DE690715C - Process for preparing materials that contain tantalum and / or niobium - Google Patents
Process for preparing materials that contain tantalum and / or niobiumInfo
- Publication number
- DE690715C DE690715C DE1937S0126906 DES0126906D DE690715C DE 690715 C DE690715 C DE 690715C DE 1937S0126906 DE1937S0126906 DE 1937S0126906 DE S0126906 D DES0126906 D DE S0126906D DE 690715 C DE690715 C DE 690715C
- Authority
- DE
- Germany
- Prior art keywords
- niobium
- tantalum
- tin
- manganese
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zum Vorbereiten von Stoffen, die Tantal und/oder Niob enthalten Die Erfindung betrifft ein Verfahren zum Vorbereiten von Tantal oder Niob und mindestens eines der Metalle Zinn, Mangan, Eisen enthaltenden Ausgangsstoffen für die vqr der eigentlichen Aufarbeitung auf Tantal oder Niob erfolgende Entfernung,des Zinns, Mangans und Eisens durch Auslaugen dieser Bestandteile.Process for preparing materials containing tantalum and / or niobium The invention relates to a method for preparing tantalum or niobium and at least one of the metals tin, manganese, iron containing raw materials for the vqr of actual processing to remove tantalum or niobium, the tin, Manganese and iron by leaching these components.
Es ist bekannt, Zinn auf chemischem Wege aus Anodenschlamm zu entfernen, nachdem dieses zuerst durch Metalle (Al, Mg, Zn) reduziert worden ist, welche mit dem feuchten Anodenschlamm bei Zimmertemperatur vermischt werden und reagieren.It is known to chemically remove tin from anode sludge, after this has first been reduced by metals (Al, Mg, Zn), which with are mixed with the moist anode sludge at room temperature and react.
Die Anwendung ,dieses Verfahrens auf tantal- und niobhaltige Rohstoffe würde ohne Erfolg bleiben, da die reduzierenden Metalle bei .dieser Temperatur überhaupt nicht einwirken können.The application of this process to raw materials containing tantalum and niobium would be unsuccessful, since the reducing metals at .this temperature at all cannot act.
Auch die Verwendung von festem Kohlenstoff, von Wasserstoff, Wassergas, Kohlenoxyd für Reduktionszwecke .ist bekannt. Man konnte aber nicht voraussagen, daß die Reduktion von tantal- und niobhaltigen. Stoffen durch Kohlenstoff keine unerwünschte Nebenreaktionen, wie z. B. Carbidbildung, hervorrufen würde, denn die Wirksamkeit der obengenannten Gase als Reduktionsmittel hängt ab von der Form, unter welcher sich die Oxyde der zu reduzierenden Metalle befinden.Also the use of solid carbon, hydrogen, water gas, Carbon oxide for reduction purposes is known. But you couldn't predict that the reduction of tantalum and niobium. Substances due to carbon none undesirable side reactions, such as. B. Carbide formation would cause, because the Effectiveness of the above gases as reducing agents depends on the form under which are the oxides of the metals to be reduced.
Die Erfindung ist dadurch .gekennzeichnet, daß das Gut im ungeschmolzenen Zustande mit einem gasförmigen oder vergasbaren Reduktionsmittel, z. B. Kohlenstoff, Kohlenoxyd, Wasserstoff, Wassergas, Methan u.sw., zwischen 8oo und i2oo° C behandelt wird, so daß allein das Zinn, Mangan, Eisen reduziert werden, nicht aber nennenswerte Mengen an Tantal -oder Niob.The invention is characterized in that the material in the unmelted Conditions with a gaseous or gasifiable reducing agent, e.g. B. carbon, Carbon oxide, hydrogen, water gas, methane, etc., between 800 and 1200 ° C treated so that only the tin, manganese, and iron are reduced, but not noteworthy Amounts of tantalum or niobium.
Die Mischung wird auf die erforderliche Temperatur gebracht, die für jeden besonderen Fall durch Versuche bestimmt wird, und zwar ganz nach der Zusammensetzung des Ausgangsstoffes. Auf alle Fälle soll die Temperatur so bemessen werden, daß ein Schmelzen der Beschickung vermieden wird. In gewissen Fällen hat sich für Holzkohle eine Temperatur zwischen 8oo und i2oo° C als vorteilhaft erwiesen, während bei Verwendung von Wasserstoff 85o bis goo° C- genügen. Wird die Reduktion durch Koks oder Kohlenoxyd., herbeigeführt, so muß .die Temperatur höher bemessen werden.The mixture is brought to the required temperature for each particular case is determined by experiment, according to its composition of the starting material. In any case, the temperature should be measured so that melting of the feed is avoided. In certain cases it has opted for charcoal a temperature between 800 and 1200 ° C is advantageous proven while when using hydrogen 85o to goo ° C is sufficient. Will the reduction brought about by coke or carbon dioxide, the temperature must be higher will.
Nach der Reduktion und erforderlichen= nach Zerkleinerung kann das behandelte Erzeugnis einer Auslaugung unterworfen werden, um das reduzierte Zinn und/oder Mangan und/oder Eisen zu lösen. Die Lösung des Zinns und/oder des Mangans und/oder des Eisens kann von -dem Rückstand -in bekannter Weise geschieden werden. Das Tantal und/ oder das Niob werden dann auf bekanntem Wege aus dem Rückstand extrahiert. Diese Extraktion ist sehr erleichtert, wenn Zinn, Mangan und Eisen nicht vorliegen.After reduction and required = after comminution, that can treated product undergoes leaching to produce the reduced tin and / or to dissolve manganese and / or iron. The solution of tin and / or manganese and / or the iron can be separated from the residue in a known manner. The tantalum and / or the niobium are then extracted from the residue in a known manner. This extraction is much easier when tin, manganese and iron are not present.
Claims (1)