DE2153809A1 - Process for the anti-corrosion treatment of z. B. body parts - Google Patents

Process for the anti-corrosion treatment of z. B. body parts

Info

Publication number
DE2153809A1
DE2153809A1 DE19712153809 DE2153809A DE2153809A1 DE 2153809 A1 DE2153809 A1 DE 2153809A1 DE 19712153809 DE19712153809 DE 19712153809 DE 2153809 A DE2153809 A DE 2153809A DE 2153809 A1 DE2153809 A1 DE 2153809A1
Authority
DE
Germany
Prior art keywords
steel part
phosphate
zinc
powder coating
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19712153809
Other languages
German (de)
Inventor
Mervyn John Lytham-St-Annes Lancashire Hannam (Großbritannien)
Original Assignee
British Leyland Track and Bus Division^Ltd., Leyland, Lancashire (Großbritannien)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by British Leyland Track and Bus Division^Ltd., Leyland, Lancashire (Großbritannien) filed Critical British Leyland Track and Bus Division^Ltd., Leyland, Lancashire (Großbritannien)
Publication of DE2153809A1 publication Critical patent/DE2153809A1/en
Pending legal-status Critical Current

Description

PATENTANWÄLTEPATENT LAWYERS DIPL.-ING. DR. IUR. DIPL.-ΙΝβ.DIPL.-ING. DR. IUR. DIPL.-ΙΝβ. VOLKER BUSSE DIETRICH BUSSEVOLKER BUSSE DIETRICH BUSSE

45 Osnabrück , den 27. Oktober 197145 Osnabrück, October 27, 1971

MOSERSTRASSE 2Ο/24 VB /PiMOSERSTRASSE 2Ο / 24 VB / Pi BRITISH LEYLAND TRUCK AND BUS DIVISION LIMITEDBRITISH LEYLAND TRUCK AND BUS DIVISION LIMITED

Leyland. Lancashire. EnglandLeyland. Lancashire. England

Verfahren zur Korrosionsschutzbehandlung von z. B. KarosserieteilenProcess for the anti-corrosion treatment of z. B. body parts

Die Erfindung bezieht sich auf ein Verfahren zur Korrosionsbzw. Rostschutzbehandlung und betrifft insbesondere die Behandlung von beim Bau von Kraftfahrzeugkarosserien verwendeten Pertigungsteilen aus Stahl. Die nachstehend benutzte Bezeichnung "Stahlteil" erstreckt sich auf jede Art von aus Stahl bestehenden Einheiten, Einzelteilen, Platten oder sonstigen Fabrikationsteilen.The invention relates to a method for Korrosionsbzw. Anti-rust treatment and specifically relates to treatment of manufactured steel parts used in the construction of motor vehicle bodies. The one used below The term "steel part" extends to any type of units, individual parts, plates or made of steel other manufacturing parts.

Das erfindungsgemäße Verfahren zur Korrosionsschutzbehandlung ist gekennzeichnet durch folgende Schritte:The method according to the invention for anti-corrosion treatment is characterized by the following steps:

a) Galvanisieren eines Stahlteils zum überziehen mit einer Zinkschicht;a) Electroplating a steel part to be coated with a Zinc layer;

b) Behandeln des verzinkten Stahlteils mit einer Phosphatlösung zur Schaffung einer Zink/Phosphat-Schicht auf dem Zinküberzug; undb) Treating the galvanized steel part with a phosphate solution to create a zinc / phosphate layer the zinc coating; and

c) Aufbringen eines Pulverüberzuges auf der Zink/Phosphat-Schicht. c) Applying a powder coating to the zinc / phosphate layer.

209820/0925209820/0925

Nach einem ersten Merkmal der Erfindung kann der Stahlteil entweder durch Feuer- oder durch Elektrogalvanisierung verzinkt werden.According to a first feature of the invention, the steel part can either be galvanized by hot or electrogalvanizing.

Nach einem weiteren Merkmal der Erfindung erfolgt die erwähnte Phosphatbehandlung in einer Phosphatierungsanlage, die aus einem ersten Wasserspülbad, einem zweiten Wasserspülbad, einem Zink/ Phosphat-Behandlungsbad, einem dritten Wasserspülbad, einem Chromatspülbad und schließlich einem Trockenofen besteht.According to a further feature of the invention, the above-mentioned phosphate treatment takes place in a phosphating plant, which consists of a first water rinsing bath, a second water rinsing bath, a zinc / phosphate treatment bath, a third water rinsing bath, a Chromate rinsing bath and finally a drying oven.

Vorzugsweise besteht der Pulverüberzug aus einer Epoxypulverschicht, die bei 150 bis 2000C eingebrannt wird. Der Pulverüberzuj; kann aus einem Epoxyharz, einem Acrylharz oder einem Alkydharz bestehen.Preferably, the powder coating consists of a Epoxypulverschicht, which is baked at 150 to 200 0 C. The powder coating; can be made of an epoxy resin, an acrylic resin or an alkyd resin.

Vorteilhaft wird der Pulverüberzug elektrostatisch aufgebracht; es ist ebenso möglich, den Pulverüberzug durch überführen des Pulvers in ein fluidisiertes Bett und Einbringen des Stahlteils in das Bett aufzubringen.The powder coating is advantageously applied electrostatically; it is also possible to transfer the powder coating by the Apply powder to a fluidized bed and insert the steel part into the bed.

Erfindungsgemäß hat die Phosphatschicht eine Stärke von wenigerAccording to the invention, the phosphate layer has a thickness of less

2 22 2

als 150 mg/9,3 dm , vorzugsweise von weniger als 100 mg/9,3 dm Nach der Erfindung kann ein Unterschutz auf den Pulverüberzug aufgebracht werden. Auf den Unterschutz kann eine Öl/Harz-Mischuni; aufgetragen werden.than 150 mg / 9.3 dm, preferably less than 100 mg / 9.3 dm According to the invention, an underprotection can be applied to the powder coating be applied. An oil / resin mixture can be placed on the underguard; be applied.

Nach einem weiteren Merkmal der Erfindung kann ein verzinkter Teil zu Transport- und Lagerzwecken mit einem Schutzüberzug ausAccording to a further feature of the invention, a galvanized part can be made of a protective coating for transport and storage purposes

209820/092S209820 / 092S

einer Harz- oder Lanolinmischung behandelt werden, die vor der erwähnten Phosphatbehandlung entfernt wird. Dabei wird der Stahlteil nach Entfernen des Schutzüberzugs in einem Entfetter mit Trichloräthylendampf entfettet.a resin or lanolin mixture, which is removed before the mentioned phosphate treatment. The After removing the protective coating, the steel part is degreased in a degreaser with trichlorethylene vapor.

Weitere Merkmale und Vorteile der Erfindung ergeben sich aus der nachfolgenden Beschreibung eines Ausführungsbeispieles des Gegenstandes der Erfindung in Verbindung mit der Zeichnung, deren einzige Figur eine schematische Darstellung eines erfindungsgemäßen Verfahrens zeigt:Further features and advantages of the invention emerge from the following description of an exemplary embodiment of the The subject of the invention in connection with the drawing, the single figure of which is a schematic representation of an inventive Procedure shows:

Die Erfindung ist zum Behandeln von Stahl-Untereinheiten und Nieten entwickelt worden, die zum Bau selbsttragender Karosserien für als öffentliche Verkehrsmittel dienende Fahrzeuge, z.B.The invention has been developed for treating steel subassemblies and rivets used in the construction of self-supporting bodies for vehicles used as public transport, e.g.

für Autobusse der in den Patenten ... (Patentanmeldungen P 21 13 433.8 und P 21 kl 489.1) beschriebenen Art, Verwendung finden.for buses of the type described in the patents ... (patent applications P 21 13 433.8 and P 21 kl 489.1).

Es hat sich gezeigt, daß ein erheblicher Anteil der bei als öffentliche Verkehrsmittel dienenden Fahrzeugen auftretenden Korrosion auf Reibkorrosion bzw. Passungsrost zurückzuführen ist, und es sind umfangreiche Versuche zum Ermitteln des einfachsten Weges zur Überwindung dieses Problems angestellt worden.It has been shown that a significant proportion of the vehicles used as public transport vehicles occur Corrosion is due to fretting corrosion or fretting corrosion, and extensive attempts have been made to determine the simplest Way to overcome this problem has been employed.

Dabei hat sich herausgestellt, daß die oben beschriebene Behandlung zum Korrosionsschutz erfolgreicher ist als andere bereits früher vorgeschlagene Versuche, Karosserien -von als öffentliche Verkehrsmittel dienenden Fahrzeugen an genieteten und punktge-It was found that the treatment described above for corrosion protection is more successful than other previously proposed attempts to car bodies -of than public Vehicles used for transport on riveted and punctiform

209820/0925209820/0925

schweißten Verbindungen gegen Korrosion und insbesondere gegen Reibkorrosion bzw. Passungsrost zu schützen.to protect welded connections against corrosion and especially against fretting corrosion or fretting corrosion.

Beim Bau der Karosserien von als öffentliche Verkehrsmittel dienenden Fahrzeugen können die gefertigten Untereinheiten aus zuvor im Stahlwerk feuerverzinktem Stahlblech hergestellt werden. Es ist ebenso möglich, die gefertigten Untereinheiten aus Stahlblech herzustellen, das zuvor im Stahlwerk elektroverzinkt worden ist. Eine andere Möglichkeit besteht.darin, die Untereinheiten aus rohem Stahlblech herzustellen und dann die komplette Untereinheit einer Feuer- oder Elektroverzinkung zu unterwerfen. Der Verzinkungsvorgang ist in der Zeichnung bei 1 dargestellt. Angenommen, die Untereinheiten werden an einem Ort hergestellt und anschließend zu einem zweiten überführt, an dem die komplette Karosserie herzustellen ist, so wird Jede Einheit vor demWhen building the bodies of those used as public transport Vehicles, the manufactured sub-units can be made from sheet steel that has been hot-dip galvanized in the steelworks. It It is also possible to manufacture the manufactured sub-units from sheet steel that has previously been electro-galvanized in the steelworks is. Another possibility is to manufacture the sub-units from raw sheet steel and then the complete sub-unit to be subjected to hot or electro galvanizing. The galvanizing process is shown at 1 in the drawing. Accepted, the sub-units are manufactured in one place and then transferred to a second where the complete Body is to be manufactured, so each unit will be before the

zumto the

Transport/und der Lagerung am zweiten Ort mit einem provisorischen Schutzüberzug aus einer Harz- oder Lanolinmischung behandelt. Soll die Untereinheit ^ in die Karosserie eingesetzt werden so wird sie zunächst von dem provisorischen Schutzüberzug befreit und anschließend in einem Entfettungs-Tank 5 mit Trichloräthylendampf entfettet. Die Untereinheit 4 wird von einem Schlitten 3 getragen, der:sie in den Tank 5 eintauchen und aus diesem hochziehen kann. Der Schlitten ist entlang einer Hochschiene 2 bewegbar. Transport / and storage at the second location treated with a temporary protective coating made of a resin or lanolin mixture. If the subunit ^ are inserted into the body so it is first freed from the temporary protective coating and then degreased in a degreasing tank 5 with Trichloräthylendampf. The sub-unit 4 is carried by a slide 3 which: can dip it into the tank 5 and pull it up from it. The slide can be moved along a high rail 2.

Nachdem die verzinkte Untereinheit ^ zwei Wasserspültanks 6 und 7 durchlaufen hat, wird sie in einem Phosphattank 8 einer Phosphatbehandlung unterworfen. Die mit Phosphat behandelte Untereinheit 1JAfter the galvanized subunit ^ has passed through two water rinsing tanks 6 and 7, it is subjected to a phosphate treatment in a phosphate tank 8. The phosphate treated subunit 1 J

2098 2 0/09252098 2 0/0925

wird alsdann in einen dritten Wasserspültank 9 und einen Chromat spültank 10 eingetaucht, von wo sie zu einem Trockenofen 11 läuft. Der mit Phosphat behandelte Teil wird dann erhitzt und in einer Spritzkabine 12 od. dgl. mittels elektrostatischer Spritzpistolen mit einem Epoxypulver überzogen. Aufgrund der Phosphatbehandlung ergibt sich ein kristallartiger Zink/Phosphat-überzug auf der Zinkschicht, der bei einem Gewicht von weniger alsis then immersed in a third water rinse tank 9 and a chromate rinse tank 10, from where it goes to a drying oven 11 runs. The part treated with phosphate is then heated and placed in a spray booth 12 or the like by means of electrostatic spray guns coated with an epoxy powder. The phosphate treatment results in a crystalline zinc / phosphate coating on the zinc layer, weighing less than

2
100 mg/9,3 dm relativ dünn ist.2
100 mg / 9.3 dm is relatively thin.

Nach dem Aufbringen der Pulverschicht durchläuft die Untereinheit 4 eine Kabine 13 zum Aufschmelzen des Epoxyharzes auf die Untereinheit. Auf diejenigen Untereinheiten, die Teil der Bodenkonstruktion der Pahrzeugkärosserie bilden, wird alsdann ein herkömmlicher Unterschutz aufgebracht. Diejenigen Untereinheiten die Kastenprofile umfassen, werden außerdem mit einer Öl/Harz-Mischung gespritzt.After the powder layer has been applied, the sub-unit 4 passes through a booth 13 for melting the epoxy resin onto the Subunit. The sub-units that form part of the floor structure of the vehicle body are then dealt with conventional underguard applied. Those subunits which include box sections are also coated with an oil / resin mixture injected.

Niete zum Zusammenhalten der verschiedenen Teile der Fahrzeugkarosserie werden in gleicher Welse behandelt wie die Stahlteile um Reibkorrosion bzw. Passungsrost zu vermeiden. Insbesondere werden die Niete mit einem Pulverüberzug versehen.Rivets used to hold the various parts of the vehicle body together are treated in the same way as the steel parts in order to avoid fretting corrosion or fretting corrosion. In particular the rivets are provided with a powder coating.

209820/0925209820/0925

Claims (1)

Patentansprüche:Patent claims: Verfahren zur Korrosionsschutzbehandlung, gekennzeichnet
durch folgende Schritte:Process for anti-corrosion treatment, marked
by the following steps: a) Galvanisieren eines Stahlteils zum überziehen mit einer
Zinkschicht;a) Electroplating a steel part to be coated with a
Zinc layer; b) Behandeln des verzinkten Stahlteils mit einer Phosphatlösung (8) zur Schaffung einer Zink/Phosphat-Schicht auf dem Zinküberzug; und b) treating the galvanized steel part with a phosphate solution (8) to create a zinc / phosphate layer on the zinc coating; and c) Aufbringen eines Pulverüberzuges (12) auf der Zink/Phosphat-Schicht. c) applying a powder coating (12) to the zinc / phosphate layer. 2. __Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der Stahlteil entweder durch Feuer- oder durch Elektrogalvanisierung verzinkt wird.2. __Verfahren according to claim 1, characterized in that the Steel part is galvanized either by hot or electrogalvanizing. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Phosphatbehandlung in einer Phosphatierungsanlage durchgeführt wird, die aus einem ersten Wasserspülbad (6), einem
zweiten Wasserspülbad (7), einem Zink/Phosphat-Behandlungsbad
(8), einem dritten Wasserspülbad (9), einem Chromspülbad (10)
und schließlich einem Trockenofen (11) besteht.3. The method according to claim 1 or 2, characterized in that the phosphate treatment is carried out in a phosphating system, which consists of a first water rinsing bath (6), a
second water rinsing bath (7), a zinc / phosphate treatment bath
(8), a third water rinsing bath (9), a chrome rinsing bath (10)
and finally a drying oven (11). Jj. Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß der Pulverüberzug aus einer Epoxypulverschicht besteht, die bei 150 bis 2000C eingebrannt wird.Yy. Method according to one of claims 1 to 3, characterized in that the powder coating consists of a Epoxypulverschicht, which is baked at 150 to 200 0 C. 209820/0925209820/0925 5. Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß der Pulverüberzug aus einer der ein Epoxyharz, ein Acrylharz oder Alkydharz enthaltenden Gruppen besteht.5. The method according to any one of claims 1 to 3, characterized in, that the powder coating consists of one of the groups containing an epoxy resin, an acrylic resin or an alkyd resin. 6. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß der Pulverüberzug elektrostatisch aufgebracht wird.6. The method according to any one of claims 1 to 5, characterized in that that the powder coating is applied electrostatically. 7. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß der Pulverüberzug durch überführen des Pulvers in ein fluidisiertes Bett und Einbringen des Stahlteils in das Bett aufgebracht wird.7. The method according to any one of claims 1 to 5, characterized in that that the powder coating by transferring the powder into a fluidized bed and introducing the steel part into the Bed is applied. 8. Verfahren nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß die Phosphatschicht eine Stärke von weniger8. The method according to any one of claims 1 to 7, characterized in that that the phosphate layer has a thickness of less 2 22 2 als 150 mg/9,3 dm , vorzugsweise weniger als 100 mg/9,3· dm aufweist. than 150 mg / 9.3 dm, preferably less than 100 mg / 9.3 x dm. 9. Verfahren nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß ein Unterbodenschutz auf den Pulverüberzug aufgebracht wird.9. The method according to any one of claims 1 to 8, characterized in that that an underbody protection is applied to the powder coating. 10. Verfahren nach Anspruch 9, dadurch gekennzeichnet, daß eine Öl/Harz-Kischung auf den Unterbodenschutz aufgebracht wird.10. The method according to claim 9, characterized in that an oil / resin mixture is applied to the underbody protection. 11. Verfahren nach einem oder mehreren der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß der verzinkte Stahlteil zu Transport- und Lagerzwecken mit einem Schutzüberzug aus einer Harz- oder11. The method according to one or more of claims 1 to 10, characterized in that the galvanized steel part for transport and storage purposes with a protective coating made of a resin or 209Ö20/0925209Ö20 / 0925 Lanolinmischung behandelt wird, die vor dar Phosphatbehandlung entfernt wird.Lanolin mixture is treated prior to phosphate treatment Will get removed. 12. Verfahren nach Anspruch 11, dadurch gekennzeichnet, daß der Stahlteil nach Entfernen des Schutzüberzugs in einem Entfetter (5) mit Trichloräthylendampf entfettet wird.12. The method according to claim 11, characterized in that the steel part after removing the protective coating in a degreaser (5) is degreased with trichlorethylene vapor. 209820/0925209820/0925
DE19712153809 1970-11-03 1971-10-28 Process for the anti-corrosion treatment of z. B. body parts Pending DE2153809A1 (en)