Die Verwendung von Rohblei zur Herstellung von Kabelmänteln Zur Herstellung
von Kabelmänteln verwendet man entweder reines Hüttenweichblei oder Hüttenweichblei,
dem zur Verbesserung seiner mechanischen Eigenschaften geringe Anteile an anderen
Metallen, wie Antimon, Zinn, Kalzium, Selen, Tellur, Zink u. d'-I., zugesetzt s!i;nd.
Der Hauptbestandteil ist also immer raffiniertes Blei, sogenanntes Hüttenweichblei.The Use Of Raw Lead To Make Cable Sheaths For Manufacturing
for cable sheaths, either pure metallurgical soft lead or metallurgical soft lead is used,
to improve its mechanical properties small proportions of others
Metals such as antimony, tin, calcium, selenium, tellurium, zinc and the like, are added.
The main component is always refined lead, so-called soft lead.
Erfindungsgemäß wird zur Herstellung der Bleikabelmäntel Rohblei verwendet,
wie es beispielsweise in der Bleihütte nach der Zinkentsilberung oder in der Zinkhütte
als Rückstand bei der Zinkgewinnung anfällt. Derartiges Rohblei enthält neben größeren
Anteilen Zink bis etwa 3 % im wesentlichen Antimon, Zinn, Kupfer, Arsen und Wismut
als Verunreinigung. Ist die Summe der Verunreinigungen nicht überdurchschnittlich
hoch, so kann das Blei so, wie es anfällt, zur Kabelherstellung verwendet werden.
Zu diesen Rohbleisorten gehört beispielsweise das Blei, das nach der Zinkentsilberung
in der Bleihütte anfällt. Enthält das Rohblei jedoch größere Anteile an Verunreinigungen,
so soll ihm erfindungsgemäß entweder weniger verunreinigtes Rohblei oder Hüttenweichblei
zugesetzt werden. Hierdurch soll erreicht werden, daß die Summe der Verunreinigungen
3 % nicht überschreitet, vorzugsweise jedoch i bis 2 % beträgt. Besonders vorteilhaft
ist es, wenn auf eine Zusammensetzung hingearbetet wird, die innerhalb folgender
Grenzwerte liegt: 0,4 bis 1,5 % Zn, o,i bis 0,5 % Sb, o bis o,5 % Sn, o bis o,i5
% Cu, o bis o, i % Bi, o bis o,2 % As, Rest Blei.
Es hat sich gezeigt,
daß sich bei erfindungsgemäßer Verwendung von Rohblei Kabelmäntel herstellen lassen,
die in ihren Eigenschaften den aus legiertem Hüttenweichblei hergestellten Kabelmänteln
vollkommen entsprechen. Der mengenmäßige Anteil an Verunreinigungen und das Verhältnis
der einzelnen Verunreinigungen zueinander ist vor allem in den deutschen Rohbleisorten
so günstig, daß es ohne Schwierigkeit gelingt, den Anteil der Verunreinigungen innerhalb
der erfindungsgemäß angegebenen Grenzwerte zu halten. In diesem Falle erhält man,
wie die Patentinhaberin feststellte, Kabelmäntel mit besonders guten mechanischen
Eigenschaften.According to the invention, raw lead is used to manufacture the lead cable sheaths,
As is the case, for example, in the lead smelter after zinc desilvering or in the zinc smelter
is obtained as a residue from zinc extraction. Such raw lead contains in addition to larger ones
Zinc proportions up to about 3%, mainly antimony, tin, copper, arsenic and bismuth
as an impurity. Is the sum of the impurities not above average
high, the lead can be used as it is for the manufacture of cables.
These types of raw lead include, for example, the lead that is obtained after zinc desilvering
accrues in the lead smelter. However, if the raw lead contains large amounts of impurities,
so according to the invention either less contaminated raw lead or metallurgical soft lead should be given to it
can be added. This is to ensure that the sum of the impurities
Does not exceed 3%, but is preferably i to 2%. Particularly beneficial
it is when praying toward a composition that is within the following
Limit values is: 0.4 to 1.5% Zn, o, i to 0.5% Sb, o to o, 5% Sn, o to o, i5
% Cu, o to o, i% Bi, o to o, 2% As, remainder lead.
It has shown,
that cable sheaths can be produced with the use of raw lead according to the invention,
the properties of the cable sheaths made from alloyed metallurgical soft lead
completely correspond. The quantitative proportion of impurities and the ratio
the individual impurities to each other is mainly in the German raw lead types
so cheap that it succeeds without difficulty, the proportion of impurities within
to maintain the limit values specified according to the invention. In this case one obtains
as the patent proprietor found, cable sheaths with particularly good mechanical
Properties.
Die Vorteile der erfindungsgemäßen Verwendung von Rohblei sind offensichtlich.
Der ganze Raffinationsprozeß fällt für das Rohblei, das dieser Venwendung zugeführt
wird, weg. Das bedeutet Einsparung an Kohlen, Ofenbaustoffen u. dggl. Die bei der
Raffination des Rohbleis entstehenden Bleiverluste fallen weg. Die anfallenden oxydischen
Metallrückstände brauchen nicht mehr aufgearbeitet und in ihre einzelnen Bestandteile
zerlegt zu werden. Das Legieren des Hüttenweichbleis erübrigt sich. Legierungsmetalle
für diesen Zweck werden erspart, und da alle diese Maßnahmen Arbeitskraft und -zeit
erfordern, kommt man bei Anwendung der Lehre nach der Erfindung außerdem noch schneller
zu dem erwünschten Ziele.The advantages of using raw lead according to the invention are evident.
The whole refining process falls on the raw lead which is used for this purpose
will, gone. That means savings on coal, furnace building materials and the like. The at the
There are no lead losses resulting from the refining of the raw lead. The resulting oxidic
Metal residues no longer need to be worked up and broken down into their individual components
to be dismantled. Alloying the metallurgical soft lead is not necessary. Alloy metals
for this purpose are saved, and since all these measures manpower and time
require, one comes even faster when applying the teaching according to the invention
to the desired goal.