DE2559790C2 - Water-based printing varnish for the production of gravure printing inks for plastic webs - Google Patents
Water-based printing varnish for the production of gravure printing inks for plastic websInfo
- Publication number
- DE2559790C2 DE2559790C2 DE19752559790 DE2559790A DE2559790C2 DE 2559790 C2 DE2559790 C2 DE 2559790C2 DE 19752559790 DE19752559790 DE 19752559790 DE 2559790 A DE2559790 A DE 2559790A DE 2559790 C2 DE2559790 C2 DE 2559790C2
- Authority
- DE
- Germany
- Prior art keywords
- printing
- weight
- water
- varnish
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
10 bis 30 Gew.-% Polyacrylsäureester-10 to 30% by weight polyacrylic acid ester
dispersion,
1,5 bis 4,5 Gew.-% Polymethacrylsäure-dispersion,
1.5 to 4.5% by weight of polymethacrylic acid
esterdispersion,
Rest azeotropes Alkohol-Wasser-Gemisch,ester dispersion,
Remainder of the azeotropic alcohol-water mixture,
mit Ammoniak oder Aminwith ammonia or amine
auf einen pH-Wert über 8 eingestellt,adjusted to a pH value above 8,
bestehtconsists
2. Dnjcldack nach Anspruch 1, dadurch gekennzeichnet, daß er 22 bis 28 Gew.-% Polyacrylsäureesterdispersion und 2 bis 2£ Gew.-% Polymethacrylsäureesterdispersion enthält2. Dnjcldack according to claim 1, characterized in that that he has 22 to 28 wt .-% polyacrylic acid ester dispersion and 2 to 2 pounds percent by weight polymethacrylic acid ester dispersion contains
3. Verwendung des Druckiackes nach Anspruch 1 oder 2 zur Herstellung einer Tiefdruckfarbe, dadurch gekennzeichnet, daß 70 bis 95 Teile Drucklack mit 30 bis 5 Teilen einer Druckfarbenpräparation, welche aus3. Use of the printing ink according to claim 1 or 2 for the production of a gravure printing ink, characterized in that 70 to 95 parts of printing varnish with 30 up to 5 parts of a printing ink preparation consisting of
30 bis 55 Gew.-% einer Polyacrylester-30 to 55% by weight of a polyacrylic ester
dispersion,
40 bis 65 Gew.-% eines azeotropendispersion,
40 to 65% by weight of an azeotropic
Alkohol-Wasser-Gemisches,
5 bis 20 Gew.-Teilen PigmentAlcohol-water mixture,
5 to 20 parts by weight pigment
besteht und mit Ammoniak oder Amin auf einen pH-Wert über 8 eingestellt ist, gemischt werden.and adjusted to a pH value above 8 with ammonia or amine.
4. Verwendung des Drucklackes nach Anspruch 2 mit einer Druckfarbenpräparation, die 40 bis 50Gew.-% Polyacryiesterdispersion und 50 bis 55 Gew.-% azeotropes Alkohol-Wasser-Gemisch enthält für den Zweck und in den Mengenverhältnissen von Anspruch 3.4. Use of the printing varnish according to claim 2 with a printing ink preparation which is 40 to 50% by weight polyacrylic ester dispersion and 50 to 55% by weight azeotropic alcohol-water mixture contains for the purpose and in the proportions of claim 3.
Die Erfindung betrifft einen Drucklack auf wäßriger Basis zur Herstellung von Tiefdruckfarben für Kunststoffbahnen, insbesondere von Polyvinylchlorid (PVC), sowie dessen Verwendung.The invention relates to an aqueous-based printing varnish for the production of gravure printing inks for plastic webs, especially of polyvinyl chloride (PVC) and its use.
Zum Bedrucken von PVC-Folien wird im allgemeinen das Rotationstiefdruckverfahren angewendet, da hiermit überlegene Druckqualitäten erzielbar sind. Dieses Verfahren erfordert den Einsatz von lösungsmittelhaltigen Dnicklacken auf Basis von Vinylcopolymeren oder anderen ähnlichen Polymeren. Ein besonderes Problem besteht hierbei in der erforderlichen guten Haftung der Drucklacke auf der PVC-Folie. Für diese gute Haftung ist in erster Linie das sorgfältig ausgewählte Lösungsmittelgemisch verantwortlich. Durch dieses organische Lösungsmittelgemisch werden auch die Trocknungszeiten so beeinflußt, daß ein schnelles und damit wirtschaftliches Bedrucken der Kunststoffbahnen möglich ist.The rotogravure printing process is generally used for printing on PVC films, because it is used superior print quality can be achieved. This process requires the use of solvent-based Thick lacquers based on vinyl copolymers or other similar polymers. A particular problem consists in the required good adhesion of the printing varnishes to the PVC film. For this good adhesion is primarily responsible for the carefully selected solvent mixture. Through this organic Solvent mixture are also the drying times influenced so that a quick and thus economical printing of the plastic webs is possible.
Ein großes Problem bei der Verwendung derartiger Drucklacke im Tiefdruckverfahren sind die sehr erheblichen Lösungsmittelmengen, welche in die Atmosphäre gelangen. Die Lösungsmittelverluste können dabei in der Größenordnung von einigen Tonnen pro Tag liegen. Eine wirtschaftliche Zurückgewinnung ist praktisch nicht möglich. Außer den erheblichen Verlusten ergibt sich dabei gleichzeitig eine beträchtliche Umweltverschmutzung.A major problem with the use of such printing varnishes in the gravure printing process is the very significant amounts of solvent released into the atmosphere. The solvent losses can are of the order of a few tons per day. An economic recovery is practically impossible. In addition to the considerable losses, there is also a considerable one Environmental pollution.
Eine einfache Möglichkeit, dieses insbesondere unter dem Gesichtspunkt des Umweltschutzes schwerwiegende Problem zu lösen, bestünde im Übergang auf Drucklacke, bei denen praktisch keine Lösungsmitteldämpfe anfallen. Derartige Drucklacke sind Kunststoffdispersionsfarben. Sie werden zum Bedrucken von Papier und Kunststoffbahnen nach dem Sieb- und Offsetdruck verwendet Hierbei handelt es sich stets um großflächige und einfache Drucke, weiche den Qualitätsanforderungen für viele Arten von bedruckten Kunststoffolien nicht genügen. Beispielsweise ist es mit diesen Druckmethoden nicht möglich, eine feine Holzmaserung aufzudrucken, um holzfumierartige Folien herzustellen. Demgegenüber erlaubt das Rotationstiefdruckverfahren die Hersteilung besonders feiner, naturgetreuer Holzimitationen. Die Kunststoffdispersionslacke können jedoch nach dem Rotationstiefdruckverfahren zur Bedrückung von Kunststoffolien nicht eingesetzt werden, da sie hierfür hinsichtlich Haftfestigkeit Druckschärfe und Trocknungseigenschäften ungeeignet sind.An easy way of taking this particular one Solving serious problems from the point of view of environmental protection would exist in the transition Printing varnishes that produce practically no solvent vapors. Such printing varnishes are plastic emulsion inks. They are used for printing on paper and plastic sheets after screen and offset printing large-scale and simple prints that meet the quality requirements for many types of printed matter Plastic foils are not enough. For example, with these printing methods it is not possible to print a fine To print wood grain to produce wood veneer-like foils. In contrast, the rotogravure printing process allows the production of particularly fine, lifelike wood imitations. The plastic dispersion paints can, however, be used for printing on plastic foils using the rotogravure printing process are not used, as they are used for this in terms of adhesive strength, pressure sharpness and drying properties are unsuitable.
Ziel der Erfindung ist daher die Schaffung eines Drucklackes, welcher die oben aufgeführten Nachteile nicht aufweist und insbesondere keine wesentlichen Mengen an organischen Lösungsmitteln erfordert andererseits jedoch die für das Rotationstiefdruckverfahren erforderlichen Eigenschaften besitzt und qualitativ hochwertige Drucke herzustellen gestattetThe aim of the invention is therefore to create a printing varnish which has the disadvantages listed above does not have and in particular does not require substantial amounts of organic solvents on the other hand, however, has the properties required for the rotogravure printing process and qualitatively Allowed to produce high quality prints
Gelöst wird diese Aufgabe wie in den Patentansprüchen definiertThis object is achieved as defined in the claims
Die Erfindung beruht auf der Erkenntnis, daß ein ganz bestimmtes Verhältnis von Polyacrylaten und Polymethacrylaten verwendet werden muß, um im Tiefdruckverfahren ohne störende organische Lösungsmittel auskommen zu können und gleichzeitig neben hoher Druckqualität auch Trocknungseigenschaften zu erzielen, welche die im Rotationstiefdruckverfahren üblichen Bedruckungsgeschwindigkeiten zulassen.The invention is based on the knowledge that a very specific ratio of polyacrylates and polymethacrylates must be used in order to get by in the gravure printing process without troublesome organic solvents to be able to and at the same time achieve drying properties in addition to high print quality, which allow the printing speeds customary in rotogravure printing.
Der erfindungsgemäße Drucklack eignet sich zum Bedrucken von Kunststoffbahnen auf Basis von Polyolefinen, Polyestern, Polyamiden, Polycarbonaten, Polyacrylaten, Polystyrolen, ABS, SAN, EVA und PVC. Besonders bevorzugt wird er zum Bedrucken von PVC-Folien angewendet. Hierunter fallen sowohl weichgemachte als auch weichmacherfreie PVC-Folien sowie PVC-Mischpolymerisatfolien, deren überwiegender Anteil aus Vinylchlorid stammt.The printing varnish according to the invention is suitable for printing plastic webs based on Polyolefins, polyesters, polyamides, polycarbonates, polyacrylates, polystyrenes, ABS, SAN, EVA and PVC. It is particularly preferably used for printing PVC films. This includes both plasticized as well as plasticizer-free PVC films and PVC mixed polymer films, the majority of which Part comes from vinyl chloride.
Das erfindungsgemäß verwendete Bindemittel für einen Drucklack besteht aus einer Mischung von Estern der Polyacrylsäure und der Polymethacrylsäure in ganz bestimmtem Gewichtsverhältnis, deren Estergruppe vorzugsweise aus einer geradkettigen, verzweigten oder cyclischen Alkylgruppe bis 1 bis 8, vorzugsweise mit 1 bis 4 Kohlenstoffatomen besteht. Ganz besonders gute Ergebnisse werden mit den Methyl- und Äthylestern erzielt.The binder used according to the invention for a printing varnish consists of a mixture of esters of polyacrylic acid and polymethacrylic acid in a specific weight ratio, their ester group preferably from a straight-chain, branched or cyclic alkyl group up to 1 to 8, preferably with 1 to 4 carbon atoms. Particularly good results are achieved with the methyl and ethyl esters achieved.
Die besten Ergebnisse, insbesondere hinsichtlich der Blockfreiheit beim Hedrucken, werden dann erzielt, wenn das Gewichtsverhältnis von Polyacrylsäureester zu Polymethacrylsäureester zwischen 100 :4 und 100 :8 liegt.The best results, especially with regard to the non-alignment when printing, are achieved when when the weight ratio of polyacrylic acid ester to polymethacrylic acid ester is between 100: 4 and 100: 8 lies.
Das Bindemittel liegt als Dispersion in wäßrigem Medium vor. Bevorzugt wird als Dispersionsmedium ein azeotropes Wasser-Alkohol-Gemisch. Als AlkoholThe binder is in the form of a dispersion in an aqueous medium. A is preferred as the dispersion medium azeotropic mixture of water and alcohol. As alcohol
kommt Methanol, Äthanol oder/und Propanol in Betracht Bevorzugt wird Äthanol. Der pH-Wert der Bindemitteldispersion soll neutral oder alkalisch sein. Bevorzugt wird ein pH-Wert über 8 eingestellt unter Verwendung von Ammoniak oder einem geeigneten Amin.methanol, ethanol and / or propanol come into consideration. Ethanol is preferred. The pH of the The binder dispersion should be neutral or alkaline. A pH value above 8 is preferably set using ammonia or a suitable one Amine.
Besonders bevorzugt ist eine Drucklackzusammensetzung, welcheParticularly preferred is a printing varnish composition which
22 bis 28 Gew.-% Polyacrylsäureesterdispersion22 to 28% by weight polyacrylic acid ester dispersion
und 2 bis 24 Gew.-% Polymethacrylsäureester-and 2 to 24% by weight of polymethacrylic acid ester
dispersion enthältdispersion contains
Aus dem erfindungsgemäßen Drucklack erhält man durch Vermischen mit einer Druckpigmentpräparation (Wasserteig) die eigentliche Farbe. Hierzu werden 30 bis 95 Teile des Drucklackes und 30 bis 5 Teile einer Druckpigmentpräparation (Wasserteig), welche aus The actual color is obtained from the printing varnish according to the invention by mixing it with a printing pigment preparation (water dough). For this purpose, 30 to 95 parts of the printing varnish and 30 to 5 parts of a printing pigment preparation (water dough), which are made of
30 bis 55 Gew.-% einer Polyacrylesterdispersion
40 bis 65 Gew.-% eines azcotropen 30 to 55 % by weight of a polyacrylic ester dispersion
40 to 65% by weight of an azcotropic
Alkohol-Wasser-Gemisches und
5bis20Gew.-% PigmentAlcohol-water mixture and
5 to 20% by weight pigment
besteht und mit Ammoniak oder Amin auf einen pH-Wert über 8 eingestellt ist vermischtand is mixed with ammonia or amine to a pH value above 8
Eine bevorzugte Druckpigmentpräparation (Wasserteig) enthältA preferred printing pigment preparation (water dough) contains
40 bis 50 Gew.-% Polyacrylesterdispersion und
50 bis 55 Gew.-% a-^otropes40 to 50% by weight polyacrylic ester dispersion and
50 to 55% by weight a- ^ otropes
Alkohol-Wasser-Gemisch.Alcohol-water mixture.
Die Polyacrylsäureester- und Polymethacrylsäureesterdispersionen, die für die Herstellung der Druckfarbe eingesetzt werden, sind im Handel erhältlich. In beiden Bestandteilen der Druckfarbe, also dem Drucklack und dem Wasserteig, wird zweckmäßig die gleiche Polyacrylatdispersion verwendetThe polyacrylic acid ester and polymethacrylic acid ester dispersions that are used for the production of printing inks are used are commercially available. In both components of the printing ink, i.e. the printing varnish and the water dough, the same polyacrylate dispersion is expediently used
Mit dem erfindungsgemäßen Drucklack bzw. der damit hergestellten Druckfarbe wird im Tiefdruckverfahren, insbesondere im Kupferrotationstiefdruckverfahren, eine einwandfreie Haftung auf den Kunststoffbahnen, insbesondere der Polyvinylchloridbahn bzw. -folie erzielt, sowie eine schnelle Trocknung und gute Abriebfestigkeit der Druckfarbe. Die Trocknungszeit kann durch Einstellung des Wasser-Alkohol-Verhältnisses in der Trägerflüssigkeit beeinflußt werden. Desgleichen kann die jeweils günstigste Viskosität, die sich nach der Oberfläche der zu bedruckenden Folienbahn und der Gravurtiefe der Walzen richtet, im Rahmen des angegebenen pH-Wertbereiches durch entsprechend größere oder kleinere Zusätze von Ammoniak oder Amin eingestellt werden.With the printing varnish according to the invention or the printing ink produced therewith, in the gravure printing process, especially in the copper rotogravure printing process, perfect adhesion to the plastic webs, in particular the polyvinyl chloride sheet or film achieved, as well as quick drying and good Abrasion resistance of the printing ink. The drying time can be adjusted by adjusting the water-alcohol ratio are influenced in the carrier liquid. Likewise, the most favorable viscosity in each case, which depends on the surface of the film web to be printed and the engraving depth of the rollers aligned, within the framework of the specified pH value range through correspondingly larger or smaller additions of ammonia or Amine can be adjusted.
Demgegenüber sind handelsübliche Dispersionsdruckfarben im Rahmen der Erfindung unbrauchbar. Auch die handelsüblichen Wasserteige können nicht im Rahmen der Erfindung erfolgreich eingesetzt werden. Haftung und Naßabriebfestigkeit der Druckfarbe werden durch die handelsüblichen Wasserteige wesentlich beeinträchtigt.In contrast, commercially available dispersion printing inks cannot be used in the context of the invention. The commercially available water doughs cannot be used successfully within the scope of the invention either. Adhesion and wet abrasion resistance of the printing ink are essential when using commercially available water doughs impaired.
Aus der FR-PS 15 39 467 ist eine Drucktinte auf Basis einer Alkohol-Wasser-Mischung bekannt, welche als Bindemittel ein carboxylgruppenhaltiges Olefinpolymer enthält. Diese Druckfarbe eignet sich jeooch nicht für die Bedruckung von Kunststoffolien im Tiefclruckverfahren. da die Trocknungszeit hierfür viol zu lange ist und außerdem die Benetzbarkeit schlecht ist und die Filme keine Festigkeit aufweisen. From FR-PS 15 39 467 a printing ink based on an alcohol-water mixture is known which contains an olefin polymer containing carboxyl groups as a binder. However, this printing ink is not suitable for printing on plastic films in the deep-printing process. because the drying time is too long for this and, moreover, the wettability is poor and the films have no strength.
Aus der DE-AS 15 19 495 ist ein Verfahren zum Färben oder Bedrucken von Kunststoffolien mit s wasserlöslichen Farbstoffen bekannt Schon aufgrund der Wasserlöslichkeit ist dieses Verfahren für die Zwecke, denen der erfmdungsgemäße Drucklack dient unbrauchbar.DE-AS 15 19 495 discloses a method for dyeing or printing plastic films with s water-soluble dyes known Already because of the water solubility this process is for the Purposes for which the printing varnish according to the invention is useless.
Aus der US-PS 32 61 787 ist eine einen Süchtigen Ätheralkohol enthaltende Druckfarbe bekannt dit zum Bedrucken von Kühlbehältern und dergleichen verwendet werden soll. Für das Tiefdruckverfahren ist sie wegen zu langer Trockenzeit ungeeignet abgesehen von der Notwendigkeit ein organisches Lösungsmittel zu verwenden, welches erfindungsgemäß ja gerade vemieden werden soll. From US-PS 32 61 787 an addict containing ether alcohol printing ink is known to be used for printing cooling containers and the like. For the gravure printing method is due to prolonged dry season unsuitable apart from the need to use an organic solvent which is to be inventively precisely vemieden.
Aus der JP-PS 49/19 691 sind filmbildende Mittel zur Beschichtung und Verwendung in Druckfarben beschrieben, die zur Trocknung mehrere Minuten auf höhere Temperatur erhitzt werden müssen. Für eine Tiefdruckanwendung scheiden sie schon aus diesem Grunde aus. JP-PS 49/19 691 describes film-forming agents for coating and use in printing inks which have to be heated to a higher temperature for several minutes in order to dry. For this reason alone, they are ruled out for use in gravure printing.
Die folgenden Beispiele erläutern die Erfindung weiter.The following examples further illustrate the invention.
Zur Herstellung einer druckfähigen Farbe für den Kupferrotationstiefdmcä von PVC-Folien werden ein Drucklack und eine Druckfarbenpräparation (Wasserteig) nachstehender Zusammensetzung verwendet:In order to produce a printable color for the copper rotation deep dmcä of PVC foils, a Printing varnish and a printing ink preparation (water dough) with the following composition are used:
i. Drucklacki. Printing varnish
25 Gew.-Teile Polyacryisäureäthylesterdispersion
2 Gew.-Teile Polymethacrylsäureäthylesterdispersion 25 parts by weight of ethyl polyacrylate dispersion
2 parts by weight of ethyl polymethacrylate dispersion
1 Teil Ammoniak1 part ammonia
bis zu 100 Gew.-Teilen mit azeotropem Gemisch von Äthanol und Wasser aufgefüllt.Made up to 100 parts by weight with azeotropic mixture of ethanol and water.
2. Druckpigmentpraparatiort2. Printing pigment preparation
45 Gew.-Teile Polyacrylsäureäthylesterdispersion
20 Gew.-Teile Wasser
32 Gew.-Teile Äthanol
3 Gew.-Teile Ammoniak
13 Gew.-Teile Pigment.45 parts by weight of polyacrylic acid ethyl ester dispersion
20 parts by weight of water
32 parts by weight of ethanol
3 parts by weight of ammonia
13 parts by weight pigment.
Die Mischung wird zuerst im Dissolver vordispergiert und anschließend in der Perlmühle abgerieben.The mixture is first pre-dispersed in the dissolver and then rubbed in the bead mill.
Mit einer Druckfarbe aus 80 bis 95 Teilen des Drucklacks 1 und 20 bis 5 Teilen der Druckpigmentpräparation 2 wird die zu bedruckende Folienbahn auf einer üblichen Druckmaschine im Rotationstiefdruckverfahren mehrfarbig bedruckt. Es werden die bei lösungsmittelhaltigen Druckfarben üblichen Druckgeschwindigkeiten und Trocknungsbedingungen erreicht. Es wird ein einwandfreier blockfreier Druck erzielt.With a printing ink composed of 80 to 95 parts of the printing varnish 1 and 20 to 5 parts of the printing pigment preparation 2 is the film web to be printed on a conventional printing machine using the rotogravure printing process multicolored printed. The printing speeds customary for solvent-based printing inks are used and drying conditions achieved. A flawless block-free print is achieved.
Bedrucken von Polyäthylenterephthalat-Folien
Es wird ein Drucklack ausPrinting on polyethylene terephthalate foils
It becomes a print varnish
30 bis 35 Gew.-Teilen Polyacrylsäureäthylesterdispersion 30 to 35 parts by weight of polyacrylic acid ethyl ester dispersion
2 bis 3 Gew.-Teilen Polymethacrylsäureäthyl-2 to 3 parts by weight of ethyl polymethacrylic
ester-dispersion
1 bis 1,5 Gew.-Teilen Ammoniak (pH über 8)ester dispersion
1 to 1.5 parts by weight ammonia (pH above 8)
mit einem azeotropen Alkohol-Wasser-Gemisch auf lOOGew.-Teile aufgefüllt.made up to 100 parts by weight with an azeotropic alcohol-water mixture.
70 bis 95 Gewichtsteile dieses Drucklacks werden mit 30 bis 5 Gew.-Teilen der Druckpigmentpräparatton von Beispiel 1 gemischt und zum Bedrucken der Polyesterbahn verwendet Die Ergebnisse entsprechen denen von Beispiel 1.70 to 95 parts by weight of this printing varnish are with 30 to 5 parts by weight of the printing pigment preparation of Example 1 mixed and used to print the polyester web. The results correspond to those of FIG Example 1.
Claims (1)