DE310176C - - Google Patents
Info
- Publication number
- DE310176C DE310176C DENDAT310176D DE310176DA DE310176C DE 310176 C DE310176 C DE 310176C DE NDAT310176 D DENDAT310176 D DE NDAT310176D DE 310176D A DE310176D A DE 310176DA DE 310176 C DE310176 C DE 310176C
- Authority
- DE
- Germany
- Prior art keywords
- lead
- baths
- iron
- bath
- pfannhauser
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Die Rüstungsindustrie stellt heute bei dem Mangel an Kupfer viele. Gegenstände, die bisher aus Kupfer, Kupferlegierungen, Messing u. dgl. bestanden, aus Eisen her, wodurch sie der Gefahr des Röstens ausgesetzt sind. Ein Mittel zur Vermeidung des Röstens ist das Verbleien.The armaments industry today represents a large number due to the shortage of copper. Items so far made of copper, copper alloys, brass and the like, made of iron, which makes them dangerous are exposed to roasting. One way to avoid roasting is to use lead.
Man hat das Verbleien bisher nur in Bädern mit äußerer Strom'quelle vorgenommen, jedoch ohne besonderen Erfolg. Ein verbessertes Verfahren ist das von Betts. Von diesem Bade jedoch sagt Pfannhauser, 1910, S. 597, daß es, wie alle neuen Bleibäder, die mit freier Säure arbeiten, den auch bei den Zinkbädern beobachteten Übelstand besitzt, daß sie nicht in die Tiefen arbeiten ; maii müßte daher die Arbeitsweise beim elektrolytischen Verbleien, sofern man sich neuer Elektrolyte bedient, so einrichten, daß man die Anoden den zu' verbleienden Objekten in Form und Größe anpaßt, ferner müßte man zu sogenannten Hilfs- und Innenarioden Zuflucht nehmen. Dieses Verfahren ist naturgemäß sehr umständlich und . besonders ungeeignet für dieRüstungsindustrie, wo es sich oft um Hohlkörper handelt, die innen ' und außen zu verbleien sind, z. B. ist besonders bei Geschossen die Innenverbleiung wesentlich, da hier irgendein innerer Teil, z. B. der Zünder, festrosten kann, so daß dann das Geschoß nicht zum Krepieren kommt.Leading has hitherto only been carried out in baths with an external power source, however without any particular success. An improved method is that of Betts. From this bath however, Pfannhauser, 1910, p. 597 says that, like all new lead baths, those with free acid work, which also has the disadvantage observed in the zinc baths that they are not in the Working deep; maii would therefore have to work with electrolytic lead, if if new electrolytes are used, they should be arranged in such a way that the anodes are the ones to be left Objects in shape and size adapts, also one would have to so-called auxiliary and Take refuge in interior aisles. This process is naturally very cumbersome and . particularly unsuitable for the armaments industry, where it is often hollow bodies that are inside 'and are to be left outside, z. B. the interior lead is essential, especially in the case of projectiles, because here some inner part, e.g. B. the detonator, can rust, so that then the projectile does not comes to creping.
Nun hat man vorgeschlagen, das Eisen vor der Verbleiung zu verkupfern (Langbein, 1906, S. 391). Aber dieses Verfahren ist naturgemäß zur Zeit wegen des Mangels an Kupfer nicht anwendbar und auch an sich in normalen Zeiten zu unwirtschaftlich und umständlich.It has now been suggested to copper-plate the iron before it is leaded (long leg, 1906, p. 391). But this procedure is natural Not applicable at the moment due to the lack of copper and also in itself in normal Times too uneconomical and cumbersome.
Nach der Erfindung sollen diese Nachteile durch die Kombination einer Verbleiung nach dem Sud- . oder Kontaktverfahren' mit der daiauffolgenden Hauptverbleiung durch äußere Stromzuführung beseitigt werden.According to the invention, these disadvantages are alleviated by the combination of leading the Sud-. or contact method with the subsequent main lead by external Power supply to be eliminated.
Durch das Sud- oder Kontaktbad wird ein dünner, hauchartiger Überzug hergestellt, der sich fest mit dem Metall verbindet und daher auch vorzüglich als Grundlage für die Weiterbehandlung in gewöhnlichen Bleibädern mit äußerer Stromquelle zwecks Erzielung dicker Bleiüberzüge dienen kann.The brewing or contact bath creates a thin, puff-like coating, the bonds firmly to the metal and is therefore an excellent basis for further treatment in ordinary lead baths with an external power source in order to achieve thicker ones Lead coatings can serve.
Die bisherigen Bäder mit äußerer Stromquelle waren nicht geeignet zur Herstellung einer homogenen Verbindung des Eisens o. dgl. mit dem Blei, vielmehr bildete sich nach kurzer Zeit schon Bleischwamm. So gibt auch Buchner, 1912, S. 177, an, daß es bisher schwierig war, einen vollkommen dichten Bleiniederschlag auf anderen Metallen zu erhalten, und auch Pfannhauser erklärt, daß bisher die Wünsche der Galvanotechnik nach einem Universalbade für die Verbleiung nicht erfüllt seien; diese Lücke füllt die Erfindung aus. ■The previous baths with an external power source were not suitable for producing one homogeneous connection of iron or the like with lead, rather it formed after a short time Time already lead sponge. Buchner, 1912, p. 177, states that so far it was difficult to get a completely dense lead deposit on other metals, and Pfannhauser also explains that so far the needs of electroplating have been for a Universal bath for the lead are not fulfilled; the invention fills this gap. ■
Andererseits ist bei Pfannhauser, S. 597 unten, ein Verfahren Fischer-Pfannhauser beschrieben, wo angegeben ist, daß es gelungen wäre, Schichten von 10 mm Dicke herzustellen. Dazu ist zu bemerken, daß nach der Erfindung gerade mit geringsten Kosten im· Sudbade ein dünner, hauchartiger Überzug hergestellt wer-On the other hand, a Fischer-Pfannhauser method is described in Pfannhauser, p. 597 below, where it is stated that it would have been possible to produce layers 10 mm thick. It should be noted that, according to the invention, a brewing bath is available at the lowest cost thin, puff-like coating can be produced
den soll, besonders auch für Innenverbleiungen von Hohlkör^eJ^riiW.öiiiii φ& angegebene Verfahren Pfaia.nhau.s.er-piSQher .ungeeignet ist. the intended especially indicated for Innenverbleiungen of Hohlkör ^ eJ ^ riiW.öiiiii φ & procedures Pfaia.nhau.s.er-pi S Qher is .ungeeignet.
Dazu WMn^MSS teläe^Bätfern mit äußerer Stromquelle das Eisen nur einen Moment ohne Strom zu sein braucht, um in Lösung zu gehen und das gelöste Blei kristallinisch auszuscheiden. Hierauf weist auch Pf annhauser, S. 599, hin, indem er sagt, daß die Bleibäder sämtlich sehr heikel gegen Verunreinigungen sind, besonders Eisen und Zink wären ungemein schädlich, und es könnte daher nur zur größten Vorsicht geraten werden, wenn man sich nicht der Gefahr aussetzen .wolle, die teueren Bäder zu verderben.For this purpose, the iron needs to be without electricity for only a moment in order to dissolve and to precipitate the dissolved lead in a crystalline manner. Pfannhauser, p. 599, also points to this when he says that the lead baths are all very sensitive to contamination, especially iron and zinc would be extremely harmful, and therefore the greatest caution could be advised if one does not himself Exposing yourself to the risk of spoiling the expensive baths.
Mit den Bleibädern sind hier von Pf annhauser solche mit. äußerer Stromquelle gemeint.With the lead baths there are some from Pfannhauser. external power source meant.
Das bei Pfannhauser, S. 596 unten, erwähnte Bleibad ist kein Sudbad, sondern, ein Strombad und dazu eine alkalische Lösung, welche nicht die Ergebnisse wie die saure Lösung nach der Erfindung bietet, indem insbesondere die dort erwähnte Bildung von Bleischwamm auftritt, die bei dem Verfahren nach der Erfindung vermieden wird.The lead bath mentioned in Pfannhauser, p. 596 below, is not a brew bath, but a Electric bath and an alkaline solution, which does not produce the same results as the acidic solution offers according to the invention by in particular the formation of lead sponge mentioned there occurs, which is avoided in the method according to the invention.
Das Sudbad nach der Erfindung kann folgende Zusammensetzung haben:The brewing bath according to the invention can have the following composition:
H2O 10 1,H 2 O 10 1,
Pb(G2H3Cy2 35g,Pb (G 2 H 3 Cy 2 35g,
,0 C2H4O3 5-, 0 C 2 H 4 O 3 5-
d Glutin 5 -. d Glutin 5 -.
Diese Lösung wird erwärmt auf 80. bis 100 ° C. Die gereinigten Eisen- oder Zinkteile werden in die Lösung gebracht und verbleiben darin, bis sie überall ein grauweißes Aussehen haben. Dieser Niederschlag muß festhaften, was nach ι bis 2 Minuten eintritt.This solution is heated to 80-100 ° C. The cleaned iron or zinc parts are brought into the solution and remain in it, until they have a gray-white appearance everywhere. This precipitate must adhere to what is after ι occurs up to 2 minutes.
Verbleiung für andere Metalle außer Eisen und Zink :Leading for other metals besides iron and zinc:
Das Bad hat dieselbe Zusammensetzung wie oben. Als Kontaktmetall kann jetzt Eisen, Zink und Aluminium dienen. Der Vorgang ist im übrigen derselbe wie oben.The bathroom has the same composition as above. Iron can now be used as a contact metal, Zinc and aluminum are used. The process is otherwise the same as above.
Kurz zusammengefaßt sind die Vorzüge des Verfahrens nach Ansicht des Erfinders die folgenden.Briefly summarized, the inventor believes that the advantages of the method are the following.
1. Das Blei haftet direkt auf Eisen, während bei anderen Verfahren vielfach eine vorherige Verkupferung nötig ist. .1. The lead adheres directly to iron, while with other methods often a previous one Copper plating is necessary. .
2. Der Niederschlag bildet sich an allen Stellen der Metalloberfläche gleichmäßig und schnell, während bei gewöhnlichen Bleibädern die Vertiefungen der Metalle überhaupt kleine Bleiauflage erhalten oder die Erhöhungen übermäßig stark verbleit werden, ehe die Vertiefungen nur zum Teil mit Blei gedeckt sind.2. The precipitate forms evenly and quickly at all points on the metal surface, while in ordinary lead baths the depressions of the metals generally have a small amount of lead or the ridges are excessively leaded before the depressions are only partially covered with lead.
3. Es werden große Mengen Blei gespart, weil ein dünner Bleiniederschlag genügt, um das'Grundmetall damit gleichmäßig zu überziehen. 3. Large amounts of lead are saved because a thin deposit of lead is enough to to cover the base metal evenly with it.
4. Weitere Vorteile bestehen darin, daß das neue Verfahren sehr einfach und billig ist, nur wenige Arbeitskräfte erfordert und von jedem Arbeiter oder jeder Arbeiterin leicht erlernt werden kann.4. Other advantages are that the new process is very simple and cheap, only requires little labor and is easily learned by any worker can be.
Claims (1)