DE2457496A1 - Coating piece goods, esp. open work fabrics, with pastes - giving smooth or embossed, water, fat etc., repellant finishes - Google Patents
Coating piece goods, esp. open work fabrics, with pastes - giving smooth or embossed, water, fat etc., repellant finishesInfo
- Publication number
- DE2457496A1 DE2457496A1 DE19742457496 DE2457496A DE2457496A1 DE 2457496 A1 DE2457496 A1 DE 2457496A1 DE 19742457496 DE19742457496 DE 19742457496 DE 2457496 A DE2457496 A DE 2457496A DE 2457496 A1 DE2457496 A1 DE 2457496A1
- Authority
- DE
- Germany
- Prior art keywords
- coating
- embossed
- pastes
- coated
- esp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Verfahren zum Beschichten bahnenfdrmiger Materialien Die Erfindung betrifft ein Verfahren zum Beschichten bahnenförmiger Materialien, vorzugsweise von offenen Geweben,Gewirken oder Vliesen, mit Kunststoffpasten.Method of coating sheet materials. The invention relates to a method for coating sheet-like materials, preferably of open woven, knitted or non-woven fabrics, with plastic pastes.
Derart beschichtete Materialien werden in großen Mengen für LKW-Planen sowie für Abdeckplanen für die Bauindustrie,Landwirtschaft, für das Transport- und Lagerwesen usw.verwendet und dienen ferner als Konstruktionselement für sogenannte Traglufthallen. Leichtere Qualitäten werden für Regenbekleidung, Zeltplanen, Arbeitskleidung für Fischer, Metzger usw. verwendet.Materials coated in this way are used in large quantities for truck tarpaulins as well as for tarpaulins for the construction industry, agriculture, transport and Warehousing, etc., and also serve as a construction element for so-called Air domes. Lighter qualities are used for rainwear, tarpaulins, work clothes used for fishermen, butchers, etc.
Die Beschichtung der bahnenförmigen Materialien erfolgt bei den bekannten Verfahren überwiegend mittels Rakeln. Je nach Struktur des zu beschichtenden Materials wird entweder das Direktverfahren oder das Transfer- bzw. lndirektverfahren verwendet.The coating of the sheet-like materials takes place in the known ones Process mainly by means of doctor blades. Depending on the structure of the material to be coated either the direct method or the transfer or indirect method is used.
Im Direktverfahren wird das zu beschichtende Material einer plangeschliffenen Stahl- oder Gummiwalze zugeführt, über der ein Rakelmesser höhenverstellbar angeordnet ist,so daß ein definierter Spalt eingestellt werden kann, der die Schichtdicke der Beschichtung bestimmt. Die Beschichtungsmasse, beispielsweise PVC-Plastisol, Organosol oder andere Kunststofflösungen bzw.In the direct process, the material to be coated is ground flat Steel or rubber roller supplied, above which a doctor blade is arranged to be adjustable in height is, so that a defined gap can be set that the layer thickness of the Coating determined. The coating compound, for example PVC plastisol, organosol or other plastic solutions or
Kunststoffdispersionen, liegt dabei vor dem Rakel auf der zu beschichtenden Ware.Plastic dispersions, lies in front of the squeegee on the one to be coated Were.
Beim Transferverfahren wird die Beschichtungsmasse in der voranstehend beschriebenen Weise auf ein antiadhäsives Trägermaterial wie beispielsweise Releasepapier,Stahlband oder mit Silikonkautschuk beschichtetes Gewebe, gestrichen; erst hinter dem Rakel wird das zu beschichtende Material der audem Trägermaterial befindlichen Beschichtungsmasse zugeführt und in diese mittels einer Andrückwalze eingedrückt. Nach dem Trocknen oder Gelieren wird die nun einseitig beschichtete Ware vom TrägermaX terial, dem sogenannten Transferträger abgezogen.In the transfer method, the coating compound is in the above described manner on an anti-adhesive carrier material like for example Release paper, steel tape or fabric coated with silicone rubber, coated; Only after the doctor blade does the material to be coated become the carrier material The coating compound is supplied and fed into it by means of a pressure roller depressed. After drying or gelling, it is now coated on one side Goods removed from the carrier material, the so-called transfer carrier.
Um bahnenfdrmige Materialien doppelseitig zu beschichten, muß bei beiden bekannten Verfahren der Beschichtungsprozeß wiederholt werden. Sehr offene Materialien, wie beispielsweise Gittergewebe, können mit den beschriebenen beiden Verfahren nicht beschichtet werden, da die durch das zu beschichtende Material durchdringende Beschichtungsmasse entweder die Streichwalze oder aber die Andrückwalze verschmiet,Es bildet sich dann ein zunehmend größer werdender Pastenwulst vor der Streichwalze oder der AndrUckwalze, so daß der Beschichtungsprozeß schon nach wenigen Metern unkontrollierbar wird.In order to coat materials in the form of a railway line on both sides, at two known methods of the coating process are repeated. Very open Materials such as mesh fabric can be used with the two described Process not be coated because the penetrating through the material to be coated Coating mass either the coating roller or the pressure roller smears, It An increasingly larger bead of paste then forms in front of the doctor roller or the pressure roller, so that the coating process takes only a few meters becomes uncontrollable.
Zum Beschichten derartiger offener Materialien wird deshalb das sogenannte Tauchverfahren benutzt. Bei diesem Verfahren läuft das zu beschichtende Material um Umlenk- und Abquetschwalzen,die in einem wannenähnlichen Behälter angeordnet sind, in welchem sich auch die Beschichtungsmasse befindet. Oberhalb des Behälters sind meist noch zwei Rakelmesser angeordnet, die das überschüssige Beschichtungsmaterial, welches das Gittergewebe aus dem Behälter mitnimmt, beidseitig abstreifen. Das beschichtete Material muß dann zum Gelieren oder Trocknen auf einem Spannrahmen durch den Heizkanal geführt werden. Hierdurch wird die gesamte Anlage kompliziert und teuer. Darüber hinaus ist die verwendete Anlage nur für das Tauchverfahren zu gebrauchen. Schließlich ist die zu erzielende Materialoberfläche sehr ungleichmäßig und nur für technische Artikel akzeptabel.For coating such open materials, the so-called Dipping method used. In this process, the material to be coated runs around deflection and squeegee rollers, which are arranged in a trough-like container are in which the coating compound is also located. Above the container there are usually two doctor blades arranged to remove the excess coating material, which takes the mesh from the container, wipe off on both sides. That coated Material then has to pass through the heating channel for gelling or drying on a tenter frame be guided. This makes the entire system complicated and expensive. About that In addition, the system used can only be used for the immersion process. In the end the material surface to be achieved is very uneven and only for technical Item acceptable.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zum Beschichten bahnenförmiger Materialien mit SunststofSpasten zu schaffen,das mit geringem konstruktiven Aufwand auch die Beschichtung von offenen Geweben, Gewirken oder Vliesen gestattet.The invention is based on the object of a method for coating sheet-like materials with plastic pastes create that Also the coating of open fabrics, knitted fabrics with little construction effort or fleece permitted.
Die Lösung dieser Aufgabenstellung durch die Erfindung ist dadurch gekennzeichnet, daß das zu beschichtende Material zusammen mit der Beschichtungsmasse und einem Transferträger durch eine Streichrakel hindurchgeführt wird. Als Transferträger kann gemäß einem weiteren Merkmal der Erfindung entweder ein nach dem Trocknen oder Gelieren wieder entfernbares Material oder ein im fertigen Erzeugnis verbleibendes Material verwend&werden.The solution to this problem by the invention is thereby characterized in that the material to be coated together with the coating compound and a transfer support is passed through a doctor blade. As a transfer medium can according to a further feature of the invention either a after drying or Gelling removable material or a material remaining in the finished product Material should be used.
Das erfindungsgemäße Verfahren erlaubt die Beschichtung auch offener Materialien mit den bekannten Vorrichtungen, ohne daß irgend welche Schwierigkeiten auftreten.Indem gleichzeitig mit dem Transferträger und der Beschichtungsmasse auch das zu beschichtende bahnenförmige Material durch den Rakelspalt hindurchläuft, wird ein doppelseitig beschichtetes Material erhalten, das vodhervorragend glatter Oberflächenbeschaffenheit ist und keinen separaten Prägeprozeß benötigt. Durch Verwendung von geprägtem Releasepapier kann man zudem jede gewünschte Prägenarbe erhalten,wogegen im Tauchverfahren beschichtete Gittergewebe nicht mit einer Prägenarbe versehen werden können, da die Gitterstruktur des Gewebes bei diesem bekannten Verfahren stets sichtbar bleibt.The method according to the invention also allows the coating to be more open Materials with the known devices without any difficulties By doing this at the same time as the transfer carrier and the coating compound the web-like material to be coated runs through the doctor blade gap, a double-sided coated material is obtained, which is outstandingly smoother Surface texture is and does not require a separate embossing process. By using embossed release paper can also be used to obtain any desired embossing color, on the other hand Mesh fabric coated in the dipping process is not provided with an embossed grain can be, as the lattice structure of the fabric in this known method always remains visible.
Das erfindungsgemäße Verfahren erlaubt aber auch die Herstellung von Materialkombinationen, die mit den bekannten Applikationsmethoden nicht herstellbar sind. Beispielsweise kann auf einen Umkehrträger zunächst ein kompakter Deckstrich von o,l bis 1 mm Stärke ohne Gewebezulauf aufgestrichen und getrocknet bzw.geliert werden. Bei einem zweiten Strich wird dann eine treibmittelhaltige PVC-Paste auf den Deckstrich aufgestrichen,wobei am Rakelmesser erfindungsgemäß ein Gittergewebe aus Polyester- oder Polyamidfaser mit zuläuft. Das Gittergewebe ist somit nach dem Ausschäumen der PVC-Paste voll darin eingebettet und verleiht dem so entstanzonen Kunstleder eine hohe Stabilität und Reißfestigkeit.Sol¢he geschäumten Kunstleder finden vielfältige Anwendung für Täschner-und Polsterzwecke, Harrnonikatüren,Gürtel usw. Mit dem erfindungsgemäßen Verfahren sind sie erheblich preiswerter und mit geringerem Maschinenaufwand herzustellen als nach den bekannten Verfahren.The inventive method also allows the production of Material combinations that cannot be produced with the known application methods are. For example, a compact top coat can first be applied to a reverse carrier from 0.1 to 1 mm thick, without tissue inflow, painted on and dried or gelled will. A PVC paste containing propellant is then applied in a second line the top coat is painted on, with a mesh fabric according to the invention on the doctor blade made of polyester or polyamide fibers. The grid fabric is thus after Foaming of the PVC paste is fully embedded in it and gives it a de-punching effect Synthetic leather has high stability and tear resistance. Sol ¢ he foamed Artificial leather is used in many ways for bag-making and upholstery purposes, harness doors, belts etc. With the method according to the invention, they are considerably cheaper and with produce less machine effort than according to the known method.
Das erfindungsgemäße Verfahren besitzt den produkttechnischen Vorteil, daß synthetische Gittergewebe, beispielsweise aus Polyester oder Polyamid, schon bei einem Quadratmetergewicht von 50 Gramm dieselbe Reißfestigkeit und eine erheblich höhere Weiterreißfestigkeit erbringen können als ein Baumwollgewebe von 250 Gramm pro Quadratmeter, das üblicherweise verwendet wird.The method according to the invention has the product-technical advantage that synthetic mesh, for example made of polyester or polyamide, already With a weight per square meter of 50 grams, the same tear strength and a considerable one Can provide higher tear strength than a cotton fabric of 250 grams per square meter that is commonly used.
Darüber hinaus zeigt ein solches Gittergewebe,welches voll im PVC-Schaum eingebettet ist, keinerlei Schrumpf- oder Dehnverhalten bei Feuchtigkeitseinwirkungen,was für Harmonikatüren und Trennvorhänge sehr wichtig ist.In addition, such a mesh fabric shows, which is fully in the PVC foam is embedded, no shrinkage or expansion behavior when exposed to moisture, what is very important for accordion doors and partition curtains.
Das erfindungsgemäße Verfahren bietet also neben der ungewöhnlichen Einfachheit und Wirtschaftlichkeit die Möglichkeit, neue Produkte mit den in den Beschichtungsbetrieben vorhandenen Anlagen herzustellen.The inventive method thus offers in addition to the unusual Simplicity and economy allow new products to be created with those in the Coating companies to produce existing systems.
Auf der Zeichnung ist das erfindungsgemäße Verfahren schematisch dargestellt.The method according to the invention is shown schematically in the drawing.
Oberhalb eines Streichzylinders 1 ist ein Rakelmesser 2 in der Höhe verstellbar angeordnet,vor dem sich die Beschichtungsmasse 3 befindet. Inden Rakelspalt wird gleichzeitig von unten her ein Transferträger 4 und von oben her die zu beschichtende Materialbahn 5 eingeführt,so daß sich hinter der Rakel auf dem Transferträger 4 ein beidseitig beschichtetes Material ergibt, dessen eine Oberfläche Je nach Art des verwendeten Transferträgers 5 glatt oder genarbt ist, ohne daß die Struktur der Materialbahn 5 durchschlägt. Der Transferträger 5 mit der in der Beschichtungsmasse 3 eingebetteten Materialbahn 5 wird nunmehr durch einen Heizkanal 6 geführt, bevor der Transferträger 4 entfernt wird.Above a coating cylinder 1 is a doctor blade 2 in height arranged adjustable, in front of which the coating compound 3 is located. In the squeegee gap a transfer carrier 4 is simultaneously from below and the one to be coated from above Material web 5 introduced so that behind the doctor blade on the transfer carrier 4 results in a material coated on both sides, one surface of which, depending on the type of the transfer carrier 5 used is smooth or grained without affecting the structure the web of material 5 penetrates. The transfer carrier 5 with that in the coating compound 3 embedded web of material 5 is now passed through a heating channel 6 before the transfer support 4 is removed.
Im folgenden sollen einige Beispiele des erfindungsgemäßen Verfahrens angeführt werden: 1. Beispiel: Ein schiebefest ausgerüstetes Polyester-Gittergewebe der Einstellung 8/8, 280 dtx in Kette und Schuß wird mit einer Paste folgender Zusammensetzung beschichtet: 6o,o Teile verpastbares E-PVC 4o,o Teile Weichmacher (Dioctylphtalat) 1,o Teile Ba-Cd Stabilisator lo,o Teile CaCO3 5,o Teile Pigment (z.B. TiO2) Das Gelieren erfolgt im Heizkanal bei 1800 C in ca 9o Sekunden. Some examples of the method according to the invention are given below The following are listed: 1. Example: A non-slip polyester mesh fabric the setting 8/8, 280 dtx in warp and weft is mixed with a paste of the following composition coated: 6o, o parts pasteable E-PVC 4o, o parts plasticizer (dioctyl phthalate) 1, o parts Ba-Cd stabilizer lo, o parts CaCO3 5, o parts pigment (e.g. TiO2) Das Gelling takes place in the heating channel at 1800 C in about 90 seconds.
Nach dem Abkühlen und Abziehen vom Transferträger liegt ein Material vor, das für Regenbekleidung,Arbeitskleidung,Zeltstoff, Abdeckplanen usw.verwendC werden kann. Bei Austausch des Weichmadners DOP durch polymeren Adipinsäureester entsteht ein fettresistentes Material, das bevorzugt für Metzgerschürzen und Fischereibe-Meidung eingesetzt wird. Das Quadratmetergewicht soll zweckmäßig zwischen 400 und 700 g liegen. After cooling and peeling off from the transfer carrier, a material lies used for rainwear, workwear, tent fabric, tarpaulin, etc. C. can be. When replacing soft men’s DOP with polymeric adipic acid ester the result is a grease-resistant material, which is preferred for butcher's aprons and avoidance of fishing is used. The square meter weight should expediently be between 400 and 700 g lie.
2. Beispiel: Ein schiebefest ausgerüstetes Polyester- oder Polyamid-Gittergewebe ir Einstellung 5/5, 11ovo dtx in Kette und Schuß wird mit einer Paste folgender Zusammensetzung beschichtet: 6o,o Teile verpastbares E-PVC lo,o Teile Chlorparaffin 50 30,0 Teile DOP 1,o Teile Stabilisator 3,0 Teile So20) lo,o Teile CaCO3 5,0 Teile Pigment Bei einer Rakelspalteinstellung von o,8 bis 1,2 mm erhält man ein Quadratmetergewicht von 700 bis 11ovo g. Das so erhaltene flammwidri- -ge Kunstleder wird zu Planen,Traglufthallen,Wetterlutten usw. 2nd example: A non-slip polyester or polyamide mesh fabric ir setting 5/5, 11ovo dtx in warp and weft is followed with a paste Composition coated: 6o, o parts pasteable E-PVC 10, o parts chlorinated paraffin 50 30.0 parts of DOP 1, o parts of stabilizer 3.0 parts of So20) lo, o parts of CaCO3 5.0 parts Pigment With a doctor blade gap setting of 0.8 to 1.2 mm, a square meter weight is obtained from 700 to 11ovo g. The flame-retardant synthetic leather obtained in this way becomes tarpaulins, air dwellings, weather flutes etc.
verarbeitet.processed.
3. Beispiel: Eine PVC-Paste wie im Beispiel 1 wird in einer Schichtdicke von vorzugsweise 0,2 bis 0,7 mm auf genarbtes oder glattes Releasepapier aufgetragen und im Heizkanal geliert. Der gelierte Film verbleibt auf dem Papier und wird einem zweiten Rakel zugeführt. Hier wird eine treibmittelhaltige PVC-Paste nachstehender Rezeptur in einer Schichtdicke von vorzugsweise o,4 bis 1 mm aufgetragen,während gleichzeitig ein Polyester-Gittergewebe der Einstellung 5/6, 550 dtx in Kettrichtung und 280 dtx in Schußrichtung durch den Rakelspalt mit einläuft. Im Heizkanal wird 0 dann bei logo0 C dieser zweite Pastenauftrag ausgeliert und zugleich aufgeschäumt,wobei die treibmittelhaltige Paste auf das Doppelte bis Dreifache der aufgetragenen Schichtdicke expandiert.3rd example: A PVC paste as in example 1 is applied in one layer from preferably 0.2 to 0.7 mm applied to grained or smooth release paper and gelled in the heating channel. The gelled film remains on the paper and becomes a second doctor blade fed. Here, a PVC paste containing blowing agent is described below Recipe applied in a layer thickness of preferably 0.4 to 1 mm while at the same time a polyester mesh fabric of the setting 5/6, 550 dtx in the warp direction and 280 dtx enters through the doctor gap in the weft direction. In the heating channel 0 then at logo0 C this second paste application gelled and foamed at the same time, whereby double to triple the applied layer thickness of the paste containing blowing agent expands.
Die PVC-Paste besitzt hierbei folgende Zusammensetzung: 55,o Teile verpastbares E-PVC 35,o Teile Dioctylphtalat lo,o Teile Benzyl-Butylphtalat 2,0 Teile Azodicarbonamid 1,5 Teile ZnO aktiv lo,o Teile CaCO5 3,o Teile Pigment.The PVC paste has the following composition: 55.00 parts Pastable E-PVC 35, o parts dioctyl phthalate 10, o parts benzyl butyl phthalate 2.0 Parts of azodicarbonamide 1.5 parts of ZnO active lo, o parts of CaCO5 3, o parts of pigment.
4. Beispiel: Man verfährt in derselben Weise wie in Beispiel 3, jedoch wird hinter dem zweiten Rakel, d.h. wenn der Deckstrich, die Schaumpaste und das Gittergewebe schon auf dem Transferträger liegen, noch ein Faservlies aufgelegt und mittels Andrückwalze leicht in die aufgeschäumte Paste eingedrückt.4. Example: Proceed in the same way as in Example 3, however is behind the second squeegee, i.e. when the top coat, the foam paste and the The mesh fabric is already on the transfer carrier, a fiber fleece is still in place and lightly pressed into the foamed paste using a pressure roller.
Claims (3)