DE3854889T2 - Dielektrische Keramik mit hoher Dielektrizitätskonstante, niedrigem Verlustfaktor und flachem Temperaturkoeffizienten - Google Patents

Dielektrische Keramik mit hoher Dielektrizitätskonstante, niedrigem Verlustfaktor und flachem Temperaturkoeffizienten

Info

Publication number
DE3854889T2
DE3854889T2 DE3854889T DE3854889T DE3854889T2 DE 3854889 T2 DE3854889 T2 DE 3854889T2 DE 3854889 T DE3854889 T DE 3854889T DE 3854889 T DE3854889 T DE 3854889T DE 3854889 T2 DE3854889 T2 DE 3854889T2
Authority
DE
Germany
Prior art keywords
temperature coefficient
low loss
loss factor
high dielectric
flat temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE3854889T
Other languages
English (en)
Other versions
DE3854889D1 (de
Inventor
Terence C Dean
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tam Ceramics LLC
Original Assignee
Tam Ceramics LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from PCT/US1987/002907 external-priority patent/WO1988008830A1/en
Application filed by Tam Ceramics LLC filed Critical Tam Ceramics LLC
Application granted granted Critical
Publication of DE3854889D1 publication Critical patent/DE3854889D1/de
Publication of DE3854889T2 publication Critical patent/DE3854889T2/de
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01G—CAPACITORS; CAPACITORS, RECTIFIERS, DETECTORS, SWITCHING DEVICES OR LIGHT-SENSITIVE DEVICES, OF THE ELECTROLYTIC TYPE
    • H01G4/00—Fixed capacitors; Processes of their manufacture
    • H01G4/002—Details
    • H01G4/018—Dielectrics
    • H01G4/06—Solid dielectrics
    • H01G4/08—Inorganic dielectrics
    • H01G4/12—Ceramic dielectrics
    • H01G4/1209—Ceramic dielectrics characterised by the ceramic dielectric material
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/46—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates
    • C04B35/462—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates
    • C04B35/465—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates based on alkaline earth metal titanates
    • C04B35/468—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates based on alkaline earth metal titanates based on barium titanates
    • C04B35/4682—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates based on alkaline earth metal titanates based on barium titanates based on BaTiO3 perovskite phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/6261—Milling
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/62605—Treating the starting powders individually or as mixtures
    • C04B35/62625—Wet mixtures
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/02—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of inorganic substances
    • H01B3/12—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of inorganic substances ceramics
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01G—CAPACITORS; CAPACITORS, RECTIFIERS, DETECTORS, SWITCHING DEVICES OR LIGHT-SENSITIVE DEVICES, OF THE ELECTROLYTIC TYPE
    • H01G4/00—Fixed capacitors; Processes of their manufacture
    • H01G4/002—Details
    • H01G4/018—Dielectrics
    • H01G4/06—Solid dielectrics
    • H01G4/08—Inorganic dielectrics
    • H01G4/12—Ceramic dielectrics
    • H01G4/1209—Ceramic dielectrics characterised by the ceramic dielectric material
    • H01G4/1218—Ceramic dielectrics characterised by the ceramic dielectric material based on titanium oxides or titanates
    • H01G4/1227—Ceramic dielectrics characterised by the ceramic dielectric material based on titanium oxides or titanates based on alkaline earth titanates
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01G—CAPACITORS; CAPACITORS, RECTIFIERS, DETECTORS, SWITCHING DEVICES OR LIGHT-SENSITIVE DEVICES, OF THE ELECTROLYTIC TYPE
    • H01G4/00—Fixed capacitors; Processes of their manufacture
    • H01G4/30—Stacked capacitors
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2311/00—Metals, their alloys or their compounds
    • B32B2311/02—Noble metals
    • B32B2311/08—Silver
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3251—Niobium oxides, niobates, tantalum oxides, tantalates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3275—Cobalt oxides, cobaltates or cobaltites or oxide forming salts thereof, e.g. bismuth cobaltate, zinc cobaltite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
    • C04B2235/449—Organic acids, e.g. EDTA, citrate, acetate, oxalate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5409—Particle size related information expressed by specific surface values
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5445—Particle size related information expressed by the size of the particles or aggregates thereof submicron sized, i.e. from 0,1 to 1 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/60—Aspects relating to the preparation, properties or mechanical treatment of green bodies or pre-forms
    • C04B2235/602—Making the green bodies or pre-forms by moulding
    • C04B2235/6025—Tape casting, e.g. with a doctor blade
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/345—Refractory metal oxides
    • C04B2237/346—Titania or titanates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/408—Noble metals, e.g. palladium, platina or silver
DE3854889T 1987-11-03 1988-10-04 Dielektrische Keramik mit hoher Dielektrizitätskonstante, niedrigem Verlustfaktor und flachem Temperaturkoeffizienten Expired - Fee Related DE3854889T2 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US1987/002907 WO1988008830A1 (en) 1986-11-03 1987-11-03 Dielectric ceramic with high k, low df and flat tc

Publications (2)

Publication Number Publication Date
DE3854889D1 DE3854889D1 (de) 1996-02-22
DE3854889T2 true DE3854889T2 (de) 1996-05-15

Family

ID=22202652

Family Applications (1)

Application Number Title Priority Date Filing Date
DE3854889T Expired - Fee Related DE3854889T2 (de) 1987-11-03 1988-10-04 Dielektrische Keramik mit hoher Dielektrizitätskonstante, niedrigem Verlustfaktor und flachem Temperaturkoeffizienten

Country Status (3)

Country Link
EP (1) EP0315324B1 (de)
AT (1) ATE133001T1 (de)
DE (1) DE3854889T2 (de)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100418590B1 (ko) * 1998-05-20 2004-02-11 도호 티타늄 가부시키가이샤 티탄산바륨 분말
EP1245945A3 (de) * 2001-03-28 2003-12-17 Sysmex Corporation Teilchenmessverfahren

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61193419A (ja) * 1985-02-20 1986-08-27 株式会社村田製作所 還元再酸化型半導体コンデンサ磁器組成物
JPS61275164A (ja) * 1985-05-03 1986-12-05 タム　セラミツクス　インコ−ポレイテツド 誘電体セラミック組成物
US4710227A (en) * 1986-04-28 1987-12-01 The Dow Chemical Company Dispersion process for ceramic green body
WO1988008830A1 (en) * 1986-11-03 1988-11-17 Dean Terence C Dielectric ceramic with high k, low df and flat tc
JP2649342B2 (ja) * 1986-12-04 1997-09-03 太陽誘電株式会社 電子部品用磁器の製造方法

Also Published As

Publication number Publication date
EP0315324B1 (de) 1996-01-10
EP0315324A2 (de) 1989-05-10
DE3854889D1 (de) 1996-02-22
ATE133001T1 (de) 1996-01-15
EP0315324A3 (en) 1990-01-31

Similar Documents

Publication Publication Date Title
DE3686086T2 (de) Dielektrische keramische zusammensetzung mit hoher dielektrizitaetskonstante und flacher temperaturkoeffizientencharakteristik.
DE3880895D1 (de) Dielektrische keramische zusammensetzung.
DE3854889T2 (de) Dielektrische Keramik mit hoher Dielektrizitätskonstante, niedrigem Verlustfaktor und flachem Temperaturkoeffizienten
ATE14714T1 (de) Temperaturstabile dielektrische keramische zusammensetzung auf basis von bariumtitanat und kondensator mit dieser zusammensetzung.
EP0221696A3 (de) Dielektrische Zusammensetzungen
DE3278775D1 (en) Heating diesel fuel
GR850003B (de)
ATE164370T1 (de) Keramische zusammensetzungen auf basis von blei- perowskit ohne freies bleioxid
SU1137088A1 (ru) Стекло
US2754313A (en) Stabilizing methylpolysiloxane fluids
EP0200484A3 (en) Ultralow fire ceramic composition
SU928672A1 (ru) Металлокерамический материал дл изготовлени электронагревателей
SU1643491A1 (ru) Керамический материал
KR890015301A (ko) 반도성 BaTiO₃의 제조방법
JPS53149696A (en) Dielectric porcelain composition for substrate
FEDOROV ELECTRICAL PROPERTIES OF THE COMPOUND 12 H-LA 4 TI 3 O 12.
SU967974A1 (ru) Стекло
SU834781A1 (ru) Резистивный материал
JPS5436598A (en) Ceramic dielecyric composite for temperature compensation
JPS6031793B2 (ja) 誘電体磁器組成物
JPS6054901B2 (ja) 高周波用誘電体磁器組成物
JPH0345556A (ja) セラミック回路基板用誘電体組成物
JPS5427999A (en) Porcelain dielectric compound for temperature compensation
JPS5436599A (en) Ceramic dielecyric composite for temperature compensation
MIKHAILOVA et al. SINTERING AND ELECTROPHYSICAL PROPERTIES OF MATERIALS OF THE SYSTEM CATIO 3-CATISIO 5.

Legal Events

Date Code Title Description
8364 No opposition during term of opposition
8339 Ceased/non-payment of the annual fee