DE2616705C3 - Verfahren zum Verbinden von Formteilen aus Polyvinylidenfluorid - Google Patents

Verfahren zum Verbinden von Formteilen aus Polyvinylidenfluorid

Info

Publication number
DE2616705C3
DE2616705C3 DE2616705A DE2616705A DE2616705C3 DE 2616705 C3 DE2616705 C3 DE 2616705C3 DE 2616705 A DE2616705 A DE 2616705A DE 2616705 A DE2616705 A DE 2616705A DE 2616705 C3 DE2616705 C3 DE 2616705C3
Authority
DE
Germany
Prior art keywords
polyvinylidene fluoride
molded parts
heated
parts made
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE2616705A
Other languages
English (en)
Other versions
DE2616705B2 (de
DE2616705A1 (de
Inventor
Huynh Van Lyon Lang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PRODUITS CHIMIQUES UGINE KUHLMANN PARIS FR
Original Assignee
PRODUITS CHIMIQUES UGINE KUHLMANN PARIS FR
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PRODUITS CHIMIQUES UGINE KUHLMANN PARIS FR filed Critical PRODUITS CHIMIQUES UGINE KUHLMANN PARIS FR
Publication of DE2616705A1 publication Critical patent/DE2616705A1/de
Publication of DE2616705B2 publication Critical patent/DE2616705B2/de
Application granted granted Critical
Publication of DE2616705C3 publication Critical patent/DE2616705C3/de
Expired legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren zum Verbinden von Formteilen aus Polyvinylidenfluorid, bei dem ein Teil mit einem Mittel zum Lösen von Polyvinylidenfluorid in der Wärme oder mit einer Lösung von Polyvinylidenfluorid bestrichen wird, das andere Teil auf eine Temperatur oberhalb von 1000C erwärmt wird und bei dem die beiden zu verbindenden Flächen miteinander in Kontakt gebracht und in dieser Stellung abgekühlt werden.
Bei dem Verfahren zum Verbinden von Gegenständen unterschiedlicher Dicke aus Polyvinylidenfluorid, das Gegenstand des Hauptpatentes ist, bestreicht man den Gegenstand von geringerer Dicke erst mit einer Lösung von Polyvinylidenfluorid oder einem Mittel zum Lösen von Polyvinylidenfluorid in der Wärme, erhitzt den dickeren Gegenstand auf eine Temperatur zwischen 1500C und 3200C und läßt die miteinander in Kontakt gebrachten Flächen in dieser Stellung abkühlen.
Aufgabe der Erfindung ist es, das Verfahren des Hauptpatents 25 41 573 zu vereinfachen und die Festigkeit der Klebefuge noch zu verbessern.
Im Verlauf der weiteren Untersuchungen des KIebens von Formteilen aus Polyvinylidenfluorid und insbesondere von dünnen Teilen oder Rohren mit dünnen Wänden wurde überraschend gefunden, daß das Verbinden in einfacher Weise vorgenommen werden kann, wenn die beiden zu verbindenden Flächen mit dem Mittel oder mit der Lösung bestrichen, und die verbundenen Teile erwärmt werden.
Die zu verbindenden Flächen werden mit irgendeinem bekannten Mittel, z. B. Heißluftschweißen, Gasschweißen mit einem Flammenschutzschirm, mit einem Heizband mit elektrischer Widerstandsheizung, mit Thermofluiden, Wärmeschränken usw. erwärmt, wobei die Verklebung erst in dem Moment eintritt, in dem das Lösungsmittel oder die Polyvinylidenfluorid-Lösung in einem Lösungsmittel auf genügend hohe Temperatur erhitzt ist, um die vereinigten Oberflächen anzugreifen. Diese Temperatur liegt oberhalb 1000C und vorzugsweise zwischen einschließlich 120 und 17O0C. Die Zeit von der Verbindung der in ein Lösungsmittel oder in eine Polyvinylidenfluoridlösung eingetauchten Teile bis zu ihrem Erhitzen kann ohne Nachteil im Bereich mehrer Stunden, selbst im Mehrfachen von zehn Stunden
liegen.
Der Vorteil dieser Technik ist leicht einzusehen: Vor dem Erhitzen auf die Verklebungstemperatur, bei dem eine sofortige und endgültige Befestigung der Verbindung eintritt, kann jede Verbindung leicht hergestellt werden, beispielsweise die Montage von Rohrleitungen, die Änderung daran, oder das Ersetzen eines oder mehrerer Teile.
Das verwendete Lösungsmittel soll ein polares aprotisches Lösungsmittel und vorzugsweise eines der folgenden Lösungsmittel sein, die allein oder im Gemisch eingesetzt werden:
Dimethylformamid, Dimethylacetamid
Tetrahydrofuran, Dimethylsulfoxid,
Cyclohexanon, Hexamethylphosphoramid.
Butyrolacton.
Man kann ebenso eine Lösung von Polyvinylidenfluorid in einem der genannten Lösungsmittel verwenden.
Diese Lösung wird durch Auflösen von 0,1 bis 20 Gew.-% Polyvinylidenfluorid, bezogen auf das Lösungsmittel, vorzugsweise von 12 bis 14 Gew.-% erhalten, weil bei diesen letzteren PolyvinylideEiluoridkonzentrationen die Lösungen !agerbeständig sind und bei Temperaturen, die bis zu — 10C gehen, nicht ausgelieren. Wenn die Viskosität dieser Lösungen als zu gering angesehen wird, ist es möglich, sie zu erhöhen, indem man inerte Verdickungsmittel wie kolloidale Siliziumdioxide oder einen montmorillonitischen Ton zusetzt
Die folgenden Beispiele verdeutlichen die Erfindung.
Beispiel 1
Plättchenförmige Polyvinylidenfiuoridproben mit folgenden Maßen: 65 mm lang, 20 mm breit, 3 mm dick, werden bei den Klebeversuchen verwendet Man bestreicht eine Seite ihrer zu verklebenden Enden auf einer Fläche von 4 cm2 mit Dimethylacetamid von Raumtemperatur. Man bringt die mit Lösungsmittel bestrichenen Oberflächen miteinander in Kontakt Man erhitzt die verbundenen Enden der Probekörper mit Hilfe eines auf 1600C eingestellten Heißluftgebläses. Man heizt 30 see lang und bestimmt nach dem Abkühlen die Zugfestigkeit, indem man die freien Enden der zusammenklebenden Probekörper in die Spannbacken eines Dynamometers einspannt Man benötigt eine Kraft von 3000 kp, um den einen der beiden Probekörper zu zerbrechen, wobei die Verbindung unversehrt bleibt
Beispiel 2
Man nimmt die gleichen Probekörper wie in Beispiel 1 und verfährt auf folgende Weise: Man bestreicht eine Seite der zu verklebenden Enden auf einer Fläche von 4 cm2 mit vorher auf 12O0C erwärmtem Dimethylacetamid.
Man bringt die mit Lösungsmittel bestrichenen Seiten gegeneinander und legt die so verbundenen Probekörper 15 min lang in einen auf 1200C gehaltenen Heizschrank. Nach dem Abkühlen mißt man wie in Beispiel 1 die Zugfestigkeit auf einem Dynamometer und auch in diesem Falle reißt der Probekörper nicht in der Verklebung.
Beispiel 3
Man nimmt Proben aus Polyvinylidenfluorid mit ei-
nem äußeren Durchmesser von 20 mm, einer Stärke von 1,5 mm und einem vorher gemufften Ende zur Erleichterung der Verbindung. Man bestreicht die innere Wand des Endes eines anderen Rohres mit einer 12gew.-%igen Polyvinylidenfluorid-Lösung in Diaiethylacetamid in der Kälte. Nach dem Ineinanderfügen der beiden Rohre heizt man mit Hilfe eines auf 1700C eingestellten Heißluftgebläses den zusammengesetzten Teil, indem man das heiße Gebläse auf die ganze Oberfläche dieses Teils 15 bis 20 see lang richtet Nach dem Abkühlen teilt man die Verbindung durch Aufschlitzen in Längsrichtung in vier gleiche Teile, um vier Probekörper für die Messung der Zugfestigkeit zu erhalten. Wie in den voranstehenden Beispielen reißen die Probekörper nicht an den Verbindungsstellen.
10
15
60

Claims (2)

Patentansprüche:
1. Verfahren zum Verbinden von Formteilen aus Polyvinylidenfluorid, bei dem ein Teil mit einem Mittel zum Lösen von Polyvinylidenfluorid in der Wärme oder mit einer Lösung von Polyvinylidenfluorid bestrichen wird, das andere Teil auf eine Temperatur oberhalb von 1000C erwärmt und bei dem die beiden zu verbindenden Flächen miteinander in Kontakt gebracht und in dieser Stellung abgekühlt werden, nach Patent 2541 573, dadurch gekennzeichnet, daß beide zu verbindenden Flächen mit dem Mittel oder mit der Lösung bestrichen und die beiden verbundenen Teile erwärmt werden.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß man als zu verbindende Teile aus Polyvinylidenfluorid Rohrelemente mit einer maximalen Wandstärke von 10 mm verwendet.
DE2616705A 1975-04-16 1976-04-15 Verfahren zum Verbinden von Formteilen aus Polyvinylidenfluorid Expired DE2616705C3 (de)