103498 T ES 91103498T ES 2148141 T3 ES2148141 T3 ES 2148141T3
- Authority
- ES
- Spain
- Prior art keywords
- cobalt
- solution
- conversion coating
- hexavalent complex
- iii hexavalent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
(A) UN PROCESO PARA FORMAR UN RECUBRIMIENTO DE CONVERSION DE COBALTO SOBRE UN SUSTRATO METALICO, IMPARTIENDO ASI UNA RESISTENCIA A LA CORROSION Y PROPIEDADES DE ADHESION DE PINTURA. LA INVENCION SE DESARROLLO PARA SUSTITUIR A LA MANERA EN QUE SE LLEVABA A CABO EL PROCESO ACIDO CROMATICO. EL PROCESO CONSISTE EN LOS PASOS SIGUIENTES: (A) PRODUCIR UNA SOLUCION DE CONVERSION DE COBALTO QUE CONTENGA UNA SOLUCION ACUOSA, ALCALINA, QUE CONTIENE UN COMPLEJO HEXAVALENTE DE COBALTO-III SOLUBLE, SIENDO LA CONCENTRACION DEL COMPLEJO HEXAVALENTE DE COBALTO-III DE 0,1 MOL APROXIMADAMENTE POR GALON DE SOLUCION AL LIMITE DE SATURACION DEL COMPLEJO HEXAVALENTE DE COBALTO-III; Y (B) PONER EN CONTACTO EL SUSTRATO CON LA SOLUCION DURANTE UN PERIODO DE TIEMPO SUFICIENTE, CON LO QUE SE FORMA EL RECUBRIMIENTO DE CONVERSION DE COBALTO. EL SUSTRATO PUEDE SER ALUMINIO O UNA ALEACION DE ALUMINIO ASI COMO CD PLATEADO, ZN PLATEADO, ZN-NI PLATEADO Y ACERO. EL COMPLEJO HEXAVALENTE DE COBALTO-III PUEDE ESTAR PRESENTE EN FORMA DE [CO-(NH SUB 3) SUB 6]X SUB 3 EN DONDE X ES CL, BR, NO SUB 3, CN, SCN, PO SUB 4, C SUB 2H SUB 3O SUB 2 O CO SUB 3. (B) UNA SOLUCION DE RECUBRIMIENTO DE CONVERSION QUIMICA PARA PRODUCIR EL RECUBRIMIENTO DE CONVERSION DE COBALTO SOBRE UN SUSTRATO METALICO, INCLUYENDO LA SOLUCION UNA SOLUCION ACUOSA, ALCALINA, QUE CONTIENE UN COMPLEJO HEXAVALENTE DE COBALTO-III SOLUBLE, SIENDO LA CONCENTRACION DEL COMPLEJO HEXAVALENTE DE COBALTO-III DE 0,1 MOL APROXIMADAMENTE POR GALON DE SATURACION AL LIMITE DE SATURACION DEL COMPLEJO HEXAVALENTE DE COBALTO-III. LA SOLUCION DE CONVERSION DE COBALTO SE PUEDE PREPARAR MEDIANTE UNA SECUENCIA DE FORMACION DEL BAÑO QUE CONSISTE EN LOS PASOS SIGUIENTES: (A) DISOLVER UNA SAL DE AMONIO; (B) DISOLVER A CONTINUACION UNA SAL DE COBALTO-II; Y (C) AÑADIR DESPUES HIDROXIDO DE AMONIO (AMONIACO). (C) UN ARTICULO RECUBIERTO QUE PRESENTA UNA RESISTENCIA A LA CORROSION Y PROPIEDADES DE ADHESION A LA PINTURA, CONSTANDO EL SUSTRATO DE: (A) UN SUSTRATO METALICO; Y (B) UN RECUBRIMIENTO DE CONVERSION DE COBALTO FORMADO SOBRE EL SUSTRATO, INCLUYENDO EL RECUBRIMIENTO DE CONVERSION DE COBALTO OXIDO DE ALUMINIO ALO SUB 3 COMO EL MAYOR PORCENTAJE DE VOLUMEN Y OXIDOS DE COBALTO COO, COO SUB 4 Y CO SUB 2O SUB 3 .
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US07/525,800 US5298092A (en) | 1990-05-17 | 1990-05-17 | Non-chromated oxide coating for aluminum substrates |
Publications (1)
Publication Number | Publication Date |
---|---|
ES2148141T3 true ES2148141T3 (es) | 2000-10-16 |
Family
ID=24094649
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES91103498T Expired - Lifetime ES2148141T3 (es) | 1990-05-17 | 1991-03-07 | Revestimiento de oxido no cromado para sustratos de aluminio. |
Country Status (8)
Country | Link |
---|---|
US (3) | US5298092A (es) |
EP (1) | EP0458020B1 (es) |
JP (1) | JP3194593B2 (es) |
AT (1) | ATE194857T1 (es) |
DE (1) | DE69132326T2 (es) |
DK (1) | DK0458020T3 (es) |
ES (1) | ES2148141T3 (es) |
GR (1) | GR3034635T3 (es) |
Families Citing this family (39)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5551994A (en) * | 1990-05-17 | 1996-09-03 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
US5298092A (en) * | 1990-05-17 | 1994-03-29 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
US5472524A (en) * | 1990-05-17 | 1995-12-05 | The Boeing Company | Non-chromated cobalt conversion coating method and coated articles |
CA2087473C (en) * | 1990-05-17 | 2001-10-16 | Matthias P. Schriever | Non-chromated oxide coating for aluminum substrates |
US5411606A (en) * | 1990-05-17 | 1995-05-02 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
US5468307A (en) * | 1990-05-17 | 1995-11-21 | Schriever; Matthias P. | Non-chromated oxide coating for aluminum substrates |
EP0488430B1 (en) * | 1990-11-30 | 1997-06-11 | The Boeing Company | Non-chromated cobalt conversion coating |
DK0523288T3 (da) * | 1991-07-19 | 1999-08-02 | Boeing Co | Ikke-chromaterede oxidovertræk til aluminiumsubstrater |
MY111371A (en) * | 1992-06-25 | 1999-12-31 | Boeing Co | Non-chromated oxide coating for aluminum substrates. |
CN1138873C (zh) * | 1992-06-25 | 2004-02-18 | 波音公司 | 在金属基体上形成钴转化膜层的方法,钴转化镀膜液及其用途 |
US5948178A (en) * | 1995-01-13 | 1999-09-07 | Henkel Corporation | Composition and process for forming a solid adherent protective coating on metal surfaces |
WO1996021753A1 (en) * | 1995-01-13 | 1996-07-18 | Henkel Corporation | Composition and process for forming a solid adherent protective coating on metal surfaces |
ZA962178B (en) * | 1995-03-22 | 1996-07-29 | Henkel Corp | Compositions and processes for forming a solid adherent protective coating on metal surfaces |
US6059867A (en) * | 1995-10-10 | 2000-05-09 | Prc-Desoto International, Inc. | Non-chromate corrosion inhibitors for aluminum alloys |
US5951747A (en) * | 1995-10-10 | 1999-09-14 | Courtaulds Aerospace | Non-chromate corrosion inhibitors for aluminum alloys |
US5866652A (en) * | 1996-02-27 | 1999-02-02 | The Boeing Company | Chromate-free protective coatings |
US5940729A (en) * | 1996-04-17 | 1999-08-17 | International Business Machines Corp. | Method of planarizing a curved substrate and resulting structure |
FR2752851B1 (fr) * | 1996-09-02 | 1998-11-13 | Cfpi Ind | Bain et procede de phosphatation de substrats metalliques, concentre pour la preparation de ce bain et substrats metalliques traites a l'aide de ces bain et procede |
US5873953A (en) * | 1996-12-26 | 1999-02-23 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
US6315823B1 (en) | 1998-05-15 | 2001-11-13 | Henkel Corporation | Lithium and vanadium containing sealing composition and process therewith |
DE19834394A1 (de) * | 1998-07-30 | 2000-02-03 | Rheinmetall W & M Gmbh | Waffenrohr mit einer verschleißmindernden Hartchromschicht |
US6432225B1 (en) | 1999-11-02 | 2002-08-13 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
WO2003060019A1 (en) * | 2002-01-04 | 2003-07-24 | University Of Dayton | Non-toxic corrosion protection pigments based on cobalt |
US7235142B2 (en) * | 2002-01-04 | 2007-06-26 | University Of Dayton | Non-toxic corrosion-protection rinses and seals based on cobalt |
US7294211B2 (en) * | 2002-01-04 | 2007-11-13 | University Of Dayton | Non-toxic corrosion-protection conversion coats based on cobalt |
US6946078B2 (en) * | 2002-02-27 | 2005-09-20 | Lynntech, Inc. | Electrochemical method and apparatus for producing and separating ferrate (VI) compounds |
US7045051B2 (en) * | 2002-02-27 | 2006-05-16 | Lynntech, Inc. | Electrochemical method for producing ferrate(VI) compounds |
US20040011252A1 (en) * | 2003-01-13 | 2004-01-22 | Sturgill Jeffrey A. | Non-toxic corrosion-protection pigments based on manganese |
US20030221590A1 (en) * | 2003-01-13 | 2003-12-04 | Sturgill Jeffrey A. | Non-toxic corrosion-protection pigments based on permanganates and manganates |
US7090112B2 (en) * | 2003-08-29 | 2006-08-15 | The Boeing Company | Method and sealant for joints |
US6905060B2 (en) * | 2003-10-24 | 2005-06-14 | The Boeing Company | Method and sealant for weld joints |
US20050282003A1 (en) * | 2004-06-18 | 2005-12-22 | Alexander Mayzel | Coated article and process for coating article with anticorrosive finish |
US7732033B2 (en) * | 2005-08-26 | 2010-06-08 | The Curators Of The University Of Missouri | Sealants for structural member joints and methods of using same |
CN101384751B (zh) * | 2006-02-14 | 2013-01-02 | 汉高股份及两合公司 | 在金属表面上使用的原地干燥的三价铬抗腐蚀涂料的组合物与方法 |
KR20090018067A (ko) * | 2006-05-10 | 2009-02-19 | 헨켈 아게 운트 코. 카게아아 | 금속 표면 상의 내부식성 코팅에 사용하기 위한 개선된 3가 크롬-함유 조성물 |
US20110005287A1 (en) * | 2008-09-30 | 2011-01-13 | Bibber Sr John | Method for improving light gauge building materials |
US11072712B2 (en) | 2011-06-08 | 2021-07-27 | Henkel Ag & Co. Kgaa | Corrosion resistant sol-gel coating and composition and process for making the same |
CA2808981A1 (en) * | 2013-03-05 | 2014-09-05 | Sherritt International Corporation | Method of recovering metals while mitigating corrosion |
US10156016B2 (en) | 2013-03-15 | 2018-12-18 | Henkel Ag & Co. Kgaa | Trivalent chromium-containing composition for aluminum and aluminum alloys |
Family Cites Families (50)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1551613A (en) * | 1923-03-07 | 1925-09-01 | Aluminum Co Of America | Coated aluminum articles and process and means for producing same |
US1607676A (en) * | 1924-10-29 | 1926-11-23 | Firm Dr Otto Sprenger Patentve | Process for obtaining metal coatings on articles of aluminum and aluminum alloys |
DE745704C (de) * | 1941-04-18 | 1944-12-06 | Verfahren zur Herstellung glasklarer und farbloser Oxydschichten auf Aluminium und seinen Legierungen | |
US2906009A (en) * | 1954-04-30 | 1959-09-29 | Siemens Ag | High temperature-resisting insulating coatings of increased durability and methods of producing same |
US2796370A (en) * | 1955-03-04 | 1957-06-18 | Charles W Ostrander | Composition and method for producing corrosion resistant protective coating on aluminum and aluminum alloys |
US2796371A (en) * | 1955-03-16 | 1957-06-18 | Allied Res Products Inc | Corrosion resistant protective coating on aluminum and aluminum alloys |
NL283192A (es) * | 1961-09-14 | |||
US3138479A (en) * | 1961-12-20 | 1964-06-23 | Burroughs Corp | Method for the electroless deposition of high coercive magnetic film |
US3403035A (en) * | 1964-06-24 | 1968-09-24 | Process Res Company | Process for stabilizing autocatalytic metal plating solutions |
US3423214A (en) * | 1965-06-30 | 1969-01-21 | Ibm | Magnetic cobalt and cobalt alloy plating bath and process |
US3438798A (en) * | 1965-08-23 | 1969-04-15 | Arp Inc | Electroless plating process |
US3592747A (en) * | 1966-08-17 | 1971-07-13 | Samuel L Cohn & Charles C Cohn | Method of forming a decorative and protective coating on a surface |
US3444007A (en) * | 1967-03-13 | 1969-05-13 | Hooker Chemical Corp | Process of forming paint-base coatings on zinc and zinc alloy surfaces |
US3615740A (en) * | 1970-02-02 | 1971-10-26 | Pennwalt Corp | Chromate conversion coating compositions containing prusside accelerator |
US3790453A (en) * | 1971-03-22 | 1974-02-05 | Lockheed Aircraft Corp | Corrosion protected anodized aluminum surfaces |
US3870607A (en) * | 1971-04-21 | 1975-03-11 | Avco Corp | Bearing Manufacture |
US3819424A (en) * | 1971-06-17 | 1974-06-25 | Oxy Metal Finishing Corp | Method and composition for treating metal surfaces |
US3954510A (en) * | 1972-10-18 | 1976-05-04 | Diamond Shamrock Corporation | Metal treating compositions of controlled pH |
US3928237A (en) * | 1972-11-17 | 1975-12-23 | Robert E Davis | Method of catalyst preparation for use in suppressing hydrocarbon and carbon monoxide emission from internal combustion engines |
GB1345868A (en) * | 1973-02-14 | 1974-02-06 | Rca Corp | Electroless cobalt plating bath |
US3877981A (en) * | 1973-04-30 | 1975-04-15 | Rca Corp | Method of electroless plating |
US3905838A (en) * | 1974-04-10 | 1975-09-16 | Hikaru Ito | Bath for treating aluminum and aluminum alloys to form oxide film nonelectrolytically thereon and method for the treatment |
US3993510A (en) * | 1975-05-21 | 1976-11-23 | The United States Of America As Represented By The Secretary Of The Navy | Thixotropic chemical conversion material for corrosion protection of aluminum and aluminum alloys |
CA1057108A (en) * | 1975-08-06 | 1979-06-26 | Vernon L. Bissonette | Process of bleaching silver images to form dye images |
JPS53104301A (en) * | 1977-02-22 | 1978-09-11 | Ricoh Kk | Treating solution for lithographic printing |
US4150172A (en) * | 1977-05-26 | 1979-04-17 | Kolk Jr Anthony J | Method for producing a square loop magnetic media for very high density recording |
US4218240A (en) * | 1979-05-14 | 1980-08-19 | Gte Products Corporation | Method for producing cobaltic hexammine compounds and cobalt metal powder |
US4233063A (en) * | 1979-05-14 | 1980-11-11 | Gte Products Corporation | Process for producing cobalt powder |
AU526731B2 (en) * | 1979-12-28 | 1983-01-27 | Matsushita Electric Industrial Co., Ltd. | Method for making a selective absorption film for solar energy |
US4278477A (en) * | 1980-03-19 | 1981-07-14 | Amchem Products, Inc. | Metal treatment |
US4278463A (en) * | 1980-03-28 | 1981-07-14 | Gte Products Corporation | Process for recovering cobalt |
US4261766A (en) * | 1980-06-13 | 1981-04-14 | Early California Industries, Inc. | Method for inhibiting fatigue of aluminum |
US4392920A (en) * | 1981-06-10 | 1983-07-12 | The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration | Method of forming oxide coatings |
JPS581076A (ja) * | 1981-06-26 | 1983-01-06 | Nisshin Steel Co Ltd | Lng又はlpgタンク用高ニッケル―鉄合金鋼板の表面処理方法 |
US4348224A (en) * | 1981-09-10 | 1982-09-07 | Gte Products Corporation | Method for producing cobalt metal powder |
US4381203A (en) * | 1981-11-27 | 1983-04-26 | Amchem Products, Inc. | Coating solutions for zinc surfaces |
US4637374A (en) * | 1982-09-08 | 1987-01-20 | Sharp Kabushiki Kaisha | Selective absorption film of a solar heat collector |
US4659605A (en) * | 1984-05-16 | 1987-04-21 | Richardson Chemical Company | Electroless deposition magnetic recording media process and products produced thereby |
US4631093A (en) * | 1984-07-27 | 1986-12-23 | Tre Corporation | Chromate free method of treating metal substrates to impart corrosion resistance and color to the substrate surface |
US4647347A (en) * | 1984-08-16 | 1987-03-03 | Amchen Products, Inc. | Process and sealant compositions for sealing anodized aluminum |
JPS61238979A (ja) * | 1985-04-15 | 1986-10-24 | Kobe Steel Ltd | 着色亜鉛合金めつき鋼板の製造方法 |
US4897129A (en) * | 1986-05-12 | 1990-01-30 | The Lea Manufacturing Company | Corrosion resistant coating |
US4804407A (en) * | 1988-05-13 | 1989-02-14 | Gte Products Corporation | Method for recovering cobalt from hexammine cobaltic (111) solutions |
BR8903960A (pt) * | 1988-08-08 | 1990-03-20 | Nihon Parkerizing | Processo para tratamento de uma superficie de zinco |
JPH0730458B2 (ja) * | 1988-08-08 | 1995-04-05 | 日本パーカライジング株式会社 | 亜鉛又は亜鉛系めっき材料の黒色化処理方法 |
JPH0331484A (ja) * | 1989-06-27 | 1991-02-12 | Nippon Parkerizing Co Ltd | 亜鉛または亜鉛系メッキ材料の黒色化処理法 |
JPH03226584A (ja) * | 1990-01-30 | 1991-10-07 | Nippon Parkerizing Co Ltd | 亜鉛系めっき鋼板用表面処理液及び表面処理方法 |
US5298092A (en) * | 1990-05-17 | 1994-03-29 | The Boeing Company | Non-chromated oxide coating for aluminum substrates |
EP0488430B1 (en) * | 1990-11-30 | 1997-06-11 | The Boeing Company | Non-chromated cobalt conversion coating |
DK0523288T3 (da) * | 1991-07-19 | 1999-08-02 | Boeing Co | Ikke-chromaterede oxidovertræk til aluminiumsubstrater |
-
1990
- 1990-05-17 US US07/525,800 patent/US5298092A/en not_active Expired - Lifetime
-
1991
- 1991-03-07 ES ES91103498T patent/ES2148141T3/es not_active Expired - Lifetime
- 1991-03-07 DE DE69132326T patent/DE69132326T2/de not_active Expired - Lifetime
- 1991-03-07 AT AT91103498T patent/ATE194857T1/de not_active IP Right Cessation
- 1991-03-07 DK DK91103498T patent/DK0458020T3/da active
- 1991-03-07 EP EP91103498A patent/EP0458020B1/en not_active Expired - Lifetime
- 1991-05-17 JP JP11281791A patent/JP3194593B2/ja not_active Expired - Lifetime
-
1993
- 1993-12-23 US US08/173,593 patent/US5415687A/en not_active Expired - Lifetime
- 1993-12-23 US US08/173,591 patent/US5487949A/en not_active Expired - Lifetime
-
2000
- 2000-10-16 GR GR20000402321T patent/GR3034635T3/el not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
EP0458020A1 (en) | 1991-11-27 |
DE69132326T2 (de) | 2001-05-03 |
JPH04231478A (ja) | 1992-08-20 |
ATE194857T1 (de) | 2000-08-15 |
US5298092A (en) | 1994-03-29 |
DK0458020T3 (da) | 2000-10-30 |
DE69132326D1 (de) | 2000-08-24 |
EP0458020B1 (en) | 2000-07-19 |
JP3194593B2 (ja) | 2001-07-30 |
US5415687A (en) | 1995-05-16 |
US5487949A (en) | 1996-01-30 |
GR3034635T3 (en) | 2001-01-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES2148141T3 (es) | Revestimiento de oxido no cromado para sustratos de aluminio. | |
MX9102254A (es) | Solucion acuosa y procedimiento para formar un revestimiento de conversion de cobalto sobre un substrato de metal. | |
US4263059A (en) | Coating solutions of trivalent chromium for coating zinc and cadmium surfaces | |
ES2125231T3 (es) | Revestimientos de oxido no cromado para sustratos de aluminio. | |
BR9306602A (pt) | Revestimento de óxido não cromado para substratos de alumínio | |
CA2087473A1 (en) | Non-chromated oxide coating for aluminum substrates | |
JP2003166074A (ja) | 亜鉛及び亜鉛合金めっき上に六価クロムフリー防錆皮膜を形成するための処理溶液、六価クロムフリー防錆皮膜及びその形成方法。 | |
CA2019810A1 (en) | Surface blackening treatment for zinciferous surfaces | |
GB1461244A (en) | Treatment of metal surfaces with trivalent chromium solutions | |
MY110203A (en) | Non-chromated oxide coating for aluminium substrates | |
Schriever | Non-chromated cobalt conversion coating | |
MY111371A (en) | Non-chromated oxide coating for aluminum substrates. | |
RU93004412A (ru) | Нехромированное окисное покрытие для алюминиевых подложек |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
FG2A | Definitive protection |
Ref document number: 458020 Country of ref document: ES |