DE8023197U1 - Durchbruchhemmende Verbundscheibe - Google Patents
Durchbruchhemmende VerbundscheibeInfo
- Publication number
- DE8023197U1 DE8023197U1 DE8023197U DE8023197DU DE8023197U1 DE 8023197 U1 DE8023197 U1 DE 8023197U1 DE 8023197 U DE8023197 U DE 8023197U DE 8023197D U DE8023197D U DE 8023197DU DE 8023197 U1 DE8023197 U1 DE 8023197U1
- Authority
- DE
- Germany
- Prior art keywords
- breakthrough
- resistant composite
- epoxy resin
- thickness
- pane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
'"""' ' Λ' DEUTSCHE SPEZIALGLAS AG
GrUnenpian Postfach 80
3223 Deliigsen 2
Die Erfindung betrifft eine durchbruchhemmende Verbundscheibe
nach dem Oberbegriff des Anspruchs 1.
Durchbruchhemmende Verbundscheiben werden 1n steigendem MaBe
1m öffentlichen,privaten und gewerblichen Bereich zum Schutz
von Gegenstanden und Einrichtungen vor unerlaubtem Zugriff, als Abschirmung z.B. an Werkzeugmaschinen und nicht zuletzt
1m modernen Strafvollzug als Ersatz fllr unschön wirkende Vergitterungen
eingesetzt. Dabei wird neben guter Transparenz der Scheiben ein hoher Widerstandswert nicht nur gegen mechanische
Angriffe, beispielsweise durch Schlä'ge mit Hammer, Bell
oder Brechelsen oder durch umherfliegende Bruchstücke von berstenden Hochgeschwindigkeits-Schleifscheiben, sondern auch
gegen thermische Belastungen, beispielsweise von Schweißbrennern, verlangt. Der Widerstandswert bezieht sich aber nicht nur auf
die Heftigkeit der vorgetragenen Angriffe,sondern auch, und das
1st bei durchbruchhemmenden Scheiben sogar besonders wichtig,
auf die LSnge der Zelt, die solche Scheiben einem Angriff zu
widerstehen vermögen.
Eine weitere ganz wesentliche Forderung an durchbruchhemmende
Scheiben 1st die nach möglichst geringen Dicken, um neben der Vermeidung zu hoher Material kosten und zu großen Gewichts den
Einbau möglichst einfach und unaufwendig zu gestalten.
Es sind Verbundscheiben bekannt, bei denen SHIkatgiasscheiben
verschiedener Dicken und verschiedener Anzahl durch Kunststoff-Zwischenschichten
wie Polyvinylbutyral, Polymethyimetacrylat oder Epoxidharze miteinander verklebt sind.
Derartige Verbünde werden als PanzerglSser mit hoher Schußsicherheit
eingesetzt, sie bieten aber nur kurzfristig Schutz gegen Beschüß
mit Handfeuerwaffen, schwere Schlüge oder thermische Belastung und können nicht als durchbruchhemmend angesehen werden. |
Weiterhin sind Verbünde bekannt, bei denen einzelne SiHkatgias- f
scheiben durch massive Kunststoffscheiben ersetzt sind. So 1st aus i
der DE-PS 27 54 684 eine durchbruchhemmende Scheibe bekannt, bei tder
smkatglas- und Polycarbonatscheiben 1n wechselnder Folge mit- |
einander verbunden sind. Diese Scheibe hat bereits sehr gute durch- fj
bruchhemmende Eigenschaften und widersteht selbst einem massierten jg
Angriff bei gleichzeitigem Einsatz thermischer und mechanischer *
MIttel für längere Zelt.
Ziel der Erfindung 1st es, eine durchbruchhemmende Scheibe mit einem
noch höheren Widerstandswert zu entwickeln, um gegebenenfalls bei gleicher druchbruchhemmender Wirkung aber verringerter Dicke einen
problemlosen Einbau 1n herkömmliche TUr- und Fensterrahmen zu ermöglichen.
Diese Aufgabe wird Überraschenderweise dadurch gelöst, daß ein
Kern-Verbund von zwei oder mehreren Polycarbonatscheiben von je
2 bis 10 mm Dicke auf der Vorder- und Rückseite von je einer
S1l1katglassche1be mit einer Dicke von 2 bis 10 mm flankiert wird.
FUr die Verklebung sowohl der SHIkatglasscheiben mit dem PoIycarbonat-Kern
als auch der den Kern bildenden Polycarbonatscheiben
miteinander wird flexibilisieftes Epoxidharz verwendet, wie ss aus
der DE-PS 20 17 723 bekannt 1st. Die Dicke der Zwischenschichten bewegt sich zweckmäßigerweise zwischen 0,2 und 2,5 mm.
Eine besonders bevorzugte AusfUhrungsform der Erfindung ergibt
sich aus dem Anspruch 5.
50 mm, wobei selbstverständlich auch daran gedacht 1st, sie fUr ;
besonders hohe Anforderungen als Bausteine fUr dickere Verbünde ·
zu verwenden, Indem mehrere durchbruchhemmende Scheiben gemäß der
Erfindung entweder mit gegenseitigem Abstand oder In unmittelbarer
Aufeinanderfolge, jeweils mit Epoxidharz-Zwischenschichten verbunden,
eingesetzt werden.
Die Zeichnung zeigt eine erf 1ndungsgema*ße durchbruchhemmende
Verbundscheibe 1m Schnitt. Diese besteht aus einer SiHkatglasscheibe
(10) mit einer Dicke von 4 mm, einer Epoxidharz-Zwischenschicht
(12) mit einer Dicke von 1 mm, einer ersten Polycarbonatscheibe
(14) mit einer Dicke von 4 mm, einer Epoxidharz-Zwischenschicht (16) mit einer Dicke von 0,5 mm, einer zweiten Polycarbonatscheibe
(18) mit einer Dicke von 4 mm, einer Epoxidharz-Zwischenschicht (20) mit einer Dicke von 1 mm und einer S1l1katglasscheibe
(22) mit einer Dicke von 4 mm. Die dargestellte Verbundscheibe
hat eine Gesamtdicke von 18,5 mm und ISBt sich problemlos
1n jeden normalen TUr- oder Fensterrahmen einbauen. Selbstverständlich
kann eine solche Scheibe erf Indungsgema'ß nicht nur
als E1nfach-Verbundsche1be verwendet werden, sondern es können mehrere solcher E1nfach-Verbundsche1ben hintereinander angeordnet
und mittels flex1b1Hs1erten Epoxidharzes miteinander verklebt werden, wodurch sich besonders hohe Widerstandswerte ergeben.
Eine Einfach-Verbundscheibe gernüß dem gezeigten Ausftlhrungsbeispiel
macht trotz der geringen Dicke von nur 18,5 mm einen Durchbruch mit mechanisch wirkenden Werkzeugen wie Hammer, Bell, Stemmelsen
nahezu unmöglich, da zwar die S1l1katglassche1ben zerspringen,
die mit elastischen Gießharzen beschichteten Polycarbonatscheiben
aber selbst sehr heftigen und vielen Schlägen widerstehen.
Ein gleichzeitig durchgeführter Angriff mit thermischen und mechanischen
Mitteln auf eine Scheibe der erfindungsgemSßen Art zeigt
besonders deutlich Ihre durchbruchhemmenden Eigenschaften: Eine
E1nfach-Verbundsche1be nach dem gezeigten AusfUhrungsbe1sp1e1
widersteht trotz der geringen Dicke von nur 18,5 mm selbst einem
III I
Il t t
t Ir (ti
kombinierten Angriff mit Lötlampe, Hammer, Messer und Säge sehr lange
Zelt. Zunächst zersplittern bei einem solchen Angriff die S1l1katglasscheiben,
sie lassen sich aber nur 1n kleinen Stückchen abschlagen.
Sind die Kunststoffscheiben bloßgelegt, gelingt es zwar, durch
Erhitzen mit der Lötlampe und Bearbeiten der erweichten Stellen mit
Messer oder SSge, kleine Löcher zu schaffen, fUr einen endgültigen
Ourchbruch 1st aber eine mühevolle und sehr langwierige Kleinarbeit
erforderlich. Auch schwere Schläge mit einem Vorschlaghammer zeigen
keine Wirkung, da die Polycarbonatscheiben die Schläge zurückfedern
lassen.
Wie aus dem AusfUhrungsbe1sp1el ersichtlich 1st, bietet die erfindungsgemäße
Verbundscheibe einen zuverlässigen Schutz gegen kriminelle Delikte, wie Einbrüche. Die Scheibe 1st aber auch hervorragend
fUr den Einsatz 1n Strafvollzugsanstalten, als Ersatz fUr unschöne Vergitterungen, geeignet, da sie durch Ihren selbst bei
geringen Dicken hohen Widerstandswert ein wirksames Bollwerk gegen
Ausbruchsversuche darstellt und gleichzeitig problemlos In herkömmliche
TUr- und Fensterrahmen eingepaßt werden kann. Schließlich läßt sich die Scheibe auch als Schutzschild an Maschinen mit schnell
rotierenden Werkzeugen, wie Hochgeschw1nd1gke1tsschle1fsche1ben, einsetzen.
Claims (5)
1.) Durchbruchhemmende Verbundscheibe» dadurch gekennzeichnet»
daß ein Kern aus zwei oder mehreren miteinander verklebten Polycarbonatscheiben
(14,18) auf der Vorder- und Rückseite Über kiebfKhige
Zwischenschichten aus f1ex1b1Hs1ertem Epoxidharz (12,20)
mit S111katglassche1ben (10, 22) verbunden 1st.
2.) Durchbruchhemmende Verbundscheibe nach Anspruch 1, dadurch gekennzeichnet, daß die
S1T1katglassche1ben (10,22) eine Dicke von 2 bis 10 mm
haben.
3.) Durchbruchhemmende Verbundscheibe nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Polycarbonatscheiben
(14,18) eine Dicke von 2 bis 10 mm haben.
4.) Durchbruchhemmende Verbundscheibe nach einem der Ansprüche
1 bis 3, dadurch gekennzeichnet, daß die klebfffhigen Zwischenschichten (12,16,20) aus flexibi-Hsiertem
Epoxidharz eine Dicke von 0,5 bis 2,5 mm haben.
5.) Durchbruchhemmende Verbundscheibe nach einem ^r Ansprüche
1 bis 4, gekennzeichnet durch den nachfolgenden Schichtaufbau: S111katglassche1be 4 mm (10);
Epoxidharzzwischenschicht 1 mm (12); Polycarbonatscheibe 4 mm (14); Epoxidharzzwischenschicht 0,5 mm (16); PoIycarbonatscheibe
4 mm (18); Epoxidharzzwischenschicht 1 mm (20); SHIkatglasscheibe 4 mm (22).