DE202009004798U1 - Surface coating with a natural stone content - Google Patents

Surface coating with a natural stone content Download PDF

Info

Publication number
DE202009004798U1
DE202009004798U1 DE202009004798U DE202009004798U DE202009004798U1 DE 202009004798 U1 DE202009004798 U1 DE 202009004798U1 DE 202009004798 U DE202009004798 U DE 202009004798U DE 202009004798 U DE202009004798 U DE 202009004798U DE 202009004798 U1 DE202009004798 U1 DE 202009004798U1
Authority
DE
Germany
Prior art keywords
surface coating
mixture
coating according
binder
flour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202009004798U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DUBBEL HARTWIG
Original Assignee
DUBBEL HARTWIG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DUBBEL HARTWIG filed Critical DUBBEL HARTWIG
Priority to DE202009004798U priority Critical patent/DE202009004798U1/en
Publication of DE202009004798U1 publication Critical patent/DE202009004798U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Oberflächenbeschichtung,
mit einem Gemisch aus Gesteinsmehl sowie einem Bindemittel,
wobei das Gemisch auf einen Untergrund auftragbar und erhärtend ausgebildet ist,
dadurch gekennzeichnet,
dass das Gesteinsmehl einen Anteil von höchstens 96% an dem Gemisch ausmacht,
und dass das Gemisch einen Entschäumer, ein Verdickungsmittel, und ein Netzmittel für das Bindemittel enthält.Surface coating,
with a mixture of rock flour and a binder,
the mixture being coatable and hardenable on a substrate,
characterized,
that the rock flour accounts for not more than 96% of the mixture,
and that the mixture contains a defoamer, a thickener, and a wetting agent for the binder.

Description

Die Neuerung betrifft eine Oberflächenbeschichtung nach dem Oberbegriff des Anspruchs 1.The Innovation relates to a surface coating after the Preamble of claim 1.

Eine gattungsgemäße Oberflächenbeschichtung ist aus der DE 201 03 506 U bekannt.A generic surface coating is from the DE 201 03 506 U known.

Der Neuerung liegt die Aufgabe zugrunde, eine gattungsgemäße Oberflächenbeschichtung dahingehend zu verbessern, dass diese sich möglichst vielseitig einsetzen lässt.Of the Innovation is the object of a generic Surface coating to improve that this can be used as versatile as possible.

Diese Aufgabe wird durch eine Oberflächenbeschichtung mit den Merkmalen des Anspruchs 1 gelöst.These Task is accomplished by a surface coating with the Characteristics of claim 1 solved.

Die Neuerung schlägt mit anderen Worten vor, den Anteil des Gesteinsmehls auf ein Maß zu begrenzen, welches einerseits den Natursteincharakter der Oberflächenbeschichtung nach wie vor wahrt, andererseits jedoch durch die Zugabe eines vergleichsweise höheren Bindemittelanteils die Möglichkeit eröffnet, die obere Flächenbeschichtung mit einem höheren Maß an Flexibilität zu versehen, so dass beispielsweise ein mit der Oberflächenbeschichtung versehener Träger verformt werden kann.The In other words, innovation proposes the proportion of To limit rock flour to a level, on the one hand the natural stone character of the surface coating as before, on the other hand, however, by the addition of a comparatively higher binder content opens the possibility the upper surface coating with a higher Degree of flexibility, so for example a carrier provided with the surface coating can be deformed.

Auf diese Weise lässt sich beispielsweise im Bereich des Innenausbaus die Herstellung gewölbter Wandflächen erreichen, indem zunächst ein Trägermaterial, wie beispielsweise eine Holzwerkstoffplatte oder eine metallische Platte mit der vorschlagsgemäßen Oberflächenbeschichtung versehen wird und anschließend gebogen wird.On This way, for example, in the field of interior design achieve the production of arched wall surfaces, by first a carrier material, such as a wood-based panel or a metallic plate with the proposed Surface coating is provided and then is bent.

Eine problemlose Verarbeitung der einzelnen Inhaltsstoffe des Gemisches wird durch einen Entschäumer unterstützt, und ein Verdickungsmittel ist vorgesehen, um die gewünschte Konsistenz des Gemisches einstellen zu können, so dass dieses problemlos aufgestrichen werden kann und anschließend „steht", ohne wie eine Flüssigkeit weg zu laufen.A easy processing of the individual ingredients of the mixture is supported by a defoamer, and a thickening agent is provided to the desired Consistency of the mixture to be able to adjust so that this can be painted easily and then "stands", without running away like a liquid.

Ein Netzmittel dient zur Erzielung eines optimalen Verbundes zwischen dem Bindemittel und den einzelnen Teilchen des Gesteinsmehl, indem es die Benetzung der Gesteinsmehl-Körperchen mit dem Bindemittel unterstützt bzw. verbessert. Hierdurch wird auch ein optimaler Zusammenhalt der einzelnen Körnchen des Gesteinsmehls durch das Bindemittel begünstigt, was für die gewünschte Verformbarkeit des beschichteten Trägermaterials von Bedeutung ist: Durch die optimale Benetzung der Gesteinsmehl-Körnchen wird das Auftreten von Rissen vermieden, wenn das Trägermaterial samt seiner darauf befindlichen Beschichtung verformt wird.One Wetting agent serves to achieve an optimal bond between the binder and the individual particles of the rock flour by it wetting the rock flour particles with the binder supports or improves. This will also be an optimal Cohesion of the individual granules of the rock flour the binder favors what the desired Deformability of the coated support material is important: Due to the optimal wetting of the rock meal granules The occurrence of cracks is avoided when the carrier material is deformed together with its coating thereon.

Die vorschlagsgemäße Oberflächenbeschichtung kann auf unterschiedlichsten Untergründen wie z. B. auf Holz und auf Holzwerkstoffen, oder auf Metallen, oder auf Kunststoffen wie z. B. Acrylglas verarbeitet werden. Sie eignet sich hervorragend zur Beschichtung von wahlweise ebenen Flächen – die dann eben verbleiben oder gebogen werden können – oder von Flächen, die von vornherein gewölbt sind, z. B. Lampenschirme, Vasen oder dergleichen.The Proposed surface coating can be used on a variety of surfaces such. B. on Wood and on wood-based materials, or on metals, or on plastics such as B. acrylic glass are processed. It is ideal for coating flat surfaces - the then just remain or can be bent - or of surfaces that are arched from the beginning, z. As lampshades, vases or the like.

Vorteilhaft kann in an sich bekannter Weise das Gemisch Acryl als Bindemittel enthalten. Dieses hat sich einerseits hinsichtlich der Verarbeitung und der späteren Produkteigenschaften der ausgehärteten Beschichtung bewährt und beeinträchtigt aufgrund seiner Transparenz die ansonsten gewünschte Farbgebung des Beschichtungsmaterials nicht.Advantageous can in a conventional manner, the mixture of acrylic as a binder contain. This has on the one hand in terms of processing and the later product properties of the cured Coating proven and impaired due to its transparency the otherwise desired coloring of the coating material not.

Vorteilhaft kann das Gemisch Marmormehl als Gesteinsmehl enthalten. Dieses Material ist problemlos und wirtschaftlich erhältlich und problemlos verarbeitbar; es bewirkt zudem eine her vorragende Natursteinoptik bzw. mineralische Optik der Beschichtung.Advantageous The mixture may contain marble powder as rock flour. This material is easily and economically available and easy to process; It also produces a protruding natural stone look or mineral Optics of the coating.

Vorteilhaft kann dabei ein helles Marmormehl verwendet werden, beispielsweise ein Marmormehl mit weißer oder beiger Farbgebung. Einerseits stellt dies einen hervorragenden natürlichen Stein-Farbton dar, und andererseits lässt sich dieser helle Grundton problemlos einfärben, beispielsweise von bestimmten Mineralien, Oxyden oder Pigmenten. Diese den Farbton des Gesteinsmehls beeinflussenden Materialien werden im Rahmen des vorliegenden Vorschlages als Farbstoffe bezeichnet, und je nach gewünschter Oberflächencharakteristik des herzustellenden Produkts kann die vorschlagsgemäße Oberflächenbeschichtung einen derartigen Farbstoff enthalten. Insbesondere kann beispielsweise Eisenoxyd als Farbstoff verwendet werden, der der Oberflächenbeschichtung eine sehr natürliche Farbgebung verleiht.Advantageous In this case, a light marble flour can be used, for example a marble flour with white or beige coloring. On the one hand this is an excellent natural stone hue, and on the other hand, this bright basic tone can be easily Coloring, for example, certain minerals, oxides or pigments. These affect the color of the rock flour Materials are used in the context of the present proposal as dyes referred, and depending on the desired surface characteristics of the product to be produced may be as proposed Surface coating containing such a dye. In particular, for example, iron oxide can be used as the dye the surface coating is a very natural Coloring gives.

Die Körnchen des Gesteinsmehls können vorzugsweise eine Korngröße von 0 bis höchstens 1,5 mm aufweisen, vorzugsweise eine Korngröße von nicht mehr als 1 oder 1,2 mm. Durch diese sehr feine Körnung des Gesteinsmehls wird einerseits die Abformung von reliefartigen Vorlagen begünstigt, so dass beispielsweise natürlich vorkommende oder künstlich geschaffene Vorlagen abgeformt werden können und in diese Form dann die vorschlagsgemäße Oberflächenbeschichtung eingebracht wird oder eine derartige Form auf die auf ein Trägermaterial aufgetragene Oberflächenbeschichtung aufgedrückt wird, um eine Oberflächenprofilierung der Beschichtung zu erreichen. Aufgrund der sehr kleinen Korngröße des Gesteinsmehls können derartige Vorlagen besonders detailgetreu abgeformt werden. Die geringe Korngröße begünstigt darüber hinaus den Zusammenhalt innerhalb der Oberflächenbeschichtung, also die Verformbarkeit eines beschichteten Trägers, ohne dass dabei Risse auftreten.The granules of the rock flour may preferably have a grain size of 0 to at most 1.5 mm, preferably a grain size of not more than 1 or 1.2 mm. Due to this very fine grain size of the rock flour, on the one hand the impression of relief-like templates is favored, so that, for example, naturally occurring or artificially created templates can be molded and then the proposed surface coating is introduced into this mold or such a form is pressed onto the surface coating applied to a carrier material is to achieve a surface profiling of the coating. Due to the very small grain size of the rock flour, such templates can be molded particularly true to detail. The small grain size also favors the Zusam within the surface coating, ie the deformability of a coated carrier, without causing cracks.

Durch die geringe Korngröße lässt sich die Oberflächenbeschichtung in einer sehr dünnen Schichtstärke auf ein Trägermaterial auftragen, so dass sie einerseits besonders wirtschaftlich verarbeitet werden kann aufgrund eines vergleichsweise geringen Materialeinsatzes, und so dass aufgrund der dünnen Schichtstärke die Verformbarkeit der beschichteten Trägermaterialien begünstigt wird und besonders kleine Krümmungsradien erzielbar sind, ohne dass in der Oberflächenbeschichtung Risse auftreten.By The small grain size allows the surface coating in a very thin layer thickness on a carrier material Apply, so that on the one hand processed particularly economical can be due to a relatively small amount of material, and so because of the thin layer thickness the deformability of the coated substrates is favored and particularly small radii of curvature can be achieved without being in the surface coating Cracks occur.

Vorteilhaft kann die Oberfläche der erhärteten Beschichtung angeschliffen sein. Dabei wird eine besonders natürlich wirkende, mineralische Oberfläche der Beschichtung erzielt, indem das umhüllende Bindemittel durch das Schleifen entfernt wird und die angeschliffenen einzelnen Körperchen des Gesteinsmehls frei liegen. Die Oberflächenbeschichtung weist daher die gleichen Eigenschaften auf wie ein geschnittener oder geschliffener Naturstein, beispielsweise dadurch, dass Feuchtigkeit aufgenommen werden kann und anschließend langsam durch Verdunstung wieder abgegeben wird.Advantageous may be the surface of the hardened coating be sanded. This is a particularly natural effective, mineral surface of the coating, by removing the enveloping binder by grinding and the sanded individual bodies of the rock flour lie free. The surface coating therefore has the same characteristics as a cut or ground Natural stone, for example, by absorbing moisture can and then slowly by evaporation again is delivered.

Unabhängig von diesem Effekt kann vorgesehen sein, die Oberfläche anzuschleifen, um entweder eine besonders glatte Oberfläche zu erzielen, also Oberflächenrauigkeiten abzutragen, oder um durch den Schleifvorgang eine gewünschte Oberflächenstruktur in der Beschichtung zu schaffen.Independently from this effect can be provided, the surface grind to either a particularly smooth surface to achieve, so remove surface roughness, or by the grinding process a desired surface structure to create in the coating.

Es kann vorteilhaft sein, die Oberfläche der erhärteten Beschichtung mit einer transparenten Versiegelung zu versehen, beispielsweise als Verschleißschutz oder um bei einer möglichst glatten Oberfläche, die beispielsweise durch das Anschleifen der erhärteten Oberflächenbeschichtung erzielt worden war, das Eindringen von Feuchtigkeit oder Verschmutzungen in die einzelnen Gesteinskörperchen zu vermeiden.It may be beneficial to the surface of the hardened To provide coating with a transparent seal, for example as wear protection or at a possible smooth surface, for example, by grinding the hardened surface coating has been achieved was the ingress of moisture or dirt into the to avoid single rock bodies.

Für eine derartige Versiegelung kommt vorteilhaft insbesondere ein Material in Betracht, welches dem Bindemittel gleich ist oder ähnlich ist, beispielsweise Acryl, wenn auch Acryl als Bindemittel verwendet wird. Auf diese Weise ist durch die Stoffgleichheit ein besonders guter Halt der Versiegelung auf der Oberflächenbeschichtung erzielbar.For Such a seal is advantageous in particular a material which is the binder or the like is, for example, acrylic, although acrylic used as a binder becomes. In this way, the material equality is a special good hold of the seal on the surface coating achievable.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - DE 20103506 U [0002] - DE 20103506 U [0002]

Claims (10)

Oberflächenbeschichtung, mit einem Gemisch aus Gesteinsmehl sowie einem Bindemittel, wobei das Gemisch auf einen Untergrund auftragbar und erhärtend ausgebildet ist, dadurch gekennzeichnet, dass das Gesteinsmehl einen Anteil von höchstens 96% an dem Gemisch ausmacht, und dass das Gemisch einen Entschäumer, ein Verdickungsmittel, und ein Netzmittel für das Bindemittel enthält.A surface coating comprising a mixture of rock flour and a binder, the mixture being coatable and hardenable on a substrate, characterized in that the rock flour constitutes at most 96% of the mixture, and in that the mixture comprises a defoamer, a thickening agent, and a wetting agent for the binder. Oberflächenbeschichtung nach Anspruch 1, dadurch gekennzeichnet, dass das Gemisch Acryl als Bindemittel enthält.Surface coating according to claim 1, characterized characterized in that the mixture contains acrylic as a binder. Oberflächenbeschichtung nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Gemisch Marmormehl als Gesteinsmehl enthält.Surface coating according to claim 1 or 2, characterized in that the mixture marble flour as rock flour contains. Oberflächenbeschichtung nach Anspruch 3, dadurch gekennzeichnet, dass das Marmormehl einen hellen Farbton aufweist wie Weiß oder Beige.Surface coating according to claim 3, characterized characterized in that the marble flour has a light hue like white or beige. Oberflächenbeschichtung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass das Gemisch einen Farbstoff enthält.Surface coating according to one of the preceding Claims, characterized in that the mixture has a Contains dye. Oberflächenbeschichtung nach Anspruch 5, dadurch gekennzeichnet, dass das Gemisch Eisenoxyd als Farbstoff enthält.Surface coating according to claim 5, characterized characterized in that the mixture contains iron oxide as a dye. Oberflächenbeschichtung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Körnchen des Gesteinsmehl eine Korngröße von 0 bis höchstens 1,5 mm aufweisen.Surface coating according to one of the preceding Claims, characterized in that the granules of the rock flour has a particle size of 0 to at most 1.5 mm. Oberflächenbeschichtung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Oberfläche der erhärteten Beschichtung angeschliffen ist.Surface coating according to one of the preceding Claims, characterized in that the surface the hardened coating is sanded. Oberflächenbeschichtung nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, dass die Oberfläche der erhärteten Beschichtung mit einer transparenten Versiegelung versehen ist.Surface coating according to one of the preceding Claims, characterized in that the surface the hardened coating with a transparent seal is provided. Oberflächenbeschichtung nach Anspruch 9, dadurch gekennzeichnet, dass die Versiegelung aus Acryl besteht.Surface coating according to claim 9, characterized characterized in that the seal is made of acrylic.
DE202009004798U 2009-05-11 2009-05-11 Surface coating with a natural stone content Expired - Lifetime DE202009004798U1 (en)