Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F291/00—Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds according to more than one of the groups C08F251/00 - C08F289/00
  • C08F291/06—Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds according to more than one of the groups C08F251/00 - C08F289/00 on to oxygen-containing macromolecules
  • C08F291/08—Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds according to more than one of the groups C08F251/00 - C08F289/00 on to oxygen-containing macromolecules on to macromolecules containing hydroxy radicals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F290/00—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups
  • C08F290/08—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups on to polymers modified by introduction of unsaturated side groups
  • C08F290/14—Polymers provided for in subclass C08G
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
  • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
  • C08G65/32—Polymers modified by chemical after-treatment
  • C08G65/329—Polymers modified by chemical after-treatment with organic compounds
  • C08G65/337—Polymers modified by chemical after-treatment with organic compounds containing other elements

Definitions

• This invention is directed to a polymer dispersion prepared by reacting a polyol containing added ethylenic unsaturation and an ethylenically unsaturated monomer or mixture thereof in the presence of a free radical catalyst characterized in that the dispersion is prepared by the Williamson synthesis or a phase transfer catalyst modification thereof employing in situ polymerization of the ethylenically unsaturated monomer or mixture of monomers in the polyol containing added ethylenic unsaturation.
• the stable dispersions of the present invention wherein the vinyl polymerization has been conducted in situ in an unsaturated polyol or polyol blend prepared by the above mentioned methods have lower viscosities as compared to those unsaturated polyols prepared from unsaturated compounds having a hydroxyl, a carboxyl or an epoxy group.
• dispersions of relatively low viscosity are known in the art, the dispersions of the present invention are even lower in viscosity for the same amount of polymer and ethylenic unsaturation in the polyol.
• the lower viscosity allows for greater ease of handling in commercial urethane applications and for the incorporation of higher levels of dispersed polymer solids.
• the unsaturated polyols employed in the present invention are prepared preferably by the Williamson method wherein a conventional polyol is reacted with an alkali or alkaline earth metal hydroxide to form the metal alcoholate of the polyol and the resultant metal alcoholate is then reacted with an allyl halide or a vinylbenzyl halide.
• the proportion of allyl halide or vinylbenzylhalide employed is such that on the average at least one hydroxyl group per molecule of polyol is not capped with the allyl or vinylbenzyl group. Preferably at least two hydroxyl groups per molecule are not capped.
• the reaction between the polyol and the alkali or alkaline earth metal hydroxide is usually conducted at a temperature of from 80°C to 140°C, preferably from 100°C to 120°C for a time sufficient to essentially complete the reaction.
• the reaction between the resulting metal alcoholate ' and the allyl halide or vinylbenzyl halide is conducted at a temperature of from 80°C to 140°C, preferably from 100°C to 120°C for a time sufficient to essentially complete the reaction. Since the reaction results in the formation of a metal halide salt byproduct, such salt can be removed by such methods as, for example, filtration or centrifugation. In some instances it may be preferred to add some quantities of water, e.g. from 1 to 10 parts per part by weight of metal halide salt and then after removing the water by flashing or other means, removing the salt as indicated above.
• Suitable alkali and alkaline earth metal hydroxides include, for example, sodium hydroxide, potassium hydroxide, lithium hydroxide, barium hydroxide, calcium hydroxide and mixtures thereof.
• Suitable allyl halides include, for example, allyl chloride, allyl bromide, allyl iodide, allyl fluoride and mixtures thereof.
• Suitable vinylbenzyl halides include, for example, vinylbenzyl chloride, vinylbenzyl bromide, vinylbenzyl iodide, vinylbenzyl fluoride and mixtures thereof.
• the unsaturated polyols of the present invention are also prepared by a phase transfer catalysis modification of the traditional Williamson ether synthesis which employs an additional catalyst such as tetra-alkyl ammonium or phosphonium halides, sulfates or bisulfates..
• a polyol containing added ethylenic unsaturation is prepared by reacting a polyol having at least one primary or secondary alcoholic hydroxyl group, allyl halide or vinylbenzyl halide and an aqueous solution of an alkali metal hydroxide, the reaction being conducted in the presence of a catalytic amount of a quaternary ammonium or phosphonium salt having a total carbon content of from 10 to 40 carbon atoms.
• the aqueous solution of an alkali metal hydroxide varies in concentration from 40 weight percent to a saturated solution of -the alkali metal hydroxide. A saturated solution is preferred.
• the preferred catalysts are tetra-n-butyl ammonium salts.
• the preferred halide compounds are allyl chloride or vinylbenzyl chloride.
• the unsaturated polyols prepared by these methods may be used alone or they may be blended with polyols not containing added ethylenic unsaturation. If a blend of polyols is employed, the level of added unsaturation can be easily adjusted to a desired level.
• Suitable polyols which may be employed in the present invention include, for example, polyalkylene polyether polyols, polyhydroxyl-contairiing phosphorus compounds, and alkylene oxide adducts of polyhydric polythioethers, polyacetals, aliphatic polyols, and thiols, ammonia, and amines including aromatic, aliphatic and heterocyclic amines, as well as mixtures thereof well known in the art.
• Alkylene oxide adducts of compounds which contain two or more different groups within the above-defined classes may also be used such as, for example, amino alcohols which contain an amino group and a hydroxyl group.
• Any suitable polyalkylene polyether polyol may be used such as, for example, the polymerization product of an-alkylene oxide or of an alkylene oxide with a polyhydric alcohol having from 2 to 6 hydroxyl groups.
• Polyethers which are preferred include the alkylene oxide addition products of trimethylolpropane, glycerine, pentaerythritol, sucrose, sorbitol, propylene glycol, and 2,2-(4,4'-hydroxyphenyl) propane and blends thereof having hydroxyl equivalent weights of from 250 to 5000.
• Suitable polyhydric polythioethers which may be condensed with alkylene oxides include the condensation product of thiodiglycol or the reaction product of a dihydric alcohol such as disclosat abore for the an paration of the hydroxyl-containing polyethers with a other suitable thioether glycol.
• Polyhydroxyl-containing phosphorus compounds which may be used include those compounds disclosed in U.S. Patent 3,639,542.
• Preferred polyhydroxyl-containing phosphorus compounds are prepared from alkylene oxides and acids of phosphorus having a phosphorus pentexide equivalency of from 72 percent to 95 percent.
• Suitable polyacetals which may be condensed. with alkylene oxides include the reaction product of formaldehyde or other suitable aldehyde with a dihydrig alcohol or an alkylene oxide such as those disclosed abave.
• Suitable aliphatic thiols which may be condensed with alkylene oxides include alkane thiols Containing at least two -SH groups such as 1,2-ethane dithiol,1,2-propane dithiol, and 1,6-hexane dithiol; alkene thiols such as 2-butene-1,4-dithiol; and alkyne thiols such as 3-hexyne-1,6-dithiol.
• Suitable amines which may be condersed with alkylene oxides include aromatic amines such as aniline, o-chlorcaniline, p-amino aniline, 1,5-diaming naphthalene, methylene dianiline, the condensation products of aniline and formaldehyde, and 2,4-diamino toluene; aliphatic amines such as methylamine, triisopropanolamine, isopropanolamine, diisopropanolamine, erhyllenediamine, 1,3--propylenediamine, 1,4-butylenediamine, and 1,3-butylenediamine, and mixtures thereof.
• aromatic amines such as aniline, o-chlorcaniline, p-amino aniline, 1,5-diaming naphthalene, methylene dianiline, the condensation products of aniline and formaldehyde, and 2,4-diamino tolu
• the present polymers of the invention are prepared by the in situ polymenization of the above-described unsaturated polyols with an.ethylenically unsaturated monomer or a mixture of ethylenically unsaturated monomers.
• Preferred monomers are styrene and acrylonitrile.
• the proportion of ethylenically unsaturated monomer employed in the polymerization reaction is generally from 1 percent to 50 percent, preferably from 3 percent to 35 percent, based on the weight of the unsaturated polyol or polyol blend.
• the polymerization occurs by simultaneously adding at a steady or constant rate the monomer and a free radical catalyst to the unsaturated polyol at a temperature usually from about 80° to about 170°C, preferably from about 100° to 135°C.
• the catalyst may be dispersed or dissolved in a portion of the polyol and thereafter be added along with the monomer to the remaining portion of the unsaturated polyol or polyol blend.
• the catalyst may be dissolved or dispersed in some solvent which does not detrimentally affect the course or rate of polymerization and does not detrimentally affect the useful character of the product' and thereafter be added along with monomer to the unsaturated polyol or polyol blend.
• some solvent which does not detrimentally affect the course or rate of polymerization and does not detrimentally affect the useful character of the product' and thereafter be added along with monomer to the unsaturated polyol or polyol blend.
• organic solvent it is preferably removed by conventional means.
• the concentration of the free radical catalyst can vary from 0.05 percent to 10 percent, preferably from 0.1 percent to 5 percent by weight based on the weight of the.monomer.
• Suitable catalysts are well known in the art. Azobis(isobutyronitrile) is the preferred catalyst.
• the polymer dispersions of the present invention are employed in the preparation of polyurethane compositions, particularly polyurethene foamy and elaste mers,
• the polyurethane products are generally prerared by the reaction of the copolymer dispersions with an organic polyisocyanate, optionally in the presence cf additional polyhydroxyl-containing components, chain- extending agents, catalysts, surface-active agents, stabilisers, blowing agents, fillers and pigments
• Saitable processes for the preparation of elaptomeril and cellular polyurethane plastics are well kncwn in the art.
• the polymer dispersions are preferably employed along with another polyhydroxyl-containing component commonly employed in the art. Any of the pclyhydroxyl--containing components which are described above for use in the preparation of the polymer dispersions of the prodent insertion may be employed along with the unsaturated polylos in the preparation of the polyurethane compositions of the present invention.
• the amount of unsaturation was determined by prcton NMR analysis.
• the unsaturation was calculated as weicht per- gent allyl alcohol. This figure was then converted to moles of carbon-carbon double bends (moleular weight 24) per mole of polyol.
• Polyol A a polyol
• Polyol B a polyol
• the mixture was heated to 110 to 120°C and after about 30 minutes 52 g (0.68 moles) pf allyl chloride was added. After reacting at 100°C for 12 hours, the product was cooled to 60°C and 300 g deionized water and 50 g magnesium silicate were added. The water was stripped at 120 0 C and 2 to 3-mm mercury for 2 hours to precipitate the salts. The product was then filtered.
• the polyol with the added unsaturation was designated as Polyol B.
• Polyol B has 1.4 moles of unsaturation per mole of polyol. Polyol A had 0.4 mole of unsaturation per mole of polyol. Polyol B therefore contained 1 mole of added unsaturation per mole of polyol.
• the above prepared unsaturated Polyol B was used to prepare polymer dispersions according to the following general procedure.
• the unsaturated Polyol B was blended with Polyol A to give a predetermined level of unsaturation.
• the polyol blend was then heated to 120°C while nitrogen gas was bubbling through the blend. This was done in a 1-liter round bottom flask equipped with a mechanical stirrer, condenser, thermometer, heating mantle with temperature controller, addition funnel and nitrogen gas inlet. While the polyol was heating, styrene and acrylonitrile (VCN) were blended in a separate container.
• the monomer blend was prepared as a 50 percent solution by weight in a polyol blend of the same composition as that being heated.
• the monomer/polyol blend was then refrigerated to prevent polymerization.
• the nitrogen gas bubbling was switched to a static nitrogen gas pad.
• Azobis(isobutyronitrile) was then weighed into the cold monomer/polyol blend.
• the catalyst level was 0.7 weight percent based on the monomers.
• the monomer/polyol/catalyst blend was then added at a steady rate to the stirred hot polyol blend. The addition times ranged from 30 to 56 minutes but were typically 40 minutes.
• the of monomer added was 25 weight percent based upon the weight of the polyol.
• the reaction was maintained at 120°C during the addition and for about one hour after the completion of the addition.
• the product was then cooled to ambient temperature. Viscosities were recorded using a Brookfield Viscometer; Model LVF, with a #4 spindle at 20 rpm and at ambient temperature (23 to 26°C).
• the product was digested at 120°C for"40 minutes after completion of the addition of styrene monomer.
• the product was cooled to 90°C and was stripped of unreacted styrene at 1 mm mercury for 50 minutes.
• the product was a tan dispersion containing 10.4 weight percent polymer solids ana having a Brookfield viscosity of 1200 centipoise at ambient temperature. The dispersion did settle out after 3 weeks storage at 25°C but could be redispersed by agitation.
• a polyol containing added unsaturation by the procedure of Examples 1 through 9 be heating a mixture of 3232 g (0.66 mole) of Polyol A and 26.4 g (0.66 mole) sodium hydroxide. After purging with nitrogen, 101 g (0.66 mole) of vinylbenzyl chloride was added over a one hour period. The mixture was digested for two hours at 100°C. To the mixture was added 35 g of magnesium silicate. The crude product was vacuum stripped at 110°C for two hours. The subsequently filtered product had 0.8 mole of added unsaturation and is designated as Polyol D.
• Example 10 The procedure of Example 10 above was repeated using 80 g of Polyol D and 320 g of Polyol A. A dispersion was then prepared using 101 g of styrene monomer and 2 g of azobis(isobutyronitrile). After stripping the product was a smooth white stable dispersion containing 7.4 weight percent polymer solids and having a Brookfield viscosity of 1100 centipoise at ambient temperature (25°C).
• Example 10 The procedure in Example 10 was repeated with the exception that Polyol A was the only polyol used. 797 g Polyol A, 200 g styrene monomer and 1.4 g azobis-(isobutyronitrile) were reacted according to the procedure in Example 10. Upon cooling to 90°C after digestion agglomeration of the polymer was observed. Further cooling caused the polymer to form a solid ball about 1-1/2 inches (4.3 cm) in diameter. No dispersion was formed.
• a reaction vessel fitted with stirrer, heating mantle with temperature controller, condenser, thermometer, nitrogen gas inlet, and dropping funnel was charged with '(a) 1522 g (0.31 mole) of a 4907 molecular weight triol, designated Polyol E, which was an adduct of glycerine and propylene oxide and subsequently end capped with 13 weight percent ethylene oxide, (b) 980 g (0.41 mole) of a 2383 molecular weight diol which was an adduct of propylene glycol and propylene oxide and subsequently end capped with 15 weight percent ethylene oxide, and (c) 76 g (0.78 mole) of maleic anhydride.
• Polyol E 4907 molecular weight triol
• the charge was heated to 130°C and digested for five hours and then cooled to room temperature. After the product was cooled, 2500 g of the product was heated to 150°C. Then 170 g of ethylene oxide was gradually added over a 3 hour period. Upon completion of the oxide addition, the reaction mixture was maintained at 150 to 170°C for 3 hours, after which time it was stripped at 130°C for 3 hours at less than 10 mm of mercury.
• the product, designated Polyol F was an amber fluid.
• a polymer dispersion employing Polyol F was prepared following the teaching found in U.S. Patent 4,014,846, column 12.
• a reaction vessel equipped with a stirrer, condenser, heating mantle with controller, addition funnel and nitrogen inlet was charged with 200 g isopropanol, 50 g of Polyol E, 200 g acrylonitrile, 50 g styrene, 0.4 g tert-dodecyl mercaptan and 1.25 g azobis-(isobutyronitrile).
• the charge was heated to 75°C for 5 hours. At the end of this period the product was a milky fluid.
• the polymer dispersion was cooled to room temperature.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Graft Or Block Polymers (AREA)
• Polymerisation Methods In General (AREA)
• Macromonomer-Based Addition Polymer (AREA)

Applications Claiming Priority (2)

Publications (1)

Family

ID=25216943

Family Applications (1)

Country Status (7)

Cited By (5)

Citations (4)

• 1978
  • 1978-07-12 BR BR7804510A patent/BR7804510A/pt unknown
  • 1978-07-12 CA CA307,256A patent/CA1094531A/fr not_active Expired
  • 1978-07-12 AU AU37947/78A patent/AU3794778A/en active Pending
  • 1978-07-12 IT IT50257/78A patent/IT1156857B/it active
  • 1978-07-12 EP EP78100371A patent/EP0000503A1/fr not_active Withdrawn
  • 1978-07-13 AR AR272943A patent/AR219761A1/es active
  • 1978-07-13 JP JP8565478A patent/JPS5440887A/ja active Pending

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events