DE2353898C2 - Process for the manufacture of wear-exposed bodies and applications thereof - Google Patents

Process for the manufacture of wear-exposed bodies and applications thereof

Info

Publication number
DE2353898C2
DE2353898C2 DE19732353898 DE2353898A DE2353898C2 DE 2353898 C2 DE2353898 C2 DE 2353898C2 DE 19732353898 DE19732353898 DE 19732353898 DE 2353898 A DE2353898 A DE 2353898A DE 2353898 C2 DE2353898 C2 DE 2353898C2
Authority
DE
Germany
Prior art keywords
hard metal
base body
wear
metal scrap
scrap pieces
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19732353898
Other languages
German (de)
Other versions
DE2353898B1 (en
Inventor
Hans Dr.-Ing. Habil. 7000 Stuttgart Wahl
Wolfgang Dr.-Ing. 7302 Nellingen Wahl
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Verschleiss-Technik Dr-Ing Hans Wahl 7304 Ruit
Original Assignee
Verschleiss-Technik Dr-Ing Hans Wahl 7304 Ruit
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to DE2365747A priority Critical patent/DE2365747C3/en
Application filed by Verschleiss-Technik Dr-Ing Hans Wahl 7304 Ruit filed Critical Verschleiss-Technik Dr-Ing Hans Wahl 7304 Ruit
Priority to DE19732353898 priority patent/DE2353898C2/en
Priority to CH932774A priority patent/CH582574A5/xx
Priority to AT574874A priority patent/AT336818B/en
Publication of DE2353898B1 publication Critical patent/DE2353898B1/en
Priority to FR7424317A priority patent/FR2236953B1/fr
Priority to GB3122674A priority patent/GB1480057A/en
Application granted granted Critical
Publication of DE2353898C2 publication Critical patent/DE2353898C2/en
Expired legal-status Critical Current

Description

Man hat bereits vorgeschlager», die verschleißbeanspruchte Oberfläche metallischer Grandköfper, z. B. Schneidwerkzeuge, mit neuem, d. h. unbenutztem Hartmetall zu panzern. Dies ist aber für größere Grundkörper und entsprechend große VerschleifSfjächen ein sehr teures ,Verfahren, weil der Preis von Hartmetall sehr hoch liegt; I kg Hartmetall kostet rund das HundertfaOne already has suggestions », which is subject to wear and tear Surface of metallic grand bodies, e.g. B. Cutting tools, with new, d. H. unused carbide to armor. However, this is very important for larger base bodies and correspondingly large abrasive surfaces expensive process because the price of hard metal is very high; I kg of hard metal costs around a hundred

che von t kg verschleißfestem Hartguß.surface of t kg of wear-resistant chilled cast iron.

Wegen des sehr hohen spezifischen Gewichtes von Hartmetall bedarf es pudern eines sehr höhen Hartmetall-Gewichte* ui. ■« eine besti-nmte Räche zu panzern; die Panzerung kostet also rund das Hundertfache des G-undkörpers. Solche extrem hoh_n Panzerungskosten sind nur in seltenen Fällen, bei kleineren Grundkörpern und höchster Anforderung aa die Lebensdauer tragbar, nicht aber für die große Masse normaler Verschleißtei-Due to the very high specific weight of hard metal, powdering requires a very high hard metal weight * ui. ■ «to armor a certain vengeance; the armor costs around a hundred times as much G-and-body. Such extremely high armoring costs are only in rare cases, with smaller base bodies and the highest requirements aa the life expectancy, but not for the large mass of normal wear parts

Ie, wie sie z. B. in den Industrien der Steine um." Erden, bei der HartzerkJein^rung, beim Mischen und Fördern usw. vielfach benötigt werden. Hier fehlte bisher eine Lösung, welche die außergewöhnliche Verschleißfestigkeit von Hartmetall mit niedrigen Gestehungskosten 'erbindet.Ie, as they z. B. in the stone industries. "Earth, in hard grinding, in mixing and conveying etc. are often needed. Up until now, there was no solution that would provide exceptional wear resistance of hard metal with low production costs'.

Die vorliegende Erfindung löst dieses Problem, indem sie ein Verfahren zur Herstellung verschleißbeanspruchter metallischer Körper vorschlägt, wobei deren Verschleißzonen mit Hartmetall-Schroit-Stückchtn mit einer auf die Verschleißzone projizierten Größe zwischen etwa 0.1 und etwa 10 cm3. vorzugsweise zwischen etwa O^ und et va 5 cm2 gepanzert werden.The present invention solves this problem by proposing a method for the production of metallic bodies which are subject to wear and tear, the wear zones of which are provided with hard metal-Schroit-Stückchtn with a size projected onto the wear zone between about 0.1 and about 10 cm 3 . armor should preferably be between about O ^ and about 5 cm 2.

Insbesondere bezieht sich die vorliegende Erfindung auf ein Verfahren, bei dem d> <; Verschleißzonen mit abgenutzten prismatischen Hartmetall-Wendeschneidplättchen gepanzert werden.In particular, the present invention relates to a method in which d> <; Wear zones with worn prismatic carbide indexable inserts be armored.

Hartmetall Schrott md Hartmetall-Wende-Schneidplättchen fa.,en bei d-;r Fabrikation bzw. bei der Verwendung von Hartmetall in sehr großen Mengen an; sie werden teils weggeworfen, teils wieder verkleinert zur Verwendung als Ausgangsstoffe für neue Fabrikation. Die Preise solchen Hartmetall-Schrottes bzw. abgenützte· Wendeschneidplättchea liegen bei '/50 und darunter der neuen Hartmetallteile.Carbide scrap md carbide reversible cutting tips fa., en at d-; r manufacture or use of carbide in very large quantities; some are thrown away, some are reduced in size again for use as raw materials for new fabrication. The prices of such hard metal scrap or worn Indexable insert sizes are 1/50 and below the new carbide parts.

Es wurde weiterhin gefunden, daß die leuchten Abnutzungsspuren, die z. B. an abgenutzten Wendeschneidplatten festzustellen sind, deren Verwendung als Verschleißpanzerung praktisch üb .»rhaupt nicht be einträchtigen.It was also found that the glowing signs of wear, the z. B. on worn indexable inserts, their use as wear armor practically over. »not at all amalgamate.

Die vorliegende Erfindung ist im feigenden beispielsweise beschrieben und dargestellt, es zeigtThe present invention is described and illustrated in the figurative example, it shows

A b b. 1 eine gepanzerte Platte mit zweiseitiger Abstützung der Hartmelallnlätichen.
A b b. 2 eine Platte mit dreiseitiger Absiützung der Hartmetallplättchen,A b b. 1 an armored plate with two-sided support of the hard metal sheets.
A b b. 2 a plate with three-sided support for the hard metal plate,

A b b. 3 den schematischen Schnitt durch eine Mischerschaufel mit senkrechter, gepanzerter Anstellung. In Abb.) ist 1 ein Grundkörper mit einer Ausnehmung 2,3,4. 5.6. 7. 2. weiche beidseitig (2,3.4 und 5.6.A b b. 3 shows the schematic section through a mixer blade with a vertical, armored adjustment. In Fig.) 1 is a base body with a recess 2, 3, 4. 5. 6. 7. 2. soft on both sides (2, 3, 4 and 5, 6.

7) frei ausläuft, so daß die Flächen 3.4. 5,6 und 2. 3,6,7 fortlaufend geschliffen oder sonstwie bearbeitet wer den können.7) runs out freely so that the surfaces 3.4. 5.6 and 2. 3,6.7 continuously ground or otherwise processed.

in der genannten Ausnehmung sind abgenutzte Wendescnneidpiattchen 8. 9. 10. Il durch Löten. Kleben oder Klemmen mit geringem Abstand voneinander bzw. in enger Berührung miteinander befestigt. Mit 12. 13, 14 sind einige Abnutzungsspuren an den Wende- scnue'tdpiaiicuuü bsz&chfici. Dia en Wemfcschneädplänchen liegen mit einer groujeren ebenen, FlM-In the recess mentioned are worn reversible cutting blades 8. 9. 10. Il by soldering. Gluing or clamping fixed with a small distance from each other or in close contact with each other. With 12. 13, 14 there are some signs of wear on the reversible scnue'tdpiaiicuuü bsz & chfici. The little Wemfcschneädplänchen lie with a larger, flat, flM-

60- cHe auf dem Grundkörper auf, wobei die beiderseitigen Aüflageflächen zweckmäßig bearbeitet werden. Die Auflagefläche itn Grundkörper bildet eine Ebene; eventuell gönnen auch mehrere AuflagsfUchsn in parallelen Ebenen vorgesenen werden. Beide Anordnungen ge-60-cHe on the base body, whereby the support surfaces on both sides are expediently processed. The support surface with the base body forms a plane; if necessary, several support foxes can be provided in parallel planes. Both arrangements

statten leichtes Löten, weif das flüssige Lot πίςΐιί so leicht wegfließtequip easy soldering, the liquid solder knows πίςΐιί so easily flows away

Die Zwischenfugen zwischen den einzelnen Hartmetallplättchen sind auf dem Grundkörper % so angeord-The joints between the individual hard metal plates are arranged on the base body %

net, daß sie winkelig zur Bewegungsrichtung 15,16 des Gegenkörpers bzw. Gegenstoffes über der Verschleißzone stehen. Dadurch wird einer stärkeren Auswaschuf·? der Fugen im Betrieb vorgebeugtnet that it is angled to the direction of movement 15,16 des Counter body or counter material are above the wear zone. This creates a stronger washout ·? the joints in operation prevented

D Hartmetallplättchen sind im vorliegenden Falle dun die beiden Flächen 2,3,6.7 und 3,4,5,6 umgeben und abgestützt.In the present case, the two surfaces 2, 3, 6, 7 and 3, 4, 5, 6 are surrounded by hard metal plates and supported.

In Anwendung auf Mischerschaufeln, Abstreifer u. dgl. bilden die Kanten 17,18,19, 20 eine beinahe geschlossene Außenkante oder Abstreifkante 21,22.When used on mixer blades, scrapers and the like, the edges 17, 18, 19, 20 form an almost closed one Outer edge or scraper edge 21,22.

Die Wendeschneidplättchen sind im Grundkörper 1 so vertieft angeordnet, daß inre nF^h oben weisenden Oberflächen rr.it der anschließenden FIa-1Ie des Grundkörpers fluchten; dadurch wiH z- B. c·" angestörter Abfluß des über die gepanzerte YerseMdBzone strömenden Gegenkörpers (z. 3. Viischgutes) gewährleistet.The indexable cutting plates are arranged in the base body 1 so absorbed that inre nF ^ h above rr.it the subsequent FIA 1 Ie of the base body are aligned facing surfaces; characterized wih z · B. c "is störter outflow of the air flowing over the armored YerseMdBzone counter body (eg. 3rd Viischgutes) is ensured.

In A b b. 2 ist eine analogt lösung dargestellt, bei der die abgenumen Fjrtmerail-Wendeschneidpläuchen nunmehr von 3 Sehe" vom Grundkörper abgestützt und gehalten sind. Dies wird erreicht durch An- «o ordnuny eines Steges 23,24,25,26.In A b b. 2 an analog solution is shown at of the abgenumen Fjrtmerail indexable cutting tubes are now supported and held by the base body from 3 sides. This is achieved by means of attachment Orduny of a web 23,24,25,26.

Durch diese Anordnung wird erreicht, daß sich die Plättchen beim Löten kaum verschieben können und daß das flüssige Lot nicht so leicht wegläuft Der Sieg 23, 24, 25, 26 kann nach dem Löten eventuell wieder mechanisch entfernt oder durch anfänglichen Verschleiß abgetragen weiden, so daß die Hartmetallpanzerung zum Tragen kommt.This arrangement ensures that the platelets can hardly move during soldering and that the liquid solder does not run away so easily The victory 23, 24, 25, 26 can possibly be removed again mechanically after soldering or due to initial wear grazed so that the hard metal armoring comes into play.

An A b b. 3 ist schematisch eine fwischerschaufe» 27 dargestellt, die über einer Bodenfläche 28, 29 umläuft und an ihrem bodennahen Teil eine sogenannte senkrechte Anstellung 30 trägt, an deren in Bewegungsrichtung vorderer Stirnfläche abgenutzte Hartmetall-Wendeschneidplättchen 31 z. B. durch Löten befestigt sind, deren untere Vorderkante 32 als Bodenstreifkante dient und den Verschleiß der Schaufel entscheidend herabsetztAt A b b. 3 is a schematic of a wiper blade »27 shown, which revolves over a floor surface 28, 29 and on its part close to the ground a so-called vertical adjustment 30 carries, on its in the direction of movement Worn hard metal indexable inserts on the front face 31 z. B. are attached by soldering, the lower front edge 32 of which serves as a ground scraping edge and is decisive for the wear and tear of the shovel degrades

Die Grundkörper 1 bzw. 27 werden zweckmäßig aus Hartguß hergestellt, wei! die Verwendung von Hartmetall an den Häuptversehleißzpnen unter Verwendung von Hartguß an den Nebenverschleißzoneh eine besonders haltbare Kombination erg^ü.The base body 1 and 27 are expediently made of chilled cast iron, white! the use of hard metal on the main wear zips using of chilled cast iron to the secondary wear zones is a special one durable combination erg ^ ü.

Hierzu 1 Blatt Zeichnungen1 sheet of drawings

Claims (10)

2 353 89B ·*■ Patentansprüche2 353 89B · * ■ Claims 1. Verfahren zur Herstellung verschlei3faean- $pruchter. metallischer Körner, dadurch gelee nnzeichnet, daß derei. Verschleiuzonen mit HartmetaU-Schrott-Stücken m;i einer auf die VerichleiBzone projizierien Größe zwischen etwa 0,1 und etwa 10 cm2. vorzugsweise zwischen etwa 0,5 und etwa 5 cm2 gepanzert werden.1. Process for making wear and tear pads. metallic grains, marked by the fact that they are jelly. Wear zones with hard metal scrap pieces m ; A size projected onto the comparison zone between about 0.1 and about 10 cm 2 . preferably between about 0.5 and about 5 cm 2 are armored. 2. Verfahren nach Anspruch t, dadurch gekennzeichnet, daß.die Verschleißzonen mit c ^genutzten, prismatischen fiai-fmetall-Wejidescnneidplättchen gepanzert werden.2. The method according to claim t, characterized in that that the wear zones with c ^ used, prismatic fiai-fmetallic cutting tips be armored. 3. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die Hartmetall-Schrott-Stücke in entsprechenden Ausnehmungen im Grundkörper in an steh bekannter Weise durch Löten, Kleben oder Klemmen befestigt werden.3. The method according to claim 1 and 2, characterized in that the hard metal scrap pieces in corresponding recesses in the base body in a known manner by soldering, gluing or Clamps are attached. 4. Verfahren nach Anspruch 1 und 2, dadurch gf kennzeichnet, dj I die Hartinetall-Schrott-Stüt
auf dem Grundkörper mit geringem Abstand voneinander bzw. in enger Berührung miteinander angeordnet werden.4. The method according to claim 1 and 2, characterized gf indicates, dj I the hard metal scrap Stüt
be arranged on the base body at a small distance from one another or in close contact with one another. 5. Verfanren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die Hartmetall-Schrott-Stücke mit einer ebenen Fläche auf dem Grundkörper liegend angeordnet werden.5. Verfanren according to claim 1 and 2, characterized in that that the hard metal scrap pieces lie with a flat surface on the base body to be ordered. 6. Verfahren nach Anspruch 1, 2 und 5, dadurch gekennzeichnet daß die Auflageflächen auf dem Grundkörper in einer Ebene bzw. in parallelen Ebenen angeordnet werden.6. The method according to claim 1, 2 and 5, characterized in that the bearing surfaces on the Base body can be arranged in one plane or in parallel planes. 7. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die Auflage· lärmen auf dem Grundkörper frei auslaufend gestaltet werden.7. The method according to claim 1 and 2, characterized in that that the pad · make noise on the Base body can be designed freely tapering. 8. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß sowohl die Aufijgefiächen auf8. The method according to claim 1 and 2, characterized in that that both the surface area dem Grundkörper. als auch die Auflageflächen an den Hartmetall-Schrott-Stücken bearbeitet werden.the main body. as well as the bearing surfaces on the hard metal scrap pieces are processed. 9. Verfahren nacb„Ansprucn 1 und 2, dadurch gekennzeichnet, daIi die Hartmetall-Schrott-Stücke so auf dem Grur.dkörper angeordnet werden, daß die Zwischenfugen winkelig zu- Bewegungsrichtung des Gegenkörpers (Gegenstoffes) über der Verschleißzone stehen.9. The method according to "Claims 1 and 2, characterized in that that the hard metal scrap pieces are arranged on the body in such a way that the Intermediate joints at an angle to the direction of movement of the counter body (counter material) over the wear zone stand. 10. Verfahren nach Anspruch 2, dadurch gekennzeichnet daß die abgenutzten Wendeschneidplättchen auf mindestens 2 Seiten von dem Grundkörper umgeben werde.ι10. The method according to claim 2, characterized that the worn indexable cutting tips on at least 2 sides of the base body be surrounded.ι Π. Anwendung des Verfahrens nach Anspruch 1 und 2 auf etwa plattenförmige, mehreckige, vorzugsweise aus Hartguß besiehende Körper, insbesondeie Abstreifer, Mischerschaufeln u. dgl, dadurch gekennzeichnet, äaö aui der Arbeitsfläche entlang mindestens einer Außenkante (Streiienk > ite) Hartmeiillplättchen nebeneinander angeordnet sind.Π. Application of the method according to claims 1 and 2 to approximately plate-shaped, polygonal bodies, preferably made of chilled cast iron, in particular scrapers, mixer blades and the like, characterized in that hard- chipping plates are arranged next to one another along at least one outer edge (stripes) of the work surface.
DE19732353898 1973-07-13 1973-10-27 Process for the manufacture of wear-exposed bodies and applications thereof Expired DE2353898C2 (en)