DE69925014D1 - Verfahren zur herstellung von extrudiertem schaumstoff - Google Patents

Verfahren zur herstellung von extrudiertem schaumstoff

Info

Publication number
DE69925014D1
DE69925014D1 DE69925014T DE69925014T DE69925014D1 DE 69925014 D1 DE69925014 D1 DE 69925014D1 DE 69925014 T DE69925014 T DE 69925014T DE 69925014 T DE69925014 T DE 69925014T DE 69925014 D1 DE69925014 D1 DE 69925014D1
Authority
DE
Germany
Prior art keywords
mixture
melt index
styrenic polymer
extruded foam
major amount
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE69925014T
Other languages
English (en)
Other versions
DE69925014T2 (de
Inventor
M Miller
E Cisar
M Breindel
Z Weekley
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Owens Corning Intellectual Capital LLC
Original Assignee
Owens Corning
Owens Corning Fiberglas Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Owens Corning, Owens Corning Fiberglas Corp filed Critical Owens Corning
Publication of DE69925014D1 publication Critical patent/DE69925014D1/de
Application granted granted Critical
Publication of DE69925014T2 publication Critical patent/DE69925014T2/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/0061—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof characterized by the use of several polymeric components
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
    • C08J9/12—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a physical blowing agent
    • C08J9/122—Hydrogen, oxygen, CO2, nitrogen or noble gases
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
    • C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
    • C08J9/12—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent by a physical blowing agent
    • C08J9/127—Mixtures of organic and inorganic blowing agents
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L25/00—Compositions of, homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Compositions of derivatives of such polymers
    • C08L25/02—Homopolymers or copolymers of hydrocarbons
    • C08L25/04—Homopolymers or copolymers of styrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2201/00—Foams characterised by the foaming process
    • C08J2201/02—Foams characterised by the foaming process characterised by mechanical pre- or post-treatments
    • C08J2201/03—Extrusion of the foamable blend
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/06—CO2, N2 or noble gases
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2203/00—Foams characterized by the expanding agent
    • C08J2203/12—Organic compounds only containing carbon, hydrogen and oxygen atoms, e.g. ketone or alcohol
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2205/00—Foams characterised by their properties
    • C08J2205/04—Foams characterised by their properties characterised by the foam pores
    • C08J2205/052—Closed cells, i.e. more than 50% of the pores are closed
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C08J2325/02—Homopolymers or copolymers of hydrocarbons
    • C08J2325/04—Homopolymers or copolymers of styrene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2425/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2205/00—Polymer mixtures characterised by other features
    • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y10T428/249954—With chemically effective material or specified gas other than air, N, or carbon dioxide in void-containing component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y10T428/249976—Voids specified as closed
    • Y10T428/249977—Specified thickness of void-containing component [absolute or relative], numerical cell dimension or density

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)
DE69925014T 1998-10-21 1999-10-21 Verfahren zur herstellung von extrudiertem schaumstoff Expired - Lifetime DE69925014T2 (de)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US10505898P 1998-10-21 1998-10-21
US105058P 1998-10-21
PCT/US1999/024565 WO2000023511A1 (en) 1998-10-21 1999-10-21 Process for producing extruded foam

Publications (2)

Publication Number Publication Date
DE69925014D1 true DE69925014D1 (de) 2005-06-02
DE69925014T2 DE69925014T2 (de) 2006-03-09

Family

ID=22303828

Family Applications (1)

Application Number Title Priority Date Filing Date
DE69925014T Expired - Lifetime DE69925014T2 (de) 1998-10-21 1999-10-21 Verfahren zur herstellung von extrudiertem schaumstoff

Country Status (9)

Country Link
US (1) US6268046B1 (de)
EP (1) EP1124887B1 (de)
KR (1) KR100595337B1 (de)
AT (1) ATE294211T1 (de)
AU (1) AU757026B2 (de)
CA (1) CA2346992C (de)
DE (1) DE69925014T2 (de)
ES (1) ES2239463T3 (de)
WO (1) WO2000023511A1 (de)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DK1345986T3 (da) 2000-12-21 2009-01-12 Dow Global Technologies Inc Opblæsningsmiddelsammensætning og polymerskum indeholdende en normalt flydende hydroflourcarbon og carbondioxid
AU2002219980A1 (en) 2000-12-21 2002-07-08 Dow Global Technologies Inc. Blowing agents compositions containing hydrofluorocarbons, a low-boiling alcohol and/or low-boiling carbonyl compound
US8557884B2 (en) * 2002-05-31 2013-10-15 Owens Corning Intellectual Capital, Llc To enhance the thermal insulation of polymeric foam by reducing cell anisotropic ratio and the method for production thereof
US20030225172A1 (en) * 2002-05-31 2003-12-04 Miller Larry M. To enhance the thermal insulation of polymeric foam by reducing cell anisotropic ratio and the method for production thereof
US20050070663A1 (en) * 2003-09-29 2005-03-31 Fina Technology, Inc. Impact modified polystyrene and process for preparing same
US7358282B2 (en) * 2003-12-05 2008-04-15 Kimberly-Clark Worldwide, Inc. Low-density, open-cell, soft, flexible, thermoplastic, absorbent foam and method of making foam
GB0407463D0 (en) * 2004-04-01 2004-05-05 Nova Chem Int Sa Extruded foam structure with an inorganic blowing agent
US7291382B2 (en) * 2004-09-24 2007-11-06 Kimberly-Clark Worldwide, Inc. Low density flexible resilient absorbent open-cell thermoplastic foam
US8314161B2 (en) 2005-08-22 2012-11-20 Owens Corning Intellectual Capital, Llc Deformable, rigid polystyrene foam board
US8143337B1 (en) 2005-10-18 2012-03-27 The Ohio State University Method of preparing a composite with disperse long fibers and nanoparticles
WO2007053802A2 (en) * 2005-10-20 2007-05-10 The Ohio State University Drug and gene delivery by polymer nanonozzle and nanotip cell patch
US8158689B2 (en) 2005-12-22 2012-04-17 Kimberly-Clark Worldwide, Inc. Hybrid absorbent foam and articles containing it
TWI442086B (zh) * 2006-08-31 2014-06-21 Liquavista Bv 包含一單元陣列之電子裝置及其操作方法
US8507568B2 (en) * 2008-05-28 2013-08-13 The Ohio State University Suspension polymerization and foaming of water containing activated carbon-nano/microparticulate polymer composites
EP2486094A1 (de) 2009-10-09 2012-08-15 Basf Se Polymermischungen von polystyrol mit styrol-butadien-blockcopolymeren
JP6545098B2 (ja) * 2012-04-13 2019-07-17 スリーエム イノベイティブ プロパティズ カンパニー 感圧性接着剤フォーム及びそれからなる物品
DE102015000393A1 (de) 2014-01-21 2015-07-23 Frank Becher Verfahren zur Herstellung von geschlossen-porigen Erzeugnissen mit hohlen Zellen, mittels dessen der Druck in den Zellen kontrolliert während des Aufschäumens erhöht oder reduziert werden kann, sowie Erzeugnisse, die nach diesem Verfahren hergestellt werden

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4176144A (en) 1978-01-19 1979-11-27 Mobil Oil Corporation Block copolymers
US4636527A (en) 1985-04-12 1987-01-13 The Dow Chemical Company Method for the preparation of styrene polymer foam and foam prepared thereby
AU564115B2 (en) 1985-04-12 1987-07-30 Dow Chemical Company, The Method for the preparation of styrene polymer foam and foam prepared thereby
US4764420A (en) 1986-07-09 1988-08-16 The Celotex Corporation Foam insulation board faced with polymer-fibrous sheet composite
BR8807460A (pt) 1987-04-15 1990-04-10 Dow Chemical Co Metodo de extrusao de um corpo de espuma de resina sintetica aromatica de alquenila dotado de celulas fechadas
DE3741095A1 (de) 1987-12-04 1989-06-15 Basf Ag Verfahren zur herstellung von schaumstoffen mit hoher druckfestigkeit
DE3829632A1 (de) 1988-09-01 1990-03-15 Basf Ag Verfahren zur herstellung von schaumstoffplatten mit hoher druckfestigkeit
DE3829633A1 (de) 1988-09-01 1990-03-15 Basf Ag Verfahren zur herstellung von schaumstoffplatten mit hoher druckfestigkeit und hohem waermedaemmvermoegen
DE3829630A1 (de) 1988-09-01 1990-03-15 Basf Ag Verfahren zur herstellung von schaumstoffplatten mit hoher druckfestigkeit und hoher dimensionsstabilitaet
US5250577A (en) 1989-08-02 1993-10-05 The Dow Chemical Company Polystyrene foam made with only carbon dioxide as a blowing agent and a process for making the same
US5462794A (en) 1990-03-16 1995-10-31 Amoco Corporation Foamed core-reclaim multi layer sheet having improved resistance to barrier film delamination
US5082608A (en) 1990-06-14 1992-01-21 Owens-Illinois Plastic Products Inc. Polystyrene foam sheet manufacture
EP0464581B1 (de) 1990-07-04 1995-02-22 BASF Aktiengesellschaft Verfahren zur Herstellung von Schaumstoffplatten mit hoher Druckfestigkeit
US5240657A (en) 1990-11-26 1993-08-31 Basf Corporation Process for making expanded polymeric product with low level of emission of blowing agent
US5110837A (en) 1990-11-26 1992-05-05 Basf Corporation Process for making molded polymeric product with multipass expansion of polymer bead with low blowing agent content
US5110524A (en) 1990-11-26 1992-05-05 Basf Corporation Process for making molded polymeric product with multipass expansion of polymer bead with low blowing agent content
US5258415A (en) 1991-11-14 1993-11-02 Basf Aktiengesellschaft Expandable styrene polymers containing carbon dioxide as blowing agent
DE4137405A1 (de) 1991-11-14 1993-05-19 Basf Ag Expandierbare styrolpolymerisate, enthaltend als treibmittel kohlendioxid
DE4138388A1 (de) 1991-11-22 1993-05-27 Basf Ag Verfahren zur herstellung von schaumstoffplatten mit hoher druckfestigkeit
US5218006A (en) 1992-06-01 1993-06-08 Reedy Michael E Process for producing polystyrene foam
DE4236579A1 (de) 1992-06-04 1993-12-09 Basf Ag Verfahren zur Herstellung von Schaumstoffplatten mit hoher Druckfestigkeit aus Styrolpolymerisaten
US5244927A (en) 1992-06-09 1993-09-14 The Dow Chemical Company Low density styrene polymer foams and process for preparing same
US5332761A (en) 1992-06-09 1994-07-26 The Dow Chemical Company Flexible bimodal foam structures
US5288740A (en) 1992-10-23 1994-02-22 The Dow Chemical Company Process for making alkenyl aromatic foam packing bodies with carbon dioxide and/or ethane blowing agent systems
US5269987A (en) 1992-12-22 1993-12-14 Reedy Michael E Process for producing alkenyl aromatic foams using a combination of atmospheric and organic gases and foams produced thereby
WO1994028058A1 (de) 1993-05-27 1994-12-08 Basf Aktiengesellschaft Unter verwendung halogenfreier treibmittel hergestellte schaumstoffplatten
US5422378A (en) * 1993-06-04 1995-06-06 The Dow Chemical Company Foamable styrenic polymer gel and resulting foam
US5389694A (en) 1993-06-04 1995-02-14 The Dow Chemical Company Foamable styrenic polymer gel having a carbon dioxide blowing agent and a process for making a foam structure therefrom
US5434195A (en) 1994-06-23 1995-07-18 The Dow Chemical Company Extruded, open-cell alkenyl aromatic polymer foam and process for making
GB9420644D0 (en) 1994-10-13 1994-11-30 Dow Chemical Co Non-linear styrenic polymer-based foams
DE4445140A1 (de) 1994-12-17 1996-06-20 Basf Ag Mit Kohlendioxid getriebener Schaum aus Styrolpolymeren
JP3816523B2 (ja) 1995-04-27 2006-08-30 ダウ グローバル テクノロジーズ インコーポレイティド 押出連続気泡の微小気泡発泡体、及びその製造方法
DE19615486A1 (de) 1996-04-19 1997-10-23 Basf Ag Unter Verwendung halogenfreier Treibmittel hergestellte Schaumstoffplatten
DE19637366A1 (de) * 1996-09-13 1998-03-19 Basf Ag Schaumstoffplatten mit verbesserter Mineralölbeständigkeit und Expandierbarkeit

Also Published As

Publication number Publication date
US6268046B1 (en) 2001-07-31
CA2346992C (en) 2009-12-29
AU6521799A (en) 2000-05-08
AU757026B2 (en) 2003-01-30
ES2239463T3 (es) 2005-09-16
ATE294211T1 (de) 2005-05-15
EP1124887B1 (de) 2005-04-27
KR100595337B1 (ko) 2006-07-03
EP1124887A1 (de) 2001-08-22
WO2000023511A1 (en) 2000-04-27
KR20010083914A (ko) 2001-09-03
CA2346992A1 (en) 2000-04-27
DE69925014T2 (de) 2006-03-09

Similar Documents

Publication Publication Date Title
DE69925014D1 (de) Verfahren zur herstellung von extrudiertem schaumstoff
ATE196641T1 (de) Verfahren zur herstellung von alkenyl aromatischen schaumstoffen unter verwendung einer zusammensetzung aus atmosphärischen und organischen gasen und danach hergestellte schaumstoffe
PL311753A1 (en) Foamed plastic boards made using foaming agents being free of halogens
ATE152956T1 (de) Schlagverfahren und system zur kontinuierlichen herstellung von polyurethanschaumstoffblocken
BR9612060A (pt) Espuma termoplástica e processo para a produção da mesma usando dióxido de carbono
DE69412601D1 (de) Verfahren zur herstellung von polyurethanhartschaumstoffen
KR910004722A (ko) 발포제로서 이산화탄소만으로 제조된 폴리스티렌 발포체 및 이의 제조방법
CA2344228A1 (en) Process for producing extruded foam products having polystyrene blends with high levels of co2 as a blowing agent
DE69323869D1 (de) Verfahren zur herstellung von polystyrolschaumstoff
ATE277733T1 (de) Schaumstoff und verfahren zur herstellung
MY130472A (en) A process for producing thermoformable foam sheet using a physical blowing agent.
ATE151096T1 (de) Verfahren zur herstellung von schaumstoffplatten mit hoher druckfestigkeit aus styrolpolymerisaten
DE59100137D1 (de) Verfahren zur herstellung von geschaeumten polystyrolfolien.
ATE138849T1 (de) Verfahren zur herstellung eines schaumkunststoffes
CA2347267A1 (en) Process and apparatus for producing foam
DK0602262T3 (da) Baneformede skumplastplader af polyolefiner
ATE344822T1 (de) Verfahren zur herstellung von styrolschaumstoff
AU2677595A (en) Foaming method
DE69229894D1 (de) Verfahren zur Herstellung von expandierbaren Partikeln aus Styrolpolymer
ATE195330T1 (de) Unter verwendung halogenfreier treibmittel hergestellte schaumstoffplatten
DE69013365D1 (de) Verfahren zur herstellung eines wärmedämmenden geschäumten plastikmaterials und bei diesem verfahren verwendetes treibmittel.
ATE111495T1 (de) Verfahren zur herstellung von schaumstoff auf isocyanatbasis.
DE69832271D1 (de) Mischung und Verfahren zur Herstellung eines expandierten polymeren Produkts
ATE358008T1 (de) Verfahren zur herstellung einer düsenanordnung
DE59002683D1 (de) Verfahren zur Herstellung von Fibrillen aus offenzelligen Schäumen.

Legal Events

Date Code Title Description
8364 No opposition during term of opposition
8327 Change in the person/name/address of the patent owner

Owner name: OWENS CORNING INTELLECTUAL CAPITAL,LLC (N. D. , US

8328 Change in the person/name/address of the agent

Representative=s name: PATENT- UND RECHTSANWAELTE BARDEHLE, PAGENBERG, DO