DE483341C

DE483341C - Lining compound for crucibles made of metal

Info

Publication number: DE483341C
Application number: DEA53684D
Authority: DE
Original assignee: AEG AG
Current assignee: AEG AG
Priority date: 1927-03-26
Filing date: 1928-03-27
Publication date: 1929-09-30

Description

Auskleidungsmasse für Schmelztiegel aus lnetall Bei Schmelztiegeln, die zum Schmelzen von Metallen dienen, tritt oft der Übelstand auf, daß das geschmolzene Metall das Metall des Tiegels selbst auflöst und dadurch verunreinigt wird. So kommt es vor, daß beim Schmelzen von Aluminium in einem Eisen- oder Stahltiegel das Aluminium das Tiegelmaterial auflöst und dann einen Eisengehalt von q. bis 5 ° /o aufweist, wodurch es brüchig und seine Leitfähigkeit beeinträchtigt wird.Lining compound for crucibles made of metal For crucibles, which are used to smelt metals, the disadvantage often occurs that the molten Metal dissolves the metal of the crucible itself and becomes contaminated as a result. So come it is said that when aluminum is melted in an iron or steel crucible, the aluminum the crucible material dissolves and then an iron content of q. up to 5%, making it brittle and impairing its conductivity.

Um diesem Übelstande abzuhelfen, hat man z. B. das Tiegelinnere mit Kalk gestrichen oder getüncht, doch mußte der Anstrich oder die Tünche immer wieder erneuert werden.To remedy this inconvenience, one has z. B. the inside of the crucible Lime painted or whitewashed, but the painting or whitewash had to be repeated over and over again to be renewed.

Gemäß der Erfindung wird eine dauerhafte Auskleidung, die die Legierung des geschmolzenen Metalles mit dem Tiegelmaterial verhindert, dadurch erzielt, daß man Calciumhydroxyd mit einem in der Hitze schmelzenden Bindemittel, wie Magnesiumsulfat oder Borax, verwendet. Zu diesem Zwecke wird Calciumhydroxyd, etwa als gelöschte KalkschIacke aus Stahlschmelzöfen, mit Magnesiumsulfat oder Borax und weißem Email, wie es zum Anstrich für Gußeisen verwendet wird, gemischt. Diese Teile werden dann ganz fein gemahlen und mit Wasser zu einer dünnen Paste verrührt, wobei man noch ein klebriges, organisches Bindemittel, z. B. Melasse, zusetzt. Der auszukleidende Metalltiegel wird nun mäßig erwärmt und innen mit der Paste ausgestrichen. Nach Trocknen derselben erhitzt man den Tiegel auf etwa 5oo bis 7oo° C während einer bestimmten Zeit, j e nach Dicke des Tiegels und Anstriches, bis derselbe verschmolzen ist. Bei einer Wandstärke des Tiegels von etwa 18 mm genügen etwa 2 Stunden. Gußeiserne Tiegel dürfen nicht über 7oo° C erhitzt werden, da die von dem Gußeisen absorbierten Gase bei einer höheren Temperatur entweichen und auf dem Überzug Blasen verursachen, während bei Stahltiegeln die genannte Temperatur ohne Gefahr überschritten werden kann. Ist der Überzug einmal verhärtet, so widersteht er späterhin beliebig hohen Temperaturen. Zur Erzielung einer größeren Dichtigkeit kann man den Anstrich wiederholen und etwa entstandene Löcher mittels einer dicken Paste verstreichen. Die beschriebene Auskleidung hat den Vorteil, daß sie in der Hitze mit der Oberfläche- des Tiegels verschmilzt, da beide Materialien bis zu einem gewissen Grade ineinander löslich sind.According to the invention, a permanent lining that contains the alloy of the molten metal with the crucible material prevented, achieved in that calcium hydroxide with a hot melt binder such as magnesium sulfate or borax is used. For this purpose calcium hydroxide is used, roughly as extinguished Lime slag from steel melting furnaces, with magnesium sulfate or borax and white enamel, as used to paint cast iron. These parts are then ground very finely and mixed with water to form a thin paste, while still a sticky organic binder, e.g. B. molasses, adds. The one to be lined The metal crucible is now moderately heated and the paste is spread on the inside. To Drying the same is heated the crucible to about 500 to 700 ° C during a A certain time, depending on the thickness of the crucible and paint, until the same fused is. With a wall thickness of the crucible of about 18 mm, about 2 hours are sufficient. Cast iron Crucibles must not be heated above 700 ° C, as they would be absorbed by the cast iron Gases escape at a higher temperature and cause bubbles on the coating, while in the case of steel crucibles, the specified temperature can be exceeded without risk can. Once the coating has hardened, it will later withstand any high level of resistance Temperatures. The painting can be repeated to achieve greater impermeability and spread any holes that may have arisen with a thick paste. The described Lining has the advantage that it is in the heat with the surface of the crucible fuses because both materials are soluble in one another to a certain extent are.

Ein geeignetes Mischungsverhältnis ist: etwa zoo Gewichtsteile Calciumhydroxyd, - 6 - Magnesiumsulfat oder Borax, - 26 - Email, - 12 - Melasse. Vorteilhaft verwendet man ein Boro-Silikat-Email, wie es gewöhnlich zum Anstrich von Gußeisen verwendet wird, um der Masse eine größere Härte und Steinähnlichkeit zu verleihen; doch kann es auch unter Umständen weggelassen werden.A suitable mixing ratio is: about zoo parts by weight of calcium hydroxide, - 6 - magnesium sulfate or Borax, - 26 - Email, - 12 - molasses. It is advantageous to use a borosilicate enamel, as is commonly used for painting cast iron, in order to give the mass greater hardness and resemblance to stone; but it can also be omitted under certain circumstances.

Magnesiumsulfat oderBoraxwerden zugesetzt, um in der Hitze die einzelnen Teile der Mischung fest aneinanderzubinden und das Zusammenschmelzen mit der Tiegeloberfläche zu bewirken. Aber auch andere Bindemittel können verwendet werden, z. B. Natriumsilikat bei Schmelztiegeln für Blei oder Zinn, jedoch nicht für Aluminium.Magnesium sulfate or borax are added to keep the individual in heat Tying parts of the mixture tightly together and melting together with the crucible surface to effect. But other binders can also be used, e.g. B. sodium silicate in the case of crucibles for lead or tin, but not for aluminum.

Melasse wird nur als Bindemittel benutzt, um der Mischung den ersten Halt zu geben, bis diese dann durch das Brennen zu einer festen Masse umgewandelt wird.Molasses is only used as a binder to get the mix first Hold until it is then converted to a solid mass by the burning process will.

Claims

PATENT CLAIMS: i. Lining compound for crucibles made of metal, characterized in that it consists of a mixture of calcium hydroxide with a heat-melting binders such as magnesium sulfate or borax.

2. Lining compound according to claim i, characterized in that it is also a borosilicate enamel contains.

3. Lining compound according to claim r and 2, characterized in that the starting material contains an addition of organic binding agent, such as molasses. q ..

Lining compound according to claims i to 3 ,. characterized in that they instead Borax contains sodium silicate.

5. Method of making the lining compound according to claims i to q., characterized in that the form a thin paste or Solution of mixed starting materials spread on the heated crucible, dried and heated to about 5oo to 7oo °, the lining with the crucible surface merges.

6. The method according to claim 5, characterized in that one of 100 parts by weight of calcium hydroxide, 6 - magnesium sulfate or Borax, 26 - Email and 12 - molasses goes out.