DE19954484A1 - Schütt-Dämmstoffe - Google Patents
Schütt-DämmstoffeInfo
- Publication number
- DE19954484A1 DE19954484A1 DE19954484A DE19954484A DE19954484A1 DE 19954484 A1 DE19954484 A1 DE 19954484A1 DE 19954484 A DE19954484 A DE 19954484A DE 19954484 A DE19954484 A DE 19954484A DE 19954484 A1 DE19954484 A1 DE 19954484A1
- Authority
- DE
- Germany
- Prior art keywords
- shives
- materials according
- bulk insulation
- insulation materials
- shavings
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Es werden Schütt-Dämmmaterialien aus Stängeln faserliefernder Pflanzen beschrieben, die mit einem Polymermaterial umhüllt und gegebenenfalls mit Flammschutzmitteln imprägniert sind.
Description
Holzteile aus Stengel der faserliefernden Pflanzen, die Schäben, sind aufgrund
ihres geringen Schüttgewichtes und der niedrigen Dichte als Schütt-Dämm
material besonders geeignet. Sie können in der dämmenden Fußbodensanierung
in Altbauten, in Neubauten als Dämmschicht sowie in Böden von Sporthallen
und Gymnastikräumen besonders vorteilhaft, aber auch als ausgleichende
Dämmschicht in anderen Bereichen eingesetzt werden.
Nachteile der Schäben sind jedoch der hohe Staubgehalt, der beim Transport
und beim Verarbeiten wächst, die leichte Entzündbarkeit und die geringe
Beständigkeit gegen Mikroorganismen, was je nach Feuchtigkeitsgehalt zum
allmählichen Zerfall führt.
Diese Schwierigkeiten können weitgehend dadurch behoben werden, dass man
die Schäben mit organischen Polymerstoffen umhüllt. Es kann zweckmäßig
sein, zuerst mit einer Flammschutzausrüstung auf Phosphorbasis, wie z. B. in der
DE-OS 196 30 828, gegebenenfalls mit einem Gehalt an Bor, zu imprägnieren.
Durch eine Hitzebehandlung wird dann getrocknet, wobei die von Natur vorhan
denen Mikroorganismen zerstört werden.
Gegenstand der vorliegenden Patentanmeldung sind daher verholzte Teile aus
Stengeln faserliefernder Pflanzen (Schäben), die mit einem Polymermaterial
umhüllt sind und als Schüttdämmstoffe eingesetzt werden können.
Gegebenenfalls können die Materialien mit Flammschutzmitteln imprägniert
sein. Geeignete Holzteile sind die Schäben von Hanf, Kenaf und Flachs, sowie
von Ramie, Schönmalve, Sunn-Hanf und Kendyr-Schäben.
Als organische Polymere können grundsätzlich gängige Kunststoffe und
Kunstharze eingesetzt werden, wie z. B. Polyolefine, Polyester und Polyamide,
insbesondere niedrigschmelzende Sorten, sowie ungesättigte Polyester,
Polyacrylnitril, Phenolharze, Melamin- und Harnstoff-Formaldehyd-Harze,
Epoxydharze, Acryl- und Methacrylharze, Polyvinylalkohol und Polyvinylacetat
usw.
Vom ökologischen Standpunkt scheint es jedoch sinnvoll, nur baubiologisch
unbedenklich erscheinende Polymere zu verwenden. Besonders geeignet sind
Polyglykolat, Polylactat, Polyhydroxybutyrat, Polyhydroxybutyrat-valeriat,
Poly-ε-caprolacton, Poly(1,4-dioxanon-2) sowie deren Copolymerisate. Auch
Acylstärken und Acylcellulosen, wie die Acetate, Propionate und Butyrate und
deren Mischungen sowie Lignin sind geeignet. Zur Erniedrigung der
Erweichungstemperatur können den Polymeren geeignete Weichmacher, wie
z. B. Azelain- und Sebacinester sowie Polyole, beigefügt sein. Um ein gewisses
Verdichten zu begünstigen, ist es zweckmäßig Additive mit
Weichmachercharakter, wie Ester ungesättigter oder epoxidierter Fettsäuren,
wie z. B. Leinöl, epoxidierte Leinöl- und Sojaöle, Isanoöle sowie Methylester
ungesättigter Fettsäuren zuzusetzen.
Zur Herstellung der Schütt-Dämm-Stoffe werden die Schäben - falls erwünscht -
mit der Lösung des Flammschutzmittels imprägniert und getrocknet, wobei die
Trocknungstemperatur über 120°C liegen sollte. Anschließend wird das
Schäbenmaterial in einem Schaufelmischer mit Pulvern, Granulat, Lösungen
oder Dispersionen der genannten Polymere behandelt. Die Behandlung kann
auch durch Besprühen oder einfaches Mischen erfolgen. Nach dem
Mischvorgang wird das vorhandene Lösungsmittel verdampft. Den Lösungen
bzw. Dispersionen können die genannten Additive beigefügt werden.
Es kann aber auch so verfahren werden, dass man die Schäben bei
Raumtemperatur mit pulverförmigen oder granulierten Polymermaterialien
mischt und die Mischung über die Erweichungstemperatur des Polymers hinaus
erwärmt.
Im Falle der Phenolharze, Harnstoff und Melaminharze werden Vorkondensate
eingesetzt, die bei der anschließenden Trocknungsphase kondensieren.
Die Schäben können in jedem Verhältnis mit den Polymermaterialien verarbeitet
werden. Geeignete Auftragsmengen liegen bei 15-75%, vorzugsweise 30-50%
Polymermaterial bezogen auf die Schäbenmenge.
In einem heizbaren Pflugscharmischer werden 2 kg Hanfschäben (Teilchengröße
2-7 mm) mit 400 gr. einer Monoammonium-Phosphatlösung, die 50 gr.
Ammoniumborat enthält, besprüht, gut durchmischt und bei einer Temperatur
von 125°C getrocknet. Die Mischung wird mit 800 gr. Polyhydroxybutyrat und
100 gr. Azelainsäure-diethylester versetzt und unter kräftigem Mischen
allmählich auf 145°C gebracht. Anschließend wird das Material unter weiterem
Bewegen abgekühlt.
Eine vorher behandelte Mischung aus 1 kg Flachs- und 1 kg Kenafschäben
werden in einem Schaufeltrockner mit 2 kg einer 40%igen Lösung von
Polystyrol in Ethylacetat und 150 gr. Leinöl auf 120°C erhitzt, wobei das
Lösungsmittel abdestilliert. Wenn das gesamte Lösungsmittel verdampft ist,
wird unter weiterem Bewegen auf Raumtemperatur abgekühlt.
In einer Sprühmischtrommel nach Telschik werden 1000 gr. Flachsschäben mit
einer Ammoniumphosphatlösung analog Beispiel 1 behandelt und dann mit
800 gr. einer Movilith-Dispersion beaufschlagt und anschließend in einem
Pflugscharmischer bei 120°C getrocknet.
In einem Wirbelschichtreaktor werden ca. 2 kg Flachsschäben gemeinsam mit
einer äquivalenten Menge Acylstärke oder Acylcellulose aufgewirbelt und
anschließend auf ca. 140-150°C geheizt. Hierbei legt sich eine Polymerschicht
als feiner Film um die Schäben. Eine weitere Temperaturerhöhung von ca.
10-15°C dient der Vergleichmäßigung. Anschließend wird der Reaktor abgekühlt
und die ummantelten Schäben entnommen.
Claims (7)
1. Schütt-Dämmstoffe aus Holzteilen faserliefernder Pflanzen (Schäben)
umhüllt mit organischen Polymeren unter Zusatz weichmachender Additive.
2. Schütt-Dämm-Stoffe nach Anspruch 1, dadurch gekennzeichnet, dass sie als
Holzteile Schäben von Hanf, Flachs, Kenaf, Ramie, Schönmalve, Sunn-
Hemp und Kedyr sowie deren Mischungen enthalten.
3. Schütt-Dämm-Stoffe nach Anspruch 1, dadurch gekennzeichnet, dass sie mit
Flammschutzmitteln auf Phosphor- und Borbasis imprägniert sind.
4. Schütt-Dämm-Stoffe nach Anspruch 1, dadurch gekennzeichnet, dass sie mit
einer Imprägnierung und Umhüllung von 5-70%, vorzugsweise 35-50%, der
folgenden Polymere enthalten: Polyolefine, Polyester und Polyamide,
insbesondere niedrigschmelzende Sorten, sowie ungesättigte Polyester,
Polyacrylnitril, Phenolharze, Melamin- und Harnstoff-Formaldehyd-Harze,
Epoxydharze, Acryl- und Methacrylharze, Polyvinylalkohol und
Polyvinylacetat usw.
5. Verfahren zur Herstellung von Schütt-Dämm-Stoffen nach Anspruch 1,
dadurch gekennzeichnet, dass die Schäben mit einer Lösung des Polymers in
einem geeigneten Lösungsmittel in einer Sprüh-Mischtrommel beaufschlagt
und anschließend getrocknet werden.
6. Verfahren zur Herstellung von Schütt-Dämm-Stoffen nach Anspruch 1,
dadurch gekennzeichnet, dass die Schäben mit Pulver oder Granulat der
Polymere gemischt und anschließend unter weiterem Mischen auf die
Schmelztemperatur des Polymers gebracht werden.
7. Schütt-Dämm-Stoffen nach Anspruch 1, dadurch gekennzeichnet, dass die
eingesetzten Polymere weitere Additive, wie gängige Weichmacher, sowie
ungesättigte und epoxidierte Pflanzenöle sowie ungesättigte und epoxidierte
Methylester ungesättigter Fettsäuren enthalten.